Modifier for paving asphalt

Abstract

A modifier for paving asphalt, which comprises Trinidad Epure having a maximum size of less than 25 mm and a pulverulent solid having a maximum size of less than 2.5 mm, the powder comprising essentially a substance having a higher softening point than Trinidad Epure and compatibility with paving petroleum asphalt, wherein the volume of the powdery solid is 0.8 to 2.8 times the void volume of the granulated Trinidad Epure when in the stored state.

Description

BACKGROUND OF THE INVENTION

(1) Field of the Invention

The present invention relates to a modifier for modifying paving asphalt and a paving asphalt composition. More particularly, the present invention relates to an asphalt modifier which can easily be handled at the step of mixing the modifier into asphalt and will exert a highly improved modifying effect. The invention also relates to a paving asphalt composition containing this modifier.

(2) Description of the Prior Art

As one conventional method for preparing a paving asphalt composition having an improved flow resistance, there can be mentioned a method in which 100 parts of paving petroleum asphalt having a low softening point (about 50.degree. C.) is mixed with 25 to 100 parts of Trinidad Epure having a higher softening point (about 90.degree. to about 100.degree. C.), whereby deformation of an asphalt-paved road, which is readily caused at a high temperature, for example, in summer, is prevented. By the term "Trinidad Epure used herein, is meant a product obtained by purifying Trinidad lake asphalt, a kind of natural asphalt, which comprises 53 to 55% by weight of hard natural bitumen, 36 to 37% by weight of mineral substances, and 9 to 10% by weight of other substances.

In the method presently used with Trinidad Epure as a modifier for modifying paving asphalt, there can be mentioned a method in which Trinidad Epure is liquefied and is then added to asphalt and a method in which Trinidad Epure is added in the solid state.

When Trinidad Epure is used in the liquefied state, Trinidad Epure taken out from a storage vessel is roughly broken and heated and melted in a kettle equipped with a stirrer. Then the melted Trinidad Epure is mixed with paving petroleum asphalt after increasing the flowability of the melt by incorporation of an appropriate amount of paving petroleum asphalt, or the melt and paving petroleum asphalt are independently charged into a mixer for preparing the asphalt composition.

However, this method is defective in that long periods and a great deal of labor are necessary for pulverizing, heating and melting Trinidad Epure, and because mineral substances contained in Trinidad Epure are precipitated at the melting step, special care should be taken so as to prevent precipitation of these mineral substances at the melting and stirring step. Furthermore, areas where Trinidad Epure can be used is restricted.

A method for using Trinidad Epure in the solid state has been adopted in Germany. According to this method, Trinidad Epure stored in the pulverized state is directly charged into a mixer for preparing an asphalt composition, or is added into a mastic-preparing cooker of a lorry equipped with a stirrer. This method is economically advantageous over methods using Trinidad Epure in the liquefied state because the time is shortened and labor is saved.

When pulverized Trinidad Epure is used in the solid state, it readily undergoes re-caking during storage, and it is necessary to prevent this re-caking. Conventional pulverized Trinidad Epure, which has been subjected to re-caking-preventing treatment, include Trinidad Pulver and Trinidad Epuree Z. The former product comprises 50% by weight of finely divided Trinidad Epure and 50% by weight of paving stone powder, and the latter product comprises Trinidad Epure pulverized to a size of 12 to 0 mm and 3% by weight of diatomaceous earth, which is packed in a plastic bag.

In the case of trinidad Pulver, the bitumen content is as low as about 27% by weight, and transportation of Trinidad Pulver as the modifying bitumen is economically disadvantageous because stone powder should be transported. Furthermore, re-caking is caused at a high temperature according to the size of granulated Trinidad Epure. In case of Trinidad Epure Z, the bitumen content is satisfactorily high. However the content of diatomaceous earth is low, and if the absolute amount of diatomaceous earth is insufficient, and the average temperature is considerably higher than the method used in Germany, re-caking occurs and handling is difficult. Moreover, long-time storage is impossible. Therefore, both Trinidad Pulver or Trinidad Epure Z are insufficient as asphalt modifiers.

SUMMARY OF THE INVENTION

It is a primary object of the present invention to provide a modifier for paving asphalt in which the above-mentioned defects of the conventional techniques are eliminated.

Another object of the present invention is to provide a paving asphalt composition comprising an improved modifier, which gives a pavement having improved properties.

Still another object of the present invention is to provide a paved road comprising a paving asphalt composition including an improved modifier.

These and other objects of the present invention can be attained by a modifier comprising granulated Trinidad Epure having a predetermined size and a predetermined volume of a specific re-caking-preventing agent, in which re-caking is not in granulated Trinidad Epure even if stored over long periods, handling is very easy when the modifier is incorporated in paving asphalt and a high modifying effect on paving asphalt can be attained. More specifically, in accordance with the present invention, there is provided a modifier for paving asphalt, which comprises granulated Trinidad Epure having a maximum size of less than 25 mm, and as a re-caking-preventing agent a pulverant solid having a maximum size of less than about 2.5 mm, said solid being composed mainly of a substance having a higher softening point than the Trinidad Epure compatibility with paving petroleum asphalt, wherein the volume of the powdery solid is 0.8 to 2.8 times the void volume of the granulated Trinidad Epure when in the stored state.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention will now be described in detail.

In the present invention, the maximum size of granulated Trinidad Epure is controlled to be less than 25 mm. The reason is that as the size of the granule is increased, the separation phenomenon becomes conspicuous and homogeneity is not ensured in a granule having a maximum size larger than 25 mm. Further the practical operation of charging and mixing in a mixer becomes difficult if the maximum size is larger than 25 mm. In order to shorten the mixing time in the mixer, it is preferred that the maximum size of granulated Trinidad Epure be reduced to, for example, 12.5 mm or 5 mm so as to increase the melting speed of granulated Trinidad Epure. Examples of the particulate size distribution and properties of granulated Trinidad Epure are shown in Table 1.

TABLE 1__________________________________________________________________________ UnitSize Sieve (mm) Passing Ratio (%) Specific Volume Weight Void Ratio (%)(mm) 25 mm 13 mm 5 mm 2.5 mm 0.6 mm 0.3 mm 0.15 mm 0.074 mm Gravity (.gamma.1) (.gamma.2) [(.gamma.1-2)/1]__________________________________________________________________________25/0 100 58 25 10 3 2 1 0.3 1.41 0.90 36.2 5/0 100 52 12 8 4 1 1.41 0.75 46.8__________________________________________________________________________

The re-caking-preventing agent incorporated into the above-mentioned granulated Trinidad Epure will now be described.

Re-caking of granulated Trinidad Epure is caused by mutual interaction and contact of Trinida Epure particles. Accordingly, re-caking can be prevented if the re-caking-preventing agent particles are located among the particles of granulated Trinidad Epure so as to prevent mutual contact of the particles of granulated Trinidad Epure. Therefore, it is necessary that the particles of the re-caking-preventing agent should fill in the voids defined by the particles of granulated Trinidad Epure. In the present invention, in view of the foregoing, a re-caking-preventing agent that can be pulverized is used and the maximum size is controlled to be smaller than 2.5 mm. As the particle size is smaller, the unit volume weight is ordinarily reduced, and use of a re-caking-preventing agent having a smaller particle size is preferred. However, the operation of finely dividing the re-caking-preventing agent is costly and handling of finer particles becomes difficult.

When granulated Trinidad Epure is stored, it is ordinarily packed in bags which are stacked. In this case, the re-caking speed is influenced mainly by the temperature and the pressure imposed on the particles in the accumulated state. Namely, the higher the temperature and the larger the load, the more increased is the re-caking speed.

Accordingly, in the present invention, while the actual conditions for using granulated Trinidad Epure are taken into account, the temperature is set at 30.degree. C. corresponding to the ordinary highest temperature in summer in the United States or at 40.degree. C. corresponding to an abnormal temperature which may be experienced in the United States in summer. The pressure is set at a level produced when 10 of 25-Kg bags are stacked (in this case, the pressure applied to the bottom is about 0.1 Kg/cm.sup.2). In the present invention, it is prescribed that Trinidad Epure should be stored under these temperature and pressure conditions for at least 3 months.

It is considered that it is sufficient if the volume of the re-caking-preventing agent corresponds to the void volume of granulated Trinidad Epure in the accumulated state. However, this volume differs according to the application method for the pavement, the storing method, the storing period, the storing temperature and the transporting method. Accordingly, in the present invention, the volume of the re-caking-preventing agent is controlled to be 0.8 to 2.8 times the void volume of granulated Trinidad Epure in the stored state. In this case, the volume is converted to the weight by multiplying the volume by the unit volume weight of the re-caking-preventing agent.

The results of experiments conducted on the supposition of the foregoing conditions are shown in Table 2. The experimental procedures are as follows.

A sample is packed in a thickness of 7 cm in a cylinder having a diameter of 10 cm, and a pressure of 0.1 Kg/cm.sup.2, which corresponds to the weight observed when 10 of 25-Kg bags are piled on the sample, is applied to the sample. The sample is placed in a thermostat furnace maintained at 30.degree. or 40.degree. C. for 90 days. The sample is carefully taken out from the cylinder and is let fall from a height of 1 m. When the sample breaks into crumbles, it is judged that re-caking is prevented.

From the foregoing experimental results, it has been found that an asphaltite powder having a higher softening point than Trinidad Epure, such as a gilsonite powder, an asphalt pitch powder, a powder of a polymeric resin having a high softening point, such as an ethylene-vinyl acetate copolymer, an ethylene-ethyl acrylate copolymer or a polyolefin, a paving lime stone powder and a powder of a mineral substance such as cement, fly ash, slaked lime, kaolin or Aerosil are effective as the re-caking-preventing agent in the present invention, and that also mixtures of two or more of the foregoing substances are effective. In the case where a mineral substance alone is used, the effective content of bitumen in the total composition is reduced. Accordingly, it is preferred that such a mineral substance be used as an adjuvant together with other re-caking-preventing agent.

When asphaltite such as gilsonite, which is composed essentially of bitumen, is used as the re-caking-preventing agent, it not only acts as a re-caking-preventing agent but also enhances the effect of modifying paving petroleum asphalt and is utilized at a high efficiency as bitumen throughout the transportation, handling and use of the modifier. Accordingly, in this case, the economical advantage is increased.

The effects of modifying paving asphalt compositions by the modifier of the present invention including gilsonite are shown in Tables 3 and 4. Table 3 shows the results of the experiments made on hot rolled asphalt and Table 4 shows the results of the experiments made on Guss asphalt.

TABLE 2__________________________________________________________________________Amount of Re-Caking-Preventing Agent Necessary for AttainingRe-Caking-Preventing Effect 25-0 mm (void 5-0 mm (void ratio of 36.2%) ratio of 46.8%) Unit Volume (%) of Re-Caking Volume (%) of Re-CakingParticle size of Trinidad Epure Volume Preventing Agent Corre- Preventing Agent Corre-Kinds and Weight ratios of Specific Weight sponding to Void Ratio sponding to Void ratio ofGroup Re-Caking Preventing Agents Gravity (g/cm) 30.degree. C. 40.degree. C. 30.degree. C. 40.degree.__________________________________________________________________________ C.asphal- gilsonite (medium) 1.06 0.69 40 75 55 105titeasphal- gilsonite (fine) 1.06 0.56 30 65 45 90titeasphalt cracked asphalt pitch 1.26 0.86 50 100 70 125pitchpolymeric ethylene-vinyl acetate copolymer 0.95 0.37 40 80 55 100resin (EVA)polymeric ethylene ethyl acrylate copolymer 0.94 0.38 40 80 55 100resin (EEA)polymeric polyolefin 0.97 0.45 45 85 60 105resinpowdered lime stone powder 2.70 1.32 35 75 50 95mineral(adjuvant)powdered Portland cement 3.15 1.40 40 80 55 100mineral(adjuvant)powdered fly ash 2.12 0.98 35 70 50 95mineral(adjuvant)powdered slaked lime 2.33 0.65 30 60 40 85mineral(adjuvant)powdered kaolin 2.50 0.75 35 75 50 95mineral(adjuvant)powdered aerosil -- 0.06 30 60 40 80mineral(adjuvant)mixture gilsonite (fine)/cracked asphalt 1.16 0.66 45 90 60 110 pitch (1/1)" gilsonite (fine)/EEA (2/1) 1.02 0.59 40 75 55 95" cracked asphalt pitch/EEA (2/1) 1.15 0.57 50 95 65 120" gilsonite (fine)/lime stone powder (2/1) 1.60 0.67 40 70 50 95" cracked asphalt pitch/lime 1.75 0.88 50 95 60 115 stone powder (2/1)" EEA/lime stone powder (2/1) 1.53 0.54 40 80 50 100" gilsonite (fine)/cracked asphalt pitch/ 1.67 0.78 45 85 55 105 lime stone powder (1/1/1)" gilsonite (fine)/EEA/lime stone powder 1.57 0.71 40 75 50 95(1/1/1)" cracked asphalt pitch/EEA/lime 1.63 0.68 45 90 60 115stone powder (1/1/1)__________________________________________________________________________ TABLE 3__________________________________________________________________________Results of Experiments made on Hot Rolled Asphalt Conventional Present Present Unit Technique Invention Invention__________________________________________________________________________Componentscrushed stone No. 5 % by weight 20 20 20crushed stone No. 6 % by weight 20 20 20coarse sand % by weight 28 28 28fine sand % by weight 19 19 19lime stone powder % by weight 4.7 5.0 5.3binder % by weight 8.3 8.0 7.7ingredients of binder80-100 asphalt % by weight 70 75 80Trinidad Epure 25-0 % by weight 30 18 12gilsonite (fine) % by weight -- 5 8bitumen content in composition % by weight 7.2 7.2 7.2Test ItemsMarshall test (60.degree. C.)stability Kg 920 990 1070flow 1/100 cm 35 34 34wheel tracking test (dynamic stability)(tip embedded turns/mm 700 1150 1430sample)(60.degree. C., 64 Kg/cm.sup.2)__________________________________________________________________________ TABLE 4__________________________________________________________________________Results of Experiments Made on Guss Asphalt Conventional Present Conventional Present Unit Technique Invention Technique Invention__________________________________________________________________________Componentscrushed stone No. 6 % by weight 23.1 23.1 23.1 23.1crushed stone No. 7 % by weight 21.3 21.3 21.3 21.3coarse sand % by weight 13.0 13.0 13.0 13.0fine sand % by weight 13.9 13.9 13.9 13.9lime stone powder % by weight 20.3 20.8 19.6 20.4binder % by weight 8.4 7.9 9.1 8.3ingredients of binder20-40 asphalt % by weight 75 82 -- --60-80 asphalt % by weight -- -- 60 70Trinidad Epure % by weight 25 12 40 23gilsonite (fine) % by weight -- 6 -- 7bitumen content in composition % by weight 7.5 7.5 7.5 7.5Test Itemspenetration of bitumen (25.degree. C.) 1/10 mm 21 22 29 32softening point of bitumen (R & B) .degree.C. 64 66 58 59intrusion test (40.degree. C., 30 minutes) mm 1.5 1.3 1.9 1.4wheel tracking test (dynamic stability)(60.degree. C., 64 turns/mmp.2) 570 1050 450 790__________________________________________________________________________

As may be seen from the foregoing experimental results, when a modifier formed by incorporating gilsonite into Trinidad Epure is used, the quality of a paving asphalt composition is drastically improved over the quality attained when Trinidad Epure alone is used.

It is expected that a similar effect will be attained when an asphalt pitch composed of bitumen, which has a high softening point, is used as the re-caking-preventing agent.

It is known that a polymeric resin having a high softening point, such as an ethylene-vinyl acetate copolymer, an ethylene-ethyl acrylate copolymer or a polyolefin can be used as a modifier for paving petroleum asphalt. If this polymeric resin is used as an additional re-caking-preventing agent for Trinidad Epure, the modifying effect is further enhanced.

When an asphaltite solid or polymeric resin solid is used as the re-caking-preventing agent, according to the type of paving petroleum asphalt or the type and use of the paving asphalt composition, the amount of the re-caking-preventing agent necessary only for obtaining the intended modifying effect may be smaller than the amount necessary for obtaining the intended re-caking-preventing effect in Table 2. In this case, since a re-caking occurs a mineral substance such as mentioned above, may be added as the adjuvant for compensating the insufficient re-caking-preventing effect while reducing the amount of the asphalt or polymeric resin. However, in this case, it is necessary that the amount of the adjuvant should be up to 45% by weight based on the total re-caking-preventing agent. If the amount of the adjuvant is controlled within this range, the sum of the entire bitumen content and the modifier is maintained at a level higher than the bitumen content (53 to 55% by weight) of Trinidad Epure as the starting material, and no economical disadvantage is brought about.

As is apparent from the foregoing illustration, according to the present invention, re-caking of Trinidad Epure can be sufficiently prevented in the actual application, and handling of granulated Trinidad Epure can be facilitated and the effect of modifying paving asphalt can be enhanced. Therefore, a very excellent modifier for paving asphalt can be provided according to the present invention.

Furthermore, the present invention provides an improved paving asphalt composition comprising the above-mentioned modifier. Namely, according to the present invention, as shown in Tables 3 and 4, the above-mentioned modifier is used instead of Trinidad Epure in a known paving apshalt composition such as hot rolled asphalt comprising inorganic paving materials such as about 30 to about 55% by weight of crushed stone (for example, crushed stone No. 5, 6 or 7), about 20 to about 60% by weight of sand and about 5 to about 30% by weight of lime stone powder, and about 6 to about 10% by weight of asphalt type binders and other necessary ingredients, or Guss asphalt having a similar composition. As is shown in Tables 3 and 4, the paving asphalt composition of the present invention is characterized in that the above-mentioned modifier is present in an amount of about 25 to about 100 parts by weight per 100 parts by weight of straight asphalt in the binder of the asphalt composition. As is apparent from the data shown in tables 3 and 4, this paving asphalt composition of the present invention has an improved quality.

Moreover, the present invention provides a road paved with the above-mentioned paving asphalt composition. This paved road can be provided by carrying out the paving operation by using the paving asphalt composition of the present invention according to known paving methods, and the paved road has excellent properties as described above.

Claims

1. A modifier for paving asphalt, which consists essentially of a mixture of granulated Trinidad Epure having a maximum size of less than 25 mm, and a pulverulent solid for preventing recaking of said granulated Trinidad Epure during storage thereof, said pulverulent solid having a maximum size of less than 2.5 mm, a higher softening point than said granulated Trinidad Epure and compatibility with paving petroleum asphalt, wherein the volume of said pulverulent solid is 0.8 to 2.8 times the void volume of the granulated Trinidad Epure when in the stored state, and further wherein said pulverulent solid is selected from one or more members of the group consisting of asphaltite powder, asphalt pitch powder, polymeric resin powder, paving limestone powder, and mineral powder.

2. A modifier for paving asphalt according to claim 1, wherein the pulverulent solid is an asphaltite having a higher softening point than Trinidad Epure.

3. A modifier for paving asphalt according to claim 1, wherein the pulverulent solid is a solid of asphalt pitch having a higher softening point than Trinidad Epure.

4. A modifier for paving asphalt according to claim 1, wherein the pulverulent solid is a solid of a polymeric resin having a higher softening point than Trinidad Epure.

5. A modifier for paving asphalt according to claim 1, wherein the pulverulent solid is a mixture comprising at least two members selected from the group consisting of asphaltite having a higher softening point than Trinidad Epure, asphalt pitch having a higher softening point than Trinidad Epure, and a polymeric resin having a higher softening point than Trinidad Epure.

6. A modifier for paving asphalt according to claim 1 wherein the pulverulent solid comprises as a main component, an asphaltite having a higher softening point than Trinidad Epure, an asphalt pitch having a higher softening point than Trinidad Epure, a polymeric resin having a higher softening point than Trinidad Epure or a mixture of two or more of said solids and as an adjuvant, a powder of a mineral substance.

7. A paving asphalt composition comprising an inorganic paving filler material and an asphaltic binder, said binder comprising 100 parts by weight of paving petroleum asphalt to 25 to 100 parts by weight of an asphalt modifier, said modifier consisting essentially of a mixture of granulated Trinidad Epure having a maximum size of less than 25 mm and a pulverulent solid for preventing recaking of said granulated Trinidad Epure during storage thereof, said pulverulent solid having a maximum size of less than 2.5 mm, a higher softening point than Trinidad Epure and compatibility with paving petroleum asphalt, wherein the volume of said pulverulent solid is 0.8 to 2.8 times the void volume of the granulated Trinidad Epure when in the stored state, and further wherein said pulverulent solid is selected from one or more members of the group consisting of asphaltite powder, asphalt pitch powder, polymeric resin powder, paving limestone powder, and mineral powder.

8. A paving asphalt composition according to claim 7, wherein the solid is an asphaltite having a higher softening point than Trinidad Epure.

9. A paving asphalt composition according to claim 7, wherein the solid is an asphalt pitch having a higher softening point than Trinidad Epure.

10. A paving asphalt composition according to claim 7, wherein the solid is a polymeric resin, having a higher softening point than Trinidad Epure.

11. A paving asphalt composition according to claim 7, wherein the solid is a mixture comprising at least two members selected from the group consisting of an asphaltite having a higher softening point than Trinidad Epure, an asphalt pitch having a higher softening point than Trinidad Epure, and a polymeric resin having a higher softening point than Trinidad Epure.

12. A paving asphalt composition according to claim 7, wherein the pulverulent solid comprises as a main component, an asphaltite which has a higher softening point than Trinidad Epure, an asphalt pitch which has a higher softening point than Trinidad Epure, a polymeric resin which has a higher softening point than Trinidad Epure, or a mixture of two or more of said solids, and as an adjuvant, a powder of a mineral substance.

13. A paved road material which is paved with a paving asphalt composition comprising an inorganic paving filler material and an asphaltic binder comprising 100 parts by weight of paving petroleum asphalt to 25 to 100 parts by weight of an asphalt modifier, said modifier consisting essentially of a mixture of granulated Trinidad Epure having a maximum size of less than 25 mm and a pulverulent solid for preventing recaking of said granulated Trinidad Epure during storage thereof, said pulverulent solid having a maximum size of less than 2.5 mm, a higher softening point than Trinidad Epure and compatibility with paving petroleum asphalt, wherein the volume of said pulverulent solid is 0.8 to 2.8 times the void volume of the granulated Trinidad Epure when in the stored state, and further wherein said pulverulent solid is selected from one or more members of the group consisting of asphaltite powder, asphalt pitch powder, polymeric resin powder, paving limestone powder, and mineral powder.

14. A method of preventing recaking in granulated Trinidad Epure in the stored state by adding to said Trinidad Epure the pulverulent solid of claim 1.