Claims
- 1. A porous, open-pore, hardened, plastic composition suitable as a replacement for plaster for use as a mold in shaping a ceramic article by any of various ceramic shaping methods in which said mold has ceramic body formation properties similar to those of plaster by virtue of the capillary action of the open pores of said mold, said porous, open-pore, hardened, plastic composition having been prepared by forming a water-in-oil emulsion comprising an aqueous phase dispersed in a continuous phase comprising (a) at least one unsaturated polyester resin dissolved in at least one hardenable compound containing at least one ethylenically unsaturated group and (b) at least one emulsifying agent; incorporating in said water-in-oil emulsion about 2-12% by weight of said hardenable compound of a material effective in accelerating the formation of a ceramic article to be shaped in said mold, said material being selected from sodium disilicate and disodium tetraborate; controlling the aquoeus phase/oil phase ratio so that said porous, open-pore, hardend, plastic composition has an open-pore volume, which is refillable with water, of about 10-60% of the total volume of said porous, open-pore, hardened, plastic composition; and subjecting the hardenable compound of the continuous oil phase to hardening without breaking the water-in-oil emulsion; and then drying to obtain said porous, open-pore, hardened, plastic composition.
- 2. A porous, open-pore, hardened, plastic composition according to claim 1 in which about 4-8% of said material is incorporated in said water-in-oil emulsion.
- 3. A porous, open-pore, hardened, plastic composition according to claim 1 in which the unsaturated polyester resin is made from (a) a polybasic carbonic acid or its anhydride selected from maleic, fumaric adipic, sebacic, phthalic, isophthalic and terephthalic, and (b) a multivalent alcohol selected from ethylene glycol, 1,3-butylene glycol, 1,2-propylene glycol and neopentyl glycol.
- 4. A porous, open-pore, hardened, plastic composition according to claim 1 in which the hardenable compound is selected from styrene, .alpha.-methylstyrene, phthalic acid allyl esters, and esters of methacrylic and acrylic acids.
- 5. A porous, open-pore, hardened, plastic composition according to claim 2 in which the polyester resin is made from maleic anhydride and glycol and the hardenable compound is a mixture of styrene and methyl methacrylate.
- 6. A water-in-oil emulsion for forming a porous, open-pore, hardened, plastic composition suitable as a replacement for plaster for use as a mold in shaping a ceramic article by any of various shaping methods in which said mold has ceramic body formation properties similar to those of plaster by virtue of the capillary action of the open pores of said mold, comprising (1) an aqueous phase dispersed in a continuous oil phase comprising (a) at least one unsaturated polyester resin dissolve in at least one hardenable compound containing at least one ethylenically unsaturated group and (b) at least one emulsifying agent; and (2) about 2-12% by weight of said hardenable compound of a material selected from sodium disilicate and disodium tetraborate effective in accelerating the formation of a ceramic article to be shaped in said mold.
- 7. A porous, open-pore, hardened, plastic composition prepared from the water-in-oil emulsion according to claim 6.
Priority Claims (2)
Number |
Date |
Country |
Kind |
3345188 |
Dec 1983 |
DEX |
|
3409278 |
Mar 1984 |
DEX |
|
Parent Case Info
This application is a division of application Ser. No. 054,682 filed May 22, 1987 which, in turn, is a continuation of application Ser. No. 764,851 filed Aug. 12, 1985 now abandoned.
US Referenced Citations (12)
Foreign Referenced Citations (2)
Number |
Date |
Country |
1284890 |
Aug 1972 |
GBX |
1458203 |
Dec 1976 |
GBX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
54682 |
May 1987 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
764851 |
Aug 1985 |
|