Molding composition

Information

  • Patent Grant
  • 4689098
  • Patent Number
    4,689,098
  • Date Filed
    Friday, October 11, 1985
    38 years ago
  • Date Issued
    Tuesday, August 25, 1987
    37 years ago
Abstract
EMI shielded stampable sheet contains two fiber mats, one of which provides primarily reinforcing function, the other of which provides primarily EMI shielding function.
Description

BACKGROUND OF THE INVENTION
In one aspect, the invention relates to a fiber mat suitable for incorporating into a molding composition. In another aspect, the invention relates to a process for forming the fiber mat. In yet another aspect, the invention relates to molding composition containing the fiber mat.
For many applications, it is desirable to provide finished parts with electromagnetic interference (EMI) shielding characteristics. In the automotive field, EMI shielding is required for plastic hoods, fenders, and fire walls. Office business machines require some form of shielding over parts of their internal areas. By regulation, emissions from all digital computing devices must be within certain radiation limits. Regulation of emissions is necessary because of increasing complaints of electrical malfunctions caused by electromagnetic interference. Examples include TV snow, flight instrument malfunctions caused by pocket calculators and activation of electrically controlled devices by citizen band radios.
Methods presently used to shield electronic components have been ranked in order of preference. The methods, in order of preference, include silver paint application, nickel paint application, conductive filler utilization, silver reduction, cathode sputtering, foil application, copper paint, vacuum metalizing, electroplating, flame/arc spraying and graphite paint application. With the exception of conductively filled plastics, all of the shielding methods suffer from either a limited life due to chipping, cracking, peeling or the fact that they involve costly secondary operations.
The most desirable method of shielding is with conductively filled plastic because the shielding material is an integral part of the plastic and will not chip or blister and does not require a secondary operation. However, incorporating conductive fillings in plastics frequently reduces product properties in an unacceptable extent because of the high amount of filler required to provide acceptably high shielding characteristics.
OBJECTS OF THE INVENTION
It is an object of this invention to provide a fiber reinforcement for polymer components which imparts superior mechanical properties.
It is another object of the invention to provide a polymer sheet containing the fiber reinforcement which exhibits good mechanical properties.
It is yet another object of the invention to be able to use lesser amounts of conductive filler in a polymer sheet without reducing shielding effectiveness.
It is still a further objective of this invention to provide a process for forming a conductive fiber mat which is easily processed and provides good properties when incorporated into a polymer sheet.
STATEMENT OF THE INVENTION
In accordance with the first embodiment of the invention, there is provided a fiber mat suitable for deploying as an EMI shield in a polymer matrix. The mat comprises a first layer formed from a nonwoven reinforcing fiber and a second layer carried by the first layer comprising metal whiskers or fibers formed from a ductile metal or metal alloy. By using these metal whiskers or fibers in a second layer, low metal concentrations are possible in the final product because of the high aspect ratio (1/d) of the fiber. By carrying the metal whiskers on the reinforcing mat the second layer can be present in an amount which would otherwise be inadequate to provide sufficient structural integrity for independent handling.
In another aspect of the invention, the above described two layer mat is incorporated into a polymer matrix to form a composite. The resulting composite is suitable for use as panels and the like requiring EMI shielding. The nonwoven layers of fiber are flowable under stamp molding conditions and thus the composite is highly suitable for use as stampable sheet or sheet molding compound.
In another aspect of the invention, a conductive mat suitable for use in a polymer matrix to provide good mechanical properties and EMI shielding is provided by a process comprising conveying a mat of nonwoven fabric beneath a distributor of metal whiskers and distributing metal whiskers onto the mat from the distributor in an amount sufficient to impart conductivity to the resultant blend. The procedure provides advantages in (1) ease of fabrication and economy in the use of conductive material (2) ease of handling of the resulting two component mat.
DETAILED DESCRIPTION OF THE INVENTION
In accordance with a first embodiment of the invention, a fiber mat suitable for incorporating into a polymer or resin to provide reinforcement and EMI shielding therein comprises a first layer and a second layer. The first layer comprises a nonwoven reinforcing fiber mat. Conventional reinforcing fibers can be used if desired, the exact type depending on the properties desired to be imparted to the matrix and cost. Nonwoven fiberglass mat is presently preferred since it is readily available and inexpensive, especially fiberglass in which the fiber is continuous because of the resulting properties in the composite although chopped glass or chopped or continuous carbon fiber can be used if desired. Carbon fibers, either chopped or continuous, also provide a desirable alternative.
The second layer of the mat is carried on the first layer and comprises nonwoven metal whiskers or fibers of a ductile conductive metal or metal alloy. Preferably, the metal whiskers have a sufficient length to diameter ratio (aspect ratio) so as to provide good EMI shielding at a low concentration. To provide good EMI shielding it is important that a sufficient amount of the metal whiskers be deposited on the nonwoven reinforcing fiber mat so that a conductive network is formed and that the deposit be sufficiently dense to yield the desired degree of EMI shielding. Normally, the second layer will provide a screen on top of the first layer that can be seen through since the wavelengths to be shielded are generally greater than 30 centimeters. Open areas defined by interconnected individual whiskers on the first layer of up to about one square centimeter are thus satisfactory. Various ductile conductive metals or metal alloys are suitable for forming the whiskers. The metals which can be used for electrical conductors are suitable, such as for example, aluminum, copper, silver, or gold. Other metals, such as nickel, tin, and lead are also expected to work well, provided that the resins selected does not interact with the metal selected, such as by corrosion.
Whisker diameter is not particularly important provided that the whisker is not so fragile as to be broken during the thermoforming process. For economy, the whiskers should be of relatively small diameter, preferably in the range of 0.01 to 1 millimeter. Suitable whisker length ranges from 1 millimeter to continuous strand. Preferably, each whisker has a length of greater than 1 centimeter to provide a high aspect ratio and good effectiveness for EMI shielding. Preferably, a major portion of the whiskers have a length in the range of 0.5 to 20 centimeters, more preferably in the range of 1 to 10 centimeters, for ease of processing and most desirable shielding properties. Diameters of the whiskers are preferably in the range of from 0.05 millimeters to 0.5 millimeters although whiskers of other dimensions will work. A preferred metal whisker is comprised of alumimum. Whiskers of this type are formed by the Transmet Corp. (Columbus, Ohio) by distributing molten aluminum on a rapidly spinning wheel followed by a rapid quenching.
The polymer used to form a resin matrix around the first layer and second layer of the fibers can be either thermoplastic or thermoset resin. Polyethylene, polypropylene, and polyester resins are believed highly suitable where high performance properties are not required. Other suitable resins include polystyrene, ABS, other acrylic polymers and copolymers polyethers, polyamides, PVC (polyvinylchlorides), polycarbonates, epoxy resins, phenolic resins, melamines and polyarylene sulfides such as polyphenylene sulfide, polyphenylene sulfide sulfone, polyphenylene sulfide ketone, polyphenylene ether ketone, polyphenylene ether polyphenylsulfone and the like. Almost any polymer which is suitably strengthened by incorporating glass mat can be made into a conductive composite by the inclusion of glass mat on which is deposited a conductive amount of aluminum fiber.
The relative amounts of polymer matrix, reinforcing fiber, and shielding fiber can vary depending upon the reinforcing and shielding properties desired. Generally, the two layer mat can be formed with a weight ratio of reinforcing fiber, generally glass, to metal whiskers such as aluminum, in the range of 4:1 to 1:1. It is believed that by providing the mat with a ratio of glass fiber to aluminum in the range of 3:1 to 1:1 on a weight basis will provide very good results for most applications. The amount of polymer in the composite will generally range from about 25 to 75 percent by weight. A polymer content in the composite ranging from about 40 to 60 percent by weight will provide good results in the case of engineering thermoplastics. Greater amounts of inexpensive polymer such as polypropylene can be used in applications where the mechanical properties are adequate. It is a relatively simple matter when using the invention to attain EMI shielding of at least 40 decibels (dB) and EMI shielding of at least 50 dB such as in the range 50 to 70 dB can be attained without undo experimentation.
To form the conductive mat of the present invention, the nonwoven reinforcing fabric can be passed beneath a distributor of metal whiskers and the metal whiskers are distributed onto the mat from the distributor in an amount sufficient to impart the desired conductivity to the mat. Entanglement between layers can be avoided by interspersing layers of paper of film, such as a film of the polymer to be used as the matrix, between layers of conductive mat in the stack or on the roll. Good results are expected where the glass fibers are continuous and the metal whiskers have a length in the range of 0.5 to 20 centimeters and are distributed on the nonwoven mat in an amount sufficient to impart to the resulting 2-layer conductive mat in the range of 25 to 50 weight percent metal. In a preferred embodiment of the invention, a major portion of the metal whiskers have length in the range of 1 to 10 centimeters.
EMI shielded stampable sheet can be formed on a compaction line in accordance with the invention simply by substituting the conductive mat for the nonconductive mat normally used in such applications. The conductive mat is sandwiched between films of polymer and subjected to sufficiently elevated conditions of temperature and pressure to form the stampable sheet. To form EMI shielded stampable sheet from thermo setting materials the conductive mat is passed through a bath of the thermo setting resin, withdrawn and allowed to partially cure.





The invention is illustrated by the following example:
EXAMPLE 1
Continuous glass fiber mat (Owens-Corning Fiberglass OCF M-8608) was pressed in a laminate with polyphenylene sulfide (PPS) at 600.degree. F. for 1.5 minutes at contact pressure and then at 100 psi and 600.degree. F. for 2 minutes followed by 3 minutes at 100 psi in a room temperature press. Properties of the laminate are shown in Table I.
EXAMPLE 2
PPS-Glass Fiber-Aluminum Fiber Composites
Aluminum fiber (0.75-inch; Transmet Corp., Columbus, Ohio) was placed between layers of continuous glass fiber mat (OCF M-8608) at the desired weight level and laminated with PPS as in Example I. Properties of the laminates at various ratios of glass and aluminum to polymer are shown in Table I.
Comparisons of the data show that EMI shielding varies in relation concentration of the aluminum fiber but as the aluminum fiber content increases from 5 to 20 percent and simultaneously the glass fiber content decreases from 35 to 20 percent, the impact strength (notched Izod) decreases from 16.7 to 11.8 ft.-lb/inch. A good balance of properties is obtained in a composite comprised of 33 percent glass, 17 percent aluminum fibers and 50 percent PPS. Raising the glass fiber content to 40 percent and the aluminum to 20 percent provides a small increase in EMI shielding but at the expense of a distinct reduction of impact strength.
TABLE I__________________________________________________________________________Properties of Polyphenylene Sulfide (PPS)--Glass Fibers - Aluminum FibersComposites__________________________________________________________________________Glass Fibers (%) 40 35 30 25 20 33 40 32Al.degree. Fibers (%) 0 5 10 15 20 17 20 18.sup.aResin (%) 60 60 60 60 60 50 40 50Tensile Strength.sup.c 23 23.6 24.8 17.2 16.9 22.5 22.1 9.6(.times.10.sup.3 psi)Flexural Strength.sup.d 34.5 40.9 39.8 40.5 29.5 40.2 32.5 17.8(.times.10.sup.3 psi)Flexural Modulus.sup.e 1.45 1.35 1.29 1.33 1.12 1.34 1.3 0.8(.times.10.sup.6 psi)Notched Izod.sup.f 14.0 16.7 16.6 13.0 11.8 14.8 12.6 0.8(ft-lb/in)Unnotched Izod.sup.g 25.0 29.6 25.6 27.0 21.3 22.3 19.0 3.2(ft-lb/in)Heat Deflection.sup.h 273 252 271 266 101 272 244 176Temperature, .degree.C.@ 264 psiElongation (%).sup.i 1.9 2.49 2.35 1.52 2.05 4.3 1.24 2.7EMI Shielding.sup.j -- 26-35 38-45 32-55 46-41 57-54 62-69.sup.bfrom 0.1-1000 MHz__________________________________________________________________________ .sup.a Continuous aluminized glass supplied by .sup.b 0.5-1000 MHz .sup.c ASTM D638 .sup.d ASTM D790 .sup.e ASTM D790 .sup.f ASTM D256 .sup.g ASTM D256 .sup.h ASTM D648 .sup.i ASTM D638 .sup.j ASTM ES 783
EXAMPLE 3
Polypropylene (PP)-Glass Fiber Composite
The procedure was the same as in Example 1 except that polypropylene was used and a molding temperature of 500.degree. F. was used. The properties of the composite are shown in Table II.
EXAMPLE 4
PP-Glass Fiber-Aluminum Fiber Composite
The procedure was the same as in Example 2 except that PP was used and a molding temperature of 500.degree. F. was used. The properties of the composite are shown in Table II. At the 33 percent glass fiber--17 percent Al fiber loading the EMI shielding is very good and the change in physical properties due to the addition of the Al fiber is within acceptable limits.
EXAMPLE 5
Polyethylene Terephthalate (PET)-Glass Fiber Composite
The procedure was the same as in Example 1 except that PET was used and the molding temperature was 525.degree. F. Properties are shown in Table II.
EXAMPLE 6
PET-Glass Fiber-Aluminum Fiber Composite
The procedure was the same as in Example 2 except that PET was used and the molding temperature was 525.degree. F. Properties are shown in Table II.
TABLE II______________________________________Properties of Other Polymer - Glass Fibers -Aluminum Fibers CompositesPolymer PP PP PET PET______________________________________Glass Fibers (%) 40 33 40 33Al Fibers (%) 0 17 0 17Resin 60 50 60 50Tensile Strength 16.7 12.6 31.2(.times.10.sup.3 psi)Flexural Strength 14.9 12.3 44.2(.times.10.sup.3 psi)Flexural Modulus 0.6 0.67 1.2(.times.10.sup.6 psi)Notched Izod 20.9 19.3 21.0(ft-lb/in)Unnotched Izod 27.9 24.4 34.6(ft-lb/in)Heat Deflection 156 156 254Temperature .degree.C.Elongation (%) 2.6 1.57 2.26EMT Shielding from -- 60-47 -- 47-530.1-1000 MHz______________________________________
EXAMPLE 7
Preparation of Aluminum Fiber on Glass Mat
Transmet Corp., (Columbus, Ohio) a producer of aluminum fibers using a spinning wheel and quick quench method, STET produced aluminum fibers deposited directly onto a glass mat at 0.5 oz/ft.sup.2 and 1.0 oz/ft.sup.2. This aluminum fiber-glass fiber mat was used without further treatment.
Claims
  • 1. Composition comprising:
  • (a) a mat of non-metallic reinforcing fibers; and
  • (b) a distribution of nonwoven metal whiskers or fibers of a ductile conductive metal or metal alloy carried on the mat.
  • 2. A composition as in claim 1 wherein continuous glass fibers form the mat and the metal whiskers have a length in the range of about 0.5 to about 20 cm.
  • 3. A composition as in claim 2 wherein the metal whiskers comprise aluminum fibers having a length a major portion of which is within the range of 1-10 cm.
  • 4. A composition as in claim 2 further comprising a polymer matrix encasing the mat of non-metallic reinforcing fibers and the distribution of nonwoven metal whiskers or fibers.
  • 5. A composition as in claim 4 wherein the polymer matrix is formed from a thermoplastic resin or thermoset resin having a crystalline character.
  • 6. A composition as in claim 5 wherein the polymer matrix comprises a thermoplastic resin.
  • 7. A composition as in claim 6 which is in the form of a sheet and the polymer comprises polypropylene resin.
  • 8. A composition as in claim 6 further characterized by EMI shielding of at least 40 dB.
  • 9. A composition as in claim 6 further characterized by EMI shielding of at least 50 dB.
  • 10. A composition as in claim 6 wherein the polymer matrix comprises poly(phenylene)sulfide and the metal whiskers are formed from aluminum.
  • 11. A composition as in claim 10 further characterized by a weight ratio of glass fiber to aluminum whiskers in the range of 4:1 to 1:1.
  • 12. A composition as in claim 10 further characterized by a weight ratio of glass fiber to aluminum whiskers in the range of 3:1 to 1:1.
  • 13. A composition as in claim 12 characterized by in the range of 25 to 75 weight percent polyphenylene sulfide matrix material.
  • 14. A composition as in claim 12 characterized by in the range, of 40-60 weight percent polyphenylene sulfide matrix material.
  • 15. A process for forming a conductive mat suitable for use in a polymer matrix to provide improved mechanical properties and EMI shielding, said process comprising:
  • (a) conveying a mat of nonwoven fabric beneath a distributor of molten metal;
  • (b) distributing molten metal from the distributor and forming metal whiskers; and
  • (c) depositing said whiskers on said mat in an amount sufficient to impart conductivity to the mat.
  • 16. A process as in claim 15 wherein the mat is formed from nonwoven glass fibers and the metal whiskers contain aluminum.
  • 17. A process as in claim 16 wherein the glass fibers are continuous and the metal whiskers have a length of 0.5-20 cm.
  • 18. A process as in claim 17 wherein the metal whiskers are distributed on the nonwoven mat in an amount sufficient to impart to the conductive mat in the range of 25-50 wt% metal.
  • 19. A process as in claim 18 wherein a major portion of the metal whiskers have a length in the range of 1.0-10 cm.
US Referenced Citations (44)
Number Name Date Kind
2979424 Whitehurst et al. Apr 1961
3041131 Juras et al. Jun 1962
3167427 Slayter Jan 1965
3184368 Juras May 1965
3356559 Juras Dec 1967
3356914 Juras Dec 1967
3521214 Bennett et al. Jul 1970
3577295 Kraft et al. May 1971
3578544 Thorsrud May 1971
3609104 Ehrreich Sep 1971
3649438 Walker et al. Mar 1972
3708387 Turner et al. Jan 1973
3775365 Mathis et al. Nov 1973
3781170 Nakao et al. Dec 1973
3836422 Bischoff Sep 1974
3988286 Edmonds et al. Oct 1976
3992160 Marzocchi et al. Nov 1976
4042569 Bell et al. Aug 1977
4044188 Segal Aug 1977
4215084 Maringer Jul 1980
4216423 Davenport Aug 1980
4227037 Layton Oct 1980
4229328 Makino et al. Oct 1980
4234648 Patz et al. Nov 1980
4243460 Nagler Jan 1981
4247594 Shea et al. Jan 1981
4276397 Froix Jun 1981
4281284 Stutz et al. Jul 1981
4332853 Hornbeck et al. Jun 1982
4356228 Kobayashi et al. Oct 1982
4375493 George et al. Mar 1983
4378322 Atterbury Mar 1983
4379098 Gumienny Apr 1983
4383942 Davenport May 1983
4388422 Gerteisen et al. Jun 1983
4389453 Kitanaka et al. Jun 1983
4399084 Sagawa et al. Aug 1983
4404125 Abolins et al. Sep 1983
4429216 Brigham Jan 1984
4442139 Brigham Apr 1984
4461860 Vives Jul 1984
4474685 Annis Oct 1984
4495017 Abe et al. Jan 1985
4542056 Anglin et al. Sep 1985
Foreign Referenced Citations (2)
Number Date Country
3236447 Apr 1984 DEX
56-27344 Mar 1981 JPX
Non-Patent Literature Citations (11)
Entry
Modern Plastics, May 1982, p. 68--"Conductive Fiber Mats as EMI Shield for SMC" Quick & Mate.
Plastics Compounding, Jan.-Feb. 1980, "Electrically Conductive Fillers and Reinforcements", p. 19.
Industrial Research & Development, Jun. 1982, "EMI Shielding can be made of Conductive Plastics", Simon.
Plastics Technology, Sep. 1983, p. 59: EMI/RFI Shield Deadline Looms: Here's Composite Source Guide--Kirkland.
Advanced Ryton Composites (published Jan. 1984) by Phillips Petroleum Company.
Modern Plastics, Oct. 1984, p. 62, "Conductive Fillers Yield EMI Shielding Gains".
LNP Corporation "Electrically Conductive Plastics", Materials Engineering, Feb. 1980, Crosby & Theberge.
Dow: Formable Metallized Plastic: Form No. 500-930-84.
Plastics Engineering, Jun. 1981, p. 29: Formulating Cost-effective Conductive Composites, Fowler et al.
Electrafil-Electrically Conductive Thermoplastics, Wilson-Fiberfil Internat., Dart & Kraft .COPYRGT.Dart 1983.
Metalloplastics, Don Davenport, PhD, San Ramon, Calif. 94583.