The present invention relates to nanomaterials and in particular HEPA air filter media.
Nanofibers have desirable properties that make them capable of wide-ranging technological and commercial application. Nanofibers are useful candidates for application as a filtration medium but lack physical strength due to their nano size. Advancements in nanomaterials with better mechanical integrity are needed.
One example embodiment is a nanomaterial that includes a plurality of nanofibers that form a randomly interwoven network defining three-dimensional pores therein. The nanomaterial further includes a plurality of beads with a bead diameter of 2-20 μm that are distributed randomly within the plurality of nanofibers. The beads support the nanofibers to prevent the pores from collapsing.
Example embodiments relate to apparatus and methods that provide a filtration medium that includes a substrate layer, a nanofiber layer and a plurality of beads. The nanofiber layer coats the substrate layer and includes a plurality of nanofibers that form a randomly interlaced matrix defining three-dimensional pores within. The plurality of beads are randomly interspersed within the plurality of nanofibers and support the nanofibers to prevent the pores from collapsing. In one example embodiment, the beads have a bead diameter of 2-20 μm.
Example embodiments relate to a method of preparing a filtration medium that include providing at least one substrate layer, producing threads of nanofibers containing beads that are dispersed irregularly and at random along a length of each nanofiber to generate a plurality of beaded nanofibers, and depositing the beaded nanofibers onto the surface of the substrate layer to create a coating of randomly oriented interwoven nanofibers with three-dimensional pores of 5-50 μm to produce at least one nanofiber filtration layer.
Other example embodiments are discussed herein.
Nanofibers have properties including small fiber diameter, high porosity and high surface area to volume ratio that make them an important material capable of wide-ranging application. One such application is as a HEPA air filtration medium. Nanofibers are a desirable filtration medium in view of their high filtration efficiency and high specific surface area. However, one problem with nanofibers is their weak mechanical integrity. Nanofibers used in conventional filtration mediums are inherently weak. Conventional filtration mediums have attempted to overcome this weakness in various ways but have not been able to provide a nanomaterial with enhanced mechanical integrity. Example embodiments solve this problem.
Example embodiments relate to a nanomaterial that includes a plurality of nanofibers and a plurality of beads. The beads may be part of the same material as the nanofibers and are formed as thicker or irregular droplets of 2-20 μm in diameter along the length of the nanofibers as the nanofibers are formed. The plurality of nanofibers form a randomly interwoven network defining three-dimensional pores within. The plurality of beads with a bead diameter of 2-20 μm are randomly distributed within the plurality of nanofibers and support the nanofibers to prevent the pores from collapsing. The beads improve the mechanical integrity of the nanomaterial.
Example embodiments relate to an air filtration medium that includes a substrate layer, a nanofiber layer, and a plurality of beads. The nanofiber layer coats the substrate layer and includes a plurality of nanofibers that form a randomly interlaced matrix defining three-dimensional pores within. The plurality of beads with a bead diameter of 2-20 μm are randomly interspersed within the plurality of nanofibers and support the nanofibers to prevent the pores from collapsing.
Example embodiments relate to a method of preparing an air filtration medium that include providing at least one substrate layer, producing threads of nanofibers containing beads that are dispersed irregularly and at random along a length of each nanofiber to generate a plurality of beaded nanofibers, and depositing the beaded nanofibers onto the surface of the substrate layer to create a coating of randomly oriented interwoven nanofibers with three-dimensional pores of 5-50 μm to produce at least one nanofiber filtration layer.
In one example embodiment, the beads in the nanofiber filtration layer reinforce the nanofibers and prevent them from collapsing, providing the nanofiber filtration layer with increased air permeability. In an example embodiment, the beads and the nanofibers are formed at the same time.
In an example embodiment, the nanofibers have a diameter of 10-1000 nm. In another example embodiment the pores have a pore size of 1-10 μm. In an example embodiment, the nanofibers have a diameter of 100-500 nm. In a further example embodiment, the pores have a pore size of 3-8 μm. In an example embodiment, each bead is part of at least one nanofiber. In another example embodiment, each bead is an irregularity that forms a bulge along the length of at least one nanofiber. In an example embodiment, the beads have a bead diameter of 5-15 μm. In one example embodiment, the beads support the nanofibers and prevent delamination.
In an example embodiment, the nanofibers are made from one or more polymers selected from a group consisting of polyvinylidene fluoride (PVDF), poly(vinylidene fluoride-co-hexafluoropropene) (PVDF-co-HFP), polyamide 6 (PA-6), poly(hexamethyleneadipamide), polystyrene, polysulfone, polyethersulfone, polyethylene oxide, polyvinyl chloride, cellulose acetate, chitosan and zein.
The high specific area of nanofibers, as shown in
In an example embodiment, the substrate layer of the air filtration medium comprises a plurality of microfibers. In an example embodiment, the microfibers have a diameter of 2-30 μm. In a further example embodiment, the substrate layer is selected from, but not limited to, polypropylene (PP), polyethylene (PE), polyethylene terephthalate (PET), PET reinforced glass fibers, or a combination thereof. In an example embodiment, the nanofibers are covalently bonded to the microfibers with an adhesion strength higher than 0.01N. In an example embodiment, the filtration medium may be composed of chemical bonds including but not limited to C—C, C—N, C—O and CONH.
In an example embodiment, the basis weight of the nanofiber layer is 0.1-10 grams per square meter (gsm). In another example embodiment, the basis weight of the nanofiber layer is 0.5-1 gsm. In an example embodiment, the nanofiber layer has an air permeability range of 4-20 cm3/cm2/s under air flow pressure of 125 pascal (Pa).
One example embodiment functionalizes the air filtration medium with agents that provide the air filtration medium with additional properties. In an example embodiment, the nanofiber layer is treated with antimicrobial agents to prevent microbial activity in a filtrate that the filtration medium is used as a filter for. In another example embodiment, antimicrobial agents prevent biological contamination of the air filtration medium. The treatment of the nanofibers with antimicrobial agents prevent the proliferation of microbes trapped by the air filtration medium and increases the shelf life of the air filtration medium
The antimicrobial agents may include but are not limited to thymol, chlorhexidine gluconate and polyhexamethylene biguanide (PHMB). In another example embodiment, the nanofiber layer is treated with volatile organic compound (VOC) removal agents. The VOC removal agents include but are not limited to halloysite, loess and zeolites. In an example embodiment, the filtration medium may have viral removal capability. In another example embodiment, the filtration medium neutralizes odors and chemicals and removes allergens including dust, pollen and mold.
In an example embodiment, the air filtration medium may be folded or pleated. In a further example embodiment, the air filtration medium is a high efficiency particulate air (HEPA) filter with an E13 level of filtration efficiency.
In an example embodiment, the air filtration medium is pleated into a “V” configuration with corrugated aluminium separators between the pleats to form a filter element. The filter element is then bonded into a rigid frame using a special polyurethane compound and sealed to form a HEPA filter. The HEPA filter is further sealed when installed in equipment in order to prevent air flow and the sub-micron particles it contains from by-passing the HEPA filter. In an example embodiment, the HEPA filter is further sealed by use of a closed cell neoprene gasket. In an example embodiment, the HEPA filter has a depth of 150 mm. In another example embodiment, the HEPA filter has a depth of 300 mm.
In an example embodiment, the air filtration medium may capture airborne contaminants by mechanisms including but not limited to inertia impaction, interception and Brownian motion.
In an example embodiment, the microfibers in the substrate layer are treated with an atmospheric plasma treatment (APT) system before the beaded nanofibers are deposited on the substrate layer. In one example embodiment, the duration of the APT is 2-10 seconds. In another example embodiment, the duration of the APT is 3-6 seconds. The APT system applies stable and uniform plasma to the microfibers at a low frequency of 1-2 kHz. In another example embodiment, the frequency is 1.3-1.5 kHz. A mixture of helium (He) and oxygen (O2) is used as plasma carrier gas with a He:O2 ratio of 100:0-98:2. In an example embodiment, the He:O2 ratio is 99:1. In an example embodiment, the gas flow of helium is 10-30 L/min. In a further example embodiment, the gas flow of helium is 18-22 L/min. In an example embodiment, the gas flow of oxygen is 0.1-0.5 L/min. In a further example embodiment, the gas flow of oxygen is 0.2-0.4 L/min. In an example embodiment, the time gap between the end of the APT treatment and the start of the deposition of the beaded nanofibers is 5-30 seconds. In another example embodiment, the time gap is 8-12 seconds.
In an example embodiment, the beaded nanofibers are produced by free surface electrospinning. In an example embodiment, the beaded nanofibers are produced from polymer resins not limited to polyvinylidene fluoride (PVDF) and poly(vinylidene fluoride-co-hexafluoropropene) (PVDF-co-HFP) dissolved in organic solvents including dimethylformamide (DMF) with a concentration range of 10%-20%. In a further example, the concentration range is 13%-17%. Organic solvent soluble salts including but not limited to tetraethylammonium chloride (TEAC), tetraethylammonium bromide (TEAB) and benzyltriethylammonium chloride (BTEAC) are added to the polymer solution, and the concentration is 0.1%-5%. In a further example embodiment, the concentration is 0.5%-2%. In an example embodiment, the organic solvent soluble salts including TEAC, TEAB, and BTEAC vary the conductivity of the polymer solution and destabilize the polymer solution to form beaded nanofibers. In one example embodiment, the conditions in the electrospinning chamber are 5%-50%, or 10%-20% relative humidity, inward air flow of 50-100 m3/min or 70-90 m3/min, and outward air flow of 100-170 m3/min or 120-140 m3/min.
The processing parameters for electrospinning, including but not limited to electric field, air flow difference, carriage speed, and substrate speed, are optimized. For example, the electric field is 0.1-0.5 kV/mm. In another example embodiment, the electric field is 0.2-0.4 kV/mm. In an example embodiment, the air flow difference is 0-120 m3/h. In another example embodiment, the air flow difference is 30-70 m3/h. In an example embodiment, the carriage speed is 25-100 mm/sec. In another example embodiment, the carriage speed is 40-80 mm/sec. In an example embodiment, the substrate speed is 20-8000 mm/min. In another example embodiment, the substrate speed is 100-2000 mm/min.
In one example embodiment, the nanofibers have a diameter of 10-1000 nm, the beads have a diameter of 2-20 μm, and the distance between the beads is 5-50 μm. In another example embodiment, the nanofibers have a diameter of 100-500 nm, the beads have a diameter of 5-15 μm, and the distance between the beads is 10-30 μm.
In one example, the folded air filtration medium is assembled with other microfibrous layers to form a HEPA filter with a filtration efficiency of 99.97% or above when tested with aerosol at the most penetrating particle size while maintaining a pressure drop of 50 mmH2O or below.
The unwinding system 520 unwinds the substrate layer 515 and the atmospheric plasma treatment (APT) system 530 applies uniform and stable plasma 525 to the substrate layer 515 to produce a substrate layer that has undergone APT treatment 510. The moving reservoir 545 applies polymer solution onto the spinning electrode 540 producing a polymer jet 535 that becomes nanofiber after solvent evaporation and deposits beaded nanofibers onto a surface of the substrate layer that has undergone APT treatment 510 to produce a nanofiber filtration layer, and the filtration medium comprising a substrate layer and a nanofiber filtration layer 505 is rewound by the rewinding system 550. In an example embodiment, the substrate layer comprises microfibers.
A substrate layer is provided 610. Threads of nanofibers containing beads that are irregularly dispersed along a length of each nanofiber to generate a plurality of beaded nanofibers are produced 620.The beaded nanofibers are deposited onto a surface of the substrate layer 610 to create a coating of randomly oriented interwoven beaded nanofibers 620 with three-dimensional pores of 5-50 μm to produce a nanofiber filtration layer 630.
In an example embodiment, the air filtration medium 600 undergoes additional processes including but not limited to lamination and pleating to form a HEPA air filtration medium.
The exemplary embodiments of the present invention are thus fully described. Although the description referred to particular embodiments, it will be clear to one skilled in the art that the present invention may be practiced with variation of these specific details. Hence this invention should not be construed as limited to the embodiments set forth herein.
Methods discussed within different figures can be added to or exchanged with methods in other figures. Further, specific numerical data values (such as specific quantities, numbers, categories, etc.) or other specific information should be interpreted as illustrative for discussing example embodiments. Such specific information is not provided to limit example embodiment.
As used herein, a “nanomaterial” is a material comprising particles or constituents of nanoscale dimensions, including but not limited to nanofibers with diameters of 10-1000 nm.
As used herein, a “bead” is a lump of material of regular or irregular shape of diameter of approximately 2-20 μm. A bead is an irregular swelling or protuberance that forms a bulge along the length of, along varying lengths of, and/or along random lengths of, at least one nanofiber. A singular bead, a plurality of beads or no beads may form along the length of at least one nanofiber.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2018/091308 | 6/14/2018 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62648401 | Mar 2018 | US |