Patent Grant
9849451
Field of the Invention
Embodiments relate generally to ionic material compositions and in particular to ionic liquid material compositions and ionic gel material compositions. More particularly, embodiments relate to nanoscale ionic material (NIM) compositions and in particular nanoscale ionic liquid (NIL) material compositions and nanoscale ionic gel (NIG) material compositions, related methods and related applications.
Description of the Related Art
Recent research has demonstrated nanoscale ionic material (NIM) compositions as a new platform for hybrid nanoparticle based materials, which in turn generally comprise an inorganic nanoparticle material core component and an organic polymer material canopy component. Due to their hybrid inorganic nanoparticle material core component and organic polymer material canopy component composition, the properties of nanoscale ionic materials may be tailored over an unusually wide range. Included at one end of the range are nanoscale ionic materials with high inorganic content, which display properties similar to solids. These nanoscale ionic material compositions may be designated as nanoscale ionic solid (NIS) material compositions. Included at an opposite end of the range are nanoscale ionic material compositions with high organic content. These nanoscale ionic material compositions spontaneously form nanoscale ionic liquid (NIL) material compositions that are characterized by transport properties remarkably similar to those of simple molecular liquids, but with negligible vapor pressures. Finally, nanoscale ionic gel (NIG) material compositions include nanoscale ionic material compositions of intermediate inorganic material content and organic material content. As well, nanoscale ionic gel (NIG) material compositions are generally characterized by physical and chemical properties intermediate to those of nanoscale ionic solid (NIS) material compositions and nanoscale ionic liquid (NIL) material compositions.
Since nanoscale ionic material compositions, including in particular nanoscale ionic liquid (NIL) material compositions and nanoscale ionic gel (NIG) material compositions, thus often have unique materials properties, desirable are additional nanoscale ionic material compositions, including but not limited to nanoscale ionic liquid (NIL) material compositions and nanoscale ionic gel (NIG) material compositions, methods for preparing the nanoscale ionic material compositions and applications of the nanoscale ionic material compositions.
Embodiments provide nanoscale ionic material compositions including but not limited to nanoscale ionic solid, gel and liquid material compositions, and methods for preparing the nanoscale ionic material compositions including but not limited to the nanoscale ionic solid, gel and liquid material compositions. Within the embodiments, the nanoscale ionic material compositions and methods for preparing the nanoscale ionic material compositions rely upon a generalized acid/base reaction directly between a core inorganic metal oxide nanoparticle and a canopy organic polymer material that encapsulates the core inorganic metal oxide nanoparticle. By using such a direct acid/base reaction between the core inorganic metal oxide nanoparticle and the canopy organic polymer material, a simplified processing scheme may be effectuated for preparing a homogeneous nanoscale ionic material composition such as but not limited to a nanoscale ionic solid, gel or liquid material composition, with an attendant avoidance of a coupling agent chemical functionalization processing step that is otherwise used to form a corona interposed between the core inorganic metal oxide nanoparticle and the organic polymer material canopy.
Within the context more specifically of
As a reference point, a particular nanoscale ionic material that illustrates such a core component, a corona component and a canopy component is shown in
Within the embodiments, and also the claims, the terminology of a “homogeneous” nanoscale ionic material or a “uniformly distributed” core inorganic metal oxide nanoparticle within a nanoscale ionic material is intended as a nanoscale ionic material in accordance with the embodiments where the core inorganic metal oxide nanoparticles are equally volumetrically distributed within a bulk nanoscale ionic material and/or equally areally distributed within a coated nanoscale ionic material. In particular with respect to such a coated nanoscale ionic material, such a uniform distribution of core inorganic metal oxide nanoparticles with respect to each other and a canopy organic polymer material may be determined using a computer assisted image analysis (using, for example and without limitation, ImageJ software available from the National Institutes of Mental Health, Bethesda, Md., USA) of a transmission electron microscopy image of the nanoscale ionic material when coated upon a substrate (see, e.g., the upper transmission electron microscopy image in
Within the context of any one of the foregoing software assisted image analysis method, small angle x-ray scattering spectroscopy analysis method or qualitative determination method, a nanoscale ionic material in accordance with the embodiments is intended as at least substantially non-agglomerated with respect to inorganic metal oxide nanoparticle cores and an intervening organic polymer material canopy, and thus having no greater than about 10 number percent inorganic metal oxide nanoparticle cores agglomerated and touching each other, more preferably no greater than about 5 number percent inorganic metal oxide nanoparticle cores agglomerated and touching each other and still more preferably no greater than about 1 number percent inorganic metal oxide nanoparticle cores agglomerated and touching each other.
Within the embodiments, and also the claims, the terminology “absent a corona” is intended to indicate that no coupling agent functionalization of a core inorganic metal oxide nanoparticle is present when preparing a nanoscale ionic material in accordance with the embodiments. To that end, also thus absent is a related process step in a method for preparing the corona within a nanoscale ionic material in accordance with the embodiments. Within the embodiments, absence of a corona may under certain circumstances be determined using a depth profiling elemental analysis of a nanoscale ionic material composite in accordance with the embodiments to discern that the nanoscale ionic material composite consists of, or consists essentially of, only a core inorganic metal oxide nanoparticle and a canopy organic polymer material (i.e., there will be one organic rich layer surrounding a core inorganic metal oxide nanoparticle rather than two organic rich layers surrounding the core inorganic metal oxide nanoparticle and separated by a comparatively inorganic rich layer). Under such circumstances, analytical tools and methodology such as but not limited to secondary ion mass spectroscopy (SIMS), electron spectroscopy for chemical analysis (ESCA), Auger electron spectroscopy (AES), and other relevant analytical tools and methodology may be used. Alternatively, an investigation of molecular spectroscopy of a nanoscale ionic material in accordance with the embodiments may also be undertaken to inform of the presence or absence of materials compositions that may be identified as a corona that surrounds a core inorganic metal oxide nanoparticle within a nanoscale ionic material. These molecular spectroscopy methods may include, but are not necessarily limited to infrared spectroscopy methods and Raman spectroscopy methods.
Yet another method for discerning the presence or absence of a corona within a nanoscale ionic material in accordance with the embodiments involves preliminary treatment of a nanoscale ionic material in accordance with the embodiments with an alkaline hydroxide material, such as but not limited to a sodium hydroxide material or a potassium hydroxide material, which may be provided in an aqueous solution or a polar non-aqueous solution such as but not limited to an alcohol polar non-aqueous solution. Incident to such alkaline hydroxide material treatment, alkali metal cations are intended and anticipated to exchange with a core inorganic metal oxide nanoparticle of the nanoscale ionic material and release the canopy component that may be soluble within the polar aqueous or polar non-aqueous solvent. The core inorganic metal oxide nanoparticle may then be further analyzed (i.e., using methodology as described above) for the presence, or in particular the absence, of organic chemical functional groups. As noted above, such chemical analysis may be effected using methods including but not limited to spectroscopic analysis methods such as but not limited to infrared spectroscopic analysis methods and Raman spectroscopic analysis methods. Alternatively, a weight loss measurement at a temperature from about 200 to about 300 degrees Celsius for a time period of at least about 2 minutes and typically from about 5 to about 10 minutes using a thermogravimetric analysis method may also be used as an analysis method. Under the foregoing circumstances a “substantial absence” of any residual organic functionality within a released inorganic metal oxide nanoparticle core is intended as less than about 10 weight percent, more preferably less than about 5 weight percent and still more preferably less than about 1 weight percent.
Commonly, a nanoscale ionic material in accordance with the embodiments may be additionally characterized as having an aqueous solution zeta potential of magnitude greater than about +/−5 mV, more preferably of magnitude greater than about +/−10 mV and still more preferably of magnitude greater than about +/−15 mV. Commonly, a nanoscale ionic material in accordance with the embodiments may be additionally characterized as having a conductivity measured neat greater than about 1e−7 S/cm, more preferably greater than about 1e−5 S/cm.
A particular nanoparticle in accordance with the embodiments includes an inorganic metal oxide material core absent an organofunctional corona. The particular nanoparticle also includes an organic polymer material canopy surrounding the inorganic metal oxide material core.
A particular composition in accordance with the embodiments includes a plurality of inorganic metal oxide nanoparticle cores each absent an organofunctional corona. The particular composition also includes an organic polymer material canopy uniformly surrounding and uniformly separating each of the plurality of inorganic metal oxide nanoparticle material cores.
A particular method for preparing an ionic material in accordance with the embodiments includes reacting directly at least one inorganic metal oxide nanoparticle core absent an organofunctional corona in an acid/base reaction with a functional organic polymer material to provide a nanoscale ionic material.
The objects, features and advantages of the embodiments are understood within the context of the Detailed Description of the Embodiments, as set forth below. The Detailed Description of the Embodiments is understood within the context of the accompanying drawings, which form a material part of this disclosure, wherein:
Embodiments provide a nanoscale ionic material composition and a method for preparing the nanoscale ionic material composition. The nanoscale ionic material composition and the method for preparing the nanoscale ionic material composition in accordance with the embodiments are predicated upon an acid/base reaction directly between an acid or base functionalized core inorganic metal oxide nanoparticle and a corresponding complementary base or acid functionalized canopy organic polymer material. The use of such an intrinsic acid or base functionalized core inorganic metal oxide nanoparticle in a direct reaction with a corresponding base or acid functionalized canopy organic polymer material allows for preparing a homogeneous nanoscale ionic material composition, such as but not limited to a homogeneous nanoscale ionic liquid material composition, homogeneous nanoscale ionic gel material composition or homogeneous nanoscale ionic solid material composition, absent need for an intervening chemical functionalization process step to form a corona surrounding the core inorganic metal oxide nanoparticle, such as but not limited to an intervening silane coupling agent (or alternative coupling agent) chemical functionalization process step that forms the corona surrounding the core inorganic metal oxide nanoparticle.
In turn, avoidance of such an intervening chemical functionalization process step, such as but not limited to the intervening silane coupling agent (or alternative coupling agent) chemical functionalization process step allows for materials cost savings, as well as reduced material processing apparatus requirements and related procedures, when preparing a nanoscale ionic material in accordance with the embodiments in comparison with a nanoscale ionic material that is prepared using a method not in accordance with the embodiments.
While the embodiments that follow are illustratively described within the context of a nanoscale ionic material that comprises a nanoscale ionic fluid (i.e., at a particular elevated temperature) that further comprises an acidified silica nanoparticle as a core inorganic metal oxide nanoparticle that is directly reacted within an acid/base reaction with a basic amine functional polyethylene glycol organic polymer material as a canopy organic polymer material, the embodiments are not intended to be so limited.
Rather the embodiments consider within the context of nanoscale ionic material compositions such as but not limited to nanoscale ionic liquid material compositions, nanoscale ionic gel material compositions and nanoscale ionic solid material compositions, the use of inorganic metal oxide materials such as but not limited to at least one of silicon oxide, titanium oxide, zinc oxide, magnesium oxide, calcium oxide, copper oxide, tungsten oxide and zirconium oxide (i.e., both stoichiometric and non-stoichiometric metal oxide particle compositions) inorganic metal oxide materials that may be effectively treated to provide an acid functional inorganic metal oxide nanoparticle or a base functional inorganic metal oxide nanoparticle. Determination of whether a particular metal oxide nanoparticle is a viable candidate as an acid functional metal oxide nanoparticle or a base functional metal oxide nanoparticle may be assisted by considering the isoelectric point of the particular metal oxide nanoparticle. Metal oxide nanoparticles with an isoelectric point below pH 7, or alternatively above pH 7, act within the context of the embodiments as acidic metal oxide nanoparticles or basic metal oxide nanoparticles, respectively. Such acidic or basic inorganic metal oxide nanoparticle materials in turn may be directly reacted with a corresponding complementary base functional organic polymer material or a corresponding complementary acid functional organic polymer material. Most commonly, such acidic or basic inorganic metal oxide nanoparticles may thus include, but are not necessarily limited to silicon oxide, titanium oxide, zinc oxide, magnesium oxide, calcium oxide, copper oxide, tungsten oxide and zirconium oxide inorganic metal oxide nanoparticles in a size range from about 1 to about 500 nanometers and preferably from about 5 to about 100 nanometers and more preferably from about 10 to about 50 nanometers. Similarly, the acidic or basic inorganic metal oxide nanoparticles have a loading within a particular nanoscale ionic material composition from about 1 to about 85 weight percent, more preferably from about 10 to about 75 weight percent and still more preferably from about 15 to about 50 weight percent.
The embodiments also contemplate that a nanoscale ionic material composition in accordance with the embodiments may alternatively comprise: (1) a mixed inorganic metal oxide material nanoparticle (i.e., an inorganic metal oxide material nanoparticle comprising a single inorganic metal oxide material composition that includes multiple inorganic metal oxides); as well as (2) mixtures of different inorganic metal oxide nanoparticles comprised of different and single inorganic metal oxide material compositions. Under either circumstance of: (1) a mixed inorganic metal oxide nanoparticle; or (2) a mixture of different inorganic metal oxide nanoparticles, the same group of inorganic metal oxide materials as listed above may be considered, but individual compositions within the mixed inorganic metal oxide material nanoparticle or within the mixture of inorganic metal oxide nanoparticles are selected to provide only acidic inorganic metal oxide nanoparticles or basic inorganic metal oxide nanoparticles, to thus avoid and minimize nanoparticle to nanoparticle acid/base interactions. Thus, under these circumstances, a mixed inorganic metal oxide material nanoparticle or a mixture of inorganic metal oxide material nanoparticles may comprise at least two of silicon oxide, titanium oxide, zinc oxide, magnesium oxide, calcium oxide, copper oxide, tungsten oxide and zirconium oxide inorganic metal oxide nanoparticle materials selected to provide the mixed inorganic metal oxide material nanoparticle or the mixture of inorganic metal oxide material nanoparticles of only acidic or basic characteristics.
Within the context of base functionality of an organic polymer material canopy in accordance with the embodiments, amine functionality is generally considered but not limiting of the embodiments. Alternative base functionality may include, but is also not limited to imine functionality or pyridine functionality. As well, within the context of acid functionality of an organic polymer material canopy in accordance with the embodiments, carboxylic acid functionality and sulfonic acid functionality are similarly also considered, but also not limiting of the embodiments. Alternative acid functionality may include, but is also not limited to phenol functionality or phosphonic acid functionality. Within the context of either base functionality of an organic polymer material or acid functionality of an organic polymer material in accordance with the embodiments, generally intended (due to expected enhanced performance and processability), but not necessarily specifically required is terminal base functionality or terminal acid functionality.
Thus, the embodiments provide a class of nanoscale ionic material compositions based upon an alternative direct acid/base reaction scheme architecture directly between an inorganic metal oxide nanoparticle core and an organic polymer material canopy that covers the inorganic metal oxide nanoparticle core. The alternative direct acid/base reaction scheme architecture in accordance with the embodiments exploits the innate acid/base character of different types of nanoparticles, and allows for a direct reaction between an inorganic metal oxide nanoparticle core and an organic polymer material canopy when forming a nanoscale ionic material composition in accordance with the embodiments. Compared with alternative processing sequences that may include a chemical functionalization process sequence to provide an organofunctional charged corona for an inorganic metal oxide nanoparticle core, such as but not limited to a silane coupling agent chemical functionalization process sequence to provide the organofunctional chemical charged corona for the inorganic metal oxide nanoparticle core, the present approach eliminates this intermediate, often complex, chemical functionalization process sequence to create the charged corona, which greatly simplifies a synthesis protocol and reduces a number of system components. For example, the reaction conditions for a silane coupling agent silylation chemical functionalization process step to provide a charged corona need to be controlled precisely so that only a monolayer of the corona is formed. Additionally, the product of the reaction of the chemically functional silane coupling agent with the inorganic metal oxide nanoparticle core needs to be exhaustively purified by dialysis or ultrafiltration to ensure removal of frequent byproducts. Since all steps required to synthesize the nanoscale ionic materials in accordance with the embodiments are simple and scalable a manufacturing process sequence in accordance with the embodiments may be readily integrated into current manufacturing environments.
Material System Considerations
The following illustrative embodiment describes the use of silica nanoparticles with an average diameter of 18 nm as a model system for preparing a nanoscale ionic material composition in accordance with the embodiments. Acidic silica nanoparticles were prepared by passing a commercially available Na+ stabilized silica suspension through an H+ ion-exchange column. The resulting acidic solution was then neutralized with an amine terminated polyethylene glycol, PEG-NH2. A range of compositions was readily prepared by controlling the extent of neutralization (i.e. the ratio between the acidic silica nanoparticles and the amine terminated polyethylene glycol polymer PEG-NH2). Finally the water was evaporated to produce the final product.
The presence of the ionic interactions endows the composite nanoscale ionic material composition that results from the acidic silica particles and the amine terminated polyethylene glycol polymer material with a unique behavior not found in dispersions of charged silica in ionic liquids or PEG. First, the new materials do not suffer from the persistent challenges of miscibility and poor dispersion encountered in physical mixtures of inorganic nanoparticle and organic polymer material nanohybrid compositions. In addition, the materials are liquids at 70° C. and exhibit an ionic conductivity of 10e−5 S/cm. More importantly, when compared with two control samples composed of a physical mixture of SiO2 and PEG (i.e. systems that are void of any electrostatic interactions and thus akin to a dispersion of SiO2 nanoparticles into the polymer) the ionic SiO2 fluids in accordance with the embodiment's exhibit remarkably different dispersion and flow properties. Of the embodied nanoscale ionic material and the two control samples, only the silica nanoscale ionic materials in accordance with the embodiments flow and behave like viscoelastic liquids while both of the control samples are solids exhibiting significant aggregation and phase separation of the particles.
Experimental
PEG-NH2 with a molecular weight (MW) of 20,000 g/mol and polydispersity index (PI) 1.02 was purchased from Laysan Biotech. Ludox sodium-stabilized silica (HS30-Na+), α-ω OH-PEG (MW 20,000 g/mol, PI 1.08) and Dowex W2 ion exchange resin were obtained from Sigma Aldrich. All materials were used as supplied.
The chemical reaction scheme as illustrated in
Two control samples void of the ionic interactions present in nanoscale ionic materials in accordance with the embodiments were prepared for comparison. The first control sample (Control-I) was prepared by simply adding the silica solution (HS30)-Na+ without the ion exchange step directly to the PEG-NH2 solution in the appropriate ratio. The second control sample (Control-II) was prepared by adding ion-exchanged silica (HS30)-OH to α-ω OH-terminated polyethylene glycol in the appropriate ratios.
Chemical and Physical Characterization
Dynamic light scattering (DLS) and zeta potential measurements were obtained in water at 25° C. using a Malvern Nano-ZS zetasizer.
Thermogravimetric analysis (TGA) measurements were obtained using a TA Instruments TGA Q5000 apparatus. Samples were heated at 10° C./min in platinum pans with a dry nitrogen purge gas.
Differential scanning calorimetry (DSC) measurements were obtained using a TA Instruments DSC Q2000 apparatus. Samples of approximately 4-8 mg were sealed in hermetic pans, and heated to 160° C. at 10° C./min to eliminate any previous thermal history before being cooled to 100° C. and heated again to 160° C. at the same rate.
Rheological measurements were obtained using an Anton-Paar Physica MCR-501 rheometer apparatus. The rheometer in turn used a 25 mm diameter parallel plate geometry, and a separation of 0.5 mm in a temperature controlled dry nitrogen atmosphere. All measurements were made at 75° C. For oscillatory measurements, an amplitude sweep was undertaken first, and then oscillation measurements were undertaken using an amplitude that kept the response in the linear viscoelastic range.
Transmission electron microscopy (TEM) measurements were obtained using an FEI T-12 apparatus. A filament voltage of 120 kV was also used. Samples were either deposited on a TEM grid directly from a water suspension, or microtomed into thin films onto carbon-coated grids obtained from Electron Microscope Supplies, Inc.
Results and Discussion
The pH and zeta potential of the as obtained, Na+ stabilized silica suspension are 11 and −30 mV, respectively. Passing the silica through a proton exchanged resin resulted in a suspension with a pH of 3 and a zeta potential of −5 mV. The pH and zeta potential values indicate that nearly all surface groups are in the neutral protonated form as illustrated in
The acidity of silica surface hydroxyls (silanols) is well established, although the exact pKa values will generally depend on the details of the system under investigation. Typically, two pKa values have been reported for silanols. One of the pKa values is in the 4-5 range, and the other is in the 8-10 range. The more acidic groups are reported to make up anywhere between 10% to 20% of the total surface silanols.
The amount of amine functional polyethylene glycol canopy organic polymer material required for full neutralization of the available silanol groups within the acidified silica inorganic metal oxide core was determined by locating an equivalence point in the titration curve for the two materials.
(SiO2)—OH+H2N—R→(SiO2)—O−H3N+—R
Aliquots of the solution were taken at regular intervals and the particle size was measured while using the above described dynamic light scattering apparatus and methodology. When the amine functional polyethylene glycol material was added dropwise to the silica, the suspension turned turbid instantly suggesting that particle aggregation took place. In contrast, the suspension remained clear if the silica was added drop-wise to a solution of the amine. To avoid particle aggregation all subsequent titrations were undertaken by adding the silica suspension to the amine solution.
After the neutralization reaction, the zeta potential of the resulting suspension was about ζ=−17 mV, indicating that the protons from the hydroxyls had reacted with the terminal amine groups on the PEG-NH2, and the particles were again more negatively charged. Electrical conductivity measurements show an ionic conductivity of 2×10e−5 S/cm confirming the ionic character of the samples prepared in accordance with the embodiments. The equivalence point obtained from the titration curve corresponds to a sample containing ˜20 wt % silica (abbreviated as H-20). Using the mass fraction of silica, and assuming an average radius and density of 9 nm and 2.2 g/cm3, respectively for the silica nanoparticles, one may calculate approximately 1100 PEG chains per silica particle, which corresponds with about 0.8 OH groups per square nanometer surface area of silica reacted. This value is approximately 15% of the ˜5 OH groups per square nanometer commonly reported suggesting that it is the more acidic of the two forms of hydroxyls mentioned above that are reacting with the amine. Samples with silica compositions above the equivalence point are not completely neutralized while those below the equivalent point contain excess PEG molecules.
The transmission electron microscopy images of
Oscillatory shear measurements provide a useful probe into the rheological behavior of the system.
It is possible to obtain characteristic relaxation times from both flow and oscillatory rheological measurements. For flow curves, the relaxation time is estimated as the reciprocal of the shear rate where the viscosity becomes shear-rate dependent, while for oscillatory curves it is the reciprocal of the frequency at which the complex viscosity becomes frequency-dependent.
The approximate relaxation times for the nanoscale ionic material samples in accordance with the embodiments are τH-25=1600 s, τH-20=12.5 s, τH-15=5 s, and τH-10=1.2 s, (the subscript refers to the mass fraction of silica) and is approximately the same for flow and oscillatory measurements. One may consider that this relaxation time may be due to the movement of the core silica nanoparticles through the organic polymer material chains. The abrupt decrease in relaxation time for H-20 corresponds to the fully neutralized sample. Comparison of H-20 with the control HC-20 shows that the long relaxation is much slower for HC-20, with an extrapolated time, τHC-20˜1500 s, as compared to τH-20=12.5 s for H-20. One may attribute the longer relaxation time to the diffusion of larger, more aggregated particles and the absence of ionic interactions in the control sample.
Demonstrated in accordance with the foregoing embodiment is a new platform of nanoparticle ionic material compositions (i.e. including nanoscale ionic liquid material compositions, nanoscale ionic gel material compositions and nanoscale ionic solid material compositions) synthesized and prepared by reacting directly acidified silica nanoparticles with an average diameter of 18 nm with an amine-terminated polyethylene glycol, PEG-NH2 in an acid-base reaction. In contrast with alternative systems, the inventive approach eliminates an intervening surface modification processing step intended to create a charged corona surrounding a silica nanoparticle and thus greatly simplifies the synthesis protocol and reduces the number of system components. Additionally, a processing scheme for a nanoscale ionic material composition in accordance with the embodiments eliminates any dialysis or ultrafiltration steps previously required to ensure absence of byproducts. Since all steps required to synthesize the new fluids are simple and scalable the process can be readily integrated into current manufacturing.
In addition, an equivalence point obtained from a neutralization reaction when preparing a nanoscale ionic material in accordance with the foregoing illustrative embodiments corresponds with a sample containing ˜20 wt % silica. This silica content corresponds to about 1100 PEG chains per particle, suggesting that approximately 15% of the available OH groups are reacted. The presence of ionic species is corroborated by zeta potential and electrical conductivity measurements. The presence of ionic species endows the materials with a unique behavior. First, they show remarkable dispersion of the SiO2 nanoparticles into the polymer. The materials become liquids at 70° C. and exhibit an ionic conductivity of 10e−5 S/cm. The fully neutralized sample corresponding to the equivalence point in the neutralization reaction shows abrupt decreases in the melting point and heat of fusion. More importantly, compared to two series of controls composed of a physical mixture with the same ratio of SiO2 to PEG (i.e. systems that are void of any electrostatic interactions) the ionic SiO2 fluids exhibit remarkably different dispersion and flow properties. G″ being greater than G′ throughout the frequency range and shear thinning behavior are consistent with a viscoelastic fluid behavior for the silica nanoscale ionic materials in accordance with the embodiments. In addition, the relative zero-shear viscosity of the silica nanoscale ionic materials in accordance with the embodiments is at least three orders of magnitude lower compared to one of the controls, Control-II, which exhibits solid-like behavior. The other control is also solid and with a modulus/viscosity outside the range of the rheometer capabilities.
All references, including publications, patent applications, and patents cited herein are hereby incorporated by reference in their entireties to the extent allowed, and as if each reference was individually and specifically indicated to be incorporated by reference and was set forth in its entirety herein.
The use of the terms “a” and “an” and “the” and similar referents in the context of describing the invention (especially in the context of the following claims) is to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e., meaning “including, but not limited to,”) unless otherwise noted. The term “connected” is to be construed as partly or wholly contained within, attached to, or joined together, even if there is something intervening.
The recitation of ranges of values herein is merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and each separate value is incorporated into the specification as if it was individually recited herein.
All methods described herein may be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, or exemplary language (e.g., “such as”) provided herein, is intended merely to better illuminate embodiments of the invention and does not impose a limitation on the scope of the invention unless otherwise claimed.
No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the invention.
It will be apparent to those skilled in the art that various modifications and variations can be made to the present invention without departing from the spirit and scope of the invention. There is no intention to limit the invention to the specific form or forms disclosed, but on the contrary, the intention is to cover all modifications, alternative constructions, and equivalents falling within the spirit and scope of the invention, as defined in the appended claims. Thus, it is intended that the present invention cover the modifications and variations of this invention provided they come within the scope of the appended claims and their equivalents.
This application is related to, and derives priority from, U.S. Provisional Patent Application Ser. No. 61/466,805, filed 22 Mar. 2011 and titled “Ionic Fluid and Method of Manufacture,” the contents of which are incorporated herein fully by reference.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US2012/029910 | 3/21/2012 | WO | 00 | 11/21/2013 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2012/129279 | 9/27/2012 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6225374 | Vaia et al. | May 2001 | B1 |
| 7915353 | Lee et al. | Mar 2011 | B2 |
| 20050266246 | Reiss et al. | Dec 2005 | A1 |
| 20070254994 | Giannelis et al. | Nov 2007 | A1 |
| 20090017378 | Charest et al. | Jan 2009 | A1 |
| 20090208845 | Howard | Aug 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 2005037397 | Apr 2005 | WO |
| Entry |
|---|
| Commissioner, International Search Report and Written Opinion, Korean Intellectual Property Office, dated Oct. 29, 2012. |
| Bourlinos et al., Surface-Functionalized Nanoparticles with Liquid-Like Behavior, Advanced Materials, 2005, 17, No. 2, Jan. 31, 234-237. |
| Bhattacharjee et al., A Plasmonic Fluid with Dynamically Tunable Optical Properties, Journal of Materials Chemistry, 2009, 19, 8728-8731. |
| Fernandes et al., Fullerol Ionic Fluids, Nanoscale, 2010, 2, 1653-1656. |
| Giannelis, Emmanuel P., Synthesizing Optimal NIMS for Carbon Capture, Chemical and Biomolecular Engineering & Materials Science and Engineering, Cornell University, Jun. 16, 2008. |
| Meerwall et al., Canopy Molecular Mobility in Nanoscale Ionic Materials, Session B4: Biophysics and Nanomaterials May 1, 2010. |
| Jespersen et al., Canopy dynamics in Nanoscale ionic material, ACS NANO, 2010, vol. 4, No. 7, 3735-3742. |
| Mullens et al., Modified silica-containing matrices towards the MALDI-TOF-MS detection of small molecules, International Journal of Mass Spectrometry 308 (2011) 311-315. |
| Rodriguez et al., nanoscale ionic material, Advanced material, 2008,20,4353. |
| Fernandes et al., A silica nanoparticle based ionic material, Bulletin of the American Physical Society, APS March Meeting 2011, vol. 56, No. 1. |
| Rodriguez, Robert, Nanoscale Ionic Materials: Synthesis and Properties, Theses and Dissertations (CLOSED). |
| Meerwall et al., Canopy Dynamics in a Nanoscale Ionic Material, American Physical Society, 2011 Fall Meeting of the APS Ohio-Region Section. |
| Rodriguez et al., The synthesis and properties of nanoscale ionic materials, Appl. Organometal. Chem. 2010, 24, 581-589. |
| Rodriguez et al., Nanoscale Ionic Materials, Advanced Materials, 2008, vol. 20, Issue: 22, 4353-4358. |
| Park, Ah-Hyung Alissa, CO2Capture using Nanoparticle-based Ionic Materials (NIMs), Columbia University presentation, May 4, 2010. |
| An et al., Preparation and self-assembly of carboxylic acid-functionalized silica, Journal of Colloid and Interface Science 311 (2007) 507-513. |
| Schoonman, J., Nanostructured materials in solid state ionics, Solid State Ionics 135 (2000) 5-19. |
| Number | Date | Country | |
|---|---|---|---|
| 20140070139 A1 | Mar 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61466805 | Mar 2011 | US |