This patent application is co-pending with one related patent application entitled “SENSING/ACTUATING MATERIALS MADE FROM CARBON NANOTUBE POLYMER COMPOSITES AND METHODS FOR MAKING SAME” (NASA Case No. LAR-16867-1), U.S. patent application Ser. No. 11/076,460, filed Mar. 3, 2005, by the same inventors as this patent application.
This invention relates to electroactive materials. More specifically, the invention relates to a multilayer electroactive composite material made from layers of electroactive materials wherein each layer is tailored in terms of its dielectric, electric and mechanical properties.
An electroactive material comprises multiple layers of electroactive material with each layer having unique dielectric, electrical and mechanical properties that define an electromechanical operation thereof when affected by an external stimulus.
The present exemplary embodiments provide a new class of electroactive polymer composite materials made from layers of electroactive materials. Each layer is tailored in terms of its dielectric, electric and mechanical properties that ultimately define the layer's electromechanical operation. By making each layer unique, the ultimate electroactive material is functionally gradient in its electromechanical operation. For example, each layer could be designed to have its electromechanical operation triggered only in response to a certain level (or range of levels) of external stimulus. Another option is for each layer to have a specific performance capability (e.g., an amount of displacement or voltage generated in response to an external stimulus) triggered by any level of external stimulus. Still another option is a combination of the previous two examples whereby each layer is designed for a specific performance that is triggered only when a specific level (or range of levels) of external stimulus affect the device. Accordingly, the term “functionally gradient electromechanical operation,” as used herein, can refer to the material's electroactive sensitivity and/or the material's electroactive performance.
Referring now to the drawings,
The layers in each of the above-described materials could be made from a variety of electroactive materials. For example, each layer could comprise one of the new electroactive materials described in the cross-referenced patent application entitled “SENSING/ACTUATING MATERIALS MADE FROM CARBON NANOTUBE POLYMER COMPOSITES AND METHODS FOR MAKING SAME,” U.S. patent application Ser. No. 11/076,460, filed Mar. 3, 2005, the contents of which are hereby incorporated in their entirety by reference. The new materials are carbon nanotube polymer composites that provide improved electromechanical operation when affected by some external stimulus. For example, the electromechanical operation can be a sensing operation that involves the generation of an electrical signal in response to deformation of the electroactive material caused by a change in its physical environment (e.g., changes in noise, vibration, stress, pressure, flow, temperature, etc.). The electromechanical operation could also be an actuating operation that involves mechanical movement of the electroactive material when the material has a stimulating electric potential applied thereto.
More specifically, each layer in a multilayer material of the exemplary embodiments can be an electroactive sensing/actuating (“sensuating”) material that comprises a 2-component or “2-phase” composite material. The base material is a polymer matrix wherein the polymer comprises an electroactive type having polarizable moieties. The remaining component or phase comprises nanotubes incorporated in the polymer matrix. Electroactive polymers with polarizable moieties include those with asymmetrically strong dipoles. Suitable polymer classes fitting this description include, but are not limited to, polyimides, polyamides, silicon-based polymers, vinyl polymers, polyurethanes, polyureas, polythioureas, polyacrylates, polyesters, and biopolymers. The polyimides include but are not limited to 2,6-bis(3-aminophenoxy) benzonitrile ((β-CN)APB)/4,4′oxydiphthalic anhydride (ODPA) ((β-CN)APB-ODPA) and other polyimides with polarizable moieties, and polyetherimide (e.g., the commercially-available ULTEM®). The polyamides include but are not limited to odd-numbered nylons. The silicon-based polymers include but are not limited to silicone and polydimethylsiloxane (PDMS). The vinyl polymers include but are not limited to PVDF, PVDF/TrFE (copolymer of vinylidene fluoride and trifluoroethylene), poly(vinyl alcohol) (PVA), a graft elastomer such as that claimed in U.S. Pat. No. 6,515,077, the entire contents of which are incorporated herein by reference, and vinyl copolymers. The polyacrylates include but are not limited to polymethyl methacrylate (PMMA). The biopolmers include but are not limited to polypeptides and keratin.
The presence of strong dipoles (associated with the above-mentioned-polymers with polarizable moieties) have led researchers and industry to attempt to construct piezoelectric sensors and actuators from these materials and blends of such polymers as disclosed, for example, in U.S. Pat. No. 6,689,288, the entire contents of which are incorporated herein by reference.
The 2-phase electroactive materials described herein use nanotube inclusions to improve the electomechanical response of the polymer having polarizable moieties. In general, such nanotubes can be based on a variety of elements, including carbon or other metallic and semi-metallic elements. However, carbon nanotubes will be described specifically in the example. Such carbon nanotubes can be single-wall nanotubes (referred to as “SWNT”), or they can be nanotubes made from multiple walls, e.g., double-wall, few-wall, multi-wall, etc., all of which are referred to herein as “MWNT”.
Accordingly, the 2-phase electroactive sensing/actuating (or sensuating) composite comprises a selected polymer matrix having nanotube inclusions. In order to produce an electroactive material that acts as either a sensor or actuator, it has been discovered that only small amounts of carbon nanotubes need to be incorporated into the polymer matrix. The small amounts of nanotubes used in the 2-phase composite materials are defined herein as a volume fraction of the ultimate composite. For example, the volume fraction of nanotubes in the exemplary 2-phase composite is expressed as “X percent of the volume of the composite”. The value of “X” is arrived after consideration of the type of operation (e.g., sensing, actuating) and the amount of electromechanical motion of interest for a given polymer matrix and given external stimulus. No specific volume fraction of nanotubes (for a particular polymer) will define a clear transition between sensing and actuating operations. Rather, a general range of volume fraction of nanotubes will enable the composite to behave better as either a sensor or actuator. Thus, the sensing or actuating functions of the material for the present embodiment can be varied and controlled by the volume fraction of nanotube inclusions.
The above-described 2-phase sensing/actuating (sensuating) polymer composite comprises pure polymers with polarizable moieties having nanotube inclusions. However, the layers in the multilayer composite material of the exemplary embodiments could also be made from, for example, a 3-phase polymer composite wherein the three components comprise:
(i) a polymer matrix wherein the polymer is an electroactive type having polarizable moieties,
(ii) micro to nano-sized particles of an electroactive ceramic incorporated in the polymer matrix, and
(iii) carbon nanotubes incorporated in the polymer matrix.
Prior efforts to improve the electromechanical operation of pure piezoelectric polymers have focused on incorporating various piezoelectric ceramics (e.g., lead-zirconium-titanate or “PZT”) into the polymers to form a, composite. However, the large dielectric mismatch between these two significantly different types of materials (i.e., ceramic-to-polymer dielectric ratios on the order of 50:1 or greater) makes it difficult to pole both phases of the composite. That is, the electric field required to pole both phases is generally much larger than the electric field required to pole the pure ceramic phase because of a large dielectric mismatch.
The 3-phase sensing/actuating (sensuating) composites reduce dielectric mismatch through the use of small amounts of nanotube inclusions. As in the 2-phase case, nanotubes utilized in the 3-phase composites can be based on a variety of elements to include carbon and other metallic or semi-metallic elements. Carbon nanotubes will be described specifically in the example. The carbon nanotubes used in the 3-phase composite can be SWNT or MWNT.
The electroactive ceramics utilized in the 3-phase composite of the present embodiment can be any piezoelectric ceramic that can be reduced to micro-sized or nano-sized particles while providing the appropriate electromechanical response, thermal stability and chemical stability for a predetermined application. Such ceramics include but are not limited to lead-zirconium-titanate (PZT), lanthanum-modified lead zirconate titanate (PLZT), niobium-modified lead zirconate titanate (PNZT), and barium titanate. By way of illustrative example, the electroactive ceramic PZT will be-specifically discussed.
An embodiment of the 3-phase composite comprises a selected polymer matrix with both ceramic and nanotube inclusions.
To produce a 3-phase composite that acts as either a sensor or actuator, only small amounts of nanotubes need to be incorporated in the composite. Similar to the 2-phase composite, the amount of nanotube inclusions is expressed as a volume fraction of nanotubes to the total volume of the ultimate 3-phase composite.
Methods for making the 3-phase composite include steps for the nanotubes to be either: (i) incorporated in the polymer matrix before incorporation of the ceramic particles, or (ii) first mixed with the ceramic particles in a solution that is then incorporated in the polymer matrix.
The three-component nature of the 3-phase composite provides for the tailoring and adjusting of composition and morphology to optimize mechanical, electrical, and electromechanical properties for sensing and actuating operations. The effects of the dielectric mismatch between the polymer and ceramic are greatly reduced by nanotube inclusions that serve to raise the dielectric constant of the polymer matrix in the 3-phase composite even when small amounts of nanotubes are used. Thus, the amount of nanotubes used is a predetermined volume fraction that balances the amount required to minimize the dielectric mismatch between the polymer and ceramic against the amount requisite for providing a predetermined electromechanical operation during a given application.
Multilayer electroactive composite materials of the present invention can be made from layers of the above-described (i) 2-phase composites, (ii) 3-phase composites, or (iii) 2-phase and 3-phase composites. The base polymer in each layer can be the same or different. In terms of the 3-phase composites, the ceramic used in each layer can be the same or different. Under this approach, each layer of the multilayer material can be specifically tailored in terms of its dielectric, electric and mechanical properties that define the electromechanical operation of the layer.
Examples of 2-phase and 3-phase composite materials suitable for use in multilayer composite materials of the exemplary embodiments will now be described. The selected polymer in both the 2-phase and 3-phase materials was an aromatic piezoelectric polyimide, β-CN APB/ODPA polymer matrix. The nanotubes used were single-wall carbon nanotubes or “SWNT” as they will be referred to hereinafter. The diameter and length of the SWNTs were approximately 1.4 nm and 3 μm, respectively. The2-phase SWNT-polyimide composites were prepared by in situ polymerization under sonication and stirring. The density of pure polyimide was about 1.3 g/cm3, and the calculated density of the SWNTs have been reported ranging from 1.33-1.40 depending on chirality. The diamine and dianhydride used to synthesize the nitrile polyimide were 2,6-bis(3-aminophenoxy) benzonitrile ((β-CN)APB) and 4,4′oxidiphthalic anhydride (ODPA), respectively. To prepare the SWNT-polyimide 2-phase composite, the SWNTs were dispersed in anhydrous dimethyl formamide (DMF) that served as a solvent for the poly(amic acid) synthesis. The entire reaction was carried out with stirring in a nitrogen-purged flask immersed in a 40 kHz ultrasonic bath until the solution viscosity increased and stabilized. Sonication was terminated after three hours and stirring was continued for several hours to form a SWNT-poly(amic acid) solution. The SWNT-poly(amic acid) solution was cast onto a glass plate and dried in a dry air-flowing chamber. Subsequently, the dried tack-free film was thermally cured in a nitrogen oven to obtain solvent-free freestanding SWNT-polyimide film.
A series of SWNT-polyimide nanocomposite films were prepared with SWNT concentrations ranging from just greater than 0.00 percent (e.g., 0.01 percent) to approximately 2.0 percent volume fractions. A similar procedure was followed to make the 3-phase SWNT-PZT-polyimide composites (having similar SWNT concentrations) where, in addition to dispersing the SWNT in DMF before the poly(amic acid) synthesis, nano-sized PZT particles/powders were also dispersed in DMF separately and then mixed with SWNT-DMF and the polyimide precursor.
In
The 3-phase composite will generally need the step of poling due to the piezoceramic incorporated therein. Accordingly, Table 2 presents the results of poling (i) pure polyimide, (ii) polyimide with just PZT ceramic inclusions, and (iii) a 3-phase composite material of polyimide having 0.1 percent SWNT and PZT ceramic inclusions. The remanent polarization values, which are indicative of the piezoelectric response, indicate that adding the PZT increases the Pr slightly. The Pr value increases dramatically, however, when poling a similar content of PZT-polyimide composite that further includes SWNTs. This result confirms that the presence of SWNTs raises the dielectric constant of the composite so that it is possible to pole the PZT particles and the polyimide simultaneously.
The mechanical properties of the 2-phase and 3-phase composites were also measured to assess the effect of adding the SWNTs and PZT inclusions oh the modulus of the polyimide. Test results reveal that significant reinforcement occurs at temperatures below and above the glass transition temperature due to the addition of SWNTs, although a larger reinforcement effect occurs at temperatures above the glass transition temperature.
Having various layers of electroactive composites exhibit variable electroactive properties can be valuable in a number of sensor applications where tunable optical and dielectric properties might be required for optimal performance, e.g., chemical sensors, optical waveguides, etc. By utilizing uniquely tailored electroactive materials to form a multilayer electroactive material, the embodiments can be used to provide functionally gradient electromechanical operation in a single device. Each layer is made from a new class of carbon nanotube polymer composite sensing/actuating materials. Sensing and actuating can be tailored layer-by-layer as a function of carbon nanotube loadings. The 2-phase and 3-phase carbon nanotube polymer composites described herein by way of illustration are good candidates for material layers of the exemplary embodiments as they provide greater sensing and actuating responses at much lower external stimuli as compared to other known electroactive materials.
Although only a few exemplary embodiments of this invention have been described in detail above, those skilled in the art will readily appreciate that many modifications are possible in the exemplary embodiments without materially departing from the novel teachings and advantages of this invention. Accordingly, all such modifications are intended to be included within the scope of this invention as defined in the following claims. In the claims, means-plus-function and step-plus-function clauses are intended to cover the structures or acts described herein as performing the recited function and not only structural equivalents, but also equivalent structures. Thus, although a nail and a screw may not be structural equivalents in that a nail employs a cylindrical surface to secure wooden parts together, whereas a screw employs a helical surface, in the environment of fastening wooden parts, a nail and a screw may be equivalent structures.
Pursuant to 35 U.S.C. §119, the benefit of priority from provisional application 60/551,055, with a filing date of Mar. 9, 2004, is claimed for this non-provisional application.
The invention was made in part by employees of the United States Government and may be manufactured and used by and for the Government of the United States for governmental purposes without the payment of any royalties thereon or therefore.
| Number | Name | Date | Kind |
|---|---|---|---|
| 6265466 | Glatkowski et al. | Jul 2001 | B1 |
| 6515077 | Su et al. | Feb 2003 | B1 |
| 6689288 | St. Clair et al. | Feb 2004 | B2 |
| 6762237 | Glatkowski et al. | Jul 2004 | B2 |
| 6764628 | Lobovsky et al. | Jul 2004 | B2 |
| 6809462 | Pelrine et al. | Oct 2004 | B2 |
| 6936653 | McElrath et al. | Aug 2005 | B2 |
| Number | Date | Country | |
|---|---|---|---|
| 20060057361 A1 | Mar 2006 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60551055 | Mar 2004 | US |