The present invention relates to a molded article of a resin composition obtained by compounding a functional filler into a resin made from poly-L-lactic acid, the functional filler being yielded by a copolymerization of a compound having 2-4 hydroxyl groups with 1-100 molecules of D-lactic acid and a low-molecular-weight polymer selected from a group consisting of glycols, aliphatic polyesters and aromatic polyesters.
PET bottles become world-widely popular as a revolutionary container and are applied for soybean sauce, water for food, drinking water, light drinks and beers, which largely contribute to civil life and distribution. It is noted that the progression of plastics including PET bottles highly contributes to human life and industrial activity, whereas it becomes noticed as a factor causing environmental issues such as depletion of recent petroleum sources, global warming and so on.
As a countermeasure for these issues, it is attempted to develop plastics from botanical resources being a renewable resource. A polylactic acid resin is one of biodegradable resins obtained from renewable materials such as corn, potato and the like, and has excellent transparency and hardness and possesses properties similar to polystyrene currently and widely used in food containers and the like.
In the container field, PET bottles are most frequently used. Even in this field, the development of biodegradable resins is anticipated as a key word for solving the resource-waste issues. However, the development for use in the bottle is not promoting contrary to the anticipation at the present time.
Since the polylactic acid is a crystalline polymer, it is low in the melt viscosity required for the forming of the bottle and has no temperature stability and further slow in the crystallization rate and long in the shaping cycle. On the other hand, a method of lowering the crystallinity is adopted for increasing the melt viscosity to attain the stabilization, but such a method has drawbacks that the crystallinity is too low and the heat resistance of the resulting shaped product is deteriorated. Since the polylactic acid resin presently used has the melting temperature Tm of 155° C. and a crystallinity of about 16%, there can not be expected the improvement of the heat resistance by the crystallization. As an example of preparing a container or preform using the polylactic acid resin, there is a report that a resin film of a polyvinyl alcohol-based coating agent is formed on a surface of a container made from polylactic acid (see JP 8244781 A).
In order to develop a bottle using the polylactic acid as a starting material, therefore, it is required that the resin has the improved heat resistance and a good drop impact resistance in order to put the bottle into practical use. The present inventors have intensively consider a solution of the heat resistance issue and attempted to compound a functional filler having 2-4 hydroxyl groups such as D-lactic acid into a resin made from poly-L-lactic acid. As a result, it is found that the heat resistance of the resin can be improved. However, compounding the D-lactic acid into the resin made from poly-L-lactic acid involves a disadvantage that the drop impact resistance is significantly lowered. In order to address this disadvantage, it is necessary to study a further improvement of the resin obtained by compounding D-lactic acid into the resin made from poly-L-lactic acid.
It is, therefore, an object of the invention to solve the above-mentioned problems by improving the drop impact resistance of a resin made from poly-L-lactic acid compounded with a functional filler without sacrificing the heat resistance.
In order to achieve the above-mentioned object, the present invention provides a molded article characterized in that said molded article is made from a resin composition obtained by compounding a functional filler into a resin made from a poly-L-lactic acid, the functional filler being yielded by a copolymerization of a compound having 2-4 hydroxyl groups with 1-100 molecules of D-lactic acid and a low-molecular-weight polymer selected from a group consisting of glycols, aliphatic polyesters and aromatic polyesters.
When a functional filler obtained by a copolymerization of poly-D-lactic acid and a low-molecular-weight polymer such as polyethylene glycol selected from a group consisting of glycols, aliphatic polyesters and aromatic polyesters is compounded into a resin of poly-L-lactic acid, the heat resistance of the obtained resin is improved by poly-D-lactic acid in the filler, and the drop impact is absorbed by polyethylene glycol integrated introduced in the functional filler. Thus, by compounding the above-mentioned filler into the resin of poly-L-lactic acid, an enhancement of the heat resistance and an improvement of the drop impact resistance can be achieved.
As mentioned above, the present inventors have succeeded in an improvement of the drop impact resistance without sacrificing the heat resistance by compounding a functional filler yielded by a copolymerization of a compound having 2-4 hydroxyl groups with 1-100 molecules of D-lactic acid and a low-molecular-weight polymer selected from a group consisting of glycols, aliphatic polyesters and aromatic polyesters into a resin made from a poly-L-lactic acid.
The present invention, therefore, provides a molded article prepared by compounding functional filler into a resin made from poly-L-lactic acid. In the following examples, LACEA H400 made by Mitsui Chemicals Inc. is used as a resin made from poly-L-lactic acid, and the use of the resin is a preferable embodiment of the invention. However, the resin made from poly-L-lactic acid for use in the object of the invention is not limited thereto, and LACEA 440 available from Mitsui Chemicals Inc., Nature Works 7000D and 7032D available from Nature Works LLC U'z S12 and S22 available from Toyota Motor Corporation or the like may be used.
In the following example, it is proved that the molded article according to the present invention prepared by compounding a functional filler containing the above-mentioned molecular weight of polyethylene glycol of 600 (PEG 600) into a resin has the significantly improved drop impact resistance as compared with a molded article prepared by compounding a filler not containing PEG 600 into a resin. In addition, this molded article shows a superior result of a storage test of at 50° C.
In a preferable embodiment of the invention, the polylactic acid has a number average molecular weight of 60,000-80,000. When the number average molecular weight is within the above range, it is possible to preferably shape hollow shaped products such as bottles and the like.
The functional filler is preferably obtained by copolymerization of a compound having 2-4 hydroxyl groups with 1-100 molecules of D-lactic acid and a low-molecular-weight polymer selected from a group consisting of glycols, aliphatic polyesters and aromatic polyesters. In the functional fillers, it is preferable that 30-50 molecules of D-lactic acid are graft-polymerized, and it is most preferable that 50 molecules of D-lactic acid are graft-polymerized. In the invention, the thermal crystallization can be made by the formation of a stereo-complex between D-lactic acid included in the functional filler and L-lactic acid in the resin, whereby the target effects such as heat resistance and the like are obtained. The feature that it is preferable to graft-polymerize about 50 molecules of D-lactic acid is confirmed by a differential scanning calorimetry (DSC).
Moreover, when the polymerizing quantity of D-lactic acid is not more than 10 molecules, the formation of stereo-complex in H400+pentaerythritol could not be confirmed by DSC. Further, when the polymerizing quantity of D-lactic acid is not less than 50 molecules, the crystal of the stereo-complex itself becomes large, from which is further crystallized a homo polylactic acid, so that there may be unfavorably a tendency of being opacified.
In the invention, the compound in the functional filler is preferable to be sugars selected from polysaccharides and oligosaccharides. Particularly, the oligosaccharide is preferable to be a pentasaccharide. As a concrete example of the preferable sugars may be mentioned monosaccharides such as glucose, fructose and the like; disaccharides such as sucrose and the like; and polysaccharides such as starch, cyclodextrin and the like.
In a further preferable embodiment of the invention, the compound in the functional filler is an inorganic compound such as silica nano particles or the like, or an organic compound selected from polyethylene glycol, trimethylol propane and pentaerythritol. In the case that the above-mentioned compound is polyethylene glycol, it is particularly preferable that the molecular weight of polyethylene glycol is within a range of 200-1,000.
Further, in the invention, the amount of the functional filler compounded is preferably 5-20% by weight, more preferably 10% by weight per the poly-L-lactic acid. If the functional filler is added in an amount of 30% or more by weight, the viscosity in the injection molding becomes low and hence there is caused a problem in the workability of the secondary shaping. Moreover, the formation of the stereo-complex between the filler and the lactic acid resin is confirmed by DSC when the amount of the filler compounded is 5% by weight, 10% by weight or 20% by weight.
In a further preferable embodiment of the invention, one or more melting peaks are existent in addition to the melting point of the resin made from poly-L-lactic acid alone as measured by the differential scanning calorimetry (DSC). The melting point of the resin made from poly-L-lactic acid alone is about 145° C. to 170° C. As shown in the following examples, however, one or two melting peaks are observed even at a higher temperature of from about 180° C. to 200° C. by compounding the functional filler.
The melting peak observed at a temperature higher than that of the resin single body made from poly-L-lactic acid shows that L-lactic acid of the resin and D-lactic acid of the filler form a stereo-complex. The thus formed stereo-complex affects the crystallization behavior of the polylactic acid resin and contributes to the promotion of the crystallization, and hence the improvement of the heat resistance can be attained.
Further, the low-molecular-weight polymer is selected from a group consisting of glycols, aliphatic polyesters and aromatic polyesters. The term “low-molecular-weight” as used herein means the molecular weight of 10,000 or less. If the molecular weight is too large, the formation of the stereo-complex is inhibited. The introduced low-molecular-weight polymer such as glycols, aliphatic polyesters and aromatic polyesters has flexibility, so that it serves as a soft segment to impart the impact resistance to the resin thus obtained.
In the case that the above-mentioned low-molecular-weight polymer is aliphatic polyesters, the molecular weight is preferably 5,000 or less. As a concrete example of the preferable aliphatic polyesters may be mentioned polybutylene succinate (PBS) and polycaprolactone (PCL). In the case that the above-mentioned low-molecular-weight polymer is aromatic polyesters, the molecular weight is preferably 10,000 or less. As a concrete example of the preferable aromatic polyesters may be mentioned polyethylene terephthalate (PET) and polyethylene naphthalate (PEN). In the case that the above-mentioned low-molecular-weight polymer is glycols, the molecular weight is preferably 2,000 or less. In the case that the above-mentioned glycol is polyethylene glycol, the molecular weight is preferably within a range of 200-1,000. PEG 600, which is used in the following examples, is particularly preferred among others.
PEG 600 may be used as a polymerization initiator for polymerization reaction of poly-D-lactic acid, so that it is considered that it can easily be introduced into units of poly-D-lactic acid. The most remarkable feature of the present invention reside in a point that units of polyethylene glycol are copolymerized in units of poly-D-lactic acid in the functional filler used in the present invention to absorb the drop impact. It is considered that the molecular chains of polyethylene glycol do not form stereo-complex with L-lactic acid or D-lactic acid but move flexibly to give the drop impact resistance.
Moreover, the molded article according to the present invention may be made by compounding the functional filler into the resin made from poly-L-lactic acid and extrusion molding, compression molding or injection molding the resin compounded with the functional filler. The methods for extrusion molding, compression molding and injection molding are well known in the art.
The molded article according to the present invention may have various forms and shapes. The molded article according to the present invention may be, for example, a hollow shaped product used as a container for beverages. The molded article according to the present invention may also be formed as a thin elongated container such as a drink cup by means of injection molding. The elongated drink cup is, however, a way of example, and its form and shape is not particularly limited.
Further, the molded article according to the present invention may be a preform for forming a hollow shaped article. Forming a hollow shaped article by blow molding of the preform is also within a scope of the invention. As the blow molding method, biaxial blow molding and direct blow molding, which are well known in the art, are preferably used without limiting thereto.
The following examples are given in illustration of the present invention and are not intended as limitation thereof.
A filler in which units of PEG 600 are introduced into units of poly-D-lactic acid (hereinafter referred to as a drop impact resistant filler) and a filler having no unit of PEG 600 but units of poly-D-lactic acid (hereinafter referred to as a conventional filler) are synthesized in the following manner. The expected configuration of the conventional filler and the drop impact resistant filler thus synthesized are shown in
The conventional filler not containing PEG 600 is made in the following manner.
Starting Material
Synthetic Method
1. The initiator, pentaerythritol, (7.4 g) and D-lactic acid solution (1100 g) are charged in a 1-litter separable flask.
2. The solution is heated at 130° C. to remove water in the solution (24 hours).
3. The temperature is increased to 160° C. and the solution is agitated for 24 hours.
The drop impact resistant filler containing PEG 600 is made in the following manner.
Starting Material
Synthetic Method
1. The initiator, pentaerythritol, (6.8 g) and D-lactic acid solution (1000 g) are charged in a 1-litter separable flask.
2. The solution is heated at 130° C. to remove water in the solution (24 hours).
3. The temperature is increased to 160° C., 45 g of PEG 600 are added after three hours, and then the solution is agitated for 48 hours.
As the below-mentioned sample for evaluation, a filler compounded with a flexibility improver for polylactic acid (PLA), Plamate PD-350 manufactured by Dainippon Ink is also used. Plamate PD-350 is a block copolymer having a structure of PLA-PBS-PLA. In this regard, PBS means polybutylene succinate.
The conventional filler and the drop impact resistant filler are added to PLA by means of a biaxial extruder to give pellets. More specifically, polylactic acid resin, LACEA H400, and 10% by weight of a functional filler (the conventional filler or the drop impact resistant filler) are blended, and the bulk of the blended materials are charged into a feed slot of a biaxial extruder having a screw size L/D=43 (screw diameter Φ=35.5 mm). The charged materials are melted and kneaded to extrude a strand from a die, and the extruded strand is passed through a cooling water bath to allow the strand to solidify. Thereafter, the strand is cut by a pelletizer to give pellets. In this example, the bulk of the materials are charged into a main feed slot. It is noted that the functional filler may be charged separately into a side feed slot, or into the main feed slot or other feed slots by means of a liquid adding pump or the like. In order to examiner behaviors of temperature characteristics of the materials, DSC measurements are carried out. In the DSC measurements, DSC 6220 manufactured by SII Inc. is used and the measurements are carried out under a condition with a temperature range of 30-220° C. and a temperature rising rate of 10° C./min.
DSC charts of the pellets thus measured are shown in
In order to evaluate drop impact resistance, bottles made from PLA resin compounded with filler are prepared and subjected to a drop test. The samples used for the evaluation are the following four types. The amount of the filler compounded to PLA is 10% by weight per PLA.
(1) LACEA H400 made by Mitsui Chemicals Inc. alone
(2) LACEA H400 made by Mitsui Chemicals Inc.+the conventional filler
(3) LACEA H400 made by Mitsui Chemicals Inc.+Plamate PD-350+the conventional filler (Plamate: 20% by weight and filler: 10% by weight are compounded)
(4) LACEA H400 made by Mitsui Chemicals Inc.+the drop impact resistant filler
The above-mentioned four samples are molded into 180 ml bottles and the molded bottles are subjected to the test. That is, preform products for 180 ml bottle having a wall thickness of 3 mm are prepared by a molder, M-100A manufactured by Meiki Seisakusyo Co. Ltd. Then, the preform products are set in a biaxial blow molder with the heat set temperature of 55° C., 70° C., 90° C., 100° C. and 110° C. to mold 180 ml bottles. The bottle thus manufactured is shown in
Each of the bottles thus manufactured is filled with 180 ml of water and then the bottles are sealed with plastic caps. After storing at 23° C. for 24 hours, the bottles are subjected to the drop test. The drop test is carried out by dropping the bottle in a vertical position from one meter high onto a concrete plate for ten times. Every time the bottle is dropped, the appearance of the bottle is inspected for a break and a crack. The result of the drop test is shown in Table 1. As a result, a crack is found in the bottle made from the resin consisting of LACEA H400 with the conventional filler after one to three drops. In contrast, no crack is found in the bottle made from the resin consisting of LACEA H400 with the drop impact resistant filler even after 10-20 drops, which, in turn, proves a significant improvement of the drop impact resistance as compared with the conventional filler. A crack is also found in the bottle made from the resin consisting of LACEA H400 with Plamate PD-350 and the conventional filler after one to three drops, which does not satisfy the required drop impact resistance.
In order to evaluate the heat resistance, a storing test at 50° C. is carried out. The test is carried out by storing bottles made from the PLA resin compounded with the filler in a thermostatic chamber (manufactured by TABAI ESPEC CORP.) at 50° C. without humidification for four weeks. The bottles used for the evaluation are the same four samples subjected to the drop test. The method and condition for molding the bottles are the same as those described with reference to the drop test in example 3.
The above-mentioned bottles are stored at 50° C. for 0 day, 1 day, 4 days, 7 days, 14 days, 21 days and 28 days, and changes in the total height, capacity and bottom depth of the bottles are measured. The results of the storing test at 50° C. are shown in Table 2 and
When functional filler yielded by copolymerizing poly-D-lactic acid and a low molecular-weight polymer such as polyethylene glycol is compounded into a resin made from poly-L-lactic acid, the heat resistance of the resin is improved by poly-D-lactic acid in the filler, and the drop impact is absorbed by polyethylene glycol introduced in the functional filler. Accordingly, by compounding the above-mentioned functional filler into the resin made from poly-L-lactic acid, it is possible to increase the heat resistance and improve the drop impact resistance. The poly-L-lactic acid resin compounded with the above-mentioned functional filler, which exerts a superior effect on improvements of the heat resistance and the drop impact resistance, can overcome the defects of the conventional polylactic acid resin bottle. The present invention can facilitate a practical use of a polylactic acid bottle which is an environmentally friendly container.
Number | Date | Country | Kind |
---|---|---|---|
2007-161810 | Jun 2007 | JP | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/JP2008/059740 | 5/27/2008 | WO | 00 | 12/30/2009 |