Molded article and method for producing molded article

Information

  • Patent Grant
  • 10961285
  • Patent Number
    10,961,285
  • Date Filed
    Thursday, September 8, 2016
    8 years ago
  • Date Issued
    Tuesday, March 30, 2021
    3 years ago
Abstract
Provided is a molded article of a composition comprising a polypeptide, wherein the polypeptide is at least one kind selected from the group consisting of natural spider silk protein and polypeptides derived from natural spider silk protein.
Description
SEQUENCE LISTING SUBMISSION VIA EFS-WEB

A computer readable text file, entitled “SequenceListing.txt” created on or about Jul. 22, 2019 with a file size of about 35 kb contains the sequence listing for this application and is hereby incorporated by reference in its entirety.


TECHNICAL FIELD

The present invention relates to a molded article and a method for producing a molded article.


BACKGROUND ART

For the purpose of weight reduction, cost reduction, the facilitation of forming, and the like, attempts for substituting metallic materials with organic materials are underway. As the above-described organic materials, phenolic resins having a high resin hardness are often used, and a method of adding a phenolic resin fiber to a matrix resin containing a phenolic resin is known since the bending elastic modulus or the bending strength is further increased (for example, refer to Patent Literature 1). In addition, due to a rising demand for environmental protection, bioplastics which are petroleum free materials have been thus far drawing attention, and the fact that formed articles having 4.5 GPa of a bending elastic modulus can be obtained by resinifying silk powder is known (for example, refer to Non Patent Literature 1).


CITATION LIST
Patent Literature

[Patent Literature 1] JP 2014-80491 A


Non Patent Literature

[Non Patent Literature 1] Shinji HIRAI, Monthly Journal of Function & Materials, June 2014, “Keratin and Fibroin Resins For Environmental Friendly Materials Using Animal Proteins Derived from Industrial Wastes”


SUMMARY OF INVENTION
Technical Problem

However, materials as disclosed by Patent Literature 1 are materials that are caused to exhibit a reinforcement effect by adding a fiber thereto, and it is difficult to obtain a high strength with the matrix resin alone. In addition, it is not possible to obtain formed articles having a bending elastic modulus of more than 4.5 GPa from biodegradable materials.


Therefore, an object of the present invention is to provide a biodegradable formed article that exhibits an excellent bending elastic modulus without using any additive materials such as reinforced fibers and a production method therefore.


Solution to Problem

The present invention provides a molded article of a composition comprising a polypeptide, wherein the polypeptide is at least one kind selected from natural spider silk protein and polypeptides derived from natural spider silk protein.


The above-described formed article has characteristics of being biodegradable, including natural spider silk protein and/or a polypeptide derived from natural spider silk protein as a raw material, and additionally, being obtained by molding the raw material and, due to these characteristics, exhibits an extremely high bending elastic modulus (for example, more than 4.5 GPa) even without using any additive materials such as reinforced fibers. Furthermore, the formed article can also be imparted with transparency and thus, compared with resins having a high strength but lacking transparency such as phenolic resins or polyether ether ketone (PEEK), the formed article has an advantage of significantly broadening applicable uses. Additionally, spider silk protein can be genetically modified in diverse manners, and thus it is possible to easily optimize the performance depending on the final uses. Meanwhile, the bending elastic modulus is preferably 4.7 GPa or more, more preferably 5.0 GPa or more, and still more preferably 5.2 GPa or more. The upper limit of the bending elastic modulus is not limited, but can be set to, for example, 15.0 GPa or less. The bending elastic modulus can be set to 10.0 GPa or less and, furthermore, 7.0 GPa or less.


The molded article may be provided as a hot press-molded article. The molded article refers to an article or the like formed using a casting mold (mold), but articles having a superior bending elastic modulus can be produced by hot pressing procedure.


The molded article can be produced using a production method comprising a step of hot pressing a composition comprising at least one kind selected from the group consisting of natural spider silk protein and polypeptides derived from natural spider silk protein.


Advantageous Effects of Invention

According to the present invention, a biodegradable formed article exhibiting an excellent bending elastic modulus without using any additive materials such as reinforced fibers and a production method therefore are provided.





BRIEF DESCRIPTION OF DRAWINGS


FIG. 1 is a schematic cross-sectional view of a press molding machine.



FIG. 2 illustrates schematic cross-sectional views of the press molding machine (a) before the introduction of a composition, (b) immediately after the introduction of the composition, and (c) with the composition in a state of being hot pressed.



FIG. 3 is a photograph of a molded article of Example 1.





DESCRIPTION OF EMBODIMENTS

Hereinafter, a preferred embodiment of the present invention will be described. However, the present invention is not limited to the following embodiment by any means.


A molded article according to the embodiment is made of a composition comprising natural spider silk protein and/or a polypeptide derived from natural spider silk protein. The molded article can be obtained by introducing the above-described composition into a casting mold (mold) and carrying out forming or the like, and, in the forming step, heating and/or pressing is possible. The composition has, typically, a shape of a powder form (lyophilized powder or the like) or a fibrous shape (a fiber or the like obtained by spinning), and the molded article may be a fused article of a composition including natural spider silk protein and/or a polypeptide derived from natural spider silk protein which have the above-described shape.


Examples of the natural spider silk protein include a major dragline silk protein and a flagelliform silk protein.


The major dragline silk protein is produced from spider's major ampullate glands and has a characteristic of excellent toughness. Examples of the major dragline silk protein include major ampullate spidroin MaSp1 or MaSp2 derived from Nephila clavipes, ADF3 or ADF4 derived from Araneus diadematus, and the like.


The flagelliform silk protein is produced from spider's flagelliform glands, and examples of the flagelliform silk protein include flagelliform silk protein derived from Nephila clavipes.


Examples of the polypeptides derived from natural spider silk protein include recombinant spider silk protein, for example, mutants, analogues, derivatives, and the like of natural spider silk protein. The above-described polypeptide is particularly preferably the recombinant spider silk protein of the major dragline silk protein.


The molded article may be a molded article including only natural spider silk protein and/or a polypeptide derived from natural spider silk protein (hereinafter, in some cases, these will be collectively referred to as “spider silk polypeptide”) and also may be a molded article in which additive components (for example, a plasticizer, a coloring agent, a filler such as lamellar silicate or basic calcium phosphate, water, synthetic resins, and the like) are added to a spider silk polypeptide. In a case in which additive components of a plasticizer and the like are used, it is preferable to set the amount thereof to 50% by mass or less of the total amount of the spider silk polypeptides. In addition, foreign substances that are generated in a process of obtaining other protein, for example, silk fibroin, soybean protein, casein, keratin, collagen, or milk whey protein or polypeptides may also be included. Meanwhile, the molded article exhibits the effects of the present invention even in a case in which the above-described additive components are not added thereto.


The molded article comprising the spider silk polypeptide preferably has transparency. The transparency can be visually determined, but the molded article preferably has a transmittance of 50% or more in a case in which an optical transmittance measurement instrument is used and, for example, the cumulative time is set to 0.1 seconds in a wavelength range of 220 to 800 nm.


The molded article can be produced using a press molding machine. FIG. 1 is a schematic cross-sectional view of a press molding machine that can be used to produce the molded article. A press molding machine 10 illustrated in FIG. 1 includes a die 2 in which a through hole is formed and which can be heated and an upper side pin 4 and a lower side pin 6 which can be moved up and down in the through hole of the die 2. The molded article can be obtained by introducing the composition including the spider silk polypeptide into a cavity formed by inserting the upper side pin 4 or the lower side pin 6 into the die 2, and pressing the composition with the upper side pin 4 and the lower side pin 6 while heating the die 2.



FIG. 2 illustrates step views of obtaining the molded article and are schematic cross-sectional views of the press molding machine (a) before the introduction of the composition, (b) immediately after the introduction of the composition, and (c) with the composition in a state of being heated and pressed. As illustrated in FIG. 2(a), the composition is introduced into the through hole in a state in which only the lower side pin 6 is inserted into the through hole of the die 2, and, as illustrated in FIG. 2(b), the upper side pin 4 is inserted into the through hole of the die 2 and moved down, and the heating of the die 2 is initiated, thereby heating and pressing a composition 8a which is not yet heated and pressed in the through hole. The upper side pin 4 is moved down until a predetermined pressurization force is reached, and heating and pressing are continued until the composition reaches a predetermined temperature in a state illustrated by FIG. 2(c), thereby obtaining a composition 8b which has been hot pressed. After that, the temperature of the die 2 is lowered using a cooler (for example, a spot cooler), the upper side pin 4 or the lower side pin 6 is removed from the die 2 when the composition 8b reaches a predetermined temperature, and the resulting content is taken out, thereby obtaining a molded article. The pressing may be carried out by moving down the upper side pin 4 in a state in which the lower side pin 6 is fixed, but it is also possible to move down the upper side pin 4 and move up the lower side pin 6 at the same time.


The heating is preferably carried out at 80° C. to 300° C., more preferably carried out at 100° C. to 180° C., and still more preferably carried out at 100° C. to 130° C. The pressing is preferably carried out at 5 kN or more, more preferably carried out at 10 kN or more, and still more preferably carried out at 20 kN or more. In addition, the time during which the treatment is continued under predetermined hot pressing conditions after the conditions are satisfied (temperature retention condition) is preferably 0 to 100 minutes, more preferably 1 to 50 minutes, and still more preferably 5 to 30 minutes.


The molded article of the composition comprising a spider silk polypeptide is preferably produced using the polypeptide derived from natural spider silk protein, and thus the production method will be described below in detail.


Examples of the polypeptide derived from the major dragline silk protein which serves as a raw material of the molded article of the composition including a spider silk polypeptide include polypeptides including two or more, preferably including five or more, and more preferably including 10 or more units of an amino-acid sequence represented by Formula 1: REP1-REP2 (1). Alternatively, the polypeptide derived from the major dragline silk protein may be a polypeptide which includes a unit of the amino-acid sequence represented by Formula 1: REP1-REP2 (1) and in which a C terminal sequence is an amino-acid sequence represented by any of SEQ ID Nos. 1 to 3 or an amino-acid sequence having 90% or more homology with the amino-acid sequence represented by any of SEQ ID Nos. 1 to 3. Meanwhile, in the polypeptide derived from the major dragline silk protein, the units of the amino-acid sequence represented by Formula 1: REP1-REP2 (1) may be identical to or different from each other. In a case in which the production of recombinant protein c is carried out using a microbe such as Escherichia coli as a host, the molecular weight of the polypeptide derived from the major dragline silk protein is preferably 500 kDa or less, more preferably 300 kDa or less, and still more preferably 200 kDa or less from the viewpoint of productivity.


In Formula 1, REP1 represents polyalanine. In REP1, alanines that are continuously arranged are preferably two or more residues, more preferably three or more residues, still more preferably four or more residues, and particularly preferably five or more residues. In addition, in REP1, alanines that are continuously arranged are preferably 20 or less residues, more preferably 16 or less residues, still more preferably 12 or less residues, and particularly preferably 10 or less residues. In Formula 1, REP2 is an amino-acid sequence made of 10 to 200 residues of amino acid, and the total residue number of glycine, serine, glutamine, and alanine in the amino-acid sequence is 40% or more, preferably 60% or more, and more preferably 70% or more of the total number of amino acid residues.


In the major dragline silk protein, REP1 corresponds to a crystalline region that forms a crystalline β sheet in the fiber, and REP2 corresponds to an amorphous region which is more flexible and lacks a regular structure in a majority area in the fiber. In addition, [REP1-REP2] corresponds to a repetitive region made up of crystalline regions and amorphous regions (repetitive sequence) and is the characteristic sequence of dragline silk protein.


An amino-acid sequence represented by SEQ ID No. 1 is the same as an amino-acid sequence made of 50 residues of amino acid at the C terminal of an amino-acid sequence of ADF3 (NCBI accession number: AAC47010, GI: 1263287), and an amino-acid sequence represented by SEQ ID No. 2 is the same as an amino-acid sequence obtained by removing 20 residues from the C terminal of the amino-acid sequence represented by SEQ ID No. 1, and an amino-acid sequence represented by SEQ ID No. 3 is the same as an amino-acid sequence obtained by removing 29 residues from the C terminal of the amino-acid sequence represented by SEQ ID No. 1.


As the polypeptide including two or more units of the amino-acid sequence represented by Formula 1: REP1-REP2 (1), it is possible to use, for example, a polypeptide made of an amino-acid sequence represented by SEQ ID No. 7. The polypeptide made of the amino-acid sequence represented by SEQ ID No. 7 is an amino-acid sequence of ADF3 (NCBI accession number: AAC47010, GI: 1263287) having an amino-acid sequence (SEQ ID No. 4) made up of an initiation codon, a His10 tag, and a Human rhinovirus 3C protease (HRV3C protease) recognition site added to an N terminal which is mutated so that translation ends at the 543rd amino acid residue.


In addition, as the polypeptide including two or more units of the amino-acid sequence represented by Formula 1: REP1-REP2 (1), it is possible to use a protein which is made of the amino-acid sequence represented by SEQ ID No. 7 in which one or a plurality of amino acids is substituted, deleted, inserted, and/or added, and has a repetitive region made up of crystalline regions and amorphous regions. In the present invention, “one or a plurality” means, for example, 1 to 40, 1 to 35, 1 to 30, 1 to 25, 1 to 20, 1 to 15, 1 to 10, or 1 or several. In addition, in the present invention, “one or several” means 1 to 9, 1 to 8, 1 to 7, 1 to 6, 1 to 5, 1 to 4, 1 to 3, 1 or 2, or 1.


In addition, examples of the polypeptide including two or more units of the amino-acid sequence represented by Formula 1: REP1-REP2 (1) include ADF4-derived recombinant protein having an amino-acid sequence represented by SEQ ID No. 8. The amino-acid sequence represented by SEQ ID No. 8 is an amino-acid sequence obtained by adding the amino-acid sequence (SEQ ID No. 4) made up of an initiation codon, a His10 tag, and a Human rhinovirus 3C protease (HRV3C protease) recognition site to an N terminal of a partial amino-acid sequence of ADF4 (NCBI accession number: AAC47011, GI: 1263289) procured from NCBI database. In addition, as the polypeptide including two or more units of the amino-acid sequence represented by Formula 1: REP1-REP2 (1), a polypeptide which is made of the amino-acid sequence represented by SEQ ID No. 8 in which one or a plurality of amino acids is substituted, deleted, inserted, and/or added, and has a repetitive region made up of crystalline regions and amorphous regions may be used. In addition, examples of the polypeptide including two or more units of the amino-acid sequence represented by Formula 1: REP1-REP2 (1) include MaSp2-derived recombinant protein having an amino-acid sequence represented by SEQ ID No. 9. The amino-acid sequence represented by SEQ ID No. 9 is an amino-acid sequence obtained by adding an amino-acid sequence made up of an initiation codon, a His10 tag, and a Human rhinovirus 3C protease (HRV3C protease) recognition site to an N terminal of a partial amino-acid sequence of MaSp2 (NCBI accession number: AAT75313, GI: 50363147) procured from NCBI database. In addition, as the polypeptide including two or more units of the amino-acid sequence represented by Formula 1: REP1-REP2 (1), a polypeptide which is made of the amino-acid sequence represented by SEQ ID No. 9 in which one or a plurality of amino acids is substituted, deleted, inserted, and/or added, and has a repetitive region made up of crystalline regions and amorphous regions may also be used.


Examples of the polypeptides derived from the flagelliform silk protein include polypeptides including 10 or more, preferably including 20 or more, and more preferably including 30 or more units of an amino-acid sequence represented by Formula 2: REP3 (2). In a case in which the production of recombinant protein is carried out using a microbe such as Escherichia coli as a host, the molecular weight of the polypeptide derived from the flagelliform silk protein is preferably 500 kDa or less, more preferably 300 kDa or less, and still more preferably 200 kDa or less from the viewpoint of productivity.


In Formula (2), REP3 refers to an amino-acid sequence constituted of Gly-Pro-Gly-Gly-X (SEQ ID No. 12), and X refers to one amino acid selected from the group consisting of Ala, Ser, Tyr, and Val.


In spider silk, flagelliform silk has a significant characteristic of having a repetitive region which does not have any crystalline regions and is made of an amorphous region. Major dragline silk and the like have a repetitive region made up of crystalline regions and amorphous regions and are thus assumed to have both a high stress and a favorable stretching property. On the other hand, flagelliform silk has a stress that is poorer than that of major dragline silk, but has a favorable stretching property. This is considered to be due to the fact that a majority of flagelliform silk is constituted of an amorphous region.


Examples of the polypeptide including 10 or more units of the amino-acid sequence represented by Formula 2: REP3 (2) include flagelliform silk protein-derived recombinant protein having an amino-acid sequence represented by SEQ ID No. 10. The amino-acid sequence represented by SEQ ID No. 10 is an amino-acid sequence obtained by combining an amino-acid sequence of the 1220th residue through the 1659th residue from an N terminal that corresponds to a repeat portion and a motif of a partial sequence of a flagelliform silk protein of Nephila clavipes (NCBI accession number: AAF36090, GI: 7106224) procured from NCBI database (referred to as the PR1 sequence) and a C terminal amino-acid sequence of the 816th residue through the 907th residue from a C terminal of a partial sequence of a flagelliform silk protein of Nephila clavipes (NCBI accession number: AAC38847, GI: 2833649) procured from NCBI database and adding the amino-acid sequence (SEQ ID No. 4) made up of an initiation codon, a His10 tag, and an HRV3C protease recognition site to an N terminal of the combined sequence. In addition, as the polypeptide including 10 or more units of the amino-acid sequence represented by Formula 2: REP3 (2), a polypeptide which is made of the amino-acid sequence represented by SEQ ID No. 10 in which one or a plurality of amino acids is substituted, deleted, inserted, and/or added, and has a repetitive region made of an amorphous region may also be used.


The polypeptide can be produced using a host that is transformed by an expression vector containing a gene that codes the polypeptide. A method for producing the gene is not particularly limited, and the gene is produced by amplifying a gene that codes natural spider silk protein from a spider-derived cell by means of a polymerase chain reaction (PCR) or the like and cloning the gene or is chemically synthesized. A method for chemically synthesizing the gene is not particularly limited, and, for example, the gene can be synthesized by linking oligonucleotides that are automatically synthesized with AKTAoligopilot plus 10/100 (manufactured by GE Healthcare Company Japan) or the like by means of PCR on the basis of the amino-acid sequence information of natural spider silk protein procured from the web database of NCBI or the like. At this time, in order to facilitate the refining or confirmation of protein, a gene that codes a protein made of an amino-acid sequence obtained by adding an amino-acid sequence made up of an initiation codon and a His10 tag to an N terminal of the amino-acid sequence may be synthesized.


As the expression vector, it is possible to use a plasmid, a phage, a virus, or the like which is capable of expressing proteins from DNA sequences. The plasmid-type expression vector is not particularly limited as long as the expression vector is capable of expressing the target gene in host cells and is self-amplifiable. For example, in a case in which Escherichia coli Rosetta (DE3) is used as a host, it is possible to use a pET22b(+) plasmid vector, a pCold plasmid vector, or the like. Among these, from the viewpoint of the productivity of protein, the pET22b(+) plasmid vector is preferably used. As the host, it is possible to use, for example, an animal cell, a plant cell, a microbe, or the like.


The polypeptide that is used in the present invention is preferably a polypeptide derived from ADF3 which is one of the two important dragline silk proteins of Araneus diadematus. This polypeptide, basically, has a high strength-elongation degree and a high toughness and also has an advantage of ease of synthesis.


EXAMPLES

Hereinafter, the present invention will be described in more detail using examples, but the present invention is not limited to these examples within the scope of the technical concept of the present invention.


<Gene Synthesis>


(1) Synthesis of Gene of ADF3Kai


A partial amino-acid sequence of ADF3 which is one of the two important dragline silk proteins of Araneus diadematus (NCBI accession number: AAC47010, GI: 1263287) was acquired from the web database of NCBI, and the synthesis of a gene that codes an amino-acid sequence (SEQ ID No. 5) obtained by adding (SEQ ID No. 4) made up of an initiation codon, a His10 tag, and a Human rhinovirus 3C protease (HRV3C protease) recognition site to an N terminal of the same sequence was entrusted to GenScript Japan Inc. As a result, a pUC57 vector (having an NdeI site at right upstream region of a 5′ terminal of the gene and an Xba I site at right downstream region of the 5′ terminal) into which a gene of ADF3Kai made of a base sequence represented by SEQ ID No. 6 was introduced was acquired. Then, a restriction enzyme treatment was carried out on the same gene using Nde I and EcoR I, and the gene was recombined to a pET22b(+) expression vector.


(2) Synthesis of Gene of ADF3Kai-noNR


The above-obtained pET22b(+) expression vector into which the gene of ADF3Kai was used as a template, and a codon GTG corresponding to the 543rd amino acid residue valine (Val) in the amino-acid sequence (SEQ ID No. 5) of ADF3Kai was mutated to a termination codon TAA by means of site-directed mutagenesis using PrimeStar MutagenesisBasal Kit (manufactured by Takara Bio Inc.), thereby constructing a gene of ADF3Kai-noNR represented by SEQ ID No. 11 on pET22b(+). The accuracy of the mutagenesis was confirmed from a sequence reaction for which 3130×1 Genetic Analyzer (Applied Biosystems) was used. Meanwhile, the amino-acid sequence of ADF3Kai-noNR is as indicated by SEQ ID No. 7.


<Expression of Protein>


The pET22b(+) expression vector including a gene sequence of the above-obtained ADF3Kai-noNR was transformed to Escherichia coli Rosetta (DE3). The obtained single colony was cultured for 15 hours in a 2 mL LB culture medium including ampicillin, 1.4 mL of the resulting culture liquid was added to a 140 mL LB culture medium including ampicillin, and the culture liquid was cultured under conditions of 37° C. and 200 rpm until OD600 of the culture liquid reached 3.5. Next, the culture liquid having OD600 of 3.5 was added to a 7 L 2xYT culture medium including ampicillin together with 140 mL of 50% glucose and was further cultured until OD600 reached 4.0. Then, isopropyl-β-thiogalactopyranoside (IPTG) was added to the obtained culture liquid having OD600 of 4.0 so that the final concentration reached 0.5 mM, thereby inducing protein expression. After two hours elapsed from the addition of IPTG, the culture liquid was centrifugally separated, and a bacterial body was collected. As a result of electrophoresing protein solutions prepared from the culture liquid before that addition of IPTG and after the addition of IPTG in polyacrylamide gels, bands having a target size were observed depending on the addition of IPTG, and it was confirmed that target protein was expressed. Escherichia coli that expressed the protein of ADF3Kai-noNR was stored in a freezer (−20° C.).


<Polypeptide Preparation Example>


(I) Approximately 4.5 g of the bacterial body of Escherichia coli that expressed the protein of ADF3Kai-noNR and 30 ml of a buffer solution AI (20 mM of Tris-HCl, pH 7.4) were added to a centrifuge tube (50 mL), the bacterial body was dispersed using a mixer (manufactured by General Electric, SI-0286, level 10), then, centrifugal separation (10,000 rpm, 10 minutes, room temperature) was carried out using a centrifugal separator (manufactured by Tomy Seiko Co., Ltd., MX-305), and the supernatant was removed.


(II) 30 mL of a buffer solution AI and 0.3 mL of 0.1 M PMSF (dissolved using isopropanol) were added to the precipitate (bacterial body) obtained by the centrifugal separation and were dispersed for three minutes using the mixer (level 10) manufactured by General Electric. After that, the bacterial body was crushed using an ultrasonic crusher (manufactured by Sonic & Materials, Inc., VCX500), and centrifugal separation (10,000 rpm, 10 minutes, room temperature) was carried out.


(III) 30 mL of the buffer solution AI was added to the precipitate obtained by the centrifugal separation, was dispersed for three minutes using a mixer (manufactured by IKA, T18 basic ULTRA-TURRAX, level 2) manufactured by General Electric, then, centrifugal separation (10,000 rpm, 10 minutes, room temperature) was carried out using the centrifugal separator manufactured by Tomy Seiko Co., Ltd., and the supernatant was removed.


(IV) A 7.5 M urea buffer solution I (7.5 M of urea, 10 mM of sodium dihydrogen phosphate, 20 mM of NaCl, 1 mM of Tris-HCl, pH 7.0) was added to the centrifuge tube from which the supernatant was removed, and the precipitation was favorably dispersed using the ultrasonic crusher manufactured by SMT (level 7). After that, the precipitate was dissolved for 120 minutes using a shaker manufactured by Taitec Corporation (200 rpm, 60° C.). A protein solution after the dissolution was centrifugally separated (11,000×g, 10 minutes, room temperature) using the centrifugal separator manufactured by Tomy Seiko Co., Ltd., and the supernatant was dialyzed using a dialysis tube (manufactured by Sanko Junyaku Co., Ltd., cellulose tube 36/32). White agglomerated protein obtained after the dialysis was collected by means of centrifugal separation, water was removed using a freeze dryer, and freeze-dried powder was collected. The degree of refining of the target protein ADF3Kai-noNR in the obtained freeze-dried powder was confirmed by image-analyzing the results of the polyacrylamide gel electrophoresis (CBB dyeing) of the powder using Totallab (Nonlinear Dynamics Ltd.). As a result, the degree of refining of ADF3Kai-noNR was approximately 85%.


Example 1

<Method for Producing Molded Article>


1.35 g of the freeze-dried powder obtained in the “polypeptide preparation example” (hereinafter, referred to as “sample”) was weighed, and this sample was introduced into the through hole of the die 2 (a cylindrical die having a rectangular through hole having a 35 mm×15 mm cross section) of the press molding machine 10 illustrated in FIG. 1. At this time, the sample was added so that it became uniform thickness. After the entire sample was introduced, the heating of the die 2 was initiated, and the upper side pin 4 and the lower side pin 6 were inserted into the through hole using a hand presser (manufactured by NPa System Co., Ltd., NT-100H-V09), thereby pressing the sample. At this time, the pressurization condition of the sample was controlled to be 40 kN. The heating was stopped when the temperature of the sample reached 200° C., the sample was cooled using a spot cooler (manufactured by Trusco Nakayama Corporation, TS-25EP-1) and was removed when the temperature of the sample reached 50° C., and deburring was carried out, thereby obtaining a 35 mm×15 mm×2 mm rectangular molded article.


In Example 1, the heating was stopped when the temperature of the sample reached 200° C., the sample was cooled using the spot cooler and was removed when the temperature of the sample reached 50° C. That is, the heating temperature (X) was 200° C., and the annealing time (Y) was 0 minutes since the rapid cooling was initiated immediately after the heating temperature was reached.


Example 2

A molded article was obtained in the same manner as in Example 1 except for the fact that the heating temperature (X) was set to 100° C., the annealing time (Y) was set to 30 minutes, and the pressurization condition was set to 30 kN.


<Methods for Measuring Bending Elastic Modulus and Bending Strength>


After the obtained molded article was left to stand for one day in a constant temperature and humidity tank (manufactured by ESPEC Corp., LHL-113) under conditions of 20° C./65%, the following measurements were carried out.


That is, a three-point bending test was carried out using a basket jig in an autograph (manufactured by Shimadzu Corporation, AG-Xplus). A load cell used was 50 kN. At this time, the distance between the support points for three-point bending was fixed to 27 mm, and the measurement rate was set to 1 mm/minute. In addition, the size of the molded article was measured using a microcaliper, and the molded article was installed in the jig and was measured. The bending elastic modulus was obtained from a displacement (strain) of up to 0.05 to 0.25%.


<Method for Measuring Transparency>


For the obtained molded articles, the transparency in the thickness direction (2 mm-thick) was visually measured, and molded articles that were transparent were evaluated as O, and molded articles that were not transparent were evaluated as X. That is, the transparency was confirmed from whether or not the logo was visible when the molded article was placed on paper on which the logo of Spiber Inc. was printed.


Comparative Examples 1 to 4

35 mm×15 mm×2 mm rectangular formed articles were obtained in the same manner as in Example 1 using polyether ether ketone (PEEK), polycarbonate (PC), poly(methyl methacrylate) (PMMA), and an ABS resin (ABS). These formed articles were left to stand for one day in the constant temperature and humidity tank (manufactured by ESPEC Corp., LHL-113) under conditions of 20° C./65%, and then the bending elastic moduli, the bending strengths, and the transparency were measured in the same manner as in Example 1.


The results of the example and the comparative examples are summarized in Table 1. A photograph of the molded article used to evaluate the transparency of Example 1 is illustrated in FIG. 3.













TABLE 1







Bending
Bending




Elastic Modulus
Strength
Trans-



(GPa)
(MPa)
parency



















Example 1
5.39
74
O


Example 2
6.6
64.6
O


Comparative Example 1 (PEEK)
4.4
171
X


Comparative Example 2 (PC)
2.68
97.3
O


Comparative Example 3 (PMMA)
3.2
105
O


Comparative Example 4 (ABS)
2.32
62.9
X









Examples 2 to 17

Molded articles were obtained in the same manner as in Example 1 except for the fact that the heating temperature (X) and the annealing time (Y) were changed as shown in Table 2 and the pressurization condition was set to 30 kN.












TABLE 2







Heating Temperature
Annealing Time



X (° C.)
Y (Minutes)




















Example 2
110
0



Example 3
120
0



Example 4
130
0



Example 5
140
0



Example 6
160
0



Example 7
180
0



Example 8
90
5



Example 9
100
5



Example 10
110
5



Example 11
120
5



Example 12
90
15



Example 13
120
15



Example 14
80
30



Example 15
90
30



Example 16
110
30



Example 17
120
30










Examples 18 to 23

Molded articles were obtained in the same manner as in Example 1 except for the fact that the heating temperature (X), the annealing time (Y), and the pressing condition were set as shown in Table 3.













TABLE 3







Heating





Temperature
Annealing Time
Pressing



X (° C.)
Y (Minutes)
Condition (kN)



















Example 18
90
0
40


Example 19
100
0
40


Example 20
110
0
40


Example 21
120
0
40


Example 22
90
0
50


Example 23
100
0
50









For Examples 5 to 7, 16 and 17, the bending elastic moduli and the bending strengths were measured and are summarized in Table 4.














TABLE 4







Heating
Annealing
Bending
Bending



Temperature
Time
Elastic
Strength



X (° C.)
Y (Minutes)
Modulus (GPa)
(MPa)




















Example 5
140
0
5.2
52.1


Example 6
160
0
5.8
56.7


Example 7
180
0
5.7
63.5


Example 16
110
30
6.3
67.1


Example 17
120
30
5.9
62.5









REFERENCE SIGNS LIST


2: DIE, 4: UPPER SIDE PIN, 6: LOWER SIDE PIN, 8a: COMPOSITION BEFORE HOT PRESSING, 8b: COMPOSITION AFTER HOT PRESSING, 10: PRESS MOLDING MACHINE


Sequence Listing

Claims
  • 1. A non-fibrous, hot-press molded, fused article of a composition comprising a refined recombinant polypeptide, wherein the polypeptide is at least one kind selected from the group consisting of natural spider silk protein and polypeptides derived from natural spider silk protein,wherein the natural spider silk protein and polypeptides derived from natural spider silk protein comprise a unit of the amino acid sequence represented by Formula 1: REP1-REP2  (1),wherein 2 to 20 alanine amino acid residues are continuously arranged in REP1, and REP2 is an amino acid sequence of 10 to 200 amino acid residues, in which the total amino acid residue number of glycine, serine, glutamine, and alanine in the amino acid sequence is 40% or more of the total number of the amino acid residues, andwherein the non-fibrous, hot-press molded, fused article has a bending elastic modulus of more than 4.5 GPa.
  • 2. The non-fibrous, hot press molded, fused article according to claim 1, wherein the bending elastic modulus is 4.7 GPa or more and 15.0 GPa or less.
  • 3. The non-fibrous, hot press molded, fused article according to claim 2, wherein the bending elastic modulus is more than 5.0 GPa or more and 10.0 GPa or less.
  • 4. The non-fibrous, hot press molded, fused article according to claim 3, wherein the bending elastic modulus is more than 5.2 GPa or more and 7.0 GPa or less.
  • 5. The non-fibrous, hot press molded, fused article according to claim 1, wherein the non-fibrous, hot press molded, fused article has a transmittance of 50% or more in a case in which an optical transmittance measurement instrument is used and a cumulative time is set to 0.1 seconds in a wavelength range of 220 to 800 nm.
  • 6. The non-fibrous, hot press molded, fused article according to claim 5, wherein the bending elastic modulus of more than 4.7 GPa or more and 15.0 GPa or less.
  • 7. The non-fibrous, hot press molded, fused article according to claim 6, wherein the bending elastic modulus is more than 5.0 GPa or more and 10.0 GPa or less.
  • 8. The non-fibrous, hot press molded, fused article according to claim 7, wherein the bending elastic modulus is more than 5.2 GPa or more and 7.0 GPa or less.
Priority Claims (1)
Number Date Country Kind
JP2015-185777 Sep 2015 JP national
PCT Information
Filing Document Filing Date Country Kind
PCT/JP2016/076501 9/8/2016 WO 00
Publishing Document Publishing Date Country Kind
WO2017/047504 3/23/2017 WO A
US Referenced Citations (5)
Number Name Date Kind
8666471 Rogers et al. Mar 2014 B2
20090075868 Keeley et al. Mar 2009 A1
20100228359 Vogt et al. Sep 2010 A1
20140058066 Sekiyama et al. Feb 2014 A1
20150291673 Sekiyama Oct 2015 A1
Foreign Referenced Citations (16)
Number Date Country
102892356 Jan 2013 CN
103502516 Jan 2014 CN
104718244 Jun 2015 CN
104936979 Sep 2015 CN
H05-171049 Jul 1993 JP
2010-526582 Aug 2010 JP
2014-080491 May 2014 JP
2014-129639 Jul 2014 JP
2014-198715 Oct 2014 JP
2008071226 Jun 2008 WO
2008140703 Nov 2008 WO
WO 2012165476 Dec 2012 WO
2014062134 Apr 2014 WO
2014103799 Jul 2014 WO
2014175179 Oct 2014 WO
2017047503 Mar 2017 WO
Non-Patent Literature Citations (9)
Entry
Xu & Lewis, “Structure of a protein superfiber: Spider dragline silk”, Proc. Nati. Acad. Sci. USA, 1990, vol. 87, pp. 7120-7124.
Tucker et al., “Mechanical and Physical Properties of Recombinant Spider Silk Films Using Organic and Aqueous Solvents”, BioMacromolecules, Jul. 2014, vol. 15, pp. 3158-3170. dx.doi.org/10.1021/bm5007823.
Hirai, “Keratin and Fibroin Resins for Environmental Friendly Materials Using Animal Proteins Derived from Industrial Wastes;” Functions & Materials, 34: 40-48 (2014) (partial English translation).
International Search Report issued in corresponding International Patent Application No. PCT/JP2016/076501 dated Oct. 11, 2016.
Supplemental European Search Report issued in counterpart European Patent Application No. 16846375.0 dated Jan. 8, 2019.
International Preliminary Report on Patentability and Written Opinion issued in corresponding International Patent Application No. PCT/JP2016/076501 dated Mar. 29, 2018.
Akiyama et al., “Effect of preparation method of powdered silk on the mechanical properties of moulded silk,” Polymer, 35: 2355-2358 (1994).
Guerette et al., “Silk Properties Determined by Gland-Specific Expression of a Spider Fibroin Gene Family,” Science, 272: 112-115 (1996).
“Pressing of Powder Silk and the Properties of the Molded Product,” Modern Silk Science & Technology, 8-12 (1994) (see partial English translation).