Patent Application
20110198013
This application claims priority of European application No. 10001532.0 filed Feb. 15, 2010, which is incorporated by reference herein in its entirety.
The invention relates to a mould for manufacturing a composite part including at least one fibre reinforced matrix for manufacturing a composite part including at least one fibre reinforced matrix, in particular a wind turbine blade.
Composite parts show extraordinary mechanical properties. Thus, composite parts have gained popularity in high-performance products that need to be lightweight, yet strong enough to take harsh loading conditions such as aerospace components (wings or propellers), boat hulls, bicycle frames, racing car bodies or wind turbine blades. While the manufacturing of such composite parts including one or more fibre materials within a duroplastic or thermoplastic resin-like matrix, e.g. a wind turbine blade, usually a plurality of fibre composite layers are built up inside one or more moulds together with other structure parts and the resin-like matrix is injected into the mould(s) preferably under the application of low pressures.
EP 1 310 351 B1 refers to a method for manufacturing wind turbine blades in a closed mould with a mould core inside upper and lower mould parts forming a mould cavity in the shape of the wind turbine blade. After placing fibre material and core material in the mould cavity, a vacuum is applied and the curable resin-like matrix is injected via a filling pipe. To cure the resin-like matrix a special temperature profile has to be realised. Thus, diverse heating and cooling ramps and/or temperature plateaus need to be adjusted and monitored while the resin-like matrix cures forming the wind turbine blade.
A traditional mould structure as used in the above mentioned EP 1 310 351 B1 comprises a monolith fibre composite laminate of certain thickness having water pipes made of copper together with a copper mesh mounted underneath the laminate. The pipes are usually insulated with a foam material, consequently heating and cooling respectively is predominantly forced to progress through the laminate and not to the surroundings.
The water pipes made of copper together with the mesh are heavy components, which require a strong, that is thick laminate to carry the pipes and the mesh. Additionally, the laminate must ensure that temperature variations do not affect the shape of the moulded part(s). Thus, heat transfer from the water in the pipes to the outer surface of the mould and further in a surface of the mould structure is limited and slow due to the relatively low thermal conductivity of the used materials.
Hence, the only possibility for proper controlling of the heating or cooling is achieved by measuring the inflow temperature and the outflow temperature of the fluid flowing through the pipes.
Thus, controlling the heating and cooling processes is challenging. How much heating or cooling is needed and for how long temperature should be applied depends mainly on the mould thickness and the applied heating and cooling means.
So it is a decisive question how to reduce the laminate thickness of the mould to achieve a faster reacting thermal response for a better control of the process, without compromising the structural integrity of the mould.
Thin moulds give rise to unstable, mechanically weak mould structures sensitive to thermal variations and causing large differences in the shape of the moulded parts. In addition, thin moulds might easily break.
The object of the present invention is to provide an improved mould allowing a better controllability of the process of manufacturing of composite parts.
This is achieved by the above mentioned mould, comprising at least one thermal insulating core layer disposed between at least one outer laminate layer and at least one inner laminate layer and at least one heating and/or cooling means disposed in contact or in close proximity to the inner and/or outer laminate layer.
With the at least one thermal insulating core layer disposed between the at least one outer laminate layer and the at least one inner laminate layer the inventive mould comprises a sandwich-like panel or structure having two stiff, strong inner and outer laminate layers separated by the preferably light weight thermal insulating core layer. The separation of the inner and outer laminate layers, which actually carry the load, by a low density core increases the moment of inertia of the panel with little increase in weight producing an efficient structure. Mechanical properties of the sandwich depend on the thermal insulating core layer and inner and outer laminate layer materials as well as the thickness of thermal insulating core layer and the inner and/or outer laminate layers respectively. The inventive mould gives rise to thinner inner and/or outer laminate layers in comparison to the mould disclosed within prior art.
The at least one heating and/or cooling means disposed in contact or in close proximity to the inner and/or outer laminate layer provides in addition with the thinner inner and/or outer laminate layers an improved heat transfer to and through the inner and/or outer laminate layers. In addition, shorter reaction and latent times (the time for the mould to be heated from an initial to a certain process dependent working temperature) are feasible. Thus, the mould can be faster heated or cooled, which has enormous effects on the part to be built. Steep temperatures ramps may be accomplished if need be for saving process energy. Hence, the inventive mould has better and faster adjustability of temperature and gives rise to a better controllable process.
It is possible that the mould comprises heating and/or cooling means disposed in contact or in close proximity either to the inner laminate layer or to the outer laminate layer. Likewise, heating and/or cooling means can be disposed in contact or in close proximity to both the inner and outer laminate layers, which is advantageous regarding the built-up of thermal induced stress, e.g. thermal loading of the mould caused by a temperature gradient between the inner and outer laminate layers. The way of arrangement and total number of heating and/or cooling means involved within the mould depends on the dimensions of the composite part and the employed materials.
Preferably, the heating and/or cooling means is disposed in at least one recess within the thermal insulating core layer and/or the inner and/or the outer laminate layer, or is exposed on top of the thermal insulating core layer or is moulded into the thermal insulating core layer and/or the inner and/or outer laminate layer. Hence, the invention discloses diverse possible locations for arranging the heating and/or cooling means, which can be deemed in combination or as alternatives. Recesses like grooves, cut-outs or the like openings for accommodating the heating and/or cooling means are possible within the thermal insulating core layer and/or the inner and/or outer laminate layers. Besides, it is possible, to dispose the heating and/or cooling means on top, e.g. on the surface or surface near areas of the thermal insulating core layer.
Similarly, moulding of the heating and/or cooling means into the thermal insulating core layer and/or the inner and/or outer laminate layers is feasible. All arrangements are under the premise, that the heating and/or cooling means provide proper and fast heat transfer to the inner and/or outer laminate layers and further to the composite part. The inventive mould can be tempered easily and fast, that is be adjusted to a desired temperature.
The heating and/or cooling means may comprise at least one pipe for transporting a heating and/or cooling medium and/or electrical heating wires, whereby preferably the pipes are at least partially encompassed by the electrical heating wires. The pipes are wound through the mould preferably in a meander-like structure. The electrical heating wires may though also be places above or below the heating pipes. The inventive mould can be heated or cooled respectively by using different heating sources. One is a fluid heating and/or cooling media, whereby the heating and/or cooling means are built as pipes or the like transporting the liquid or gaseous or vaporous heating and/or cooling medium. Generally, any fluid which is capable to convey heat from a hot or cold source, either directly or through a suitable heating device, to a substance or space being heated or cooled is meant by heating and/or cooling media. As an example water is named because of its high heat capacity.
Second, the heating means can comprise electrical wires, thus, the mould is tempered through the application of an appropriate electrical current, which is a very fast method to heat an object. Preferably, the electrical wires at least partially encompass the aforesaid heating and/or cooling pipes representing a possible combination of the pipes and the wires. Metal or alloy wires with a circular cross-section and a suitable electrical resistance per unit length, that results in a desired generation of heat in the wire under applied voltage or current are useable. An appropriate example would be a wire made of nickel-chrome based alloy.
Likewise, it is possible, that the mould comprises areas having only electrical heating wires as heating means and areas having only pipes or pipes as heating and/or cooling means encompassed by electrical heating wires.
Preferably the mould has at least one sensor for determining the flow and/or temperature and/or heating power of the heating and/or cooling medium or the heating and/or cooling means itself. In such a manner all process-relevant parameters are being measured and can be monitored. Process-parameters primarily are flow, temperature and heating power of the heating and/or cooling medium or the heating power of the electrical heating wires. Preferably, the sensors are allocated to each of the heating and/or cooling means. Likewise, it is possible, that only particular heating and/or cooling means comprise these sensors. Referring to the above mentioned meander-like structure of the pipes, it is imaginable, that only every second winding features one or more sensor for example.
In another embodiment of the invention, at least one thermal sensor is disposed at or in the inner and/or outer laminate layer for determining the temperature of the inner and/or or outer laminate layer. Thermal sensors permit a fast and precise measurement of temperature or temperature changes respectively within the immediate area of the thermal sensor. A plurality of thermal sensors maybe placed separately or forming arrays on diverse positions within the mould.
It is advisable, if a coupling agent strengthening the bond between the at least one thermal insulating core layer and the inner and/or outer laminate layer is disposed between the at least one thermal insulating core layer and the inner and/or outer laminate layer. Thus, an appropriate bond avoiding delamination between the inner and/or outer laminate layers and the thermal insulating core layer is provided. Coupling agents in terms of the invention maybe usual adhesive or surface activating methods like plasma- or corona-treatments or any combination of these. In case of heating and/or cooling means disposed on top of the thermal insulating core layer layers of chopped strand mat or the like can act as coupling agent and thus enhance the bond between thermal insulating core layers and the inner and/or outer laminate layers embedding the heating and/or cooling means.
Preferably, the inner and outer laminate layers are made from a fibre composite material, in favour from glass fibre, inorganic fibre or carbon fibre or a combination of said fibres within a cured resin matrix, and the thermal insulating core layer is made from balsa wood, polymeric foam material or a combination of these. Fibre reinforced materials are composite materials made from a polymer matrix reinforced with one or more layers of one or more types of fibres. The fibres are usually based on glass, carbon or aramide, while the matrix comprises usually an epoxy, vinylester or polyester or diverse durable duroplastic or thermoplastic polymers. Specifying the orientation of the reinforcing fibres or layers of fibres can increase the strength and resistance to deformation of the mould, but also the heat conductance of the layers. If need be coupling agents as mentioned above may be provided between single layers or a multi-layer structure. Materials suitable for the inner and/or outer laminate layers generally possess good mechanical properties especially regarding stiffness and rigidity.
The thermal insulating core layer is preferably made from balsa or other types of light weight woods or any polymeric foam material like polyurethane- or polystyrene-based foam or any combination of these. Materials suitable for core layers generally possess low weight and low thermal conductivity.
The thickness of the inner and/or outer laminate layer is within a range of 12 to 4 mm, preferably 8 mm. In comparison to mould known from prior art a reduction of the thickness of the laminate up to 70% is achievable giving rise to the above mentioned better heating and/or cooling properties of the inventive mould. Of course other dimensions of the inner and/or outer laminate layers are also within the scope of the invention, even though a reduction of thickness is desirable.
Furthermore, the invention relates to an apparatus for manufacturing a composite part, especially a wind turbine blade, comprising at least one mould as described above connectable or connected with a heating and/or cooling system with control unit for controlling the heating and/or cooling process of the mould. The inventive apparatus connects the mould with a heating and/or cooling system with a control unit giving rise to an optimised manufacturing, in particular curing process, of the part to be built through providing improved control of the heating and/or cooling, e.g. tempering, of the mould. While manufacturing composite parts strict temperature profiles regarding the curing of the part have to be maintained to obtain high-quality products. This requires an exact adjustment and control of the temperature and/or temperature gradients and if need be other process relevant parameters along the mould. Connecting the inventive mould with a heating and/or cooling system with a control unit makes it possible to optimise manufacturing composite parts and leads to better products in comparison to the existing moulding techniques.
In a preferred embodiment of the invention the mould comprises at least one sensor for determining the flow and/or temperature and/or heating power of the heating and/or cooling medium or the heating and/or cooling means itself and/or at least one thermal sensor disposed at or in the inner and/or outer laminate layer, whereby the control unit is built to receive and process data from the sensor generating control data for controlling the heating and/or cooling system. Thus, the control unit is able to monitor and control all process-relevant parameters from data sent by sensors distributed at diverse positions within the mould. The sensors may, preferably in real time, determine data regarding every process-relevant parameter like the flow and/or temperature and/or heating power of the heating and/or cooling medium or the temperature or heating power of the heating and/or cooling means, e.g. the heating power of the electrical heating wires as well as the temperature or pressure of the fluid flowing through the pipes.
Further, the sensors may send data containing information on one or more process-parameters for example as an input signal to the control unit of the heating and/or cooling system. The input data from at least one sensor is processed and a control data (data set) is generated for controlling the heating and/or cooling system by means of which heating and/or cooling of the mould or parts of it is carried out. In such a manner for example undesired temperature deviations or deviations of other process-parameters are firstly detectable and secondly adjustable on the basis of the control data. Preferably, this takes place in real time. For example, if less heat is provided within one region of the mould, the control data delivers a signal to the heating means which increase the temperature in the according region. Thus, the advantageous control unit embedded or provided with the heating and/or cooling system leads to a better control and adjustability of the temperature of the mould during manufacturing a composite part. The number and arrangement of the moulds comprised by the apparatus is substantially dependent on the geometry of the composite part.
Furthermore, a control unit is adapted to determine and control the degree of cure of the part at least from the data from the thermal sensor. In this embodiment, the control unit is adapted to calculate the degree of cure from the moulded composite part according to the input data from one or more thermal sensors for example disposed in the vicinity of the mould surface using one or more mathematical algorithm(s) or the like in real time. According to the invention the curing process of the composite part being mainly dependent on temperature of the mould is adjustable through the control unit and the heating and/or cooling system controlling and adjusting the heating and/or cooling means and the temperature of the mould.
Likewise, process-time can be shortened as it is clear determinable when curing of the composite part has finished and thus the mould maybe switched from heating to cooling mode by the heating and/or cooling system on the basis of the control data for example. According to the real time input of the temperature or temperature gradients within the mould from the thermal sensors conclusion on the progression of the curing process of the composite part can be made as well as the curing process is controllable by adjusting appropriate temperatures within the mould by the use of the heating and/or cooling means.
The heating and/or cooling system preferably comprises at least one pump and/or at least one valve and/or at least one heating and/or cooling source controlled by the control unit. Thereby, the control unit is adapted to quickly adjust proper mould temperatures according to the employed materials and progression of cure in addition by controlling the heating and/or cooling system. Pumps and valves of the heating and/or cooling system contribute to an accurate control of the heating and/or cooling medium within the heating and/or cooling means and hence the temperature of the mould, preferably according to the progression of cure of the composite part. Likewise, the aforesaid electrical heating wires may be actuated by supplying them with an appropriate electrical current by the heating and/or cooling system. Hence, the control unit and accordingly the heating system incorporates and controls every means for tempering, e.g. heating or cooling, of the mould or along separate areas of the mould respectively.
Moreover, the invention relates to a method for manufacturing a composite part, in particular a wind turbine blade, using the above mentioned apparatus. Along with the inventive apparatus comprising the inventive mould and the inventive heating and/or cooling system with control unit the process of manufacturing of composite parts is significantly improved in terms of control and duration of the process predominantly based on a relative fast adjustability of the temperature of the mould both for heating and cooling due to its comparatively thin inner and/or outer laminate layer giving raise to quick heat transfer from the heat source to the moulded composite part placed within a specific mould cavity exposed within the mould. Preferably, the apparatus comprises an upper and a lower mould part.
Preferably, a control unit receives and processes data from at least one sensor for determining the flow and/or temperature and/or heating power of the heating and/or cooling medium or the heating and/or cooling means itself and/or from at least one thermal sensor and generates control data (data set) for controlling the heating and/or cooling system. The control system in favour permanently receives information on all process-relevant parameters concerning flow, temperature and heating power of the heating and/or cooling medium and/or the heating and/or cooling means itself permanently sent by the sensors by means of which the control unit generates control data for controlling the heating and/or cooling system. Hence, the control unit performs a real-time monitoring and if need be an optimisation of all process-relevant parameters of the manufacturing process predominantly through quick and exact adjustment of the temperature of the mould.
Favourably, the control unit determines the degree of cure of the composite part at least from the data from the thermal sensor which leads to a further optimised process of manufacturing composite parts due to fast adjustment of the temperature through the heating and/or cooling system with the associated control unit capable of determining and predicting the progression of the curing process, e.g. the progress of the degree of cure of the composite part by means of mathematical algorithms implemented in the control unit. The curing process may be controlled or influenced by quick tempering of separate areas of the mould or the entire mould using the heating and/or cooling system. After the part has completely cured, which is also detectable by the control unit based mainly on the data from the thermal sensors, cooling of the mould is instantly initiated and the cured composite part maybe released from the mould.
In the following the invention is described in detail as reference is made to the figures, whereby
Recesses in form of cut-outs 5 are disposed within the thermal insulating core layer 2 in contact to the inner laminate layer 3 accommodating pipes 6 each encompassed by electrical wires 7 wound around the pipes 6 acting as heating and/or cooling means by transporting a heating and/or cooling medium like water for example. Due to a reduced thickness of the inner and outer laminate layer 3, 4 the mould 1 exhibits quicker response to heating or cooling respectively giving rise to a shortened process of manufacturing a composite part. The thickness of the inner and outer laminate layers 3, 4 is approximately 8 mm.
Dotted lines indicate an optional arrangement of additional cut-outs 5′, pipes 6′ and electrical wires 7′ disposed in contact to the outer laminate layer 4, which maybe of advantage as they avoid the occurrence of thermal induced stress within the mould 1 due to temperature gradients between the inner and outer laminate layers 3, 4.
The pipes 6, 6′ are arranged within the mould 1 in a wound, meander-like structure. The pipes 6′ and electrical wires 7′ maybe deemed as an additional heating and/or cooling cycle or otherwise may be connected to the pipes 6 and electrical wires 7 forming a combined heating and/or cooling cycle.
Sensors 17 for determining the flow and/or temperature and/or heating power of the heating and/or cooling medium flowing through the pipes 6, 6′ or the heating and/or cooling means itself are related to the pipes, 6, 6′ or the electrical wires 7, 7′. Thus, for example a permanent or intermitting measurement of temperature, pressure, flow of water or any other liquid acting as heating or cooling medium respectively floating through the pipes 6, 6′ is achievable. Moreover, the temperature or heating power of the electrical wires 7, 7′ is measurable. Analogous sensors 17′ may be provided as well.
Besides, thermal sensors 8, 8′ are distributed at certain locations within the mould 1.
It is possible, that the control unit 12 is adapted to determine the degree of cure of a moulded composite part from the data sent from thermal sensors 8 using mathematical algorithms. This gives rise to a plurality of advantages concerning better products as every product is completely cured after being released from the mould 1, shorter process-times, as it can be concisely determined when curing of the part has finished, as well as better control of the curing process, e.g. that temperature and following curing deviations are detectable and maybe corrected by the associated heating and/or cooling system 11 giving rise to an isotropic heating and/or cooling of the mould and the curing of the composite part in addition.
Moreover, the inventive method also offers a determination of the degree of cure of the moulded part in whole or in parts through the input data at least from thermal sensors 8, 8′ (
The invention offers fast and precise adjustability of temperature of the mould 1 or parts of it by means of the heating and/or cooling system 11 with the associated control unit 12 and even allows determining and influencing the degree of cure of the moulded composite part through an interaction of the control unit and the heating and/or cooling system with the mould 1.