1. Field of the Invention
The present invention relates to a molded component for protecting a radar apparatus, especially to a molded component for the beam path of a radar apparatus disposed behind the front grill of an automobile.
2. Background Art
In general, antennas that transmit and receive radio waves in communication devices, radar devices, and the like have rarely been restricted in terms of the design of their bodies and peripheral structures, since their functions have been given priority. For example, a rod antenna whose shape is exposed is used for automobile radio antennas and the like. There may be a case where the antenna is hopefully hidden depending on the location in which the antenna is attached. For example, in a radar system or the like that measures obstacles in front of an automobile and the distance between automobiles, the antenna is preferably disposed in a central position at the front of the automobile in order to make the most of its performance. In this case, although the antenna is likely to be installed near the front grill of automobile, it is preferable that it not be possible to view the antenna from the outside in terms of design.
An auto cruise system involves technology for controlling the distance between vehicles by accelerating or decelerating one's own vehicle, in which a sensor mounted in the front of the vehicle measures the distance and a relative speed between a vehicle in front and one's own vehicle, and the throttle and brakes are controlled based on this information. The auto cruise system has recently attracted attention as one of the core technologies of the intelligent transportation system (ITS) for easing traffic congestion and decreasing traffic accidents. In general, a radio transmitter-receiver device such as a millimeter-wave radar is used as a sensor for the auto cruise system.
As shown in
Therefore, it is preferable to use materials and paints that provide low radio transmission loss and a predetermined appearance for the front grill and the emblem, especially where the beam path of a radar apparatus is arrayed.
In this manner, a radio transmitter-receiver device is generally disposed behind the back surface of the front grill of a vehicle. However, there are many cases where the front grill is metal plated, so that it is difficult to transmit radio waves satisfactorily through the highly conductive metal. Also, front grills have a structure where air holes for taking in air are disposed, and front grills do not have uniform thicknesses. Therefore, when radio waves pass in and out through such a front grill, there is a difference in a radio transmission speed between the thin portion and the thick portion of the front grill, so that it is difficult to obtain good radar sensitivity.
On account of these reasons, in general, a window portion that is capable of transmitting radio waves is disposed in a portion of the front grill that corresponds to the portion where the radio transmitter-receiver device is disposed. When the window portion is disposed in the front grill, radio waves can pass in and out through the window portion. However, by including a window portion, the appearance of the front grill loses continuity and the appearance of the vehicle may be spoiled, since the internal portions of the vehicle, such as the radio transmitter-receiver device and the engine area, are viewed.
Therefore, conventionally, unity is provided between the window portion and the front grill body by inserting a radio transmission cover as disclosed in JP Patent Publication (Kokai) No. 2000-159039 A into the window portion of the front grill, for example. The radio transmission cover as disclosed in JP Patent Publication (Kokai) No. 2000-159039 A is formed by laminating a plurality of resin layers formed with concavity and convexity. This covering component can provide an impression by a metal layer deposited with concavity and convexity between the resin layers such that the fin member of the front grill continuously exists in the radio transmission cover.
Indium is used as a metal deposited in such a radio transmission cover. When depositing indium on a deposit member, indium is not deposited on the surface of the deposit member in a uniform film manner, but deposited in a minute insular manner. In other words, when indium is deposited on the deposit member, the surface of the deposit member has a minute mixture of a deposit portion where indium is deposited in a minute insular manner and a non-deposit portion where nothing is deposited. In this case, radio waves can pass in and out through the non-deposit portion and the surface of the deposit member can be recognized upon viewing as a member that has metallic luster, since the deposit portion has indium deposited in a minute insular manner.
However, as indium is an expensive metallic material, the increased material cost when the deposition is performed using indium is problematic. Moreover, it is difficult to form the deposited portion and the non-deposited portion in a well-balanced manner. For example, there is a case where radio waves do not pass in and out satisfactorily when the deposit portions are formed extremely closely together.
JP Patent Publication (Kokai) No. 2003-252137A discloses a method for manufacturing a radio transmission cover in order to enable processing of a metallic film using various metallic materials in addition to indium, and to provide a method for manufacturing a radio transmission cover in which radio waves pass in and out satisfactorily. The method comprises a first step for forming a cover base member in a planar table manner, a second step for forming the metallic film on one surface of the cover base member such that the shape of the metallic film corresponds to the shape of the aforementioned fin portion, a third step for forming a bright portion in an insular manner by physically or chemically removing a part of the metallic film, and a fourth step for forming a transparent resin layer on the upper layer of a plane where the bright portion of the cover base member is formed. The radio transmission cover is disposed on the front grill of a vehicle, the front grill having a reticular fin portion, and a radio transmitter-receiver device is disposed on the back surface side thereof.
JP Patent Publication (Kokai) No. 2000-159039 A and JP Patent Publication (Kokai) No. 2000-49522 A disclose a thin metallic layer comprising indium deposited on a metal portion area that can be viewed from the outside at a plastic-plated member for the beam path of a radar apparatus. However, it is necessary to ensure a bright design and the reliability of durability for radio transmittance by forming a stable protective layer so as not to allow the indium bright film layer to undergo exfoliation or be damaged by an external force, or to be corroded by an external environmental stress such as water or polluted air.
This is due to the following facts: indium is a very soft metallic material with a value of 1.2 in the Mohs hardness scale; indium corrodes under the aforementioned environmental stress since it is basically a metallic material; it is necessary to ensure the reliability of durability by securing the film thickness with certainty such that the bright-effect design of indium can be obtained without thickening the indium film layer more than is necessary since a radio transmission loss occurs as a conductivity loss based on the fact that indium is basically a metallic material; and the indium layer melts due to the heat of molten resin when successively conducting secondary formation of the lining resin on a resin-molded component in which a film is formed on the surface of a base body in advance, since the melting point of indium is 156° C., which is extremely low, for example.
JP Patent Publication (Kokai) No. 2000-344032 A discloses a ceramic film comprising silicon dioxide disposed as a protective layer for preventing exfoliation and ensuring anticorrosion of an indium film.
Although indium film is suitable for a film of an emblem or the like as it shows a metallic color, it poses problems in that it readily experiences exfoliation and lacks durability and abrasion resistance. Also, indium film may corrode, since it is basically a metal. Thus, when a ceramic film comprising silicon dioxide is disposed, the durability is improved and the film, or a paint, can be protected. However, the ceramic film comprising silicon dioxide is colorless, so that the appearance of a metallic color, for example, cannot be provided.
In view of the aforementioned problems in the prior art, it is an object of the present invention to provide a molded component that offers stable effects as a product over a long period of time, which is a molded component providing a low level of radio transmission loss for the beam path of a radar apparatus. It is also an object of the present invention to provide a molded component that shows a bright color for the beam path of a radar apparatus.
The inventors found that the aforementioned object could be achieved by using a specific metal for a bright decoration layer and arrived at the present invention.
The present invention is an invention of a molded component for the beam path of a radar apparatus. The molded component comprises a base body composed of a resin layer, and a bright decoration layer on the surface of the base body, the bright decoration layer being composed of tin and/or a tin alloy. By using the bright decoration layer composed of tin and/or a tin alloy, hardness and abrasion resistance can be improved as compared with the indium layer of the prior art. Also, radio transmittance can be improved as compared with the indium layer.
Preferably, the aforementioned tin and/or a tin alloy is tin (Sn) alone or an alloy of tin (Sn) and one or more elements selected from indium (In), gallium (Ga), antimony (Sb), and bismuth (Bi).
The bright decoration layer comprising the aforementioned tin and/or a tin alloy can include a plurality of layers. For example, the bright decoration layer comprising the aforementioned tin and/or a tin alloy can include an Sn-alone layer and an Sn-alloy layer.
Methods for forming the bright decoration layer comprising the aforementioned tin and/or a tin alloy are not limited. Specifically, methods include vacuum film forming methods such as a vacuum deposition method, an ion plating method, and a sputtering method, for example; vapor growth methods such as thermal CVD, plasma CVD, photo CVD, and MOCVD, for example; the LB (Langmuir-Blodgett) method, electroless deposition, the sol-gel method; and the like.
Preferably, each layer that forms the bright decoration layer comprising the aforementioned tin and/or tin alloy has a thickness of 1 nm to 500 nm. Further preferably, the thickness is 10 nm to 100 nm.
Preferably, the aforementioned base body is formed by a transparent resin that resulting in low radio transmission loss or a transparent resin resulting in low dielectric loss.
The molded component for the beam path of a radar apparatus according to the present invention can further include a non-transparent resin layer for enhancing the tone of color.
According to the present invention, a molded component for the beam path of a radar apparatus with low radio transmission loss and improved hardness and abrasion resistance can be provided.
The bright decoration layers 12 and 15 composed of tin, and bright decoration layers 13 and 14 composed of a tin alloy, may be formed by a vacuum deposition method. Preferably, each layer used to form the bright decoration layer has a thickness of 1 nm to 500 nm. Further preferably, the thickness is 10 nm to 100 nm.
A desired color can be expressed by suitably selecting the material types that constitute the bright decoration layers 12 and 15 composed of tin, and bright decoration layers 13 and 14 composed of a tin alloy, and by suitably selecting the thickness of the layers.
The base body 10 is composed of a material that is provides low radio transmission loss and is superior in terms of dielectric properties. Relative permittivity ε′ and dielectric loss tan δ, for example, provide an indication of the dielectric property. The base body 10 is composed of a transparent resin, preferably polycarbonate.
In the following, an example and comparative examples of the present invention are described.
A test piece composed of a polycarbonate film base body (base) whose thickness was 3.5 mm was prepared (comparative example 1). Bright film pieces were obtained by vacuum depositing tin on the polycarbonate film base bodies whose thicknesses were 3.5 mm such that the thicknesses of tin were 10 nm, 30 nm, and 50 nm (example). Bright film pieces were obtained by vacuum depositing indium instead of tin such that the thicknesses of indium were 10 nm, 30 nm, and 50 nm (comparative example 2). The tin-deposit pieces in the example had an appearance featuring a bright-silver effect that was equivalent to that of the indium-deposit pieces in comparative example 2.
Table 1 shows these test pieces.
[Performance Evaluation]
Radio Transmission Loss
As shown in
Measurement of Hardness of Film Layer
A hardness test carried out by the inventors is described with reference to
Abrasion Resistance Test of Film Layer
An abrasion resistance test carried out by the inventors is described with reference to
The stroke width of the friction block 803 was 100 mm and the movement speed was 50 strokes per minute. The number of strokes was measured when the film on the surface of the sample started to experience exfoliation. The exfoliation of the film was determined by visual observation.
Table 2 shows the measurement results.
As Table 2 indicates, a tin-film component according to the present invention obtains a design featuring bright-silver effect equivalent to that of an indium-film component of the prior art and performance of millimeter-wave transmission loss, and provides a strong film layer that overcomes the problems of the indium-film component. Therefore, the component can be provided by a simpler material arrangement than in the case of a bright decoration component composed of the indium-film component of the prior art. The simpler material arrangement leads to productivity improvement, and materials can be obtained at a low price. Also, by using low-price tin materials, components can be provided at a low price, since indium-film components are considerably expensive.
Number | Date | Country | Kind |
---|---|---|---|
2004-025793 | Feb 2004 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
3154432 | Herrick | Oct 1964 | A |
3255035 | Clough et al. | Jun 1966 | A |
3396400 | Kelly et al. | Aug 1968 | A |
4241129 | Marton et al. | Dec 1980 | A |
4419570 | Kalbskopf et al. | Dec 1983 | A |
4837135 | Milner | Jun 1989 | A |
5877727 | Saitou et al. | Mar 1999 | A |
5911899 | Yoshikai et al. | Jun 1999 | A |
5964113 | Wake et al. | Oct 1999 | A |
6184842 | Leinweber et al. | Feb 2001 | B1 |
6328358 | Berweiler | Dec 2001 | B1 |
6413630 | Nakayama | Jul 2002 | B1 |
6433753 | Zimmermann | Aug 2002 | B1 |
6465102 | Honigfort et al. | Oct 2002 | B1 |
6500910 | Koike et al. | Dec 2002 | B1 |
6504501 | Tsuno et al. | Jan 2003 | B2 |
6620493 | Hasegawa et al. | Sep 2003 | B2 |
6663957 | Takushima et al. | Dec 2003 | B1 |
6726964 | Thompson et al. | Apr 2004 | B1 |
6777610 | Yamada et al. | Aug 2004 | B2 |
6803540 | Yamada et al. | Oct 2004 | B2 |
6811850 | Hirata | Nov 2004 | B1 |
6875484 | Kogure et al. | Apr 2005 | B1 |
6930140 | Amou et al. | Aug 2005 | B2 |
20010037935 | Oya et al. | Nov 2001 | A1 |
20020171579 | Artis et al. | Nov 2002 | A1 |
20030039839 | Haruta et al. | Feb 2003 | A1 |
20030152756 | Yamada et al. | Aug 2003 | A1 |
20030170410 | Buch-Rasmussen et al. | Sep 2003 | A1 |
20040174596 | Umeki | Sep 2004 | A1 |
20040200818 | Yamada et al. | Oct 2004 | A1 |
20050020781 | Sugimasa et al. | Jan 2005 | A1 |
20050168374 | Kamiya et al. | Aug 2005 | A1 |
20050237261 | Fujii et al. | Oct 2005 | A1 |
20060172100 | Hu et al. | Aug 2006 | A1 |
20060216442 | Kamiya et al. | Sep 2006 | A1 |
20060234002 | Nee | Oct 2006 | A1 |
Number | Date | Country |
---|---|---|
A-08-103982 | Apr 1996 | JP |
A-10-193549 | Jul 1998 | JP |
A-2000-049522 | Feb 2000 | JP |
A-2000-159039 | Jun 2000 | JP |
A-2000-344032 | Dec 2000 | JP |
A-2002-135030 | May 2002 | JP |
A-2003-252137 | Sep 2003 | JP |
Number | Date | Country | |
---|---|---|---|
20050168374 A1 | Aug 2005 | US |