Nano-composite and compositions manufactured thereof

Abstract

The present invention is directed to nano-composite and composition comprising a cationic mediator and method thereof. The cationic mediator is comprised of a hydrophobic unit and a heterocyclic cationic unit. The nano-composite is practically useful in formulating compositions such as rubber and tire products with improved gas permeability, cure properties, and/or mechanical properties etc.

Description

BACKGROUND OF THE INVENTION

The present invention is directed to nano-composites, alternatively referred to as organo-clay. More particularly, the invention is directed to a cationic mediator comprised of a hydrophobic unit and a heterocyclic cationic unit used to prepare nano-composites and rubber compositions including the nano-composites.

Since the discovery of exfoliated nylon/clay nanocomposites by Usuki et al. (J. Mater. Res. 1993, 8, 1174), there have been extensive efforts directed to the preparation of various polymer-layered material composites. One common morphology for miscible polymer-layered material dispersions is known as intercalation and exfoliation, which improves polymeric properties such as mechanical, gas barrier/permeability, thermal, and heat distortion temperature. However, for polymers, particularly nonpolar polymers, well-exfoliated polymer-layered material nanocomposites are notoriously difficult to obtain.

Gas permeability is an important element of quality for many polymer products, for example, butyl rubber. Unsaturated bonds in butyl rubber, contributed by the presence of isoprene monomer units in the backbone, can be attacked by atmospheric ozone. These attacks may, over time, lead to oxidative degradation, which may subsequently lead to chain cleavage. As such, there exists a continuous interest in lowering gas permeability of polymer products by various techniques, among which is using well-exfoliated layered materials as an additive. However, other properties such as vulcanization plateau, hardness Shore A, cure capability, rubber damping properties, cure time, modulus, stress, moisture absorption, and strain etc. cannot be negatively impacted.

The present invention provides nano-composites and polymeric compositions derived from a cationic mediator, comprised of a hydrophobic unit and a heterocyclic cationic unit. Advantageously, the invention can employ compounds used as green solvents, e.g. 1-methylimidazol, as the reactant in preparing the cationic mediator, making both the process and product more environmentally friendly.

SUMMARY OF THE INVENTION

According to one embodiment, the present invention provides a nano-composite, comprised of (a) a cationic mediator having a hydrophobic unit and a heterocyclic cationic unit, and (b) a clay, wherein said clay is exfoliated by said cationic mediator.

According to another embodiment, a composition comprising (a) a cationic mediator having a hydrophobic unit and a heterocyclic cationic unit, (b) a clay, and (c) a carbon-chain or a heterochain polymer is provided.

Still other embodiments of the invention provide novel rubber formulations and tire products including the nano-composites. The addition of the nano-composite can improve properties such as gas permeability, cure, and various mechanical properties.

According to a further embodiment of the invention, a method of exfoliating clays and producing a nano-composite is provided.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention may take form in various components and arrangements of components, and in various steps and arrangements of steps. The drawings, in which like reference numerals denote like components throughout the several views, are only for purposes of illustrating preferred embodiments and are not to be construed as limiting the invention.

In the drawings appended hereto:

FIG. 1 shows small angle x-ray scattering (SAXS) of an ionic liquid surfactant treated mica.

FIG. 2 shows the 2-dimensional image of small angle x-ray scattering (SAXS) of ionic liquid surfactant treated mica.

FIG. 3 shows the small angle x-ray scattering (SAXS) of an organo-clay/butyl rubber nanocomposite.

FIG. 4 shows 2-dimensional image of small angle x-ray scattering of the organo-clay/butyl rubber nanocomposite.

FIG. 5 shows the changing of torque as a function of cure time for an organo-clay treated rubber.

FIGS. 1-4 show the small-angel x-ray scattering patterns measured when ionic liquid surfactant treated mica and organo-clay/butyl rubber nanocomposite according to the present invention were irradiated with x-ray. The scattering of x-ray from these samples was caused by the difference of the electron densities in clay layers, surfactants and/or butyl rubber molecules. The scattering patterns were formed by the interference of secondary waves that were emitted from clay layers, surfactants and/or butyl rubber molecules. The result of SAXS is essentially the intensity of the Fourier transform of the electron density and reflects the microstructures of the sample. In accord with Bragg's law, structural parameters of the sample, such as distance between clay layers, can be calculated from the peak positions and intensities.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

The term “cationic mediator” is used in the present invention to describe a chemical species able to effectively mediate, or compatiblize, immiscible organic polymer and inorganic layered material such as clay, into a relatively homogenous state substantially without phase separation. Generally, the mediator facilitates the intercalation of organic polymer between the layers of the layered material.

The cationic mediator can comprise at least one cationic unit, which typically is also hydrophilic, that can bind to the layers of inorganic layered material with effectively higher affinity than to bonding to an organic material. The cationic mediator typically also includes a hydrophobic unit, such as butyl rubber. While a cationic mediator typically binds to an inorganic layered material by hydrophilic interaction or ionic bond, it can also bind or link to an organic material through a variety of physical and chemical forces such as hydrophobic interaction, covalent bonds, π-π stacking interaction, lock-key type interaction, hydrogen bonds, and coordination bonds etc.

The cationic unit may be monoatomic or polyatomic, and bear one or more elementary charges of the proton, i.e. positive charges. Depending upon the specific structure of the cationic mediator, such as the presence or absence of a conjugated system and whether the cationic unit includes the optional conjugated system, the positive charge(s) can be either localized or delocalized. The cationic mediator can be accompanied by negatively charged species to balance its positive charge and neutralize the overall charge of the system. Although the negatively charged species is typically independent, e.g. a counter ion(s), it is also feasible that the negatively charged species is part of the cationic mediator, by which an inner salt is formed. In various embodiments, the counter ion of the cationic mediators may also be those negatively charged groups of the layers in the layered material, for example, after the cationic mediator has exchanged cation of the layered material by intercalating in between the layers.

Exemplary counter ions include, but are not limited to, simple anions such as Cl⁻, Br⁻, F⁻, I⁻, O²⁻, S²⁻, Se²⁻, Te²⁻, N³⁻, As³⁻, and the like; and polyatomic anions such as BF₄⁻, PF₆⁻, CO₃²⁻, HCO₃⁻, SO₄²⁻, CF₃SO₃⁻, SO₃²⁻, S₂O₃²⁻, HSO₄⁻, H₂PO₄⁻, HPO₄²⁻, PO₄³⁻, NO₂⁻, NO₃⁻, C₂O₄²⁻, C₂H₃O₂⁻, OH⁻, O₂²⁻, N₃⁻, CrO₄²⁻, Cr₂O₇²⁻, BO₃³⁻, MnO₄⁻, AsO₄³⁻, SCN⁻, CN⁻, CNO⁻, ClO⁻, ClO₂⁻, ClO₃⁻, ClO₄⁻, BrO⁻, BrO₂⁻, BrO₃⁻, BrO₄⁻, IO⁻, IO₂⁻, IO₃⁻, IO₄⁻, and the like.

The present invention provides a nano-composite comprising (a) a cationic mediator comprised of a hydrophobic unit and a heterocyclic cationic unit, and (b) a clay, wherein said clay is intercalated and/or exfoliated by said cationic mediator. In one embodiment, the cationic mediator does not degrade at temperatures up to about 150° F., preferably up to about 250° F., more preferably up to about 350° F., and even more preferably up to about 400° F. Preferably, the clay will be sufficiently exfoliated to provide an average gap greater than about 0.1 nm between layers.

The heterocyclic cation unit of the present invention may be, but is not limited to, imidazolium, 1-alkylimidazolium, 1,3-dialkylimidazolium, 1-arylalkylimidazolium, 1-arylalky-3-alkyl-limidazolium, 1,3-diarylalkylimidazolium, benzimidazolium, imidazolinium, pyridinium, piperidinium, pyrazinium, piperazinium, pyrrolium, pyrrolidinium, pyrazolium, diazolium, triazolium, pyridazinium, tetrazolium, amidinium, guanidinium, oxazolium, oxadiazolium, oxatriazolium, thiazolium, thiadiazolium, thiatriazolium, quaternary pyrazolidine, quaternary pyrrolidones, indolium, isoindolium, quinolinium, isoquinolinium, quinazolinium, quinoxalinium, derivates thereof, and mixtures thereof.

The hydrophobic unit may be selected from the group consisting of butyl, isobutyl, behenyl, palmitoleyl, oleyl, linoleyl, linelenyl, erucyl, capryl, tallow, n-pentyl, any isopentyl, n-hexyl, any isohexyl, n-heptyl, any isoheptyl, n-octyl, any isooctyl, n-nonyl, any isononyl, n-decyl, any isodecyl, n-undecyl, any isoundecyl, n-dodecyl or lauryl, any isododecyl, n-tridecyl, any isotridecyl, n-tetradecyl, myristyl, any isotetradecyl, n-pentadecyl, any isopentadecyl, n-hexadecyl or cetyl, palmityl, any isohexadecyl, n-heptadecyl, any isoheptadecyl, n-octadecyl, stearyl, any isooctadecyl, n-nonadecyl, any isononadecyl, n-eicosyl, any isoeicosyl, n-henicosyl, any isohenicosyl, n-docosyl, any isodocosyl, n-tricosyl, any isotricosyl, n-tetracosyl, any isotetracosyl, n-pentacosyl, any isopentacosyl, n-hexacosyl, any isohexacosyl, n-heptacosyl, any isoheptacosyl, n-octacosyl, any isooctacosyl, n-nonacosyl, any isononacosyl, n-triacontyl, any isotriacontyl, n-hentriacontyl, any isohentriacontyl, n-dotriacontyl, any isodotriacontyl, n-tritriacontyl, any isotritriacontyl, n-tetratriacontyl, any isotetratriacontyl, n-pentatriacontyl, any isopentatriacontyl, n-hexatriacontyl, any isohexatriacontyl, n-heptatriacontyl, any isoheptatriacontyl, n-octatriacontyl, any isooctatriacontyl, n-nonatriacontyl, any isononatriacontyl, n-tetracontyl, any isotetracontyl, n-hentetracontyl, any isohentetracontyl, n-dotetracontyl, any isodotetracontyl, n-tritetracontyl, any isotritetracontyl, n-tetratetracontyl, any isotetratetracontyl, n-pentatetracontyl, any isopentatetracontyl, n-hexatetracontyl, any isohexatetracontyl, n-heptatetracontyl, any isoheptatetracontyl, n-octatetracontyl, any isooctatetracontyl, n-nonatetracontyl, any isononatetracontyl, n-pentacontyl, isopentacontyl and mixtures thereof.

An exemplary cationic mediator has the formula (I) as shown below.

in which at least one of R₁, R₂, R₃, R₄, and R₅ can be the hydrophobic unit as defined above and up to four of the remaining of R₁, R₂, R₃, R₄, and R₅ can be independently of each other selected from hydrogen, methyl, ethyl, vinyl, allyl, propyl, isopropyl, or aryl-containing or hetaryl-containing group. As used herein, the terms “aryl” and “hetaryl” are intended to embrace monocyclic or polycyclic aromatic hydrocarbon and heterocyclic groups. Examples of aralkyl and alkylaralkyl groups include, but are not limited to, benzyl, benzhydryl, tolylmethyl, trityl, cinnamyl, phenethyl, styryl, phenylbutyl, neophyl, and the like. Examples of aryl and alkylaryl groups include, but are not limited to, phenyl, biphenyl, tolyl, xylyl, mesityl, cumenyl, di(t-butyl)phenyl, anthryl, indenyl, naphthyl, and the like. Haloaryl and haloaralkyl groups are aryl and aralkyl groups which have been substituted with one or more halo groups. Examples of such groups include, but are not limited to, halobenzyl (e.g., fluorobenzyl, chlorobenzyl, bromobenzyl, or iodobenzyl, whether ortho-, meta-, or para-substituted), dihalobenzyl, trihalobenzyl, tetrahalobenzyl, pentahalobenzyl, halophenyl (e.g., fluorophenyl, chlorophenyl, bromophenyl, or iodophenyl, whether ortho-, meta-, or para-substituted), dihalophenyl, trihalophenyl, tetrahalophenyl, and pentahalophenyl and mixtures thereof.

Specific examples of other aryl-containing and hetaryl-containing groups are phenoxy, tolyloxy, xylyloxy, mesityloxy, and cumenyloxy; biphenyl, anilino, toluidino, tosyl, allyl-benzyl or -phenyl, furyl, pyridyl, 2-pyridyl (pyridin-2-yl), indol-1-yl, chloromethyl-benzyl or -phenyl, trifluoromethyl-benzyl or -phenyl, hydroxy-benzyl or -phenyl, methoxy-benzyl or -phenyl, ethoxy-benzyl or -phenyl, methoxyethoxy-benzyl or -phenyl, allyloxy-benzyl or -phenyl, phenoxy-benzyl or -phenyl, acetoxy-benzyl or -phenyl, benzoyloxy-benzyl or -phenyl, methylthio-benzyl or -phenyl, phenylthio-benzyl or -phenyl, tolylthio-benzyl or -phenyl, methylamino-benzyl or -phenyl, dimethylamino-benzyl or -phenyl, ethylamino-benzyl or -phenyl, diethylamino-benzyl or -phenyl, acetylamino-benzyl or -phenyl, carboxy-benzyl or -phenyl, methoxycarbonyl-benzyl or -phenyl, ethoxycarbonyl-benzyl or -phenyl, phenoxycarbonyl-benzyl or -phenyl, chlorophenoxycarbonyl-benzyl or -phenyl, N-cyclohexylcarbamoyloxy-benzyl or -phenyl, allyloxycarbonyl-benzyl or -phenyl, carbamoyl-benzyl or -phenyl, N-methylcarbamoyl-benzyl or -phenyl, N,N-dipropylcarbamoyl-benzyl or -phenyl, N-phenylcarbamoyl-benzyl or -phenyl, nitro-benzyl or -phenyl, cyano-benzyl or -phenyl, sulfo-benzyl or -phenyl, sulfonato-benzyl or -phenyl, phosphono-benzyl or -phenyl, phosphonato-benzyl or -phenyl groups, and morpholino-benzyl or -phenyl and mixtures thereof.

Specific examples of the cationic mediator include the following cations with a halide such as chloride as their counter ion.

Optionally, the cationic mediator of the present invention may work together with another cationic mediator or surfactant in exfoliating clay and forming the nano-composite. Examples of the other cationic mediators include dimethyl ditallow ammonium, trimethyl tallow ammonium, dimethyl dihydrogenated tallow ammonium, methyl ethyl ditallow ammonium, methyl ethyl benzyl tallow ammonium, dimethyl ethyl tallow ammonium.

In preparing the cationic mediator, some reagents may be used as the precursors for the heterocyclic cationic unit. Examples of such reagents include, but are not limited to, imidazole, 1-methylimidazole, 1-benzylimidazole, pyrazine, pyrazole, pyridazine, pyridine, imidazolidine, piperazine, piperidine, pyrazolidine, pyrrolidine, the derivatives thereof, and the mixtures thereof. In some embodiments the reagent may be a room temperature ionic liquid that functions as a reactant, a solvent, and an environmentally friendly, nonvolatile, nonflammable, or recyclable agent. 1-methylimidazole and 1-benzyllimidazole are good examples of such room temperature ionic liquids and have been used in the present invention. For example, cationic mediators of formulas (II) and (III) can be formed by mixing alkyl halides such as octyl chloride or hexadecyl chloride with 1-methylimidazol at elevated temperatures, such as between about 23° C. to about 500° C., preferably between about 50° C. and about 180° C., more preferably between about 75° C. and about 100° C. A significant benefit is therefore the reduction, if not elimination, of harmful VOC emissions. Accordingly, certain of the cationic mediators disclosed herein can be used as a general-purpose surfactant, in addition to a clay exfoliating agent.

In certain embodiments, the cationic mediator may be used to exfoliate a layered material and form useful products such as a nano-composite, or organo-clay, or exfoliated clay. An exfoliated layered material does not retain the degree of order or uniformity in layer spacing and/or position that may be found in layered materials or intercalated layered materials. In the present invention, the ratio between clay and cationic mediator can be by weight from 5:95 to 95:5, preferably from 30:70 to 70:30, and more preferably from 40:60 to 60:40. Preferably, the exfoliated clay will have an average between-layer gap greater than about 0.1 nm, preferably greater than 1.0 nm, and more preferably greater than about 3.0 nm.

“Layered material” means an inorganic material that is in the form of a plurality of adjacent bound layers or plates. Layered materials used in the present invention are those that can give at least one of the cationic mediators access to their interlayer spaces through exchanging, partially or completely, their cations with cationic mediators, a process called intercalation. Intercalated layered materials may retain order or uniformity in layer spacing and/or layer position. In one embodiment, the layered material is first intercalated, and then exfoliated. In many cases, the layered material is clay, which typically comprises an inorganic phase having layered materials in plates or other shapes with a significantly high aspect ratio. The aspect ratio is defined as the ratio of the largest and smallest dimension of the clay particles.

Exemplary clays suitable for the present invention include, but are not limited to, synthetic mica; smectites such as montmorillonite (Bentonite), sodium montmorillonite, magnesium montmorillonite, calcium montmorillonite, beidellite, nontronite, hectorite, sodium hectorite, saponite, synthetic saponite, and sauconite; pyrophyllite; glauconites; vermiculites; polygorskines; sepiolites; allophanes; imogolites; talc; mica; fluoro-mica; illites; glauconite; phyllosilicates; volkonskoite; sobockite; stevensite; svinfordite; magadiite; kenyaite; kaolinite; dickite; nacrite; anauxite; ledikite; montronite; silicate; halloysite; metahalloysite; sericite; allophone; serpentine clays; chrysotile; antigorite; attapulgite; sepiolite; palygorskite; Kibushi clay; gairome clay; hisingerite; chlorite; and mixtures thereof.

Typical clays have a layered structure with a gap of about 0.1 nm between each layer and cations such as K⁺ and Na⁺ on the surface of each layer. The cations are attached by an ionic interaction with the negatively charged surface of the clay layers, and create a net neutral charge between clay layers.

In the exfoliation procedure, optionally, a clay may be first swelled by placing it in water. Swelling takes place because the cations of the clay become solubilized in the water, leaving adjacent negatively charged clay layers. The adjacent clay layers are repulsed by their similar negative charges, resulting in gaps of up to about 3 nm between the layers. A cationic mediator may then be added to the swollen clay to form an organo-clay or the nano-composite. Alternatively, before addition of the cationic mediator, the clay may be pre-exfoliated with a cationic surfactant such as an ammonium salts. In some embodiments, if an ionic liquid is used, the clay may be directly mixed with the cationic mediator. The cationic mediator is attracted to the negatively charged surface of the clay, keeping the swelling state stable and forming gaps of about 5-10 nm between the layers.

The intercalated cationic mediator may be accompanied by one or more polymers connected by forces such as hydrophobic interaction, π-π stacking interaction, lock-key type interaction, hydrogen bonds, coordination bonds, covalent bonds, and combinations thereof. Accordingly, the “mediation” of the cationic mediator, helps intercalate polymers between the layers of the layered material.

Additional non-polar polymer, such as rubber can further separate the layers of the clay, because the added polymer and the cationic mediator can attract each other at, e.g., their hydrophobic portions, and the added polymer will also penetrate between the clay layers. The large molecule size of the cationic mediator and/or the added polymer may counteract any remaining Van der Waals interactions between the clay layers and the clay can be fully exfoliated, i.e. separated into discrete layers.

Therefore, the present invention further provides a composition comprising (a) a cationic mediator including of a hydrophobic unit and a heterocyclic cationic unit, (b) a clay, and (c) a polymer, wherein the clay is exfoliated by the heterocyclic cationic mediator and the polymer.

There is no specific limitation on the polymers suitable for use in the present invention. However, preferred polymers are those that can intercalate between clay layers more effectively with than without the aid of the cationic mediator as demonstrated above. The polymer can have a saturated or unsaturated polyvinyl-type (i.e., carbon-chain) backbone, such as polychloroprene, polyethylene, isobutene-isoprene rubber (butyl rubber, IIR), halogenated butyl rubber (HIIR) such as ClIR and BrIIR, neoprene rubber, nitrile rubber (NBR), 1,2-polybutadiene, polyallene, polybutadiene (butadiene rubber, BR), polyisobutylene (PIB), polyisoprene, 3,4-polyisoprene, poly(methyl acrylate), poly(methyl vinyl ketone), ethylene-propylene elastomer, polystyrene (PS), polyacrylamide, poly(acrylamide oxime), polypropylene (PP), styrene-butadiene rubber (SBR), poly(methyl methacrylate), acrylonitrile-butadiene-styrene terpolymer (ABS), poly(vinyl chloride) (PVC), poly(vinylidene chloride), poly(vinyl pyridine), poly(vinyl pyrrolidone), poly(acrylic anhydride), polyacrylonitrile, styrene-acrylonitrile copolymer (SAN), ethylene-vinyl acetate copolymer (EVA), and the like.

The polymer can also possess a backbone with one or more functional groups such as carbonyl, or a non-carbon element such as N, S or O etc. (i.e. heterochain polymer). Exemplary heterochain polymers include, but are not limited to, polyether such as poly(oxyethylene), polyformadehyde, poly(phenylene oxide) or polyacetaldehyde; polyacrolein, polysulfide, polysulfone, poly(alkylene polysulfide), polyester, polycarbonate, polyphosphate ester, polyamide, polyurea, polyurethane, heterocyclic polymer, polyhydrazides, polyimide, melamine-formaldehyde resin (MF), polysaccharides, phenol-formaldehyde resin (PF), and polyanhydride etc.

The polymeric group can also be an inorganic or inorganic/organic polymer such as polysiloxane, polysilane, carborane polymer, and organometallic polymer etc.

The nano-composite may be utilized in rubber formulation and tire production. Effective exfoliation of clays and production of nano-clay are beneficial in improving gas permeability and other physical properties of rubber. As such, the present invention additionally provides a rubber formulation and a tire product, both comprising the nano-composite as described above.

An organo-clay (nano-composite) can be dispersed into a rubber such as butyl rubber. Optionally, preferably prior to dispersing the organo-clay in the rubber, the organo-clay may be washed and dried. Preferably, the organo-clay is washed with an alcohol, such as, but not limited to, isopropanol, water or mixtures thereof. According to the present invention, the rubber so formulated has lower gas permeability without incurring a negative effect on the cure properties associated with traditional clay/surfactant systems.

In a rubber formulation, additional stabilizers, antioxidants, conventional fillers, processing aids, accelerators, extenders, curing agents, reinforcing agents, reinforcing resins, pigments, fragrances, and the like can optionally be added. Specific examples of useful antioxidants and stabilizers include 2-(2′-hydroxy-5′-methylphenyl)benzotriazole, nickel di-butyl-di-thiocarbamate, tris(nonylphenyl)phosphite, 2,6-di-t-butyl-4-methylphenol, and the like. Exemplary conventional fillers and pigments include silica, carbon black, titanium dioxide, iron oxide, and the like. Suitable reinforcing materials are inorganic or organic products of high molecular weight. Examples include glass fibers, asbestos, boron fibers, carbon and graphite fibers, whiskers, quartz and silica fibers, ceramic fibers, metal fibers, natural organic fibers, and synthetic organic fibers.

As one exemplary benefit of the present invention, good cure properties and low gas permeability can both be achieved for some rubber formulations. Exemplary rubbers suitable to the present invention include, but not limited to, butyl rubber, BR, Hcis BR, SBR, NR and so on. As used herein, the butyl rubber composition may include isobutylene, halobutyl rubber, and copolymers of isobutylene and one or more additional monomers, such as isoprene, styrene, butadiene, and mixtures thereof. Tensile strength, gas permeability, and cure properties including cure capability and cure time etc. have been improved in various rubber compounds by using the nano-composite of the present invention. The butyl rubber composition is useful in the formation of inner liners for automobile tires and in applications requiring good damping characteristics, such as engine mounts. Other uses for the butyl rubber include use in air cushions, pneumatic springs, air bellows, accumulator bags, tire-curing bladders, high temperature service hoses, and conveyor belts for handling hot materials.

The nano-composite of the present invention can be advantageously incorporated into butyl rubber by any method known to a skilled artisan, for example, wet/solvent method or a dry mixing method under mild mixing conditions. Such mild mixing conditions are, for example, similar to those normally used in butyl rubber mixing. The mixing may be accomplished, for example, by using any integral mixing device such as a Brabender mixer, a twinscrew extruder or a kneader, at a mixing rate of from about 20 to about 200 rpm, at a temperature of about 25° C. to about 250° C. for a period of about 3˜30 minutes. In one embodiment, the mixing conditions are for example, mixing in a Brabender mixer at about 60 rpm at a temperature of about 70° C. for about three minutes. Of course, the organo-clay can be added according to any other method known by the skilled artisan. It is preferred that between about 1 and about 70%, more preferably, between about 3 and about 40% by weight of organo-clay or nano-composite is incorporated into the butyl rubber. Preferably, the clay in the final product is at least about 50% exfoliated, more preferably at least about 70% exfoliated. The degree of exfoliation may be found using an image created by transmission electron microscopy (TEM). The image includes black areas representing clay particles. The ratio of the population of the black areas that have a thickness of less than about 5 nm to the total population of black areas is the degree of exfoliation.

In the following, the invention will be described in more detail with reference to non-limiting examples. The following examples and tables are presented for purposes of illustration only and are not to be construed in a limiting sense.

EXAMPLES

Example 1

Cationic Mediator of Formula (II), A Liquid Surfactant

654 g of 1-choloroctane (Aldrich) and 360 g of 1-methylimidazal (Aldrich) were added into a 2000 mL tri-neck round-bottom flask. A refluxing/cooling column was installed on the right neck. A thermometer was installed on the left neck. To the middle neck was connected a nitrogen purging tube that delivered the nitrogen gas below the liquid phase. The reactants were mixed with vigorous stirring using magnetic agitation at a temperature between 75 and 80° C. After 8 hours, the solution in the flask turned into a milk-like mixture. After two days, the mixture in the flask turned homogenous again. The reaction was continued for three days. Then, the product was washed with ethyl acetate five times and toluene three times. Thereafter, it was dried in vacuum for three days.

Example 2

Cationic Mediator of Formula (III), A Liquid Surfactant

The procedure of Example 1 was repeated with minor changes. 868 g of 1-cholorohexadecane (Aldrich) and 570 g of 1-methylimidazal (Aldrich) were added into a 2000 mL tri-neck round-bottom flask. The reaction temperature was set to 95 to 100° C. After four hours, the milk-like solution transformed into a homogenous solution. The reaction was continued for three days. The post-treatment was the same as Example 1.

Example 3

Organo-Mica

60 g of the product from Example 1, 40 g of ME-100 (Coop Chemicals, Tokyo, Japan), and 800 g of deionized water were mixed together and shaken for about 16 hours. The organo-treated mica was collected through vacuum-filtration. The treated mica was further washed with isopropenol three times, and was then dried in vacuum. The clay contained 28.77% of organo-matter (i.e., the surfactant), as measured by thermo-gravity analysis (TGA). TGA was carried out on equipment manufactured by TA Instruments and Perkin Elmer, among others.

Example 4

Organo-Mica

80 g of the product from Example 2, 40 g of ME-100 (Coop Chemicals), and 800 g of deionized water were mixed together and shaken for about 16 hours. The organo-treated mica was collected through vacuum-filtration. The treated mica was further washed with isopropanol three times, and was then dried in vacuum. TGA was conducted in the same manner as Example 3, and the result showed that the clay contained 31.71% of organo-matter (i.e., the surfactant).

The products were checked using small angle X-ray scattering (SAXS). FIG. 1 and FIG. 2 show the SAXS result of the mica treated with ionic liquid surfactant of formula (III). Based on the scattering intensity profile between 2θ≈1.0 and 2θ≈10.0 of scattering angles, particularly the 2θ≈2.2 peak and the 2θ≈4.2 triplet peaks, calculation indicates that the mica has been intercalated by the ionic liquid surfactant, and the distances between the mica layers are approximately in the range of 30-40 Å.

Examples 5-11

Bromobutyl Rubber Testing

Seven bromobutyl rubber compounds were prepared according to the formulation shown in Table 1 and Table 2. The bromobutyl rubber is commercially available as Bayer XG124 Bromobutyl, BIIR. In each example, a blend of the ingredients was kneaded by the method listed in Table 3. The physical characteristics of the compositions of Examples 5-11 are shown in Table 4. Testing of the cure characteristics of rubber compounds follow the guidelines of, but were not be restricted to, ASTM-D 2084. A Monsanto Moving Die Rheometer (MDR 2000) was used to measure the cure characteristics of compounded rubbers. Cure capability (S_max−S_min) is defined as the difference between the maximum torque and the minimum torque 90% cure time at 165° C. is defined as the time required to achieve 90% cure capability. Measurement of gas permeability was conducted by using 1 mm thick sheets according to ASTM-D1434. The gas permeability index (GPI) value was calculated according to the formula: GPI=P_c/P_p where P_c=permeability of the nanocomposite and P_p=the permeability of the polymer. Shore A Hardness at 23° C., defined as relative resistance of the rubber surface to small deformations, was measured by using a Durometer following ASTM-D2240.

	TABLE 1
			Amount of ionic liquid	Amount of
		Amount of	surfactant in organo-	bromobutyl
	Organo-clay used	organo-clay (g)	clay (g)	rubber (g)
Example 5	Example 3	11.14	2.89	43.86
Example 6	Example 3	18.56	4.81	36.44
Example 7	Example 4	12.5	4.25	42.49
Example 8	Example 4	20.85	7.1	34.15
Example 9	ME-100	8.25	0	46.75
(Control 1)
Example 10	ME-100	13.75	0	41.25
(Control 2)
Example 11	No	0	0	55
(Control 3)

TABLE 2
Final Batch Formulation (for Examples 5 to 11, by parts)
Stearic Acid             0.50
Sulfur                   0.60
Zinc Oxide               0.45
Altax-MBTS (Accelerator) 0.75

TABLE 3
Mixing Conditions
	Mixer:	60 g Brabender	Agitation Speed:	60 rpm
	Mater Batch Stage
	Initial Temperature	70° C.
	0 min	charging polymers
	0.5 min	charging oil and Carbon Black
	3.0 min	drop
	Final Batch Stage
	Initial Temperature	70° C.
	0 sec	charging master stock
	2 min	charging curing agent and accelerators
	2.5 min	drop

TABLE 4
Physical properties of the test bromobutyl rubbers.
	HSA1	GPI	CC2	CT3	M&S4	STREM5	STRAM6
Example	35		2.865	13.87
5
Example	38		2.987	16.43
6
Example	50	50.2	2.846	9.22	105	909	844
7
Example	53	60	3.445	13.48
8
Example	40	86.3	2.811	13.01	18.9	373	772
9
(Control
1)
Example	42	66.4	3.161	16.74
10
(Control
2)
Example	33	100	2.237	8.69	14	324	812
11
(Control
3)
Note:
1HSA means Hardness Shore A at 23° C.
2CC means Cure Capability (Smax–Smin) (kg–cm).
3CT means 90% Cure time 165° C. (Min.).
4M&S means modulus at 23° C. and 35% strain.
5STREM means stress at maximum (psi).
6STRAM means strain at maximum (%).

The addition of exfoliated clay from example 4 into butyl rubber has significantly lowered gas permeability of the butyl rubber, as compared to control samples. In Examples 5, 6, 7, and 8, various amounts of exfoliated clay from examples 3 or 4 were added to butyl rubber, and the samples have maintained approximately the same cure capability and cure time as those of the control samples. FIGS. 3 and 4 show the SAXS results for Example 8. Comparing to FIGS. 1 and 2, FIGS. 3 and 4 have an increased baseline, disappeared triplet peak around 2θ≈4.2, and decreased peak values between 2θ≈1.0 and 2θ≈3.0. FIGS. 3 and 4 indicate that the clay exists in a less organized form, reflecting that the organo-clay has been further exfoliated in the rubber compound.

Examples 12-14

Natural Rubber Testing

In a manner similar to the procedures of Examples 5-11, natural rubber commercially available as TC10 NR from Firestone Company has been tested with the organo-clay of Example 4. The testing results are tabulated in Table 5.

TABLE 5
Physical properties of the test TC10 NR.
	Formulation	GPI	CC2	CT3	M&S4	STREM5	STRAM6
Example 12	Ex. 4 Organo-clay +	30.7	6.47	2.54	143	1949	765
	TC10 NR
Example 13	ME-100 + TC10		8.19	3.43	28	692	679
	NR (Control)
Example 14	TC10 NR (Control)	100	5.89	2.04	19	1149	862

Examples 15-17

Styrene-Butadiene Rubber (SBR) Testing

In a manner similar to the procedures of Examples 5-11, solution SBR commercially available as HX263 from Firestone Company has been tested with the organo-clay of Example 4. The testing results are tabulated in Table 6.

TABLE 6
Physical properties of the test HX263 SBR.
	Formulation	GPI	CC2	CT3	M&S4	STREM5	STRAM6
Example 15	Ex. 4 Organo-clay +	38.3	8.0	7.62	159	1155	619
	HX263
Example 16	ME-100 + HX263		11.07	16.75	40	335	242
	(Control)
Example 17	HX263 (Control)	100	8.58	16.86	28	176	200

Examples 18-20

Hcis-Butyl Rubber Testing

In a manner similar to the procedures of Examples 5-11, Hcis-BR commercially available as Diene 600 from Firestone Company has been tested with the organo-clay of Example 4. The testing results are tabulated in Table 7.

TABLE 7
Physical properties of the test Diene 600 Hcis-BR.
	Formulation	GPI	CC2	CT3	M&S4	STREM5	STRAM6
Example 18	Ex. 4 Organo-clay +	30.7	8.6	4.56	121	498	548
	Diene 600
Example 19	ME-100 + Diene		10.73	17.49	39	186	251
	600 (Control)
Example 20	Diene 600 (Control)	100	8.78	16.21	26	167	185

Examples 21-23

Solution Butyl Rubber Testing

In a manner similar to the procedures of Examples 5-11, solution butyl rubber commercially available as Diene 40NF from Firestone Company has been tested with the organo-clay of Example 4. The testing results are tabulated in Table 8.

TABLE 8
Physical properties of the test Diene 40NF Soln BR.
	Formulation	GPI	CC2	CT3	M&S4	STREM5	STRAM6
Example 21	Ex. 4 Organo-clay +	34.1	7.95	5.76	136	555	523
	Diene 40NF
Example 22	ME-100 + Diene		12.68	17.50	42	255	177
	40NF (Control)
Example 23	Diene 40NF	100	10.03	18.36	27	156	162
	(Control)

The results of Examples 5-23 show that under 15 wt % of loading, the tensile strengths of the test compounds were all better than that of the controls. Particularly, SBR shows the strongest interactions with the organo-mica, and it displays an 800% improvement in the tensile strength. Other benefits of using the treated ME100 include, for example, improved gas permeability and cure properties.

The rubber compositions of the present invention can be formulated into any component or article for which butyl rubber is typically utilized. Typical articles for which the butyl rubber compositions can be used include, but are not limited to, inner-tubes and tire inner liners, sidewall, thread rubber, hose, containers, air cushions, pneumatic sprays, air bags, tire-curing bladders, air bellows, accumulator bags, pharmaceutical closures, high temperature hoses and conveyor belts, damping mounts for engines and the like.

Example 24

The Synthesis of 1-benyzl-3-hexadecanyl Imidazolium Chloride with Formula (IV)

103 g of 1-benzylimidazole (Aldrich) and 170 g of 1-chlorohexadecane were added into a 2000 ml three-neck round-bottom flask. A refluxing/cooling condenser was set on the left neck. A thermometer was set on the right neck. A rubber stopper was set on the middle neck. Nitrogen gas was delivered into the liquid phase through a needle inserted into the rubber stopper in the middle neck. The reactants were mixed with vigorous stirring using a magnetic stirrer. After heating the contents of the flask to about 70-80° C., 1-benzylimidazole dissolved into the 1-chlorohexadecane. The temperature of the contents of the flask was maintained between 70 and 80° C. The solution in the flask turned into a red brown solution. The reaction was continued for 72 hours. Then, the product was cooled and a white product precipitated out of the solution. The product was washed with ethyl acetate. The washing step was repeated five times. After that, the product was dried in vacuum for seven hours at about 50° C.

Example 25

Preparation of Organo-Mica

80 g of the product from Example 24, 40 g of ME100 (Coop Chemical Co.) and 800 g of deionized water were mixed together in a vessel and tumbled for 16 hours. The solution was filtered and the treated mica was collected. Then, it was dried in vacuum. TGA analysis showed that the treated mica contained 50.31% of the inorganic residue.

Example 26

Preparation of Organo-Mica

80 g of the product from Example 2, 40 g of ME100 (Coop Chemical Co.) and 800 g of deionized water were mixed together in a vessel and tumbled for 16 hours. The solution was filtered and the treated mica was collected. Then, it was dried in a vacuum. TGA analysis showed that the treated mica contained 48.57% of the inorganic residue.

Examples 27, 28, 29, and 30

Rubber Mixing

Examples 27, 28, 29, and 30 were prepared according to the formulation and the mixing conditions shown in Tables 9 and 10.

TABLE 9
Rubber Formulations
	Ex. 27	Ex. 28	Ex. 29	Ex. 30
Treated mica	Ex. 25	Ex. 26	Me100	None
Amount of the treated mica (g)	12.99	13.33	7.5	—
Amount of Br-IIR (g)	37.01	36.67	42.5	50
Remill stock (g)	46.81	46.84	46.37	45.79
Cure Packages (g)
Accelerator (DM)*	0.69	0.69	0.79	0.92
Sulfur	1.04	1.03	1.18	1.37
Stearic Acid	0.62	0.62	0.71	0.82
Zinc Oxide	0.83	0.82	0.95	1.10
*Altx-MBTS

TABLE 10
mixing conditions
Mixer 60 g Brabender Rotation Speed 60 rpm
Master batch stage
Initial temperature  70° C.
0.0 min              charging polymers
0.5 min              charging treated mica
3.0 min              drop
Remill stage
Initial temperature  70° C.
0.0 min              charging master stocks
3.0 min              drop
Final Batch
Initial temperature  70° C.
0.0 min              charging remill stocks
0.5 min              charging cure packages
2.0 min              drop

After sheeting, rubber compounds were cured for 30 min at 165° C.

Example 31

Rubber Testing

In this example, the gas permeability was measured at 100° C. by GTR-30ABS (GTR TEK Co LTD) and Fleon gas (F-134a, 1,1,1,2-tertrafluoroethane) was used as test gas.

Experimental results shown in Table 11 and FIG. 5 indicate that Example 27 test rubber compounds have some improved cure properties such as presence of vulcanization plateau, and gas permeability index.

TABLE 11
Physical properties of test rubbers
	Ex. 27	Ex. 28	Ex. 29	Ex. 30
Cure Capability (Smax−Smin)	2.63	2.35	2.68	2.14
(kg−cm)
T0,1 (10% cure time; min)	1.86	1.13	2.06	1.96
T0,9 (90% cure time, min)	10.59	16.40	19.88	16.98
Gas permeability index	40	42	78	100

The technology developed here can be used to develop rubber compounds for tire inner liners, sidewall, tread rubber, hose and containers. The technology can provide good cure systems and low gas permeability materials.

The present invention has been described with reference to certain preferred embodiments. Obviously, modifications and alterations will occur to others upon reading and understanding the preceding detailed description. It is intended that the exemplary embodiment be construed as including all such modifications and alterations insofar as they come within the scope of the appended claims or the equivalents thereof.

Claims

1. A rubber tire comprising: a nano-composite comprising (a) a cationic mediator comprised of a hydrophobic unit and a heterocyclic cationic unit, and(b) a clay, wherein said clay is exfoliated or intercalated by said cationic mediator;wherein the heterocyclic cationic unit includes an imidazole;wherein the cationic mediator comprises one of the formulas shown below:

2. The product of claim 1, in which the clay is selected from the group consisting of mica; fluoro-mica; synthetic mica; montmorillonite, Bentonite, sodium montmorillonite, magnesium montmorillonite, calcium montmorillonite, beidellite, nontronite, hectorite, sodium hectorite, saponite, synthetic saponite, sauconite; pyrophyllite; glauconites; vermiculites; polygorskines; sepiolites; allophanes; imogolites; talc; illites; glauconite; volkonskoite; sobockite; stevensite; svinfordite; magadiite; kenyaite; kaolinite; dickite; nacrite; anauxite; ledikite; montronite; halloysite; metahalloysite; sericite; allophone; chrysotile; antigorite; attapulgite; sepiolite; palygorskite; Kibushi clay; gairome clay; hisingerite; chlorite; and mixtures thereof.

3. The rubber tire of claim 1, in which the clay comprises mica or synthetic mica.

4. The rubber tire of claim 1, further comprising a counter ion selected from the group consisting of Cl−, Br−, F−, I−, O2−, S2−, Se2−, Te2−, N3−, As3−, BF4−, PF6−, CO32−, HCO3−, SO42−, CF3SO3−, SO32−, S2O32−, HSO4−, H2PO4−, HPO42−, PO43−, NO2−, NO3−, C2O4−, C2H3O2−, OH−, O22−, N3−, CrO42−, Cr2O72−, BO33−, MnO4−, AsO43−, SCN−, CN−, CNO−, ClO−, ClO2−, ClO3−, ClO4−, BrO−, BrO2−, BrO3−, BrO4−, IO−, IO2−, IO3−, and IO4−.

5. A rubber tire comprising: a composition comprising (a) a cationic mediator comprised of a hydrophobic unit and a heterocyclic cationic unit, (b) a clay, and (c) a carbon-chain or a heterochain polymer, wherein said clay is exfoliated or intercalated by said heterocyclic cationic unit and said polymer;wherein the heterocyclic cationic unit includes an imidazole;in which the cationic mediator comprises one of the formulas shown below:

6. The rubber tire of claim 5, wherein the carbon-chain polymer is selected from the group consisting of polychloroprene, polyethylene, isobutene-isoprene rubber, halogenated butyl rubber, CuR, BrIIR, neoprene rubber, nitrile rubber, 1,2-polybutadiene, polyallene, polybutadiene, polyisobutylene, polyisoprene, 3,4-polyisoprene, poly(methyl acrylate), poly(methyl vinyl ketone), ethylene-propylene elastomer, polypropylene, styrene-butadiene rubber, poly(methyl methacrylate), acrylonitrile-butadiene-styrene terpolymer, poly(vinyl chloride), poly(vinylidene chloride), poly(vinyl pyridine), poly(vinyl pyrrolidone), poly(acrylic anhydride), polyacrylonitrile, styrene-acrylonitrile copolymer, ethylene-vinyl acetate copolymer, and combinations thereof.

7. A method of exfoliating a clay and incorporating it in a rubber tire, including mixing into the clay a sufficient amount of a cationic mediator comprised of a hydrophobic unit and a heterocyclic cationic unit wherein the cationic mediator comprises one of the formulas shown below:

8. A method to improve rubber properties in a tire product including at least one of gas permeability, cure properties, and mechanical properties, comprising mixing a clay with sufficient amount of a cationic mediator comprised of a hydrophobic unit and a heterocyclic cationic unit as defined in claim 1; exfoliating the clay by the cationie mediator; and mixing the exfoliated clay into a rubber tire; wherein the heterocyclic cationic unit includes an imidazole;wherein the cationic mediator comprises one of the formulas shown below:

9. A rubber tire comprising: a nano-composite composition comprising (a) a layered material comprising cations, and (b) a cationic mediator comprising a hydrophobic unit and a hetercyclic unit, wherein at least one of the cationic mediators comprises at least partial exchange with at least one of the cations;wherein the heterocyclic cationic unit includes an imidazole;wherein the cationic mediator comprises one of the formulas shown below:

10. The tire product of claim 5, wherein the carbon chain polymer is butyl rubber.

11. The rubber tire of claim 1, in which the clay is selected from the group consisting of smectites, phyllosilicates, and serpentine clays.