Patent Application
20050276956
The present invention relates to a multi-layer article. More particularly, an article with at least one layer that is an absorbent cellulosic web, and at least one layer that is a multi-ply laminate with at least three plies, including a center ply that is apertured.
Laminate articles formed by the joining of discrete webs in a layered relationship are well known in the art. Laminate articles include laminates of dissimilar materials. The materials may be dissimilar in mechanical tensile properties, thermal properties, or visual/tactile properties. For example, a non-woven web may be joined to a relatively stiff fabric to provide for a soft surface feel to the fabric.
The dissimilar materials may be joined by melt bonding, adhesive bonding, ultrasonic bonding, and the like. Bonding methods are often determined by the materials themselves, and often require adhesive bonding. For example, a laminate of materials having widely differing melt properties may require an adhesive layer between laminate layers. Even materials having similar melt properties, such as non-woven and thermoplastic film materials are often joined by adhesive for adequate bonding to prevent unwanted delamination. Although adhesive may be necessary, such processing methods can be expensive due to the addition of adhesive, and the resulting laminate is often relatively stiff, depending on the laminate materials and the level of adhesive added.
Often laminate articles are intended to combine properties of the constituent layers to achieve synergistic benefits. For example, a multi-layered non-woven laminated article could be intended for use as a substitute for a woven web such as a textile web. A web comprised of a layer of thermoplastic man-made fibers and a layer of cellulose-based fibers is known. The cellulose-based fiber layer is disclosed as thermally bonded to the thermoplastic man-made fiber layers at spaced apart locations. However, it appears that thermal bonding between all the layers is necessary to produce the requisite bonding.
EP-A-112,654 issued to Haq, et al. discloses a laminate comprising two sheets of non-woven fabric or the like having sandwiched between them a solid core material which may be a highly porous, optionally liquid-containing, polymer. The two outer sheets are bonded to each other, without involving the core material, by means of a plurality of small, spaced bonding points, for example, spot-welds. Preferably the core material is in continuous sheet form and is perforated to accommodate the bonding points. However, it appears it would present a significant processing problem to register the perforations of the core material in order to have the outer layers bonded therethrough.
Non-woven webs are beneficial as components of disposable consumer products, such as diapers, incontinence briefs, training pants, feminine hygiene garments, and the like, as well as in wipes such as disposable wet wipes. However, used alone, such non-wovens are limited in the range of beneficial properties, including visual, tactile, strength or absorbent properties due to the limits of known methods of making, particularly as compared to woven or knitted materials. Importantly, laminates of non-woven webs and other materials for use in disposable consumer products have heretofore been limited due to processing limitations, including incompatible materials (e.g., thermally dissimilar materials), cost considerations (e.g., adhesive lamination costs) or tactile properties (e.g., softness and visual aesthetics).
Also known in the art is a laminate of at least three layers with the outermost layers bonded to each other through apertures formed in the center or inner layer(s) during the bonding process. Such laminates have a variety of possible properties depending upon the choice of materials for the outer and inner layers. It is possible to achieve a soft, cloth-like hand feel through the use of non-woven outer layers, and to add absorbency by using a cellulosic center layer similar to a BOUNTY® paper towel. The continuity of the inner layer is disrupted however, because the layer is apertured at the bond sites between the outer layers.
Accordingly, it would be desirable to have laminate articles with webs of dissimilar material properties, which are not dependent upon thermal compatibility of each constituent layer for structural integrity.
Additionally, it would desirable to have a laminate article comprising both non-woven webs and cellulosic webs.
Additionally, it would be desirable to have a laminate web formed by joining the constituent layers without adhesive.
Further, it would be desirable to have a multi-layer web combining the softness and durability of a non-woven layer with the absorbency of a continuous cellulosic layer.
The present invention provides a multi-layer article comprising a first layer and a second layer bonded to each other. The first layer comprises a first ply and a second ply joined to the first ply in face-to-face relationship at a plurality of discrete bond sites. The first and second plies form an interior region therebetween. A third material is disposed between the first and second plies. The third material is differentiated from the first or second ply by at least one material property selected from the group consisting of thermal properties, elongation properties, elastic properties, conductive properties, and combinations thereof. The third material substantially fills the interior region. Additionally, the third material is apertured in regions coincident with the bond sites such that the first and second plies are joined through the apertures.
The present invention also provides for a multi-layer article comprising a first layer and a second layer bonded to each other. The first layer comprises a laminate web having a plurality of apertures. The laminate web comprises first and second extensible webs being joined at a plurality of discrete bond sites. A third material is disposed between the first and second extensible webs. The first and second extensible webs are in fluid communication via the apertures and have distinct regions being differentiated by at least one property selected from the group consisting of basis weight, fiber orientation, thickness, and density.
As used herein, the term “absorbent article” refers to devices that absorb and contain body exudates, and, more specifically, refers to devices that are placed against or in proximity to the body of the wearer to absorb and contain the various exudates discharged from the body. The term “disposable” is used herein to describe absorbent articles not intended to be laundered, or otherwise restored or reused (i.e., they are intended to be discarded after a single use and, preferably, to be recycled, composted or otherwise disposed of in an environmentally compatible manner). A “unitary” absorbent article refers to absorbent articles that are formed of separate parts united together to form a coordinated entity so that they do not require separate manipulative parts like a separate holder and liner.
As used herein, the term “non-woven web” is used in its plain meaning as understood in the art and refers to a web that has a structure of individual fibers or threads which are interlaid, but not in any regular, repeating manner. Non-woven webs have been, in the past, formed by a variety of processes, such as, for example, melt-blowing processes, spin-bonding processes, and bonded carded web processes.
As used herein, “laminate” and “composite” when used to describe webs of the present invention, are synonymous. Both refer to a web structure comprising at least two webs joined in a face-to-face relationship to form a multiple-layer unitary web.
As used herein, the term “extensible” refers to any material that, upon application of a biasing force, is elongatable, at least about 25 percent without experiencing catastrophic failure. Catastrophic failure includes substantial tearing, fracturing, rupturing, or other failure in tension such that, if tested in a standard tensile tester, the failure would result in a sudden significant reduction in tensile force. As used herein, the term “highly extensible” refers to any material that, upon application of a biasing force, is elongatable, at least about 100 percent without experiencing catastrophic failure.
A multi-layer article of the present invention comprises at least a first layer and a second layer. The layers are bonded at one, or a plurality of, bond sites to each other in a face-to-face relationship. The bond site(s) comprises a macroscopic pattern on the face of the article. The pattern may include bonding along the edge of the article as well as disposed across the interior face of the article. The edge of the article is considered to be the area of the article from the perimeter of the article, extending inward about one inch (25 mm). The remainder of the area of the article is considered to be the interior face of the article. The bonding along the edge prevents delamination of the article at the edge. Delamination, or the separation of the layers of the article, reduces the unitary feel of the article and is therefore undesirable.
The layers may be continuously bonded to each other. An example of continuous bonding is an article with bonding at the edge that extends uninterrupted along the entire perimeter of the article.
The layers may also be bonded with a pattern comprised of a plurality of discrete bonding sites. The shape of the bond sites is not critical to the invention. Square, oval, circular, triangular, line segments, and arc segments have all been found acceptable. The bond sites of the article must be larger in area than the bond sites of the first layer. It is believed that article bond sites that are smaller than the bond sites of the first layer and are coincident with bond sites of the first layer will produce an aperture through the first layer. In this instance, no bonding between the first and second layers occurs.
The bonding area of the article, as used herein, is defined as the sum of the areas of all the bond sites between the first and second layers, divided by the overall area of the article. Bonding area is expressed as a percentage. For example, an article with an area of 10 square inches, where the sum of the areas of all the bonding sites between the layers is one square inch has a bonding area of 10%. The bond sites between the first and second plies of the first layer are not included in this calculation.
Higher bonding areas result in a more unitary article. Higher bonding areas also reduce the overall absorbent capacity of the article by reducing the caliper of a greater portion of the article. Higher bonding areas can also result in a stiffer article and in a reduction in the softness of the article. This is because there is a reduction or alteration in the surface properties of the first and second layers of the article in the regions of the bond sites. The melting of the fibers of the first layer reduces the softness of the article and the reduction in the caliper of the second layer reduces the absorbent capacity of the article.
An article bonded only at the edge may have a bonding area as low as 2%. Articles with bonding throughout the interior face as well as the edge may have bonding areas as high as about 60%. One embodiment of the article having a soft, absorbent, cloth-like feel, has a bonding area of between 3% and 10%. The actual bonding area in such an embodiment depends upon the size and number of bonds along the edge.
The bond sites disposed throughout the interior of the article provide structural unity for the article. These sites provide the article with a greater unitary hand feel that is more like a woven textile or cloth-like. The pattern of the interior bond sites is not critical to the invention and any pattern of sites producing the desired level of unitary feel without compromising the absorbent capacity, or softness of the article, may be used. Geometrically regular patterns or irregular patterns may be used. Patterns in any shape comprised of a series of discrete bond sites, also of any shape, may be used.
The continuity of the layers is maintained with both continuous and discrete bonding. Although the caliper of the second layer is reduced in the bond sites the absorbent capabilities of the layer are not eliminated. The layers are not pierced and maintain their continuity. For the cellulosic second layer, this continuity allows absorbed fluids to easily migrate throughout the sheet. This ease of fluid migration is important to maintaining the rate of absorption of the cellulosic web and the article.
The First Layer
In the non-limiting embodiment shown in
In addition to thermoplastic non-woven materials, the outer plies of the first layer 10 can comprise a polymeric film, for example a polyolefinic (e.g., PP or PE) film. If the entire outer plies are not uniformly thermoplastic, at least sufficient amounts to effect melt bonding should be thermoplastic. Conjugate fibers, such as bi-component fibers can be used in the outer layers to facilitate thermal bonding of the outer layers. The outer plies of the first layer can comprise a formed film, such as a three-dimensional formed film having micro-apertures as described in commonly assigned U.S. Pat. Nos. 4,629,643 and 4,609,518.
Any non-woven outer plies used in accordance with the present invention may be extensible, highly extensible, elastic, highly elastic and/or non-elastic. The non-woven plies may be any melt-fusible web, including a spun-bonded ply, a melt-blown ply, or a bonded carded ply. If the non-woven ply is a web of melt-blown fibers, it may include melt-blown microfibers. The non-woven ply may be made of fiber forming polymers such as, for example, polyolefins. Exemplary polyolefins include one or more of polypropylene, polyethylene, ethylene copolymers, propylene copolymers, and butene copolymers. The non-woven plies may also comprise synthetic cellulose fibers, or extruded starch fibers. The non-woven plies can have a basis weight between about 10 to about 90 grams per square meter (gsm), or in another embodiment about 15 to about 30 gsm.
Further, any non-woven outer plies used in accordance with the present invention may themselves be a multi-layer material having, for example, at least one layer of a spun-bonded web joined to at least one layer of a melt-blown web, a bonded carded web, or other suitable material. For example, the non-woven ply may be a multi-layer web having a first layer of spun-bonded polypropylene having a basis weight from about 0.2 to about 8 ounces per square yard, a ply of melt-blown polypropylene having a basis weight from about 0.2 to about 4 ounces per square yard, and a second ply of spun-bonded polypropylene having a basis weight from about 0.2 to about 8 ounces per square yard. Alternatively, the non-woven plies may be a single layer of material, such as, for example, a spun-bonded ply having a basis weight from about 0.2 to about 10 ounces per square yard or a melt-blown ply having a basis weight from about 0.2 to about 8 ounces per square yard.
Such non-woven outer plies may also be a composite comprising a mixture of two or more different fibers or a mixture of fibers and particles. Such mixtures may be formed by adding fibers and/or particulates to the gas stream in which melt-blown fibers or spunbond fibers are carried so that an intimate entangled co-mingling of fibers and other materials, (e.g., wood pulp, staple fibers, synthetic cellulose, starch fibers and particles) occurs prior to collection of the fibers. Prior to processing, the non-woven web outer ply of fibers can be joined by bonding to form a coherent web structure. Suitable bonding techniques include, but are not limited to, chemical bonding, thermobonding, such as point calendering, hydro-entangling, and needling.
At least one third central ply 30 is disposed between the two outer plies. The first layer 10 is processed by joining means, such as by ultrasonic welding, or thermal calendaring to provide a plurality of melt bond sites 50 that serve to couple the outer plies 20 and 40, thereby forming the constituent plies into a unitary layer. When joined together, the two outer plies form an interior region therebetween. The interior region is the space between the outer plies surrounding the bond sites 50. In one embodiment, central ply 30 substantially fills the interior region, central ply 30 being apertured coincident the bond sites 50.
While the first layer 10 is disclosed primarily in the context of non-woven plies and composites, in principle the first layer 10 can be made out of any materials that meet the requirements, (e.g., melt properties, extensibility) as disclosed herein. For example, the outer plies 20 and 40 can be thermoplastic films, micro-porous films, apertured films, and the like. Central ply 30 can be paper, including tissue paper, metal, including metal foil; other non-thermoplastic web material, woven fabric, and the like. In general, it is required that outer ply materials be flexible enough to be processed as described herein.
One benefit of the laminate of the present invention is the ability to provide a first layer 10 as a structure of dissimilar materials without the use of adhesive for joining. Because the central ply 30 of the first layer 10 can be formed by the penetration of the protuberances of the calendaring roll at melt bond sites, first layer 10 can comprise non-thermally-bondable materials. The plurality of melt bond sites 50 are sufficient to keep the component webs together in the laminate web, so that the laminate web behaves as a unitary web for processing integrity and use, without unwanted delamination. However, in some embodiments, and for certain materials, it may be beneficial to apply adhesive between at least two of the constituent layers.
The first layer 10 of the present invention, being bonded by a plurality of relatively closely spaced thermal bond sites (without the use of thermoplastic adhesives) can be beneficially used for durable multi-layer articles. For example, a multi-layer article of the present invention comprising non-woven web outer layers and having a cloth-like feel and appearance can be used in durable garments. Certain embodiments of the multi-layer article of the present invention can survive repeated washing and drying in household washing and drying equipment, depending on the component webs of the laminate, and the level of thermal bonding. Due to the knit-like or fabric-like look and feel of certain embodiments of the present invention, such durability can result in durable garment components such as inter-liners and the like.
Non-Apertured Embodiment
In one embodiment, as shown in cross-section in
The first layer 10 is further characterized in that the joining of the three plies into a unitary web can be achieved in the absence of adhesive. That is, in certain preferred embodiments no adhesive is required to bond the plies together; joining is achieved by the input of energy into the constituent layers, such as by thermal melt bonding of the two outer layers together at the melt bond sites 50. In other embodiments, the energy input can be via ultrasonic bonding. Accordingly, a significant benefit of the present invention is the provision of a laminate web, that is a unitary web, formed without the use of adhesives. Not only does this simplify processing and lower the cost of the laminate web, when certain materials such as non-woven webs are used, it results in a more flexible, softer web.
As shown in
An advantage of such a laminated web is that, in some embodiments, e.g., for solid core central ply 30 materials (i.e., a continuous sheet, that is, not having substantial apertures, gaps, or other voids), it results in a unitary web having an apertured central ply 30 in full, intimate contact with the outer plies 20, and 40. By “full” and “intimate” is meant that central ply 30 fills all the unbonded regions between outer plies 20 and 40 such that outer plies 20 and 40 do not contact except at the bond sites 50. Of course, it is recognized that many materials of interest have significant air content, and filling “all” the unbonded region between outer plies 20 and 40 is not meant to imply that all air content is removed.
Central ply 30 can be involved, or participate, in the bonding between outer plies 20 and 40. By “involved” is meant that the central ply can, to some extent, be in intimate contact with, and possibly partially merged with, one or both immediate outer plies. The involvement may be due to actual melt bonding about the perimeter of bond site 50 (e.g., for thermoplastic central plies 30), or it may be due to mechanical interaction, such as by entanglement (e.g., for cellulosic fibrous central ply 30 between fibrous non-woven plies), also about the perimeter of bond site 50.
Such separation of central ply 30 can occur by shearing, cutting, or otherwise fracturing the central ply 30, and displacing the material of the central ply 30 sufficiently to permit thermal bonding of the two outer plies 20 and 40. Thus, central ply 30 must be chosen to have properties that permit such displacement. Therefore, central ply 30 should have one or more of the properties of relatively low extensibility, relatively high frangibility, or relatively high deformability, such that the material of central ply 30 can be “squeezed” or otherwise displaced out of the region of thermal bond sites 50. Importantly, it is not required that the central ply 30 be melted out of the region of the thermal bond sites. Thus, central ply can be elastic, highly elastic, extensible, or highly extensible, depending on the desired end results and purposes of the resulting unitary web.
Without being bound by theory, it is believed that to accomplish the displacement of central ply 30 to form apertures therein and to bond the outer plies, the thermal point calendaring described below should form thermal bond sites having a narrow width W dimension and a high aspect ratio. For example,
It is believed that the aspect ratio of melt bond site 50 can be as low as about 3 (i.e., ratio of L/W equals 3/1). It can also be between about 4 and 20. In one preferred embodiment, the aspect ratio was about 10. It is believed that the aspect ratio of the melt bond sites 50 is limited only by the corresponding aspect ratio of the point bonding protuberances of the calendaring roller(s), as detailed below.
In one embodiment, the longitudinal axis of each bond site, 1, which corresponds directionally to the length dimension of bond site 50, is disposed in a regular, repeating pattern oriented generally parallel to the machine direction, MD as shown in
When non-woven webs are used as constituent plies of first layer 10, an important distinction should be drawn between bond sites 50 which bond together outer plies 20 and 40, and thermal bond sites that may be present in the constituent plies themselves. For example, non-woven webs are typically consolidated by thermal bonding in a regular pattern of discrete spaced apart fused bonding areas, such as the pattern disclosed in U.S. Pat. No. 3,855,046, and the patterns shown generally in
The bond sites of the base non-woven do not typically have an aspect ratio greater than about 1, so that these bonds do not typically form apertures in the constituent ply during the stretching step disclosed below. Also, the spacing of such bond sites is typically a repeating pattern of bonded and unbonded area that may or may not provide for machine direction (MD) columns of bonded area next to columns of unbonded area. After forming bond sites 50, however, there is not likely to be any significant MD columns of unbonded areas; the overall bond pattern of any constituent non-woven fabric is a combination of existing bonded areas and bond sites 50. Together the two sets of bond sites result in a complex pattern of bond sites that may or may not be described as columnar, regular, or uniform.
The resulting web of the first layer 10, as shown in cross-section in
The central ply 30 need not be thermally compatible with the outer plies. The central ply 30 need not even be melt processible. It can be, for example, a cellulosic material, such as paper; a metallic material, such as a metal foil; a woven or knit material, such as cotton or rayon blends; or a thermoset material, such as a polyester or aromatic polyamide film, or a web comprised of starch fibers. The central ply 30 can be another non-woven having suitable properties for processing into an apertured ply. If central ply 30 has a melting point, it is preferably at least about 10° C. higher, more preferably about 20° C. higher than the outer plies. However, central ply 30 need not have a melting point, and may simply experience softening at the calendaring temperatures required to bond the laminate structure.
Central ply 30 can be any of a great number of dissimilar materials. For example, if outer plies 20 and 40 are non-woven webs having a relatively high elongation to break, central ply 30 can be paper, tissue paper, thermoplastic film, metal foil, closed or open cell foam, or any other material that has a relatively low elongation to break compared to the two outer layers. The outer layer materials may themselves be dissimilar, with the only constraint being that the central layer be relatively less extensible in the direction of extension to form apertures.
Additionally, more than one central ply 30 can be used with beneficial results. For example, a structure comprising a cellulosic tissue central web and a polymeric film central web between two non-woven webs can produce an absorptive wiping article with one side being relatively more absorptive than the other. If the film layer is a three-dimensional formed film, the film side can provide added texture to the laminate that is beneficial in many wiping applications. Macroscopically-expanded, three-dimensional formed films suitable for use in the present invention include those described in U.S. Pat. Nos. 3,929,135 and 4,342,314.
Central ply 30 can be elastomeric, an elastomeric macroscopically-expanded, vacuum-formed, three-dimensional formed film, a three-dimensional formed film having micro-apertures, a web material having a strainable network, absorbent gelling materials, and the like.
Apertured Embodiments
A further benefit is obtained when the non-apertured thermally bonded laminate first layer 10 described supra, is stretched or extended in a direction generally orthogonal to the longitudinal axis 1 of melt bond sites 50. The melt bonding at the melt bond sites 50 tends to make localized weakened portions of the layer at the bond sites. Thus, as portions of the first layer 10 are extended in a direction generally orthogonal to the longitudinal axis 1 of bond sites 50, the material at the bond site fails in tension and an aperture is formed. The relatively high aspect ratio of melt bond sites 50, permits a relatively large aperture to be formed upon sufficient extension. When the first layer 10 is uniformly tensioned, the result is a regular pattern of a plurality of apertures 45 corresponding to the pattern of melt bond sites 50.
When apertures 45 are formed, the thermally bonded portions of outer plies 20 and 40 remain primarily on the portions of the aperture perimeters corresponding to the length dimension of bond sites 50. Therefore, each aperture 45 does not have a perimeter of thermally bonded material, but only portions remain bonded, represented as 62 in
To the extent that central ply 30 is involved, or participates, in any bonding between outer plies 20 and 40, it also participates in the remnant of bonded portions 62, as shown in
The first layer 10 may also be extended as described with reference to
One example of a first layer 10 having a structure similar to that shown in
One surprising beneficial characteristic of the laminate web structure of the present invention is the presence of distinct regions in the non-apertured portion of the web being differentiated by at least one property selected from the group consisting of basis weight, thickness, or density. In a preferred embodiment, the regions are visually distinct, giving the laminate an aesthetically pleasing look and feel. The regions may also give the laminate a garment-like or knit-like texture.
In general, for a first layer 10 having generally parallel rows of melt bond sites 50 extending in the machine direction MD, which correspondingly form generally parallel rows of apertures when extended, and having a central layer with a lower elongation to break than the outer layers, the resulting extended, apertured layer 10 is characterized by generally low basis weight, low density regions between the apertures in the machine direction, MD. Likewise, such a first layer 10 is characterized by relatively high basis weight, high density regions between adjacent rows of apertures in the cross-machine direction, CD. By choice of central ply 30 material and possibly post laminating operations, e.g., an embossing process, the thickness of the laminate web can likewise be varied, the thicker regions generally corresponding to the higher density regions.
The Second Layer
Referring to
Two-dimensional cellulosic webs suitable for use as the second layer 60 are preferably composed of fibers, which are approximated by linear elements. The fibers are components of the two-dimensional fibrous web, which components have one very large dimension (along the longitudinal axis of the fiber) compared to the other two relatively very small dimensions (mutually perpendicular, and both radial and perpendicular to the longitudinal axis of the fiber), so that linearity is approximated. While, microscopic examination of the fibers may reveal two other dimensions, which are small, compared to the principal dimension of the fibers, such other two small dimensions need not be substantially equivalent or constant throughout the axial length of the fiber. It is only important that the fiber be able to bend about its axis and be able to bond to other fibers.
The fibers may be synthetic, such as polyolefin or polyester; may be cellulosic, such as cotton linters, rayon or bagasse; or may be wood pulp, such as softwoods (gymnosperms or coniferous) or hardwoods (angiosperms or deciduous) or layers of the foregoing. As used herein, a fibrous web is considered “cellulosic” if the fibrous web comprises at least about 50 weight percent or at least about 50 volume percent cellulosic fibers, including but not limited to those fibers listed above. A cellulosic mixture of wood pulp fibers comprising softwood fibers having a length of about 2.0 to about 4.5 millimeters and a diameter of about 25 to about 50 micrometers, and hardwood fibers having a length of less than about 1 millimeter and a diameter of about 12 to about 25 micrometers has been found to work well for the fibrous webs described herein.
Such a fibrous web suitable for use as second layer 60 may be comprised of a single ply or of multiple plies. Each of the plies comprising the fibrous web may be embossed or nonembossed. An exemplary ply can comprise a tissue paper such as a BOUNTY® paper towel, available from The Procter & Gamble Co., Cincinnati Ohio, USA. One of the beneficial characteristics in such an embodiment is that the BOUNTY® sheet retains much of its absorbency. The continuous web of the BOUNTY® is not disrupted by the discontinuous bonding pattern. Therefore the BOUNTY® sheet retains much of its absorbent capacity.
In one embodiment of the present invention, the center ply 30 disposed between the first and second plies 20,40 of the first layer 10 is also a cellulosic web. Preferably, the cellulosic web of the center ply 30 has a basis weight ranging from about 20 gsm to about 50 gsm, and comprises a mixture of softwood pulp fiber and hardwood pulp fiber, preferably with the softwood comprising from about 50 to about 90 per cent of the web, and the hardwood comprises from about 10 to 50 percent of the web.
The cellulosic webs of the present invention could be produced by a through air drying process, by a conductive Yankee drying process, or any other paper manufacturing process known in the art. In one embodiment, a single ply of cellulosic web used as the third material of the first layer, and bonded to a sheet of BOUNTY® paper towel as the second layer. A representative BOUNTY® paper towel is made by a through air dried process and has a basis weight of 42 gsm and comprises 70% softwood and 30% hardwood fibers. The absorbent rate of such an embodiment is equivalent to the absorbent rate of two sheets of BOUNTY®. The absorbent capacity of this embodiment exceeds that of an equivalent amount of cellulosic material alone. This is surprising because the embodiment contains less absorbent cellulosic structure than two sheets of BOUNTY® and the non-woven plies of the first layer 10 do no add absorbent capacity.
The first layer 10 can also be more durable than the second layer 60 and therefore can function as a cleaning surface to enable more mechanically intensive cleaning with the article than is possible with a cellulosic wipe such as a paper towel. The use of non-woven outer plies in the first layer 10 results in a soft outer surface in the present invention.
In one embodiment, the cellulosic second layer also comprises an outer layer of the invention. Such an embodiment demonstrates a high rate of absorption due to the direct exposure of the absorbent cellulosic web to fluids.
Three Layer Embodiment
A third layer, substantially similar, or identical, to the first layer may also be added as an outer layer. In such an embodiment, the second layer is disposed between the first and third layers. In such an embodiment, the second layer is bonded to each of the first and third layers without aperturing the second layer.
Such an embodiment has the advantage of a soft clothlike feel on both sides of the article. Additionally, when the third material of the third layer is a cellulosic web the article gains additional absorbent capacity.
Method of Making
The laminate article is further characterized in that the joining of the two layers into a unitary web can be achieved in the absence of adhesive. That is, in certain embodiments no adhesive is required to bond the layers together; joining is achieved by the input of energy into the constituent layers, such as by thermal melt bonding of the two layers together at the melt bond sites. In other embodiments, the energy input can be via ultrasonic bonding, by infrared bonding, or by pressure bonding. Accordingly, a significant benefit of the present invention is the provision of a laminate article, that is a unitary article, formed without the use of adhesives. Not only does this simplify processing and lower the cost of the laminate article, it results in a more flexible, softer article.
Referring to
The patterned calendar roller 110 is configured to have a circular cylindrical surface 114, and a plurality of protuberances or pattern elements 116 which extend outwardly from surface 114. The protuberances 116 are disposed in a predetermined pattern with each protuberance 116 being configured and disposed melt bond the two outer layers together at a plurality of locations. One pattern of protuberances is shown schematically in
As shown in
The height of the protuberances should be selected according to the thickness of the laminate being bonded. In general, the height dimension should be greater than the maximum thickness of the laminate web during the calendaring process, so that adequate bonding occurs at the bond sites, and only at the bond sites.
After passing through nip 106, the two (or more) component webs 120, and 140 have been formed into unitary first layer 10. At this point in the process the outer layers are thermally bonded to each other and unapertured, as shown in
A preferred diaper configuration for a diaper comprising laminates of the present invention is described generally in U.S. Pat. No. 3,860,003. Alternatively, preferred configurations for disposable diapers are also disclosed in U.S. Pat. Nos. 4,808,178, 4,695,278, 4,816,025, and 5,151,092.
In addition to disposable diapers, various embodiments of laminates of the present invention are useful for topsheets, backsheets, and cores in other disposable absorbent articles, such as catamenials, panty liners, pull-up diapers, adult incontinence products, and the like.
Laminates of the present invention can also be useful as wipes, including wet wipes, shop wipes, facial wipes, and the like. For example, an absorbent cellulosic layer as central ply 30 would be an excellent wipe for picking up spills and particulate matter that can be captured in the apertures. Likewise, a polyethylene film would be an excellent wipe for harsh jobs requiring a more durable wipe having extra scrubbing capability. A laminate of the present invention can be considered a durable or semi-durable rag or sponge for most purposes.
Because of the virtually infinite variety of patterns achievable by the method of the present invention, laminates of the present invention can find use as components in home furnishings, including drapes and upholstery. For example, very lacy, sheer patterns can be made that are attractive as window coverings. The colors can be varied easily by varying the component materials, including central ply 30. Higher basis weight materials can be made durable for seat coverings, particularly disposable seat coverings useful in airplanes, buses, and the like.
Laminates of the present invention can be useful as disposable bibs. For example, a polyethylene layer would serve as an effective bib. Even apertured versions, depending on the size of the apertures can be useful as bibs, as the apertures tend to capture food particles better. After use as a bib the bib can be used as a wipe to clean up the baby's surroundings after eating.
A laminate web of the present invention can find use as a filter for filtering fluids. Air, for example, can be filtered in passing air through a suitably designed laminate web of the present invention. For example, electrostatic air filters can be made by laminating appropriate dissimilar polymeric non-woven materials. In one embodiment the filter would comprise non-woven materials of suitable material and pore size, and would be provided in an unstretched condition, that is, in a laminate such as that shown with respect to
Other uses for laminates of the present invention include medical dressings, textured wall coverings, mats and throws, mop heads for dry or wet mops, and geo-textiles.
All documents cited in the Detailed Description of the Invention are, in relevant part, incorporated herein by reference; the citation of any document is not to be construed as an admission that it is prior art with respect to the present invention. To the extent that any meaning or definition of a term in this written document conflicts with any meaning or definition of the term in a document incorporated by reference, the meaning or definition assigned to the term in this written document shall govern.
While particular embodiments of the present invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the invention. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of this invention.
This application is a continuation of U.S. application Ser. No. 10/192,372, filed on Jul. 10, 2002 which claims the benefit of U.S. Provisional Application Ser. No. 60/308,749, filed Jul. 30, 2001; and this application is also a continuation of US Application No. PCT/US00/34746, filed on Dec. 20, 2000 which claims priority to U.S. application Ser. No. 10/149,878, filed Dec. 20, 2000 which is a continuation-in-part of U.S. application Ser. No. 09/584,676, filed on May 31, 2000 which is a continuation-in-part of U.S. application Ser. No. 09/467,938, filed on Dec. 21, 1999, now issued as U.S. Pat. No. 6,884,494 on Apr. 26, 2005.
| Number | Date | Country | |
|---|---|---|---|
| 60308749 | Jul 2001 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10192372 | Jul 2002 | US |
| Child | 11205831 | Aug 2005 | US |
| Parent | PCT/US00/34746 | Dec 2000 | US |
| Child | 11205831 | Aug 2005 | US |