1. Technical Field
The present disclosure relates to a molding roller, an apparatus and a method for manufacturing the molding roller.
2. Description of Related Art
Optical films include a number of micro structures. One method for forming the micro structures is a roll forming process using a metallic roller. The metallic roller has a circumferential surface including molding patterns for forming the micro structures. The molding pattern is formed by a laser knife. However, it is difficult to machine the molding patterns on a curved surface of the metallic roller, therefore, the machining efficiency is relatively low.
Therefore, it is desirable to provide a molding roller, an apparatus and a method for manufacturing the molding roller that can overcome the above-mentioned limitations.
Many aspects of the embodiments should be better understood with reference to the following drawings. The components in the drawings are not necessarily drawn to scale, the emphasis instead being placed upon clearly illustrating the principles of the present disclosure. Moreover, in the drawings, like reference numerals designate corresponding parts throughout the several views.
The molding film 20 is wound around and fixed to the circumferential surface 101 of the main body 10 via the adhesive glue 102. The molding film 20 includes a molding surface 201 opposite to the main body 10. The molding surface 201 includes a number of molding patterns 202. In the first embodiment, the molding patterns 202 are micro striped grooves. In other embodiments, the molding patterns 202 also can be micro-dots, striped protrusions or micro domes.
The molding film 20 is made of flexible polymer material consisting of polymer resin and a number of silica nanoparticles formed in polymer grids of the polymer resin. In the first embodiment, the polymer resin is polydimethylsiloxane (PDMS) resin, and the silica nanoparticles are formed by sol-gel method.
The film chemical treatment device 310 is used for chemically processing an original film 20b to obtain a preprocessed molding film 20a. In this embodiment, the original film 20b is made of PDMS resin, the film chemical treatment device 310 is used for forming a number of silica nanoparticles in the polymer grids of the PDMS resin. The film chemical treatment device 310 includes a receiving chamber 311 and a vacuum chamber 313. A reaction liquid 312 (such as tetraethoxy silane, TEOS) is received in the receiving chamber 311. The original film 20b is immersed in the reaction liquid 312 for a first predetermined period until the reaction liquid 312 penetrates the original film 20b, then the original film 20b is taken out from the receiving chamber 311, and the reaction liquid 312 covered on the original film 20b is removed.
A first container 314 and a second container 315 are received in the vacuum chamber 313. The first container 314 is used for receiving an alkaline catalyst 313a, and the second container 315 is used for receiving deionized water 313b. In this embodiment, the alkaline catalyst 313a is 95% 2-amino-2-methyl-propanol solution (AMP-95), and the volume ratio of the alkaline catalyst 313a to the deionized water 313b is 1:5. The penetrated original film 20b is received in the vacuum chamber 313, and is positioned upon the first container 314 and the second container 315. When the temperature of the vacuum chamber 313 is gradually increased, the alkaline catalyst 313a and the deionized water 313b are vaporized to arrive at the penetrated original film 20b, so as to promote the original film 20b condensation react with the reaction liquid 312, and the growth rate of the silica nanoparticles is increased to obtain the preprocessed molding film 20a. In this embodiment, the PH value of the alkaline catalyst 313a is 8-10.
The loading plate 320 is used for loading the preprocessed molding film 20a. The preprocessed molding film 20a has a planar preprocessed surface 201a opposite to the loading plate 320. The loading plate 320 has a planar loading surface 321. Two opposite ends of the preprocessed molding film 20a are fixed to the planar loading surface 321 using an adhesive glue (not shown) or other fixing means.
The processing device 330 is used for forming a number of molding patterns 202 on the planar preprocessed molding surface 201a, and thus the molding film 20 having the molding surface 201 are obtained. In this embodiment, the processing device 330 includes a laser emitter 331, a reflector 332, and a converging lens 333. The laser emitter 331 is used for emitting laser rays. The transmitting direction of the laser rays is substantially parallel to the preprocessed molding surface 201a. The reflector 332 is used for changing the transmitting direction of the laser rays and reflecting the laser rays to the converging lens 333. The converging lens 333 converges the laser rays to the preprocessed molding surface 201a. In other embodiments, the reflector 332 and the converging lens 333 can be omitted, and the transmitting direction of the laser rays should be substantially perpendicular to the preprocessed molding surface 201a. If the molding patterns are V-shaped grooves, and the processing device 330 may include a diamond knife having a V-shaped blade.
The mounting device 340 is used for mounting the molding film 20 on the circumferential surface 101 of the main body 10, and includes an auxiliary roller 341 having a smooth rolling surface 342. The auxiliary roller 341 is at a predetermined distance from the main body 10 to form a molding channel 343. The auxiliary roller 341 and the main body 10 are rotated in opposite directions of each other. The circumferential surface 101 is coated with the adhesive glue 102. An end of the molding film 20 is adhered on the circumferential surface 101, then the main body 10 and the auxiliary roller 341 are rotated to make the molding film 20 pass through the molding channel 343, and thus the molding film 20 is wound around and fixed to the circumferential surface 101 via the adhesive glue 102.
The cutting device 350 cuts the molding film 20.
In step S1, a number of silica nanoparticles are formed in the polymer grids of the original molding film 20b using the film chemical treatment device 310 to obtain the preprocessed molding film 20a.
In step S2, the preprocessed molding film 20a is positioned on the loading plate 320.
In step S3, the molding patterns 202 are formed on the preprocessed molding surface 201a using the processing device 330 to obtain the molding surface 201 with the molding film 20.
In step S4, the molding film 20 is separated from the loading plate 320 and is wound around and fixed to the circumferential surface 101 of the main body 10 using the mounting device 340.
In step S5, the molding film 20 is cut.
In other embodiments, the step S4 and the step S5 also can be interchanged.
In step S11, the original film 20b is immersed in the reaction liquid for a predetermined period until the reaction liquid 312 penetrates the original film 20b.
In step S12, the penetrated original film 20b is received in the vacuum chamber 313, and is positioned above the alkaline catalyst 313a and the deionized water 313b.
In step S13, the temperature of the vacuum chamber 313 is gradually increased, the alkaline catalyst 313a and the deionized water 313b are vaporized to arrive at the original film 20b, so as to promote the original film 20b condensation react with the reaction liquid 312, and the growth rate of the silica nanoparticles is increased to obtain the preprocessed molding film 20a.
In step S41, the circumferential surface 101 is coated with the adhesive glue 102.
In step S42, an end of the molding film 20 is adhered on the circumferential surface 101, and the molding surface 201 faces the auxiliary roller 341.
In step S43, the main body 10 and the auxiliary roller 341 are rotated to make the molding film 20 pass through the molding channel 343 until the molding film 20 is wound around the circumferential surface 101.
By employing the apparatus 300 and the above described method, it is easier for the processing device 330 to machine the molding patterns 202 on the planar preprocessed molding surface 201a of the preprocessed molding film 20a relative to on a curved surface of the metallic roller in the related art, therefore, the machining efficiency is improved.
It will be understood that the above particular embodiments are shown and described by way of illustration only. The principles and the features of the present disclosure may be employed in various and numerous embodiments thereof without departing from the scope of the disclosure as claimed. The above-described embodiments illustrate the scope of the disclosure but do not restrict the scope of the disclosure.