Patent Grant
11377616
The field of this invention relates to the latest technology for substantially reducing steel-to-steel wear along with eliminating the need for Zinc Dialkyldithiophosphates (ZDDP) in motor oils as an anti-wear component. The composition of this invention has been shown to modify the plastic response of steel while having a positive influence on the chemical reactivity of the surfaces subjected to being worn down due to friction. Specifically, based on the tribological testing detailed in U.S. 62/109,172, spectroscopic analysis of the wear tracks of an engine disk revealed that chemical elements like P, S, Mn, Zn, which can be from the ZDDP in the oil, were not detected. This suggests that this composition inhibits the reaction of ZDDP and renders it unnecessary for reducing wear.
This is important, because today there is a movement within a number of states and countries to remove or substantially reduce the need for ZDDP in motor oils. Environmentalists in the US have lobbied both State and Federal departments to legislate such a ban. Unfortunately, governments have been reluctant to issue or enforce such a ban until a cost-effective alternative becomes available which can have the same or better anti-wear performance results as ZDDP, while eliminating the need for ZDDP itself.
There are in fact two types of zinc-thiophosphates universally added to motor oils used today: zinc di-alkyl-di-thiophosphates (which is ZDDP proper), and/or zinc di-thiophosphate (which is often abbreviated to ZDTP). Unless otherwise specified, when the acronym ZDDP is used in this disclosure, it is being used to refer to either of these, with or without the di-alkyl group. And specifically, the composition of this invention eliminates the need for either of ZDDP-proper, or ZDTP to be used in motor oils any longer.
The automotive industry was much simpler in the early days. Engines bearings were made from a soft tin/copper/antimony alloy, commonly referred to as babbitt. This alloy is relatively inert chemically and has the ability to absorb small amounts of foreign particulate material. But, as engine horsepower increased, babbitt alloy surfaces proved to be inadequate to bear the increased loading on these surfaces.
Thus, the need for harder bearings arose, and new types of bearings with cadmium/silver, cadmium/nickel, and copper/lead construction were developed. Such bearings were much stronger, but were not as chemically inert as babbitt and could be attacked by the acids generated from oil oxidation. These new bearings were unable to absorb foreign material such as carbon, grit and wear debris into the bearing material, and consequently, improvements in oil filtration were developed and used in vehicles to decrease premature wear.
Further, bearing corrosion inhibitors, anti-wear agents and acid inhibitor compounds were developed to protect these new bearings. There was a need to protect the bearings against both corrosive and mechanical wear, and many of these compounds served both functions. Compounds such as sulfurized sperm oil, organic phosphates, dithiocarbonates and dithiophosphates were experimented with to reduce premature wear. In 1941, Lubrizol developed Zinc Dialkyldithiophosphates, which remain the most commonly-used form of ZDDP, and introduced these to the market.
Initially, ZDDP was added to motor oils in low concentrations of less than 0.3% by volume as a bearing passivator, defined as treating or coating a metal in order to reduce the chemical reactivity of its surface. In addition, ZDDP was found to be a remarkably effective anti-wear agent; a true extreme-pressure (EP) additive for heavily loaded steel-on-steel sliding mechanisms such as camshafts and valve lifters or tappets. During these years, there was little if any concern about the impact of ZDDP upon the environment.
For years, these ZDDP additives have been providing sufficient anti-wear service, starting with the early days of gasoline and diesel non-detergent motor oils, through the present day. Diesel engines of more than half a century ago, which generally operated at lower speeds and were more massively built, did not exhibit the same wear problems. But in a gasoline engine, the valve train is more heavily stressed due to the higher engine speeds, and these additives have played and continue to play an important role in reducing wear.
Current and previous motor oils have depended upon the use of ZDDP as a means to protect against premature wear between bearing surfaces and from steel-to-steel contact. In view especially of the detrimental impact of ZDDP on the environment, it would be desirable to have available a replacement additive which can eliminate the need for ZDDP, which additive at the same time provides the same level of protection—and even better protection—for engine components.
In U.S. Pat. No. 7,745,382, which was the first of several US and foreign patents issued to Ronald J. Sloan and assigned to BestLine International Research Inc. (BestLine) who are the inventor and assignee for the present application as well, it was disclosed that a synthetic lubricant additive comprising polymerized alpha-olefins (PAOs), hydroisomerized hydro-treated severe hydrocracked base oil, and synthetic sulfonates could provide better engine lubrication and reduce engine wear, and that in fact the PAOs and the base oils could be the primary composition for a broad range of lubricants useful in many different circumstances including and beyond automotive applications, and as applied to many different materials including and beyond steel. This includes diesel fuel additives (U.S. Pat. No. 8,062,388 et. seq.), gasoline additives (U.S. Pat. No. 7,931,704 et. seq.), general purpose lubricants (U.S. Pat. No. 8,022,020 et. seq.), marine lubricants (U.S. Pat. No. 8,334,244 et. seq.) and even golf club cleaners (U.S. Pat. No. 8,071,522 et. seq.).
But until the tribological testing detailed in U.S. 62/109,172, the tribological mechanism underlying the effectiveness of BestLine's synthetic lubricant additive was not fully understood. This testing established that not only did this PAO, base oil and (optionally) synthetic sulfonate composition enhance lubrication, but this composition was also found to modify the plastic response of the investigated steel and to influence the chemical reactivity of the worn surfaces. Particularly, as noted above, because elements like P, S, Mn, Zn were not detected when this composition was added to engine oils with ZDDP, this means that this composition inhibits the reaction of ZDDP and renders ZDDP unnecessary for reducing wear if the PAO and base oil is employed as a substitute.
Thus, it was only with the new understandings first disclosed in U.S. 62/109,172, that consideration could be given to adding this PAO, base oil and optionally synthetic sulfonate composition to motor oils, while at the same time removing all of the ZDDP and/or ZDTP from these very same motor oils. Thus, the addition of this PAO, base oil, sulfonate composition to motor oils simultaneously with the removal of all forms of ZDDP not only reduces engine wear by superior lubrication, but also favorably modifies the plastic response of all steel elements which it lubricates, and at the same time solves an important environmental problem.
The use of this composition to improve motor oils while removing the environmental harm caused by ZDDP and ZDTP is applicable to all of the five groups of motor oil as defined by the American Petroleum Institute (API). This API categorization is hereby incorporated by reference into this disclosure and its associated claims. Specifically, the September 2011 standards of the API at http://www.api.org/˜/media/files/certification/engine-oil-diesel/publications/appendix-e-rev-09-01-11.pdf?la=en specify as follows:
“All base stocks are divided into five general categories
An additive and related method for modifying the plastic response of steel, the additive comprising: polymerized alpha olefins; hydroisomerized hydro-treated severe hydrocracked base oil; and optionally, synthetic sulfonates. A tribological study detailed in U.S. 62/109,172 and herein concludes that: (1) This additive significantly reduces wear of the carbon steel disk to 6% of the wear observed in pure oil without additive; (2) There is no obvious effect of the additive on friction except a slightly better stability with time of the coefficient of friction; (3) The additive appears to inhibit the reaction of ZDDP and renders ZDDP unnecessary for reducing wear. This suggests that the additive may be a replacement for ZDDP in motor oils; and (4) The additive was found to modify the plastic response of the investigated steel and to influence the chemical reactivity of the worn surfaces. Although testing was not conducted to establish the coefficient of friction, as this will be concluded at a later time, previous testing supports that the friction is reduced.
This invention is for a synthetic lubricant additive that can be added at various ratios to provide the need protect against steel-to-steel wear or between bearing and steel surfaces, as well as related method of manufacturing this additive and related methods of its use. Further, this additive can be added to synthetic, synthetic blends and non-synthetic motor oils (motor oils in all of Groups I through V) to provide them with the anti-wear protection necessary in today's high speed and low speed gasoline and diesel motor oils. Further the invention allows steel under extreme pressure to yield or to respond to plastic deformation without the fracturing of the metal surface.
The additive incorporates the use of polymerized alpha olefins (PAO); hydroisomerized hydro-treated severe hydrocracked base oil; and optionally, synthetic sulfonates. Further, one can optionally employ vacuum distilled non aromatic solvents and liquefied polytetrafluoroethylene (PTFE) and when combined into the additive a specific sequence, this forms a finished product that exceeds the metal-protecting capability and benefits of ZDDP while providing an environmentally-friendly replacement. Further this product provides protection against steel-to-steel contact while positively influencing the chemical reactivity of worn metal surfaces. Further this product in independent testing reported in provisional application U.S. 62/109,172 has demonstrated the ability to modify the plastic response of steel placed under extreme pressure.
As previous indicated the ingredients of this additive when blended in a very specific sequence under specific conditions will provide a lubricant that has shown its ability to replace the need for ZDDP as an anti-wear agent in motors oils. The blending is a combination of accurately-controlled sheering and homogenization of the compounds resulting in a long-term stable blend. Once blended in a specific sequence, simple purification or physical separation, such as distillation or freezing, does not constitute synthesis, in the manner, for example, of making synthetic Group III and Group IV from crude oil via a chemical reaction.
The finished product is a combination of:
Synthetic lubricants have been successfully used for some time. They have the ability to offer very-high-viscosity index, low volatility, superior oxidation resistance, high thermal stability, excellent temperature fluidity and low toxicity to the environment. These characteristics in a finished lubricant are very important in modern high-speed and high-horsepower engines. Further these characteristics benefit the long term goals of being less toxic to the environment while providing maximum protection for automotive components.
This synthetic lubricant when tested has demonstrated the ability to provide and exceed the anti-wear protection currently provided by the inclusion of ZDDP in motor oils. The synthetic lubricant can provide the necessary anti-wear in automotive, diesel and marine motor oil, but without the environmental impact of ZDDP. It has the ability to blend with, and be effective with, all of Group I, II, III, IV and Group base oils.
In its preferred embodiment, disclosed here is an environmentally-improved motor oil blend and related methods for properly lubricating components of an engine and favorably modifying a plastic response of components of the engine, the blend being free of zinc di-alkyl-di-thiophosphates (ZDDP) and free of zinc di-thiophosphate (ZDTP), comprising: a motor oil selected from the motor oil group consisting of Group I, Group II, Group III, Group IV, and Group V motor oils; a motor oil additive comprising alpha-olefins and hydroisomerized hydro-treated severe hydrocracked base oil; ZDDP omitted from the chemical constituents of the motor oil; and ZDTP omitted from the chemical constituents of the motor oil.
The preferred blending ratios for each of the components of this additive are shown below. It is important to maintain a blend of components falling within the following percentages:
Polymerized alpha-olefins (PAO): It is preferred that these comprise from 20% to 60% by volume. It is most preferred that these comprise approximately 55% by volume. One may also use alpha-olefins (AO) which have not been polymerized, though PAOs are preferred. One may also use the modern metallocene poly-alpha-olefins (mPAO) which have higher viscosity indexes than conventional PAOs.
Hydroisomerized high viscosity index (VI) hydro-treated (HT) severe hydro-cracked base oils: It is preferred that these comprise from 5% to 55% by volume. It is more preferred that these comprise from 7% to 25% by volume. It is most preferred that these comprise approximately 21% by volume. It is preferred, but not required, that these base oils have a viscosity grade 32. One may also use can also saturated hydrocarbons, process oil and hydraulic oil for this base oil.
Synthetic sulfonates: These are preferred, albeit optional ingredients. It is preferred that when used these comprise from 0.05% to 10% by volume. It is most preferred that these comprise approximately 3% by volume. It is preferred that these synthetic sulfonates comprise a total base number (TBN) from 200 to 600. It is most preferred that these comprise a 300 TBN. One may also use thixotropic calcium sulfonates.
Vacuum Distilled Low-Viscosity and Low-Aromatic Solvents: Often referred to as aliphatic or mineral spirits, these are optional ingredients. It is preferred that when used, these comprise from 10% to 40% by volume. It is most preferred that these comprise approximately 21.5% by volume. The low-aromatic range is preferred to be less than 0.5% aromatic. It is preferred that these solvents have a VOC Exemption, defined by the California Air Resources Board as including those compounds “not expected to meaningfully contribute to ozone formation due to their low reactivity in the atmosphere.” The envisioned low viscosity is in the approximate range of 40 C mm2/s (ASTM D 445) and viscosity at 25 C cSt 2.60 and at 40 C cSt 1.98 (ASTM D 445).
Liquefied Polytetrafluoroethylene (PTFE): This is an optional ingredient. When used, it is preferred that these comprise from 0.001% to 10% by volume. It is most preferred that these comprise approximately 0.45% by volume. The PTFE should be liquefied to avoid agglomeration, and preferably comprise a stable aqueous dispersion of PTFE particles in water or oil. If oil is used, it is preferred to use 150 solvent neutral petroleum oil or an approximate equivalent.
The following describes the preferred method for blending these components to produce this motor oil additive.
Initially, the alpha olefins, and the base oils are blended until the liquid is a consistent amalgamation without any appearance of separation, to yield a first blend. Blending is based on speed of the agitator, and temperature will dictate the amount of time for the blend to complete. The blending time range may vary from 4 to 6 hours. The ideal temperature for each component is between 22 to 30 degrees centigrade for optimum blending.
Further, the vacuum distilled non-aromatic solvent and synthetic sulfonates are blended together to yield a second blend. This second blend may be prepared in a much smaller, high-speed, enclosed blender. This second blend is then added to the first blend.
If PTFE is used, then the first and second blends are finally blended together with the PTFE.
If low-aromatic aliphatic solvent is used, then the first and second blends are blended with additional low-aromatic aliphatic solvents to produce a third blend. Then, if PTFE is used, all of the foregoing is blended together with the PTFE.
It is preferred that there is an approximate 25%/75% ratio of calcium sulfonates to aliphatic or mineral spirits, when these are used.
This third blend, or the mineral spirits alone absent the synthetic sulfonates, together with the balance of the ingredients, added to the first blend and the agitator is run until the components appear to have thoroughly blended into a consistent liquid. Following the blending, the product is sheered by a high speed sheering pump until the product is consistent. The sheering provides a stable flow viscosity exhibiting Newtonian behavior and greatly enhances the shelf life when there are substantial differences in specific gravity of each component.
The preferred blending equipment used in this process is as follows: This process involves several blending and holding tanks in which the product can be weighed and then pumped through control valves to maintain consistent flow and pressure. The blending should be performed in an enclosed tank to reduce product evaporation loss and prevent exposure to open spark. Blending equipment can be by a combination of high- or low-speed blending apparatus. The size or volume of the tank is not critical to the blend. Sheering equipment should have a range of 60 to 5200 cycles per second with a typical speed of 3600 cycle per second and be capable of making stable emulsions of products with oil ingredients providing liquid suspensions and dispersions without aeration.
This motor additive is then combined with a motor oil selected from the motor oil group consisting of Group I, Group II, Group III, Group IV, and Group V motor oils, without the use of ZDDP of ZDTP, to provide an environmentally-improved motor oil blend for properly lubricating components of an engine and favorably modifying a plastic response of components of the engine. The preferred blend ratio is from 85% to 95% by volume of motor oil, and from 5% to 15% by volume of the motor oil additive.
To create the motor-oil blend, the motor oil and the additive are combined together, and this combination is then simply mixed with a high-speed blender before being packaged. Given the chemical characteristics of motor oil and of the additive, there should be minimal or no separation thereafter while the packaged blend is maintained on a shelf, i.e., the blend should remain homogeneous for whatever shelf-life the motor oil blend may have before it is poured by a user into an engine.
While not the preferred mode of usage, one could take a motor oil with no ZDDP and no ZDTP and introduce that into an engine separately from introducing the lubricant. However, in this circumstance the user would need to take care to maintain an optimum mix of 85% to 95% by volume of motor oil and 5% to 15% by volume of the motor oil additive. Using a blend that is already combined in the desired ratios is preferred because the user need not then be concerned with maintaining the ratio of motor oil to additive within the desired ranges, and the possibility of user mistake is eliminated.
Referring to the API properties laid out earlier in the background of the invention, the overall combination of the motor oil with the lubricant, depending upon the viscosity of the host motor oil without ZDDP or ZDTP, will have the following characteristics: 1) For some selected temperatures: 100° C., kinematic viscosity 1.7 to 102.0; 40° C., kinematic viscosity 5.4 to 1350; −40° C.; kinematic viscosity 2,704 to 35,509. 2) Viscosity index: 90 to 200. 3) NOACK Volatility 0.6 to 99.5. 4) Pour point up to −20 to −61 C. Again, these ranges are dependent on the viscosity of the host oil. Finally, 5) the POA (or AO or mPAO) base should have a PAO Unsaturates viscosity grade from PAO-2 to PAO-100.
Generally, for motor oil blends, the range from PAO-2 to PAO-10 is sufficient. However, for other lubricating applications in which it is desirable to remove environmentally-undesirable chemicals such as ZDDP and ZDTP replace them with the alpha-olefin and base oil additive of this disclosure, given the understanding disclosed in U.S. 62/109,172 regarding how this additive favorably modifies plastic response and influences chemical reactivity, one may find it desirable to use alpha-olefins in the higher range up to and including PAO-100 for other lubricating applications, as outlined further below.
Specifically, it is also understood and disclosed here that the base combination of alpha-olefins and hydroisomerized hydro-treated severe hydrocracked base oil can serve as a replacement for environmentally-undesirable chemicals not only in motor oils, but in other lubricating/anti-wear agents and applications including, but not limited to:
The ability to omit environmentally-undesirable chemicals in this broad range of circumstances, which chemicals are widely thought to be essential to providing proper lubrication and protecting against wear, emanates from the disclosure in U.S. 62/109,172 that this base combination of alpha-olefins and hydroisomerized hydro-treated severe hydrocracked base oil modifies the plastic response of steel and changes the chemical reactivity of the surfaces subjected to being worn down due to friction whereby these environmentally-undesirable chemicals were not detected under spectroscopic analysis of the wear tracks. So while a very important application of this disclosure is to motor oils because of the widespread usage of these oils and the consequent substantial environmental impact of these oils, it is also understood that the same favorable plastic response modifications and chemical reactivity changes will also transpire in many other applications, which enables this disclosure to be fruitfully applied to those other applications as well, and particularly, to the removal from fluids, lubricants and oils generally of environmentally-undesirable chemicals widely regarded to be essential for proper lubrication and anti-wear protection.
The knowledge possessed by someone of ordinary skill in the art at the time of this disclosure, including but not limited to the prior art disclosed with this application, is understood to be part and parcel of this disclosure and is implicitly incorporated by reference herein, even if in the interest of economy express statements about the specific knowledge understood to be possessed by someone of ordinary skill are omitted from this disclosure. While reference may be made in this disclosure to the invention comprising a combination of a plurality of elements, it is also understood that this invention is regarded to comprise combinations which omit or exclude one or more of such elements, even if this omission or exclusion of an element or elements is not expressly stated herein, unless it is expressly stated herein that an element is essential to applicant's combination and cannot be omitted. It is further understood that the related prior art may include elements from which this invention may be distinguished by negative claim limitations, even without any express statement of such negative limitations herein. It is to be understood, between the positive statements of applicant's invention expressly stated herein, and the prior art and knowledge of the prior art by those of ordinary skill which is incorporated herein even if not expressly reproduced here for reasons of economy, that any and all such negative claim limitations supported by the prior art are also considered to be within the scope of this disclosure and its associated claims, even absent any express statement herein about any particular negative claim limitations.
Finally, while only certain preferred features of the invention have been illustrated and described, many modifications, changes and substitutions will occur to those skilled in the art. It is, therefore, to be understood that the appended claims are intended to cover all such modifications and changes as fall within the true spirit of the invention.
This application is a continuation of application U.S. Ser. No. 14/699,924 filed Apr. 29, 2015. Said U.S. Ser. No. 14/699,924 claims priority of provisional application U.S. 62/109,172 filed Jan. 29, 2015, which is hereby incorporated by reference in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2055456 | Eichwald | Sep 1936 | A |
| 2124628 | Moser | Jul 1938 | A |
| 2133734 | Moser | Oct 1938 | A |
| 2270577 | Bergstrom et al. | Jan 1942 | A |
| 2402325 | Greisinger et al. | Jun 1946 | A |
| 2418894 | McNab et al. | Apr 1947 | A |
| 2485861 | Sumner et al. | Oct 1949 | A |
| 2501731 | Mertes | Mar 1950 | A |
| 3406419 | Young | Oct 1968 | A |
| 3480550 | Henderson | Nov 1969 | A |
| 3984599 | Norton | Oct 1976 | A |
| 4127491 | Reick | Nov 1978 | A |
| 4131551 | Thompson et al. | Dec 1978 | A |
| 4218330 | Shubkin | Aug 1980 | A |
| 4224170 | Haugen | Sep 1980 | A |
| 4224173 | Reick | Sep 1980 | A |
| 4228021 | Lenack | Oct 1980 | A |
| 4261840 | Gragson | Apr 1981 | A |
| 4375418 | Zoleski et al. | Mar 1983 | A |
| 4387033 | Lenack et al. | Jun 1983 | A |
| 4443348 | Wright et al. | Apr 1984 | A |
| 4483195 | Brown et al. | Nov 1984 | A |
| 4504404 | Schumacher et al. | Mar 1985 | A |
| 4534873 | Clark | Aug 1985 | A |
| 4543195 | Grangette et al. | Sep 1985 | A |
| 4597880 | Eliades | Jul 1986 | A |
| 4640792 | Groenhof et al. | Feb 1987 | A |
| 4659488 | Vinci | Apr 1987 | A |
| 4844825 | Sloan | Jul 1989 | A |
| 4859359 | DeMatteo et al. | Aug 1989 | A |
| 4879053 | Matthews et al. | Nov 1989 | A |
| 4946510 | Kinnebrew et al. | Aug 1990 | A |
| 4956122 | Watts et al. | Sep 1990 | A |
| 5013463 | Slama | May 1991 | A |
| 5120358 | Pippett | Jun 1992 | A |
| 5136118 | Buchanan et al. | Aug 1992 | A |
| 5169564 | Gallacher et al. | Dec 1992 | A |
| 5202040 | Sanderson et al. | Apr 1993 | A |
| 5332516 | Stephens | Jul 1994 | A |
| 5364994 | Scharf | Nov 1994 | A |
| 5431841 | Lockhart | Jul 1995 | A |
| 5439602 | Eckard et al. | Aug 1995 | A |
| 5505867 | Ritter | Apr 1996 | A |
| 5578235 | Jao et al. | Nov 1996 | A |
| 5631211 | Nakagawa et al. | May 1997 | A |
| 5672572 | Araik et al. | Sep 1997 | A |
| 5681797 | Lawate | Oct 1997 | A |
| 5741764 | Patel et al. | Apr 1998 | A |
| 5885942 | Zhang et al. | Mar 1999 | A |
| 5888281 | Longo | Mar 1999 | A |
| 5972853 | Boffa et al. | Oct 1999 | A |
| 6008164 | Aldrich et al. | Dec 1999 | A |
| 6046142 | Zilonis et al. | Apr 2000 | A |
| 6074993 | Waddoups et al. | Jun 2000 | A |
| 6143701 | Boffa | Nov 2000 | A |
| 6323162 | Yasunori et al. | Nov 2001 | B1 |
| 6413916 | Baumgart et al. | Jul 2002 | B1 |
| 6551967 | King et al. | Apr 2003 | B2 |
| 6761645 | Weber | Jul 2004 | B1 |
| 6774091 | Dituro et al. | Aug 2004 | B2 |
| 6858567 | Akao | Feb 2005 | B2 |
| 6919300 | Dituro | Jul 2005 | B2 |
| 6962895 | Scharf et al. | Nov 2005 | B2 |
| 6992049 | Deckman et al. | Jan 2006 | B2 |
| 7018960 | Negoro et al. | Mar 2006 | B2 |
| 7022766 | Okada et al. | Apr 2006 | B2 |
| 7055534 | Goode et al. | Jun 2006 | B2 |
| 7109152 | Corby et al. | Sep 2006 | B1 |
| 7124728 | Carey et al. | Oct 2006 | B2 |
| 7745382 | Sloan | Jun 2010 | B2 |
| 7776233 | Arafat et al. | Aug 2010 | B2 |
| 7931704 | Sloan | Apr 2011 | B2 |
| 8022020 | Sloan | Sep 2011 | B2 |
| 8039424 | Sloan | Oct 2011 | B2 |
| 8062388 | Sloan | Nov 2011 | B2 |
| 8071513 | Sloan | Dec 2011 | B2 |
| 8071522 | Sloan | Dec 2011 | B2 |
| 8168572 | Thoen et al. | May 2012 | B2 |
| 8268022 | Sloan | Sep 2012 | B2 |
| 8334244 | Sloan | Dec 2012 | B2 |
| 8377861 | Sloan | Feb 2013 | B2 |
| 8415280 | Sloan | Apr 2013 | B2 |
| 8491676 | Sloan | Jul 2013 | B2 |
| 8623807 | Sloan | Jan 2014 | B2 |
| 8771384 | Sloan | Jul 2014 | B2 |
| 10400192 | Sloan | Sep 2019 | B2 |
| 20010036906 | Locke et al. | Nov 2001 | A1 |
| 20030040444 | Garmier | Feb 2003 | A1 |
| 20030087769 | Dituro et al. | May 2003 | A1 |
| 20040014613 | Dituro et al. | Jan 2004 | A1 |
| 20040060229 | Todd et al. | Apr 2004 | A1 |
| 20040077506 | Arrowsmith et al. | Apr 2004 | A1 |
| 20040102335 | Carrick et al. | May 2004 | A1 |
| 20060160708 | Sloan | Jul 2006 | A1 |
| 20080182769 | Sloan | Jul 2008 | A1 |
| 20080190014 | Volkel et al. | Aug 2008 | A1 |
| 20080236538 | Lam | Oct 2008 | A1 |
| 20100261626 | Sloan | Oct 2010 | A1 |
| 20100269404 | Sloan | Oct 2010 | A1 |
| 20100273687 | Sloan | Oct 2010 | A1 |
| 20100273688 | Sloan | Oct 2010 | A1 |
| 20110009301 | Sloan | Jan 2011 | A1 |
| 20110015103 | Sloan | Jan 2011 | A1 |
| 20110197499 | Sloan | Aug 2011 | A1 |
| 20120035087 | Sloan | Feb 2012 | A1 |
| 20120060410 | Sloan | Mar 2012 | A1 |
| 20120077720 | Sloan | Mar 2012 | A1 |
| 20120077724 | Sloan | Mar 2012 | A1 |
| 20130157918 | Sloan | Jun 2013 | A1 |
| 20130178403 | Sloan | Jul 2013 | A1 |
| 20130298450 | Sloan | Nov 2013 | A1 |
| 20140305030 | Sloan | Oct 2014 | A1 |
| 20200002641 | Sloan | Jan 2020 | A1 |
| Number | Date | Country |
|---|---|---|
| 2496921 | Aug 2006 | CA |
| 1209452 | Mar 1999 | CN |
| 101805657 | Aug 2010 | CN |
| 19723460 | Jan 1998 | DE |
| 0361180 | Apr 1990 | EP |
| 0837122 | Apr 1998 | EP |
| 1203803 | May 2002 | EP |
| 1736529 | Dec 2006 | EP |
| 2619292 | Jul 2013 | EP |
| 2193080 | Jul 1972 | FR |
| 59204700 | Nov 1984 | JP |
| 07233001 | Sep 1995 | JP |
| 2001-271077 | Oct 2001 | JP |
| 199103533 | Mar 1991 | WO |
| 1997019153 | May 1997 | WO |
| 2002034867 | May 2002 | WO |
| 2003064571 | Aug 2003 | WO |
| 2006-015800 | Feb 2006 | WO |
| 2006100188 | Sep 2006 | WO |
| 2007004789 | Jan 2007 | WO |
| 2009078882 | Jun 2009 | WO |
| 2009079020 | Jun 2009 | WO |
| 2009085957 | Jul 2009 | WO |
| 2009085967 | Jul 2009 | WO |
| 2011094571 | Aug 2011 | WO |
| 2012-40153 | Mar 2012 | WO |
| 2012-40153 | Mar 2012 | WO |
| Entry |
|---|
| https://en.wikipedia.org/wiki/Babbitt_(alloy) (Year: 2021). |
| Rudnick, Leslie R., Ed., Synthetic Mineral Oils and Bio Based Lubricants: Chemistry and Technology, Taylor & Francis (2006). |
| Journal of Automotive Engineering, May 1, 2001, vol. 55, No. 5, pp. 67-72. |
| Journal of Automotive Engineering, May 1, 2001, vol. 55, No. 5, pp. 67-72, English translation of: p. 70, last paragraph; Figures 6 and 7. |
| Kioupis, L.I. ; Maginn, E.J., Molecular simulation of poly-{alpha}-olefin synthetic lubricants: Impact of molecular architecture on performance properties, Journal of Physical Chemistry B: Materials, Surfaces, Interfaces, amp Biophysical; Journal vol. 103; Journal Issue: 49; Dec. 9, 1999. |
| http://www.sasoltechdata.com/MSDS/SASOLAB_C12L.pdf. |
| United States Environmental Protection Agency, “Status Report, Chemical Activities,” Third Edition, vol. I (Jun. 1982), cover page, pp. 21, 38, 201. |
| 40 CFR 700 to 789, Revised as of Jul. 1, 2006. cover page, p. 52. |
| Leslie R. Rudnick, Lubricant Additives: Chemistry and Applications, section 17.4.6, p. 428 (2009). |
| Corrosion Inhibitors, http://www.chemtura.com/bu/v/index.jsp?vgnextoid=2e6aeaa547e9f010VgnVCM100000b70215acRCRD&vgnextchannel=2e6aeaa547e9f010VgnVCM100000b70215acRCRD, printed on Jan. 22, 2014. |
| Calcinate C-300CS, http://www.chemtura.com/bu/v/index.jsp?vgnextoid=851c81a7bfd01110VgnVCM1000008ed7010aRCRD&vgnextchannel=2e6aeaa547e9f010VgnVCM100000b70215acRCRD&vgnextfmt=default, printed on Jan. 22, 2014. |
| International search report dated May 11, 2016 for PCT/US16/15256. |
| International Preliminary Report on Patentability, dated Feb. 28, 2017, finding that the subject matter of the claims in counterpart application PCT/US16/15256 are novel and involve an inventive step under PCT articles 33(2) and (3). |
| Declaration Traversing Rejection under 37 CFR 1.132 for application U.S. Appl. No. 14/699,924, by Prof. Nicholas D. Spencer, Department of Materials, ETH Zürich, Switzerland and by Prof. Stefano Mischler, Institute for Materials, EPF Lausanne, Switzerland. |
| http://www.sccoa.com/forums/showthread.php?136304-What-oil-brands-offer-the-best-protection-***Good-read***, printed Jun. 23, 2019. |
| https://www.portcityracecars.com/KENDALL-OIL-GT-1-HI-PERF-20W50.html, printed Jun. 23, 2019. |
| Number | Date | Country | |
|---|---|---|---|
| 20200157458 A1 | May 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62109172 | Jan 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14699924 | Apr 2015 | US |
| Child | 16750368 | US |