Patent Grant
6848163
The present invention relates generally to high-pressure ducting and more particularly to high-pressure liquid ducting for propellants in rocket engines.
High-pressure liquid propellant ducts on rocket engines are generally heavy and can represent approximately 10-20 percent of the total weight of the engine. Generally, the ducts comprise a tubular section that is joined to a flange portion at each end thereof to form a section of high-pressure liquid ducting. The section of high-pressure liquid ducting is further joined to another section of ducting or to another component of the rocket engine such as a propellant feed tank or an inlet to the rocket engine of, for example, an aerospace vehicle.
In the known art, high-pressure liquid propellant ducts are fabricated from nickel or iron-based superalloys such as 625 or 718, which have relatively high densities and thus contribute significantly to the weight of a rocket engine. To minimize weight, therefore, the ducts are ideally fabricated from materials with high specific strength and toughness for the tubular sections, which generally perform as pressure vessels. Similarly, the flange portions are fabricated from materials with high specific stiffness and hardness, wherein the flange portion performs primarily as a sealing section.
At the ambient or cryogenic temperatures of typical liquid propellant ducts, superalloys do not have an ideal high specific strength for the tubular section or an ideal high specific stiffness for the flange portion. For example, when a superalloy tubular section has been designed with sufficient strength to accommodate propellant pressure, the associated stiffness is relatively high such that small misalignments of the flange portions results in high stresses therein after assembly of the duct. Further, the assembly stress can represent approximately 60 percent of the total flange loading. Moreover, welding, weld inspection, and any rework necessary during assembly of high-pressure liquid ducts of the known art adds substantial cost to the rocket engine.
High strength aluminum alloys, although approximately one third the density of superalloys, have not been used for propellant ducts for a variety of reasons. Generally, the high strength condition in conventional aluminum alloys is achieved by a solution heat treat, followed by a water quench and age, which introduces constraints on forming, welding, and maximum component section thickness. Unfortunately, the aluminum alloy comprises undesirable residual stresses, anisotropic properties, and susceptibility to stress corrosion as a result of the heat treat, water quenching, and aging processes.
Further, conventional aluminum alloys generally have low stiffness, and thus any potential weight benefits of high specific strength in the stiffness-critical flange portions have not been achievable. Moreover, the high coefficient of thermal expansion of conventional aluminum alloys would require an excessively high preload in steel or superalloy bolts that are used to fasten and seal the flange portions to prevent loosening of the bolts during a chill-down process.
Accordingly, there remains a need in the art for lightweight high-pressure liquid ducts comprising aluminum alloys to provide significant weight savings over superalloy ducting of the known art. The high-pressure liquid ducts should comprise lightweight tubular sections in addition to lightweight flange portions, which are fabricated and assembled using manufacturing techniques applicable to the particular materials employed throughout the ducting.
In one preferred form, the present invention provides a nanophase composite duct assembly that comprises a high pressure liquid duct formed from an ultra-high strength nanophase aluminum alloy, which is joined with a high-pressure liquid ducting flange formed from a ceramic particulate in a metal matrix such as aluminum. Preferably, the duct is joined with the flange using solid-state friction welding such as inertia welding or friction stir welding, among others, as described in greater detail below.
The nanophase aluminum alloy duct is preferably formed by synthesizing a nanophase aluminum alloy to form a billet, extruding the billet into a predetermined geometrical shape, followed by bending the extruded billet into a profile to form the high-pressure liquid duct. Further, the extruded billet may be flow formed prior to bending in order to achieve a precise wall thickness with relatively tight tolerances for a particular application.
Generally, the nanophase aluminum alloy is synthesized by a powder processing sequence of cryogenic milling, out-gassing, and hot isostatic pressing (HIP) to form the billet. The billet is then extruded into a predetermined geometrical shape such as a cylindrical tube for use in many ducting applications for rocket engines. Further, in order to meet the dimensional requirements of rocket engine and other applications, the extruded billet is further flow formed to reduce the wall thickness of the duct to a desired dimension prior to bending, wherein relatively tight tolerances are maintained along the entire length of the extruded billet. (Generally, flow forming is a manufacturing technique that is used for high precision, high tolerance net shape component fabrication).
In preparation of the extrusion process, a center hole is machined through the center of the billet and an internal liner is secured within the center hole, along with an extrusion mandrel. A leader is then positioned at one end of the billet and a follower is positioned at another end of the billet, and an extrusion jacket is placed over the billet, the leader, and the follower. The billet is then extruded through an extrusion die, along with the internal liner, the extrusion jacket, the leader, and the follower, to form an extruded billet having a predetermined geometrical shape. Furthermore, other extrusion methods commonly known in the art may be employed in accordance with the teachings of the present invention. Accordingly, the preferred extrusion method as described herein shall not be construed as limiting the scope of the present invention.
The high-pressure liquid ducting flange comprising a ceramic particulate in a metal matrix is preferably formed by powder processing or by a liquid metal infiltration process. Further, the metal matrix is preferably aluminum in one form of the present invention. The high-pressure liquid ducting flange in one form comprises a series of radial holes wherein bolts are used to secure the flange to another flange portion or to another component within the systems of, for example, a rocket engine. In another embodiment, the high-pressure liquid ducting flange is a two-piece component comprising a nanophase flange joined to a discontinuously reinforced aluminum (DRA) base, preferably using inertia welding, wherein the nanophase flange is then joined to the high-pressure liquid duct.
The high-pressure liquid duct is joined to the high-pressure liquid ducting flange preferably using solid-state friction welding. The solid-state friction welding may comprise inertia welding or friction stir welding, or a combination of both inertia welding and friction stir welding, among others. Furthermore, the nanophase composite duct assembly may also comprise a collar between the high-pressure liquid duct and the high-pressure liquid ducting flange to further seal and secure the interface therebetween. Similarly, the collar is preferably welded to the high-pressure liquid duct and the high-pressure liquid ducting flange using solid-state friction welding.
Although the present invention is directed to a high-pressure liquid duct within a rocket engine, the invention may also be applicable to other high-pressure ducting applications. Accordingly, the reference to rocket engines throughout the description of the invention herein should not be construed as limiting the scope of the present invention.
Further areas of applicability of the present invention will become apparent from the detailed description provided hereinafter. It should be understood that the detailed description and specific examples, while indicating the preferred embodiment of the invention, are intended for purposes of illustration only and are not intended to limit the scope of the invention.
The present invention will become more fully understood from the detailed description and the accompanying drawings, wherein:
The following description of the preferred embodiments is merely exemplary in nature and is in no way intended to limit the invention, its application, or uses.
Referring to the drawings, a nanophase composite duct assembly according to the present invention is illustrated and generally indicated by reference numeral 10 in FIG. 1. As shown, the nanophase composite duct assembly 10 generally comprises a high-pressure liquid duct 12 joined to a high-pressure liquid ducting flange 14. Preferably, the high-pressure liquid duct 12 is an ultra-high strength nanophase aluminum alloy and the high-pressure liquid ducting flange 14 is formed from a ceramic particulate in a metal matrix, wherein the metal matrix is preferably aluminum. Accordingly, the nanophase composite duct assembly 10 provides significant weight and cost savings over superalloy high-pressure ducting of the known art.
The high-pressure liquid duct 12 is preferably formed by first synthesizing the nanophase aluminum alloy using powder processing. More specifically, the nanophase aluminum alloy is milled in a cryogenic high-energy ball mill while submerged in liquid nitrogen. After cryogenic milling, the nanophase aluminum alloy is out-gassed and pressed into a billet using hot isostatic pressing (HIP). As a result, a nanophase aluminum alloy billet is produced that is then preferably extruded into predetermined geometrical shape as described in greater detail below. Alternately, the nanophase aluminum alloy billet may be formed into the desired geometrical shape using other methods commonly known in the art such as machining, pultrusion, and die forming, among others. Accordingly, the extrusion process as described herein shall not be construed as limiting the scope of the present invention.
Referring to
The mandrel 20 further comprises a collar 21 as shown, which is preferably larger in diameter than the extrusion jacket 26. Further, the mandrel 20 and the internal sleeve 18 extend through the extrusion jacket 26 as illustrated. Accordingly, the internal sleeve 18 is preferably split to form ears 29, which prevent the internal sleeve 18 from slipping during the extrusion process.
As further shown, the extrusion jacket 26 is placed over the nanophase aluminum alloy billet 16, the leader 22, and the follower 24. Generally, the extrusion jacket 26 is provided to encapsulate the nanophase aluminum alloy billet 16 during the extrusion process. Preferably, the extrusion jacket 26, along with the internal sleeve 18, are a copper material, and the leader 22 and the follower 24 are preferably an aluminum material such as 6061-T6.
The extrusion jacket 26, the nanophase aluminum alloy billet 16 with the internal sleeve 18 and the extrusion mandrel 20, the leader 22, and the follower 24 are then placed in an extrusion die (not shown), wherein the mandrel 20 is activated to force the aluminum alloy billet 16 with the internal sleeve 18, along with the extrusion jacket 26, the leader 22, and the follower 24 through the die to form an extruded billet having a predetermined geometrical shape. Preferably, the nanophase aluminum alloy billet 16, the leader 22, and the extrusion jacket 26 are preheated prior to extrusion, while the follower 24 remains at approximately room temperature. Further, the internal sleeve 18 is also preheated, however, at temperatures somewhat higher than the nanophase aluminum alloy billet 16, the leader 22, and the extrusion jacket 26.
In one form of the present invention, a nanophase aluminum alloy billet having a diameter of approximately 9.125 inches is extruded at an area reduction ratio of approximately 20:1. The nanophase aluminum alloy billet 16, the leader 22, and the extrusion jacket 26 are preheated to approximately 400° F., the follower 24 remains at approximately room temperature, the internal sleeve 18 is preheated to approximately between 550° F. and 610° F., and the die temperature is approximately between 350° F. and 500° F. with an extruder having approximately a 5,000 ton capacity. Accordingly, a high-pressure liquid duct is extruded in one form of the present invention that has an outer diameter of approximately 3.35 inches and an inner diameter of approximately 2.80 inches. Additionally, alternate dimensions according to specific applications may also be achieved in accordance with the teachings of the present invention.
Referring to
Once the nanophase aluminum alloy billet 16 is extruded into the predetermined geometrical shape to form the extruded billet 30, the extruded billet 30 is preferably flow formed to further reduce the wall thickness 36 to a desired dimension. Generally, flow forming produces precise and consistent dimensions along the entire length of the extruded billet 30 within relatively tight tolerances. Accordingly, for applications requiring tighter dimensional control, flow forming is employed after the extrusion process as described herein.
To complete the high-pressure liquid duct 12, the extruded billet undergoes a bending operation to form a profile that corresponds with the final shape of the nanophase composite duct assembly 10. In one form, the geometry of the high-pressure liquid duct 12 is tubular as shown, and thus tube bending operations as commonly known in the art are employed to create the desired profile. Accordingly, further forming methods known in the art may also be employed in accordance with the teachings of the present invention.
The high-pressure liquid duct 12 may also be formed using other methods commonly known in the art such as die forming, pultrusion, or blow forming, among others. Accordingly, the description of extrusion and bending processes herein to form the high-pressure liquid duct 12 shall not be construed as limiting the scope of the present invention.
Referring to
In another form of the present invention, the high-pressure liquid ducting flange 14 is a two-piece component comprising a nanophase flange joined to a discontinuously reinforced metal matrix base (not shown). Preferably, the nanophase flange is joined to the discontinuously reinforced metal matrix base using inertia welding to form the completed high-pressure liquid ducting flange 14. Further, the nanophase flange portion of the high-pressure liquid ducting flange 14 is joined to the high-pressure liquid duct, while the discontinuously reinforced metal matrix base portion is joined to other portions of rocket engine systems as previously described. Accordingly, the nanophase flange portion defines a tapered outer surface that generally transitions from the diameter of the high-pressure liquid duct 12 to the larger diameter of the discontinuously reinforced metal matrix base portion. Preferably, the metal matrix is aluminum for the discontinuously reinforced metal matrix base portion.
Referring now to
As shown in
Accordingly, a lightweight, low cost composite duct assembly is provided in accordance with the teachings of the present invention. The composite duct assembly comprises a lightweight nanophase aluminum alloy duct that is joined with a lightweight ceramic particulate reinforced aluminum matrix flange, which together with the joining methods as described herein provide significant weight savings over superalloy ducting of the known art.
The description of the invention is merely exemplary in nature and, thus, variations that do not depart from the substance of the invention are intended to be within the scope of the invention. Such variations are not to be regarded as a departure from the spirit and scope of the invention.
This application is a divisional of U.S. patent application Ser. No. 09/945,280 filed on Aug. 31, 2001, presently pending.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1302412 | Murray | Apr 1919 | A |
| 2367206 | Davis | Jan 1945 | A |
| 3727843 | Parilla | Apr 1973 | A |
| 3837066 | Mori et al. | Sep 1974 | A |
| 3873139 | McCabe | Mar 1975 | A |
| 3885548 | Regan | May 1975 | A |
| 4077813 | Fletcher et al. | Mar 1978 | A |
| 4159217 | Selines et al. | Jun 1979 | A |
| 4333671 | Holko | Jun 1982 | A |
| 4412869 | Vernam et al. | Nov 1983 | A |
| 4643779 | Abbaschian et al. | Feb 1987 | A |
| 4818481 | Luton et al. | Apr 1989 | A |
| 5053084 | Masumoto et al. | Oct 1991 | A |
| 5054184 | Gerard | Oct 1991 | A |
| 5074762 | Mechin | Dec 1991 | A |
| 5098871 | Ray | Mar 1992 | A |
| 5148965 | Hayes et al. | Sep 1992 | A |
| 5156316 | Nied et al. | Oct 1992 | A |
| RE34442 | Reiso | Nov 1993 | E |
| 5334266 | Kawanishi et al. | Aug 1994 | A |
| 5342575 | Nagai | Aug 1994 | A |
| 5352269 | McCandlish et al. | Oct 1994 | A |
| 5365108 | Anderson et al. | Nov 1994 | A |
| 5561829 | Sawtell et al. | Oct 1996 | A |
| 5728195 | Eastman et al. | Mar 1998 | A |
| 5766380 | Lo et al. | Jun 1998 | A |
| 5805657 | Heubeck | Sep 1998 | A |
| 5849373 | Barbour et al. | Dec 1998 | A |
| 5856025 | White et al. | Jan 1999 | A |
| 5911845 | Fukagawa et al. | Jun 1999 | A |
| 5993575 | Lo et al. | Nov 1999 | A |
| 6033624 | Gonsalves et al. | Mar 2000 | A |
| 6264719 | Zhang et al. | Jul 2001 | B1 |
| 6334911 | Kita et al. | Jan 2002 | B2 |
| 6368406 | Deevi et al. | Apr 2002 | B1 |
| 6449942 | Dean et al. | Sep 2002 | B1 |
| 6502480 | Walker et al. | Jan 2003 | B1 |
| 20010025676 | Taguchi et al. | Oct 2001 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20040255460 A1 | Dec 2004 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09945280 | Aug 2001 | US |
| Child | 10352307 | US |