Patent Application
20160375413
Multiple emulsions and techniques for the formation of multiple emulsions are generally described.
An emulsion is a fluidic state which exists when a first fluid is dispersed in a second fluid that is typically immiscible or substantially immiscible with the first fluid. Examples of common emulsions are oil in water and water in oil emulsions. Multiple emulsions are emulsions that are formed with more than two fluids, or two or more fluids arranged in a more complex manner than a typical two-fluid emulsion. For example, a multiple emulsion may be oil-in-water-in-oil, or water-in-oil-in-water. Multiple emulsions are of particular interest because of current and potential applications in fields such as pharmaceutical delivery, paints and coatings, food and beverage, and health and beauty aids.
Systems, articles, and methods related to multiple emulsions are provided. The subject matter of the present invention involves, in some cases, interrelated products, alternative solutions to a particular problem, and/or a plurality of different uses of one or more systems and/or articles.
In one aspect, a method of forming droplets is described. In some embodiments, the method comprises flowing a first fluid in a first conduit; expelling the first fluid from an exit opening of the first conduit into a second fluid in a second conduit such that droplets of the first fluid are not formed at the exit opening of the first conduit; and expelling the first fluid and the second fluid from an exit opening of the second conduit into a third fluid to form a multiple emulsion droplets comprising the second fluid surrounding droplets of the first fluid.
The method comprises, in some embodiments, expelling a first fluid from an exit opening of a first conduit into a second fluid in a second conduit; and expelling the first fluid and the second fluid from an exit opening of the second conduit into a third fluid to form a multiple emulsion droplets comprising a shell of the second fluid surrounding droplets of the first fluid. In some embodiments, the shell has an average thickness of less than about 0.05 times the average cross-sectional diameter of the multiple emulsion and/or the shell has an average thickness of less than about 1 micrometer.
In some embodiments, the method comprises expelling a first fluid from an exit opening of a first conduit into a second fluid being transported through a second conduit via a first entrance opening of the second conduit; and flowing a third fluid and a fourth fluid through a second entrance opening of the second conduit to form multiple emulsion droplets comprising a shell of the third fluid surrounding the second fluid and a shell of the second fluid surrounding the first fluid.
In one aspect, a device is provided. In some embodiments, the device comprises a first conduit, an outer injection conduit having an exit opening contained within the first conduit, an inner injection conduit having an exit opening contained within the outer injection conduit, and a collection conduit having an entrance opening contained within the first conduit but not contained within the outer injection conduit. In some embodiments, the outer injection conduit is at least partially coated with a hydrophobic coating, and the other tubes are not coated with the hydrophobic coating.
In one aspect, an article is provided. In some embodiments, the article comprises a microfluidic device comprising a double emulsion droplet production region, wherein the double emulsion droplet production region consists essentially of a first conduit, an outer injection conduit having an exit opening contained within the first conduit, an inner injection conduit having an exit opening contained within the outer injection conduit, and a collection conduit having an entrance opening contained within the first conduit but not contained within the outer injection conduit.
The article comprises, in some embodiments, a particle having a shell comprising a polymer, the particle having an average diameter of less than about 1 mm, the shell at least partially containing a fluid. In some embodiments, the shell has an average thickness of less than about 0.05 times the average cross-sectional diameter of the particle and/or the shell has an average thickness of less than about 1 micrometer; and substantially all of the polymer within the shell has a glass transition temperature of at least about 85° C. and/or substantially all of the polymer within the shell is at least partially soluble in octane.
Other advantages and novel features of the present invention will become apparent from the following detailed description of various non-limiting embodiments of the invention when considered in conjunction with the accompanying figures. In cases where the present specification and a document incorporated by reference include conflicting and/or inconsistent disclosure, the present specification shall control.
Non-limiting embodiments of the present invention will be described by way of example with reference to the accompanying figures. For purposes of clarity, not every component is labeled in every figure, nor is every component of each embodiment of the invention shown where illustration is not necessary to allow those of ordinary skill in the art to understand the invention. In the figures:
Multiple emulsions and techniques for the formation of multiple emulsions are generally described. A multiple emulsion, as used herein, describes one or more larger droplets that contain one or more smaller droplets therein. In some embodiments, the larger droplets may be suspended in a carrying fluid containing the larger droplets that, in turn, contain the smaller droplets. As described below, multiple emulsions can be formed in one step in certain embodiments, with generally precise repeatability, and can be tailored in some embodiments to include a relatively thin layer of fluid separating two other fluids.
The formation of emulsions and multiple emulsions containing droplets with a uniform size, shape, and/or a uniform number of smaller droplets contained within larger droplets is known in the art. For example, International Patent Publication No. WO 2008/121342 by Weitz, et al., describes the use of microfluidic systems to produce multiple emulsions containing uniformly sized larger droplets each containing smaller droplets. Generally, in these systems, multiple emulsions are formed by nesting multiple immiscible fluids within a microfluidic conduit system. The multiple emulsions can be produced by first producing one or more droplets of a first fluid within a second fluid at the exit of a first conduit. These droplets are then transported to the end of a second conduit, where a multiple emulsion is formed in which the second fluid surrounds the droplets of the first fluid.
In addition, the formation of multiple emulsions in which the first and second droplets are formed simultaneously is known in the art. For example, International Patent Publication Number WO 2006/096571 by Weitz, et al., includes a description of various microfluidic systems in which fluids are transported through two nested conduits contained within another conduit to produce multiple emulsions. However, multiple conduits are typically used in these systems, and in some cases, an inner conduit is nested within a surrounding conduit such that the exit opening of the inner conduit extends past the exit opening of the surrounding conduit. As another example, International Patent Publication Number WO 2011/028764, by Weitz, et al., describes the formation of multiple emulsions, but in various systems that include certain intersections of different conduits.
The present invention is generally directed to surprising new methods of flowing fluids in conduits (and associated articles and systems) to produce multiple emulsions. As described in more detail below, it has been discovered that increasing fluid flow rates from a stable operating regime produces an unstable operating regime, but unexpectedly, further increases in flow rates produce a second stable operating regime. In some cases, the multiple emulsions formed within the second, stable operating regime may comprise relatively thin intermediate fluid shells. Rather than first producing droplets of a first fluid at an exit opening of a first conduit and subsequently passing these droplets through an end of a second conduit to produce a double emulsion (i.e., operating under a “droplet flow” regime), the first and second droplets within the multiple emulsions of the present invention may be formed simultaneously. Simultaneous formation of the first and second droplets can be achieved, in some embodiments, by transporting a first fluid within a first conduit at a relatively high flow rate such that the first fluid forms a continuous stream of fluid within the second fluid as the first fluid exits the first conduit (i.e., a “jetting flow” regime). As the jet of the first fluid exits a second conduit located downstream of the first conduit, the second fluid can surround the first fluid, thereby forming a double emulsion. When operated under a jetting flow regime, the multiple emulsions formed at the exit opening of the second conduit may contain, in some embodiments, relatively thin shells of the second fluid. In addition, operation under a jetting flow regime may allow for high speed production of multiple emulsions, relative to the droplet flow regime, at least in some cases.
One reason the benefits of operation under a jetting flow regime in certain embodiments are surprising is because, in order to transition from the droplet flow regime to the jetting flow regime, one must first pass through an intermediate regime in which the fluid flow is unstable and generally unsuitable for producing multiple emulsions, especially consistently-sized multiple emulsions. In the present invention, it has been unexpectedly found that further increases in fluid flow rates do not lead to increased fluid instability, as would be expected; rather, further increases in flow rates from an unsteady regime surprisingly lead to more stability, not less. In particular, it has been found that increasing the flow rate through the unsteady regime may lead to stable operation, for example, in which consistently-sized multiple emulsions with the relatively thin shells can be produced at relatively high speeds.
A multiple emulsion droplet may contain one or more droplets therein. A “droplet,” as used herein, is an isolated portion of a first fluid that is surrounded by a second fluid. It is to be noted that a droplet is not necessarily spherical, but may assume other shapes as well, for example, depending on the external environment. In some embodiments, the droplet has a minimum cross-sectional dimension that is substantially equal to the largest dimension of the channel perpendicular to fluid flow in which the droplet is located.
Using the methods and devices described herein, in certain embodiments, a consistent volume and/or number of droplets are produced, and/or a consistent ratio of volume and/or number of outer droplets to inner droplets (or other such ratios) are produced. In addition, as described elsewhere, the relative volumes of the fluidic droplets within the multiple emulsion are configured in some cases to include a relatively thin layer of fluid, e.g., separating two other fluids. For example, in some cases, a single droplet within an outer droplet is configured/formed such that the inner droplet occupies a relatively large percentage of the volume of the outer droplet, thereby resulting in a thin layer of outer droplet fluid surrounding the inner droplet fluid. The thin layer of outer droplet fluid surrounding the inner droplet fluid, which may contain a polymer, may be subsequently dried to form a solid shell containing a fluid. The ability to precisely control the dimensions of the thin layer of outer droplet fluid can allow one to fabricate particles configured with thin shells, including any of the thicknesses or other dimensions described elsewhere herein.
In some embodiments, a triple emulsion may be produced, i.e., an emulsion containing an inner droplet (or first) fluid, surrounded by an outer droplet (or second) fluid, which in turn is surrounded by a third or carrying fluid. In some cases, the carrying fluid and the outer droplet fluid may be the same. These fluids are often of varying miscibilities due to differences in hydrophobicity. For example, the inner droplet fluid may be water soluble, the outer droplet fluid oil soluble, and the carrying fluid water soluble. This configuration is often referred to as a W/O/W multiple emulsion (“water/oil/water”). Another multiple emulsion may include an inner droplet fluid that is oil soluble, an outer droplet fluid that is water soluble, and a carrying fluid that is oil soluble. This type of multiple emulsion is often referred to as an O/W/O multiple emulsion (“oil/water/oil”). It should be noted that the term “oil” in the above terminology merely refers to a fluid that is generally more hydrophobic and not miscible or soluble in water, as is known in the art. Thus, the oil may be a hydrocarbon in some embodiments, but in other embodiments, the oil may comprise other hydrophobic fluids.
In the descriptions herein, multiple emulsions are generally described with reference to a three phase system, i.e., having an inner droplet fluid, an outer droplet fluid, and a carrying fluid. However, it should be noted that this is by way of example only, and that in other systems, additional fluids may be present within the multiple emulsion. As examples, an emulsion may contain a first fluid droplet and a second fluid droplet, each surrounded by a third fluid, which is in turn surrounded by a fourth fluid; or an emulsion may contain multiple emulsions with higher degrees of nesting, for example, a first fluid droplet surrounded by a second fluid droplet, which is surrounded by a third fluid droplet, which is contained within a carrying fluid. Accordingly, it should be understood that the descriptions of the inner droplet fluid, outer droplet fluid, and carrying fluid are for ease of presentation, and that the descriptions herein are readily extendable to systems involving additional fluids, e.g., quadruple emulsions, quintuple emulsions, sextuple emulsions, septuple emulsions, etc.
The inner diameter of conduit 220 generally decreases in a direction from left to right, as shown in
As shown in
As illustrated in
Additionally, in some embodiments, outer droplet fluid 260 may not come into contact with the surface of conduit 230, at least until after a multiple emulsion droplet has been formed, because outer droplet fluid 260 is surrounded by carrying fluid 270 as the droplet enters collection tube 230.
As inner droplet fluid 250 and outer droplet fluid 260 are transported out of exit opening 225 of conduit 220, two droplets may be formed: an outer droplet 280 (including outer droplet fluid 260) and an inner droplet 285 (including inner droplet fluid 250) positioned within the outer droplet 280. As illustrated in
While inner droplet fluid 250 is illustrated as forming a continuous jet extending from conduit 240 to exit opening 225 of conduit 220 in
In contrast, a “dripping flow” regime refers to a condition in which a first fluid is broken up into droplets in a second fluid within a distance from the exit of the conduit through which it is delivered (e.g., conduit 240 in
In some embodiments, inner droplet fluid 250 and outer droplet fluid 260 do not break to form droplets until the fluids are inside of conduit 230 (i.e., to the right of end 235, which defines the entrance orifice of conduit 230 in
Droplet formation and morphology (and/or the corresponding morphology of particles formed from the droplets) can be affected in a number of ways, in various embodiments of the invention. For example, the geometry (physical configuration) of the device 200, including the relationship of the outer conduit and the inner conduits, may be configured to develop multiple emulsions of desired volume, frequency, and/or content. For example, the diameters of the exit openings at exit openings 225 and/or 245 of conduits 220 and 240, respectively, may be selected to help control the relative volumes of the formed droplets. Droplet formation may be affected, in some cases, by the rate of flow of the inner droplet fluid, the rate of flow of the outer droplet fluid, the rate of flow of the carrying fluid, the total amount of flow or a change in the ratios of any two of these, and/or combinations of any of these flow rates.
The relative volumes of the inner droplet and the outer droplet may also be carefully controlled in certain embodiments, i.e., the ratio of the size or volume of the inner and outer droplets. The inner droplet may fill a relatively large portion of the outer droplet. Such emulsions can be useful, for example, in forming particles with relatively thin shells, as discussed herein. In some embodiments, the inner fluid droplet may fill greater than about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, about 70%, about 90%, about 95%, or about 99% of the volume of the outer droplet. In some cases, the outer droplet can be considered a fluid shell, or coating, when it contains an inner droplet, as some or most of the outer droplet volume may be filled by the inner droplet. In some embodiments, the outer fluid shell thickness can be equal to or less than, for example, about 5%, about 4%, about 3%, about 2%, about 1%, or about 0.1% of the outer fluid droplet radius. This allows, in some embodiments, for the formation of multiple emulsions with only a very thin layer of material separating, and thus stabilizing, two miscible fluids.
Of course, the invention is not limited to the formation of multiple emulsions including thin outer droplets, and, in other embodiments, the inner droplet may fill only a small portion of the outer droplet. In some embodiments, the inner droplets may fill less than about 90%, less than about 80%, less than about 70%, less than about 60%, less than about 50%, less than about 30%, less than about 20%, or less than about 10% of the volume of the outer droplet. The shell material can also be greater than or equal to, e.g., about 10%, about 20%, about 30%, about 40%, or about 50% of the outer fluid droplet radius.
In addition, by controlling the geometry (physical configurations) of the conduits and/or the flow of fluid through the conduits, the average cross-sectional diameters of the droplets that are produced may be controlled in certain embodiments. Those of ordinary skill in the art will be able to determine the average cross-sectional diameter (or other characteristic dimension) of a plurality or series of droplets, for example, using laser light scattering, microscopic examination, or other known techniques. The average cross-sectional diameter of a single droplet, in a non-spherical droplet, is the diameter of a perfect sphere having the same volume as the non-spherical droplet. The average cross-sectional diameter of a droplet (and/or of a plurality or series of droplets) may be, for example, less than about 1 mm, less than about 500 micrometers, less than about 200 micrometers, less than about 100 micrometers, less than about 75 micrometers, less than about 50 micrometers, less than about 25 micrometers, less than about 10 micrometers, or less than about 5 micrometers in some cases. The average cross-sectional diameter may also be at least about 1 micrometer, at least about 2 micrometers, at least about 3 micrometers, at least about 5 micrometers, at least about 10 micrometers, at least about 15 micrometers, or at least about 20 micrometers in certain cases. In some embodiments, at least about 50%, at least about 75%, at least about 90%, at least about 95%, or at least about 99% of the droplets within a plurality of droplets has an average cross-sectional diameter within any of the ranges outlined in this paragraph.
The droplets may be of substantially the same shape and/or size (i.e., “monodisperse”), or of different shapes and/or sizes, depending on the particular application. In some cases, the droplets may have a homogenous distribution of cross-sectional diameters, i.e., the droplets may have a distribution of cross-sectional diameters such that no more than about 10%, about 5%, about 3%, about 1%, about 0.03%, or about 0.01% of the droplets have an average diameter that is more than about 10%, about 5%, about 3%, about 1%, about 0.03%, or about 0.01% different from the average cross-sectional diameter of the droplets. Some techniques for producing homogenous distributions of cross-sectional diameters of droplets are disclosed in International Patent Application No. PCT/US2004/010903, filed Apr. 9, 2004, entitled “Formation and Control of Fluidic Species,” by Link et al., published as WO 2004/091763 on Oct. 28, 2004, incorporated herein by reference, and in other references as described below and/or incorporated herein by reference.
In some cases, such as when the outer droplets (containing outer droplet fluid 260) are formed at the same rate as are inner droplets (containing inner droplet fluid 250), there can be a one-to-one correspondence between the number of inner droplets and the number of outer droplets; for example, in some embodiments, each inner droplet is surrounded by an outer droplet, and each outer droplet contains a single inner droplet of inner fluid. In other embodiments, different ratios of the number of inner droplets and the number of outer droplets may be present. In some embodiments, substantially all of the multiple emulsion droplets that are produced are double emulsion droplets.
In some embodiments of the invention, at least a portion of a multiple emulsion may be solidified to form a particle, for example, an outer fluid and/or an inner fluid. A fluid can be solidified using any suitable method. For example, in some embodiments, the fluid may be dried, gelled, and/or polymerized, and/or otherwise solidified, e.g., to form a solid, or at least a semi-solid. The solid that is formed may be rigid in some embodiments, although in other cases, the solid may be elastic, rubbery, deformable, etc. In some cases, for example, an outer fluid may be solidified to form a solid shell at least partially containing an interior containing a fluid and/or an agent. Any technique able to solidify at least a portion of a fluidic droplet can be used. For example, in some embodiments, a fluid within a fluidic droplet may be removed to leave behind a material (e.g., a polymer) capable of forming a solid shell. In other embodiments, a fluidic droplet may be cooled to a temperature below the melting point or glass transition temperature of a fluid within the fluidic droplet, a chemical reaction may be induced that causes at least a portion of the fluidic droplet to solidify (for example, a polymerization reaction, a reaction between two fluids that produces a solid product, etc.), or the like. Other examples include pH-responsive or molecular-recognizable polymers, e.g., materials that gel upon exposure to a certain pH, or to a certain species.
In some embodiments, a fluidic droplet is solidified by increasing the temperature of the fluidic droplet. For instance, a rise in temperature may drive out a material from the fluidic droplet (e.g., within an outer fluid droplet) and leave behind another material that forms a solid. For example, in embodiments illustrated in
Thus, an outer droplet may be solidified to form a solid shell that encapsulates one or more fluids and/or agents, for example, for delivery to a target medium, as described elsewhere herein. For example, in
In some embodiments, it may be desirable to control the temperature at which the multiple emulsion droplet is dried. For example, in some such embodiments in which shells are formed by drying a multiple emulsion, controlling the drying temperature can ensure that the shell is configured so that it does not rupture during the drying process. In some embodiments, the multiple emulsion may be dried at a temperature of between about 25° C. and about 100° C., between about 40° C. and about 80° C., between about 50° C. and about 70° C., or between about 55° C. and about 65° C. In some embodiments, the multiple emulsion may be washed prior to drying (or after, in some cases) using a variety of suitable solvents including, but not limited to toluene and water. For example, in one set of embodiments, after particles are formed, the carrying fluid containing the particles may be removed and/or replaced with a vehicle (e.g., for delivery to a target medium), which may or may not be the same as the carrying fluid.
It should be noted that
As an example,
As shown in
As shown in
The multiple emulsions including more than two nestings (e.g., triple emulsions, quadruple emulsions, etc.) can have any of the properties described elsewhere herein with respect to double emulsions. For example, the flow rates of the fluids can be controlled such that each nesting includes a single droplet. In such embodiments, the multiple emulsion comprises a core fluid surrounded by multiple layers of multiple outer fluids. Each droplet within such multiple emulsions may have any of the properties (e.g., thicknesses, variations in thickness (or lack thereof), cross-sectional diameter, etc.) described elsewhere herein. For example, in the embodiments illustrated in
While multiple emulsions containing a single droplet at each nesting level have been described, it should be understood that the invention is not so limited, and, in some embodiments, one or more nesting levels contain more than one droplet. For example, in some embodiments, the inner fluid forms a plurality of droplets within a middle fluid, and the middle fluid is surrounded by a thin layer of an outer fluid which is, in turn, surrounded by a carrying fluid. Some such embodiments are illustrated in
In some cases in which multiple droplets are present within a given nesting level, for a given nesting level of a multiple emulsion droplet, each of the fluidic droplets of that level may contain substantially the same number of inner fluidic droplets therein; for example, substantially all of the droplets may contain substantially the same number of droplets therein. It should be understood that, even if the droplets appear to be substantially identical (in any portion of a multiple emulsion droplet), or to contain substantially the same number of droplets therein, not all of the droplets will necessarily be completely identical. In some cases, there may be minor variations in the number and/or size of droplets contained within a surrounding droplet. Thus, in some cases, at least about 75%, at least about 80%, at least about 85%, at least about 90%, at least about 92%, at least about 94%, at least about 95%, at least about 96%, at least about 97%, at least about 98%, or at least about 99% of a plurality of droplets may each contain the same number of droplets therein.
The rate of production of multiple emulsion droplets may be determined by the droplet formation frequency, which under many conditions can vary between approximately 1 Hz and 5000 Hz. In some cases, the rate of droplet production may be at least about 1 Hz, at least about 10 Hz, at least about 100 Hz, at least about 200 Hz, at least about 300 Hz, at least about 500 Hz, at least about 750 Hz, at least about 1,000 Hz, at least about 2,000 Hz, at least about 3,000 Hz, at least about 4,000 Hz, or at least about 5,000 Hz.
Production of large quantities of emulsions may be facilitated by the parallel use of multiple devices such as those described herein, in some instances. In some cases, relatively large numbers of devices may be used in parallel, for example at least about 10 devices, at least about 30 devices, at least about 50 devices, at least about 75 devices, at least about 100 devices, at least about 200 devices, at least about 300 devices, at least about 500 devices, at least about 750 devices, or at least about 1,000 devices or more may be operated in parallel. The devices may comprise different conduits (e.g., concentric conduits), openings, microfluidics, etc. In some cases, an array of such devices may be formed by stacking the devices horizontally and/or vertically. The devices may be commonly controlled, or separately controlled, and can be provided with common or separate sources of various fluids, depending on the application.
The systems and methods described herein can be used in a plurality of applications. For example, fields in which the particles and multiple emulsions described herein may be useful include, but are not limited to, food, beverage, health and beauty aids, paints and coatings, chemical separations, and drugs and drug delivery. For instance, a precise quantity of a fluid, drug, pharmaceutical, or other agent can be contained by a shell designed to release its contents under particular conditions. In some instances, cells can be contained within a droplet, and the cells can be stored and/or delivered, e.g., to a target medium, for example, within a subject. Other agents that can be contained within a particle and delivered to a target medium include, for example, biochemical species such as nucleic acids such as siRNA, RNAi and DNA, proteins, peptides, or enzymes. Additional agents that can be contained within an emulsion include, but are not limited to, colloidal particles, magnetic particles, nanoparticles, quantum dots, fragrances, proteins, indicators, dyes, fluorescent species, chemicals, or the like. The target medium may be any suitable medium, for example, water, saline, an aqueous medium, a hydrophobic medium, or the like.
In one particular set of embodiments, particles comprising thin shells can be formed using the multiple emulsion techniques described herein. In some embodiments, as a non-limiting illustrative example, one or more particles can be used to deliver a fluid and/or an agent to a target medium, such as a hydrocarbon, crude oil, petroleum, or other medium. In some cases, at least some of the particles may comprise a solid portion or shell at least partially containing an interior containing a fluid and/or an agent. The shells of the particles can comprise a polymer, and in some cases, substantially all of the polymer within the shells is at least partially soluble in the target medium. The carrying fluid in which the particles are formed may be used as a vehicle used to contact the particles with a target medium, and/or the carrying fluid may be substituted by a suitable vehicle, as discussed elsewhere herein. When the particles contact the target medium, at least a portion of the shells of the particles can be disrupted, for instance, such that at least some of the fluid and/or agent within the particles is expelled or otherwise transported from the particles and into the target medium. Of course, it should be understood that the particles may be used in other applications as well, e.g., as discussed herein.
In some embodiments, the inventive particles are configured to withstand relatively high absolute pressures.
Shell 110 may comprise one or more polymers, such as polystyrene, polycaprolactone, polyisoprene, poly(lactic acid), and the like. Shell 110 can be formed, for example, by removing a liquid from a suspension of droplets of polymers in an outer fluid, leaving behind a solidified polymeric shell. Examples of this are discussed below.
Vehicle 105 may comprise any suitable fluid configured for delivering the particles 100 to the target medium 116. In some embodiments (e.g., in cases where target medium 116 contains crude oil and/or other hydrocarbons), vehicle 105 is hydrophilic (e.g., an aqueous vehicle).
In some embodiments, when the particles 100 contained within vehicle 105 are exposed to a medium 116 (e.g., a medium containing oil) such that the shell contacts the medium (for example medium 116 in
In some embodiments, some or all of the polymer within the shell is configured to be at least partially soluble in the target medium (e.g., a medium containing crude oil, a hydrocarbon, petroleum, an oil, etc.). As used herein, a material is configured to be “soluble” in a liquid medium when the material is exposed to a liquid medium at 25° C. and 1 atm, where the liquid medium has a mass of at least 100 times the mass of the material, and the material enters the liquid medium such that, at equilibrium, all of the material is contained within the liquid medium and no portion of the material forms a separate, macroscopic phase (e.g., as a precipitated solid or a phase-separated fluid). It should be understood that “solubility,” as used herein, does not necessarily require that the soluble material be dissolved within the medium at a molecular level, for example, a finely-dispersed suspension, a dispersion, an emulsion, etc. may be formed at equilibrium in some cases. In addition, a material is configured to be “partially soluble” when some, but not all, of the material is soluble within the liquid medium using the screening test discussed above. In certain cases, one or more of the polymers within the shell may be configured to be at least partially soluble in a chemical “indicative” of the target medium in certain cases, for instance, where the target medium is one that is not readily compositionally defined. For example, in some embodiments, one or more polymers within the shell may be configured to be at least partially soluble in octane, which may be used as a chemical indicative of crude oil.
In some embodiments, the shell may comprise one or more materials that are configured to not be soluble in hydrophilic fluids such as water, an alcohol, etc. The materials may, in some embodiments, include one or more polymers such as those described herein. The use of such shell materials in a particle allows, in some embodiments, for delivery of fluids and/or agents contained within the particle to a medium that the particle comes in contact with, for example, hydrocarbons, petroleum, an oil, etc.
In an example, a plurality of particles comprising water-insoluble shells and containing a surfactant (or any other suitable fluid and/or agent such as those described herein) are suspended in water, or another suitable vehicle. In this example, the suspension of particles in water is transported to or otherwise brought into contact with a region or location containing, or at least suspected of containing, oil, such as an oil well, a subterranean oil reservoir, a container of oil (e.g., a vial or a barrel), a chemical plant, a refinery, etc. In this example, prior to contacting the oil, the water-insoluble shells of the particles are configured to remain substantially intact, ensuring that the surfactant remains contained within the particles. In some embodiments, once the shells of the particles contact the target medium, the shell is disrupted, e.g., at least partially dissolving within the medium, thereby exposing at least some of the surfactant to the medium.
As noted above, the shell may comprise a polymer in some embodiments.
Exemplary polymers suitable for use in shells include, but are not limited to, polystyrene (PS), polycaprolactone (PCL), polyisoprene (PIP), poly(lactic acid), polyethylene, polypropylene, polyacrylonitrile, polyimide, polyamide, and/or mixtures and/or co-polymers of these and/or other polymers.
In some embodiments, the polymer may include a relatively linear polymer. Generally, linear polymers dissolve more quickly than highly cross-linked polymers, and are therefore be particularly useful in many applications. In some embodiments, the linear polymers are not substantially crosslinked (i.e., the polymers include linear chains of carbon atoms that do not include chemical bonding to other chains, although pendant groups may be present). It should be understood that, while the linear polymers may not be cross-linked, the linear polymers may be physically entangled with one another.
All or part of the shell of a particle may comprise a polymer that has a relatively high glass transition temperature (Tg), in some embodiments. Polymers with high glass transition temperatures are more resistant to rupture or disruption at high temperatures and/or pressures, which can make their use desirable for certain high temperature applications, such as some enhanced oil recovery processes. However, in other applications, polymers with lower glass transition temperatures may also be used. In some embodiments, substantially all of the polymer within the shell has a glass transition temperature of at least about 85° C., at least about 100° C., between about 85° C. and about 250° C., or between about 85° C. and about 200° C. One of ordinary skill in the art would be capable of determining the glass transition temperature of a polymer used in a shell by, for example, using differential scanning calorimetry (DSC). Generally, DSC defines the glass transition temperature as the temperature at which the polymer matrix goes from the glass state to the rubber state. Generally, polymers with relatively long chain lengths have relatively smaller chain mobility and relatively higher strength, toughness, and glass transition temperatures. Exemplary polymers with relatively high glass transition temperatures include, but are not limited to, polystyrene (PS), polycaprolactone (PCL), and polyisoprene (PIP), and/or mixtures and/or co-polymers of these and/or other polymers.
The molecular weight of the polymeric material used in the shell of the particle can also be selected to impart desirable physical properties, in accordance with some embodiments of the invention. For example, in certain embodiments in which relatively quick disruption of the shell of the particle is desired upon contact with the target medium, polymers with low weight-averaged molecular weights (e.g., less than about 20,000 g/mol) can be employed. In some embodiments in which it is desirable to rupture the shell relatively slowly, polymers with relatively high weight-averaged molecular weights (e.g., greater than about 20,000 g/mol, e.g., between about 20,000 g/mol and about 800,000 g/mol) can be employed.
In some embodiments, the shell of the particle is configured to withstand the application of relatively high pressures without rupturing. Mechanically robust shells may be produced by fabricating the shell from a mechanically resistant material, such as polystyrene, polycaprolactone, polyisoprene, and/or other mechanically resistant polymer or other material. In some embodiments, one or more particles (e.g., after drying) may be subjected to an absolute pressure of at least about 200 kPa, at least about 500 kPa, at least about 750 kPa, between about 100 kPa and about 1000 kPa, or between about 200 kPa and about 750 kPa (for example, in embodiments where the particles are suspended in water or another vehicle that is pressurized for delivery to a subterranean oil reservoir) without rupturing. In some embodiments, including some embodiments in which high pressure resistance is desired, the materials used in the shell are relatively elastic. For example, in some embodiments, the Young's modulus of the polymeric material used in the shell may be at least about 1 MPa, at least about 10 MPa, at least about 100 MPa, or at least about 1 GPa. In some embodiments, the Young's modulus of the polymeric material used in the shell may be less than about 10 GPa, less than about 5 GPa, or less than about 3 GPa.
The particles may be configured to be able to deliver a variety of agents. The agents may be fluid or solid, and/or the agent may be contained within a fluid (e.g., dissolved, suspended, etc.) In some embodiments, for example, the agent may include one or more surfactants. The surfactants can be delivered, for example, to a medium containing oil, or other medium as discussed herein. When the surfactant is delivered to a medium containing oil, for instance, the surfactant stabilizes the oil-water interface, which prevents the oil from forming a fine emulsion in the water, thus making the oil easier to separate from the water. A variety of surfactants may be contained within the particles. In some embodiments, for example, the particles may contain an ionic (e.g., cationic or anionic) surfactant. Exemplary anionic surfactants suitable for use include, but are not limited to, sodium dodecyl sulfate (SDS), ammonium lauryl sulfate, sodium lauryl sulfate, sodium laureth sulfate, dioctyl sodium sulfosuccinate, perfluorooctanesulfonate (PFOS), perfluorobutanesulfonate, alkyl aryl ether phosphate, alkyl ether phosphate, alkyl carboxylates, fatty acid salts (soaps), sodium stearate, sodium lauroyl sarcosinate, carboxylate fluorosurfactants, perfluorononanoate, perfluorooctanoate (PFOA or PFO), or the like. Exemplary cationic surfactants suitable for use include, but are not limited to, cetyl trimethylammonium bromide (CTAB), hexadecyl trimethyl ammonium bromide, cetyl trimethylammonium chloride (CTAC), cetylpyridiniumchloride (CPC), polyethoxylated tallow amine (POEA), benzalkonium chloride (BAC), benzethonium chloride (BZT), or the like. In some embodiments, non-ionic surfactants are used, including, but not limited to: sorbitan monooleate (also referred to as Span 80); Poly(ethylene glycol)-block-poly(propylene glycol)-block-poly(ethylene glycol), Poly(propylene glycol)-block-poly(ethylene glycol)-block-poly(propylene glycol) (also referred to as F 108); polyvinyl alcohol (PVA); cetyl alcohol, stearyl alcohol; cetostearyl alcohol (e.g., consisting predominantly of cetyl and stearyl alcohols); oleyl alcohol; polyoxyethylene glycol alkyl ethers (Brij); octaethylene glycol monododecyl ether; pentaethylene glycol monododecyl ether; polyoxypropylene glycol alkyl ethers; glucoside alkyl ethers; decyl glucoside; lauryl glucoside; octyl glucoside; polyoxyethylene glycol octylphenol ethers; triton X-100; polyoxyethylene glycol alkylphenol ethers; nonoxynol-9; glycerol alkyl esters; glyceryl laurate; polyoxyethylene glycol sorbitan alkyl esters; polysorbates; sorbitan alkyl esters; cocamide MEA; cocamide DEA; dodecyldimethylamine oxide; block copolymers of polyethylene glycol and polypropylene glycol; Poloxamers; or the like.
In some embodiments, the use of ionic surfactants is advantageous because the shells may be more stable, for example in applications where the particles are suspended in a saline environment (e.g., sea water) or other suitable vehicle. Not wishing to be bound by any particular theory, it is believed that the use of ionic surfactants in saline provides an osmotic balance between the fluid (or other contents) inside the shell, and the fluid outside the shell, and this osmotic balance helps to stabilize the shell.
The particles may be suspended in any suitable vehicle (e.g., vehicle 105 in
The particles described herein may have any suitable average cross-sectional diameter. Those of ordinary skill in the art will be able to determine the average cross-sectional diameter of a single particle and/or a plurality of particles, for example, using laser light scattering, microscopic examination, or other known techniques. The average cross-sectional diameter of a single particle, in a non-spherical particle, is the diameter of a perfect sphere having the same volume as the non-spherical particle. The average cross-sectional diameter of a particle (and/or of a plurality or series of particles) may be, for example, less than about 1 mm, less than about 500 micrometers, less than about 200 micrometers, less than about 100 micrometers, less than about 75 micrometers, less than about 50 micrometers, less than about 25 micrometers, less than about 10 micrometers, or less than about 5 micrometers, or between about 50 micrometers and about 1 mm, between about 10 micrometers and about 500 micrometers, or between about 50 micrometers and about 100 micrometers in some cases. The average cross-sectional diameter may also be at least about 1 micrometer, at least about 2 micrometers, at least about 3 micrometers, at least about 5 micrometers, at least about 10 micrometers, at least about 15 micrometers, or at least about 20 micrometers in certain cases. In some embodiments, at least about 50%, at least about 75%, at least about 90%, at least about 95%, or at least about 99% of the particles within a plurality of particles has an average cross-sectional diameter within any of the ranges outlined in this paragraph.
In some embodiments, the shell of the particle(s) are relatively thin. The use of thin shells can provide a number of advantages. For example, thin shells can dissolve relatively quickly in some cases. In some embodiments, this may allow a particle to deliver its contents prior to being transported away from the target medium. Another advantage of using particles with thin shells is that, during the process by which the outer liquid of a fluidic droplet is dried to form the shell of a particle, where the outer liquid contains a polymer that solidifies to form the shell, removal of the liquid can be performed relatively easily without rupturing the shell that is formed, at least according to certain embodiments. In some embodiments, when relatively thick shells are employed, the shells tend to rupture when the liquid in which the polymer is suspended is removed. Not wishing to be bound by any particular theory, it is believed that, when relatively thick shells are employed (e.g., shells with thicknesses greater than about 10 micrometers), the outermost portion of the shell dries more quickly than the innermost portion of the shell, producing a stress that can rupture or otherwise disrupt the shell. Without wishing to be bound by any theory, it is believed that using a middle phase with a very thin thickness allows the middle phase to act as a lubricant such that the fluids are within a lubrication regime. In this regime, the drag force on the innermost fluid is significantly increased. The increase in drag force is believed to enhance the stability of thin shell fluid. For example, the migration velocity of a 98-micrometer diameter inner droplet surrounded by a 100 micrometer shell is 100,000 times lower than the migration velocity of a 50-micrometer diameter inner droplet surrounded by a 100 micrometer shell.
In some embodiments, the shell of a particle has an average thickness (averaged over the entire particle) of less than about 0.05, less than about 0.01, less than about 0.005, or less than about 0.001 times the average cross-sectional diameter of the particle, or between about 0.0005 and about 0.05, between about 0.0005 and about 0.01, between about 0.0005 and about 0.005, or between about 0.0005 and about 0.001 times the average cross-sectional diameter of the particle. In some embodiments, the shell of a particle has an average thickness of less than about 1 micron, less than about 500 nm, or less than about 100 nm, or between about 50 nm and about 1 micron, between about 50 nm and about 500 nm, or between about 50 nm and about 100 nm. In some embodiments, at least about 50%, at least about 75%, at least about 90%, at least about 95%, or at least about 99% of the particles within a plurality of particles includes a shell having an average thickness within any of the ranges outlined in this paragraph. One of ordinary skill in the art would be capable of determining the average thickness of a shell by, for example, examining scanning electron microscope (SEM) images of the particles.
For many applications, it may be desirable to deliver a plurality of particles, at least some of which contain a fluid and/or an agent such as a surfactant, to a target medium. In order to ensure predictable agent delivery, some embodiments advantageously employ particles with relatively consistent properties. For example, in some embodiments, a plurality of particles are provided wherein the distribution of shell thicknesses among the plurality of particles is relatively uniform. The use of particles with relatively uniform shell thicknesses can ensure, in some cases, consistent shell dissolution times, making agent delivery more predictable. In some embodiments, a plurality of particles are provided having an overall average shell thickness, measured as the average of the average shell thicknesses of each of the plurality of particles. In some cases, the distribution of the average shell thicknesses can be such that no more than about 5%, no more than about 2%, or no more than about 1% of the particles have a shell with an average shell thickness thinner than 90% (or thinner than 95%, or thinner than 99%) of the overall average shell thickness and/or thicker than 110% (or thicker than 105%, or thicker than about 101%) of the overall average shell thickness.
The plurality of particles may have relatively uniform cross-sectional diameters in certain embodiments. The use of particles with relatively uniform cross-sectional diameters can allow one to control the viscosity of the particle suspension, the amount of agent delivered to the target medium, and/or other parameters of the delivery of fluid and/or agent from the particles. In some embodiments, the plurality of particles has an overall average diameter and a distribution of diameters such that no more than about 5%, no more than about 2%, or no more than about 1% of the particles have a diameter less than about 90% (or less than about 95%, or less than about 99%) and/or greater than about 110% (or greater than about 105%, or greater than about 101%) of the overall average diameter of the plurality of particles.
In some embodiments, the plurality of particles has an overall average diameter and a distribution of diameters such that the coefficient of variation of the cross-sectional diameters of the particles is less than about 10%, less than about 5%, less than about 2%, between about 1% and about 10%, between about 1% and about 5%, or between about 1% and about 2%. The coefficient of variation can be determined by those of ordinary skill in the art, and may be defined as:
wherein σ is the standard deviation and μ is the mean.
As used herein, two fluids are immiscible, or not miscible, with each other when one is not soluble in the other to a level of at least 10% by weight at the temperature and under the conditions at which the emulsion is produced. For instance, two fluids may be selected to be immiscible within the time frame of the formation of the fluidic droplets. In some embodiments, two fluids (e.g., the carrying fluid and the inner droplet fluid of a multiple emulsion) are compatible, or miscible, while the outer droplet fluid is incompatible or immiscible with one or both of the carrying and inner droplet fluids. In other embodiments, however, all three (or more) fluids may be mutually immiscible, and in certain cases, all of the fluids do not all necessarily have to be water soluble. In still other embodiments, as mentioned, additional fourth, fifth, sixth, etc. fluids may be added to produce increasingly complex droplets within droplets, e.g., a carrying fluid may surround a first fluid, which may in turn surround a second fluid, which may in turn surround a third fluid, which in turn surround a fourth fluid, etc. In addition, the physical properties of each nesting layer of fluidic droplets may each be independently controlled, e.g., by control over the composition of each nesting level.
As used herein, the term “fluid” generally refers to a substance that tends to flow and to conform to the outline of its container, i.e., a liquid, a gas, a viscoelastic fluid, etc. Typically, fluids are materials that are unable to withstand a static shear stress, and when a shear stress is applied, the fluid experiences a continuing and permanent distortion. The fluid may have any suitable viscosity that permits flow. If two or more fluids are present, each fluid may be independently selected among essentially any fluids (liquids, gases, and the like) by those of ordinary skill in the art, by considering the relationship between the fluids.
In an aspect of the present invention, as discussed, multiple emulsions are formed by flowing fluids through one or more conduits. The system may be a microfluidic system. “Microfluidic,” as used herein, refers to a device, apparatus, or system including at least one fluid channel having a cross-sectional dimension of less than about 1 millimeter (mm), and in some cases, a ratio of length to largest cross-sectional dimension of at least 3:1. One or more conduits of the system may be a capillary tube. In some cases, multiple conduits are provided, and in some embodiments, at least some are nested, as described herein. The conduits may be in the microfluidic size range and may have, for example, average inner diameters, or portions having an inner diameter, of less than about 1 millimeter, less than about 300 micrometers, less than about 100 micrometers, less than about 30 micrometers, less than about 10 micrometers, less than about 3 micrometers, or less than about 1 micrometer, thereby providing droplets having comparable average diameters. One or more of the conduits may (but not necessarily), in cross-section, have a height that is substantially the same as a width at the same point. A conduit may include an opening that may be smaller, larger, or the same size as the average diameter of the conduit. For example, conduit openings may have diameters of less than about 1 mm, less than about 500 micrometers, less than about 300 micrometers, less than about 200 micrometers, less than about 100 micrometers, less than about 50 micrometers, less than about 30 micrometers, less than about 20 micrometers, less than about 10 micrometers, less than about 3 micrometers, etc. In cross-section, the conduits may be rectangular or substantially non-rectangular, such as circular or elliptical. The conduits of the present invention may also be disposed in or nested in another conduit, and multiple nestings are possible in some cases. In some embodiments, one conduit may be concentrically retained in another conduit and the two conduits are considered to be concentric. However, one concentric conduit may be positioned off-center with respect to another, surrounding conduit, i.e., “concentric” does not necessarily refer to tubes that are strictly coaxial. By using a concentric or nesting geometry, two fluids that are miscible may avoid contact.
In some embodiments, fluids, conduits (including conduit walls), and other materials may be referred to as hydrophobic or hydrophilic. A material is “hydrophobic” when a droplet of water forms a contact angle greater than 90° when placed in intimate contact with the material in question in air at 1 atm and 25° C. A material is “hydrophilic” when a droplet of water forms a contact angle of less than 90° when placed in intimate contact with the material in question in air at 1 atm and 25° C. The “contact angle,” in the context of hydrophobicity and hydrophilicity is the angle measured between the surface of the material and a line tangent to the external surface of the water droplet at the point of contact with the material surface, and is measured through the water droplet.
A variety of materials and methods, according to certain aspects of the invention, may be used to form systems (such as those described above) configured to produce the multiple emulsions and/or particles described herein. In some cases, the various materials selected lend themselves to various methods. For example, various components of the invention are configured from solid materials, in which the conduits are configured via micromachining, film deposition processes such as spin coating and chemical vapor deposition, laser fabrication, photolithographic techniques, etching methods including wet chemical or plasma processes, and the like. See, for example, Scientific American, 248:44-55, 1983 (Angell, et al). In one embodiment, at least a portion of the fluidic system is formed of silicon by etching features in a silicon chip. Technologies for precise and efficient fabrication of various fluidic systems and devices of the invention from silicon are known. In another embodiment, various components of the systems and devices of the invention are configured of a polymer, for example, an elastomeric polymer such as polydimethylsiloxane (“PDMS”), polytetrafluoroethylene (“PTFE” or Teflon®), or the like.
Different components can be fabricated of different materials. For example, a base portion including a bottom wall and side walls can be fabricated from an opaque material such as silicon or PDMS, and a top portion can be fabricated from a transparent or at least partially transparent material, such as glass or a transparent polymer, for observation and/or control of the fluidic process. Components can be coated so as to expose a desired chemical functionality to fluids that contact interior conduit walls, where the base supporting material does not have a precise, desired functionality. For example, components can be fabricated as illustrated, with interior conduit walls coated with another material. Material used to fabricate various components of the systems and devices of the invention, e.g., materials used to coat interior walls of fluid conduits, may desirably be selected from among those materials that will not adversely affect or be affected by fluid flowing through the fluidic system, e.g., material(s) that is chemically inert in the presence of fluids to be used within the device. A non-limiting example of such a coating is disclosed below; additional examples are disclosed in Int. Pat. Apl. Ser. No. PCT/US2009/000850, filed Feb. 11, 2009, entitled “Surfaces, Including Microfluidic Channels, With Controlled Wetting Properties,” by Weitz, et al., published as WO 2009/120254 on Oct. 1, 2009, incorporated herein by reference.
In some embodiments, various components of the invention are fabricated from polymeric and/or flexible and/or elastomeric materials, and can be conveniently formed of a hardenable fluid, facilitating fabrication via molding (e.g. replica molding, injection molding, cast molding, etc.). The hardenable fluid may be essentially any fluid that can be induced to solidify, or that spontaneously solidifies, into a solid capable of containing and/or transporting fluids contemplated for use in and with the fluidic network. In some embodiments, the hardenable fluid comprises a polymeric liquid or a liquid polymeric precursor (i.e. a “prepolymer”). Suitable polymeric liquids include, for example, thermoplastic polymers, thermoset polymers, or mixture of such polymers heated above their melting point. As another example, a suitable polymeric liquid may include a solution of one or more polymers in a suitable solvent, which solution forms a solid polymeric material upon removal of the solvent, for example, by evaporation. Such polymeric materials, which can be solidified from, for example, a melt state or by solvent evaporation, are well known to those of ordinary skill in the art. A variety of polymeric materials, many of which are elastomeric, are suitable, and are also suitable for forming molds or mold masters, for embodiments where one or both of the mold masters is composed of an elastomeric material. A non-limiting list of examples of such polymers includes polymers of the general classes of silicone polymers, epoxy polymers, and acrylate polymers. Epoxy polymers are characterized by the presence of a three-membered cyclic ether group commonly referred to as an epoxy group, 1,2-epoxide, or oxirane. For example, diglycidyl ethers of bisphenol A can be used, in addition to compounds based on aromatic amine, triazine, and cycloaliphatic backbones. Another example includes the well-known Novolac polymers. Non-limiting examples of silicone elastomers suitable for use according to the invention include those formed from precursors including the chlorosilanes such as methylchlorosilanes, ethylchlorosilanes, phenylchlorosilanes, etc.
Silicone polymers are utilized in some embodiments, for example, the silicone elastomer polydimethylsiloxane. Non-limiting examples of PDMS polymers include those sold under the trademark Sylgard by Dow Chemical Co., Midland, Mich., and particularly Sylgard 182, Sylgard 184, and Sylgard 186. Silicone polymers including PDMS have several beneficial properties simplifying fabrication of the microfluidic structures of the invention. For instance, such materials are inexpensive, readily available, and can be solidified from a prepolymeric liquid via curing with heat. For example, PDMSs are typically curable by exposure of the prepolymeric liquid to temperatures of about, for example, about 65° C. to about 75° C. for exposure times of, for example, about an hour. Also, silicone polymers, such as PDMS, can be elastomeric, and thus may be useful for forming very small features with relatively high aspect ratios, necessary in certain embodiments of the invention. Flexible (e.g., elastomeric) molds or masters can be advantageous in this regard.
An advantage of forming structures such as microfluidic structures of the invention from silicone polymers, such as PDMS, is the ability of such polymers to be oxidized, for example by exposure to an oxygen-containing plasma such as an air plasma, so that the oxidized structures contain, at their surface, chemical groups capable of cross-linking to other oxidized silicone polymer surfaces or to the oxidized surfaces of a variety of other polymeric and non-polymeric materials. Thus, components can be fabricated and then oxidized and essentially irreversibly sealed to other silicone polymer surfaces, or to the surfaces of other substrates reactive with the oxidized silicone polymer surfaces, without the need for separate adhesives or other sealing means. In most cases, sealing can be completed simply by contacting an oxidized silicone surface to another surface without the need to apply auxiliary pressure to form the seal. That is, the pre-oxidized silicone surface acts as a contact adhesive against suitable mating surfaces. Specifically, in addition to being irreversibly sealable to itself, oxidized silicone such as oxidized PDMS can also be sealed irreversibly to a range of oxidized materials other than itself including, for example, glass, silicon, silicon oxide, quartz, silicon nitride, polyethylene, polystyrene, glassy carbon, and epoxy polymers, which have been oxidized in a similar fashion to the PDMS surface (for example, via exposure to an oxygen-containing plasma). Oxidation and sealing methods useful in the context of the present invention, as well as overall molding techniques, are described in the art, for example, in an article entitled “Rapid Prototyping of Microfluidic Systems and Polydimethylsiloxane,” Anal. Chem., 70:474-480, 1998 (Duffy et al.), incorporated herein by reference.
In some embodiments, certain microfluidic structures of the invention (or interior, fluid-contacting surfaces) may be formed from certain oxidized silicone polymers. Such surfaces may be more hydrophilic than the surface of an elastomeric polymer. Such hydrophilic conduit surfaces can thus be more easily filled and wetted with aqueous solutions.
In some embodiments, a bottom wall of a microfluidic device of the invention is formed of a material different from one or more side walls or a top wall, or other components. For example, in some embodiments, the interior surface of a bottom wall comprises the surface of a silicon wafer or microchip, or other substrate. Other components may, as described above, be sealed to such alternative substrates. Where it is desired to seal a component comprising a silicone polymer (e.g. PDMS) to a substrate (bottom wall) of different material, the substrate may be selected from the group of materials to which oxidized silicone polymer is able to irreversibly seal (e.g., glass, silicon, silicon oxide, quartz, silicon nitride, polyethylene, polystyrene, epoxy polymers, and glassy carbon surfaces which have been oxidized). Alternatively, other sealing techniques may be used, as would be apparent to those of ordinary skill in the art, including, but not limited to, the use of separate adhesives, bonding, solvent bonding, ultrasonic welding, etc.
The following documents are incorporated herein by reference in their entirety for all purposes: International Patent Publication Number WO 2004/091763, filed Apr. 9, 2004, entitled “Formation and Control of Fluidic Species,” by Link et al.; International Patent Publication Number WO 2004/002627, filed Jun. 3, 2003, entitled “Method and Apparatus for Fluid Dispersion,” by Stone et al.; International Patent Publication Number WO 2006/096571, filed Mar. 3, 2006, entitled “Method and Apparatus for Forming Multiple Emulsions,” by Weitz et al.; International Patent Publication Number WO 2005/021151, filed Aug. 27, 2004, entitled “Electronic Control of Fluidic Species,” by Link et al.; International Patent Publication Number WO 2008/121342, filed Mar. 28, 2008, entitled “Emulsions and Techniques for Formation,” by Chu et al.; International Patent Publication Number WO 2010/104604, filed Mar. 12, 2010, entitled “Method for the Controlled Creation of Emulsions, Including Multiple Emulsions,” by Weitz et al.; International Patent Publication Number WO 2011/028760, filed Sep. 1, 2010, entitled “Multiple Emulsions Created Using Junctions,” by Weitz et al.; International Patent Publication Number WO 2011/028764, filed Sep. 1, 2010, entitled “Multiple Emulsions Created Using Jetting and Other Techniques,” by Weitz et al; and a U.S. Provisional Patent Application, filed on Jul. 6, 2011, entitled “Delivery to Hydrocarbons or Oil, Including Crude Oil,” by Abbaspourrad et al. Also incorporated herein by reference in their entireties are U.S. Provisional Patent Application Ser. No. 61/505,001, filed Jul. 6, 2011, entitled “Delivery to Hydrocarbons or Oil, Including Crude Oil,” by Abbaspourrad, et al., and of U.S. Provisional Patent Application Ser. No. 61/504,990, filed Jul. 6, 2011, entitled “Multiple Emulsions and Techniques for the Formation of Multiple Emulsions,” by Kim, et al.
All other patents, patent applications, and documents cited herein are also hereby incorporated by reference in their entirety for all purposes.
The following examples are intended to illustrate certain embodiments of the present invention, but do not exemplify the full scope of the invention.
This example describes an approach to making relatively monodisperse double emulsion droplets including a thin middle layer of fluid, using microfluidic techniques. Two immiscible streams confined in a microfluidic channel can form a stable jet or droplets under certain physical conditions, and the streams can be emulsified together to form double emulsion droplets, as discussed herein. The resultant double emulsion droplets have a thin outer layer which can enhance the stability of the double emulsion. The systems and methods described in this example can be applied to any viscous organic solvent, and in some embodiments, can facilitate the making of particles having a shell containing material, with a small amount of shell material. In addition, the systems and methods described in this example can produce double emulsions, or higher-order multiple emulsions, in a single step, at least in some cases. Relatively monodisperse particles with a shell thicknesses of less than 100 nm may be formed in some instances by evaporation of an outer phase (such as toluene) to leave behind a polymer (such as poly(lactic acid)) that solidifies to form the shell.
Two immiscible fluids flowing through a single microfluidic channel can show different distinct flow patterns of droplets and jets, depending upon several physical parameters. The fluid with the higher affinity to the walls of the microfluidic channel may form a continuous phase, while the fluid with the lower affinity may flow in the form of droplets or jets without contacting the walls of the channel. In many instances, the flow may produce a jet that is unstable due to Rayleigh-Plateau instability, which results in the breakup of the jet into separate droplets; however, spatial confinement of the interface may be used to produce a more stable jet. When the interface is formed proximate to a channel wall, the instability may be reduced in some cases.
In some experiments in this example, double emulsion droplets were produced through emulsification of a stable biphasic jet into a continuous phase. To make water-in-oil-in-water (W/O/W) double emulsion droplets, microfluidic devices were employed.
In these experiments, 25 wt % aqueous solution of poly(ethylene glycol) (PEG, MW 6000) and hexadecane (“oil” phase 602) with 1 wt % SPAN 80 was passed through the injection channel to form a dispersed phase of droplets, and 10 wt % aqueous solution of poly(vinyl alcohol) (PVA, MW 13,000-23,000) (“water” phase 606) was passed through channel 612 to form a continuous phase. It should be noted that the “oil” phase is used here to conveniently refer to a phase that is not substantially miscible in water or the “aqueous” phase (which is miscible in water). The “oil” phase should not be construed as being limited only to oils, and may include any fluid that is not substantially miscible in water.
Depending on the inner diameter of the injection channel that was used in the microfluidic device, different resulting flow patterns were observed. For example, in an injection channel with an inner diameter of 580 micrometers, a variety of water droplet formations for a wide range of flow rates were observed. As a specific non-limiting example, when the ratio of the volumetric flow rate of the inner fluid stream to the volumetric flow rate of the outer fluid was set at 4:1, a “train” of plug-like or elongated droplets was observed, as shown in the optical microscope image in
As another non-limiting example, when an injection channel with an inner diameter of 200 micrometers was used, a stable water jet was formed under these particular conditions, as shown in the optical microscope image in
The flow rates of the entering streams influenced the flow pattern in the injection channel and thus, the generation of double emulsion droplets.
Although a high flow rate of the inner stream could produce a stable jet, a double emulsion was not always generated from the jet. High inertia of the inner stream at a high flow rate can cause leakage of the inner stream into the continuous phase near the tip of the injection channel, which corresponds to region (a) in
O/W/O double emulsion droplets may be prepared in a similar manner. To produce O/W/O double emulsion droplets, 2-[methoxy(polyethyleneoxy)propyl]trimethoxyl silane (Gelest, Inc.) was coated onto the injection capillary wall to render it hydrophilic, and n-octadecyltrimethoxyl silane (Aldrich) was coated onto the collection capillary wall to render it hydrophobic. Using a microfluidic device with the same geometry but opposite surface modifications, double emulsion droplets of silicone oil (AR 20)/1 wt % aqueous solution of F108/2 wt % silicone oil of DC749 were prepared, as illustrated in
When operating in the dripping mode, droplet generation appeared to be governed by two competing forces: the capillary force that holds the droplet to the end of the channel and the drag force that pulls the droplet downstream. The size of double emulsion droplets may be controlled, for example, by controlling the flow rate of the continuous phase (which is proportional to the drag force).
The thickness, t, of the outer layer of the double emulsion droplets was difficult to accurately measure from optical microscope images. However, the thicknesses of the outer layer could also be estimated by comparing the radius of the double emulsion droplet (R) to the radius of a single “oil” droplet (Rrup) prepared by rupturing the double emulsion droplet such that the inner “water” phase is transported out of the “oil” shell and into the continuous “water” phase, leaving behind an “oil” droplet. The thickness of the “oil” shell prior to rupturing can be calculated using the following mass balance equation, noting that the volume of the initial “oil” shell (the left-hand side of Equation 2) will be equivalent to the volume of the “oil” droplet formed after rupturing the double emulsion (the right-hand side of Equation 2):
Rearranging Equation 2 to calculate the shell thickness yields:
t=R−(R3−Rrup3)1/3 [3]
As an example, two optical microscope images are shown in
In the same manner, using various double emulsion droplets produced at various relative flow rates of inner stream 604 (Q1) to outer stream 602 (Q2), the thicknesses of the outer layers of these double emulsion droplets were calculated (see
where f is frequency of drop generation. By dividing Equation 5 by Equation 4, and rearranging, the following equation can be obtained:
By contrast, the discontinuous dripping mode produced double emulsion droplets including outer fluid layers with very small relative thicknesses, regardless of the flow rates. Not wishing to be bound by any particular theory, this regime may have formed consistently thin outer fluid layers because the amount of the oil phase positioned between the plug-like water droplets and the inner wall of the injection channel (which eventually formed the outer layer of the double emulsion droplets) was very small. In fact, in this flow regime, most of the injected oil was situated between the plug-like water droplets, producing relatively large oil plugs contained between the water droplets that eventually formed the cores of the double-emulsion droplets. Because very little oil was positioned adjacent the water droplets, little oil was available to produce the outer layers, and the outer layers were very thin. Most of the injected oil flow was between two neighboring water droplets, forming large oil droplets at the exit opening rather than double emulsion droplets. Although the discontinuous dripping mode produced both relatively monodisperse double emulsion droplets with a thin outer fluid layer, as well as large oil (single-emulsion) droplets, separation of the double emulsion droplets from the mixture was easily achieved by taking advantage of the density difference between the the double emulsion droplets and the single emulsion droplets: the average density of the double emulsion droplets was almost same as the density of the aqueous inner fluid, while the density of the single emulsion oil droplets was almost the same as the density of the oil solution surrounding the droplets. Thus, the two types of droplets could readily be separated based on their density differences.
Double emulsion droplets were used to make microcapsules by removing fluid from the outer phase to produce a solid phase from material that was originally contained within the fluid of the outer phase. As a specific example, in some cases, a concentrated organic solution of polymers with high molecular weights in water was used as the outer phase. Double emulsion droplets containing a relatively thin outer fluid layer were produced, and this relatively thin outer fluid layer was solidified to form a shell that provided stability to the resulting particles. These particles could maintain their respective solidified shells around the contained inner fluid without being disrupted for relatively long times.
To illustrate some of the advantages discussed herein, polymeric particles having a shell containing a fluid were prepared, in which the shell was formed from poly(lactic acid) (PLA, MW 15,000). To produce W/O/W double emulsion droplets, a 10 wt % aqueous solution of PVA containing a green dye, 8-hydroxyl-1,3,6-pyrenetrisulfonic acid, trisodium salt, was used for the inner phase. 20 wt % of PLA in toluene containing a red dye, nile red, was used for the outer phase. A 3 wt % aqueous solution of PVA was employed for the carrying fluid. Approximately 1,000 double emulsion droplets were generated each second in the dripping mode. The resultant droplets, illustrated in the optical microscope images in
To remove toluene from the outer fluid layer, the suspension was exposed to a temperature of 65° C. for 2 hours. During this process, the toluene diffused from the outer phase to the PVA carrying fluid, from which the toluene was subsequently evaporated at 65° C. After the consolidation step, polymeric particles were produced, as shown in the confocal microscope images of
Higher-order multiple emulsion droplets were produced through a single-step emulsification process using a stable coaxial flow in a confining microfluidic channel. The device configuration used for producing triple emulsion droplets of water-in-oil-in-water-in-oil (W1/O2/W3/O4) is illustrated schematically in
In this example, inner surface of channel 706 has a hydrophilic surface, while the outer surfaces of channels 702 and 704 (facing channel 706) are hydrophobic. 2-[methoxy(polyethyleneoxy)propyl]trimethoxyl silane (Gelest, Inc.) was used to make the walls of channel 706 hydrophilic, while n-octadecyltrimethoxyl silane (Aldrich) was used to make the walls of channels 702 and 704 hydrophobic. To prepare triple emulsion droplets, water was used for the innermost phase 710, hexadecane with 1 wt % SPAN 80 surfactant was used for oil phase 712 (i.e., for the first, “oil” shell), an aqueous solution of 3 wt % poly (vinyl alcohol) (PVA) and 1 wt % F108 surfactant was used for water phase 714 (i.e., for the second, “water” shell), and hexadecane with 1 wt % SPAN 80 was used as continuous phase 716. When both water 714 and oil 716 were introduced from the right side of channel 706, between collection channel 704 and channel 706, oil passed along the outer surface of collection channel 704 with water 714 shielding oil 716, as shown in the cross-section of B-B′. In this arrangement, the fluids formed coaxial interfaces in the opening of collection channel 704, which facilitated the formation of triple emulsion droplets in a single step emulsification process.
For the preparation of triple emulsion droplets, water (W1) and hexadecane with 1 wt % SPAN 80 surfactant (O2) were passed through injection channel 702 and the channel between injection channel 702 and channel 706, respectively, while both an aqueous solution of 3 wt % poly(vinyl alcohol) (PVA) and 1 wt % F108 surfactant (W3) and hexadecane with 1 wt % SPAN 80 (O4) were passed through the channel between collection channel 704 and square channel 706. The aqueous (W3) and the hexadecane surfactant solutions (O4) formed a coaxial interface, and were passed into the opening of collection channel 704, together with the water (W1) and the hexadecane (O2) from the left side. Using this arrangement, triple emulsion droplets of W1/O2/W3/O4 were prepared in collection channel 704. The triple emulsion droplets are displayed in the optical microscope images of
In this arrangement, the flow rate of the aqueous inner phase (Q1) determined the sizes of the triple emulsion droplets.
where Q2 and Q3 are volumetric flow rates of O2 and W3, respectively. The calculated diameter of D3 appeared to be consistent with the experimentally measured diameters.
For larger values of Q2, the droplet breakup mechanism changed from core drop-triggering to jetting. The coaxial interfaces formed a long jet, and plug-like droplets containing any desirable number of core droplets could be produced, as illustrated in the optical microscope image of
Substantially monodisperse quadruple emulsion droplets were also prepared using a single-step emulsification process. The device used to produce quadruple emulsion droplets was similar to the device used to produce triple emulsion droplets, and is illustrated schematically in
Inverse quadruple emulsion droplets with an O/W/O/W/O arrangement were also produced using a device with the same geometry as the device used to produce W/O/W/O/W emulsions, but with the opposite chemical modifications, as illustrated schematically in
This example describes the use of certain microfluidic techniques to make polymer particles comprising shells with nano-scale thicknesses. The polymer shell was designed such that it remained solid during transit and liquefied upon contact with a suitable target medium, such as hydrocarbons or oil (e.g., any aromatic or short chain hydrocarbon oil, or other oil as discussed herein), locally transporting a fluid and/or an agent contained within the particle to the oil (or other target medium). Release of the contents of the particles was triggered when the solid polymer shell was exposed to the oil, after which the shell became disrupted. For example, at least a portion of the shell may liquefy and/or behave like a viscoelastic fluid, exposing the fluid and/or agent within the particle to the target medium. The liquefied shell of the particle may shrink rapidly in some embodiments, expelling or otherwise transporting the fluid and/or agent out of the particle, into the oil. Not wishing to be bound by any particular theory, it is believed that the shell of the particle shrinks in some cases in order to decrease the interfacial area and/or the surface energy of the particle. The time required for the particle to expose the agent and/or fluid to the target medium (e.g., by expelling the fluid and/or agent from the particle) may be tuned, for instance, by varying the molecular weight of the polymer. This may also be adjusted depending on the composition of the oil or other target medium. This method of triggered release may be used for a variety of different applications, for example, for reservoir applications such as enhanced oil recovery (EOR), or other applications such as those described herein.
A double emulsion template using microfluidic devices (generally described in Example 1) was used to contain one or more agents within shells having thicknesses ranging from, e.g., about 100 nm to about 1 micrometer. The microfluidic devices allowed for the control of particle properties, for example, mechanical stability, release, and/or loading efficiencies in various embodiments. The microfluidic devices also allowed for easy fabrication, e.g., for the production of particles having desirable properties and/or for tailoring the properties of the particles for use in various applications.
In this example, the carrying fluid was prepared by dissolving 10 g PVA (MW=13000-23000, Aldrich) in 90 mL of water. The outer fluid was formed using a solution of 8 wt % linear polystyrene (MW=20000-800000, Aldrich) and 0.01 g of Nile Red (fluorescent dye, Sigma) dissolved in toluene. The inner or core fluid was prepared by dissolving 1 g of PVA (MW=13000-23000, Aldrich) in 9 mL of water. To visualize the core via confocal microscopy, 0.05 g Dex-FITC (Polysciences) was added to the inner fluid solution. All fluids were pumped into the microfluidic device using syringe pumps (Harvard PHD 2000 series). Flow rates for the continuous, middle and the core fluids were set at 300, 500, and 20,000 microliters/h, respectively. In
The outer fluid was solidified to form shells by evaporating the solvent (toluene) inside the outer fluid away from the droplets using a heat treatment process (65° C. for 2 hours) to form a shell comprising the solid linear polymer.
The ability to produce thin particle shells offers several advantages. For example, the thin shell was found to be robust, and could contain a wide range of materials without failing mechanically, while the shell was still able to be disrupted upon contact with even small concentrations or amounts of oils or hydrocarbons (or other suitable target medium).
In this example, the microfluidic fabrication process was monitored using an inverted optical microscope (DM-IRB, Leica) fit with a fast camera (Phantom V9, Vision Research). Confocal images of the particles were obtained using a scanning confocal microscope (Leica TCS-SP5).
This example describes the production of particles comprising thin polymeric shells that were configured to controllably release their contents. In this example, the carrying fluid was prepared by dissolving 10 g PVA (weight-averaged MW=52500-23000; Aldrich) in 90 mL of water. The outer fluid was formed using a solution of 8 wt % linear polystyrene (MW=20,000-800,000, Aldrich) and 0.01 g of Nile Red (fluorescent dye, Sigma) dissolved in toluene. The inner or core fluid was prepared by dispersing 0.1 g of fluorescently labeled magnetic poly styrene particles (Polyscience, size=1 micrometers) in 5 mL of water. All fluids were pumped into the microfluidic device using syringe pumps (Harvard PHD 2000 series). Flow rates for the core, middle, and continuous fluids were set at 650, 400 and 12,000 microliters/h, respectively.
Controlled release of fluids or agents contained within the particles may be achieved by first contacting the shells of the particles with an oil, after which, in some cases, the shell absorbs the oil and becomes more fluid or otherwise disrupted. This solid to fluid-like transition created a shell defect, which initiated shell collapse and subsequent release of agent contained within the shell.
In another set of experiments, additional particles were formed that comprised a triblock copolymer (PS-PIP-PS) inside a shell. These particles exhibited a similar release mechanism as the one discussed above. The shells of these particles comprising the PS-PIP-PS triblock copolymer were relatively flexible, which allowed the particles to be passed through confined geometries smaller than the particle diameter without disruption or release of agents contained within the particles.
The polymer shell in these examples may be formed using a variety of polymers including polystyrene (PS), polycaprolactone (PCL), and/or a variety of other polymers. As an example, by incorporating PCL in the shell of particle, controlled release of a fluid and/or an agent contained within the particle may be made dependent upon the pH of the environment, e.g., of the target medium. The use of pH-dependent materials in the shell could also be useful in applications such as targeted drug delivery. As an example, targeted delivery of magnetic particles (useful, for example, for identification of residual oil in place (ROIP) by NMR sensing) may also be achieved. Examples of magnetic particles that may be used include iron oxide, magnetite, hematite, other compounds containing iron, or the like.
For all experiments in this example, the microfluidic fabrication process was monitored using an inverted optical microscope (DM-IRB, Leica) fit with a fast camera (Phantom V9, Vision Research). Brightfield images of dried particles were taken with an inverted optical microscope (DM-IRB, Leica) equipped with a camera (QImaging QICAM). Confocal images of the particles were obtained using a scanning confocal microscope (Leica TCS-SP5). SEM (scanning electron microscopy) images were collected with a Zeiss Ultra55 field emission microscope (FESEM) (field emission scanning electron microscopy).
While several embodiments of the present invention have been described and illustrated herein, those of ordinary skill in the art will readily envision a variety of other means and/or structures for performing the functions and/or obtaining the results and/or one or more of the advantages described herein, and each of such variations and/or modifications is deemed to be within the scope of the present invention. More generally, those skilled in the art will readily appreciate that all parameters, dimensions, materials, and configurations described herein are meant to be exemplary and that the actual parameters, dimensions, materials, and/or configurations will depend upon the specific application or applications for which the teachings of the present invention is/are used. It is, therefore, to be understood that the foregoing embodiments are presented by way of example only and that, within the scope of the appended claims and equivalents thereto, the invention may be practiced otherwise than as specifically described and claimed. The present invention is directed to each individual feature, system, article, material, kit, and/or method described herein. In addition, any combination of two or more such features, systems, articles, materials, kits, and/or methods, if such features, systems, articles, materials, kits, and/or methods are not mutually inconsistent, is included within the scope of the present invention.
The indefinite articles “a” and “an,” as used herein in the specification and in the claims, unless clearly indicated to the contrary, should be understood to mean “at least one.”
The phrase “and/or,” as used herein in the specification and in the claims, should be understood to mean “either or both” of the elements so conjoined, i.e., elements that are conjunctively present in some cases and disjunctively present in other cases. Other elements may optionally be present other than the elements specifically identified by the “and/or” clause, whether related or unrelated to those elements specifically identified unless clearly indicated to the contrary. Thus, as a non-limiting example, a reference to “A and/or B,” when used in conjunction with open-ended language such as “comprising” can refer, in one embodiment, to A without B (optionally including elements other than B); in another embodiment, to B without A (optionally including elements other than A); in yet another embodiment, to both A and B (optionally including other elements); etc.
As used herein in the specification and in the claims, “or” should be understood to have the same meaning as “and/or” as defined above. For example, when separating items in a list, “or” or “and/or” shall be interpreted as being inclusive, i.e., the inclusion of at least one, but also including more than one, of a number or list of elements, and, optionally, additional unlisted items. Only terms clearly indicated to the contrary, such as “only one of” or “exactly one of,” or, when used in the claims, “consisting of,” will refer to the inclusion of exactly one element of a number or list of elements. In general, the term “or” as used herein shall only be interpreted as indicating exclusive alternatives (i.e. “one or the other but not both”) when preceded by terms of exclusivity, such as “either,” “one of,” “only one of,” or “exactly one of.” “Consisting essentially of,” when used in the claims, shall have its ordinary meaning as used in the field of patent law.
As used herein in the specification and in the claims, the phrase “at least one,” in reference to a list of one or more elements, should be understood to mean at least one element selected from any one or more of the elements in the list of elements, but not necessarily including at least one of each and every element specifically listed within the list of elements and not excluding any combinations of elements in the list of elements. This definition also allows that elements may optionally be present other than the elements specifically identified within the list of elements to which the phrase “at least one” refers, whether related or unrelated to those elements specifically identified. Thus, as a non-limiting example, “at least one of A and B” (or, equivalently, “at least one of A or B,” or, equivalently “at least one of A and/or B”) can refer, in one embodiment, to at least one, optionally including more than one, A, with no B present (and optionally including elements other than B); in another embodiment, to at least one, optionally including more than one, B, with no A present (and optionally including elements other than A); in yet another embodiment, to at least one, optionally including more than one, A, and at least one, optionally including more than one, B (and optionally including other elements); etc.
In the claims, as well as in the specification above, all transitional phrases such as “comprising,” “including,” “carrying,” “having,” “containing,” “involving,” “holding,” and the like are to be understood to be open-ended, i.e., to mean including but not limited to. Only the transitional phrases “consisting of” and “consisting essentially of” shall be closed or semi-closed transitional phrases, respectively, as set forth in the United States Patent Office Manual of Patent Examining Procedures, Section 2111.03.
This application claims the benefit of U.S. Provisional Patent Application Ser. No. 61/505,001, filed Jul. 6, 2011, and of U.S. Provisional Patent Application Ser. No. 61/504,990, filed Jul. 6, 2011, each of which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61505001 | Jul 2011 | US | |
| 61504990 | Jul 2011 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14130531 | Apr 2014 | US |
| Child | 15235423 | US |