MOLTEN METAL ROTOR WITH HARDENED TOP

Abstract
Embodiments of the invention are directed to a rotor for a molten metal pump and a molten metal pump including the rotor. The rotor has a main body and a top comprised of a material that is at least twice as hard as the main body. The top, among other things, may form a first portion of each rotor blade wherein the first portion directs molten metal into a pump chamber or other structure in which the rotor is mounted.
Description
FIELD OF THE INVENTION

The present invention relates to a rotor for pumping molten metal, the rotor having a hardened top wherein at least some of the ceramic top preferably forms part of one or more rotor blades. The purpose of the hardened top is to decrease wear on the portions of the rotor that are struck by dross or other hard objects found in molten metal.


BACKGROUND OF THE INVENTION

As used herein, the term “molten metal” means any metal or combination of metals in liquid form, such as aluminum, copper, iron, zinc and alloys thereof. The term “gas” means any gas or combination of gases, including argon, nitrogen, chlorine, fluorine, freon, and helium, that are released into molten metal.


Known molten-metal pumps include a pump base (also called a housing or casing), one or more inlets (an inlet being an opening in the housing to allow molten metal to enter a pump chamber), a pump chamber, which is an open area formed within the housing, and a discharge, which is a channel or conduit of any structure or type communicating with the pump chamber (in an axial pump the chamber and discharge may be the same structure or different areas of the same structure) leading from the pump chamber to an outlet, which is an opening formed in the exterior of the housing through which molten metal exits the casing. An impeller, also called a rotor, is mounted in the pump chamber and is connected to a drive system. The drive system is typically an impeller shaft connected to one end of a drive shaft, the other end of the drive shaft being connected to a motor. Often, the impeller shaft is comprised of graphite, the motor shaft is comprised of steel, and the two are connected by a coupling. As the motor turns the drive shaft, the drive shaft turns the impeller and the impeller pushes molten metal out of the pump chamber, through the discharge, out of the outlet and into the molten metal bath. Most molten metal pumps are gravity fed, wherein gravity forces molten metal through the inlet and into the pump chamber as the impeller pushes molten metal out of the pump chamber.


A number of submersible pumps used to pump molten metal (referred to herein as molten metal pumps) are known in the art. For example, U.S. Pat. No. 2,948,524 to Sweeney et al., U.S. Pat. No. 4,169,584 to Mangalick, U.S. Pat. No. 5,203,681 to Cooper, U.S. Pat. No. 6,093,000 to Cooper and U.S. Pat. No. 6,123,523 to Cooper, and U.S. Pat. No. 6,303,074 to Cooper, all disclose molten metal pumps. The disclosures of the patents to Cooper noted above are incorporated herein by reference, as are U.S. Pat. Nos. 7,402,276 and 7,507,367. The term submersible means that when the pump is in use, its base is at least partially submerged in a bath of molten metal.


Three basic types of pumps for pumping molten metal, such as molten aluminum, are utilized: circulation pumps, transfer pumps and gas-release pumps. Circulation pumps are used to circulate the molten metal within a bath, thereby generally equalizing the temperature of the molten metal. Most often, circulation pumps are used in a reverbatory furnace having an external well. The well is usually an extension of the charging well where scrap metal is charged (i.e., added).


Transfer pumps are generally used to transfer molten metal from the external well of a reverbatory furnace to a different location such as a ladle or another furnace.


Gas-release pumps, such as gas-injection pumps, circulate molten metal while releasing a gas into the molten metal. In the purification of molten metals, particularly aluminum, it is frequently desired to remove dissolved gases such as hydrogen, or dissolved metals, such as magnesium, from the molten metal. As is known by those skilled in the art, the removing of dissolved gas is known as “degassing” while the removal of magnesium is known as “demagging.” Gas-release pumps may be used for either of these purposes or for any other application for which it is desirable to introduce gas into molten metal. Gas-release pumps generally include a gas-transfer conduit having a first end that is connected to a gas source and a second submerged in the molten metal bath. Gas is introduced into the first end and is released from the second end into the molten metal. The gas may be released downstream of the pump chamber into either the pump discharge or a metal-transfer conduit extending from the discharge, or into a stream of molten metal exiting either the discharge or the metal-transfer conduit. Alternatively, gas may be released into the pump chamber or upstream of the pump chamber at a position where it enters the pump chamber. A system for releasing gas into a pump chamber is disclosed in U.S. Pat. No. 6,123,523 to Cooper. Furthermore, gas may be released into a stream of molten metal passing through a discharge or metal-transfer conduit wherein the position of a gas-release opening in the metal-transfer conduit enables pressure from the molten metal stream to assist in drawing gas into the molten metal stream. Such a structure and method is disclosed in a copending application entitled “System for Releasing Gas Into Molten Metal,” invented by Paul V. Cooper, and filed on Feb. 4, 2004, the disclosure of which is incorporated herein by reference.


When a conventional molten metal pump is operated, the rotor rotates within the pump housing and the pump housing, inlet and pump chamber remain stationary relative to the rotor, i.e., they do not rotate. A problem with such molten metal pumps is that the molten metal in which it operates includes solid particles, such as dross and brick. As the rotor rotates molten metal including the solid particles enters the pump chamber through the inlet. A solid particle may lodge between the moving rotor and the stationary inlet, potentially jamming the rotor and potentially damaging one or more of the pump components, such as the rotor or rotor shaft of the pump.


Many attempts have been made to solve this problem, including the use of filters or disks to prevent solid particles from entering the inlet and the use of a non-volute pump chamber to increase the space between the inlet and rotor to allow solid pieces to pass into the pump chamber without jamming, where they can be pushed through the discharge by the action of the rotor.


Gas-release pumps generally include a gas-transfer conduit having a first end that is connected to a gas source and a second end submerged in the molten metal bath. Gas is introduced into the first end and is released from the second end into the molten metal. The gas may be released downstream of the pump chamber into either the pump discharge or a metal-transfer conduit extending from the discharge, or into a stream of molten metal exiting either the discharge or the metal-transfer conduit. Alternatively, gas may be released into the pump chamber or upstream of the pump chamber at a position where molten metal enters the pump chamber.


The materials forming the components that contact the molten metal bath should remain relatively stable in the bath. Structural refractory materials, such as graphite or ceramics, that are resistant to disintegration by corrosive attack from the molten metal may be used. As used herein “ceramics” or “ceramic” refers to any oxidized metal (including silicon) or carbon-based material, excluding graphite, capable of being used in the environment of a molten metal bath. “Graphite” means any type of graphite, whether or not chemically treated. Graphite is particularly suitable for being formed into pump components because it is (a) soft and relatively easy to machine, (b) not as brittle as ceramics and less prone to breakage, and (c) less expensive than ceramics.


SUMMARY OF THE INVENTION

The present invention relates to rotors used for pumping molten metal wherein the rotor has a hardened top to alleviate damage to the rotor caused by dross or other hard particles striking the rotor as molten metal enters the chamber of a molten metal pump in which the rotor is retained. The top is at least twice as hard as the body portion of the rotor, and the top preferably covers the entire top surface of the rotor including the tops of the rotor blades.


In one embodiment, the hardened top extends to include all or part of the surface of the rotor blades that move molten metal into the pump chamber or that push molten metal outward towards the wall of the pump chamber. Aspects of the invention can be utilized on any molten metal rotor design.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 shows a front, perspective view of a rotor according to the invention.



FIG. 2 shows a top view of the rotor of FIG. 1.



FIG. 3 shows a perspective, side view of the rotor of FIG. 1 with the top not assembled to the body.



FIG. 4 shows a perspective, side view of the rotor of FIG. 1 with the top assembled to the body.





DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

As used herein the relative hardness of materials is determined by the MOHS hardness scale. On the MOHS hardness scale, treated graphite may have a hardness between 1.5 and 2.5, whereas silicon carbide generally has a hardness of 9-10.


Turning now to the drawings, where the purpose is to describe a preferred embodiment of the invention and not to limit same, systems and devices according to the invention will be described.



FIGS. 1-4 show one preferred rotor according to aspects of the invention. Rotor 100 as shown preferably has three identical rotor blades (also called “vanes” herein) 102. As used herein, a rotor blade (or “vane”) is a structure separate from and spaced from other rotor blades. In rotor 100 each blade is dual flow, meaning that it has a first portion 102A that directs molten metal either downward or upward (if the rotor is used on a bottom feed pump) towards a second portion 102B that directs molten metal outward.


A rotor according to aspects of the invention has a body (or body portion) 101 with a hardened top surface 106. Rotor 100 may have a flow blocking and bearing plate 110. As shown, flow blocking and bearing plate 110 is cemented to the bottom 120 of rotor 100. If rotor 100 is used on a bottom feed pump, the flow blocking and bearing plate 110 may be at the top of the rotor (in essence, the rotor would be turned upside down, with the blades at the bottom, but the rotor shaft attachment mechanism would still be at the top). The flow blocking and bearing plate 110 is preferably comprised of a hard, wear-resistant material, such as silicon carbide. Alternatively, a rotor according to the invention may not have a flow blocking and bearing plate.


Rotor 100 further includes a connective portion 112, which is preferably a threaded bore, but can be any structure capable of drivingly engaging a rotor shaft (not shown). It is most preferred that the outer surface of the end of the rotor shaft that is received in portion 112 has tapered threads and connective portion 112 be threaded to receive the tapered threads.


The preferred dimensions of rotor 100 will depend upon the size of the pump chamber or other structure in which it is received.


Preferably each vane 102 has the same configuration so only one vane 102 shall be described. Each vane 102 preferably includes a horizontally-oriented first portion 102A and a vertically-oriented second portion 102B. The respective vertical and horizontal orientation of the portions described herein is in reference to a rotor positioned in a standard pump having an input port in its top surface. The invention, however, covers any rotor for use in a molten-metal pumping application, whether the flow of molten metal is first contacting the rotor at the top or bottom or both. It will be therefore understood that the terms “horizontal” and “vertical” refer to the rotor as shown in the orientation in FIGS. 1-4.


Top surface 106 is preferably flush with a pump chamber inlet, if used with a pump chamber.


Section 102A preferably has a leading edge 116 and an angled surface (or first surface) 118. Surface 118 is angled (as used herein the term angled refers to both a substantially planar surface, or a curved surface, or a multifaceted surface) such that, as rotor 100 turns (as shown it turns in a clockwise direction) surface 118 directs molten metal towards second portion 102B. Any surface that functions to direct molten metal towards second portion 102B can be used, but it is preferred that surface 118 is substantially planar and formed at a 30°-60°, and most preferably, a 45° angle.


Portion 102B, which is preferably vertical (but can be angled or curved), extends from the bottom of section 102A to the top of base (or bottom) 120. Portion 102B has a leading face (or second surface) 122. Leading face 122 is preferably planar and vertical, although it can be of any configuration that directs molten metal outward, such as towards the wall of a pump chamber or other structure in which the rotor 100 is housed.


A recess 130 is formed in top portion 104 and preferably extends from top surface 106 to at least as far as the trailing face 132 of second portion 102B. As shown, recess 130 begins at a position on surface 106 slightly forward of face 132 and terminates at a position even with trailing face 132. The purpose of recess 130 is to reduce the area of top surface 106, thereby creating a larger opening for more molten metal to enter into the rotor 100 thus enabling rotor 100 to move more molten metal per rotor revolution.


The hardened top 104 is shown in FIGS. 1-4. The hardened top (or entrance to the rotor, because what is shown as the top in the Figures may be at the bottom on a bottom-feed pump or on both the top and bottom if no flow blocking and bearing plate is used) preferably is at least twice as hard as the body portion 101, or 2-3 times harder than the body portion 101, or 2-4 times harder than the body portion 101, or 2-5 times harder than the body portion 101. In one preferred embodiment, the body portion 101 is graphite and the top 104 is silicon carbide. At least top surface 106 includes the harder material of the hardened top 104, and as shown the hardened top includes the first portion 102A of each rotor blade 102, which includes surface 118. Additionally, it is preferred that the hardened top 104 include a part of second portion 102B (and surface 122) immediately beneath surface 118, and recess 130, and a part of trailing face 132 immediately beneath trailing face 132.



FIG. 3 shows hardened top 104 prior to being assembled to the body portion. In order to secure the top 104 and body portion, it is preferred that portions of the corners of each blade section on body 101 be cut out to create recesses or gaps 150 and that the top portion 106 has sections 152 designed to fill gaps 150 when cemented in place. The mating of sections 152 and gaps 150 helps secure the top 104 and body portion to alleviate the possibility that they will come apart during use.


Additionally, gaps 150 may have openings 151 that mate with pins (not shown) in sections 152, or gaps 150 and sections 152 may have openings that receive dowel pins (not shown) to help secure top 104 to the body portion. The center opening 112 in the body portion may also include a locating ring 112A formed therein, which mates with an extending portion (not shown) in the top 104 to properly center the two.


The flow blocking and bearing plate 110 has a circumference and the first portion 102A of each blade 102 preferably extends beyond the circumference, as best seen in FIG. 2. The first portion 102A of each blade 102 has a leading edge 116, a recess 130 and a connecting portion that connects the leading edge 116 and the recess 130. As shown in the exemplary embodiment: (a) the entire leading edge 116 of each blade 102 is part of the hardened top 104; (b) the entire recess 130 of each blade 102 is part of the hardened top 104, and (c) the entire first surface 118 is part of the hardened top 104. The exemplary embodiment also shows: (d) part of the leading face 122 is part of the hardened top 104, and (e) part of the trailing surface 132 is part of the hardened top 104.


A similar hardened top may be utilized in a rotor device such as the one described in U.S. Pat. No. 7,402,276.


Having thus described some embodiments of the invention, other variations and embodiments that do not depart from the spirit of the invention will become apparent to those skilled in the art. The scope of the present invention is thus not limited to any particular embodiment, but is instead set forth in the appended claims and the legal equivalents thereof. Unless expressly stated in the written description or claims, the steps of any method recited in the claims may be performed in any order capable of yielding the desired result.

Claims
  • 1. A rotor for use in molten metal, the rotor comprising a graphite body, a top surface, and a plurality of vanes each having a leading face and a trailing face, and hardened portions comprising hardened material at least twice as hard as the graphite body, the hardened portions comprising: the top surface, less than all of the leading face, and less than all of the trailing face.
  • 2. The rotor of claim 1, wherein the hardened portions are comprised of material that is 2-3 times as hard as the graphite body.
  • 3. The rotor of claim 1, wherein the hardened portions are comprised of material that is 2-4 times as hard as the graphite body.
  • 4. The rotor of claim 1, wherein the hardened portions are comprised of material that is 2-5 times as hard as the graphite body.
  • 5. The rotor of claim 1, wherein the hardened portions are cemented to the graphite body.
  • 6. The rotor of claim 1, wherein the hardened portions are comprised of silicon carbide.
  • 7. The rotor of claim 1 that comprises a plurality of blades, wherein each blade has a first section and a second section, and the first section pushes molten metal towards the second section, and the second section pushes molten metal outward, wherein the entire first section is comprised of hardened material.
  • 8. The rotor of claim 7, wherein part of the second section is comprised of hardened material.
  • 9. The rotor of claim 7, wherein the at least part of the second portion formed by the hardened material is immediately beneath the first portion.
  • 10. The rotor of claim 7 that further includes a bearing ring having a circumference, the blades each have a length, and the length of each blade extends no more than 1½″ beyond the circumference.
  • 11. The rotor of claim 7, wherein each rotor blade has a square tip.
  • 12. The rotor of claim 7, wherein each rotor blade includes a recess on the side opposite the first portion, each recess for enlarging an opening between each rotor blade so as to allow more molten metal to pass through the opening.
  • 13. The rotor of claim 12, wherein at least part of the recess is comprised of the hardened material.
  • 14. The rotor of claim 13, wherein the body portion has a back surface and the recess begins at a position forward of the back surface and terminates at a position even with the back surface.
  • 15. The rotor of claim 1, wherein the body portion has gaps at the corner of each blade and the hardened top surface has sections that are received by and mate with the gaps.
  • 16. The rotor of claim 15, wherein the gaps include openings that each receive a pin positioned in each respective section of the hardened top.
  • 17. The rotor of claim 15, wherein the gap and the hardened top surface include mating openings, wherein each two mating openings receive a dowel pin.
  • 18. The rotor of claim 7, wherein the body portion includes a locating ring and the hardened top surface includes a projection that is received in the locating ring.
  • 19. The rotor of claim 1 that includes a top and a bottom; a plurality of openings through which molten metal can pass, wherein each of the openings is defined in part by an inlet perimeter; a plurality of imperforate rotor blades for displacing molten metal, wherein each of the plurality of rotor blades has a leading face that includes a first section that directs molten metal downward and a second section beneath the first section that directs molten metal outward, and a trailing face that includes a recess that increases the size of one of the openings to help permit molten metal to pass therethrough and into the pump chamber; wherein as the device is rotated, the openings, the inlet perimeters, and the rotor blades rotate.
  • 20. The rotor of claim 1 that further comprises a threaded connective portion at the top for connecting to a rotor shaft.
  • 21. The rotor of claim 1 that further comprises a flow-blocking plate at the bottom.
  • 22. The rotor of claim 19, wherein the first section of each rotor blade has a horizontally-extending projection with a top surface and a bottom surface, wherein the bottom surface is angled to move molten metal into the pump chamber.
  • 23. The rotor of claim 19, wherein the second section of each rotor blade is vertical.
  • 24. The rotor of claim 19, wherein each recess begins at a position forward of the second section of the rotor blade.
  • 25. The rotor of claim 1, wherein the top surface is horizontal.
  • 26. A molten metal pump including the rotor of claim 1.
  • 27. The pump of claim 26 that comprises a superstructure on which a motor is supported, a pump base including a pump chamber in which the rotor is received, and a plurality of support rests connecting the superstructure to the pump base.
CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation of, and claims priority to U.S. patent application Ser. No. 15/804,903, filed on Nov. 6, 2017, by Paul V. Cooper, which is a continuation of, and claims priority to U.S. patent application Ser. No. 13/800,460 (Now U.S. Pat. No. 9,903,383), filed on Mar. 13, 2013, by Paul V. Cooper, the contents of each of the foregoing applications, are incorporated herein by reference, to the extent such contents do not conflict with the present disclosure.

Continuations (2)
Number Date Country
Parent 15804903 Nov 2017 US
Child 16862333 US
Parent 13800460 Mar 2013 US
Child 15804903 US