Monomers with quaternary amino groups, methods for making same, and novel (co)polymers obtained from said novel monomers

Abstract

The invention relates to compounds of formula (I), prepared by quaternising a compound (II) by means of at least one compound R3—X⊖: R1=H or —CH3; R2=—CH3; —C2H5; —C3H7 or —C4H9; and compound (I) is optionally quaternised on one of the nitrogens, which is symbolised by the fact that the R3, X⊖and ⊕ associated with this nitrogen are shown between brackets; if compound (I) is quaternised on a single nitrogen, R3 and X⊖ have the following meanings: (1) R3=—CH3 or —CH2C6H5; and X⊖=Cl⊖ or CH3OSO3⊖; or (2) R3=a C1-C12-alkyl group; and X⊖=Br⊖ or I⊖; if compound (I) is quaternised on both nitrogens, the two X⊖ may be the same or different and the two R3 may be the same, in which case: (3) R3=a C5-C12 alkyl group; and X⊖=CH3OSO3⊖, Br⊖ or I⊖; or different, in which case: (4) one of the R3=—CH3 or —CH2C6H5; and X⊖=Cl⊖ or CH3OSO3⊖; and the other=a C5-C12-alkyl group; and X⊖=Br⊖ or I⊖.

Description

The present invention relates to new monomers with quaternary amino groups, to a method of manufacturing same and to the new (co)polymers obtained from these new monomers.

Compounds of the type having formula: in which:

• • R⁽⁰⁾ represents H or CH₃;
  • A represents —O— or —NH—;
  • D represents a C₁-C₆ linear or branched alkylene chain;
  • R⁽¹⁾ and R⁽²⁾, the same or different, each represent independently H or C₁-C₅ alkyl;are well known from the background literature.

Important compounds in this family are N,N-dimethylamino ethyl acrylate (ADAME) and N,N-dimethylamino ethyl methacrylate (MADAME): where R⁽⁰⁾=H or CH₃.

A very large number of publications and patents describe the manufacture of aqueous solutions of quaternary ammonium salts based on ADAME and MADAME, the most representative of these salts being expressed by the formula: where R⁽⁰⁾=H Or CH₃ and R⁽³⁾=CH₃ or benzyl, these salts being designated by the abbreviation (M)ADAMQUAT MC or (M)ADAMQUAT BZ depending on whether R⁽³⁾ represents CH₃ or benzyl.

This reaction is a quaternisation, in the presence of water, of the initial compound with a quaternising agent R⁽³⁾—Cl.

The resultant aqueous solutions of quaternary salts are used in particular to prepare polymers intended for use as cationic flocculants in the treatment of water.

Patent CZ-A-250 962 discloses compounds of formula: in which:

• • R⁽⁰⁾ represents H or —CH₃;
  • R⁽²⁾ represents —CH₃, —C₂H₅, —C₃H₇ or —C₄H₉;
  • R⁽³⁾ represents —CH₃, —C₂H₅, —C₃H₇, —C₄H₉, C₆H₅ or —CH₂C₆H₅, and
  • x^⊖ represents Cl^⊖ or Br^⊖.

During research and development work, the applicant company has discovered new monomers which form the subject matter of the present application, together with a method of manufacturing same and the homo- or copolymers containing units derived from these new monomers.

Aqueous dispersions, either saline or without salt, made from these new monomers and offering a solution to technical problems faced by the person skilled in the art, are the subject matter of three French patent applications filed this day in the name of the applicant company.

Accordingly, the present invention relates firstly to compounds of formula (I): in which:

• • R¹ represents H or —CH₃;
  • R² represents —CH₃; —C₂H₅; —C₃H₇ or —C₄H₉; and
  • compound (I) is optionally quaternised on one of the nitrogens, which is symbolised by the fact that the R³, X^⊖ and ⊕ associated with this nitrogen are shown between brackets;
  • if compound (I) is quaternised on a single nitrogen, R³ and X^⊖ have the following meanings:
    • (1) R³ represents —CH₃ or —CH₂C₆H₅; and X^⊖ represents Cl^⊖ or CH₃OSO₃^⊖; or
    • (2) R³ represents a C₁-C₁₂-alkyl group; and X^⊖ represents Br^⊖ or I^⊖;
  • if compound (I) is quaternised on both nitrogens, the two X^⊖ may be the same or different and the two R³ may be the same, in which case:
    • (3) R³ represents a C₅-C₁₂-alkyl group; and X^⊖ represents CH₃OSO₃^⊖, Br^⊖ or I^⊖;
    • or different, in which case:
    • (4) one of the R³ represents —CH₃ or —CH₂C₆H₅; and
      • X^⊖ represents Cl^⊖ or CH₃OSO₃^⊖; and
      • the other represents a C₅-C₁₂-alkyl group; and
      • X^⊖ represents Br^⊖ or I^⊖;and mixtures of these compounds.

An example of a compound (I) is a compound having formula (Ia): which may be designated by the abbreviation S-ADAMQUAT BZ.

The compounds proposed by the invention may advantageously be in aqueous solution.

The present invention also relates to a method of manufacturing compounds of formula (I) as defined above, characterised in that into a solution in an organic solvent or a mixture of organic solvents, of a compound of formula (II): in which R¹ and R² are as defined above, is introduced, at a temperature of 35 to 80° C., a quaternising agent of formula (III): R³—X^⊖  (III)in which:

• • R³ and X^⊖ have the meanings (1) and (2) given above, in which case the molar ratio of quaternising agent (III)/compound (II) is in a range of between 0.9 and 1.5 and a compound (I) is obtained which is quaternised on a single nitrogen; or,
  • R³ and X^⊖ have meaning (3) given above or two different quaternising agents are used, the R³ and X^⊖ of these two quaternising agents having meaning (4) given above, in which case the molar ratio of quaternising agent(s) (III)/compound (II) is in a range of between 0.9 and 1.5 and a compound (I) is obtained which is quaternised on both nitrogens,then the reaction is allowed to continue at said temperature until compound(s) (III) has/have disappeared completely or substantially completely, after which water is added and then an aqueous solution of compound (I) is separated and the water removed as necessary.

The organic solvent(s) used is/are chloroform, dichloromethane, dichloroethane and mixtures thereof, for example.

The reaction is not generally conducted under pressure unless at least one quaternising agent (III) is in the gaseous state.

The quaternising agent(s) (III) is/are introduced into the solution of compound (II), generally over a period of 0.5 to 2 hours, and, once all the quaternising agent(s) has/have been introduced, the reaction of compounds (II) and (III) is conducted, generally over a period of 10 to 40 hours.

After separating the aqueous solution of compound (I), it is preferable to remove all traces of organic solvent from the resultant aqueous solution by stripping in air at a reduced pressure.

Said method results in an aqueous solution with a concentration of compound (I) which is preferably between 65 and 75% by weight.

According to one specific feature of the above method, it is conducted in the presence of at least one stabiliser selected in particular from hydroquinone, hydroquinone methyl ether and 3,5-ditert.-butyl-4-hydroxytoluene and mixtures of these stabilisers, the content of stabilising agent(s) being in particular 400 to 2000 ppm relative to the aqueous solution of the final compound (I).

Compound (II) may be prepared by causing a compound of formula (IV): in which R² is as defined above,to react with (meth)acrylic anhydride in the presence of triethylamine, with a molar ratio of (meth)acrylic anhydride/compound (IV) of 0.5 to 2, at a temperature of 20 to 100° C., in particular 30 to 60° C., for a period of 2 to 10 hours,in the presence of at least one stabiliser such as phenothiazine, hydroquinone methyl ether, 3,5-ditert.-butyl-4-hydroxytoluene and hydroquinone and mixtures of these stabilisers in a ratio of 200 to 3000 ppm relative to the charge.

In the reaction with (meth)acrylic anhydride, the triethylamine acts as a catalyst for the reaction and traps the (meth)acrylic acid in the salt form. It is generally used in an equivalent molar ratio of 1 to 2 relative to the (meth)acrylic anhydride.

Another objective of the present invention is to propose homopolymers or copolymers containing units of at least one monomer of formula (I) as defined above.

The copolymers based on the monomers (I) incorporating the monomer (Ia) may be water-soluble or hydrophobic polymers in the form of an aqueous dispersion, latex, aqueous solution, inverse, emulsion or powder. They are prepared by radical copolymerisation using various synthesis methods such as polymerisation in dispersion, solution, direct emulsion, inverse emulsion and inverse suspension.

The examples below, given by way of illustration only, provide a clearer understanding of the invention. In these examples, the specified proportions and percentages are by weight unless stated to the contrary.

The following abbreviations are used in these examples:S-ADAME: compound of formula: EMHQ: hydroquinone methyl ether.

EXAMPLE 1

Synthesis of S-ADAME

The following are introduced into a 1 liter glass reactor:

• • 292 g of 1,3-bis-dimethylamino-2 propanol;
  • 242 g of triethylaminre; and
  • 0.373 g of phenothiazine as a stabiliser.

226 g of acrylic anhydride are then added to this mixture over a period of 1 hour at ambient temperature, under agitation and bubbling in air. The temperature increases, reaching 50° C. After an additional 2 hours reaction time, the mixture is cooled and 50 ml of water are added. After decanting, 450 g of a higher organic phase are obtained, which is distilled under reduced, pressure to separate 250 g of the above compound (purity GC≧99%).

EXAMPLE 2

Quaternisation of S-ADAME to Produce S-ADAMQUAT BZ

The S-ADAME obtained at point (a), stabilised with 1500 ppm of hydroquinone methyl ether and 150 g of CHCl₃, is introduced in a quantity of 44.2 g into a 250 ml glass reactor. Under agitation and whilst bubbling in air, the mixture is raised to 50° C. Over a period of 1 hour, 28 g of benzyl chloride are added. After a reaction time of 25 hours, the initial acrylate has disappeared and 33 g of water are added. A higher phase is decanted and any traces of CHCl₃ removed by air stripping at 45° C. under reduced pressure (P=1.33×10⁴ Pa (100 mm Hg). 70 g of aqueous solution are thus obtained, containing 65% of quaternary cationic monomer of the anticipated structure, determined by RMN ¹³C. Thismonomeris called S-ADAMQUAT BZ.

Claims

1. Compounds having formula (I):

2. Compound as claimed in claim 1, characterised in that it is represented by the formula (Ia):

3. Compounds as claimed in one of claims 1 and 2, characterised in that they are in the form of an aqueous solution.

4. A method of manufacturing compounds as defined in claim 1, characterized in that into a solution in an organic solvent, of a compound of formula (II):

5. A method as claimed in claim 4, characterised in that the organic solvent used is at least one selected from chloroform, dichloromethane and dichloroethane.

6. A method as claimed in claim 4, characterized in that it is conducted under pressure if the quaternising agent or at least one quaternising agent (III) is in the gaseous state.

7. A method as claimed in claim 4, characterized in that the quaternising agent or quaternising agents (III) is/are introduced into the solution of compound (II) over a period of 0.5-2 hours.

8. A method as claimed in claim 4, characterized in that once all of thee quaternising agent or quaternising agents has/have been introduced, the reaction between compounds (II) and (III) is conducted for a period of between 10 and 40 hours.

9. A method as claimed in claim 4, characterized in that all traces of organic solvent are removed from the resultant aqueous solution by stripping in air at a reduced pressure.

10. A method as claimed in claim 4, characterized in that it produces an aqueous solution with a concentration of 65 to 75% by weight of compound (I).

11. A method as claimed in claim 4, characterized in that it is conducted in the presence of at least one stabiliser chosen in particular from hydroquinone, hydroquinone methyl ether and 3,5-ditert.-butyl-4-hydroxytoluene and mixtures of these stabilisers, the content of stabilising agent(s) being in particular from 400 to 2000 ppm relative to the aqueous solution of the final compound (I).

12. A method as claimed in claim 4, characterized in that compound (II) is prepared by causing a compound of formula (IV):

13. Homopolymers or copolymers containing units of at least one monomer of formula (I) as defined in claims 1 to 3.

14. Homopolymers or copolymers containing units of at least one monomer of formula (I) as defined in claim 2.

15. A method as claimed in claim 12, wherein said stabilizer is selected from the group consisting of phenothiazine, hydroquinone methyl ether, 3,5-ditert.-butyl-4-hydroxytoluene and hydroquinone and mixtures, of these stabilisers in a ratio of 200 to 3000 ppm relative to the charge.