Patent Grant
8530573
The present invention relates to thermosetting adhesive compositions, methods of preparation and uses therefor. In particular, the present invention relates to thermosetting compositions containing modified calcium carbonate.
As the electronics industry advances, and production of light weight components increases, the development of new materials gives producers increased options for further improving the performance and ease of manufacture of such components. Adhesive compositions are used for a variety of purposes in the fabrication and assembly of semiconductor packages and microelectronic devices. The more prominent uses include bonding of electronic elements such as integrated circuit chips to lead frames or other substrates, and bonding of circuit packages or assemblies to printed wire boards.
Adhesives used in the electronic packaging industry typically contain a thermosetting resin, combined with a filler and some type of curing initiator. These resins are primarily used in the electronics industry for the preparation of non-hermetic electronic packages. Adhesives useful for electronic packaging applications typically exhibit properties such as good mechanical strength, curing properties that do not affect the component or the carrier, and Theological properties compatible with application to microelectronic and semiconductor components. Examples of such packages are ball grid array (BGA) assemblies, super ball grid arrays, IC memory cards, chip carriers, hybrid circuits, chip-on-board, multi-chip modules, pin grid arrays, and the like.
In addition, there are many potential applications for adhesives having electrically insulating properties. Such materials must, however, satisfy a combination of criteria, i.e., in addition to exhibiting a low dielectric constant, such materials must also have good dispensability and good adhesion properties. Non-conductive fillers traditionally employed for the preparation of adhesives having electrically insulating properties include aluminum nitride, boron nitride, alumina, silicon dioxide, and the like.
The rheology of an adhesive paste is a very important consideration for manufacturing purposes. For example, separation of the filler from the resin in the syringe, a clean break of adhesive between each dispense thereof, and the presence of drip-free syringes in the dispense operation are all important attributes for consistent dispensing properties.
For all these applications, the microelectronics industry continues to require new adhesive formulations that are able to meet its varying demands. Accordingly, there is a need for the development of compositions and formulations to address the requirements of this rapidly evolving industry.
The invention is based on the discovery that surface modified calcium carbonate can be used as a filler for the preparation of adhesive formulations having low coefficients of thermal expansion. Invention compositions display excellent rheological properties. In addition, adhesive compositions containing calcium carbonate filler are particularly useful in stacked die applications. Calcium carbonate has a Mohs hardness of 3.0, and therefore does not damage die surfaces when the die and adhesive are assembled in a stacked arrangement. The inherent softness of calcium carbonate makes it much less abrasive than silica (another common non-conductive filler), which has a Mohs hardness of 7.0. Calcium carbonate has another practical advantage compared to silica fillers in that it can act as its own pigment. Adhesives containing only silica fillers do not reflect light well and this can be problematic for the optical recognition equipment used in automated die bonding equipment. Calcium carbonate fillers do not have this problem.
The surface modifications described in this invention can be used to improve the properties of the thermoset adhesives. The surface modifications described herein ensure a strong bond between the calcium carbonate filler and the thermoset resin. In some embodiments the modified calcium carbonate filler can also act as the sole cross-linking component in the adhesive. In addition, the surface modifications described in this invention can be used to improve the properties of the thermoset adhesives.
Invention formulations, furthermore, possess low thermal coefficients of expansion (CTE). Calcium carbonate has a linear thermal coefficient of expansion of 9 ppm/° K. This is much lower than the lowest CTE for organic thermosets, which usually are between 50 and 85 ppm/° C. The addition of the calcium carbonate filler, therefore, can be used to lower the overall CTE of the adhesive composition. Invention formulations can be used for a variety of purposes, such as, for example, for the preparation of filled adhesive formulations with a reduced propensity to settle out, excellent dispensing characteristics due to the thixotropic nature thereof, and the like.
In one embodiment of the invention, there are provided adhesive compositions including a polymerizable monomer vehicle selected from maleimides, (meth)acrylates, vinyl ethers, propargyl ethers, vinyl esters, urethanes, polyesters, polyester-linked (meth)acrylates, fumarates, maleates, itaconates, styrenic compounds, allyl functional compounds, epoxies, oxetanes, oxazolines, benzoxazines, or a mixture of any two or more thereof, a modified calcium carbonate, and a curing catalyst.
In another embodiment, there are provided assemblies including a first article permanently adhered to a second article by a cured aliquot of a composition including a polymerizable monomer vehicle, a modified calcium carbonate, and a curing catalyst.
In another embodiment, there are provided assemblies including a microelectronic device permanently adhered to a substrate by a cured aliquot of a composition including a polymerizable monomer vehicle, a modified calcium carbonate, and a curing catalyst.
In still another embodiment, there are provided methods for adhesively attaching a first article to a second article. Such methods can be performed, for example, by (a) applying an adhesive composition to the first article, wherein the adhesive composition includes a polymerizable monomer vehicle, a modified calcium carbonate, and a curing catalyst, (b) bringing the first and second article into intimate contact to form an assembly wherein the first article and the second article are separated only by the adhesive composition applied in step (a), and thereafter, (c) subjecting the assembly to conditions suitable to cure the adhesive composition.
In another embodiment, there are provided methods for adhesively attaching a microelectronic device to a substrate. Such methods can be performed, for example, by (a) applying an adhesive composition to the substrate and/or the microelectronic device, wherein the adhesive composition comprises a polymerizable monomer vehicle, a modified calcium carbonate, and a curing catalyst, (b) bringing the substrate and the device into intimate contact to form an assembly wherein the substrate and the device are separated only by the composition applied in step (a), and thereafter, (c) subjecting the assembly to conditions suitable to cure the composition.
It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the invention claimed. As used herein, the use of the singular includes the plural unless specifically stated otherwise. As used herein, “or” means “and/or” unless stated otherwise. Furthermore, use of the term “including” as well as other forms, such as “includes,” and “included,” is not limiting.
The section headings used herein are for organizational purposes only and are not to be construed as limiting the subject matter described. Unless specific definitions are provided, the nomenclatures utilized in connection with, and the laboratory procedures and techniques of analytical chemistry, synthetic organic and inorganic chemistry described herein are those known in the art. Standard chemical symbols are used interchangeably with the full names represented by such symbols. Thus, for example, the terms “hydrogen” and “H” are understood to have identical meaning. Standard techniques may be used for chemical syntheses, chemical analyses, and formulation.
The invention is based on the discovery that modified calcium carbonates can be used as fillers for the preparation of adhesive formulations having excellent adhesive properties. Invention compositions display excellent Theological properties, in addition to low coefficients of thermal expansion.
As used herein, “aliphatic” refers to any alkyl, alkenyl, or cycloalkyl moiety.
As used herein, “alkyl” refers to straight or branched chain hydrocarbyl groups having from 1 up to about 500 carbon atoms. “Substituted alkyl” refers to alkyl moieties bearing substituents including alkyl, alkenyl, alkynyl, hydroxy, oxo, alkoxy, mercapto, cycloalkyl, substituted cycloalkyl, heterocyclic, substituted heterocyclic, aryl, substituted aryl, heteroaryl, substituted heteroaryl, aryloxy, substituted aryloxy, halogen, haloalkyl, cyano, nitro, nitrone, amino, amido, —C(O)H, —C(O)—, —C(O)O—, —S—, —S(O)2, —OC(O)—O—, —NR—C(O), —NR—C(O)—NR, —OC(O)—NR, wherein R is H or lower alkyl, acyl, oxyacyl, carboxyl, carbamate, sulfonyl, sulfonamide, sulfuryl, and the like.
As used herein, “cycloalkyl” refers to cyclic ring-containing groups containing in the range of about 5 up to about 20 carbon atoms, and “substituted cycloalkyl” refers to cycloalkyl groups further bearing one or more substituents as set forth above. In some embodiments, the cycloalkyl refers to cyclic ring-containing groups containing in the range of about 5 up to about 15 carbon atoms
As used herein, “aryl” refers to aromatic groups having in the range of 6 up to 14 carbon atoms and “substituted aryl” refers to aryl groups further bearing one or more substituents as set forth above.
In one embodiment of the invention, there are provided adhesive compositions including a polymerizable monomer vehicle selected from maleimides, (meth)acrylates, vinyl ethers, propargyl ethers, vinyl esters, urethanes, polyesters, polyester-linked (meth)acrylates, fumarates, maleates, itaconates, styrenic compounds or allyl functional compounds, epoxies, oxetanes, oxazolines, benzoxazines, or a mixture of any two or more thereof, a modified calcium carbonate, and a curing catalyst.
As readily recognized by those of skill in the art, a wide variety of additional components can optionally be incorporated into the above-described compositions, such as, for example, coupling agents, anti-oxidants, stabilizers, bleed control agents, additional fillers (other than the required modified calcium carbonate filler), inert diluents, reactive diluents, adhesion promoters, flexibilizers, dyes, pigments, and the like.
While the use of inert diluents is not excluded from the practice of the invention, it is generally preferred that compositions of the invention remain substantially free of solvent, so as to avoid the potentially detrimental effects thereof, e.g., creation of voids caused by solvent escape, the environmental impact of vaporized solvent, the redeposition of outgassed molecules in the surface of the article, and the like.
Monomer vehicles contemplated for use in accordance with the present invention include maleimides, (meth)acrylates, vinyl ethers, propargyl ethers, vinyl esters, urethanes, polyesters, polyester-linked (meth)acrylates, fumarates, maleates, itaconates, styrenic compounds, allyl functional compounds, epoxies, oxetanes, oxazolines, benzoxazines, and the like, or a mixture of any two or more thereof.
Exemplary maleimides contemplated for use in the practice of the invention include compounds having the structure:
wherein:
In some embodiments, R and Q are each independently substituted or un-substituted linear, branched, or cyclic aliphatic moieties having from 2 to about 500 carbon atoms. In other embodiments, R and Q are each independently substituted or un-substituted aromatic or heteroaromatic moieties having from 6 to about 14 carbon atoms. In still other embodiments, n is 1-6. In still further embodiments, n is 1-4. In one embodiment, n is 2.
Exemplary urethanes contemplated for use in the practice of the invention include compounds having the structure:
wherein:
In some embodiments, X is a substituted or un-substituted linear, branched, or cyclic aliphatic moiety having from 2 to about 500 carbon atoms. In other embodiments, X is a substituted or un-substituted aryl or heterocyclic moiety having from 6 to about 14 carbon atoms. In other embodiments, X is a substituted or un-substituted linear, branched, or cyclic aliphatic moiety having from 2 to about 50 carbon atoms. In still further embodiments, n is 1 to about 5. In further embodiments, n is 1 to about 3. In one embodiment, n is 2.
Exemplary polyester monomer vehicles contemplated for use in the practice of the invention include compounds having the structure:
wherein:
In some embodiments, R is a substituted or un-substituted cycloalkyl having from 5 to about 20 carbon atoms. In other embodiments, R is a substituted or un-substituted cycloalkyl having from 5 to about 12 carbon atoms. In still other embodiments, R is a substituted or un-substituted cyclopentyl, cyclohexyl, norbornyl, tetracyclododecyl, or dicyclopentadienyl.
In some embodiments, Q is a substituted or un-substituted aryl or heteroaryl having from 6 to about 14 carbon atoms. In certain embodiments, Q is a substituted or un-substituted phenyl or naphthyl. In other embodiments, Q is a substituted or un-substituted cycloalkyl. In one embodiment, Q is a substituted or un-substituted norbornenyl.
A wide variety of modified calcium carbonate fillers are contemplated for use in the practice of the invention. In some embodiments, the modified calcium carbonate is modified with an acid. In some embodiments, the acid is a carboxylic acid. In other embodiments the acid is a functionalized carboxylic acid. Some examples of functionalized carboxylic acids useful in the practice of the invention include, but are not limited to, maleimidoundecanoic acid, maleimidohexanoic acid, 4-maleimidobenzoic acid, 3-maleimidobenzoic acid, 2-maleimidoacetic acid, 3-maleimidopropionic acid, 4-maleimidobutanoic acid, 4-hydroxybenzoic acid, acrylic acid, methacrylic acid, furoic acid, cinnamic acid, sorbic acid, undecenoic acid and the like. Also contemplated are acid esters such as fumaric acid esters, maleic acid esters, itaconic acid esters, and the like. Functional non-carboxylic acids are also contemplated in the practice of the invention (e.g. vinybenzene sulfonic acid, diallyl phosphate, and the like).
As readily recognized by those of skill in the art, a wide variety of curing catalysts can be employed in the preparation of invention compositions. The preferred catalyst to be used will, of course, depend on the monomer vehicle employed. For example, for those monomer vehicles which cure by a free radical mechanism, free radical initiators such as peroxy esters, peroxy carbonates, hydroperoxides, alkylperoxides, arylperoxides, and the like can be employed.
For those monomer vehicles, which cure by cationic and/or anionic polymerization, cationic catalysts, transition metal catalysts, and the like can be employed. Exemplary cationic catalysts contemplated for use herein include onium salts, iodonium salts, sulfonium salts, zinc salts, tin salts, and the like. Exemplary anionic catalysts include tertiary amines, imidazoles, imidazole salts, dicyanodicyanamide, and the like.
Exemplary transition metal catalysts contemplated for use herein include nickel, copper, cobalt and the like, in the form of a chelate, a soap, or the like.
The ratio of the various components of invention compositions can vary within wide ranges. For example, the quantity of monomer vehicle can vary anywhere within the range of about 25 to about 90 weight percent (wt %) of invention composition. In some embodiments, the quantity of monomer vehicle is in the range of about 40 up to about 80 wt % (based on the total weight of the final composition).
Similarly, the quantity of modified calcium carbonate employed in the practice of the invention can vary within wide ranges, typically falling in the range of about 10 up to about 75 wt % of invention composition. In some embodiments, the modified calcium carbonate is present in the composition in the range of about 20 up to about 60 wt % (based on the total weight of the final composition).
The quantity of curing catalyst employed in the practice of the invention can also vary widely, typically falling in the range of about 0.01 up to about 10 wt % of the composition (based on the total weight of the finished composition). As readily recognized by those of skill in the art, quantities at the lower end of this range are generally suitable when using transition metal catalysts, while quantities falling in the middle to the upper end of the range are generally suitable when free radical initiators are employed.
Invention compositions have excellent handling properties, typically existing as a thixotropic paste, which can readily be dispensed using standard equipment.
In another embodiment of the invention, there are provided methods for adhesively attaching a first article to a second article. Such methods can be performed, for example, by (a) applying an adhesive composition to the first article, wherein the adhesive composition includes a polymerizable monomer vehicle, a modified calcium carbonate, and a curing catalyst, (b) bringing the first and second article into intimate contact to form an assembly wherein the first article and the second article are separated only by the adhesive composition applied in step (a), and thereafter, (c) subjecting the assembly to conditions suitable to cure the adhesive composition.
Curing conditions contemplated for carrying out the above-described method typically comprise a temperature in the range of about 60° C. up to 250° C., for a period of time in the range of about 0.001 up to about 6 hours. In some embodiments, the time at peak cure temperature is 0.01 up to about 0.5 hours.
In another embodiment of the invention, there are provided methods for adhesively attaching a microelectronic device to a substrate. Such methods can be performed, for example, by (a) applying an adhesive composition to the substrate and/or the microelectronic device, wherein the adhesive composition includes a polymerizable monomer vehicle, a modified calcium carbonate, and a curing catalyst, (b) bringing the substrate and the device into intimate contact to form an assembly wherein the substrate and the device are separated only by the composition applied in step (a), and thereafter, (c) subjecting the assembly to conditions suitable to cure the composition.
Curing conditions contemplated for carrying out the above-described method typically comprise a temperature in the range of about 60° C. up to 250° C., for a period in the range of about 0.001 up to about 6 hours. In some embodiments, the time at peak cure temperature is 0.01 up to about 0.5 hours.
In another embodiment of the invention, there are provided assemblies including a first article permanently adhered to a second article by a cured aliquot of the above-described composition. Such assemblies can be prepared from a variety of structures, e.g., wherein the first article is selected from a silicon-based microelectronic device, a gallium arsenide-based microelectronic device, a quartz-based microelectronic device, a sapphire-based microelectronic device, an indium phosphide-based microelectronic device, a cadmium sulfide-based microelectronic device, lithium niobate-based microelectronic device, and the like, and the second article is selected from lead frames, pin grid arrays, ceramics, and the like.
In a further embodiment of the invention, there are provided assemblies including a microelectronic device permanently adhered to a substrate by a cured aliquot of the above-described composition. Microelectronic devices contemplated for use in the practice of the present invention include lead frames, pin grid arrays, laminate materials, and the like.
As readily recognized by those of skill in the art, compositions according to the present invention can also be employed for the preparation of a variety of structures, e.g., advanced composites, molding resins, glob-top structures, underfill materials, and the like, employing techniques which are readily available in the art.
The invention will now be further described with reference to the following non-limiting examples.
The above bi-functional compound: 11-maleimidoundecanoic acid was prepared according to the following procedure: A two liter flask was charged with 61.25 grams (0.625 moles) maleic anhydride, 500 grams toluene, and 100 grams N-methylpyrrolidone (NMP). This mixture was stirred magnetically until all of the anhydride had dissolved and 100.5 grams (0.5 mole) of 11-aminoundecanoic acid was then added to this solution over the course of five minutes. The mixture was then stirred at 50-60° C. for one hour to fully form the maleamic acid. Twenty grams of methane sulfonic acid (MSA) was added to the mixture. The flask was equipped with a Dean Stark trap and condenser and then refluxed overnight. A total of 9.8 mLs water was collected (theoretical=9.0). The mixture was then cooled to room temperature and then placed in a two-liter separatory funnel and washed with twice with 200 mL deionized water to remove the NMP and MSA. The toluene phase was transferred to a two-liter round-bottom flask. The toluene was removed under vacuum at a temperature of 60° C. The residue was then sparged with air at a bath temperature of 70° C. to remove the last traces of toluene. The product was initially recovered as an amber liquid that froze to a waxy solid upon standing at room temperature. It weighed 129 grams (92% of theory).
A 500 mL single neck flask was charged with 50.0 grams “Socal 31” (a precipitated, rhombohedral, high surface area, calcium carbonate powder from Solvay Advanced Functional Minerals), 2.5 grams 11-maleimidoundecanoic acid, 250 mL acetone, and a magnetic stir bar. A bubbler was attached and the mix was stirred at room temperature. Reaction between the acid and filler was evidenced by the evolution of carbon dioxide. The generation of carbon dioxide had ceased after twenty-four hours. The mixture was poured into a large stainless steel pan and the acetone was evaporated off. The solids were then further dried at 100° C. for four hours in an oven.
A one-liter single-neck flask was charged with 100 grams Socal 31, 400 mL acetone, 3.0 grams 4-hydroxybenzoic acid, and a stir bar. A bubbler was attached to monitor the evolution of carbon dioxide. This mixture was stirred for thirty-six hours and then the modified calcium carbonate was recovered as described in example 2.
The maleimide functionalized calcium carbonate from example 2 was intimately mixed in a one to one weight ratio with tricyclodecylmethyl acrylate (a mono-functional acrylate monomer). The composition was catalyzed with two parts per hundred of dicumyl peroxide. A portion of this composition was cured to make a pellet for testing by TMA. The cured sample was found to have a glass transition temperature of 41.3° C. The CTE below the Tg was 44.5 ppm/° C. and the CTE above the Tg was 90.9 ppm/° C. There was no evidence of thermoplastic behavior during the TMA run through 225° C. (i.e. there was no penetration by the TMA probe into the pellet). This result supports the conclusion that the modified calcium carbonate filler is acting as a cross-linker and when admixed and cured with a mono-functional acrylate monomer and resulted in a thermoset matrix devoid of any thermoplastic behavior.
An adhesive composition was formulated using the treated calcium carbonate described in Example 2. A control composition was also made, using a calcium carbonate filler that was coated with a non-functional (stearic acid) coating. The compositional information for the test adhesive and its control are summarized in Table 1.
The two compositions from Table 1 were used to bond 300×300×14 mil bare silicon die onto ceramic substrates. Six test parts were made from each composition. All parts were cured at 175° C. in an oven for one hour. Adhesion was measured via die shear at 260° C. using a Dage 4000 hot stage adhesion tester. The results of this testing as well as some of the cured properties of the two adhesive compositions in Table 1 are compared in Table 2.
The results presented in Table 2 show that while the modulus and radius of curvature were substantially the same for the two compositions, the Tg was about twenty degrees higher when the functional filler was used. The coefficient of thermal expansion above, and below, the Tg was also significantly lower for the test composition versus the control. The adhesion for the functional calcium carbonate adhesive exceeded the maximum of the shear test equipment and could not be further characterized. The control calcium carbonate adhesive did have the desirable type of cohesive (material) failure mode, but the adhesion was lower and with a wider distribution. These results support the value of calcium carbonate fillers modified with co-polymerizable surface treatments.
While the invention has been described in detail with reference to certain preferred embodiments thereof, it will be understood that modifications and variations are within the spirit and scope of that which is described and claimed.
This application claims the benefit of priority of U.S. Provisional Application Ser. No. 60/799,078 filed May 10, 2006, the entire disclosure of which is incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3901845 | Newbould | Aug 1975 | A |
| 4111879 | Mori et al. | Sep 1978 | A |
| 4774267 | Weintraub | Sep 1988 | A |
| 4968738 | Dershem | Nov 1990 | A |
| 5045127 | Dershem et al. | Sep 1991 | A |
| 5064480 | Dershem et al. | Nov 1991 | A |
| 5232962 | Dershem et al. | Aug 1993 | A |
| 5306333 | Dershem et al. | Apr 1994 | A |
| 5358992 | Dershem et al. | Oct 1994 | A |
| 5403389 | Dershem | Apr 1995 | A |
| 5447988 | Dershem et al. | Sep 1995 | A |
| 5489641 | Dersehm | Feb 1996 | A |
| 5602205 | Singh et al. | Feb 1997 | A |
| 5646241 | Dershem et al. | Jul 1997 | A |
| 5714086 | Osuna et al. | Feb 1998 | A |
| 5717034 | Dershem et al. | Feb 1998 | A |
| 5718941 | Dershem et al. | Feb 1998 | A |
| 5753748 | Dershem et al. | May 1998 | A |
| 5861111 | Dershem et al. | Jan 1999 | A |
| 5969036 | Dershem | Oct 1999 | A |
| 5973166 | Mizori et al. | Oct 1999 | A |
| 6034150 | Hoyle et al. | Mar 2000 | A |
| 6034194 | Dershem | Mar 2000 | A |
| 6034195 | Dershem | Mar 2000 | A |
| 6121358 | Dershem et al. | Sep 2000 | A |
| 6187886 | Husson et al. | Feb 2001 | B1 |
| 6211320 | Dershem et al. | Apr 2001 | B1 |
| 6300456 | Musa | Oct 2001 | B1 |
| 6369124 | Hoyle et al. | Apr 2002 | B1 |
| 6369183 | Cook et al. | Apr 2002 | B1 |
| 6423780 | Dershem et al. | Jul 2002 | B1 |
| 6429281 | Dershem et al. | Aug 2002 | B1 |
| 6521731 | Dershem et al. | Feb 2003 | B2 |
| 6620946 | Dersehm et al. | Sep 2003 | B2 |
| 6743852 | Dershem et al. | Jun 2004 | B2 |
| 6750301 | Bonneau et al. | Jun 2004 | B1 |
| 6790597 | Dershem | Sep 2004 | B2 |
| 6825245 | Dershem | Nov 2004 | B2 |
| 6831132 | Liu et al. | Dec 2004 | B2 |
| 6852814 | Dershem et al. | Feb 2005 | B2 |
| 6855745 | Hoyle et al. | Feb 2005 | B2 |
| 6916856 | Dershem | Jul 2005 | B2 |
| 6946523 | Dershem et al. | Sep 2005 | B2 |
| 6960636 | Dershem et al. | Nov 2005 | B2 |
| 6963001 | Dershem et al. | Nov 2005 | B2 |
| 7102015 | Dershem et al. | Sep 2006 | B2 |
| 7157587 | Mizori et al. | Jan 2007 | B2 |
| 7176044 | Forray et al. | Feb 2007 | B2 |
| 7199249 | Liu et al. | Apr 2007 | B2 |
| 7208566 | Mizori et al. | Apr 2007 | B2 |
| 7309724 | Dershem et al. | Dec 2007 | B2 |
| 7517925 | Dershem et al. | Apr 2009 | B2 |
| 7678879 | Dershem | Mar 2010 | B2 |
| 7863346 | Dershem et al. | Jan 2011 | B2 |
| 20020046806 | Yamada et al. | Apr 2002 | A1 |
| 20020062923 | Forray | May 2002 | A1 |
| 20020099168 | Dershem et al. | Jul 2002 | A1 |
| 20020188137 | Dershem et al. | Dec 2002 | A1 |
| 20020193541 | Dershem et al. | Dec 2002 | A1 |
| 20020198356 | Dershem et al. | Dec 2002 | A1 |
| 20030008992 | Dershem et al. | Jan 2003 | A1 |
| 20030055121 | Dershem et al. | Mar 2003 | A1 |
| 20030060531 | Dershem et al. | Mar 2003 | A1 |
| 20030087999 | Dershem et al. | May 2003 | A1 |
| 20030109666 | Dershem et al. | Jun 2003 | A1 |
| 20030125551 | Dershem et al. | Jul 2003 | A1 |
| 20030199638 | Liu et al. | Oct 2003 | A1 |
| 20030208016 | Dershem et al. | Nov 2003 | A1 |
| 20040006166 | Liu et al. | Jan 2004 | A1 |
| 20040019224 | Dershem et al. | Jan 2004 | A1 |
| 20040023926 | Guennouni et al. | Feb 2004 | A1 |
| 20040076574 | Xu et al. | Apr 2004 | A1 |
| 20040077798 | Dershem et al. | Apr 2004 | A1 |
| 20040082724 | Dershem et al. | Apr 2004 | A1 |
| 20040102566 | Forray et al. | May 2004 | A1 |
| 20040123948 | Dershem et al. | Jul 2004 | A1 |
| 20040225026 | Mizori et al. | Nov 2004 | A1 |
| 20040225045 | Forray | Nov 2004 | A1 |
| 20040225059 | Mizori et al. | Nov 2004 | A1 |
| 20050004266 | Kayano et al. | Jan 2005 | A1 |
| 20050107542 | Liu et al. | May 2005 | A1 |
| 20050136620 | Dershem et al. | Jun 2005 | A1 |
| 20050137277 | Dershem et al. | Jun 2005 | A1 |
| 20050267254 | Mizori et al. | Dec 2005 | A1 |
| 20050272888 | Dershem et al. | Dec 2005 | A1 |
| 20060009578 | Dershem | Jan 2006 | A1 |
| 20060063014 | Forray | Mar 2006 | A1 |
| 20060069232 | Dershem | Mar 2006 | A1 |
| 20060116476 | Cheng | Jun 2006 | A1 |
| 20060142517 | Dershem | Jun 2006 | A1 |
| 20060148930 | Blanchard et al. | Jul 2006 | A1 |
| 20060183846 | Pfenninger et al. | Aug 2006 | A1 |
| 20070155869 | Dershem et al. | Jul 2007 | A1 |
| 20070205399 | Mizori | Sep 2007 | A1 |
| 20070299154 | Dershem et al. | Dec 2007 | A1 |
| 20080017308 | Dershem et al. | Jan 2008 | A1 |
| 20080075961 | Mizori | Mar 2008 | A1 |
| 20080075963 | Dershem | Mar 2008 | A1 |
| 20080075965 | Dershem | Mar 2008 | A1 |
| 20080103240 | Dershem | May 2008 | A1 |
| 20080142158 | Dershem | Jun 2008 | A1 |
| 20080146738 | Dershem | Jun 2008 | A1 |
| 20080160315 | Forray et al. | Jul 2008 | A1 |
| 20080191173 | Dershem et al. | Aug 2008 | A1 |
| 20080210375 | Dershem et al. | Sep 2008 | A1 |
| 20080251935 | Dershem | Oct 2008 | A1 |
| 20080257493 | Dershem | Oct 2008 | A1 |
| 20080262191 | Mizori | Oct 2008 | A1 |
| 20090061244 | Dershem | Mar 2009 | A1 |
| 20090215940 | Dershem | Aug 2009 | A1 |
| 20090288768 | Dershem | Nov 2009 | A1 |
| 20100041803 | Dershem | Feb 2010 | A1 |
| 20100041823 | Dershem | Feb 2010 | A1 |
| 20100041832 | Dershem | Feb 2010 | A1 |
| 20100041845 | Dershem et al. | Feb 2010 | A1 |
| 20100056671 | Dershem | Mar 2010 | A1 |
| 20100063184 | Dershem | Mar 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| 0393713 | Jun 1994 | EP |
| 1156036 | Nov 2001 | EP |
| WO03080720 | Oct 2003 | WO |
| WO 2004099331 | Nov 2004 | WO |
| WO-2005121190 | Dec 2005 | WO |
| WO-2007100329 | Sep 2007 | WO |
| WO-2008077141 | Jun 2008 | WO |
| WO-2008124797 | Oct 2008 | WO |
| WO-2008130894 | Oct 2008 | WO |
| WO-2010019832 | Feb 2010 | WO |
| Entry |
|---|
| Meyer, Raymond W. Handbook of Molding Compounds and Molding Technology. 1987. Kluwer, p. 83. |
| Adamson, “Review of CSP and Flip Chip Underfill Processes and When to Use the Right Dispensing Tools for Efficient Manufacturing”, Paper Presented at GlobalTRONICS Technology Conference,Singapore 2002, 1-6. |
| Andersson et al., “Initiator-Free Photopolymerization of an Aliphatic Vinyl Ether-Maleimide Monomer”, J Coatings Tech 69: 1997, 91-95. |
| Grenier-Loustalot et al., “Monofunctional maleimide or acetylene tennlnated model compounds-I. Molten state homopolymerization reactivity and kinetics”, European Polymer Journal 34: 1998 , 1705-1714. |
| Kohli et al., “Co-Polymerization of Maleimides and Vinyl Ethers: A Structural Study”, Macromolecules 31: 1998, 5681-5689. |
| Yamazaki et al., “Effect of N-substrtuents on polymerization reactivity of N-alkylitaconimides in radical polymerization”, European Polymer Journal 33: 1997, 157-162. |
| Number | Date | Country | |
|---|---|---|---|
| 20080075963 A1 | Mar 2008 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60799078 | May 2006 | US |