Patent Application
20220025118
The present invention relates to a moulding composition comprising polyether block amide (PEBA), to a moulded article produced therefrom and to the use thereof.
Polyether block amides (PEBA) are block copolymers which are obtained by polycondensation of (oligo)polyamides, in particular acid-regulated polyamides, with alcohol-terminated or amino-terminated polyethers. Acid-regulated polyamides have carboxylic acid end groups in excess. Those skilled in the art refer to the polyamide blocks as hard blocks and the polyether blocks as soft blocks. The production thereof is known in principle. DE2712987A1 (U.S. Pat. No. 4,207,410) describes polyamide elastomers of this type, composed of lactams containing 10-12 carbon atoms, dicarboxylic acids and polyether diols. The products obtainable according to this document are distinguished by long-lasting flexibility and ductility even at low temperatures, but they are already cloudy to opaque in mouldings of moderate layer thickness and, on longer-term storage at room temperature, are conspicuous due to surface deposits having a mildew-like appearance. Similarly structured polyamide elastomers, assembled from diamines containing 6-20 carbon atoms, aliphatic or aromatic dicarboxylic acids and polyether diols, are known from EP0095893. Distinctive properties are increased heat distortion resistance and flexibility. No data regarding translucency of the mouldings and formation of deposits can be gathered from this document.
PA 11-based and PA 12-based PEBA moulding compositions also stand out for negative reasons due to an opaque, cloudy appearance and formation of surface deposits. It was further observed that they have a high level of deposits with simultaneously low translucency. Current moulding compositions are therefore of little suitabllty for applications.
To this end, it was an object of the present invention to provide suitable moulding compositions, which are associated with a high translucency with low haze and freedom from deposits even over a relatively long period of time.
This object was achieved with a moulding composition comprising polyether block amide (PEBA) based on a subunit 1, composed of at least one linear aliphatic diamine containing 5 to 15 carbon atoms, preferably 6 to 12 carbon atoms and at least one linear aliphatic dicarboxylic acid containing 8 to 16 carbon atoms, preferably 8 to 14 carbon atoms, and on a subunit 2, composed of at least one polyether diol containing at least 3 carbon atoms per ether oxygen and primary OH groups at the chain ends. The sum total of the carbon atoms from diamine and dicarboxylic acid is an odd number and is 19 or 21 carbon atoms: the number-average molar mass of the subunit 2 is 200 to 900 g/mol. Preferably, the molar mass of the subunit is 400 to 700 g/mol. Subunit 1 therefore forms the part generally referred to as the hard block, subunit 2 forms the soft block. The term “linear” is to be understood as meaning that the carbon chains are unbranched.
In one preferred embodiment, the number-average molar mass of the subunit 1 is 250 to 4500 g/mol, more preferably 400 to 2500 g/mol, even more preferably 400 to 2000 g/mol, most preferably 500 to 1800 g/mol. This leads to a material with higher translucency and simultaneously reduced formation of deposits.
The polyether diol of the PEBA is preferably selected from polypropane-1,3-diol, polytetramethylene glycol and mixtures thereof.
The sum total of the carbon atoms from diamine and dicarboxylic acid in the PEBA is an odd number. It is 19 or 21. Preferably, the sum total is 19.
It is furthermore preferable for the number of carbon atoms in the diamine to be an even number and for the number of carbon atoms in the acid to be an odd number.
Suitable polyamides of subunit 1 are selected, by way of example, from 5,14, 5,16, 6,13, 6,15, 7,12, 7,14, 8,11, 8,13, 9,10, 9,12, 10,9, 10,11, 11,8, 11,10, 12,7, 12,9, 13,6, 13,8. It is furthermore preferable for the subunit 1 to be selected from nylon-6,13, nylon-10,9 and nylon-12,9.
The invention further provides a moulded article produced from the moulding composition according to the invention. The moulded article is preferably a moulding, a film, a bristle, a fibre or a foam. The moulded article may for example be produced by compression-moulding, foaming, extrusion, coextrusion, blow moulding, 3D blow moulding, coextrusion blow moulding, coextrusion 3D blow moulding, coextrusion suction blow moulding or injection moulding. Processes of this kind are known to those skilled in the art.
The invention further provides the use of the moulded article according to the invention, which may for example be used as a fibre composite component, shoe sole, top sheets for skis or snowboards, line for media, spectacle frame, design article, sealing material, body protection, insulating material or housing part provided with a film.
The diamine, 10% of the mass thereof of deionized (DI) water, dicarboxylic acid and the polyether diol polytetrahydrofuran (PTHF) are initially charged successively at below 60° C. in the feed tank of a 100-1 double-tank polycondensatlon installation, provided with an anchor stirrer. PTHF forms the subunit 2. Based on the polyether diol, 0.1% Irganox® 1098 (BASF SE) is added as process stabilizer. Based on the total solids content, 0.3% 50%-strength hypophosphorous acid is added as catalyst. After repeated pressure inertization with N2, the tank contents are heated to 180° C.-190° C.; at 160° C. the stirrer is engaged. The starting materials are stirred for 1 hour and are thereafter transferred into the polycondensation reactor, provided with a helical stirrer and torque recorder. After pressure has been equalized between the two vessels, the reactor valve is closed and the contents are brought up to 245° C. within 6 hours under stirring at 25 rpm. Upon reaching 21 bar autogenous pressure—normally between 210° C. and 225° C. internal temperature—a two-hour pressure maintenance stage is observed, after which depressurization is performed continuously to atmospheric pressure under further raising of the temperature. After 3-4 hours at atmospheric pressure, reduced pressure is applied within 5 hours until a final reduced pressure of 40-60 mbar is reached. Further stirring is performed under these conditions until the desired final torque is reached. The melt is extruded into a water bath, pelletized and dried at 70° C.-90° C. in a tumble dryer to a water content <0.1%.
Examples 1 to 14, 51-55 and 58-80:100:103: Examples 15-35, 48-50 and 58-57:100:102; Examples 38-40: 100:105.
Subsequent to drying according to the process described in DE4301801A1 in solid phase at 130° C.-135° C., 0.95 wt. % of a stabilizer mixture, based on the total weight of PEBA and stabilizer, was added to some of the PEBA (hereinafter identified with “st”).
The PEBA prepared are summarized in Table 1 which follows. The molar mass of the subunit 1 results from the molar ratio of the dicarboxylic acid used and the diamine.
The PEBA prepared were investigated in respect of appearance of the extrudate, relative viscosity ηrel and melting point Tm (cf. Table 2). Appearance of the extrudate: visual inspection. Viscosity: ISO 307. Tm: DSC, second heating step to ISO 11357.
Commercially available PEBA based on PA 12 or PA 11 were also investigated. These are available from Evonik (Vestamid®) or Arkema (PEBAX®).
Injection-moulded plaques measuring 60 mm×80 mm×2 mm were produced from the polyether block amides as test specimens. The formation of deposits was ascertained after the test specimen had been stored for a test period of 10 days in a closed vessel with water vapour saturation at 75° C. Deposits were assessed visually using a four-point scale (from 0-3, where 0=free of deposits and 3=subject to heavy deposits).
For some specimens, no deposit tests were performed. In these cases, no entry is made in the following tables.
The translucency of the aforementioned test specimens was ascertained visually. In this case the following evaluation was used (in decreasing order of translucency):
0=translucent ++
1=translucent +
2=translucent 0
3=opaque/milky, translucent 0
4=opaque/milky, translucent −
5=milky-white
The haze value specifies the illumination through an article in transmitted light. The haze value is measured here by means of the 60×60×2 mm plaques to ASTM standard D 1003 using a Konica-Minolta CM-3800d. Where the specimen was opaque/milky or even milky-white, determination of the haze value was usually dispensed with.
Despite some good deposit test results, the specimens of PEBA 6.10 exhibit insufficiently low translucency.
PEBA 6.13 satisfies both the deposit test and the requirements on translucency.
The test specimens of PEBA 10.10 and PEBA 7.13 are opaque/milky with low translucency or (Example 60) have a certain transparency with increased deposits.
Although both the non-stabilized and the stabilized PEBA 10.13 do exhibit a moderate to good translucency, these specimens do not pass the deposit test.
PEBA 10.9 exhibits few to no deposits whatsoever and a good to moderate translucency.
PEBA 6.13, having a polyether subunit the molar mass of which is 1000, leads to milky-white test specimens. In contrast, PEBA 6.13 specimens having a polyether subunit of 650 g/mol exhibit moderate to good translucency (Experiments 7 to 14).
The deposit test shows a moderate result for commercially available PEBA based on PA 11 or PA 12. The translucency in most cases turns out to be very low.
Specimens containing PEBA 6.9, PEBA 7.10 and 5.12 exhibit opaque/milky to milky-white test specimens.
Test specimens containing PEBA 7.12, 7.14 or 12.9 exhibit few to no deposits and high transparency.
| Number | Date | Country | Kind |
|---|---|---|---|
| 18213932.9 | Dec 2018 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2019/077424 | 10/9/2019 | WO | 00 |