The present invention relates to a moulding device of parts in a material to be moulded, for example concrete, and to a process of production of parts of said material by moulding.
Document WO2008/056065, in the name of the Applicant, describes a production process of concrete parts consisting of introducing a material to be moulded into a mould, placing the mould in an envelope, creating a low pressure in the envelope in order to hold the walls of the mould in place, and deforming the mould. After the concrete sets, the mould may be removed from the envelope. Moulded parts may be produced by this process in a simple manner. The low pressure is generally created in the mould using a vacuum pump, which operates by aspirating the air in the envelope.
Although this process operates quite satisfactorily, the Applicant has shown that, for certain applications, more or less important undesirable deformations could occur on the moulded parts. These deformations are related to a differential shrinkage of the moulded part due to non-uniform dehydration.
There is therefore a need for a device and a moulding process to produce parts in which the mould is contained in an envelope in which a low pressure is created and which makes it possible to reduce, or even eliminate, the undesirable deformations of the moulded parts.
With this aim, the present invention provides a moulding device comprising:
According to an example of an embodiment, the device further comprises a vacuum pump and a connecting element designed to connect the vacuum pump to the envelope.
According to an example of an embodiment, the obturating element is incorporated into the vacuum pump.
According to an example of an embodiment, the mould comprises at least first and second opposing faces. The deforming member is adapted to apply a first pressure on the mould, with interruption of the envelope, on the side of the first face. Said means is adapted to apply a second pressure on the mould, with interruption of the envelope, on the side of the second face.
According to an example of an embodiment, the deforming member is selected from the group comprising a jack and a template.
According to an example of an embodiment, said means comprises at least one load having a mass greater than one kilogram and intended to rest on at least one portion of the mould, optionally with interposition of the envelope, once the low pressure is created.
According to an example of an embodiment, said means has a shape at least partially complementary to the template.
According to an example of an embodiment, the device further comprises at least one draining element in the form of a sheet or membrane in the envelope.
According to an example of an embodiment, the device further comprises at least two draining elements in the envelope, the mould being interposed between the two draining elements.
The invention also relates to a production process, comprising the following steps:
According to an example of an embodiment, the vacuum port is connected to a vacuum pump by a connecting element. The step of creating the low pressure comprises turning the vacuum pump on and the step of stopping the gas flow comprises turning the vacuum pump off.
According to an example of an embodiment, the step of stopping the gas flow comprises at least partially obturating the connecting element.
According to an example of an embodiment, the mould is deformed by a deforming member selected in the group comprising a jack and a template.
According to an example of an embodiment, the mould comprises at least first and second opposing faces. The deforming member applies a first pressure on the mould, with interposition of the envelope, on the side of the first face. Said means applies a second pressure on the mould, with interposition of the envelope, on the side of the second face.
According to an example of an embodiment, the step of applying pressure comprises placing at least one load on at least a portion of the mould, optionally with interposition of the envelope.
According to an example of an embodiment, said means applies a substantially uniform second pressure on the mould, with interposition of the envelope, over more than half of the second face.
Through many trials, the Applicant has shown that the shrinkage was at least partly due to the water vapour present in the envelope being aspirated by the vacuum pump when the latter is connected to the envelope by the vacuum port to create the low pressure in the envelope. This results in accelerated drying of the moulding material, capable of causing undesirable deformations of the moulded part.
The Applicant has shown that, once created, the low pressure in the envelope is only slowly reabsorbed even when the gas flow, which led to the forming of the low pressure in the envelope, is stopped. The mould is then advantageously held in place by the envelope during deformation of the mould and simultaneously the time is shortened during which water vapour is extracted from the envelope. Undesirable drying of the material to be moulded is thus reduced and the shrinkage of the material to be moulded is reduced.
Furthermore, by exerting on the mould, in addition to the pressure exerted by the envelope, additional pressure by a means other than the envelope in order to keep the mould in position, the mould is advantageously held in place in the desired deformed configuration.
The expression “hydraulic binder” is understood according to the present invention to mean for example a pulverulent material which, when mixed with water, forms a paste that sets and hardens by a series of hydration reactions and processes and which, after hardening, preserves its strength and its stability, even under water.
The term “concrete” is understood for example to mean a mix of hydraulic binder, aggregates, water, optionally additives and optionally mineral additions, for example high-performance concrete, very high-performance concrete, self-placing concrete, self-levelling concrete, self-compacting concrete, fibre-reinforced concrete, ready-mixed concrete or coloured concrete. The term “concrete” is also understood for example to mean concretes that have undergone a finishing operation, such as bush-hammered concrete, deactivated or washed concrete, or polished concrete. This definition also includes pre-stressed concrete. The term “concrete” includes mortars. In this specific case, the concrete comprises a mix of hydraulic binder, sand, water and optionally additives and optionally mineral additions. According to the invention, the term “concrete” denotes indistinctly fresh concrete and hardened concrete.
According to the invention, the term “aggregates” denotes for example gravel, coarse aggregates and/or sand.
The term “setting” is understood according to the present invention to mean the process whereby a hydraulic binder passes into the solid state by chemical hydration reaction. Setting is generally followed by a hardening period.
The term “hardening” is understood according to the present invention to mean the acquisition of mechanical properties of a hydraulic binder after the end of setting.
Other characteristics and advantages of the invention will appear on reading the following detailed description of embodiments of the invention given solely by way of example and with reference to the drawings in which:
The same elements are denoted on the various figures by the same references. Furthermore, only the elements necessary to understand the present invention are described and shown in the figures.
The device 10 comprises an envelope 12 and a mould 14 which, during part of the moulding process, is placed in the envelope 12. The mould 14 is designed to receive the material used to make the parts, for example concrete. The envelope 12 includes a vacuum port 15 designed to be connected to a vacuum pump 16 by a connecting element 17, for example a pipe or hose. The vacuum pump 16 is, for example a vane pump (lubricated or dry), a piston pump, a liquid-ring pump, a diaphragm pump, a vacuum ejector using vapour or a compressed gas, a Roots pump or a dry (non-lubricated) pump. When it is not connected to the connecting element 17, the vacuum port 15 is in a closed state, i.e. it does not allow a flow of gas to pass through it.
The vacuum pump 16 is designed to create a low pressure, or vacuum, in the envelope 12 relative to atmospheric pressure. By way of example, a low pressure in the envelope 12 relative to atmospheric pressure may be obtained, using the vacuum pump 16, of for example −0.5 bar or less, for example −0.8 bar or less, for example, equal to −0.9 bar. The device 10 may be sufficiently rigidified by the low pressure in the envelope 12 so that the material to be moulded does not shift inside the mould 14 when the mould 14 is submitted to deformation. The material can then remain at a constant thickness in the mould 14. The low pressure allows the constituent elements of the moulding device 10 to become integral. In particular, the envelope 12 and/or the mould 14 may each be provided with two lips on their periphery and which are pressed against each other under the effect of the low pressure. These lips ensure in a simple manner the closing of the envelope 12 and of the mould 14 respectively. The use of mechanical sealing means may thus be avoided. The lips may also be made with a fold on one of the lips and a groove on the other of the lips, the low pressure provoking the fold to penetrate in the groove in order to ensure better sealing of the envelope 12 and/or the mould 14.
Advantageously, by creating the low pressure within the envelope 12, pumping of the material located in the mould 14 is avoided. The air trapped in the envelope 12 is aspirated by the vacuum port 15. If the vacuum port 15 were able to create a low pressure directly in the mould 14, the material to be moulded would also risk being pumped. Thus, the moulding material is confined by the mould 14 inside the envelope 12 and simultaneously a low pressure can be created in the envelope 12.
The envelope 12 comprises for example a top portion 121 and a bottom portion 122. The mould 14 is placed between the bottom portion 122 and top portion 121. The mould 14 rests on the bottom portion 122. The mould 14 may simply be sandwiched by the envelope 12. It is sufficient to place the mould 14 on the bottom portion 122 and to close the envelope using the top portion 121, the top portion 121 acting as a cover. The envelope 12 is preferably made of a flexible material. The envelope 12, due to its flexibility, may be deformed. The envelope 12 is also flexible in order to favour the creation of the low pressure in the envelope 12. The envelope, due to its flexibility, may take on the shape of the mould 14 under the effect of the low pressure. For example, the envelope 12 is of a plastic material.
The mould 14 may comprise a top shell 141 and a bottom shell 142. The bottom shell 142 of the mould 14 rests on the bottom portion 122 of the envelope 12. The material to be moulded may be confined in a simple manner by the mould 14. The material is distributed over the bottom shell 142 of the mould, then the mould 14 is closed by means of the top shell 141. The mould 14 is preferably of a flexible material. The flexibility of the mould 14 has several advantages: the mould 14 may deform under the action of a deforming member; the mould 14 favours the confinement of the material in the mould under the effect of the low pressure created in the envelope 12; and better contact between the mould 14 and the material to be moulded may be obtained. By way of example, the mould 14 is of silicone or polyurethane.
The envelope 12 is provided with the vacuum port 15. Preferably, the vacuum port 15 is on the top shell 121. The envelope 12 may rest in operation on a support by virtue of its bottom portion 122. Since the mould 14 rests on the bottom portion 122 of the envelope 12, it is preferable to provide the vacuum port 15 on the top portion 121 of the envelope 12 in order to facilitate the creation of the low pressure.
The device 10 comprises an obturating element 18 which is designed, when the low pressure has been created in the envelope 12, to interrupt any gas flow through the vacuum port 15. The low pressure in the envelope 12 may be maintained whilst interrupting the functioning of the vacuum pump 16. However, after the vacuum pump 16 has been turned off, the pressure nevertheless tends to increase slowly in the envelope 12 due to leaks. However, the low pressure remains long enough in the envelope 12 to ensure that the mould 14 is held in place by the envelope 12. The obturating element 18 may be incorporated into the vacuum pump 16. In this case, the obturating element 18 may be automatically released to obturate one end of the connecting element 17 when the functioning of the vacuum pump 16 is interrupted. In
The device 10 may also include at least one thin draining element 20 in the envelope 12, having the form of a membrane or sheet, etc. The draining element 20 favours the creation of the low pressure. The draining element indeed prevents the envelope 12 from locally adhering to the mould 14, under the effect of the low pressure created within the envelope 12, which could lead to air bubbles being trapped and hinder further creation of the low pressure. By way of example, the draining element 20 is of a woven or non-woven material. Such a material is not air-tight but allows the passage of air. While the low pressure is being created, the draining element 20 favours the circulation of air in the direction of the vacuum port 15. The draining element 20 is for example located between the top portion 121 of the envelope 12 and the top shell 141 of the mould 14. The draining element 20 thus favours the circulation of air between the top portion 121 and the top shell 141. Alternatively, the draining element 20 may be located between the bottom portion 122 of the envelope 12 and the bottom shell 142 of the mould 14. The draining element 20 therefore facilitates the circulation of air between the bottom shell 142 of the mould 14 and the bottom portion 122 of the envelope 12. The circulation of air is all the more favoured when, due to gravity, the bottom shell 142 rests against the bottom portion 122 and the low pressure could be difficult to create in this zone of the envelope 12 in the absence of the draining element 20 because air bubbles would risk being trapped between the mould 14 and the envelope 12. The draining element 20 forms a buffer zone between the mould 14 and the envelope 12. Preferably, the device 10 comprises two draining elements 20 in the envelope 12, one of the draining elements 20 being placed between the top portion 121 and the top shell 141 and the other draining element 20 being placed between the bottom portion 122 and the bottom shell 142. The presence of two draining elements 20 favours the creation of the vacuum throughout the envelope 12.
A draining element 22 may be provided in the mould 14. The draining element 22 then favours the creation of the low pressure in the mould 14. The low pressure created in the envelope 12 also propagates into the mould 14 through the edges of the shells 141 and 142. However, the low pressure in the mould 14 is less important than the one present in the envelope 12, whereby the material to be moulded is not aspirated at the same time. The draining element 22 in the mould 14 also favours the circulation and aspiration of the air contained in the mould 14. The air contained in the mould 14 is mainly between the material to be moulded and the top shell 141 of the mould 14. The draining element 22 is therefore preferably located in this zone. Thus, the shell 141 is prevented from being pressed directly against the material, permitting air to circulate between the shell 141 and the material while the low pressure is created within the envelope 12. The draining element 22 may be made of the same material as the draining element 20 and allow the air to circulate.
An insert-guiding element (not shown) may be provided in the mould 14. This guiding element corresponds for example to a flexible sheet placed between the shell 141 and the material to be moulded and covering the material to be moulded. For example, the guiding element has openings for the passage of parts or inserts that partially or completely penetrate into the material to be moulded. The inserts are thus suitably positioned.
The device 10 includes at least one deforming member 19 (two separate deforming members 19 being shown in
The deforming members 19 of the mould 14 are beneath the mould 14. At rest, the mould 14 lies flat, and, when the deforming members 19 are activated, they deform the mould 14 against gravity. The advantage is that the practical embodiment of the deformation is simpler to do than if the mould was maintained vertically and the members 19 deformed the mould laterally. A problem would indeed arise to maintain the material in place in the mould if the mould were held vertically. There would be a risk of the material flowing within the mould and the thickness of the material would vary.
More precisely, the deforming members 19 act on the envelope 12. The organs 19 are in contact with the envelope 12. By the acting on the envelope 12, the mould 14 is deformed. The advantage is that the risks of puncturing the mould 14 are reduced since a double protection is provided by the envelope 12 and the mould 14. The deforming members 19 are therefore also located beneath the envelope 12. The action on the envelope 12 and the deformation of the mould 14 are done against gravity, by lifting or supporting the envelope 12 and the mould 14.
According to the first example of an embodiment, the deforming members 19 are for example jacks. The deforming members 19 may also be more simply metal rods, the height of which is adjusted by inserting shims between the base of the rod and the ground. The advantage of using jacks is that the shapes which may be obtained are infinite, it being understood that the jacks may occupy various positions. Advantageously, the axes of the jacks or of the metal rods are positioned vertically. The device 10 may further comprise ball joints 31 (visible in
According to the first example of an embodiment, the device 10 may further comprise a table 24. The envelope 12 at rest, is on the table 24. Thus, the introduction of the material to be moulded into the mould 14 is facilitated. While the bottom portion 122 of the envelope 12 rests on the table 24 and the bottom shell 142 rests on the portion 122, it is indeed possible to spread the material easily over the bottom shell 142. The deforming members 19 extend through the table 24. When the device 10 is activated, the deforming members 19 lift the envelope 12 from the table 24. The members 19 lift the envelope 12 locally so as to create a local deformation of the mould 14. The members 19 extend from beneath the table 24 to the point of contact with the envelope 12, through the table 24. The table 24 therefore has openings 26 for the passage of the members 19.
The deformation of parts which, at rest, may for example measure approximately 5 m2 may be obtained by the device 10. The deforming members 19 are regularly or not regularly arranged, beneath the surface of the envelope 12. Preferably, the members 19 are arranged regularly in a grid pattern. The deformation of the mould 14 can thus be better controlled.
In addition to the envelope 12, the device 10 further comprises an additional means 30 making it possible to apply pressure on the mould 14, at least after the mould 14 has been deformed. In the first example of an embodiment, the additional means 30 corresponds to a load 30 which is designed to be placed on the envelope 12, when the mould 14 is placed in the envelope 12 during the process for production of moulded parts, as will be described in greater detail below. The load 30 corresponds to one or more massive elements, for example weights. By way of example, in
The invention also relates to a process for the production of parts. The parts may be of concrete, preferably high-performance fibre-reinforced concrete. Thin parts, a few millimeters in thickness, may be produced with this type of concrete.
Generally, the production process comprises a step of introducing a material to be moulded into the mould 14. The process then comprises a step of placing the mould 14 in the envelope 12. The envelope 12 is closed and a low pressure is created in the envelope 12 by the formation of a gas flow through the vacuum port 15. The low pressure in the envelope 12 may even propagate into the mould 14, attention being drawn to the fact that the material to be moulded does not escape from the mould 14. The process then comprises a step of deforming the mould 14. The process further comprises a step of stopping the gas flow after the creation of the low pressure in the envelope 12, this step being possible to be carried out before or after the deformation of the mould 14. The process then comprises a step of applying pressure, by the means 30 different from the envelope and the deforming members, on at least a portion of the mould 14, at least after the gas flow is stopped.
The material dries (or sets) at the same time as the mould 14 is deformed. Thus, a part having a particular shape is obtained, which may give an aesthetic aspect to a structure. Preferably, the process is repeated so as to obtain a plurality of parts with a particular shape. The parts may then, be assembled so that the obtained jigsaw offers an aesthetic impression. Parts having a low thickness (for example 15 mm) may in particular be moulded by the process according to the invention. Indeed, the thickness of the material is controlled throughout the duration of the process.
As described above, the interruption of the operation of the vacuum pump 16 can automatically block the flow of air through the vacuum port 15. The operation of the vacuum pump 16 may be interrupted before or after the load 30 has been put into place, even before the envelope 12-mould 14 assembly has been deformed by the deforming members 19. After the vacuum pump 16 is turned off, the pressure in the envelope 12 slowly rises, in particular due to leaks at the level of the envelope 12. However, the presence of the load 30 prevents the mould 14 from shifting and in particular the top shell 141 from shifting relative to the bottom shell 42. After the moulding material has set, the mould 14 may be removed from the envelope 12.
After a defined period of time, the part is removed from the mould 14. The obtained part has a surface which may include humps and hollows. The obtained part is a three-dimensional object with a locally variable curvature. The curvature may locally have a positive or negative sign. Preferably, there is no singularity or discontinuity. If a single deforming member 19 is implemented, the surface may have a single hump. If several members 19 are used, then the surface may have a plurality of humps of greater or lesser height and separated by hollows. The humps may then correspond to the locations of the members 19 acting on the envelope 12, while the hollows may correspond to the locations where there are no deforming members 19.
A part may be produced by moulding using the process described above. It is conceivable for the process to be repeated so as to produce several parts by moulding and then assemble these parts between themselves. The parts to be assembled are then modules. The surface thus produced is itself a three-dimensional object with a locally variable curvature. The curvature may locally have a positive or negative sign. Preferably, there is no singularity or discontinuity. A larger area (for example 8000 m2) may then be obtained by producing smaller parts (for example up to 20 m2, preferably 5 m2, more preferably 2 m2, even more preferably 1 m2). Advantageously, the deforming members act in the same way on the edges of two parts that are intended to be contiguous in the assembly, so as to be able to assemble the parts between themselves by their edges and that the obtained assembly is continuous from one part to the other. The advantage of the device and of the process is that the parts obtained and joined together are thin, therefore relatively less heavy.
The initial steps of the process are identical to those described above in relation to
placing the load 30 on the envelope 12-mould 14 assembly;
blocking the air flow passing through the vacuum port 15; and
interrupting the operation of the vacuum pump 16.
As described above, the interruption of the operations of the vacuum pump 16 may induce an automatic blocking of the flow of air by the vacuum port 15. The operation of the vacuum pump 16 may be interrupted before or after the load 30 has been put into place, even before the envelope 12-mould 14 assembly has been applied on the template 19. The pressure in the envelope 12 then slowly rises, in particular due to leaks at the level of the envelope 12. However, the presence of the load 30 prevents the mould from shifting and in particular prevents the top shell 141 from shifting relative to the bottom shell 142. After the moulding material sets, the mould 14 can be removed from the envelope 12 and the moulding material can be demoulded.
In the examples of the embodiments described above, in addition to the envelope 12, the additional means 30 allowing pressure to be applied on the mould 14 corresponds to a load placed on the mould 14 with interposition of the envelope 12. However, it is clear that the additional means 30 may correspond to any type of system making it possible to keep the mould 14 in place pressed against the deforming member 19. By way of example, the additional means 30 may correspond to a fastening system of the mould 14 to the template 19, for example a set of straps or jaws keeping the mould 14 pressed against the template 19. Preferably, the additional means 30 allows pressure to be applied on the mould 14 as uniformly as possible over the largest possible portion of the mould 14 opposite the template 19.
The material used to produce the part by the process and the device is preferably ultra-high performance fibre-reinforced concrete (UHPFC). This part has for example a thickness of 5 to 50 mm. Very thin parts may thus be obtained. Preferably the part has a thickness of approximately 15 mm.
Ultra-high performance fibre-reinforced concretes are concretes having a cementitious matrix containing fibres. The reader may refer to the document entitled “Bétons fibrés à ultra-hautes performance [Ultra-high performance fibre-reinforced concrete]” by SETRA (French Road and Motorway Technical Studies Service) and the AFGC (French Civil Engineering Association). The compressive strength of these concretes is generally greater than 150 MPa, even greater than 250 MPa. The fibres may be metal fibres, organic fibres, or correspond to a mix of organic and metal fibres. The binder content is high (i.e. the W/C ratio is low, generally the W/C ratio is at most approximately 0.3).
The cementitious matrix generally comprises cement (Portland cement), an element with a pozzolanic reaction (in particular silica fume) and a fine sand. The respective particle sizes are within chosen ranges, depending on the respective nature and quantities thereof.
By way of examples of cementitious matrices, mention may be made of the matrices described in patent applications EP-A-518 777, EP-A-934 915, WO-A-95/01316, WO-A-95/01317, WO-A-99/28267, WO-A-99/58468, WO-A-99/23046, WO-A-01/58826, and WO-2008/056065, to which the reader may refer for further details.
| Number | Date | Country | Kind |
|---|---|---|---|
| 09 02246 | May 2009 | FR | national |
This application is a divisional application of U.S. patent application Ser. No. 13/319,878, filed Nov. 18, 2011 which in turn is the U.S. National Stage of PCT/FR2010/050885, filed May 7, 2010, which in turn claims priority to French Patent Application No. 0902246, filed May 11, 2009, the entire contents of all applications are incorporated herein by reference in their entireties.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3492392 | Kasmatsu et al. | Jan 1970 | A |
| 5464337 | Bernardon et al. | Nov 1995 | A |
| 20090309272 | Behloul et al. | Dec 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 41 40 012 | Jun 1992 | DE |
| 0 393 767 | Oct 1990 | EP |
| 0 518 777 | Dec 1992 | EP |
| 0 934 915 | Aug 1999 | EP |
| 1 214 175 | Apr 1960 | FR |
| 2 908 066 | May 2008 | FR |
| 1 466 663 | Mar 1977 | GB |
| WO 9501316 | Jan 1995 | WO |
| WO 9501317 | Jan 1995 | WO |
| WO 9923046 | May 1999 | WO |
| WO 9928267 | Jun 1999 | WO |
| WO 9958468 | Nov 1999 | WO |
| WO 0158826 | Aug 2001 | WO |
| WO 2008056065 | Jun 2008 | WO |
| Entry |
|---|
| International Search Report issued for International Application No. PCT/FR2010/050885, dated Oct. 14, 2010. |
| International Preliminary Report on Patentability issued for International Application No. PCT/FR2010/050885, dated Nov. 24, 2011. |
| Number | Date | Country | |
|---|---|---|---|
| 20140319719 A1 | Oct 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13319878 | US | |
| Child | 14328462 | US |