Claims
- 1. Multilayer heat barrier system having:
- a transparent substrate;
- a transparent metal layer;
- at least one transparent layer applied to the side of the metal layer remote from the substrate, constituting an outer dielectric cover layer, said at least one layer comprising a mixture of (1) at least one compound selected from the group consisting of the oxides of titanium, silicon, tantalum and zirconium, zinc sulfide (2) at least one nitrogen compound having the same metal ion as said oxide or sulfide.
- 2. System according to claim 1, wherein at least one transparent cover layer is interposed between said transparent substrate and said transparent metal layer, constituting an intermediate dielectric coating, said at least one layer of said intermediate dielectric coating comprising at least one compound selected from the group consisting of the oxides of titanium, silicon, tantalum and zirconium and zinc sulfide and a nitrogen compound having the same metal ion as said oxide or sulfide.
- 3. System according to claim 2, in which said at least one transparent cover layer of said outer dielectric coating and also said at least one layer of said intermediate dielectric coating both comprise a mixture of titanium dioxide and titanium nitride.
- 4. System according to claim 3, wherein each of said intermediate and outer coatings each comprises oxygen and nitrogen compounds of titanium, having a titanium content of between about 60 and 70% by weight, a nitrogen content of between about 2 and 20% by weight and an oxygen content of between about 10 and 40% by weight.
- 5. System according to claim 3, wherein each of said intermediate and outer coatings comprises oxygen and nitrogen compounds of titanium, having a titanium content of about 65% by weight, a nitrogen content of about 13%, and an oxygen content of about 22%.
- 6. System according to claim 3, wherein an anti-reflection layer having an index of refraction which is less than the index of refraction of the substrate is applied on the side of the substrate opposed to the side of the substrate on which said transparent metal layer and said at least one transparent dielectric cover layer are applied.
- 7. System according to claim 2, in which said at least one transparent cover layer of said outer dielectric coating and also said at least one layer of said intermediate dielectric coating both comprise a mixture of titanium oxide, titanium nitride and titanium oxynitride.
- 8. System according to claim 2, further comprising a dielectric layer applied to the substrate remote from said metal layer.
- 9. System according to claim 8, wherein said further dielectric layer comprises a .lambda./4 magnesium fluoride layer having a thickness of about 0.09 .mu.m.
- 10. System according to claim 1 or 2, wherein said at least one transparent metal layer is a layer of at least one metal from the group consisting of silver, gold, aluminum and copper.
- 11. System according to claim 10 in which an additional dielectric layer, other than said corrosions protective layer, is interposed between said substrate and said metallic layer, said additional dielectric layer being of oxide and nitride of a metal selected from the group consisting of titanium, tantalum and zirconium and having a thickness dimensioned for maximizing visible light transmission through said system.
- 12. System according to claim 1, in which said at least one transparent cover layer comprises a mixture of titanium oxide, titanium nitride and titanium oxynitride.
- 13. System according to claim 1, in which the thickness of said dielectric outer coating is such as to reduce reflection of visible light through the combination of said dielectric outer coating and said transparent metal layer.
- 14. System according to claim 13, in which the thickness of said intermediate dielectric coating is such that to optimize transmission of visible light through the system.
- 15. System according to claim 13, in which the thickness of said outer dielectric coating is between 3 and 50 nanometers thick.
- 16. System according to claim 14, in which said intermediate dielectric coating is between 3 and 50 nanometers thick.
- 17. System according to claim 1, in which said at least one transparent cover layer comprises a mixture of titanium dioxide and titanium nitride.
- 18. Multilayer heat barrier systems, having high reflectivity in the far infrared spectral region and high transmissivity within a visible spectral region and in the near infrared spectral region comprising
- a transparent substrate;
- a metallic layer of silver, gold, aluminum, or copper, and at least one transparent dielectric layer applied to the metallic layer said dielectric layer being of oxide and nitride of a metal selected from the group consisting of titanium, tantalum and zirconium and having a thickness and an index of refraction suitable for minimizing reflection of visible light and thereby improving visible light transmission; and
- a corrosion protective layer of magnesium fluoride positioned between the substrate and the dielectric cover layer.
- 19. System according to claim 18, wherein at least one further layer of a metal oxide or metal sulfide, selected from the group consisting of titanium, oxide, tin oxide, bismuth oxide, indium oxide, tantalum oxide and zinc oxide, is applied on said dielectric layer or on said metal layer.
- 20. System according to claim 19, wherein a silver layer coated on both sides with a zinc sulfide layer is applied to the corrosion protective layer.
- 21. System according to claim 18, in which the total dielectric layer thickness overlying said metallic layer is between 3 and 50 nanometers.
Priority Claims (1)
Number |
Date |
Country |
Kind |
3039821 |
Oct 1980 |
DEX |
|
Parent Case Info
This application is a continuation-in-part application of Ser. No. 283,513, filed July 15, 1981 now abandoned.
US Referenced Citations (6)
Foreign Referenced Citations (1)
Number |
Date |
Country |
197801 |
Dec 1976 |
DEX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
283513 |
Jul 1981 |
|