Patent Application
20110129536
The present invention relates to nanocomposite materials formed by metallic nanoparticles stabilized in a matrix of branched cationic polysaccharides, preparation and use thereof for applications in biomedical, pharmaceutical and food field.
The preparation of metallic nanoparticles is a research area of high nano-technological interest; indeed, many metals have particular optical, antimicrobial and catalytic properties typically associated with the nano-scale. In particular, the broad spectrum antimicrobial activity of metals, such as for example silver, has a remarkable application interest. On the other hand, bacterial, fungal and viral infections represent a serious problem in many situations and thus the implementation of products with a broad antimicrobial spectrum is a particularly felt need. In fact, the use of metals such as silver, gold, copper, zinc and nickel in antimicrobial material field is having a great influence on the market, especially for treating topic tissue lesions, so that, for example, companies such as Johnson&Johnson® and Convatec® have recently marketed medications which are based on antibacterial properties of silver nanoparticles.
Nanoparticles are generally obtained from metal salt solutions in the presence of a reducing agent and a stabilizing agent, which serves to prevent nanoparticles from aggregating. In order to stabilize the nanoparticles, appropriate diluted polymeric solutions are widely used, which allow to obtain nanocomposite systems in which the metallic particles result to be homogeneously dispersed. For the above-mentioned applications, solutions of polyelectrolytes, such as polyphosphate, polyacrylate, poly(vinyl sulphate), poly(allylamine) (Henglein, A., J. Phys. Chem. 1993, 97 (21), 5457-5471), poly(ethylenimine) (Kuo, P. L.; Chen, W. F. J. Phys. Chem. B 2003, 107 (41), 11267-11272; Dai et al. (Nano Lett. 2002, 2 (5), 497-501) were particularly effective.
In general, the components required to obtain the formation of metallic nanoparticles are: a suitable metal salt, a reducing agent and a polymer acting as a stabilizer for the colloidal suspension.
US 2007/00036031 (Karandikar et al.) discloses methods for the formation of silver nanoparticles in the presence of a solvent, a stabilizing agent, a surfactant, a reducing agent and heating. Among the stabilizing agents, polymers such as polyacrylamide and polysorbate 20 are mentioned.
In patent WO2007/147094A2 (Sambhy V. et al.) nanocomposite systems in synthetic cationic polymeric matrices, characterized by a ternary or quaternary nitrogen atom, in which the nanoparticles-stabilizing polymer is a poly(4-vinyl pyridine) derivative and silver bromide is employed to form these silver nanoparticles, are described.
Patent WO2007/017901A2 (Omray P. et al.) reports formulations of silver nanoparticles dispersed, for example, by using polysorbate, propylene glycol, and propyl gallate.
In patent WO2007/096606A1 (Crowther N. et al.) methods for releasing metallic nanoparticles, prepared in the presence of stabilizing polymers for antimicrobial applications, are described. Among the mentioned polymers there are: poly(methacrylic acid), polyimides, poly(vinylalcohol) and copolymers thereof.
Patent WO2007/001453 (Yacaman M. et al.) reports the silver nanoparticle synthesis in the presence of polyols and polymers by using glycerin or ethylene glycol both as reducing agent and as nanostructure solvent and by using poly(vinylpyrrolidone) as coating agent for nanoparticles. It is noted that the chemical reduction mechanism of silver ions is based on the oxidation of hydroxyl groups present in polyols and breakdown of C—C bonds.
For applications in the biomedical field, systems based on polysaccharides are particularly interesting because these polymers are generally biocompatible and therefore suitable for applications that involve a direct contact with biological tissues. Among the natural polysaccharides, one of the more studied and commercially employed is chitosan. This is a basic polysaccharide, with a molecular weight from 50 to 1'500 kDa, consisting of a straight chain of D-glucosamine (GlcNH2) residues bonded by β1→4 bonds with interspersed residual N-acetyl-glucosamine units from the incomplete chitin de-acetylation. This polysaccharide is usually insoluble in neutral or basic aqueous solutions; in acidic solutions with pH equal or less than 5, the free amino group is protonated, thus making the polymer soluble. This polymer is already widely employed in medical field as it exhibits a low immunogenic, pathologic or infective response (Suh Francis J. K., Matthew H. W. T. Biomaterials, 2000, 21, 2589-2598; Miyazaki S. et al. Chem. Pharm. Bull., 1981, 29, 3067-3069). Chitosan has all ideal features to be employed as a biomaterial due to its physical-chemical properties, such as high cationic charge density in acidic solution, its high processability and the ability to give rise to porous structures where, for example, cells may be implanted. Indeed, many uses of chitosan, both in biomedical and alimentary field are known. Due to these properties, both chitosan and its derivatives were also used in order to stabilize nanoparticles.
In patent WO2007/025917A1 (Schmid H. et al.) silver nanoparticle preparations in the presence of chitosan as well as chitosan derivatives and salts such as carboxymethylchitosan, chitosan acetate and chitosan lactate, are mentioned. In the patent US 2008/0147019 (Song Xuedong), commercially available preformed metal nanoparticles are added to chitosan salts and chitosan derivatives, but not branched derivatives of saccharidic nature; these nanoparticles require further oxidation to provide for an antibacterial activity since the silver ions (Ag+) are pointed as the only antibacterial agent.
In the patent WO2008/076339 (Schauer C et al), commercially available metal nanoparticles are included in water-insoluble cross-linked chitosan based materials. The reticulated chitosans are used to prepare multilayer films to support nanoparticles which are used as coloring agents and as sensors for detecting contaminants in water.
Several recent researches have focused on improving methods for enhancing the biological effects of chitosan. In particular, most efforts were directed to increase the cationic feature of the polymer or modify the chemical features and bioavailability thereof by means of (bio)chemical modifications.
In particular, chitosan modification with saccharidic groups, for example by inserting lactose units by means of a reductive amination reaction resulted, as mentioned in U.S. Pat. No. 4,424,346 (Hall, L. D. and Yalpani, M.), in higher water solubility of chitosan derivatives and it is indeed in these derivatized forms that chitosan acquires the most useful properties for use as a highly biocompatible biomaterial.
It is a first object of the present invention to obtain a nanocomposite material, where metallic nanoparticles are stabilized and size-controlled and the properties of which are particularly suitable for applications in biomedical and optical (biosensors) field.
It is a further object that such a nanocomposite is obtainable by means of a non-complex and economically advantageous chemical approach, and in particular by colloidal solutions in which metallic nanoparticles are stabilized by appropriate polysaccharidic solutions.
It is a further object to improve these systems by employing readily commercially available polysaccharides and avoiding these polysaccharides from being subjected to chemical manipulations, as well as avoiding the need for complex preparation manipulations of these systems.
It is a further object to obtain systems that are totally soluble in aqueous systems in the conditions of neutral pH and substantial ionic strength that are required in biomedical applications.
In order to achieve the above-mentioned objects, the inventors developed suitable soluble polysaccharidic systems based on branched cationic polysaccharides which allow to obtain stable, size-controlled metallic nanoparticles. The procedures are based on mixing aqueous polymeric solutions and aqueous solutions of metal salts in the presence or absence of exogenous reducing agents. The mixing procedures can be conveniently carried out in aqueous systems at neutral pH and does not require heating, since it can be easily carried out at room temperature.
Therefore, in a first aspect, an object of the present invention is given by nanocomposite materials characterized in that they comprise a polymeric matrix consisting of branched cationic polysaccharides and metallic nanoparticles dispersed in such a polymeric matrix.
Preferred cationic polysaccharides are branched derivatives of chitosan, wherein the D-glucosamine units forming the linear chitosan chain bind, by means of the functional group —NH— on carbon atom C2, the alditolic or aldonic polyols residues equal to or different from one another represented by the general formula (I):
where:
On the other hand, the metals of nanoparticles are preferentially silver, gold, platinum, palladium, copper, zinc or nickel and mixtures thereof.
Nanocomposite materials according to the invention can be prepared under appropriate conditions with aqueous solutions of these polysaccharides and metal salts in the presence or absence of exogenous reducing agents.
Therefore, according to another aspect, it is an object of the invention a method of preparing these nanocomposite materials comprising the steps of:
A reducing agent is optionally added to the obtained colloidal solutions. According to a further aspect, the use of these nanocomposite materials in biomedical, pharmaceutical and alimentary field, for example as antimicrobial agents, or in molecular biosensors, is another object of the invention.
Example 5); 0.1% w/v Chitlac/0.5 mM AgNO3 (close-dot line
Example 4); 0.2% w/v Chitlac/0.5 mM AgNO3 (stroke-dot line
Example 6); 0.4% w/v Chitlac/0.5 mM AgNO3 (stroke-dot-dot line
Example 8). According to the reaction stoichiometry, in each sample the AgNO3/C6H8O6 ratio is 2. The measurement was carried out by means of a CaryE4 UV-visible spectrophotometer at a temperature of 25° C.
), 11 (10 mM AgNO3, line
), 25 (0.2% w/v Chitlac, 1 mM AgNO3, line - - -). The measurements were carried out as previously described in
Colloidal solution (or colloid): it means a system in which particles with size range from 1 to 1'000 nm are dispersed in a continuous solvent medium.
Nanocomposite: it means a system consisting of particles with nanometric sizes (fillers) within a macroscopic material (matrix). In the present description of the invention, the term “nanocomposite” is intended to mean a material in which metallic nanoparticles are dispersed in a polysaccharidic matrix. In particular it means a material in which the metallic nanoparticles are substantially formed in the polysaccharidic matrix by reduction of the corresponding salts, thus mostly have a zero charge, but without excluding the presence of clusters of few atoms with a ionic character (e.g. Ag4+). Thus, hereinafter the nanocomposite according to the invention can be also indicated as “metal-based nanocomposite” besides simply “nanocomposite”.
The objects and advantages of the nanocomposite materials comprising metallic nanoparticles interdispersed in a branched basic polysaccharide matrix object of the present invention, will be better understood throughout the following detailed description where, by way of non-limiting example, some examples of preparing nanocomposites according to the invention and the physical-chemical characterization thereof will be described in addition to the biological tests for evaluating their antibacterial activity.
In a polymeric matrix consisting of branched cationic polysaccharides due to the presence of primary and secondary nitrogen atoms, the nanocomposite materials object of the present invention comprise metallic nanoparticles homogeneously and stably dispersed in such a polymeric matrix.
For the purposes of the present invention, preferred cationic polysaccharides are alditolic or aldonic branched derivatives of chitosan, wherein D-glucosamine units forming the linear chitosan chain bind, by means of the functional group —NH— on carbon atom C2, mono- or oligo-saccharidic alditolic or aldonic polyols residues, equal to or different from each other, and represented by the previously reported general formula (I), where R can be —CH2— or —CO— and R1 can be hydrogen or a monosaccharide, preferably selected from the group consisting of galactose, glucose, mannose, N-acetyl glucosamine, and N-acetyl galactosamine, or an oligosaccharide, preferably comprising 2 glycosidic units, and R2 can be —OH or —NHCOCH3. Hereinafter these derivatives are also briefly referred to as alditolic or aldonic, mono- or oligo-saccharidic derivatives of chitosan or, briefly, mono- or oligo-saccharidic derivatives of chitosan.
By way of representation, D-Glucosamine units substituted with mono- or oligosaccharidic residues in the chitosan derivatives object of the invention can be represented by the general formula (II), where “n” refers to the overall number of D-Glucosamine units constituting a linear chitosan chain:
In the previously cited patent WO2007/025917A1 (Schmid H. et al.), silver nanoparticle preparations in the presence of chitosan derivatives and salts such as carboxymethylchitosan, chitosan acetate and chitosan lactate, are mentioned. Unlike the above-cited patent, in the present case derivatization is carried out by mono- or oligosaccharidic structures which, through a reductive amination reaction, lead to the insertion of side branches linked to the polymeric backbone by means of secondary amino groups. This allows i) the amino groups to be still available for metal coordination and ii) the overall polysaccharide charge not to be substantially altered.
Indeed, the polymeric matrix consists of branched derivatives of chitosan which bind, by means of the amino group, the aldonic or alditolic derivatives of mono- or oligosaccharides of general formula (I). These mono- or oligo-saccharides of general formula (I) preferably comprise from 1 to 3 glycosidic units and, according to a more preferred aspect, these are residues of oligosaccharides comprising from 2 to 3 glycosidic units and still more preferably, with reference to the different meanings of R, R1 and R2, the same are selected from the group consisting of residues of lactose, cellobiose, cellotriose, maltose, maltotriose, chitobiose, chitotriose, mannobiose as well as the corresponding aldonic acids thereof. For the purposes of the present invention, the most preferred oligosaccharidic derivative of chitosan is the derivative with lactose (hereinafter also referred to as Chitlac; CAS registry number 85941-43-1).
Furthermore, for the purposes of the present invention, the chemical substitution degree of chitosan amino groups with these mono- or oligo-saccharides is at least 20%. Preferably, the substitution degree of chitosan amino groups with mono- or oligo-saccharides is in the range from 50% to 80%, and more preferably is 70%. The average molecular weight (hereinafter referred to as MW) of the chitosan useable for obtaining the mentioned oligosaccharidic derivatives can be up to 1'500 kDa and preferably in the range from 400 kDa to 700 kDa.
The metallic nanoparticles incorporated into the polymeric matrix consisting of these branched cationic polysaccharide derivatives are of metals preferentially selected from silver, gold, platinum, palladium, copper, zinc, nickel and mixtures thereof. The nanoparticles included into the polymeric matrix consisting of oligosaccharidic derivatives of chitosan have a size in the range from 5 nm to 150 nm, and in particular a controlled average metallic nanoparticle size between 30 and 50 nm. Essential features of these nanoparticles, as will be apparent from the detailed description of the invention below, are that these nanoparticles are mostly metals in their reduced form, moreover without excluding the residual presence of clusters made of few atoms with a ionic character, and that, in their dispersion/stabilization in the polysaccharidic matrix, the oligosaccharidic side chains close to the amino groups of chitosan itself are involved.
Without being bound to the latter, the preferred ratios between matrix polysaccharides and metals are referred to nanocomposites in the form of colloidal solutions, although these metal-based nanocomposite materials can also be in the form of dehydrated films or powder and even dialyzed in order to remove residual counter-ions from the preparation of the materials themselves. In the nanocomposites according to the invention in form of aqueous colloidal solutions, the ratio of the polysaccharide concentration (expressed as % w/v) over the concentration of the starting metal salt (expressed as molarity) is from 0.0025 to 20 and preferably is 0.2.
Therefore, the silver mass, expressed as mg, which can be incorporated per gram of polysaccharide, can be from 3'000 mg/g to 0.3 mg/g and preferentially is 50 mg of silver incorporated per gram of polysaccharide.
For the pursued objects, the inventor addressed the aspect related to preparation and characterization of one polysaccharides-based system in which properties related to nanometric metal size (antimicrobial, optical, catalytic and other peculiar properties of the metals themselves) of metallic nanoparticles contained in the nanocomposites object of the invention, are exploited. These aspects are reported in detail hereinafter.
The process of preparing these oligosaccharidic derivatives of chitosan is that known and described in U.S. Pat. No. 4,424,346 (Hall, L. D. and Yalpani, M.) and includes treating a solution of chitosan with acetic acid (pH 4.5) in methanol with the selected mono- or oligo-saccharide in the presence of sodium cyanoborohydride. The interaction between the amino groups of chitosan and the aldehydic group of the mono- or oligo-saccharide leads to formation of an instable intermediate referred to as Schiff's base. In the presence of borohydride, the Schiff's base is reduced thus leading to formation of a stable secondary amine. The resulting branched polysaccharide is the oligosaccharidic derivative of chitosan and is the previously mentioned Chitlac, for example, when the oligosaccharide is lactose. In case of derivatives with aldonic acids of mono- or oligo-saccharides, the reaction is carried out in the presence of an suitable activator, as a carbo-di-imide, and leads to formation of an amide.
The nanoparticles to be incorporated into the polymeric matrix can be prepared either in the presence or absence of reducing agents.
In the first case, the nanoparticles are obtained upon reduction of metal ions with suitable reducing agents in aqueous solutions of branched polysaccharides consisting of the previously mentioned mono- or oligo-saccharidic alditolic or aldonic branched derivatives of chitosan according to the following procedure: aqueous solutions of these chitosan derivatives are prepared at different concentrations up to 2% (w/v), preferably in the range from 0.05% (w/v) to 1% (w/v) and more preferably are 0.2% (w/v). The polysaccharidic solutions are then mixed with solutions of metal salts selected from silver, gold, platinum, palladium, copper, zinc, nickel, preferably selected from chlorides, perchlorates and nitrates (e.g. AgNO3, HAuCl4, CuSO4, ZnCl2, NiCl2), so as to obtain final concentrations in the range from 0.1 mM to 20 mM, more preferably in the range 1 mM-14 mM and still more preferably of 1 mM. Suitable known reducing agents, preferably selected from ascorbic acid, sodium citrate, sodium borohydride and sodium cyanoborohydride, can optionally be added to the solutions to obtain nanoparticles in the metallic state. The reducing agent is added at concentrations from 0.05 mM to 10 mM and preferably the concentration is 0.5 mM.
However, it was found that unlikely for other polymeric systems, the nanocomposites according to the invention can also be prepared in the absence of reducing agents, since the mono- or oligo-saccharidic side chains according to the general formula (I) act as reducing agent for metal ions per se, and allow to form nanoparticles dispersed in the polymeric matrix. In this case, the metallic nanoparticles are obtainable by simply mixing the solutions of chitosan derivatives with salt solutions of the selected metal at appropriate concentrations. Also in this case, the polysaccharides and metal salt concentrations are as previously reported.
As will be readily apparent from the results obtained by the characterizations of metal-based nanocomposite materials object of the invention, hereinafter reported, all the conditions being equal, the mono- or oligo-saccharidic derivatives of chitosan, and in particular Chitlac, surprisingly prove to be more adapted to form metallic nanoparticles as compared to others polysaccharides, such as for example chitosan, as proven by the intensity and shape of the UV-Vis absorption spectra and by the spectrophotometric study assisted by transmission electron microscopy (TEM) investigations. These studies allow to demonstrate that, in the presence of the mono- or oligo-saccharidic derivatives of chitosan and in particular Chitlac, the metallic nanoparticles are more uniform in size and better dispersed due to interactions with the polymeric chains preventing the aggregation thereof in comparison with those prepared with unsubstituted chitosan. TEM microphotographs further allowed to carry out an analysis of the dimensional distribution of nanoparticles, which is highly uniform with an average size smaller than 50 nm.
It was also surprisingly found that it is possible to obtain metallic nanoparticles even in the absence of an exogenous reducing agent. A system has been discovered, in which metallic nanoparticles, which are homogeneously dispersed in the polymeric matrix, are obtained by using the reducing ability typical of the side substituents of polysaccharide, thus in the absence of any exogenous reducing agent. This second method of preparing was also characterized by means of UV-Vis spectroscopy and TEM microscopy. Plasmonic peaks and TEM images confirm the successful formation of metallic nanoparticles being roundish in shape and having an average size smaller than 10 nm.
This methodological approach is particularly advantageous because a single component of the system simultaneously offers reducing, dispersion and nanoparticle stabilization abilities.
In addition, the further biological characterizations of the metal-based nanocomposite according to the invention have shown that the nanocomposite of the invention still exhibit the antimicrobial activity of the incorporated metal and this effect is very valuable for application purposes in biomedical and pharmaceutical field. Indeed, the use of metals as silver, gold, copper, zinc and nickel in antimicrobial material field is of value, especially for the treatment of topic tissue wounds for both humans and animals. The nanocomposite object of the present could be employed as such or in combination with other diluents and/or pharmaceutically acceptable excipients. In particular, these materials can be mixed with other not-gellifying, neutral or anionic polysaccharides selected from the group consisting of dextran, hyaluronic acid, carboxymethylcellulose, galactomannans in either diluted or concentrated aqueous solution obtaining particular viscoelastic features, for preparing in combination with suitable excipients and/or diluents compositions with antimicrobial activity useable for treating infections of either intact or injured skin, mucous membranes and epithelial tissues of different anatomical localizations. These materials even in combination with other not-gellifying, neutral or anionic polysaccharides as previously mentioned can also be applied in the development of medicated devices such as gauzes, bandages, patches with broad-spectrum antimicrobial activity to be employed in the same above-mentioned therapeutic field.
Furthermore, the nanocomposites according to the invention can be used as polysaccharidic grafts (or polymer grafts)—chelating metallic nanoparticles with antimicrobial activity—on activated surfaces made of polymeric material for containers in uses in pharmaceutical and alimentary fields. The expected advantage could consist in substituting the current sterilization procedures (e.g. dry-heating) which sometimes produce even considerable lacks of homogeneity in the final sterility degree of the empty container before filling. Furthermore, coating polymeric materials can lead to obtain systems provided with antimicrobial activity for applications in the biomedical field.
Again, the metal based nanocomposite materials according to the invention can be used in polymer blends with other polysaccharides (e.g. pullulan) to obtain films for “antimicrobial” packages, in particular in the alimentary field.
A strong increase in the Raman spectroscopic signal of the polysaccharide was also found, attributable to the presence of metallic nanoparticles, which therefore have optimal dimensions and distribution to exploit SERS (Surface Enhanced Raman Spectroscopy) effect on which the operation of several molecular biosensors is based. Indeed, the Raman spectrum of a polysaccharide solution shows no experimentally detectable peak, while a polysaccharide solution (even more diluted) in the presence of metallic nanoparticles provides an intense and defined Raman spectrum, thus proving the increase of the signal caused by nanoparticles (SERS effect). In these applications, metal-based nanocomposite according to the invention can be used as probes/markers provided with molecular functionality and therefore are considered suitable for applications of optical “bioimaging”, being the nanoparticles entrapped in the polymeric matrix formed by the branched cationic polysaccharides are alditolic or aldonic derivatives of chitosan, detectable by means of TEM microscopy, confocal and Raman techniques. Therefore, metal-based nanocomposites according to the invention can be employed in developing new sensors for analyses of biomolecules and cells by exploiting the presence of specific biochemical signals recognized by different cellular types on the oligosaccharidic derivatives of chitosan (Donati, I. et al., Biomaterials 26, 2005, 987-998).
Using branched polysaccharides to form metallic nanoparticles according to the present invention introduces the following advantages:
Some non-limiting examples of preparing the nanocomposites according to the invention, on which the physical-chemical characterizations and biological tests were performed to evaluate their antibacterial activity are described hereinafter for illustrative purpose.
1a) Chitosan (1.5 g, acetylation degree 11%) is dissolved into 110 mL of a methanol solution (55 mL) and 1% w/v acetic acid buffer, pH 4.5 (55 mL). 60 mL of a methanol solution (30 mL) and 1% w/v acetic acid buffer, pH 4.5 (30 mL) containing lactose (2.2 g) and sodium cyanoborohydride (900 mg) are added. The mixture is left to stir for 24 hours, transferred to dialysis tubes (cut off 12'000 Da) and dialyzed against NaCl 0.1 M (2 changes) and against deionized water until a conductivity of 4 μS at 4° C. is achieved. Ultimately, the solution is filtered on Millipore 0.45 μm filters and freeze-dried.
1b) Chitosan (1.5 g, acetylation degree 11%) is dissolved in 110 mL of a methanol solution (55 mL) and 1% w/v acetic acid buffer, pH 4.5 (55 mL). 60 mL of a methanol solution (30 mL) and 1% w/v acetic acid buffer, pH 4.5 (30 mL) containing cellobiose (2.2 g) and sodium cyanoborohydride (900 mg) are added. The mixture is left to stir for 24 hours, transferred to dialysis tubes (cut off 12'000 Da) and dialyzed against NaCl 0.1 M (2 changes) and against deionized water until a conductivity of 4 μS at 4° C. is achieved. Ultimately, the solution is filtered on Millipore 0.45 μm filters and freeze-dried.
Nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitlac solution is according to the following procedure: an aqueous Chitlac solution at a concentration of 0.05% (w/v) is prepared. The Chitlac solution is then mixed with silver nitrate solutions so as to obtain a final concentration of AgNO3 of 0.5 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.25 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 0.05% (w/v) is prepared. The Chitlac solutions then mixed with silver nitrate solutions so as to obtain a final concentration of AgNO3 of 1 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.5 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 0.1% (w/v) so as order to obtain a final concentration of AgNO3 of 0.5 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.25 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 0.1% (w/v) is prepared. The Chitlac solution is then mixed with silver nitrate solutions so as to obtain a final concentration of AgNO3 of 1 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.5 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 0.2% (w/v) is prepared. The Chitlac solution is then mixed with silver nitrate solutions so as to obtain a final concentration of AgNO3 of 0.5 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.25 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 0.2% (w/v) is prepared. The Chitlac solutions are then mixed with silver nitrate solutions so as to obtain a final concentration of AgNO3 of 1 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.5 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 0.4% (w/v) is prepared. The Chitlac solutions are then mixed with silver nitrate solutions so as to obtain a final concentration of AgNO3 of 0.5 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.25 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 0.4% (w/v) is prepared. The Chitlac solutions are then mixed with silver nitrate solutions so as to obtain a final concentration of AgNO3 of 1 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.5 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitlac according to the following procedure: an aqueous Chitlac solution at a concentration of 0.2% (w/v) is prepared. The Chitlac solution is then mixed with a silver nitrate solution so as to obtain a final concentration of AgNO3 of 5 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitlac according to the following procedure: an aqueous Chitlac solution at a concentration of 0.2% (w/v) is prepared. The Chitlac solution is then mixed with a silver nitrate solution so as to obtain a final concentration of AgNO3 of 10 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitlac according to the following procedure: an aqueous Chitlac solution at a concentration of 0.2% (w/v) is prepared. The Chitlac solution is then mixed with a silver nitrate solution so as to obtain a final concentration of AgNO3 of 14 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitlac according to the following procedure: an aqueous Chitlac solution at concentration of 0.4% (w/v) is prepared. The Chitlac solution is then mixed with a silver nitrate solution so as to obtain a final concentration of AgNO3 of 5 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitlac according to the following procedure: an aqueous Chitlac solution at a concentration of 0.4% (w/v) is prepared. The Chitlac solution is then mixed with a silver nitrate solution so as to obtain a final concentration of AgNO3 of 10 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitlac according to the following procedure: an aqueous Chitlac solution at a concentration of 0.4% (w/v) is prepared. The Chitlac solution is then mixed with a silver nitrate solution so as to obtain a final concentration of AgNO3 of 14 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with sodium borohydride in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 0.2% (w/v) is prepared. The Chitlac solutions are then mixed with tetrachloroauric acid solutions so as to obtain a final concentration of HAuCl4 of 1 mM. Then, a solution of sodium borohydride is added so as to obtain a final concentration of 0.3 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with sodium borohydride in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 0.4% (w/v) is prepared. The Chitlac solutions are then mixed with tetrachloroauric acid solutions so as to obtain a final concentration of HAuCl4 of 1 mM. Then, a solution of sodium borohydride is added so as to obtain a final concentration of 0.3 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitlac according to the following procedure: an aqueous Chitlac solution at a concentration of 0.2% (w/v) is prepared. The Chitlac solution is then mixed with a tetrachloroauric acid solution so as to obtain a final concentration of HAuCl4 of 1 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with sodium borohydride in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 0.2% (w/v) is prepared. The Chitlac solutions are then mixed with copper sulphate solutions so as to obtain a final concentration of CuSO4 of 1 mM. Then, a solution of sodium borohydride is added so as to obtain a final concentration of 0.2 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitcell according to the following procedure: an aqueous Chitcell solution at a concentration of 0.4% (w/v) is prepared. The Chitcell solution is then mixed with a silver nitrate solution so as to obtain a final concentration of AgNO3 of 14 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitgluc according to the following procedure: an aqueous Chitgluc solution at a concentration of 0.4% (w/v) is prepared. The Chitgluc solution is then mixed with a silver nitrate solution so as to obtain a final concentration of AgNO3 of 14 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitosan solutions according to the following procedure: an aqueous Chitosan solution at a concentration of 0.2% (w/v) is prepared. The Chitosan solutions are then mixed with silver nitrate solutions so as to obtain a final concentration of AgNO3 of 1 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.5 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 1% (w/v) is prepared. The Chitlac solutions are then mixed with silver nitrate solutions so as to obtain a final concentration of AgNO3 of 1 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.5 mM.
Nanoparticles are obtained upon reduction of metal ions with ascorbic acid in Chitlac solutions according to the following procedure: an aqueous Chitlac solution at a concentration of 2% (w/v) is prepared. The Chitlac solutions are then mixed with silver nitrate solutions so as to obtain a final concentration of AgNO3 of 1 mM. Then, a solution of ascorbic acid is added so as to obtain a final concentration of 0.5 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitlac according to the following procedure: an aqueous Chitlac solution at a concentration of 0.2% (w/v) is prepared. The Chitlac solution is then mixed with a silver nitrate solution so as to obtain a final concentration of AgNO3 of 1 mM.
Nanocomposites comprising the nanoparticles are obtained upon reduction of metal ions by the polysaccharide Chitlac according to the following procedure: an aqueous Chitlac solution at a concentration of 0.4% (w/v) is prepared. The Chitlac solution is then mixed with a tetrachloroauric acid solution so as to obtain a final concentration of HAuCl4 of 1 mM.
The physical-chemical and biological characterizations of metal-based nanocomposites according to the invention obtained with the chitosan derivative with lactose, Chitlac, with nanoparticles of different metals, and in particular Ag and Au are reported below. Similar results were obtained with all oligosaccharidic derivatives object of the present invention.
In order to check the formation of nanoparticles and their stabilization in the polymeric matrix according to the objects of the invention, the nanocomposite of example 7 was subjected to transmission electron microscopy. As underlined in
The nanoparticle formation is evidenced by the appearance of absorption bands at wavelengths which vary depending on the considered metal, in UV-Vis absorption spectra; these bands are known under the name of surface plasmon resonance bands and are caused by a collective oscillation of free electrons on the nanoparticle surface. In the case of silver, for example, an intense band centered at about 400 nm is observed (
Spectra further confirm that metal particles included in the polymeric matrix mostly have a zero charge; however clusters of few atoms with a ionic character can be present (e.g. Ag4+), as indicated by the shoulder at about 260 nm in the UV absorption spectrum of the systems (
The study of UV-Vis spectrum variations according to the concentrations and reaction times allowed to improve an optimal method of preparing in terms of yield, reproducibility and stability over time.
Similarly, in case of gold, an intense plasmonic band around 530 nm, which proves the successful formation of gold nanoparticles dispersed in Chitlac (
Surprisingly, it was found that, under appropriate conditions, metallic nanoparticles can be formed even in the absence of added reducing agents; for example, in the case of silver, Chitlac is able to reduce Ag+ ions without the aid of ascorbic acid, for example. UV-Vis spectra (
Even in the case of gold, Chitlac free of added reducing agents allows the reduction of Au3+ ions to the metallic state, as proven by UV-Vis spectra in
The shape, distribution and dimensions of nanoparticles formed in the presence and absence of reducing agents were evaluated by means of Transmission electron microscopy (TEM), Nanoparticle Tracking Analysis (Nanosight®) and image analysis techniques. The images related to gold nanoparticles (
This method of preparing without reducing agents was also characterized by means of UV-Vis spectroscopy and TEM microscopy. Plasmonic peaks in
In order to evaluate the antimicrobial activity, nanocomposite systems were tested with different Gram+ and Gram− bacterial strains; growth kinetic tests and counting tests on bacterial colonies have demonstrated a strong and rapid bactericidal effect.
Growth inhibition tests were performed on different bacterial strains (Gram negative: Escherichia coli, Pseudomonas aeruginosa, and Gram positive: Staphylococcus aureus, Staphylococcus epidermidis) in the presence of Chitlac solutions with and without metallic nanoparticles. It was found that bacterial growth in Chitlac solutions free from nanoparticles is comparable to the growth in control (Mueller-Hinton broth); in contrast, a considerable bacterial growth inhibition occurs in the presence of Chitlac with metallic nanoparticles, as reported for example in the case of silver and gold (
Raman spectra on solutions containing polymer-stabilized nanoparticles were collected using an in Via Raman system (Renishaw plc, Wotton-under-Edge, U.K.). The laser (514.5 nm argon-ion laser, LaserPhysics, West Jordan Utah, U.S.A.) was focused on the sample by a 20× objective (0.4 NA). Laser power at the sample was 3 mW; to minimize laser-induced photodegradation of the sample, the laser power density was lowered by defocusing the beam by 10%. The exposure time was 5 accumulations of 10 s for each spectrum, for a total exposure time of 50 s per spectrum.
A strong increase in the Raman spectroscopic signal of the polysaccharide was found, which can be ascribed to the presence of metallic nanoparticles. The latter ones therefore have optimal dimensions and size distribution to exploit the SERS (Surface Enhanced Raman Spectroscopy) effect on which the operation of several molecular biosensors is based. Indeed, as inferred from
Methacrylic resins cylindrical samples (Ø=1.4 mm; h=2 mm) were immersed in HCl 12 M for 7 hours at 80° C.; then the samples were rinsed with deionized water (2×50 mL), NaOH 0.1 M (50 mL) and water again (50 mL). The acid-treated methacrylic resin samples were immersed in the colloidal solutions of the metal-based nanocomposite prepared according to example 9 for 24 hours. Finally the samples were rinsed in deionized water and dried under hood.
Some biological characterization of the coated methacrylic resins are hereinafter reported.
Cylindrical samples (Ø=1.4 mm; h=2 mm) of coated methacrylic resins were put in direct contact with S. aureus bacteria. On each sample 10 μL of bacteria suspension were plated at the concentration of 106 CFU/mL (CFU=Colony Forming Units) and incubated in a moist environment at 37° C. for 3 hours. Then, each sample was immersed in 2 mL of PBS in agitation to allow the bacteria detachment from the surface. These washing solutions were serially diluted and plated on agar gel to allow colony count after overnight incubation at 37° C. The colony count numbers demonstrate that in the case of methacrylic resins coated with Chitlac-nAg the number of bacteria on the surface is reduced by 98%.
After the antibacterial tests, further investigations were carried out, aimed at evaluating the toxicity of the nanocomposite coating towards eukaryotic cells. To this end, LDH cytotoxicity assays were performed by direct contact of osteoblasts-like cells (MG63) both with the material itself and with the liquid culture medium kept in contact with the material for given time (24 hours) (“extract”). Tested materials (in quadruplicate) were directly deposited on the cell layer. After 24 and 72 h, the medium was collected and the LDH assay was performed according to the manufacture's protocol. The results reported in
| Number | Date | Country | Kind |
|---|---|---|---|
| PD2008A000219 | Jul 2008 | IT | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2009/059430 | 7/22/2009 | WO | 00 | 1/21/2011 |