Patent Application
20130186469
The present invention relates to polymeric tubing typically formed by a co-extrusion process, the tubing having multiple layers of different polymeric materials.
Tubing comprised of polymeric material is used in many industrial and commercial applications, including in the medical field. Various FDA compliant plastics are used, depending upon properties desired and the intended applications. Where the tubing is used to transport fluids for in vivo treatment of human patients or for delivery of any fluid where the fluid itself or a component contained in the fluid needs to be isolated and contained within and not leach through the walls of the tube, selection of a polymeric material having a selective property can be a factor.
Polyvinyl chloride (PVC) is one of the most widely used plastics. While structurally stable and easily formable into desired shapes, PVC is typically manufactured using plasticizers which can migrate out of the PVC matrix into bodily fluids and has other properties not ideally suited for medical treatment applications. Likewise, due to the inherent nature of plasticized PVC tubing, there arises the potential absorption of medicines and other components of aqueous fluids used in medical treatments into the sidewall of the PVC tube. U.S. Pat. No. 4,627,844 to Schmitt (“Schmitt”), the disclosure of which is incorporated herein by reference as if fully set forth, discloses a tri-layer tube which is embodied in a commercial product sold under the trademark “SUREPATH 151” by the Natvar Division of Tekni-Plex, Inc. As disclosed in Schmitt, an outer layer of PVC and an inner fluid-contact layer of low density polyethylene (LDPE) are co-extruded with an intermediate tie layer of ethylene vinyl acetate copolymer (EVA). Polyurethane is potentially a substitute for PVC as disclosed in commonly owned and co-pending U.S. Ser. Nos. 13/354,029 and 13/586,288. Other tubing configurations are disclosed in U.S. Pat. No. 7,647,949, U.S. Pat. No. 4,211,741 and U.S. Patent Publication No. 2007/0119511, the disclosures of which are incorporated by reference as if fully set forth herein.
In accordance with the invention there is provided a tubing, tube or tubular device that comprises at least three concentric layers of polymeric materials comprising inner and outer layers of a polymeric material comprised of thermoplastic polyurethane and a middle layer comprised of a polymeric material comprised of an acrylate containing polymer that is disposed between and binds the inner and outer layers together by adhesion mechanisms, such as chemical adhesion, without the need for additional binders or adhesive layers. The polyurethane of which each of the inner and outer layers are comprised can be the same or different in structure, molecular weight, crystallinity, purity, monomeric unit content, branching, chain length, additive content, inorganic content and physical properties such as elongation, melting point, resistance to creep, and hardness.
The layers of polymeric materials are co-extruded together to form the tubing such that the outer and inner layers are adhered to the middle layer and thus all three layers adhered to each other. The tubing is formed with a central hollow channel, bore or passage that is radially surrounded and defined by the polymeric layers that act as the wall or walls of the tubing.
The tube or tubing is particularly suitable for transport of aqueous fluids such as fluids used in medical treatments and applications. Alternatively the tube or tubing can be used for routing, delivery and transport of liquid and gaseous non-aqueous and aqueous fluids including organic materials such as ethers, alcohols, hydrocarbons, amines, aldehydes, ketones, amides, carboxylic acids and esters and non-aqueous fluids such as oxygen, carbon dioxide, carbon monoxide, helium, neon, argon, krypton, xenon, radon, hydrogen, nitrogen and the like and mixtures of two or more of any of the foregoing with each other or one or more of the foregoing together with an aqueous fluid.
Preferably the polymeric material of the inner and outer layer is comprised of a polyurethane thermoplastic elastomeric material (“TPU”) and the middle layer is comprised of an ethylene ethyl acrylate copolymer (EEA), ethylene methyl acrylate copolymer (EMA), an anhydride grafted ethylene methyl acrylate copolymer (AEMA), a copolymer of two or more of said acrylates or a mixture of two or more of the foregoing.
In one embodiment, the middle layer preferably has a thickness substantially greater than the combined thicknesses of the inner and outer layers. The cross-sectional thickness T2 of the middle layer,
Thus, it is envisioned that in one embodiment the majority of the volume of the sidewall of a tube will be made from EEA or EMA material and the TPU inner layer and outer layer will be as thin as possible so as to still function as both the fluid contact layer (inner layer) and as the outer layer to which various fitments may be bonded (luers, etc.).
With reference to
Ethylene ethyl acrylate (EEA) copolymers, ethylene methyl acrylate (EMA) copolymers and anhydride grafted ethylene methyl acrylate (AEMA) copolymers are elastomeric in nature and have excellent visual clarity. In a typical co-extrusion process, TPU and EEA or EMA or AEMA are melt extruded through a die head to form a tubular shaped extrudate that is then cooled through conventional water baths or water vacuum tanks and which are either subsequently wound or cut into a particular length for use. The level of elasticity and softness of the EEA, EMA AEMA or copolymer thereof is controlled through the amount of ethyl acrylate or methyl acrylate comonomer utilized with ethylene in the copolymerization process. The resulting three layer tubes manufactured by such a co-extrusion process act in a monolithic manner in that they return to close to their original shape and dimensions after being strained or stretched in a tensile manner along the longitudinal axis A of the tube at a stress of up to about 55 MPa and a strain of up to about 900-950% and without any visual delaminaton between any of the layers after being submersed in water at about 60° C. for about 36 hours.
The polymeric materials are preferably “contaminant free” meaning that they do not contain more than insignificant amounts of potentially unwanted materials (typically less than about out 0.5% and preferably less than about 0.2%, by weight) and/or prevent leaching or leaking of unwanted materials such as plasticizers, catalysts, monomers, metals, salts, ions or other substances that are potentially unwanted to a human being into an aqueous solution or other fluid medium with which one or the other of the three layers may come into contact during the normal course of use of the tubing in delivering aqueous (or non-aqueous) fluid, such as insulin, chemotherapy drugs and other potentially unstable aqueous drug suspensions, to or from a human subject. The middle layer prevents delamination of the outer and inner layers from the middle layer under conditions of relatively low to moderate stress or strain. In addition, the middle layer acts as a barrier to leaching or leaking of contaminants from the outer layer to or through the inner layer into the hollow central bore or passage of the tube.
In accordance with one aspect of the invention there is provided a tube comprising an inner layer, an outer layer and a middle layer, wherein the inner layer comprises a thermoplastic polyurethane, the outer layer comprises a thermoplastic polyurethane and the middle layer comprises an ethylene ethyl acrylate copolymer or an ethylene methyl acrylate copolymer or an anhydride grafted ethylene methyl acrylate copolymer, a copolymer of two or more of said acrylates or a mixture of two or more of the foregoing.
The inner and outer layers preferably each comprise more than about 90% by weight of an aromatic or aliphatic polyether based polyurethane. The middle layer can comprise more than about 90% by weight of an ethylene ethyl acrylate copolymer, an ethylene methyl acrlylate copolymer, an anhydride grafted ethylene methyl acrylate copolymer, or more than about 90% by weight of a mixture or copolymer of two or more of the foregoing.
One or both of the inner and outer layers can comprise a polytetramethyleneglycol-based polyurethane.
The ethylene methyl acrylate copolymer typically comprises at least about 19.5 percent methyl acrylate content by weight.
The ethylene ethyl acrylate copolymer typically comprises at least about 19.5 percent ethyl acrylate content by weight.
In another aspect of the invention there is provided a medical tube for transport of aqueous fluid comprising: an inner layer comprising more than about 90% by weight of a thermoplastic polyurethane, an outer layer comprising more than about 90% by weight of a thermoplastic polyurethane and, a middle layer disposed between the outer and inner layers comprising more than about 90% by weight of an ethylene ethyl acrylate copolymer or an ethylene methyl acrylate copolymer or an anhydride grafted ethylene methyl acrylate copolymer, a copolymer of two or more of said acrylates or a mixture of two or more of the foregoing.
In another aspect of the invention there is provided a tube for transport of a non-aqueous fluid comprising: an inner layer comprising more than about 90% by weight of a thermoplastic polyurethane, an outer layer comprising more than about 90% by weight of a thermoplastic polyurethane and, a middle layer disposed between the outer and inner layers comprising more than about 90% by weight of an ethylene ethyl acrylate copolymer or an ethylene methyl acrylate copolymer or an anhydride grafted ethylene methyl acrylate copolymer, a copolymer of two or more of said acrylates or a mixture of two or more of the foregoing. In such an embodiment the non-aqueous fluid can comprise a liquid or gaseous fluid including organic materials such as ethers, alcohols, hydrocarbons, amines, aldehydes, ketones, amides, carboxylic acids and esters and non-aqueous fluids such as oxygen, carbon dioxide, carbon monoxide, helium, neon, argon, krypton, xenon, radon, hydrogen, nitrogen and the like and mixtures of two or more of any of the foregoing with each other or one or more of the foregoing together with an aqueous fluid.
In another aspect of the invention there is provided a medical tube for transport of an aqueous fluid comprising:an inner layer comprising more than about 90% by weight of a thermoplastic polyurethane, an outer layer comprising more than about 90% by weight of a thermoplastic polyurethane and, a middle layer disposed between the inner and outer layers comprised of at least about 90% by weight of an ethylene ethyl acrylate copolymer, an ethylene methyl acrylate copolymer, an anhydride grafted ethylene methyl acrylate copolymer, a copolymer of two or more of said acrylates or a mixture of two or more of the foregoing, wherein the tube does not visually delaminate after being submersed in water at 60° C. for 36 hours.
In another aspect of the invention there is provided a medical tube for transport of an aqueous fluid comprising: an inner layer comprising more than about 90% by weight of a thermoplastic polyurethane, an outer layer comprising more than about 90% by weight of a thermoplastic polyurethane and, a middle layer comprised of at least about 90% by weight of an ethylene ethyl acrylate copolymer, an ethylene methyl acrylate copolymer, an anhydride grafted ethylene methyl acrylate copolymer, a copolymer of said acrylates or a mixture of two or more of the foregoing, wherein the tube does not visually delaminate at a stress of up to about 55 MPa and a strain of up to about 900-950%, and, wherein the tube does not visually delaminate after being submersed in water at 60° C. for 36 hours.
In another aspect of the invention there is provided a method of forming a medical tube comprising an outer layer, an inner layer and a middle layer disposed between the outer layer and the inner layer, the method comprising: selecting first and second polymeric materials each comprising more than about 90% by weight of a thermoplastic polyurethane; selecting a third polymeric material that readily bonds and adheres to the first and second polymeric materials on co-extrusion and cooling of the materials; co-extruding the selected first, second and third polymeric materials to form the medical tubing in a configuration such that the inner and outer layers comprise the first polymeric material and the middle layer comprises at least about 90% by weight of the second polymeric material. In such a method the first polymeric material preferably comprises more than about 90% by weight of an aromatic or aliphatic polyether based polyurethane.
Further in accordance with the invention there is provided a method of forming a fluid delivery tube comprising;
In such a method the step of forming typically comprises co-extruding the first, second and third materials simultaneously to form the inner and outer layers having a cross-sectional thickness of between about 0.00025 and about 0.025 inches and to form the middle layer having a cross-sectional thickness of between about 0.008 inches and about 0.120 inches.
The step of forming can comprise co-extruding the first, second and third materials such that the middle layer is between about 5% and about 98% of the total cross-sectional thickness of the inner, outer and middle layers combined.
The step of forming can comprise co-extruding the first, second and third materials such that the middle layer is between about 10% and about 85% of the total cross-sectional thickness of the inner, outer and middle layers combined.
The step of forming can comprise co-extruding the first, second and third materials such that the middle layer is between about 61% and about 98% of the total cross-sectional thickness of the inner, outer and middle layers combined.
In another aspect of the invention there is provided a method of delivering an aqueous fluid to a subject comprising; selecting a tube comprising an inner layer, an outer layer and a middle layer, wherein the inner and outer layers comprise more than about 90% by weight of one or more thermoplastic polyurethanes and the middle layer comprises an ethylene ethyl acrylate copolymer or an ethylene methyl acrylate copolymer or an anhydride grafted ethylene methyl acrylate copolymer, a copolymer of two or more of said acrylates or a mixture of two or more of the foregoing; wherein the tube has a central fluid flow passage surrounded by the layers; routing an aqueous fluid through the central fluid flow passage of the tube, and, delivering the aqueous fluid routed through the central fluid flow passage into a blood vessel of the subject. In such a method the step of selecting preferably comprises co-extruding the outer, inner and middle layers to form the tube such that the intermediate layer comprises at least about 90% by weight of one or more of the acrylate copolymers.
In another embodiment of the invention, such a method enables routing and delivery of liquid and gaseous non-aqueous fluids including organic materials such as ethers, alcohols, hydrocarbons, amines, aldehydes, ketones, amides, carboxylic acids, esters and the like and fluid materials such as oxygen, carbon dioxide, carbon monoxide, helium, neon, argon, krypton, xenon, radon, hydrogen, nitrogen and the like as well as mixtures of two or more of all of the foregoing with each other or mixtures of one or more of the foregoing together with an aqueous fluid.
Most preferably, the inner, middle and outer layers of the aforementioned tubes or tubing do not visually delaminate from each other at a stress up to of about 55 MPa and a strain of up to about 900-950% when measured by pulling a length of tubing about 2 inches in axial length along its axis using a Lloyd LR5K plus mechanical tester at a pull rate of about 12 inches/minute at ambient environmental conditions of about 72 degrees F. and about 50% relative humidity, the break point of the tubing 10 being about 57-62 MPa and about 1000-1050%.
Most preferably, all of the aforementioned tubes or medical tubing do not visually delaminate after being subjected to submersion in water at 60° C. for 36 hours and subsequently mechanically flattened by manual squeezing of the tube from its normal round in cross-sectional condition to a flattened or oval shape cross-sectional shape or condition.
Preferably the aforementioned tubes or medical tubing have a central axial fluid flow passage through which aqueous fluid is routed, the inner layer having a radially inner wall surface that contacts the aqueous fluid, the outer and inner layers resisting delamination from the middle layer at a stress of up to about 55 MPa and a strain of up to about 900-950%.
Most preferably the middle layer serves as a barrier against, prevents or substantially lessens migration of mobile moieties such as monomers, short chained polymers, ions, water, small organic molecules, metals, plasticizers, catalysts and the like between the outer and inner layers or from the outer layer into the inner layer or the central flow passage or from the central flow passage or inner layer into the outer layer.
In another aspect of the invention there is provided a method of delivering a non-aqueous fluid comprising;
In such a method the fluid preferably comprises a liquid or gaseous non-aqueous fluid selected from the group of ethers, alcohols, hydrocarbons, amines, aldehydes, ketones, amides, carboxylic acids, esters, oxygen, carbon dioxide, carbon monoxide, helium, neon, argon, krypton, xenon, radon, hydrogen and nitrogen and mixtures of two or more of the foregoing with each other or one or more of the foregoing together with an aqueous fluid.
The tube preferably does not visually delaminate at a stress of up to about 55 MPa and a strain of up to about 900-950%.
In another aspect of the invention there is provided a method of delivering a selected fluid to a selected repository comprising;
In all of the embodiments and aspects of the invention described herein the polyurethane polymer or material of which the inner and outer layers are separately comprised, can be the same or can be different in structure, molecular weight, crystallinity, purity, monomeric unit content, branching, chain length, inorganic content and physical properties such as elongation, melting point, resistance to creep, and hardness.
The drawings depict one or more embodiments of the invention that are shown by way of examples of the invention wherein:
There is shown in
As shown in
As shown in
The inner layer 3 provides a radially inner fluid-contact surface S5, the thickness, of the inner layer 3 typically ranging in cross-sectional thickness T1 of between about 0.00025 inches and about 0.025 inches. The middle layer 2 has a cross-sectional thickness T2 of between about 0.008 inches and about 0.120 inches. The outer layer 1 typically ranges in cross-sectional thickness T3 of between about 0.00025 inches and about 0.025 inches.
The polyurethane elastomer (TPU) is typically the reaction product of a polyol and isocyanate and usually includes a combination of hard and soft segment domains. An aromatic polyether-based TPU or an aliphatic polyether-based TPU can be used such as a polytetramethyleneglycol-based polyurethane. Preferred, TPU's include the Pellethane 2363-80 AE series available from the Lubrizol Corporation, Wilmington, Mass. such as Lubrizol TPU Pellethane 2363-90AE.
The respective thickness of each layer of tubing 10,20 can be controlled by the extrusion tooling utilized, such as the “Tri Die” extrusion apparatus manufactured by the Genca Division of General Cable Company, Clearwater, Fla. The extrusion apparatus is selected so as to provide a uniform thickness of the layers 1, 2, 3 along the substantial entirety of the axial length L of all three layers 1, 2, 3.
The polymeric materials of which the layers 1, 2, 3 are comprised are selected so as to be visually clear or transparent and manually flexible along and around the axis A of the tubing. The polymeric materials are also selected so as to maintain the integrity of the tubing 10 (namely delamination does not occur) and its transparency or clarity after being subjected to ethylene oxide (EtO) and gamma irradiation sterilization processes.
The foregoing description is intended to illustrate and not limit the scope of the invention, those skilled in the art will realize that equivalents thereof are contemplated by the description above and that changes and modifications may be made thereto without departing from the spirit of the invention, all such equivalents, changes and modifications falling within the scope of the claims hereof.
This application is a continuation-in-part and claims the benefit of priority of U.S. patent application Ser. No. 13/354,029 filed Jan. 19, 2012 and of U.S. patent application Ser. No. 13/586,288 filed Aug. 15, 2012. The disclosures of both of the foregoing applications are incorporated by reference in their entirety as if fully set forth herein.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13586288 | Aug 2012 | US |
| Child | 13686197 | US | |
| Parent | 13354029 | Jan 2012 | US |
| Child | 13586288 | US |