Patent Application
20050202262
The invention relates to a process for producing by blow-moulding a multilayer film containing at least a polyamide layer and a polyolefin layer. Such a process is often used for producing for example agricultural film and packaging film for, for example, foodstuffs. The polyolefin layer imparts to the film certain properties such as high tear strength when linear low-density polyethylene (LLDPE) is used as polyolefin or good surface gloss when polypropylene is used as polyolefin, whilst as a rule the polyamide layer is intended to impart barrier properties to the film.
A problem of the known process is that combinations of polyamide layers and polyolefin layers that in themselves are sufficient to impart a desired combination of properties to the film often are difficult to process by blow-moulding. A suitable setting of the blow-moulding device proves difficult to find, and in addition such setting must be maintained within narrow limits. This renders the process difficult and little flexible, particularly in terms of production rate and blow-up ratio.
A known solution to this problem is to admix, in particular in the polyolefin, a material that improves processability in a blow-moulding process. Another known solution is to add a layer of for example LDPE to provide the required bubble stability. The addition of an extra layer is both technically complex and more costly.
The invention aims to provide a process for blow-moulding a film as mentioned in the opening lines with the mentioned problems and drawbacks being completely or partly avoided.
This aim is achieved by the process according to the invention by a branched polyamide being used as polyamide.
It has been found that a film bubble containing the mentioned layers possesses better stability and can be blow-moulded at a higher throughput than when non-branched polyamide is used. Films having the desired combinations of layer thickness and properties, which otherwise can be realized only by addition of another material to the polyolefin layer or by addition of an extra layer to the film can be produced at a high production rate. Due to the presence of the branched nylon, even in combination with for example LLDPE and PP, that are known for poor bubble stability, bubble stability is comparable with that of the combination of non-branched polyamide with low-density polyethyelene (LDPE), which is known for its excellent processability through blow-moulding.
Blow-moulding, including blow-moulding of multilayer films, is a process known per se that may be applied in its known embodiments in the process according to the invention, which process does not impose any special requirements therefor.
As branched polymer use may be made of the known branched polymers characterized in that at least 50% of the polymer chains possesses more than one chain branch or in that the polyamide molecule contains at least a star-shaped section. Branched polymers are known from for example EP-A-345 648, WO-00/35992 and WO-97/24388. It is preferred to use gel-free branched polyamides such as those known from WO-00/35992. These give films of highly uniform appearance without the irregularitiers caused by gels. These may be characterized as intrinsically gel-free, randomly branched polyamides at least composed of units derived from:
As material in the polyolefin layer use is made of the known polyolefins, in particular homopolymers of ethylene and copolymers thereof with one or more α-olefins and homopolymers of propylene and copolymers thereof with one or more α-olefins, in particular ethylene. The gain in bubble stability and production rate manifest themselves in particular when the polyolefin layer consists essentially of a polyolefin that, in a blow-moulding process, in itself possesses insufficient bubble stability in order for it to be processed into a film in a technically and economically acceptable manner. Examples hereof are LLDPE and polypropylene.
LLDPE is used in multilayer films for imparting high tear strength to the film but in itself can hardly be processed into a blown film in combination with the non-branched polyamide used according to the state of the art. A solution to this problem often applied in practice is to replace a proportion of the LLDPE with another polyethylene, for example LDPE or HDPE. This does improve bubble stability but the presence of the other polyethylene results in a significant decrease in tear strength.
The advantages of the process according to the invention thus best manifest themselves when LLDPE is used as material for a second layer in the film, even when the LLDPE layer contains at most 5 wt. % down to completely no other polyethylene. LLDPE is a form of polyethylene known per se to one skilled in the art. It is a copolymer of ethylene and one or more α-olefins that can be traced back in the end product as short side chains, produced in a low-pressure process and having a density of 870-940 kg/m3, more in particular of 900-930 kg/m3. The material distinguishes itself from low-density polyethylene (LDPE) by the short side chains, in contrast to the long side chains present in LDPE and from high-density polyethylene (HDPE) by low crystallinity.
The LLDPE layer then consists essentially of LLDPE, which should be taken to mean that it contains at most 10% and preferably at most 8% of another polyethylene not being LLDPE and in addition only the customary additives, examples of which are thermal and UV-stabilizers and release agents. The LLDPE layer may contain 10-50% of a modified LLDPE as adhesion modifier. Suitable modified LLDPEs are those which are described below as being suitable for use as adhesive layer between the polyamide layer and the LLDPE layer. Such LLDPE layers in combination with a layer of non-branched nylon cannot in general be blown to form a film bubble with sufficient bubble stability.
The advantages of the the process according to the invenstion are particularly prominent in that it is possible to use also LLDPE containing not more than 5% or even 0% of another polyethylene with good bubble stability. In that case, the high tear strength of the LLDPE is utilized to maximum effect with optimum layer thicknesses.
All polyethenes other than LLDPE are in principle suitable as the other polyethylene that may be admixed in the LLDPE layer. Examples hereof are (LDPE) and high-density polyethylene (HDPE) produced with the Ziegler-Natta and metallocene catalysts known per se for the purpose.
If polypropylene is used as polyolefin, the advantages of the process according to the invention best manifest themselves when linear polypropylene is used, which in itself cannot be applied in a blow-moulding process or can be applied in such process only with great difficulty and at a low poroduction rate. The Melt Flow Index of the polypropylene is preferably between 0.5 and 5 g/10 min.
As a rule, in the process according to the invention the polyamide layer preferably is adjacent to the polyolefin. Application of the polyamide layer and the polyolefin layer as adjacent functional layers directly connected to each other or connected by an adhesive layer has been found to yield the highest bubble stability. The layers may thus be directly adjacent to each other but an adhesive layer may also be present between the layers. Examples of suitable materials for these adhesive layers are modified polyolefins such as LDPE, LLDPE, metallocene PE, polyethylene-vinyl alcohol, polyethylene-acrylic acid, polyethylene-methacrylic acid and polypropylene that are grafted with at least one compound chosen from the group of α,β-unsaturated dicarboxylic acids, for example maleic acid, fumaric acid and itaconic acid and anhydrides, acidic esters, acidic imides and acidic imines thereof. Modified copolymers of ethylene and the aforementioned dicarboxylic acids may also be applied as adhesive layer in the manner indicated.
If the layers are directly adjacent to each other, the polyolefin layer preferably consists of a mixture of the polyolefin and a modified polyolefin referred to as being suitable as an adhesive layer for promoting adhesion between the polyolefin layer and the polyamide.
The polyamide layer may also be adjacent to a polyolefin layer on two sides, for example an LLDPE layer, and the other way round. The formed film then contains for example a PA-LLDPE-PA or LLDPE-PA-LLDPE sandwich structure.
Besides the mentioned layers, one or more other functional layers may also be applied. Layers often used in multilayer film are those which consist of for example ethylene-vinylalcohol and ionomers.
The total thickness of multilayer films that are produced in practice by blow-moulding and also by the process according to the invention is between 20 and 300 μm. In the process according to the invention the polyolefin layer in the multilayer film preferably has a thickness of at least 10 μm. The upper limit of the thickness is given by the intended application and the properties required therefor and extends in practice to approx. 100 μm. The branched-polyamide layer has a thickness of at least 2 μm and preferably of at least 20% of the thickness of the polyolefin layer, up to a maximum of 150, preferably 100 μm. Any other layers present have such thicknesses that they are able to perform their intended function during the production process or in the multilayer film to be formed.
The blow-up ratios applied in the process according to the invention prove to be able to be chosen higher than when the conventional non-branched polyamide is applied. Blow-up ratios of more than 10% and even 20%-40% higher have proved possible in the process according to the invention, which thus possesses significantly higher flexibility than the known process.
The invention also relates to a multilayer film containing at least a polyamide layer and a polyolefin layer connected thereto, characetrized in that the polyamide is a branched polyamide.
The film according to the invention possesses excellent barrier properties and properties introduced by the polyolefin layer at a lower thickness than the known film with non-branched nylon.
In particular, when LLDPE is used as polyolefin, the film possesses high tear strength in comparison with the amount of polyethylene present in the film and may possess the desired good barrier and tear strength properties at low total thickness. In the case of application of a polyolefin consisting essentially, i.e. at least 95%, of polypropylene there is obtained a thin film with good surface properties such as high gloss.
Each polyolefin layer may be connected to the adjacent PA layer since an adhesion modifier, in particular a modified polyolefin as described above for this purpose, is present in the polyolefin. A separate adhesive layer as described above for this purpose may also be present.
The invention is elucidated with reference to the following examples and comparative experiments.
In a Bandera blown film line equipped with 3 extruders each having an annular die 100 mm in diameter there was blown a film bubble consisting of two outer layers of a PE mixture consisting of 60 wt. % LLDPE, 30 wt. % LDPE and 10 wt. % Yparex™ 0H040, an MZA-modified LLDPE, as adhesion modifier and a polyamide intermediate layer. The LLDPE was a copolymer of ethylene and butene with a Melt Flow Index (ASTM D-1238, 2.16 kg, 190° C.) of 2.7 g/10 min, a melting point of 125° C. and a density of 928 kg/m3. The barrel temperature of the extruders was 250° C. and the head temperature 260° C. The blow-up ratio was 2.1.
The total thickness of the blown film was 25 μm, made up of 2 PE outer layers each of 10 μm and a polyamide intermediate layer of 5 μm. In Comparative Experiment A use was made of Akulon™ F126-C, a non-branched polyamide-6, as polyamide and in Example I a branched polyamide made, according to the process of WO00/35992, from 97 parts by weight of caprolactam, 0.62 part by weight of bis-hexamethylene-triamine, 0.42 part by weight of adipic acid and 0.71 part by weight of benzoic acid with a relative viscosity (measured in a 1 mass % solution in 90% formic acid at 25° C.) of 2.80.
The Elmendorf tear strength measured in the direction of extrusion was 27 kN/m and 25 kN/m, respectively. The bubble stability in Example I was markedly better than in Comparative Experiment A.
The process of Comparative Experiment A was repeated except that as PE layer use was made of a layer consisting of 90 wt. % LLDPE and 10 wt. % Yparex 0H040. It proved impossible to control the process in such a way as to obtain a bubble of sufficient stability.
The process of Example I was repeated except that the PE layers consisted of 90 wt. % LLDPE and 10 wt. % Yparex 0H040 as adhesion modifier. The blow-up ratio in Example I was 2.1 and in Example II 2.5.
The Elmendorf tear strength measured in the direction of extrusion was 104 kN/m and 98 kN/m, respectively.
From the foregoing it is clear that, where non-branched nylon is used, the presence of an amount of LDPE is indispensible if a stable film bubble is to be obtained. Also, it is clear that, by using a branched nylon, it is possible to produce a blown film with PE layers containing either only LLDPE or a mixture of LLDPE and another polyethylene, with the films in which the PE in the PE layer consists of only LLDPE possessing a markedly higher tear strength.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1020393 | Apr 2002 | NL | national |
| 1020952 | Jun 2002 | NL | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/NL03/00242 | 3/28/2003 | WO | 5/23/2005 |