Patent Application
20130125912
The present invention relates to a nanofiber and a method for producing the nanofiber. It also relates to a nanofiber sheet.
Techniques relating to water-soluble polymer-based nanofibers are known as disclosed, e.g., in patent literature 1 below. The nanofiber disclosed is prepared by electrospinning a solution of a water soluble polymer in a solvent such as water. The solution is described as optionally containing a functional component, such as an emulsifier, a stabilizer, a bactericide, a moisturizer, and so on. When the solution contains such a functional component, the resulting nanofiber contains the functional component therein.
With regard to incorporation of a functional component into a nanofiber, the technique of patent literature 2 below is also known. The literature discusses a network structure formed of polymer nanofibers holding a cosmetic or a cosmetic ingredient. The cosmetic or the like is held inside the nanofiber. The nanofiber holding the cosmetic or the like is obtained by mixing the cosmetic or the like into a solution of a polymer constructing the nanofiber.
The nanofibers described in the patent literatures cited above are likely to feel sticky because the functional component, cosmetic, etc. exists not only inside but on the surface thereof. There is a limit to the amount of a functional component or the like that can be incorporated into nanofibers. The functional component existing on the fiber surface tends to suffer from deterioration or denaturation, so that the nanofibers are expected to have poor storage stability.
The invention provides a nanofiber formed of a water soluble polymer, having a cavity, and containing an oily component in the cavity.
The invention also provides a suitable method for producing the nanofiber of the invention. The method includes electrospinning an O/W emulsion having a water soluble polymer dissolved in the aqueous phase and an oily component contained in an oily phase.
The invention also provides another suitable method for producing the nanofiber. The method includes providing a first liquid having a water soluble polymer dissolved in water and a second liquid containing an oily component and electrospinning the first liquid and the second liquid using a duplex-tube capillary having a sheath and a core. The first liquid is fed to the sheath, and the second liquid is fed to the core.
The invention includes the following subject matter.
[1] A nanofiber made from a water soluble polymer, having a cavity, and containing an oily component in the cavity.
[2] The nanofiber set forth in [1] above, wherein the oily component in the cavity is liquid at ambient temperature.
[3] The nanofiber set forth in [1] or [2] above, having a large-diametered portion and a small-diametered portion, the large-diametered portion having the cavity.
[4] The nanofiber set forth in [1] or [2] above, having a large-diametered portion and a small-diametered portion, both the large-diametered portion and the small-diametered portion having the cavity, and the cavity in the large-diametered portion and the cavity in the small-diametered portion being interconnected.
[5] The nanofiber set forth in [1] or [2] above, having a tubular shape with a substantially constant outer diameter and a substantially constant inner diameter.
[6] The nanofiber set forth in any one of [1] to [5], wherein the water soluble polymer is a naturally occurring polymer, such as a mucopolysaccharide, e.g., pullulan, hyaluronic acid, chondroitin sulfate, poly-γ-glutamic acid, modified corn starch, β-glucan, gluco-oligosaccharide, heparin, and keratosulfate, cellulose, pectin, xylan, lignin, glucomannan, galacturonic acid, psyllium seed gum, tamarind seed gum, gum arabic, tragacanth gum, soybean water-soluble polysaccharide, alginic acid, carrageenan, laminaran, agar (agarose), fucoidan, methyl cellulose, hydroxypropyl cellulose, and hydroxypropylmethyl cellulose; or a synthetic polymer, such as partially saponified polyvinyl alcohol, low-saponified polyvinyl alcohol, polyvinylpyrrolidone, polyethylene oxide, and sodium polyacrylate.
[7] The nanofiber set forth in any one of [1] to [5], wherein the water soluble polymer is pullulan or a synthetic polymer selected from the group consisting of partially saponified polyvinyl alcohol, low-saponified polyvinyl alcohol, polyvinylpyrrolidone, and polyethylene oxide.
[8] The nanofiber set forth in [6] or [7], wherein the water soluble polymers are used individually or in combination of two or more thereof.
[9] The nanofiber set forth in any one of [1] to [5], wherein the water soluble polymer is pullulan.
[10] The nanofiber set forth in any one of [1] to [9], wherein the oily component contains a solvent selected from squalane, olive oil, silicone oil, macadamia nut oil, and cetyl 1,3-dimethylbutyl ether.
[11] The nanofiber set forth in [10], wherein the oily component further contains an oil-soluble component selected from vitamin E, chamomile extract, and rose extract as dissolved in the solvent as an effective ingredient.
[12] The nanofiber set forth in [10] or [11], wherein the oily components are used either individually or in combination of two or more thereof.
[13] The nanofiber set forth in any one of [1] to [12], wherein the oily component comprising a first oily component and a second oily component, the cavity comprising a plurality of cavities discretely formed over the whole length of the nanofiber, and each cavity contains both the first oily component and the second oily component.
[14] The nanofiber set forth in any one of [1] to [12], wherein the oily component contains a first oily component and a second oily component, the cavity comprising a plurality of cavities discretely formed over the whole length of the nanofiber, some of the cavities contain the first oily component and do not contain the second oily component, and others contain the second oily component and do not contain the first oily component.
[15] The nanofiber set forth in any one of [1] to [9], wherein the oily component comprises chamomile extract and cetyl 1,3-dimethylbutyl ether.
[16] The nanofiber set forth in any one of [1] to [9], wherein the oily component contains silicone oil.
[17] The nanofiber set forth in any one of [1] to [16], containing a volatile functional agent having a vapor pressure of 13.3 Pa or less at 20° C.
[18] A nanofiber sheet containing the nanofiber set forth in any one of [1] to [17].
[19] The nanofiber sheet set forth in [18], which is for use as a moisturizing sheet, a cosmetic sheet, or a medical sheet.
[20] A method for producing the nanofiber set forth in [1], comprising electrospinning an O/W emulsion having a water soluble polymer dissolved in an aqueous phase and an oily component in an oily phase.
[21] A method for producing the nanofiber set forth in [1], comprising providing a first liquid having a water soluble polymer dissolved in water and a second liquid containing an oily component and
electrospinning the first liquid and the second liquid using a duplex-tube capillary having a sheath and a core,
the first liquid being fed to the sheath, and the second liquid being fed to the core.
[22] The method set forth in [21], wherein the second liquid is prepared by emulsification.
[23] The method set forth in [21], wherein the second liquid is prepared by emulsification using a surfactant as an emulsifier.
[24] The method set forth in [23], wherein the emulsifier is a nonionic surfactant.
[25] The method set forth in [23], wherein the emulsifier is a polyethylene glycol monoalkylate, polyethylene glycol dialkylate, ethylene glycol dialkylate, or polyoxyethylene hydrogenated castor oil.
[26] The method set forth in [23], wherein the emulsifier is polyoxyethylene hydrogenated castor oil.
[27] A method for producing a nanofiber made from a water soluble polymer, containing an easily volatile functional agent having a vapor pressure higher than 13.3 Pa at 20° C., having a cavity, and containing an oily component in the cavity,
the method comprising a step of applying the easily volatile functional agent to a layer of the nanofiber.
[28] A method for producing a nanofiber made from a water soluble polymer, containing an easily volatile functional agent having a vapor pressure higher than 13.3 Pa at 20° C., having a cavity, and containing an oily component in the cavity,
the method comprising a step of disposing the easily volatile functional agent close to the nanofiber to cause the volatile functional agent to transfer to the nanofiber.
The invention provides a nanofiber that contains an oily component in a high ratio and yet has a reduced sticky feel caused by the oily component and also exhibits excellent storage stability.
a),
a) is a scanning electron micrograph of the nanofiber sheet obtained in Example 1, and
a) is a backscattered electron image of the nanofiber sheet obtained in Example 2, and
The present invention provides a nanofiber containing a functional component in a high concentration and yet feeling dry and with the functional component being prevented from deteriorating. The invention also provides a nanofiber containing a functional component in its cavity and designed to slowly release the functional component to the skin by dissolving the outer water soluble polymer.
The invention will be described based on its preferred embodiments with reference to the accompanying drawings. The nanofiber of the invention has a thickness usually of 10 to 3000 nm, preferably 100 to 2000 nm, more preferably 200 to 1500 nm, in terms of circle equivalent diameter. The thickness of nanofibers is measured by, for example, observation using a scanning electron microscope (SEM). Specifically, a two-dimensional micrograph at a magnification of 10000 is processed by deleting defects (lumps of nanofibers, intersections of nanofibers, and polymer droplets), randomly choosing ten fibers, drawing a line perpendicular to the longitudinal direction of each fiber chosen, and reading the fiber diameter directly from the line. The length of the nanofiber is not critical in the invention and may have any appropriate length depending on the method of nanofiber manufacturing and the intended use of the nanofiber.
The nanofiber is made from a water soluble polymer. As used herein, the Willi “water soluble polymer” denotes a polymer having solubility such that, when a sample polymer weighing 1 g is immersed in 10 g of ion-exchanged water for 24 hours at 23° C. and atmospheric pressure, at least 0.5 g of the immersed polymer dissolves in the ion-exchanged water.
Examples of the water soluble polymer include naturally occurring polymers, such as mucopolysaccharides, e.g., pullulan, hyaluronic acid, chondroitin sulfate, poly-γ-glutamic acid, modified corn starch, β-glucan, gluco-oligosaccharides, heparin, and keratosulfate, cellulose, pectin, xylan, lignin, glucomannan, galacturonic acid, psyllium seed gum, tamarind seed gum, gum arabic, tragacanth gum, soybean water-soluble polysaccharides, alginic acid, carrageenan, laminaran, agar (agarose), fucoidan, methyl cellulose, hydroxypropyl cellulose, and hydroxypropylmethyl cellulose; and synthetic polymers, such as partially saponified polyvinyl alcohol, low-saponified polyvinyl alcohol, polyvinylpyrrolidone, polyethylene oxide, and sodium polyacrylate. These water soluble polymers may be used either individually or in combination of two or more thereof. Preferred of them are pullulan and synthetic polymers, such as partially saponified polyvinyl alcohol, low-saponified polyvinyl alcohol, polyvinylpyrrolidone, and polyethylene oxide, in view of ease of conversion to nanofibers.
The nanofiber has a cavity. The cavity provides a nanospace capable of holding an oily component described later.
The nanofiber 10 shown in
While in
Similarly to the nanofiber of
The nanofiber 10 shown in
According to each of the above described embodiments, because the nanofiber 10 is capable of retaining an oily component 14 in its cavity 13, it is possible to incorporate the oily component 14 in a high ratio into the nanofiber 10. In particular, the nanofibers 10 of the embodiments shown in
The oily component may be used either alone or in the form of a solution in an organic solvent. Accordingly, the cavity 13 may contain the oily component alone or a solution of the oily component in an organic solvent.
As stated, the nanofiber 10 of the invention is capable of containing an oily component in a higher ratio than conventional nanofibers, preferably in a ratio of 0.5% to 95%, more preferably 10% to 90%, even more preferably 20% to 90%, by mass. The ratio of the water soluble polymer in the nanofiber 10 is preferably 5% to 99.5%, more preferably 10% to 90%, even more preferably 10% to 80%, by mass. The ratios of the water soluble polymer and the oily component in the nanofiber 10 are determined by dissolving a given amount of a nanofiber sheet in water and subjecting the solution to centrifugation.
A variety of oily components are usable in accordance with the intended use of the nanofiber 10. The oily component that can be used for use in, for example, a moisturizing sheet, a cosmetic sheet, or a medical sheet may contain a solvent, such as squalane, olive oil, silicone oil, macadamia nut oil, or cetyl 1,3-dimethylbutyl ether, and an oil-soluble component generally used in cosmetics or for medical use, such as vitamin E, chamomile extract, or rose extract, as dissolved in the solvent as an active ingredient.
The oily components described above may be used either individually or in combination of two or more thereof. In the latter case, when a nanofiber having, for example, the cross-sectional structure shown in
The nanofiber 10 of the invention may further contain a volatile functional agent in addition to the above described components. The volatile functional agent is preferably at least one member selected from the group consisting of a fragrance, a whitening agent, and a taste corrector. As used herein, the “fragrance” means a substance capable of imparting a pleasant scent to air at ambient temperature and atmospheric pressure and having a “fragrant function”. As used herein, the “whitening agent” means a substance which is, when applied to human skin, capable of whitening the skin or maintaining the skin in a youthful and healthy condition and has a “whitening function”. As sued herein, the “taste corrector” means a substance capable of changing or diminishing a taste and having a “taste correcting function”. For example, a taste corrector may change bitterness or sourness to another taste, e.g., sweetness, or reducing a taste. These functional agents are volatile substances vaporizing at ambient temperature and atmospheric pressure. As used herein, the term “ambient temperature and atmospheric pressure” usually means a condition of a temperature of 23° C. and an atmospheric pressure of 101.325 kPa. When the volatile functional agent is water soluble, it exists along with the water soluble polymer. When it is oil soluble, it exists in the same cavity as the above discussed oily component or, as shown in
The volatile functional agent preferably has a vapor pressure at 20° C. of 13.3 Pa or less, more preferably 0.0013 to 10.7 Pa, even more preferably 0.0133 to 6.7 Pa. With the vapor pressure at 20° C. of the volatile functional agent falling within that range, the nanofiber 10 will exhibit a useful function attributed to the volatile functional agent at ambient temperature and atmospheric pressure. For instance, a nanofiber 10 containing a fragrance as a volatile functional agent is a fragranced nanofiber capable of releasing a fragrance into air at ambient temperature and atmospheric pressure thereby to make a user feel exhilarated, refreshed, cleaned, or relaxed and also produce a deodorizing effect, an anesthetic (analgesic) effect, or a like effect.
When the nanofiber is produced by electrospinning (a method for producing the nanofiber, hereinafter described) using a stock polymer solution containing a volatile functional agent whose vapor pressure at 20° C. exceeds 13.3 Pa (hereinafter also referred to as an easily volatile functional agent), the easily volatile functional agent tends to vaporize during electrospinning because of its high volatility. It can follow that the resulting nanofiber fails to retain a sufficient amount of the easily volatile functional agent for performing the function expected of the use of the functional agent, for example, a fragrant function of an easily volatile fragrance. Nevertheless, it is possible to impart the function of such an easily volatile functional agent to a nanofiber by timely adding the easily volatile functional agent (see methods A and B described infra). The vapor pressure of a volatile functional agent is obtained from the data base provided by Research Institute for Fragrance Materials.
Examples of fragrances that can be used as a volatile functional agent include vanillin, methyl jasmonate, γ-undecalactone, and phenylethyl alcohol. These volatile functional agents may be used either individually or in combination of two or more thereof
The volatile functional agent content in the nanofiber 10 is preferably 0.001% to 30%, more preferably 0.01% to 5%, by mass. The recited range of the volatile functional agent content assures production of a nanofiber performing a useful function of the volatile functional agent, such as fragrance release, and achieves reduction in the amount of the volatile functional agent to be used, leading to a reduced cost of production.
The nanofiber 10 of the invention is used to advantage in the form of a sheet that contains the nanofiber 10 of the invention. A sheet containing the nanofiber 10 of the invention (hereinafter called a “nanofiber sheet”) may be made solely of the nanofiber 10 or may contain other fibers, such as nanofibers except the nanofiber 10 of the invention and ordinary natural or synthetic fibers. Also included in the nanofiber sheet of the invention is a laminate sheet composed of a fiber sheet containing the nanofiber 10 of the invention and at least one other fiber sheet and/or film.
The nanofibers in the nanofiber sheet are bonded to one another at the intersections thereof or intertwined with one another, whereby the nanofiber sheet is self-supporting. Whether the nanofibers are bonded to or intertwined with one another depends on the method of manufacture.
The nanofiber sheet may have a thickness decided as appropriate to the intended use. For example, for use as attached to human skin, the thickness of the nanofiber sheet is preferably 50 nm to 1 mm, more preferably 500 nm to 500 μm. The thickness of the nanofiber sheet may be measured using a contact thickness gauge Litematic VL-50A from Mitutoyo Corp.
The nanofiber sheet of the invention is used as attached to, for example, human skin, the skin of mammals other than human, tooth, and surfaces of plant parts, such as foliage. Before the nanofiber sheet is applied to the surface of an object, a surface of the nanofiber sheet or the surface of the object is wetted with water or a water-containing aqueous liquid so that the nanofiber sheet successfully adheres to the surface with the surface tension taken advantage of. In addition, the water soluble polymer making up the nanofiber dissolves in the liquid. It follows that the cavity 13 is destroyed to make the oily component retained therein flow out. The flowing-out oily component covers the surface of the object such as human skin and penetrates inside the object. When, for example, a nanofiber sheet containing a plant extract as an oily component is applied to human skin, the oily component having flowed out from the destroyed cavity covers the skin surface and penetrates inside the skin to achieve its action and effect.
It is particularly advantageous that the oily component covering the surface of the object, e.g., human skin inhibits evaporation of water from the object to easily keep the surface of the object moisturized. This is expected to lead to the following effects. The functional agent, if present in the nanofiber, is helped to penetrate inside the object. The oily component effectively prevents the water soluble polymer making up the nanofiber from drying and filming, so that an uncomfortable pulling sensation that might be caused by the filming is reduced. The oily component acts as a plasticizer on the water soluble polymer film to maintain the transparency and impart flexibility to the water soluble polymer film. Uncomfortable powdery feel that might be caused by partial peeling of the water soluble polymer film and poor appearance that might be caused by whitening due to partial lifting of water soluble polymer film is reduced.
The surface of an object or the surface of the nanofiber sheet may be wetted by, for example, spreading or spraying a liquid of various kinds to the surface. The liquid to be spread or sprayed is a substance containing water and having a viscosity of about 5000 mPa·s or less at the use temperature. Such a liquid is exemplified by water, an aqueous solution, or an aqueous dispersion. Emulsions, including O/W emulsions and W/O emulsions, and aqueous liquids thickened with a thickener are also useful. More specifically, in the case when the nanofiber sheet is attached to human skin, a skin lotion or a beauty cream is useful as a liquid wetting the surface of the object (skin).
In order to wet the surface of an object or the surface of the nanofiber sheet by spreading or spraying a liquid, it suffices that the liquid be applied in a minimum amount required for the liquid to sufficiently exhibit a surface tension and to dissolve the water soluble polymer. The amount of a liquid to be applied varies with the size of the nanofiber sheet. For example, in the case of a nanofiber sheet measuring 3 cm by 3 cm, presence of about 0.01 ml of a liquid on the surface of an object will be enough to attach the nanofiber sheet to the object easily and to dissolve the water soluble polymer of the nanofiber 10 to destroy the cavity 13.
The above described nanofiber sheet is suitably produced by, for example, electrospinning deposition (ESD).
Preparation of the stock solution is of importance in order to successfully produce the nanofiber 10 having the cavity 13. In the case of obtaining the nanofiber 10 of the embodiment shown in
The first liquid preferably has a water soluble polymer concentration of 3% to 30%, more preferably 10% to 25%, by mass, in view of suitable viscosity of the resulting stock solution. The first liquid is obtained by adding a water soluble polymer to water or an aqueous liquid containing a small amount of a water soluble organic solvent and mixing them with or without heating.
The second liquid is obtained by a known emulsifying technique, such as spontaneous emulsification, phase-transfer emulsification, or forced emulsification. The mass ratio of the aqueous phase to the oily phase containing the oily component, aqueous phase/oily phase, is preferably 51:49 to 99:1, more preferably 51:49 to 85:15, to successfully accomplish emulsification. For the same reason, the amount of an emulsifier to be used for emulsification is preferably 0.001% to 20%, more preferably 0.004 to 7%, by mass based on the total mass of the first and the second liquid.
Various surfactants can be used as an emulsifier. Nonionic surfactants, such as a polyethylene glycol monoalkylate, a polyethylene glycol dialkylate, an ethylene glycol dialkylate, and polyoxyethylene hydrogenated castor oil, are particularly preferred for their low irritation to the skin.
When the second liquid is prepared by phase transfer emulsification, an emulsifier is added to an oily phase containing an oily component, followed by heating to a prescribed temperature, and an aqueous phase heated to a prescribed temperature is slowly added thereto while stirring to induce phase transfer to yield an O/W emulsion.
The resulting O/W emulsion (stock solution) is preferably composed of 55% to 98%, more preferably 60% to 97%, by mass of the aqueous phase and 2% to 45%, more preferably 3% to 40%, by mass of the oily phase.
In the cases of using two or more oily components, the following method (I) or (II) may be employed to prepare the stock solution.
Method (I): An O/W emulsion containing all the oily components in its oily phase is prepared as a second liquid, which is mixed with a first liquid to prepare a stock solution.
Method (II): An O/W emulsion is prepared for each oily component, and all the resulting O/W emulsions are mixed with a first liquid to prepare a stock solution.
When the method (I) is followed to produce the nanofiber shown in
Electrospinning using the O/W emulsion as a stock solution results in the formation of the nanofiber 10 having the structure shown in
To produce the nanofiber 10 having the structure shown in
When the above discussed volatile functional agent which is water soluble is used, it is incorporated into the first liquid. The functional agent will then exist together with the water soluble polymer in the resulting nanofiber. When the volatile functional agent which is oil soluble is used, on the other hand, the following methods (i) or (ii) may be employed.
Method (i): An O/W emulsion containing an oily component and the volatile functional agent in its oily phase is prepared as a second liquid, which is then mixed with a first liquid to prepare a stock solution.
Method (ii): Separately from an O/W emulsion containing an oily component in its oily phase as a second liquid, an O/W emulsion containing the volatile functional agent in its oily phase is prepared as a third liquid. The second and the third liquid are mixed with a first liquid to prepare a stock solution. In this method, the second liquid does not contain the volatile functional agent, and the third liquid does not contain the oily component.
When the method (i) is adapted to produce the nanofiber shown in
In the case when a highly volatile functional agent, for example, the easily volatile functional agent discussed earlier is used, the easily volatile functional agent is allowed to be imparted to a nanofiber by timely addition of the easily volatile functional agent. More specifically, a nanofiber provided with the function of an easily volatile functional agent is obtainable according to the following methods A and B.
Method A: A method for producing a nanofiber including a step of making a nanofiber having a cavity according to the above described method (nanofiber making step) and a step of applying a solution containing an easily volatile functional agent to the nanofiber (solution addition step).
Method B: A method for producing a nanofiber including a step of making a nanofiber having a cavity according to the above described method (nanofiber making step) and a step of leaving an easily volatile functional agent to stand close to the nanofiber for a prescribed period of time (easily volatile functional agent transfer step).
The solution containing an easily volatile functional agent for use in the solution addition step of the method A is prepared by dissolving or dispersing the easily volatile component in a solvent. The solvent is preferably uninfluential on the nanofiber, specifically the water soluble polymer making up the nanofiber. An organic solvent may be used, for example. Application of the solution containing the easily volatile functional agent to the nanofiber may be achieved by, for example, spraying the solution to the nanofiber or immersing the nanofiber in the solution.
The easily volatile functional agent transfer step of the method B is a step in which the nanofiber and the easily volatile functional agent are brought close to but not in contact with each other thereby to cause the vapor of the easily volatile functional agent to transfer to the nanofiber. If the nanofiber and the easily volatile functional agent are brought into contact with each other, the water soluble polymer constituting the nanofiber can dissolve or swell to lose its form. Such an inconvenience is avoided by placing them close to each other. The easily volatile functional agent placed close to the nanofiber may be exposed to open air or be enclosed in an air permeable bag or a like enclosure. Unintentional direct contact of the nanofiber with the easily volatile functional agent is certainly avoided by enclosing the easily volatile functional agent. The period of time that the easily volatile functional agent is left to stand close the nanofiber is decided as appropriate to the type of the easily volatile functional agent and the like. In general, the higher the volatility of the functional agent, the shorter the time needed.
While the invention has been described with reference to its preferred embodiments, it should be understood that the invention is not limited to these embodiments. For example, while the method for producing the nanofiber has been described with particular reference to electrospinning deposition, the method for producing the nanofiber is not limited thereto.
While, according to the electrospinning technique shown in
The invention will now be illustrated in greater detail by way of Examples, but it should be understood that the scope of the invention is not limited thereto. Unless otherwise noted, all the percents are by mass.
Pullulan available from Hayashibara Shoji Inc. was used as a water soluble polymer. Pullulan was dissolved in water to make a 20% aqueous solution as a first liquid. The first liquid was heated to 80° C.
A mixture of chamomile extract and cetyl 1,3-dimethylbutyl ether (ASE166K from Kao Corp.) was used as an oily component. The concentration of chamomile extract in the solution was 4.20%. Polyoxyethylene hydrogenated castor oil (Emanon® CH60, from Kao Corp.) as a nonionic surfactant was added to the solution in a concentration of 0.3%. A 0.95 ml portion of the resulting solution was heated to 80° C., and 4.00 ml of hot water at 80° C. was slowly added thereto while stirring to cause phase-transfer emulsification, thereby to give an O/W emulsion as a second liquid.
The first liquid and the second liquid were mixed and stirred at a mass ratio of 3:1 to prepare an O/W emulsion as a stock solution. The stock solution was found to contain 15.00% of pullulan, 80.20% of water, 4.78% of the oily component, and 0.013% of the nonionic surfactant.
The stock solution obtained above was electrospun under the conditions described below using the apparatus shown in
Applied voltage: 25 kV
Capillary-collector distance: 185 mm
Rate of ejection of stock solution: 1 ml/hr
The resulting nanofiber sheet contained 75.82% of pullulan, 24.11% of the oily component, and 0.07% of the surfactant. The thickness of the nanofiber sheet was found to be 30 μm measured with Litematic VL-50A from Mitutoyo Corp. A scanning electron micrograph of the nanofiber sheet is shown in
As is apparent from
The same as in Example 1.
Silicone oil was used as an oily component. Polyoxyethylene hydrogenated castor oil (Emanon® CH60, from Kao Corp.) as a nonionic surfactant was added to the silicone oil in a concentration of 0.3%. A 0.95 ml portion of the silicone oil was heated to 80° C., and 4.00 ml of hot water at 80° C. was slowly added thereto while stirring to cause phase-transfer emulsification, thereby to give an O/W emulsion as a second liquid.
The first liquid and the second liquid were mixed and stirred at a mass ratio of 3:1 to prepare an O/W emulsion as a stock solution. The stock solution was found to contain 15% of pullulan, 80.2% of water, 4.787% of the oily component, and 0.013% of the nonionic surfactant.
The same as in Example 1.
The resulting nanofiber sheet contained 75.82% of pullulan, 24.11% of the oily component, and 0.07% of the surfactant. The thickness of the nanofiber sheet was found to be 30 μm measured with Litematic VL-50A from Mitutoyo Corp. A backscattered electron image of the nanofiber sheet is shown in
The same as Example 1.
Chamomile extract was used as an oily component. Polyoxyethylene hydrogenated castor oil (Emanon® CH60, from Kao Corp.) as a nonionic surfactant was added to the solution in a concentration of 0.3%. A 1.72 ml portion of the resulting solution was heated to 80° C., and 2.06 ml of hot water at 80° C. was slowly added thereto while stirring to cause phase-transfer emulsification, thereby to give an O/W emulsion as a second liquid.
The first liquid and the second liquid were mixed and stirred at a mass ratio of 81:19 to prepare an O/W emulsion as a stock solution. The stock solution was found to contain 16.22% of pullulan, 75.16% of water, 8.59% of the oily component, and 0.03% of the nonionic surfactant. A nanofiber sheet was obtained in the same manner as in Example 1, except for using the resulting stock solution. The resulting nanofiber sheet contained 65.3% of pullulan, 34.58% of the oily component, and 0.12% of the surfactant. The thickness of the nanofiber sheet was found to be 30 μm measured with Litematic VL-50A from Mitutoyo Corp. A scanning electron micrograph of the nanofiber sheet is shown in
Pullulan from Hayashibara Shoji Inc. was used as a water soluble polymer. Pullulan was dissolved in water to make a 20% aqueous solution as a first liquid. Chamomile extract, an oily component, was used as a second liquid. Electrospinning was carried out using these liquids and the apparatus 30 shown in
Applied voltage: 25 kV
Capillary-collector distance: 220 mm
Rate of ejection of first liquid: 0.1 ml/hr
Rate of ejection of second liquid: 2 ml/hr
The resulting nanofiber sheet contained 80% of pullulan and 20% of the oily component. The thickness of the nanofiber sheet was found to be 30 μm measured with Litematic VL-50A from Mitutoyo Corp. A scanning electron micrograph of the nanofiber sheet is shown in
Chamomile extract was added to a 15% pullulan solution in a ratio of pullulan 16.22%, water 75.17%, and oily component 8.59%, followed by stirring using a stirrer. However, chamomile extract and the pullulan solution separated from each other, resulting in a failure to provide a uniform solution. Therefore, electrospinning was not conducted.
The stock solution prepared in Example 1 was dropped on a petri dish and left to dry to give a 30 μm thick cast film.
The stock solution prepared in Example 2 was dropped on a petri dish and left to dry to give a 30 μm thick cast film.
The stock solution prepared in Example 3 was dropped on a petri dish and left to dry to give a 30 μm thick cast film
Oil-blotting paper (from DHC Corp.) was applied to the nanofiber sheets obtained in Examples 1 to 4 and the cast films of Comparative Examples 2 to 4 to visually observe absorption of the oily component. More specifically, the oil-blotting paper was pressed onto the sheet or cast film. After removal from the sheet or film, the change in color of the oil-blotting paper was observed with naked eyes. Furtheiinore, dissolving properties of the sheets or cast films when attached to human skin were evaluated. The results of evaluation are shown in Table 1 below. The methods of evaluation are as follows.
A square of about 3 cm per side was cut out of the sheet or cast film, and the oil-blotting paper (from DHC) was applied and removed. The change in color of the oil-blotting paper was observed with naked eyes.
(2) Dissolving Properties when Attached to Human Skin
A skin lotion weighing 0.03 g was dropped on the skin and spread to a circle of about 20 mm diameter. A square of about 15 mm per side cut out of the sheet or cast film was put thereon. Immediately thereafter, the dissolved state of the sheet or cast film was observed with naked eyes and rated as follows.
A: The sheet or film immediately dissolves and becomes unable to be picked up with tweezers.
B: The sheet or film partially dissolves and partially remains in sheet form that is able to be picked up with tweezers.
As is apparent from the results in Table 1, it is seen that the nanofiber sheets of Examples have a reduced sticky feel because the oily component is not exposed on the surface of the fiber and that they easily dissolve on contact with water to release the oily component.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2010-148076 | Jun 2010 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2011/064809 | 6/28/2011 | WO | 00 | 1/23/2013 |