The present invention relates to a method of manufacturing a golf club head having a composite crown with a scarf joint attachment region. More specifically, the method involves providing a stepped, scarf-jointed crown portion that minimizes the area of the composite crown that is sanded or ground down during the post-attachment finishing process.
Golf club manufacturers often combine metallic golf club head bodies with composite crowns to reduce the overall head mass and lower the clubs' center of gravity, thus improving the mass properties of such multiple material heads. The region where the crown is affixed to the body with an adhesive material is typically known as the bond joint. In prior art multiple material golf club heads, manufacturers often employ a lap joint, or “step” structure, examples of which are shown in
The manner in which these prior art composite crown structures are processed during post-attachment finishing steps is also not ideal, as a large region of the crown (known as grindstock or polishing stock) is sanded down to achieve a smooth, fully finished upper surface and eliminate imperfections in the body, requiring additional time, steps, and materials (including multiple sanding belts) and reducing the overall cosmetic appeal of the crown. In the event that the crown incorporates a fabric with a weave pattern, that pattern is obscured from view by finishing steps, thus reducing the aesthetic appeal of the golf club head.
Therefore, there is a need for an improved bond region structure that minimizes the significant stresses of impact that cause separation of the crown from the body, and that can be manufactured efficiently and finished in a manner that does not reduce its cosmetic appeal.
One aspect of the present invention is a method of manufacturing a golf club head comprising a composite crown having a tapered, full, or partial scarf joint attachment region so that the cosmetic features (e.g., the weave pattern) of the composite are retained and not sanded down and obscured during finishing.
Another aspect of the present invention is a method comprising the steps of providing a hollow golf club head body comprising a striking face, a face extension extending from an upper edge of the striking face, a bond flange extending from the face extension, a sole extending from a lower edge of the striking face, a rear flange extending away from the sole, and an upper opening, providing a composite crown comprising a scarf region with a front edge having a first thickness, a step portion having a second thickness, and a rear region having a third thickness, the scarf region gradually increasing in thickness from the front edge to the step portion, bonding the scarf region to the bond flange and the rear region to the rear flange to form an upper golf club head surface, and grinding the upper golf club head surface only from a location proximate the front edge to a location proximate the step portion, wherein the second thickness is greater than the first thickness, wherein the second thickness is greater than the third thickness, and wherein the step portion separates the scarf region from the rear region.
In some embodiments, no portion of the rear region may subject to the grinding step. In a further embodiment, the rear region may constitute a majority of an area of the crown. In other embodiments, the grinding step may reduce the thickness of the step portion from the second thickness to a fourth thickness, and the fourth thickness may be greater than the third thickness. In a further embodiment, a difference between the second thickness and the third thickness may be 0.010 inch to 0.050 inch, and a difference between the fourth thickness and the third thickness may be 0.005 inch to 0.030 inch. In another embodiment, the scarf region may have a front-to-back width of 0.250 inch to 1.250 inch. In yet another embodiment, the first thickness may be less than 0.060 inch, the second thickness may be 0.025 inch to 0.110 inch, and the third thickness may be 0.015 inch to 0.060 inch. In still other embodiments, at least a portion of the bond flange may not comprise any convex or concave curvature, while the rear flange may comprise a convex curvature.
Yet another aspect of the present invention is a method comprising the steps of providing a golf club body comprising a striking face, a face extension extending from an upper edge of the striking face, a sole extending from a lower edge of the striking face, and a bond flange extending from the face extension, providing a carbon composite crown comprising a front edge, a scarf region, a rear region, and a groove extending approximately parallel with the front edge and separating the scarf region from the rear region, bonding the scarf region to the bond flange to form an upper golf club head surface, and grinding the upper golf club head surface only from a location proximate the front edge to a location proximate the groove, wherein no portion of the rear region is subject to the grinding step, wherein the groove has a depth of 0.010 inch to 0.100 inch, and wherein the scarf region has a front-to-back width of 0.250 inch to 1.250 inch.
In some embodiments, at least a portion of the bond flange may not comprise any convex or concave curvature. In other embodiments, the bond flange may have a maximum front-to-back width of no less than 0.100 inch and no more than 0.400 inch, and in a further embodiment, the bond flange may have a constant width. In some embodiments, the scarf region may have an approximately triangular cross-sectional shape. In other embodiments, the groove may have a rounded cross-sectional shape. In any of the embodiments, the rear region may comprise a visible weave pattern.
Another aspect of the present invention is a method comprising the steps of casting from a metal material a hollow golf club head body comprising a striking face, a face extension extending from an upper edge of the striking face, a bond flange extending from the face extension, a sole extending from a lower edge of the striking face, a rear flange extending away from the sole at an angle of less than 90°, and an upper opening defined by the striking face, bond flange, rear flange, and sole, providing a crown comprising a multi-axial carbon composite fabric, the crown comprising a scarf region with a front edge having a first thickness of less than 0.050 inch, a step portion having a second thickness of 0.025 inch to 0.110 inch, and a rear region having a third thickness of 0.015 inch to 0.060 inch, applying a first adhesive layer to the bond flange and a second adhesive layer to the rear flange, affixing the scarf region to the first adhesive layer on the bond flange and the rear region to the second adhesive layer on the rear flange to cover the upper opening and form an upper golf club head surface, and grinding the upper golf club head surface only from a location proximate the front edge to a location proximate the step portion, wherein the step portion separates the scarf region from the rear region, wherein the scarf region has an approximately triangular cross-sectional shape, wherein no portion of the rear region is subject to the grinding step, and wherein the rear region comprises a visible weave pattern.
In some embodiments of this method, the grinding step may reduce the thickness of the step portion from the second thickness to a fourth thickness of 0.020 inch to 0.090 inch. In other embodiments, the crown may comprise a compression-molded composite material co-molded with the multi-axial carbon composite fabric. In still other embodiments, each of the first and second adhesive layers may have a thickness of no more than 0.010 inch. In any of the embodiments, the step portion may extend in a heel-to-toe direction across at least 50% of the crown.
Having briefly described the present invention, the above and further objects, features and advantages thereof will be recognized by those skilled in the pertinent art from the following detailed description of the invention when taken in conjunction with the accompanying drawings.
The present invention introduces a solution to the problems set forth above by providing a composite crown with an improved scarf joint construction in combination with a golf club head having improved support flanges, and methods of finishing said golf club heads to preserve the cosmetic appeal of the composite crown.
A preferred embodiment of the present invention is shown in
The face extension 28 preferably has a front-to-back width W1 of at least 0.200 inch, and more preferably approximately 0.400 inch. The bond flange 40 may have a variable front-to-back width, but preferably has a constant front-to-back width W2 that ranges from 0.100-0.400 inch, and more preferably is approximately 0.300 inch. It is important that the bond flange 40 have no convex or concave curvature to avoid introducing weak points into the bond between the bond flange 40 and the crown 30 when the golf club head 10 is fully assembled. As shown in
The golf club head 10 also comprises a crown 30 that is permanently bonded to the body 20 with an adhesive to close the upper opening and preferably is at least partially composed of a material with a weave pattern 32, an example of which is shown in
As shown in
The dimensions of the scarf region 60 of the crown 30 before the golf club head 10 is subjected to finishing processes (e.g., sanding or polishing) are different from the dimensions of the scarf region 60 after finishing. The manufactured crown 30 has a front edge thickness T4 of less than 0.060 inch, more preferably less than 0.050 inch, and a step portion 66 thickness T5 of 0.02-0.110 inch, but after the crown 30 is bonded to the body 20, the front edge 62, transition region 64, and step portion 66 are ground down during finishing such that the thickness of the front edge 62 is reduced to a sharp edge and the of the step portion 66 is reduced by 0.005-0.020 inch to have a thickness T6 of 0.020-0.090 inch. In any event, the difference Δ between the step portion 66 thickness and the rear region 68 thickness T3 drops from 0.010-0.050 inch to 0.005-0.030 inch due to finishing. In an alternative embodiment, shown in
The step portion 66 (and/or groove 70), which preferably extends across more than 50% of the entire heel-to-toe length of the crown 30 approximately parallel with the front edge 62, and more preferably across the entire length of the crown 30 as shown in
A preferred method of the present invention is illustrated in
The golf club head 10 of the present invention may be constructed to take various shapes, including traditional, square, rectangular, or triangular. In some embodiments, the golf club head 10 of the present invention may take shapes such as those disclosed in U.S. Pat. Nos. 7,163,468, 7,166,038, 7,169,060, 7,278,927, 7,291,075, 7,306,527, 7,311,613, 7,390,269, 7,407,448, 7,410,428, 7,413,520, 7,413,519, 7,419,440, 7,455,598, 7,476,161, 7,494,424, 7,578,751, 7,588,501, 7,591,737, and 7,749,096, the disclosure of each of which is incorporated by reference in its entirety herein.
The golf club head 10 of the present invention may also have a variable thickness striking face 22, such as the thickness patterns disclosed in U.S. Pat. Nos. 5,163,682, 5,318,300, 5,474,296, 5,830,084, 5,971,868, 6,007,432, 6,338,683, 6,354,962, 6,368,234, 6,398,666, 6,413,169, 6,428,426, 6,435,977, 6,623,377, 6,997,821, 7,014,570, 7,101,289, 7,137,907, 7,144,334, 7,258,626, 7,422,528, 7,448,960, 7,713,140, 8,012,041, 8,696,489, and 9,101,809, the disclosure of each of which is incorporated by reference in its entirety herein.
The mass of the club head 10 of the present invention ranges from 165 grams to 250 grams, preferably ranges from 175 grams to 230 grams, and most preferably from 190 grams to 205 grams. The crown 30 has a mass preferably ranging from 4 grams to 30 grams, more preferably from 15 grams to 25 grams, and most preferably 20 grams.
The golf club head 10 of the present invention preferably has a volume that ranges from 290 cubic centimeters to 600 cubic centimeters, and more preferably ranges from 330 cubic centimeters to 510 cubic centimeters, even more preferably 350 cubic centimeters to 495 cubic centimeters, and most preferably 415 cubic centimeters or 470 cubic centimeters.
The center of gravity and the moment of inertia of a golf club head 10 of the present invention are preferably measured using a test frame (XT, YT, ZT), and then transformed to a head frame (XH, YH, ZH). The center of gravity of a golf club head may be obtained using a center of gravity table having two weight scales thereon, as disclosed in U.S. Pat. No. 6,607,452, entitled High Moment Of Inertia Composite Golf Club, and hereby incorporated by reference in its entirety.
The moment of inertia, Izz, about the Z axis for the golf club head 10 of the present invention preferably ranges from 2800 g-cm2 to 6000 g-cm2, preferably from 3000 g-cm2 to 600 g-cm2, and most preferably from 5000 g-cm2 to 6000 g-cm2. The moment of inertia, Iyy, about the Y axis for the golf club head 10 preferably ranges from 1500 g-cm2 to 5000 g-cm2, preferably from 2000 g-cm2 to 5000 g-cm2, and most preferably from 3000 g-cm2 to 4500 g-cm2. The moment of inertia, Ixx, about the X axis for the golf club head 10 preferably ranges from 1500 g-cm2 to 4000 g-cm2, preferably from 2000 g-cm2 to 3500 g-cm2, and most preferably from 2500 g-cm2 to 3000 g-cm2.
The golf club heads 10 of the present invention preferably have coefficient of restitutions (“COR”) ranging from 0.81 to 0.875, and more preferably from 0.82 to 0.84. The golf club heads 10 preferably have characteristic times (“CT”) as measured under USGA conditions of 256 microseconds.
From the foregoing it is believed that those skilled in the pertinent art will recognize the meritorious advancement of this invention and will readily understand that while the present invention has been described in association with a preferred embodiment thereof, and other embodiments illustrated in the accompanying drawings, numerous changes, modifications and substitutions of equivalents may be made therein without departing from the spirit and scope of this invention which is intended to be unlimited by the foregoing except as may appear in the following appended claims. The section titles included herein also are not intended to be limiting. Therefore, the embodiments of the invention in which an exclusive property or privilege is claimed are defined in the following appended claims.
The present application is a continuation-in-part of U.S. patent application Ser. No. 15/062,698, filed on Mar. 7, 2016, which claims priority to U.S. Provisional Patent Application No. 62/280,077, filed on Jan. 18, 2016, the disclosure of each of which is hereby incorporated by reference in its entirety herein.
Number | Name | Date | Kind |
---|---|---|---|
8147354 | Hartwell | Apr 2012 | B2 |
20060079349 | Rae | Apr 2006 | A1 |
20150045134 | Beno | Feb 2015 | A1 |
Number | Date | Country | |
---|---|---|---|
62280077 | Jan 2016 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 15062698 | Mar 2016 | US |
Child | 15613764 | US |