The present invention relates to sanitary or household absorbent papers, in particular to creped cellulose-web papers, hereafter tissue papers.
More specifically, the invention concerns paper towels for industrial or household uses. In this application the papers exhibit wet strength resulting from the addition of a specific resin to the pulp containing the suspended paper fibers before the sheet is formed. Once crosslinked, the resin constitutes a structure which at least temporarily resists the degrading effects of water.
It is known in this field to make paper sheets consisting of several creped plies exhibiting a specific surface weight between 12 and 30-35 g/m2 and fitted with protrusions made by embossing.
Embossing imparts bulk to the sheet and improves touch, softness and liquid absorption. Attempts already have been made to further improve absorptivity by means of multi-ply sheets made by linking at least two plies, each consisting of at least one of the embossed foils.
In this manner a sheet of several plies is attained which offers specific mechanical features, such as tensile strength and absorptivity.
Presently there are two embossing and ply-joining modes depending on the desired properties of the end product.
The first mode relates to “nesting”. It consists in first embossing each ply separately so as to form at the surface generally substantially frustoconical or frusto-pyramidal protrusions. Next, an adhesive is deposited on the top of the protrusions of one of the plies following its embossing but before it is detached from the embossing cylinder. The plies are mutually lined up in such a way that the protrusions of one ply face the protrusions of the other and that these protrusions of one side and the other shall nest between one another. Finally they are assembled by moving them close together. Accordingly, the two plies are connected by films of adhesive at the protrusion tops of one ply and unembossed zones which are situated between the protrusions of the other ply. The cavities subtended in this structure reliably assure improved absorption. Furthermore, the outer sides offer a smooth and velvety touch on account of the alveoles constituted by the backs of the protrusions. This technique is illustrated in U.S. Pat. No. 3,867,225.
The second joining mode is known in the field as “tip-to-tip”. It differs from the preceding mode by the relative configuration of the two plies. After these were separately embossed, they are moved one on the other in a way to make the tips of the protrusions coincide in part or in whole. The plies are connected to each other by the tip-to-tip arrayed protrusions. This technique is illustrated in U.S. Pat. No. 3,414,459.
The products manufactured by the above techniques have long exhibited a plain embossing pattern wherein the protrusions were uniformly arrayed in two crossing directions. While such a pattern allows attaining homogeneous properties, its visual attractiveness is modest.
For several years already attempts have been made to enhance product appearance by spreading the protrusions in different ways. Applicant; for example, is marketing a paper towel of which the surface alveoles are arrayed in concentric circles suggesting the propagation of a liquid which was poured on an absorbent sheet being absorbed, or also surface wave propagation when a drop of water falls on a liquid. More specifically, such a pattern can consist of distinct first disk-shaped zones defined by three or four concentric circles. The disks in turn are regularly configured along crossing directions. Second zones defined between adjacent disks generally assume a diamond shape.
Provided such a pattern is visually perceptible to the user, it will be commercially significant.
The objective of the present invention is to manufacture products exhibiting patterns of which the topography is emphasized and of which the visual perceptibility is enhanced.
Applicant attained this objective in the form of a multi-ply sheet comprising a first ply and a second ply, each made of tissue paper and exhibiting a specific surface weight between 12 and 35 g/m2, the first ply comprising a first embossing pattern consisting of first protrusions projecting from the first ply's inner surface and in particular subtending arrays and of which at least part of the tops is connected to the inner surface of the opposite second ply, the sheet being characterized in that the first ply comprises a second embossing pattern consisting of second protrusions projecting from the inner surface of the first play and of a lesser height and of which the density is higher and of which at least part of the tops are situated in the same plane as the tops of the first protrusions and where at least the part is connected to the inner surface of the second ply.
Thanks to the structure thusly defined, the visual perception of the first pattern is increased by creating on the outer surface second zones situated at a tier different from the first zones exhibiting the first pattern. The 3D effect is enhanced. Moreover, the sheet thickness is observed as being more homogeneous. Also this effect is intensified by the higher area density of the protrusions of the second zone.
The invention furthermore contains other features whether considered singly or in combination.
The area density of the protrusions configured on the first zones is less than 20 protrusions/cm2 and preferably less than 12 protrusions/cm2. Such a distribution of the first protrusions corresponds to protrusion heights between 1 and 2 mm. This design allows subtending spaces between the first embossed ply and the second ply that assure good absorption without thereby incurring degradation of crush resistance. This applies in particular when the second ply is unembossed in the zones facing the first and second zones.
The protrusions arrayed in the second zones are shallower than the first protrusions but their density exceeds 30 protrusions/cm2, preferably being greater than 40 protrusions/cm2. Because of their density and different height, the second protrusions constitutes plateaus improving the contrast with the first zones.
The first and the second zones are adjacent.
Third protrusions in the form of small partitions connect two adjacent first protrusions of an array. In order to further enhance the visual perceptibility of the first protrusion pattern, small partition-type protrusions are created to reinforce the layout of the array without thereby degrading the tear resistance.
The second ply is made by the “through-air-drying” method. The combination of an embossed tissue paper ply made conventionally by wet pressing with a ply made by means of through-air-drying is especially advantageous within the scope of the present invention. In this manner absorption is optimized with respect to mechanical strength.
The invention furthermore proposes a cylinder used to emboss the first ply. This cylinder is fitted with first embossing tips subtending arrays in first zones and with second embossing tips of lesser height but higher density. The tops of the first and second embossing tips are situated in the planes that are tangential to the cylinder generatrices.
The invention also proposes a method for manufacturing the product.
Other features and advantages of the invention are elucidated in the comprehensive following description and in relation to the attached drawings.
Depending on the embodiment shown, the second ply can be unembossed.
In one CWP papermaking method, the water-suspended fibers are deposited on a wire to form a web. Then the web is drained and transferred on a felt to be forced with the felt by a press against a drying cylinder. The web then is detached from the cylinder and creped by means of a scraper blade. Lastly, it is wound on a reel before being transformed into a final product. This summarily described technique is called “conventional”. There are of course many variants of it.
A TAD technique following draining consists in drying the web, at least partly until dryness is high enough to freeze the fibers within the web, without applying pressure to it. Where desired, drying is completed by applying the web against a heated cylinder. Thanks to this first drying stage, the web can be applied against the cylinder. The web retains part of its volume. This cylinder also allows creping it. Drying in absence of pressure is implemented by blowing hot air through the sheet after it was drained. This technique is known in the trade as TAD and allows attaining a thicker sheet of higher mass density than when using the conventional technique.
The web, i.e., the sheet 10 comprises two characteristic directions denoted by the arrows L and T in
The first embossing pattern 16 on the upper ply is shown as a whole in
In this embodiment the first zones 16 therefore are disks. These disk in turn are configured in two crossing directions of a network of square meshes, in this instance at 45° relative to the direction of advance L. Inside each mesh constituted by the first zone disks are located second protrusions 38 constituting second zones 36. These protrusions 38 exhibit a height H2 shallower than that of the first protrusions 18. Height H2 is between 0.2 and 1.5 mm as indicated in
The second ply 14 is unembossed. The height differential of H1 and H2 is between 0.3 and 1.3 mm.
An engraved cylinder, such as is shown in
In the shown embodiment, the embossing tips are frustoconical and have a circular base. Other geometries are also applicable, for instance rhomboids or pyramidal frustra with polygonal or linear bases.
The manufacturing method for a claimed sheet 10 consists in embossing a creped tissue paper ply on the cylinder by pressing the ply against the cylinder using a rubber cylinder or a cylinder made of another resilient material. The embossing pressure must be high enough that the tissue paper enters the space between the embossing tips of the first zones. In particular, within the first zones, the paper must penetrate a depth exceeding H′2. The second zones' geometry of a plateau with a tight pattern on the other hand restricts paper penetration between the embossing tips of the second zones. Instead the rubber is repelled toward the second zones' periphery. As a result this boundary between the first and the second zones shall be even more distinct.
In order to manufacture a two-ply sheet of the invention, adhesive is deposited on the flats 29 and 49. The flats being at the same height, the adhesive can be deposited in a simple manner using an adhesive-applying cylinder. Next, an unembossed ply is moved near and is pressed against the tops so that bonding is set up between the two plies along these tips. Once assembly has been achieved, the sheet is cut and wound conventionally into a finished product.
In this method, the bonding of the plies to one another is enhanced relative to a two-level embossing procedure of the prior art because all embossing tips have been bonded.
The above description relates to a two-ply sheet. However, the scope of the invention extends beyond two plies. Illustratively the embossed ply itself can consist of two layers; and so the unembossed ply. Obviously too the shown pattern is merely illustrative. Other patterns can be considered to the extent they conform to the disclosure of the present invention. In particular a special illustrative embodiment includes a pattern consisting at least in part of second protrusions linearly arrayed for example to show a flower.
Some of the first zone embossing tips are shown which run along an array of this line. In this embodiment, salients in the form of small partitions 30 are configured between the adjacent embossing tips 28 of an array. The embossing tips 28 are frustoconical or frusto-pyramidal with a flat top 29. The top 31 of the small partitions 30 is lower than the tops 29. The selected gap is between 0.4 and 0.9 mm. In other words, this is also the height differential of the heights H′1 and H′3.
The thickness “e” of the small partitions 30 is less than that of the embossing tips 28. In other words, the heights being the same, the thickness “e” is less than the embossing tip's diameter. Accordingly, the small partition thickness is less by 10 to 50% than that of the embossing tips in order in particular to limit the additional embossing pressure resulting from the presence of the small partitions. Preferably, the slope of the small partitions is the same as that of the embossing tips.
The gap between the heights H′1 and H′3 suffices to allow the rubber coming into contact with the upper small partition surface 31 during embossing and thus to at least partly emboss the small partition into the sheet.
Number | Date | Country | Kind |
---|---|---|---|
01403221 | Dec 2001 | EP | regional |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/FR02/04215 | 12/6/2002 | WO | 00 | 7/13/2004 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO03/050353 | 6/19/2003 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
2043351 | Fourness et al. | Jun 1936 | A |
2177490 | Kieffer | Oct 1939 | A |
3414459 | Wells | Dec 1968 | A |
3867225 | Nystrand | Feb 1975 | A |
4320162 | Schulz | Mar 1982 | A |
4659608 | Schulz | Apr 1987 | A |
4927588 | Schulz | May 1990 | A |
4978565 | Pigneul et al. | Dec 1990 | A |
5093068 | Schulz | Mar 1992 | A |
5562805 | Kamps et al. | Oct 1996 | A |
5702571 | Kamps et al. | Dec 1997 | A |
5840404 | Graff | Nov 1998 | A |
5861081 | Bredendick et al. | Jan 1999 | A |
6253373 | Peri | Jun 2001 | B1 |
6365000 | Dwiggins et al. | Apr 2002 | B1 |
6423397 | Roussel | Jul 2002 | B1 |
6524683 | Roussel et al. | Feb 2003 | B1 |
6551691 | Hoeft et al. | Apr 2003 | B1 |
6589634 | Schultz et al. | Jul 2003 | B2 |
6942755 | Basler et al. | Sep 2005 | B2 |
7083845 | Graff | Aug 2006 | B2 |
20010008179 | Oriarian et al. | Jul 2001 | A1 |
20020155257 | Schultz et al. | Oct 2002 | A1 |
20020160155 | Muller | Oct 2002 | A1 |
20030021954 | Graff | Jan 2003 | A1 |
20030026953 | Muller | Feb 2003 | A1 |
20030118782 | Graff | Jun 2003 | A1 |
20050034828 | Graff et al. | Feb 2005 | A1 |
20050067089 | Graff et al. | Mar 2005 | A1 |
20050103456 | Hein et al. | May 2005 | A1 |
20070122595 | Basler et al. | May 2007 | A1 |
Number | Date | Country |
---|---|---|
1 101 866 | May 2001 | EP |
1101867 | May 2001 | EP |
1270196 | Jan 2003 | EP |
1319748 | Jun 2003 | EP |
WO 9936253 | Jul 1999 | WO |
WO 0040800 | Jul 2000 | WO |
WO 02068758 | Sep 2002 | WO |
WO 03050353 | Jun 2003 | WO |
Number | Date | Country | |
---|---|---|---|
20050034828 A1 | Feb 2005 | US |