Nano-gold catalyst and process for preparing the same

Abstract

The present invention discloses a nano-gold catalyst including a solid carrier and gold deposited on the carrier, wherein the deposited gold has a size less than 10 nm, and the carrier is a mixed metal hydroxide and oxide having the following formula:

Description

FIELD OF THE INVENTION

[0001] The present invention relates to a nano-gold catalyst and a process for preparing the same; and particularly to a nano-gold catalyst capable of oxidizing carbon monoxide at room temperature and a process for preparing the same.

BACKGROUND OF THE INVENTION

[0002] Gold is a highly stable metal without any catalyst activity. When the size of a gold particle is smaller than 10 nm, gold exhibits a unique room temperature activity due to meta-stable interatomic bonding of gold atoms. A nano-gold catalyst has the following three features: fast reaction rate, high selectivity, and low reaction temperature.

[0003] Applications of a nano-gold catalyst include:

[0004] (1) Oxidation of carbon monoxide at room temperature

[0005] The oxidation reaction of carbon monoxide at room temperature is a best showcase reaction for a nano-gold catalyst. At present, only a nano-gold catalyst has the capability of oxidizing carbon monoxide at room temperature. The prerequisite for an active gold catalyst is the particle size of gold needs to be less than 10 nm, with an optimum catalyst particle size of <5 nm. Another factor affecting the activity of a gold catalyst is a strong metal-support interaction (SMSI) between gold and a support. The support is preferably selected from p-type and n-type semiconductor metal oxides. Available supports include: TiO2, Fe2O3, Co3O4 and NiO, etc.

[0006] At present, although a gold catalyst can be synthesized to have a particle size less than 10 nm and posses a high activity in oxidizing carbon monoxide, it can not be commercialized due to a short lifetime and the catalytic efficiency of the catalyst. The factors affecting the lifetime of the catalyst include: an insufficient interaction between gold particles and the support. The melting point of a gold catalyst with a particle size of 5 nm is drastically reduced from the original 1337K to 700K. As a result, the gold catalyst is liable of sintering along with the progress of the reaction. And the catalyst will lose its activity when the particle size of the catalyst grows beyond 10 nm.

[0007] (2) Selective oxidation reaction of hydrocarbons

[0008] The selective oxidation of hydrocarbons and aromatic hydrocarbons is an important technology for producing key intermediate materials in chemical engineering processes, e.g. preparation of an alcohol from an alkane, preparation of an epoxide from an alkene, and preparation of a hydroxyl aromatic hydrocarbon from an aromatic hydrocarbon, etc. Most of the above-mentioned processes adopt a liquid phase oxidation reaction system, which uses hydrogen peroxide as an oxidizing agent. A gas phase oxidation process cannot compete with a liquid phase oxidation process due to a poor selectivity. However, this situation is changed due to the emergence of the nano-gold catalyst. The selectivity of product for some processes can exceed 90 mol % and molecular oxygen can be used as an oxidizing agent. Even though the results are encouraging, improvements are required due to a low yield per unit catalyst. The related prior arts are listed in the following:

		Selec-	Con-
Type of reaction	Catalyst	tivity	version	Yield	Ref.
methanol →	Au gauze	100	100	100	1)
formaldehyde
propylene → PO	Au-TiO2/SiO2	93	2.6	—	2)
isobutane → t-butanol	Au-TiO2/SiO2	85	1.0	—	2)
1) C. N. Hodges and L. C. Roselaar, J. Appl. Chem. Biotechnol. 25 (1975) p609
2) T. Hayashi and M. Haruta, Shokubai, 37 (1995) p75

[0009] (3) Use of nano-gold catalyst in other chemical reactions:

	Type of reaction	Catalyst	Ref.
	Butadiene → butene	Au/Al2O3	2)
	Acetone → isopropanol	Au films	3)
	CO + H2 → methanol	Au/ZnO, Au/ZnFe2O4	4)
	CO + H2O → H2	Au/Fe2O3	5)
	NO + H2 → N2 or NH3	Au/MgO	6)
	NO + CO → N2 or N2O	Au/Fe2O3, Au/NiFe2O4	7)
	NO + hydrocarbon → N2	Au/ZnO, Au/Al2O3	8)
	2) T. Hayashi and M. Haruta, Shokubai, 37 (1995) p75
	3) C. T. H. Stoddat and C. Kemball, J. Colloid Sci., 11 (1956) p633
	4) H. Sakurai and M. Haruta, Catal. Today, 29 (1996) p361
	5) D. Andreeva, T. Tabakova, V. Idakiev, P. Christov, and R. Giovanoli, Appl. Catal. A:, 169 (1998) p9
	6) S. Galvagno and G. Parravano, J. Catal., 55(1978) p178
	7) M. Haruta, Catal. Today, 36(1996) p153
	8) A. Ueda, T. Ohshima, and M. Haruta, Appl. Catal. B:, 12 (1997) p81

[0010] WO 00/09259 (CA 246882A1) discloses a Au/Fe2O3 catalyst suitable for CO selective oxidation in a reforming gas. Said catalyst is prepared by depositing a gold cluster with a diameter less than 4.5 nm on a granular Fe2O3 catalyst support. A method for preparing said catalyst comprises: (a) reacting a water soluble Fe(III) salt with an alkaline in an aqueous medium; (b) immersing a wet hydroxide gel thus obtained in an aqueous solution of a water soluble gold compound in order to deposit a complex gold cluster on the surface of the hydroxide gel; (c) removing water from the obtained reaction product suspension; and (d) calcining the resulting dry reaction product at 350-700° C. Although said prior art catalyst can selectively oxidize CO in a reforming gas, its CO oxidation activity at room temperature is still too low.

SUMMARY OF THE INVENTION

[0011] A main objective of the present invention is to provide a novel gold catalyst, and particularly a nano-gold catalyst with a novel carrier.

[0012] Another objective of the present invention is to provide a process for preparing a new nano-gold catalyst.

[0013] In order accomplish the aforesaid objectives of the present invention, a nano-gold catalyst synthesized according to the present invention comprises a solid carrier and gold deposited on the carrier, wherein the deposited gold has a size less than 10 nm, and the carrier comprises a mixed metal hydroxide and oxide having the following formula:

M(OH)qOy

[0014] Wherein M is Ti, Fe, Co, Zr, or Ni; q is 0.1-1.5; and q+2y=z, wherein z is the valence of M.

[0015] Preferably, said carrier is composed of said mixture of metal hydroxide oxide, and said carrier is particulate having a specific surface area of 150-300 m2/g.

[0016] Preferably, q is 0.5-1.5 and M is Ti, Fe(III) or Co.

[0017] Preferably, said deposited gold has a particle size smaller than 5 nm.

[0018] The present invention also discloses a process for preparing a nano-gold catalyst, which comprises the following steps:

[0019] a) preparing a M(OH)x solid carrier with a specific surface area larger than 150 m2/g, wherein M is Ti, Fe, Co, Zr, or Ni, and x is 2-4;

[0020] b) preparing an acidic gold precursor solution;

[0021] c) mixing said M(OH)x solid carrier with said acidic gold precursor solution, and controlling pH value of the resulting mixture to be basic, so that gold is deposited on said M(OH)x solid carrier to form a M(OH)x carrier deposited with gold, abbreviated as Au/M(OH)x; and

[0022] d) partially oxidizing said Au/M(OH)x to form a nano-gold catalyst comprising a mixed metal hydroxide and oxide carrier having the following formula and gold deposited on said carrier:

M(OH)qOy

[0023] wherein M is defined as above; q is 0.1-1.5; and q+2y=z, wherein z is the valence of M.

[0024] Preferably, said partial oxidation in step d) comprises:

[0025] d1) performing a solid/liquid separation on the mixture resulting from step c) and drying the resulting Au/M(OH)x; and

[0026] d2) calcining the dried Au/M(OH)x.

[0027] Preferably, said calcining in step d2) is carried out at 100° C.-500° C. for 0.5-4 hours, and more preferably, said calcining in step d2) is carried out at 150-250° C. for 2 hours.

[0028] Preferably, said partial oxidation in step d) comprises:

[0029] d0) adding an oxidation agent into the mixture resulting from step c) to perform an oxidation reaction; and

[0030] d1′) performing a solid/liquid separation on the reaction mixture resulting from step d0), and drying the resulting solid. More preferably, said partial oxidation in step d) further comprises:

[0031] d2) calcining the dried solid obtained from step d1′).

[0032] Preferably, said oxidation agent in step d0) is a strong acid such that, after the addition of said strong acid, the resulting reaction mixture has a pH value of 0.5-4. More preferably, said strong acid is nitric acid.

[0033] Preferably, said oxidation reaction in step d0) is carried out at 40° C.-100° C. for 1-8 hours.

[0034] Preferably, said solid carrier in step a) is Ti(OH)4.

[0035] Preferably, said step b) comprises dissolving HAuCl4 or AuCl3 in a solvent. More preferably, said solvent is ethanol or water.

[0036] Alternatively, said step b) comprises dissolving solid gold in a mixed solvent of HCl and HNO3. Preferably, said mixed solvent is a mixture of 12 N HCl aqueous solution and 70% HNO3 aqueous solution with a volume ratio of 2 N HCl aqueous solution: 70% HNO3 aqueous solution=50:17.

[0037] Preferably, said pH value of the resulting mixture to be basic in step c) is 7.1-12.

[0038] Preferably, said mixing in step c) comprises: dispersing said solid carrier in water; dripping said acidic gold precursor solution into the resulting solid carrier aqueous dispersion while stirring; and dripping an alkaline solution into the aqueous dispersion concurrently with said acidic gold precursor solution, if said aqueous dispersion is acidic, and no need of adding an alkaline solution, if said aqueous dispersion is basic.

[0039] Preferably, said solid carrier aqueous dispersion has a pH value of 8-12, and said acidic gold precursor solution has a pH value of 0-4.

[0040] Preferably, said solid carrier in step a) is Fe(OH)3, and NH4(OH) is used as said alkaline solution to be dripped into said aqueous dispersion.

[0041] Preferably, said solid carrier in step a) is Co(OH)2, and NH4(OH) is used as said alkaline solution to be dripped into said aqueous dispersion.

[0042] Preferably, said solid carrier in step a) is Ti(OH)4, and no alkaline solution is dripped into said aqueous dispersion.

[0043] Preferably, said solid carrier in step a) has a particle size of 10-50 nm, and has a specific surface area of 150-300 m2/g.

[0044] Preferably, q is 0.5-1.5 and M is Ti, Fe(III) or Co in step d).

[0045] Preferably, said nano-gold catalyst formed in step (d) comprises gold with a particle size smaller than 5 nm.

[0046] A nano-gold catalyst according to the present invention at least is known to have an excellent CO oxidation activity and an excellent catalyst lifetime at room temperature. Moreover, said CO oxidation activity and catalyst lifetime are substantially not affected by the presence of moisture and a high concentration of CO2.

DETAILED DESCRIPTION OF THE INVENTION

[0047] A gold catalyst having a gold particle size <5 nm on a special carrier synthesized according to the present invention has the capability of completely converting 0˜10,000 ppm CO at room, temperature (where the gas spatial velocity (GHSV) can reach 300,000 hr−1). Such a nano-gold catalyst has passed tests regarding the lifetime of a catalyst, moisture resistance, and resistance to high concentration of CO2. In a reaction system using the invented catalyst, after 100 hours of continuous reaction, the concentration of CO in the effluent still remains at 0 ppm. The invented catalyst can be produced by using a conventional catalyst synthesis device at a relatively low cost, and thus has a high economic competitiveness.

[0048] The present invention will be further elaborated by way of the following examples, which are explanatory and not for limiting the scope of the present invention.

Preparation Example 1

[0049] 150 ml of TiCl4 was dripped into 800 ml of dehydrated alcohol in a 2L polypropylene beaker. The beaker was placed in an ice bath to maintain the temperature of the solution to be below 30° C. 700 ml of ethanol was placed in a 5L polypropylene beaker and the beaker was placed in an ice bath to maintain the temperature of the solution to be below 30° C. The above prepared lemon yellow solution of TiCl4/dehydrated alcohol was dripped into the ethanol under agitation, meanwhile 80% of ammonia solution (483 ml) was dripped in to control the pH value of the mixture in the beaker to be at 8. After completion of the dripping, the agitation was continued for two hours. The resulting mixture was filtered, and the filtration cake was washed with deionized water to remove the chlorine ions contained therein until the wash filtrate no longer formed a white precipitation when 0.1 N silver nitrate was used for titration. Next, the filtration cake was dried at 110° C. to obtain 117 g of a white dry Ti(OH)4 carrier.

Preparation Example 2

[0050] 150 ml of TiCl4 was dripped into 800 ml of deionized water in a 2L polypropylene beaker. The beaker was placed in an ice bath to maintain the temperature of the solution to be below 30° C. 700 ml of deionized water was placed in a 5L polypropylene beaker and the beaker was placed in an ice bath to maintain the temperature of the solution to be below 30° C. The above prepared aqueous solution of TiCl4 was dripped into deionized water under agitation, meanwhile 30% of ammonia solution (620 ml) was dripped in to control the pH value of the mixture in the beaker to be at 10. After completion of the dripping, the agitation was continued for two hours. The resulting mixture was filtered, and the filtration cake was washed with deionized water to remove the chlorine ions contained therein until the wash filtrate no longer formed a white precipitation when 0.1 N silver nitrate was used for titration. Next, the filtration cake was dried at 110° C. to obtain 116 g of a white dry Ti(OH)4 carrier.

Preparation Example 3

[0051] 270.5 g of FeCl3.6H2O was added into 1500 ml of water in a 5L polypropylene beaker. The mixture was dissolved under agitation. 2750 ml of 30% ammonia solution was dripped into the solution in the beaker under agitation. After completion of the dripping, the agitation was continued for two hours, meanwhile a 30% ammonia solution was dripped into the solution to control the final pH value of the solution to be at 10. The obtained mixture was filtered, and the filtration cake was washed with deionized water to remove the chlorine ions contained therein until the wash filtrate no longer formed a white precipitation when 0.1N silver nitrate was used for titration. Next, the filtration cake was dried at 110° C. to obtain 77 g of a chocolate-colored dry Fe(OH)3 carrier.

EXAMPLES 1˜6

[0052] 0.4 g HAuCl4 was dissolved in 100 ml of ethanol. The resulting solution was dripped into a dispersion formed by 20 g of the Ti(OH)4 prepared in Preparation Example 1 and 100 ml of water. The resulting mixture was placed still overnight and then filtered. The resulting filtration cake was washed with 100 ml of ethanol, and then dried in vacuum to form 20 g of a gold catalyst semi-product (abbreviated as 1% Au/Ti(OH)4). Gold catalysts were obtained by separately calcining 1 g of the gold catalyst semi-product at 300, 400, 450, and 500° C. The CO oxidation performance of said gold catalysts to a CO-containing air is in Table 1.

TABLE 1
	Calcining		Space	Inlet	Inlet CO	CO
Exam-	temp.	Air flow	velocity	temp.	conc.	conversion
ple	(° C.)	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
1	300	500	30,000	136	10,000	80
2	400	500	30,000	66	10,000	80
3	450	500	30,000	54	10,000	80
4	500	500	30,000	70	10,000	80
5	450	500	30,000	44	30,000	80
6	450	500	30,000	35	50,000	80

EXAMPLES 7˜12

[0053] The procedures in Example 1 were repeated to prepare a gold catalyst intermediate except that the amount of HAuCl4 was changed to 0.8 g (2% Au/Ti(OH)4). 1 g of the gold catalyst semi-product was calcined at 450° C. for 4 hours to obtain a gold catalyst. Analysis showed that said gold catalyst had a composition of Ti(OH)0.5-1O1.75-1.5. The CO oxidation performance of said gold catalyst to a CO-containing air is shown in Table 2.

TABLE 2
		Space	Inlet	Inlet CO	CO
	Air flow	velocity	temp.	conc.	conversion
Example	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
7	500	30,000	28	1,400	100
8	500	30,000	28	2,500	100
9	500	30,000	28	5,000	100
10	500	30,000	28	10,000	100
11	500	30,000	28	30,000	100
12	500	30,000	28	50,000	100

EXAMPLES 13˜16

[0054] The procedures in Example 1 were repeated to prepare a gold catalyst intermediate, wherein the amounts of HAuCl4 used were 0.4 g, 0.8 g, 1.2 g, and 2.0 g of HAuCl4 to prepare gold catalyst semi-products (2%, 3% and 5% Au/Ti(OH)4). 1 g of the gold catalyst semi-product was sintered at 450° C. for 4 hours to obtain a gold catalyst. The CO oxidation performance of said gold catalysts to a CO-containing air is shown in Table 3.

TABLE 3
	Amount of
	gold		Space	Inlet	Inlet CO	CO
Exam-	deposited	Air flow	velocity	temp.	conc.	conversion
ple	(%)	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
13	1	500	30,000	65	10,000	100
14	2	500	30,000	28	10,000	100
15	3	500	30,000	256	10,000	100
16	5	500	30,000	141	10,000	100

EXAMPLE 17

[0055] 0.4 g HAuCl4 was dissolved in 100 ml of ethanol. The resulting solution was dripped into a dispersion formed by 20 g of the Fe(OH)3 prepared in Preparation Example 3 and 100 ml of water. The resulting mixture was mixed for 2 hours and then filtered. The resulting filtration cake was washed with 100 ml of ethanol, and then dried at 120° C. to form 20 g of a gold catalyst semi-product (abbreviated as 1% Au/Fe(OH)3) having a carrier of Fe(OH)3. A gold catalyst was obtained by calcining 1 g of the gold catalyst semi-product at 300° C. for 4 hours. The CO oxidation performance of said gold catalyst to a CO-containing air is shown in Table 4.

EXAMPLE 18

[0056] 0.8 g of HAuCl4 was dissolved in 100 ml of deionized water. The resulting solution was dripped into a dispersion formed by 20 g of the Fe(OH)3 carrier prepared in Preparation Example 3 and 100 ml of water. Meanwhile, 30% of ammonia solution was used to adjust the pH value of the mixture to 10. The resulting mixture was mixed for 2 hours and then filtered. The resulting filtration cake was washed with 100 ml of deionized water, and then dried at 120° C. to form 20 g of a gold catalyst semi-product (abbreviated as 2% Au/Fe(OH)3) having a carrier of Fe(OH)3. A gold catalyst was obtained by calcining 1 g of the gold catalyst semi-product at 300° C. for 4 hours. The CO oxidation performances of said gold catalyst to a CO-containing air is shown in Table 4.

TABLE 4
	calcining		Space	Inlet	Inlet CO	CO
Exam-	temp.	Air flow	velocity	temp.	conc.	conversion
ple	(° C.)	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
17	300	500	30,000	203	10,000	100
18	300	500	30,000	28	10,000	100

EXAMPLES 19˜20

[0057] 0.8 g of HAuCl4 was dissolved in 100 ml of deionized water. The resulting solution was dripped into a dispersion formed by 20 g of a cobalt hydroxide carrier (Co(OH)2, ProChem, Inc, USA) and 100 ml of water. Meanwhile, 30% of ammonia solution was used to adjust the pH value of the mixture to 10. The resulting mixture was mixed for 2 hours and then filtered. The resulting filtration cake was washed with 100 ml of deionized water, and then dried at 120° C. to form 20 g of a gold catalyst semi-product (abbreviated as 2% Au/Co(OH)2) having a carrier of Co(OH)2. A gold catalyst was obtained by calcining 1 g of the gold catalyst semi-product at 200° C. for 4 hours. The CO oxidation performance of said gold catalyst to a CO-containing air is shown in Table 5.

TABLE 5
		Space	Inlet	Inlet CO	CO
	Air flow	velocity	temp.	conc.	conversion
Example	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
19	3,500	210,000	25	2,500	100
20	2,000	120,000	31	10,000	100

EXAMPLES 21˜24

[0058] 1.2 g of HAuCl4 was dissolved in 500 ml of deionized water. The resulting solution was dripped into a dispersion formed by 20 g of the Fe(OH)3 carrier prepared in Preparation Example 3 and 100 ml of water. Meanwhile, 30% of ammonia solution was used to adjust the pH value of the mixture to 10. The resulting mixture was mixed for 2 hours and then filtered. The resulting filtration cake was washed with 100 ml of deionized water for three times, and then dried at 120° C. to form 20 g of a gold catalyst semi-product (abbreviated as 3% Au/Fe(OH)3) having a carrier of Fe(OH)3. A gold catalyst was obtained by calcining 1 g of the gold catalyst semi-product at 200° C. for 2 hours. Analysis showed that said gold catalyst had a composition of Fe(OH)0.5-1.2O1.25-0.9. The CO oxidation performance of said gold catalyst to a CO-containing air is shown in Table 6.

TABLE 6
		Space		Inlet CO	CO
	Air flow	velocity	Inlet temp.	conc.	conversion
Example	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
21	600	36,000	26.0	3,904	100
22	1,200	72,000	26.2	2,028	100
23	1,800	108,000	26.5	1,788	100
24	2,400	144,000	26.7	13,544	100

EXAMPLES 25˜26

[0059] A test for resistance to saturated moisture was performed on the catalysts synthesized in Examples 21˜24. A test CO/air mixture was introduced into an aeration bottle to saturate the mixture gas with moisture, and then the moisture saturated mixture gas was passed through a catalyst bed. The results are shown in Table 7.

TABLE 7
	Reaction		Space	Inlet	Inlet CO	CO
Exam-	time	Air flow	velocity	temp.	conc.	conversion
ple	(min)	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
25	1	650	39,000	28.3	3,904	100
26	4380	650	39,000	31.7	3,904	100

EXAMPLES 27˜33

[0060] A test of the influence of carbon dioxide on the catalysts synthesized in Examples 21˜24 was carried out. Carbon dioxide at a concentration of 0˜44% was introduced into a mixture of CO/air, and the resulting mixture was passed through a catalyst bed. The results are shown in Table 8.

TABLE 8
			Space	Inlet	Inlet CO	CO
Exam-	CO2 conc.	Air flow	velocity	temp.	conc.	conversion
ple	(%)	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
27	0	1132	67,939	18.4	2,234	100
28	1.57	658	39,497	18.7	3,843	100
29	3.83	674	40,425	18.6	3,754	100
30	7.37	700	41,973	18.7	3,616	100
31	13.73	751	45,067	18.5	3,368	100
32	28.47	906	54,352	18.5	2,792	100
33	44.02	1158	69,454	18.5	2,185	99.95

EXAMPLE 34

[0061] A test on the lifetime of the catalysts synthesized in Examples 21˜24 as carried out. A mixture of 9,316 ppm CO/air was introduced through a catalyst bed. After 8 hours of reaction, the system was shut down to its original state. The above test was repeated additional three times. The results of four tests are shown in Table 9.

TABLE 9
		Space	Inlet	Inlet CO	CO
Number	Air flow	velocity	temp.	conc.	conversion
of tests*	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
1	1318	79,080	18.4	9,316	100
2	1318	79,080	18.7	9,316	100
3	1318	79,080	18.6	9,316	100
4	1318	79,080	18.7	9,316	100
*Each test was carried out continuously for 8 hours.

EXAMPLE 35

[0062] A test of the influence of saturated moisture on the lifetime of the catalyst synthesized in Examples 21˜24 was carried out. A test CO/air mixture was introduced into an aeration bottle to saturate the mixture gas with moisture, and then the moisture saturated mixture gas was passed through a catalyst bed. The result is shown in Table 10.

TABLE 10
Ex-	Reaction		Space	Inlet	Inlet CO	CO
am-	time	Air flow	velocity	temp.	conc.	conversion
ple	(min)	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
35	6,000	650	39,900	17.2	2,018	100

EXAMPLES 36˜39

[0063] 1.2 g of HAuCl4 was dissolved in 100 ml of deionized water. The resulting solution was dripped into a dispersion formed by 20 g of the Ti(OH)4 carrier prepared in Preparation Example 1 and 100 ml of water. After completion of the addition, 70% of nitric acid aqueous solution was used to adjust the pH value of the mixture to 2. The reaction was carried out at 60° C. for 6 hours. The reaction mixture was filtered. The resulting filtration cake was washed with 100 ml of deionized water three times, and then dried at 120° C. to form 20 g of a gold catalyst semi-pruduct having a carrier of Ti(OH)0.5-1O1.75-1.5. A gold catalyst was obtained by calcining 1 g of the gold catalyst semi-product at 200° C. for 2 hours. The CO oxidation performance of said gold catalyst to CO-containing air is shown in Table 11.

TABLE 11
		Space	Inlet	Inlet CO
	Air flow	velocity	temp.	conc.	CO conversion
Example	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
36	5,459	327,500	30.0	2,500	99.96
37	5,709	342,500	30.0	5,000	99.96
38	5,984	359,000	30.5	7,500	100
39	6,290	377,000	30.6	10,000	100

EXAMPLES 40˜44

[0064] 20 g of the catalysts synthesized in Examples 21˜24 were separately loaded in a round canister (diameter*height=7.25*0.48 cm). The CO oxidation performance of said loaded catalyst to CO-containing air is

	TABLE 12
			Inlet CO	CO
		Air flow	concentration	conversion
	Example	(ml/min)	(ppm)	(%)
	40	30,255	501	100.00
	41	31,020	1956	99.08
	42	31,530	2887	98.65
	43	32,755	5005	97.32
	44	34,336	7514	95.86

EXAMPLE 45

[0065] 20 g of the catalyst synthesized in Examples 21˜24 was subjected to the following activity tests:

[0066] Treatment of waste gas having a high concentration of hydrogen at room temperature

[0067] For a gas having a composition of: H2 10%, and O2/H2 mole ratio: 1.4415, the conversion of hydrogen to water is 100% at GHSV=12,600 hr−1.

[0068] Treatment of ozone in air at room temperature

[0069] For air containing 20˜70 ppm O3, the decomposition of O3 is 100% at GHSV=20,000 hr−1.

Preparation Example 4

[0070] 3.6 g of gold was dissolved in 67 ml of an aqueous solution (50 ml of 12 N HCl+17 ml of 70% HNO3). The solution was diluted with water to form 500 ml of an acid aqueous solution containing gold ions.

EXAMPLES 46˜49

[0071] 500 ml of the acid aqueous solution containing gold ions prepared in Preparation Example 4 was dripped into a dispersion formed by 100 g of the Fe(OH)3 carrier prepared in Preparation Example 3 and 500 ml of water. Meanwhile, 30% of ammonia solution was used to adjust the pH value of the mixture to 10. The mixture was mixed for 2 hours. The resulting mixture was filtered. The resulting filtration cake was washed with 500 ml of deionized water, and then dried at 120° C. to form 100 g of a gold catalyst semi-product (abbreviated as 3.6% Au/Fe(OH)3) having a carrier of Fe(OH)3. A gold catalyst was obtained by calcining 1 g of the catalyst semi-product at 180° C. for 2 hours. The CO oxidation performance of said gold catalyst to a CO-containing air is shown in Table 13.

TABLE 13
		Space		Inlet CO	CO
	Air flow	velocity	Inlet temp.	concentration	conversion
Example	(ml/min)	(1/hr)	(° C.)	(ppm)	(%)
46	4,620	277,200	21.9	2,500	100
47	4,840	290,400	21.9	5,000	100
48	5,060	303,600	22.3	7,500	100
49	5,320	319,200	23.4	10,000	100

EXAMPLE 50˜59

[0072] 0.2 of the catalyst synthesized in Examples 46˜49 was subjected to the following activity tests. The CO oxidation performance of said gold catalyst to a CO-containing air at room temperature is shown in Table 14.

TABLE 14
		Space	Inlet CO	CO
	Air flow	velocity	concentration	conversion
Example	(ml/min)	(1/hr)	(ppm)	(%)
50	2,148	644,300	1,000	100
51	2,302	690,600	1,000	99.80
52	2,454	735,600	2,500	100
53	2,762	827,700	2,500	99.96
54	1,840	549,900	5,000	100
55	2,148	642,000	5,000	99.96
56	1,432	429,100	7,500	100
57	1,656	490,200	7,500	99.93
58	1,534	457,400	10,000	100
59	1,686	502,800	10,000	99.96

Claims

1. a nano-gold catalyst comprising a solid carrier and gold deposited on the carrier, wherein the deposited gold has a size less than 10 nm, and the carrier comprises a mixed metal hydroxide and oxide having the following formula:

2. The nano-gold metal catalyst as claimed in claim 1, wherein said carrier is composed of said mixture of metal hydroxide oxide, and said carrier is particulate having a specific surface area of 150-300 m2/g.

3. The nano-gold metal catalyst as claimed in claim 1, wherein q is 0.5-1.5 and M is Ti, Fe(III) or Co.

4. The nano-gold metal catalyst as claimed in claim 1, wherein said deposited gold has a particle size smaller than 5 nm.

5. A process for preparing a nano-gold catalyst, which comprises the following steps: a) preparing a M(OH)x solid carrier with a specific surface area larger than 150 m2/g, wherein M is Ti, Fe, Co, Zr, or Ni, and x is 2-4; b) preparing an acidic gold precursor solution; c) mixing said M(OH)x solid carrier with said acidic gold precursor solution, and controlling pH value of the resulting mixture to be basic, so that gold is deposited on said M(OH)x solid carrier to form a M(OH)x carrier deposited with gold, abbreviated as Au/M(OH)x; and d) partially oxidizing said Au/M(OH)x to form a nano-gold catalyst comprising a mixed metal hydroxide and oxide carrier having the following formula and gold deposited on said carrier: M(OH)qOy wherein M is defined as above; q is 0.1-1.5; and q+2y=z, wherein z is the valence of M.

6. The process as claimed in claim 5, wherein said partial oxidation in step d) comprises: d1) performing a solid/liquid separation on the mixture resulting from step c) and drying the resulting Au/M(OH)x; and d2) calcining the dried Au/M(OH)x.

7. The process as claimed in claim 6, wherein said calcining in step d2) is carried out at 100° C.-500° C. for 0.5-4 hours.

8. The process as claimed in claim 7, wherein said calcining in step d2) is carried out at 1 50-250° C. for 2 hours.

9. The process as claimed in claim 5, wherein said partial oxidation in step d) comprises: d0) adding an oxidation agent into the mixture resulting from step c) to perform an oxidation reaction; and d1′) performing a solid/liquid separation on the reaction mixture resulting from step d0), and drying the resulting solid.

10. The process as claimed in claim 9, wherein said partial oxidation in step d) further comprises: d2) calcining the dried solid obtained from step d1′).

11. The process as claimed in claim 10, wherein said oxidation agent in step d0) is a strong acid such that, after the addition of said strong acid, the resulting reaction mixture has a pH value of 0.5-4.

12. The process as claimed in claim 11, wherein said oxidation reaction in step d0) is carried out at 40° C.-100° C. for 1-8 hours.

13. The process as claimed in claim 11, wherein said strong acid is nitric acid.

14. The process as claimed in claim 10, wherein said solid carrier in step a) is Ti(OH)4.

15. The process as claimed in claim 5, wherein said step b) comprises dissolving HAuCl4 or AuCl3 in a solvent.

16. The process as claimed in claim 5, wherein said step b) comprises dissolving solid gold in a mixed solvent of HCl and HNO3.

17. The process as claimed in claim 15, wherein said solvent is ethanol or water.

18. The process as claimed in claim 16, wherein said mixed solvent is a mixture of 12 N HCl aqueous solution and 70% HNO3 aqueous solution with a volume ratio of 2 N HCl aqueous solution: 70% HNO3 aqueous solution=50:17.

19. The process as claimed in claim 5, wherein said pH value of the resulting mixture to be basic in step c) is 7.1-12.

20. The process as claimed in claim 5, wherein said mixing in step c) comprises: dispersing said solid carrier in water; dripping said acidic gold precursor solution into the resulting solid carrier aqueous dispersion while stirring; and dripping an alkaline solution into the aqueous dispersion concurrently with said acidic gold precursor solution, if said aqueous dispersion is acidic, and no need of adding an alkaline solution, if said aqueous dispersion is basic.

21. The process as claimed in claim 20, wherein said solid carrier aqueous dispersion has a pH value of 8-12, and said acidic gold precursor solution has a pH value of 0-4.

22. The process as claimed in claim 20, wherein said solid carrier in step a) is Fe(OH)3, and NH4(OH) is used as said alkaline solution to be dripped into said aqueous dispersion.

23. The process as claimed in claim 20, wherein said solid carrier in step a) is Co(OH)2, and NH4(OH) is used as said alkaline solution to be dripped into said aqueous dispersion.

24. The process as claimed in claim 20, wherein said solid carrier in step a) is Ti(OH)4, and no alkaline solution is dripped into said aqueous dispersion.

25. The process as claimed in claim 5, wherein said solid carrier in step a) has a particle size of 10-50 nm, and has a specific surface area of 150-300 m2/g.

26. The process as claimed in claim 5, wherein q is 0.5-1.5 and M is Ti, Fe(III) or Co.

27. The process as claimed in claim 5, wherein said nano-gold catalyst formed in step d) comprises gold with a particle size smaller than 5 nm.