The present disclosure relates to the technical field of molding crystalline plastics and more particularly to a molding method of crystalline plastics, and the crystalline plastics can be molded in one shot to achieve the effects of lowering the equipment and labor costs of molding, accelerating the molding process, and improving the yield of molding.
In general, containers are made of a crystalline material such as polythene (PE), polypropylene (PP), polyethylene terephthalate (PET), polyphenylene sulphide (PS), etc., wherein PET with the advantages of excellent gas barrier property, pressure resistance, creep resistance, impact resistance, transparency, and surface gloss, the features of odorlessness, fragrance retention, and the compliance with the safety of food hygiene. In the meantime, PET comes with a beautiful appearance and features easy molding, so that it is widely used in food containers such as PET bottles.
PET is a high molecular weight polymer, and the most important feature resides on its molecular weight which is the number of uniform molecules in a PET molecular link. The greater the number of molecular links, the better the physical property of the PET. The PET is a crystalline resin with a specific gravity of approximately 1.4, and a melting point of 245° C., a molding temperature within a range of 290° C.˜315° C. In
In a conventional method of crystalline plastic molding, the mold requires the use of the ice water system for cooling to decrease the temperature to room temperature quickly in order to perform the demolding process and the crystallizer to increase the temperature in order to perform the crystallization and molding. Since the mold design of the ice water system incurs high level of difficulty and construction cost, and also requires building an additional crystallizer, and thus not occupying much space only, but also increasing the total equipment cost greatly. In addition, the process time is increased because it is necessary to increase and decrease the temperature repeatedly, and it may even produce defectives, so that the surface of the finished product of the molded body is whiten to destroy the beautiful appearance of the product.
In other words, the conventional crystalline plastic molding requires the repeated heating and cooling process and the demolding during the manufacturing process, so that there are issues of high equipment and labor costs, long manufacturing time, and high defective rate, and how to overcome the aforementioned problems of injection molding and crystallization is a main subject for related manufacturers as well as the present disclosure.
In view of the aforementioned problems of the conventional crystalline plastics, the discloser of the present disclosure based on years of experience in the related industry to conduct extensive research and experiment according to the technical development requirements in recent years, and finally developed a molding method of crystalline plastics to overcome the drawback and inconvenience of the high equipment and labor costs and the long manufacturing time caused by the repeated heating and cooling processes.
Therefore, it is the primary objective of the present disclosure to provide a molding method of crystalline plastics capable of simplifying the processing procedure, shortening the total manufacturing time, and improving the molding yield effectively.
A secondary objective of the present disclosure is to disclose a molding method of crystalline plastics capable of reducing the equipment installation cost and further saving the equipment space and labor.
To achieve the aforementioned and other objectives, the present disclosure discloses a molding method of crystalline plastics, and the method comprises the steps of:
providing a raw material;
performing a thermoforming step that heats the raw material to a molding temperature and forms a product in a mold;
performing a cooling crystallization step that cools the same mold to a crystallization temperature after molding to crystallize and shape the product that still has not been crystallized yet; and
performing a cooling and demolding step that further cools the same mold to room temperature after the cooling crystallization of the product, so as to facilitate demolding after molding.
By the aforementioned technical measure, the molding method of crystalline plastics of the present disclosure uses a staged cooling technology to achieve the effects of cooling crystallization and cooling demolding, so that this method does not require an expensive cooling system or an additional crystallizer, and the method can improve the process yield, lower the required equipment and labor costs and expenses, and reduce the total process time significantly to increase the added values and economic benefits.
The present disclosure achieves the aforementioned objectives and effects by the following technical measures:
The raw material is a PET preform with a thermoforming temperature of 290° C.˜315° C. and a crystallization temperature of 120° C.˜220° C., and the crystallization temperature is maintained for 1˜10 minutes.
To make it easier for the examiner to understand the structure, and overall operation of this invention, the specification accompanied by the drawings is described as follows, and persons having ordinary skills in the art can implement this disclosure accordingly.
In the description and drawings of this disclosure of a molding method of crystalline plastics in accordance with an exemplary example, the terms “front and rear”, “left and right”, “top and bottom”, “upper part and lower part”, and “horizontal and vertical” are provided for reference and used to describe and illustrate the present disclosure only, but not intended for limiting the scope of the present disclosure or limiting any position, space or direction of the components. It is noteworthy that the dimensions specified in the drawings and specification can be changed according to the design requirement of the exemplary examples of the present disclosure without departing from the scope of the claims of this disclosure.
With reference to
The detailed specification of the present disclosure is in accordance with
providing a raw material such as a perform being molded beforehand;
performing a thermoforming step that heats the preform to a molding temperature (such as 290° C.˜315° C.) and uses a bottle blowing technology to expand the preform inside the same mold into a bottle body of a predetermined size;
performing a cooling crystallization step that cools the same mold to a crystallization temperature (such as 120° C.˜220° C.) by a temperature controller installed in the mold after the preform is blown and molded into a bottle body and maintains the crystallization temperature for 1˜10 minutes, so as to crystallize and shape the bottle body that has not been crystallized yet; and
performing a cooling and demolding step that further cools the same mold to room temperature (such as 20° C.˜30° C.) after the cooling crystallization of the bottle body, so as to facilitate demolding the molded bottle body to produce a complete bottle body.
From the description above, the molding method of crystalline plastics of the present disclosure uses a staged cooling technology to achieve the effects of cooling crystallization and cooling and demolding. The molding method does not require any expensive cooling system or additional crystallizer to lower the equipment cost, and the method can simplify the manufacturing process to save labor and process time, while improving the process yield, performance, efficiency and product quality, saving spaces, improving the raw material, finished goods and capital turnover rates, and increasing profitability and competitiveness significantly. This method surely provides economic benefits for industrial applications.
In summation of the description above, the present disclosure is an innovative invention, not just solving the problems of the prior art only, but also making significant improvements, and the invention is novel, inventive, and in compliance with patent application requirements, and thus is duly filed for patent application.