Patent Application
20200052297
The present invention relates to nanostructured materials (including nanowires) for use in batteries. Exemplary materials include carbon-comprising, Si-based nanostructures, nanostructured materials disposed on carbon-based substrates, and nanostructures comprising nanoscale scaffolds. The present invention also provides methods of preparing battery electrodes, and batteries, using the nanostructured materials.
Traditional batteries, including lithium (Li) ion batteries, comprise an anode, a separator material with an electrolyte medium, and a cathode. The anode electrode of most commercially available Li ion batteries is a copper foil coated with a mixture of graphite powder and a polymer blend such as polyvinylidene difluoride (PVDF). The cathode generally comprises a mixture of lithium transition metal oxides, PVDF and carbon black coated onto an aluminum foil. While graphite and LiCoO2 are normally used, and have high coulombic efficiencies, there is a need for improved anode materials with superior storage capacity and thermal stability.
One material that has attracted a great deal of attention is silicon (Si), due to its high capacity. However, repeated charging/discharging cycles have been found to cause a volume change in the Si, which can ultimately cause the material to disintegrate and severely limit any potential battery life. Thus, there is a need for improved electrode materials for use in batteries, and specifically, Si-based materials.
In one embodiment the present invention provides additives for use in a battery slurry. Suitably, such additives comprise one or more carbon-comprising, Si-based nanostructures. Exemplary Si-based nanostructures include Si-based nanowires and Si-based nanoparticles. Suitably, the nanowires have a core-shell structure, and in exemplary embodiments, the core comprises Si, and the shell comprises C. The Si-based nanowires suitably have a diameter of about 20 nm to about 200 nm, and a length of about 0.1 μm to about 50 μm.
In embodiments, the additives comprise about 1 weight % to about 80 weight % (more suitably about 10 weight %) of the slurry. In exemplary embodiments, a conductive polymer, such as polyvinylidene difluoride, is disposed on the Si-based nanostructures. The present invention also provides battery slurries comprising one or more carbon-comprising, Si-based nanostructures. Exemplary characteristics of the Si-based nanostructures, including Si-based nanowires, are described herein. Suitably, the battery slurries comprise about 1 weight % to about 80 weight % (suitably about 10 weight %) of the carbon-comprising, Si-based nanostructures. In exemplary embodiments, the battery slurries further comprise a carbon-based material, such as carbon or graphite.
In another embodiment, the additives of the present invention comprise one or more nanostructures disposed on a carbon-based substrate. Exemplary nanostructures include nanowires or nanoparticles, such as nanowires having a core-shell structure. Suitably, the nanowires comprise a crystalline core (e.g., Si) and non-oxide, amorphous shell (e.g., Si or C). In exemplary embodiments, the nanowires or nanoparticles comprise Si. Suitably, the nanowires have a diameter of about 20 nm to about 200 nm, and a length of about 0.1 μm to about 50 μm.
Exemplary carbon-based substrates include a carbon-based powder, carbon black, graphite, graphene, graphene powder and graphite foil. Suitably, the carbon-based powder includes particles of about 5 microns to about 50 microns, e.g., about 20 microns. Suitably, the additives of the present invention comprise about 1 weight % to about 80 weight % (e.g., about 10 weight %) of the slurry. The additives can further comprise a conductive polymer, such as polyvinylidene difluoride, disposed on the nanostructures.
In a further embodiment, the additives of the present invention comprise one or more nanostructures comprising a nanoscale scaffold, a Si-based layer disposed on the nanoscale scaffold and a carbon-based layer disposed on the Si-based layer. Exemplary nanoscale scaffolds include nanowires, nanofibers, and nanotubes. Suitably, the nanowires have a diameter of about 20 nm to about 200 nm, and a length of about 0.1 μm to about 50 μm.
The present invention also provides a battery slurry and/or battery electrodes (e.g., anodes) comprising one or more of the carbon-comprising Si-based nanostructures, the nanostructures disposed on a carbon-based substrate, and/or the nanostructures comprising a nanoscale scaffold, as described herein. Exemplary nanostructures, including compositions and characteristics of the nanostructures are described throughout. In exemplary embodiments, the nanostructures, such as nanowires, comprise Li inserted in the nanowires. In exemplary embodiments, the electrodes comprise about 1 weight % to about 80 weight % (e.g., about 10 weight %) of the nanostructures. Suitably, the nanostructures are embedded in a Li foil.
The present invention also provides batteries having an anode comprising one or more of the nanostructures of the present invention. Suitably, the batteries are Li ion batteries. The batteries of the present invention also suitably further comprise a cathode, and an electrolyte separator positioned between the anode and the cathode. Exemplary cathode materials include, but are not limited to, LiCoO2, LiFePO4, LiMnO2, LiMnO4, LiNiCoAlO/LiNiCoMnO+LiMn2O4, LiCoFePO4 and LiNiO2. Suitably, the batteries further comprise a housing encasing the anode, the electrolytic separator and the cathode.
The present invention also provides methods of preparing a battery electrode. Suitably, the methods comprise providing one or more of the nanostructures of the present invention. The nanostructures are mixed with a conductive polymer and a carbon-based material to form a slurry. The slurry is formed into the battery electrode.
The present invention also provides methods of preparing a battery. Suitably, the methods comprise providing one or more nanostructures. The nanostructures are mixed with a conductive polymer and a carbon-based material to form a slurry. The slurry is formed into a battery anode, and a separator is disposed between the anode and a cathode.
The present invention also provides methods of preparing a carbon-coated nanostructure. Suitably, the methods comprise providing a nanoscale scaffold. A carbon-comprising polymer is disposed on the nanoscale scaffold. The carbon-comprising polymer is heated to form a carbon coating on the nanoscale scaffold.
The present invention further provides methods for preparing an additive for use in a battery slurry. Suitably, the methods comprise providing a carbon-based powder. A Si-based nanostructure is disposed on the carbon-based powder.
Further embodiments, features, and advantages of the invention, as well as the structure and operation of the various embodiments of the invention are described in detail below with reference to accompanying drawings.
The invention is described with reference to the accompanying drawings. In the drawings, like reference numbers indicate identical or functionally similar elements. The drawing in which an element first appears is indicated by the left-most digit in the corresponding reference number.
It should be appreciated that the particular implementations shown and described herein are examples of the invention and are not intended to otherwise limit the scope of the present invention in any way. Indeed, for the sake of brevity, conventional electronics, manufacturing, semiconductor devices, and nanowire (NW), nanorod, nanotube, and nanoribbon technologies and other functional aspects of the systems (and components of the individual operating components of the systems) may not be described in detail herein. Furthermore, for purposes of brevity, the invention is frequently described herein as pertaining to nanowires, though other similar structures are also encompassed herein.
It should be appreciated that although nanowires are frequently referred to, the techniques described herein are also applicable to other nanostructures, such as nanorods, nanoparticles, nanopowder, nanotubes, nanotetrapods, nanoribbons, nanosheets and/or combinations thereof.
As used herein, an “aspect ratio” is the length of a first axis of a nanostructure divided by the average of the lengths of the second and third axes of the nanostructure, where the second and third axes are the two axes whose lengths are most nearly equal to each other. For example, the aspect ratio for a perfect rod would be the length of its long axis divided by the diameter of a cross-section perpendicular to (normal to) the long axis.
The term “heterostructure” when used with reference to nanostructures refers to nanostructures characterized by at least two different and/or distinguishable material types. Typically, one region of the nanostructure comprises a first material type, while a second region of the nanostructure comprises a second material type. In another embodiment, the nanostructure comprises a core of a first material and at least one shell of a second (or third etc.) material, where the different material types are distributed radially about the long axis of a nanowire, a long axis of an arm of a branched nanocrystal, or the center of a nanocrystal, for example. A shell need not completely cover the adjacent materials to be considered a shell or for the nanostructure to be considered a heterostructure. For example, a nanocrystal characterized by a core of one material covered with small islands of a second material is a hetero structure. In other embodiments, the different material types are distributed at different locations within the nanostructure. For example, material types can be distributed along the major (long) axis of a nanowire or along a long axis or arm of a branched nanocrystal. Different regions within a hetero structure can comprise entirely different materials, or the different regions can comprise a base material.
As used herein, a “nanostructure” is a structure having at least one region or characteristic dimension with a dimension of less than about 500 nm, e.g., less than about 200 nm, less than about 100 nm, less than about 50 nm, or even less than about 20 nm. Typically, the region or characteristic dimension will be along the smallest axis of the structure. Examples of such structures include nanowires, nanopowder, nanorods, nanofilms, nanotubes, branched nanocrystals, nanotetrapods, tripods, bipods, nanocrystals, nanodots, quantum dots, nanoparticles, branched tetrapods (e.g., inorganic dendrimers), and the like. Nanostructures can be substantially homogeneous in material properties, or in other embodiments can be heterogeneous (e.g., heterostructures). Nanostructures can be, for example, substantially crystalline, substantially monocrystalline, polycrystalline, amorphous, or combinations thereof. In one aspect, one of the three dimensions of the nanostructure has a dimension of less than about 500 nm, for example, less than about 200 nm, less than about 100 nm, less than about 50 nm, or even less than about 20 nm.
As used herein, the term “nanowire” generally refers to any elongated conductive or semiconductive material (or other material described herein) that includes at least one cross sectional dimension that is less than 500 nm, and suitably, less than 200 nm, or less than 100 nm, and has an aspect ratio (length:width) of greater than 10, preferably greater than 50, and more preferably, greater than 100, for example, up to about 1000, or more.
As used herein, a “nanoparticle” refers to a particle, crystal, sphere, or other shaped structure having at least one region or characteristic dimension with a dimension of less than about 500 nm, suitably less than about 200 nm, less than about 100 nm, less than about 50 nm, less than about 20 nm, or less than about 10 nm. Suitably, all of the dimensions of the nanoparticles utilized in the present invention are less than about 50 nm, and suitably have a size of about 1 nm to about 30 nm, or about 1 nm to about 20 nm, about 1 nm to about 10 nm, about 1 nm to about 9 nm, about 1 nm to about 8 nm, about 1 nm to about 7 nm, about 1 nm to about 6 nm, about 1 nm to about 5 nm, about 1 nm to about 4 nm, about 1 nm to about 3 nm, or about 1 nm to about 2 nm, for example, about 1 nm, about 2 nm, about 3 nm, about 4 nm, about 5 nm, about 6 nm, about 7 nm, about 8 nm, about 9 nm, or about 10 nm.
The nanowires of this invention can be substantially homogeneous in material properties, or in other embodiments can be heterogeneous (e.g. nanowire heterostructures). The nanowires can be fabricated from essentially any convenient material or materials, and can be, e.g., substantially crystalline, substantially monocrystalline, polycrystalline, amorphous, or combinations thereof. Nanowires can have a variable diameter or can have a substantially uniform diameter, that is, a diameter that shows a variance less than about 20% (e.g., less than about 10%, less than about 5%, or less than about 1%) over the region of greatest variability and over a linear dimension of at least 5 nm (e.g., at least 10 nm, at least 20 nm, or at least 50 nm). Typically the diameter is evaluated away from the ends of the nanowire (e.g., over the central 20%, 40%, 50%, or 80% of the nanowire). A nanowire can be straight or can be e.g., curved or bent, over the entire length of its long axis or a portion thereof. In other embodiments, a nanowire or a portion thereof can exhibit two- or three-dimensional quantum confinement.
Examples of such nanowires include semiconductor nanowires as described in Published International Patent Application Nos. WO 02/017362, WO 02/048701, and WO 01/003208, carbon nanotubes, and other elongated conductive or semiconductive structures of like dimensions, which are incorporated herein by reference.
As used herein, the term “nanorod” generally refers to any elongated conductive or semiconductive material (or other material described herein) similar to a nanowire, but having an aspect ratio (length:width) less than that of a nanowire. Note that two or more nanorods can be coupled together along their longitudinal axis. Alternatively, two or more nanorods can be substantially aligned along their longitudinal axis, but not coupled together, such that a small gap exists between the ends of the two or more nanorods. In this case, electrons can flow from one nanorod to another by hopping from one nanorod to another to traverse the small gap. The two or more nanorods can be substantially aligned, such that they form a path by which electrons can travel.
A wide range of types of materials for nanostructures, including nanowires, nanocrystals, nanoparticles, nanopowders, nanorods, nanotubes and nanoribbons can be used, including semiconductor material selected from, e.g., Si, Ge, Sn, Se, Te, B, C (including diamond), P, BC, BP(BP6), BSi, SiC, SiGe, SiSn, GeSn, WC, SiO2, TiO2, BN, BAs, AlN, AlP, AlAs, AlSb, GaN, GaP, GaAs, GaSb, InN, InP, InAs, ZnO, ZnS, ZnSe, ZnTe, CdS, CdSe, CdTe, HgS, HgSe, HgTe, BeS, BeSe, BeTe, MgS, MgSe, GeS, GeSe, GeTe, SnS, SnSe, SnTe, PbO, PbS, Pb Se, PbTe, CuF, CuCl, CuBr, CuI, AgF, AgCl, AgBr, AgI, BeSiN2, CaCN2, ZnGeP2, CdSnAs2, ZnSnSb2, CuGeP3, CuSi2P3, (Cu, Ag)(Al, Ga, In, Tl, Fe)(S, Se, Te)2, Si3N4, Ge3N4, Al2O3, (Al, Ga, In)2 (S, Se, Te)3, Al2CO, and an appropriate combination of two or more such semiconductors.
Nanowires of the present invention may also comprise organic polymers, ceramics, inorganic semiconductors such as carbides and nitrides, and oxides (such as TiO2 or ZnO), carbon nanotubes, biologically derived compounds, e.g., fibrillar proteins, etc. or the like. For example, in certain embodiments, inorganic nanowires are employed, such as semiconductor nanowires. Semiconductor nanowires can be comprised of a number of Group IV, Group III-V or Group II-VI semiconductors or their oxides. In one embodiment, the nanowires may include metallic conducting, semiconducting, carbide, nitride, or oxide materials such as RuO2, SiC, GaN, TiO2, SnO2, WCx, MoCx, ZrC, WNx, MoNx etc. As used throughout, the subscript “x,” when used in chemical formulae, refers to a whole, positive integer (e.g., 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, etc). It is suitable that the nanowires be made from a material that is resistant to degradation in a weak acid. Nanowires according to this invention can include, or can expressly exclude, carbon nanotubes, and, in certain embodiments, exclude “whiskers” or “nanowhiskers”, particularly whiskers having a diameter greater than 100 nm, or greater than about 200 nm.
In other aspects, the semiconductor may comprise a dopant from a group consisting of: a p-type dopant from Group III of the periodic table; an n-type dopant from Group V of the periodic table; a p-type dopant selected from a group consisting of: B, Al and In; an n-type dopant selected from a group consisting of: P, As and Sb; a p-type dopant from Group II of the periodic table; a p-type dopant selected from a group consisting of: Mg, Zn, Cd and Hg; a p-type dopant from Group IV of the periodic table; a p-type dopant selected from a group consisting of: C and Si.; or an n-type dopant selected from a group consisting of: Si, Ge, Sn, S, Se and Te. Other now known or later developed dopant materials can be employed.
Additionally, the nanowires can include carbon nanotubes, or nanotubes formed of conductive or semiconductive organic polymer materials, (e.g., pentacene, and transition metal oxides).
It should be understood that the spatial descriptions (e.g., “above”, “below”, “up”, “down”, “top”, “bottom”, etc.) made herein are for purposes of illustration only, and that devices of the present invention can be spatially arranged in any orientation or manner.
Nanostructures have been produced in a wide variety of different ways. For example, solution based, surfactant mediated crystal growth has been described for producing spherical inorganic nanomaterials, e.g., quantum dots, as well as elongated nanomaterials, e.g., nanorods and nanotetrapods. Other methods have also been employed to produce nanostructures, including vapor phase methods. For example, silicon nanocrystals have been reportedly produced by laser pyrolysis of silane gas.
Other methods employ substrate based synthesis methods including, e.g., low temperature synthesis methods for producing, e.g., ZnO nanowires as described by Greene et al. (“Low-temperature wafer scale production of ZnO nanowire arrays,” L. Greene, M. Law, J. Goldberger, F. Kim, J. Johnson, Y. Zhang, R. Saykally, P. Yang, Angew. Chem. Int. Ed. 42, 3031-3034, 2003), and higher temperature vapor-liquid-solid (VLS) methods that employ catalytic gold particles, e.g., that are deposited either as a colloid or as a thin film that forms a particle upon heating. Such VLS methods of producing nanowires are described in, for example, Published International Patent Application No. WO 02/017362, the full disclosure of which is incorporated herein by reference in its entirety for all purposes.
Nanostructures can be fabricated and their size can be controlled by any of a number of convenient methods that can be adapted to different materials. For example, synthesis of nanocrystals of various composition is described in, e.g., Peng et al. (2000) “Shape Control of CdSe Nanocrystals” Nature 404, 59-61; Puntes et al. (2001) “Colloidal nanocrystal shape and size control: The case of cobalt” Science 291, 2115-2117; U.S. Pat. No. 6,306,736 to Alivisatos et al. (Oct. 23, 2001) entitled “Process for forming shaped group III-V semiconductor nanocrystals, and product formed using process;” U.S. Pat. No. 6,225,198 to Alivisatos et al. (May 1, 2001) entitled “Process for forming shaped group II-VI semiconductor nanocrystals, and product formed using process;” U.S. Pat. No. 5,505,928 to Alivisatos et al. (Apr. 9, 1996) entitled “Preparation of III-V semiconductor nanocrystals;” U.S. Pat. No. 5,751,018 to Alivisatos et al. (May 12, 1998) entitled “Semiconductor nanocrystals covalently bound to solid inorganic surfaces using self-assembled monolayers;” U.S. Pat. No. 6,048,616 to Gallagher et al. (Apr. 11, 2000) entitled “Encapsulated quantum sized doped semiconductor particles and method of manufacturing same;” and U.S. Pat. No. 5,990,479 to Weiss et al. (Nov. 23, 1999) entitled “Organo luminescent semiconductor nanocrystal probes for biological applications and process for making and using such probes.” The disclosures of each of these publications are incorporated by reference herein in their entireties.
Growth of nanowires having various aspect ratios, including nanowires with controlled diameters, is described in, e.g., Gudiksen et al. (2000) “Diameter-selective synthesis of semiconductor nanowires” J. Am. Chem. Soc. 122, 8801-8802; Cui et al. (2001) “Diameter-controlled synthesis of single-crystal silicon nanowires” Appl. Phys. Lett. 78, 2214-2216; Gudiksen et al. (2001) “Synthetic control of the diameter and length of single crystal semiconductor nanowires” J. Phys. Chem. B 105, 4062-4064; Morales et al. (1998) “A laser ablation method for the synthesis of crystalline semiconductor nanowires” Science 279, 208-211; Duan et al. (2000) “General synthesis of compound semiconductor nanowires” Adv. Mater. 12, 298-302; Cui et al. (2000) “Doping and electrical transport in silicon nanowires” J. Phys. Chem. B 104, 5213-5216; Peng et al. (2000) “Shape control of CdSe nanocrystals” Nature 404, 59-61; Puntes et al. (2001) “Colloidal nanocrystal shape and size control: The case of cobalt” Science 291, 2115-2117; U.S. Pat. No. 6,306,736 to Alivisatos et al. (Oct. 23, 2001) entitled “Process for forming shaped group III-V semiconductor nanocrystals, and product formed using process;” U.S. Pat. No. 6,225,198 to Alivisatos et al. (May 1, 2001) entitled “Process for forming shaped group II-VI semiconductor nanocrystals, and product formed using process”; U.S. Pat. No. 6,036,774 to Lieber et al. (Mar. 14, 2000) entitled “Method of producing metal oxide nanorods”; U.S. Pat. No. 5,897,945 to Lieber et al. (Apr. 27, 1999) entitled “Metal oxide nanorods”; U.S. Pat. No. 5,997,832 to Lieber et al. (Dec. 7, 1999) “Preparation of carbide nanorods;” Urbau et al. (2002) “Synthesis of single-crystalline perovskite nanowires composed of barium titanate and strontium titanate” J. Am. Chem. Soc., 124, 1186; and Yun et al. (2002) “Ferroelectric Properties of Individual Barium Titanate Nanowires Investigated by Scanned Probe Microscopy” Nanoletters 2, 447. The disclosures of each of these publications are incorporated by reference herein in their entireties.
In certain embodiments, the nanowires of the present invention are produced by growing or synthesizing these elongated structures on substrate surfaces. By way of example, published U.S. Patent Application No. US-2003-0089899-A1 (the disclosure of which is incorporated by reference herein) discloses methods of growing uniform populations of semiconductor nanowires from gold colloids adhered to a solid substrate using vapor phase epitaxy/VLS. Greene et al. (“Low-temperature wafer scale production of ZnO nanowire arrays”, L. Greene, M. Law, J. Goldberger, F. Kim, J. Johnson, Y. Zhang, R. Saykally, P. Yang, Angew. Chem. Int. Ed. 42, 3031-3034, 2003) discloses an alternate method of synthesizing nanowires using a solution based, lower temperature wire growth process. A variety of other methods are used to synthesize other elongated nanomaterials, including the surfactant based synthetic methods disclosed in U.S. Pat. Nos. 5,505,928, 6,225,198 and 6,306,736, for producing shorter nanomaterials, and the known methods for producing carbon nanotubes, see, e.g., US-2002/0179434 to Dai et al., as well as methods for growth of nanowires without the use of a growth substrate, see, e.g., Morales and Lieber, Science, V.279, p. 208 (Jan. 9, 1998). As noted herein, any or all of these different materials may be employed in producing the nanowires for use in the invention. For some applications, a wide variety of group III-V, II-VI and group IV semiconductors may be utilized, depending upon the ultimate application of the substrate or article produced. In general, such semiconductor nanowires have been described in, e.g., US-2003-0089899-A1, incorporated herein above. The disclosures of each of these publications are incorporated by reference herein in their entireties.
Growth of branched nanowires (e.g., nanotetrapods, tripods, bipods, and branched tetrapods) is described in, e.g., Jun et al. (2001) “Controlled synthesis of multi-armed CdS nanorod architectures using monosurfactant system” J. Am. Chem. Soc. 123, 5150-5151; and Manna et al. (2000) “Synthesis of Soluble and Processable Rod-, Arrow-, Teardrop-, and Tetrapod-Shaped CdSe Nanocrystals” J. Am. Chem. Soc. 122, 12700-12706. The disclosures of each of these publications are incorporated by reference herein in their entireties.
Synthesis of nanoparticles is described in, e.g., U.S. Pat. No. 5,690,807 to Clark Jr. et al. (Nov. 25, 1997) entitled “Method for producing semiconductor particles”; U.S. Pat. No. 6,136,156 to El-Shall, et al. (Oct. 24, 2000) entitled “Nanoparticles of silicon oxide alloys;” U.S. Pat. No. 6,413,489 to Ying et al. (Jul. 2, 2002) entitled “Synthesis of nanometer-sized particles by reverse micelle mediated techniques;” and Liu et al. (2001) “Sol-Gel Synthesis of Free-Standing Ferroelectric Lead Zirconate Titanate Nanoparticles” J. Am. Chem. Soc. 123, 4344. The disclosures of each of these publications are incorporated by reference herein in their entireties. Synthesis of nanoparticles is also described in the above citations for growth of nanocrystals, nanowires, and branched nanowires, where the resulting nanostructures have an aspect ratio less than about 1.5.
Synthesis of core-shell nanostructure heterostructures, namely nanocrystal and nanowire (e.g., nanorod) core-shell heterostructures, are described in, e.g., Peng et al. (1997) “Epitaxial growth of highly luminescent CdSe/CdS core/shell nanocrystals with photostability and electronic accessibility” J. Am. Chem. Soc. 119, 7019-7029; Dabbousi et al. (1997) “(CdSe)ZnS core-shell quantum dots: Synthesis and characterization of a size series of highly luminescent nanocrysallites” J. Phys. Chem. B 101, 9463-9475; Manna et al. (2002) “Epitaxial growth and photochemical annealing of graded CdS/ZnS shells on colloidal CdSe nanorods” J. Am. Chem. Soc. 124, 7136-7145; and Cao et al. (2000) “Growth and properties of semiconductor core/shell nanocrystals with InAs cores” J. Am. Chem. Soc. 122, 9692-9702. Similar approaches can be applied to growth of other core-shell nanostructures. The disclosures of each of these publications are incorporated by reference herein in their entireties.
Growth of nanowire heterostructures in which the different materials are distributed at different locations along the long axis of the nanowire is described in, e.g., Gudiksen et al. (2002) “Growth of nanowire superlattice structures for nanoscale photonics and electronics” Nature 415, 617-620; Bjork et al. (2002) “One-dimensional steeplechase for electrons realized” Nano Letters 2, 86-90; Wu et al. (2002) “Block-by-block growth of single-crystalline Si/SiGe superlattice nanowires” Nano Letters 2, 83-86; and U.S. patent application 60/370,095 (Apr. 2, 2002) to Empedocles entitled “Nanowire heterostructures for encoding information.” The disclosures of each of these publications are incorporated by reference herein in their entireties. Similar approaches can be applied to growth of other heterostructures.
As described herein, and throughout co-assigned published Patent Application Nos. 2007/0212538 and 2008/0280169, the entire contents of each of which are incorporated by reference herein, nanowire structures with multiple shells can also be fabricated, such as, for example, a conducting inner core wire (which may or may not be doped) (e.g., to impart the necessary conductivity for electron transport) and one or more outer-shell layers that provide a suitable surface for binding polymer electrolyte. Exemplary nanowires that can be used in the practice of the present invention also include carbon-comprising nanowires, such as those disclosed in Published U.S. Patent Application Nos. 2007/0212538 and 2008/0280169.
In one embodiment, the present invention provides additives for use in a battery slurry. As used herein, an “additive” refers to a composition that is added to a battery slurry, such that a portion (e.g., a weight %) of the original slurry is replaced with the additive composition. As used herein, a “battery slurry” refers to a mixture of components used to form an electrode (anode or cathode) of a battery.
In an embodiment, the additives comprise one or more carbon-comprising, Si-based nanostructures. As used herein, “carbon-comprising” is used to indicate that the nanostructures comprise carbon in at least some form. Suitably, the nanostructures comprise a carbon shell or sheet surrounding, or at least partially surrounding the nanostructure. As used herein, “Si-based” is used to indicate that the nanostructure comprises at least 50% silicon (Si). Suitably, the nanostructures comprise at least 55%, at least 60%, at least 65%, at least 70%, at least 75%, at least 80%, at least 85%, at least 90%, or at least 95% Si.
In another embodiment, the additives comprise one or more nanostructures comprising a nanoscale scaffold, a Si-based layer disposed on the nanoscale scaffold and a carbon-based layer disposed on the Si-based layer. As used herein, a “nanoscale scaffold” refers to a nanostructure upon which one or more other materials, components, layers, coatings, shells, and/or films may be disposed. Example nanoscale scaffolds include nanowires, nanopowder, nanorods, nanofilms, nanotubes, branched nanocrystals, nanotetrapods, tripods, bipods, nanocrystals, nanodots, quantum dots, nanoparticles, branched tetrapods (e.g., inorganic dendrimers), and the like.
The nanostructures of the present invention comprising a nanoscale scaffold, a Si-based layer disposed on the nanoscale scaffold, and a carbon-based layer disposed on the Si-based layer are also referred to herein as nanoscale-scaffold-based compositions, nanoscaffold-based compositions, or simply scaffold-based nanostructures.
In exemplary embodiments, the Si-based nanostructures are Si-based nanowires. Exemplary dimensions for the nanowires of the present invention are described throughout. Suitably, the nanowires have a diameter of about 10 nm to about 500 nm, or about 20 nm to about 400 nm, about 20 nm to about 300 nm, about 20 nm to about 200 nm, about 20 nm to about 100 nm, or about 40 nm to about 100 nm. Suitably, the nanowires have a length of about 100 nm to about 100 μm, or about 1 μm to about 75 μm, about 1 μm to about 50 μm, or about 1 μm to about 20 μm. Suitably, the aspect ratios of the nanowires are up to about 2000:1, or suitably, up to about 1000:1, having a diameter of about 20 nm to about 200 nm, and a length of about 0.1 μm to about 50 μm.
Methods for producing nanowires using vapor-liquid-solid (VLS) processes are disclosed, for example, in published U.S. Patent Application No. US-2003-0089899 (the disclosure of which is incorporated by reference herein). Additional methods for producing nanowires are described herein, and are well known in the art. In exemplary embodiments, in order to produce high volume, high density nanowires, methods disclosed in U.S. Provisional Patent Application No. 61/221,501, filed Jun. 29, 2009, entitled “Methods for Growth of High Density Nanowires,” Attorney Docket No. 2132.0680000, the disclosure of which is incorporated by reference herein in its entirety, are used. Following the nanowire growth, the nanowires are suitably harvested (e.g., via sonication or other mechanical means). The addition of a carbon-comprising layer (e.g., a C shell) can be added to the nanowires immediately following growth, or after harvesting. The nanowires can then be utilized as additives as described herein. Additional processing, such as ball milling, grinding or other mechanical mechanisms to break the nanowires and additives into smaller pieces or shorter segments can also be used.
As described herein, suitably the additives of the present invention can be added to currently existing battery slurries, replacing a portion of the slurry, e.g., a portion of the graphite component, with the carbon-comprising, Si-based nanostructure compositions of the present invention. Battery slurries utilized in commercial grade batteries generally comprise a mixture of graphite, carbon and a polymer binder (e.g., polyvinylidene difluoride (PVDF)). The amounts and ratios of these components generally varies from battery to battery, but slurries usually comprise about 50%-80% graphite, about 40%-10% carbon and about 10% PVDF (all percentages are weight percentages). In exemplary embodiments, a portion of the graphite component of the slurry is suitably replaced by the additives of the present invention. For example, the additives replace about 1 weight % to about 80 weight % of the slurry (replacing an equivalent amount of the graphite). For example, the additives replace about 1 weight %, about 2 weight %, about 3 weight %, about 4 weight %, about 5 weight %, about 6 weight %, about 7 weight %, about 8 weight %, about 9 weight %, about 10 weight %, about 11 weight %, about 12 weight %, about 13 weight %, about 14 weight %, about 15 weight %, about 16 weight %, about 17 weight %, about 18 weight %, about 19 weight %, about 20 weight %, about 21 weight %, about 22 weight %, about 23 weight %, about 24 weight %, about 25 weight %, about 26 weight %, about 27 weight %, about 28 weight %, about 29 weight %, about 30 weight %, about 31 weight %, about 32 weight %, about 33 weight %, about 34 weight %, about 35 weight %, about 36 weight %, about 37 weight %, about 38 weight %, about 39 weight %, about 40 weight %, about 41 weight %, about 42 weight %, about 43 weight %, about 44 weight %, about 45 weight %, about 46 weight %, about 47 weight %, about 48 weight %, about 49 weight %, about 50 weight %, about 51 weight %, about 52 weight %, about 53 weight %, about 54 weight %, about 55 weight %, about 56 weight %, about 57 weight %, about 58 weight %, about 59 weight %, about 60 weight %, about 61 weight %, about 62 weight %, about 63 weight %, about 64 weight %, about 65 weight %, about 66 weight %, about 67 weight %, about 68 weight %, about 69 weight %, about 70 weight %, about 71 weight %, about 72 weight %, about 73 weight %, about 74 weight %, about 75 weight %, about 76 weight %, about 77 weight %, about 78 weight %, about 79 weight %, or about 80 weight % of the slurry.
In exemplary embodiments, the additives of the present invention further comprise a conductive polymer (e.g., a carbon-based polymer) disposed on the nanostructures. Exemplary conductive polymers are described herein and otherwise known in the art, and include, for example, PVDF, polypyrrole, polythiaphene, polyethylene oxide, polyacrylonitrile, poly (ethylene succinate), polypropylene, poly (β-propiolactone), styrene butadiene rubber (SBR), carboxymethyl cellulose salt (CMC) and sulfonated fluoropolymers such as NAFION® (commercially available from DuPont Chemicals, Wilmington), polyimide, poly(acrylic acid) etc. Conductive polymers are suitably uniformly dispersed on the surfaces of the nanostructures, for example, along the lengths of nanowires. The interface between the nanostructures, suitably nanowires, and the conductive polymers also allows for fast charge/discharge cycles of the electrodes prepared using such materials. In addition, the conductive polymer coating on the nanowires also helps to accommodate the volume change in nanowires associated with alkali metal intercalation.
In further embodiments, the present invention provides battery slurries comprising one or more of the carbon-comprising, Si-based nanostructures, as described herein. Exemplary characteristics of the nanostructures are described throughout. As discussed herein, suitably the slurries comprise about 1 weight % to about 80 weight % of the carbon-comprising, Si-based nanostructures (suitably replacing an equivalent amount of the graphite in the slurries).
As described herein, in exemplary embodiments the slurries further comprise a carbon-based material in addition to the nanostructures described throughout. For example, the slurries suitably comprise carbon or graphite in addition to the nanostructures (as well as a polymer binder).
In another embodiment, the additives of the present invention suitably comprise one or more nanostructures disposed on a carbon-based substrate (nanostructure—carbon-based substrate compositions). As shown in
As used herein, the term “disposed” refers to any method of placing one element next to and/or adjacent (including on top of or attached to) another, and includes, spraying, layering, depositing, painting, dipping, bonding, coating, growing, forming, depositing, etc. Suitably, nanostructures are grown on carbon-based substrates. For example, as described throughout, suitably nanostructures 114 are nanowires that have been grown directly on carbon-based substrate 112, or grown separately from carbon-based substrate 112, and then disposed (e.g., attached or otherwise associated) on carbon-based substrate 112.
For example, a catalyst metal, including metal foils or colloids (e.g., gold colloids) is first disposed on the carbon-based substrate. Then, the catalyst metal is contacted with one or more precursor gases to grow nanowires using a VLS-processes. Methods for producing nanowires using such VLS-processes are disclosed, for example, in published U.S. Patent Application No. US-2003-0089899 (the disclosure of which is incorporated by reference herein). Additional methods for producing nanowires are described herein, and are well known in the art. In exemplary embodiments, in order to produce high volume, high density nanowires, methods disclosed in U.S. Provisional Patent Application No. 61/221,501, filed Jun. 29, 2009, entitled “Methods for Growth of High Density Nanowires,” Attorney Docket No. 2132.0680000, the disclosure of which is incorporated by reference herein in its entirety, are used. In such embodiments, following the nanowire growth, the nanowires can be harvested alone and then disposed on carbon-based substrates, or in other embodiments, the nanowires and the carbon-based substrates onto which they are disposed are harvested together. The nanowires and the nanowire-carbon-based substrates can then be utilized as additives as described herein. Additional processing, such as ball milling, grinding or other mechanical mechanisms to break the nanowires and additives into smaller pieces or shorter segments can also be used.
In an embodiment, Si-based nanostructures are grown on carbon-based powder, e.g., graphite powder, without micropores to create a Si-based nanostructure disposed on the graphite powder as shown in
Embodiments of the present invention achieve improved conductivity by growing Si-based nanostructures on graphite powder. In addition, the Si-based nanostructure disposed on graphite powder can be used in a battery-electrode slurry and battery-electrode layers, which leverages the high capacity of Si and the high conductivity of the graphite powder.
Additional embodiments of the present invention achieve improved conductivity by disposing a carbon coating on Si-based nanowires, which may also make it easier to integrate Si-based nanowires in carbon-based slurries for lithium-ion batteries. Lithium-ion battery slurries include a binder, typically comprised of a carbon-comprising polymer (e.g., styrene butadiene rubber (SBR), carboxymethyl cellulose (CMC), polyvinylidene fluoride (PVDF), etc.). In embodiments, the binder is used as a carbon source for carbon coating Si nanowires. Carbonizing Si nanowires using the battery slurry binder suitably improves the interaction between the carbonized Si nanowire and the battery slurry.
The compositions of the present invention comprising nanostructures disposed on carbon-based substrates are also referred to herein as nanostructure-carbon-based substrate compositions, nanowire-carbon-based substrate compositions, or simply nanostructure compositions or nanowire compositions.
As used herein a “carbon-based substrate” refers to a substrate that comprises at least about 50% carbon by mass. Suitably, a carbon-based substrate comprises at least about 60% carbon, 70% carbon, 80% carbon, 90% carbon, 95% carbon or about 100% carbon by mass, including 100% carbon. Exemplary carbon-based substrates that can be used in the practice of the present invention include, but are not limited to, carbon powder, such as carbon black, fullerene soot, desulfurized carbon black, graphite, graphene, graphene powder or graphite foil. As used throughout, “carbon black” refers to the material produced by the incomplete combustion of petroleum products. Carbon black is a form of amorphous carbon that has an extremely high surface area to volume ratio. “Graphene” refers to a single atomic layer of carbon formed as a sheet, and can be prepared as graphene powders. See e.g., U.S. Pat. Nos. 5,677,082, 6,303,266 and 6,479,030, the disclosures of each of which are incorporated by reference herein in their entireties. “Carbon-based substrates” specifically exclude metallic materials, such as steel, including stainless steel. Carbon-based substrates can be in the form of sheets, or separate particles, as well as cross-linked structures.
Suitably, the nanostructure-carbon-based substrate compositions, the carbon-comprising, Si-based nanostructures, and/or the scaffold-based nanostructures form an “ink,” which can easily be manipulated and added, i.e., as additive, to various battery slurries, or utilized in the preparation of battery electrodes, as described herein.
Nanostructures comprising Si (i.e., Si-based nanostructures), including Si nanowires, and Si nanoparticles, are suitably used in the practice of the present invention due to their ability to absorb the volume change associated with charging and discharging cycles of a rechargeable battery. Silicon has the highest known capacity of all materials, and lithiated silicon (Li15Si4, the highest lithiated phase achievable for ambient temperature lithiation of silicon) has a corresponding capacity of about 3579 m Ah/g (milliamp hours per gram) before lithiation. In addition, silicon is abundant, inexpensive and safer to manufacture and utilize than graphite. However, from x-ray data, the calculated density of Li15S14 is 1.179 g/cm3. Thus, when silicon is fully lithiated to Li14S14 it undergoes a volume expansion of 280% and has a maximum theoretical volumetric capacity of 2190 mAh/cm3 after lithiation. This volume expansion renders bulk silicon impractical for use in a battery, as the material disintegrates upon repeated charge and discharge cycles, and thus severely limits battery life.
The nanostructures of the present invention—such as, for example, scaffold-based nanostructures, nanowires, including Si nanowires, disposed on carbon-based substrates, or carbon-comprising, Si-based nanowires—absorb the volume change associated with lithiation during repeated charge/discharge cycles. The use of carbon-based structures such as graphene, carbon-black and other carbon-based substrates, aid in the absorbance of the volume change in the slurry, as the structures can easily bend, flex, and deform. In addition, the overall structure of the nanowires allows for volume change within the slurries without generating excessive forces due to the strain of the wires during deformation. A carbon shell or sheet surrounding Si-based nanowires also aids in the absorption of volume changes.
As described herein in embodiments, the nanowires for use in the practice of the present invention have a core-shell structure. Suitably, the nanowires comprise a crystalline core and non-oxide, amorphous shell. That is, the shell of the nanowire does not contain an oxide. In further embodiments, the shell can include an oxide, such as with silicon nanowires. In further embodiments, the nanowires can be of a core-shell-shell structure (or additional shells). Exemplary core-shell (and core-shell-shell) nanowire compositions are described throughout. Suitably the shell of the nanowires is an alkali metal-alloy forming materials, such as a lithium alloy-forming material. Suitably a material that allows alkali metal (e.g., Li) intercalation, or has a high Li solubility (e.g., >0.1%). Suitably, the core or a first shell of the nanowires is a good thermal conductor (e.g., thermal conductivity of k>0.2 Wm−1K (watts per meter*Kelvin)) at room temperature, and a good electrical conductor (e.g., resistance of R<5 ohm).
In exemplary embodiments, the carbon-comprising, Si-based nanowires, nanowire-carbon-based substrate compositions, or scaffold-based nanostructures of the present invention form a porous network in which the nanowires intertwine, interweave or overlap. This arrangement takes the form of a porous structure, wherein the size of pores between the nanowires is suitably mesopores and macropores. As used herein the term “mesopores” refers to pores that are larger than micropores (micropores are defined as less than about 2 nm in diameter), but smaller than macropores (macropores are defined as greater than about 50 nm in diameter), and suitably have a pore size in the range of greater than about 30 nm to less than about 200 nm in diameter. Suitably, the compositions of the present invention will be substantially free of micropores, that is, less than about 0.1% of the pores will be micropores (i.e., less than about 2 nm in diameter). The porous nature these nanowire structures allows for increase mass transport of electrolyte through the structures, resulting in rapid diffusion of the alkali metal ions.
In suitable embodiments, the nanowires comprise Si, suitably a Si core, and a shell comprising C. While nanowires comprising a SiC core, or a SiC shell can also be used, suitably the nanowires do not comprise a carbide shell (i.e., SP3 carbon), but instead simply comprise a carbon shell (i.e., SP2 carbon) that is covalently bonded to the silicon core. In the case of SiC nanowires, the carburization process is suitably controlled so as to generate partially carburized Si nanowires (see Published U.S. Patent Application No. 2008/0280169) with strongly bonded carbon nanoparticles. Nanowires of the present invention are able to accommodate the associated volume change with alkali metal (e.g., Li) intercalation. Other suitable materials for use in the core of the nanowires are described herein and include TiO2.
The use of a core-shell (or multiple shell) nanowire structure in the compositions of the present invention provide enhanced cycling (charging/discharging) performance, most likely due to the formation of passivating films on the surface of the nanowires. An initial capacity loss can originate from the reduction of the electrolyte on the nanowire surface, resulting in the formation of a solid electrolyte interface (SEI) on the nanowire surface, or from irreversible alkali metal (e.g., Li) insertion/intercalation into the nanostructures. Preformation of an artificial SEI layer (through chemical modification) on the nanostructures, and or pre-lithiating of the nanostructures, can be used to enhance performance. In embodiments, a shell comprises a metal and/or metal oxide, such as Cu, Tin oxide, Ni, and the like. Si nanowire surface conductivity can be improved in this manner, and reduce the volume change of the Cu/SiNWs or Ni/SiNWS so that a thin, dense and stable SEI can be maintained on the surface. Such metal and/or metal oxide shells can also reduce the consumption of Li in the battery. A shell comprising a metal oxide such as tin oxide, for example, also permits Li ions to diffuse through the shell, yet prevent solvents in the electrolyte from penetrating.
In embodiments, nanowires for use in the present invention can further comprise nanoparticles on their surface. For example, the nanoparticles can be graphite or graphene particles or layers. In embodiments where the nanowires are used to prepare anodes, as described herein, suitably the nanowires can further comprise nanoparticles of Si or TiO2 on their surface. In embodiments where the nanowires are used to prepare cathodes, the nanowires can comprise nanoparticles of LiNiSiO4, LiNiSiO, LiFeO2, etc. The nanoparticles decorating the surface of the nanowires of the present invention are utilized in a highly efficient manner (acting as intercalating or alloying materials) due to the high curvature of the nanowire surface (e.g., radius of less than about 100 nm) on which they are disposed, thus exposing a large number of the nanoparticles to the external environment.
Li—Si alloy compositions can be passivated in polar aprotic electrolyte solutions and by Li-ion conducting surface films that behave like a solid electrolyte interface. Ionic liquids can also be introduced to modify Si nanowire surface chemistry. Thus, surface chemistry modification can be realized by tuning components in the electrolyte solutions.
Exemplary dimensions for the nanowires of the present invention are described throughout. Suitably, the nanowires have a diameter of about 10 nm to about 500 nm, or about 20 nm to about 400 nm, about 20 nm to about 300 nm, about 20 nm to about 200 nm, about 20 nm to about 100 nm, or about 40 nm to about 100 nm. Suitably, the nanowires have a length of about 100 nm to about 100 or about 1 μm to about 75 about 0.1 to about 50 or about 1 μm to about 20 Suitably, the aspect ratios of the nanowires are up to about 2000:1, or suitably, up to about 1000:1. Such high aspect ratios allow for electrons that are generated on the nanowires to be rapidly passed between the nanowires to the conducting electrode. In addition, nanowires with diameters of less than about 50 nm, and aspect ratios of greater than about 1000:1, demonstrate increased flexibility when undergoing the volume change associated with cycling between charged and discharged states, as described herein.
In further embodiments, the nanowires for use in the practice of the present invention can be porous nanowires, such as porous Si nanowires. Electrochemical cycling during lithiation and delithiation produces pores on the walls of the nanostructures. It has been hypothesized that the presence of these pores may increase the ability of the nanostructures to accommodate volume changes, and also to increase the surface area available for contact with conductive polymers and alkali metals. Preparation of porous nanostructures, including porous nanowires, can be carried out by electrochemical cycling. In an additional embodiment, a pore forming material can be incorporated into the nanostructures and then removed to generate the porous nanostructures. For example, Sn or other secondary components can be integrated into the nanostructures (e.g., Si nanowires), and then removed by chemical (e.g., etching) or physical methods. These porous nanostructures, including porous Si nanowires are then utilized in the carbon-comprising, Si-based nanostructure compositions, the nanostructure-carbon-based substrate compositions, the scaffold-based nanostructures, and additives of the present invention.
Preparation of the additives of the presently claimed invention, including carbon-comprising, Si-based nanowire, nanowire-carbon-based substrate compositions, and scaffold-based nanostructures suitably utilize nanowire alignment methods such as those disclosed in Published U.S. Patent Application No. 2008/0224123 (the disclosure of which is incorporated by reference herein in its entirety) to generate high density nanowire compositions. Exemplary alignment methods include the use of fluid flow and shear extrusion to align the nanowires, as well as e-field alignment and deposition onto various substrates, including carbon-based substrates. Spraying can be utilized to introduce nanowires and/or conductive polymers to the nanowires. The nanowires can also be bent and compressed in order to form a more dense and interwoven composition.
As described herein, suitably the additives of the present invention can be added to currently existing battery slurries, replacing a portion of the slurry, e.g., a portion of the graphite component. Battery slurries utilized in commercial grade batteries generally comprise a mixture of graphite, carbon and a polymer binder (e.g., polyvinylidene difluoride (PVDF)). The amounts and ratios of these components generally varies from battery to battery, but slurries usually comprise about 50%-80% graphite, about 40%-10% carbon and about 10% PVDF (all percentages are weight percentages). In exemplary embodiments, a portion of the graphite component of the slurry is suitably replaced by the additives of the present invention. For example, the additives replace about 1 weight % to about 80 weight % of the slurry (replacing an equivalent amount of the graphite).
In exemplary embodiments, the additives of the present invention further comprise a conductive polymer disposed on the nanostructures. Exemplary conductive polymers are described herein and otherwise known in the art, and include, for example, PVDF, polypyrrole, polythiaphene, polyethylene oxide, polyacrylonitrile, poly(ethylene succinate), polypropylene, poly (β-propiolactone), styrene butadiene rubber (SBR), carboxymethyl cellulose salt (CMC), and sulfonated fluoropolymers such as NAFION® (commercially available from DuPont Chemicals, Wilmington), etc. Conductive polymers are suitably uniformly dispersed on the surfaces of the nanostructures, for example, along the lengths of nanowires. The interface between the nanostructures, suitably nanowires, and the conductive polymers also allows for fast charge/discharge cycles of the electrodes prepared using such materials. In addition, the conductive polymer coating on the nanowires also helps to accommodate the volume change in nanowires associated with alkali metal intercalation.
In further embodiments, the present invention provides battery slurries comprising one or more of the carbon-comprising, Si-based nanostructures, the nanostructure-carbon-based-substrate compositions, and/or the scaffold-based nanostructures as described herein. Exemplary characteristics of the nanostructures are described throughout. As discussed herein, suitably the slurries comprise about 1 weight % to about 80 weight % of the nanostructure-carbon-based-substrate compositions (suitably replacing an equivalent amount of the graphite in the slurries).
As described herein, in exemplary embodiments the slurries further comprise a carbon-based material in addition to the nanostructures described throughout. For example, the slurries suitably comprise carbon or graphite in addition to the nanostructures (as well as a polymer binder).
The present invention also provides battery electrodes comprising one or more additives of the presently claimed invention (i.e., the carbon-comprising, Si-based nanostructures, the nanostructure-carbon-substrate based compositions, and/or scaffold-based nanostructures). As shown in
As described throughout, suitably the nanostructures for use in the battery electrodes are nanowires, nanoparticles, or nanofilms. Exemplary compositions of the nanostructures, including core-shell and core-shell-shell nanowires are described throughout. In exemplary embodiments, the nanostructures are Si nanostructures, including Si nanowires, and core-shell nanowires in which the core is Si and the shell C, covalently linked to the core. Exemplary sizes of nanowires for use in the battery electrodes are described throughout.
As described herein, suitably the nanostructure compositions replace about 1 weight % to about 80 weight % of the battery slurry. Thus, when used to prepare a battery electrode, the nanostructure compositions also comprise about 1 weight % to about 80 weight % of the electrode, suitably about 5 weight % to about 20 weight %, about 5 weight % to about 15 weight %, about 5 weight % to about 10 weight %, or about 10 weight % of the battery electrode.
In suitable embodiments, compositions of the present invention suitably comprise a conductive polymer disposed on the nanostructures. Exemplary conductive polymers are described herein, and include for example, polyvinylidene difluoride, polypyrrole, polythiaphene, polyethylene oxide, polyacrylonitrile, poly(ethylene succinate), polypropylene, poly (β-propiolactone), styrene butadiene rubber (SBR), carboxymethyl cellulose salt (CMC), and sulfonated fluoropolymers such as NAFION® (commercially available from DuPont Chemicals, Wilmington), etc. The conductive polymer also serves as a binder material when forming electrodes 120.
In further embodiments, the carbon-comprising, Si-based nanostructures, the nanostructure-carbon-based substrates, and scaffold-based nanostructures of the battery electrodes further comprise an alkali metal (e.g., lithium (Li), sodium (Na), potassium (K), rubidium (Rb), caesium (Cs), or francium (Fr)). For example, nanostructures of the present invention can be embedded in an alkali metal foil, such as a lithium (Li) foil. Composites of the nanostructure compositions and alkali metal (e.g., alkali metal films) are highly conductive and as described throughout, demonstrate the ability of the nanostructures (e.g., Si nanostructures) to accommodate the large volume change due to ion insertion.
The present invention also provides batteries comprising the various carbon-comprising, Si-based nanostructures, nanostructure-carbon-based substrate compositions, and/or scaffold-based nanostructures of the present invention. The schematic shown in
In embodiments, as shown in
The carbon-comprising, Si-based nanostructure compositions, the nanostructure-carbon-based substrate compositions, and the scaffold-based nanostructures, and additives of the present invention can be utilized in any battery type. In exemplary embodiments, the batteries of the present invention are Li-ion batteries. That is, the batteries are suitably rechargeable batteries in which a lithium ion 206 moves between the anode 202 and cathode 204. The lithium ion moves from the anode to the cathode during discharge and in reverse, from the cathode to the anode, when charging.
As described herein, the ability of alkali metals, e.g., Li, to insert into the nanostructures of the present invention provides increased capacity. However, due to the ability of the nanostructures, including nanowires (e.g., Si nanowires) to absorb the volume change that accompanies this insertion, the anodes remain structurally sound. The ability of lithium to insert into the nanowires, particularly Si nanowires, provides for a dramatic increase in the capacity of anodes prepared from such materials.
Suitably, the anodes 202 of the batteries 200 of the present invention comprise about 1 weight % to about 80 weight % (suitably about 5 weight % to about 20 weight %, or about 10 weight %) of the nanostructures of the present invention. A conductive polymer—such as polyvinylidene difluoride, styrene butadiene rubber (SBR), or carboxymethyl cellulose—is also suitably disposed on the nanostructures. In exemplary embodiments, anode 202 comprises Si nanostructures embedded in a Li foil.
As shown in
As shown in
In embodiments, the present invention provides methods of preparing an additive for use in a battery slurry. As shown in flowchart 2000 of
In further embodiments, the present invention provides methods of preparing a battery electrode. As shown in flowchart 300 of
Exemplary nanostructures, including nanowires, are disclosed herein, as are compositions and characteristics of the nanostructures. Suitably, the nanostructures are Si nanowires, including core-shell (or core-shell-shell) nanowires in which the core of the nanowires comprises Si.
As noted throughout, suitably the carbon-comprising, Si-based nanostructure compositions of the present invention are utilized as additives in conventional battery slurries to generate electrodes (e.g., anodes). As noted throughout, suitably such additives are provided at about 1 weight % to about 80 weight % of the electrode, more suitably about 5 weight % to about 20 weight %, or about 10 weight % of the electrode. As noted herein, suitably the electrodes prepared according to the methods of the present invention are anodes of lithium-ion batteries.
Step 304 of flowchart 300 suitably comprises mixing the carbon-comprising, Si-based nanostructure compositions with a conductive polymer such as polyvinylidene difluoride, styrene butadiene rubber (SBR), and/or carboxymethyl cellulose salt (CMC). Other suitable conductive polymers are described herein or otherwise known in the art. The carbon-comprising, Si-based nanostructure compositions are also suitably mixed with an additional carbon-based material. Examples of such additional carbon-based substrates are described throughout, and include, carbon, carbon black, graphite, graphene, graphene powder or graphite foil. This combination forms a battery slurry typically used to form electrodes.
The present invention provides further methods of preparing a battery electrode. As shown in flowchart 310 of
Exemplary nanostructures, including nanowires, are disclosed herein, as are compositions and characteristics of the nanostructures. Suitably, the nanostructures are Si nanowires, including core-shell (or core-shell-shell) nanowires in which the core of the nanowires comprises Si. Exemplary carbon-based substrates are also described herein, and suitably include carbon black, graphite, graphene, carbon-based powder, graphene powder or graphite foil.
As noted throughout, suitably the nanostructure-carbon-based substrate compositions of the present invention are utilized as additives in conventional battery slurries to generate electrodes (e.g., anodes). As noted throughout, suitably such additives are provided at about 1 weight % to about 80 weight % of the electrode, more suitably about 5 weight % to about 20 weight %, or about 10 weight % of the electrode. As noted herein, suitably the electrodes prepared according to the methods of the present invention are anodes of lithium-ion batteries.
Step 314 of flowchart 310 suitably comprises mixing the nanostructure-carbon-based substrate compositions with a conductive polymer such as polyvinylidene difluoride. Other suitable conductive polymers are described herein or otherwise known in the art. The nanostructure-carbon-based substrate compositions are also suitably mixed with an additional carbon-based material (in addition to the carbon-based substrates on which the nanostructures are disposed). Examples of such additional carbon-based substrates are described throughout, and include, carbon, carbon black, graphite, graphene, graphene powder or graphite foil. This combination forms a battery slurry typically used to form electrodes.
As shown in flowchart 400 of
As shown in flowchart 410 of
Methods of preparing lithium batteries, as well as suitable components for cathodes, separator materials, and electrolytes, can be found, for example, in “Lithium batteries: Science and Technology,” G Nazri and G. Pistoia, eds., Springer, New York (2004), the disclosure of which is incorporated by reference herein in its entirety. These well known methods are suitably combined with the methods and nanostructure compositions described herein to prepare batteries.
As described throughout, exemplary nanostructures include nanowires, nanoparticles, or nanofilms, suitably Si nanostructures, such as Si nanowires, and core-shell (including core-shell-shell) nanowires. Suitable characteristics and sizes of the nanostructures, such as nanowires, are described throughout as well. Exemplary carbon-based substrates are also described herein.
Suitably, the carbon-comprising, Si-based nanostructures, the nanostructure-carbon-based substrate compositions, and the scaffold-based nanostructures of the present invention comprise about 1 weight % to about 80 weight % of the anode, suitably about 10 weight %. In suitable embodiments, the nanostructures are mixed with a polyvinylidene difluoride conductive polymer and graphite and/or carbon to prepare the slurry in step 404/414 that ultimately will become the battery anode. Additional conductive polymers and carbon-based materials are described herein.
In suitable embodiments, a conductive polymer membrane (separator 208) is disposed between the anode and the cathode in step 408/418. Exemplary conductive polymer membranes are disclosed herein or otherwise known in the art.
Methods of preparing the anode, separator and cathode to form the battery include rolling, heating, drying and storage methods (including temperatures and times) that are well known in the art. See for example, “Lithium batteries: Science and Technology,” and U.S. Pat. Nos. 6,165,642, 7,541,114 6,440,606, 5,681,357, 5,688,293 and 5,834,135 the disclosures of each of which are incorporated by reference herein in their entireties.
As described herein, the carbon-comprising, Si-based nanostructure compositions, the nanostructure-carbon-based substrate compositions, and the scaffold-based nanostructures of the present invention are suitably used as additives in conventional battery electrode (e.g., anode) formation techniques. Thus, these additives are easily substituted in the battery manufacturing process by simply replacing a portion of the battery electrode slurry with the presently disclosed additives (e.g., about 1 weight % to about 80 weight %, suitably about 5 weight % to about 20 weight %, or about 10 weight %). The remainder of the traditional battery formation process is then followed. No additional modifications are required when using the additives of the present invention, though the processes can be further modified if desired.
The present invention provides further methods of preparing a carbon-coated nanostructure. As shown in flowchart 1900 of
In a step 1904 of flowchart 1900, a carbon-comprising polymer is disposed on the nanoscale scaffold 152. The carbon-comprising polymer may comprise, for example, styrene butadiene rubber (SBR), carboxymethyl cellulose (CMC), polyvinylidene fluoride (PVDF), and the like, and combinations thereof.
In a step 1906, the carbon-comprising polymer is heated to form a carbon coating 156 on the nanoscale scaffold 152. The carbon-comprising polymer may be heated to about 160° C. to about 1000° C. For example, the carbon-comprising polymer may be heated to about 200° C. to about 400° C., about 250° C. to about 350° C., or about 300° C. As another example, it may be heated to about 600° C. to about 800° C., about 650° C. to about 750° C., or about 700° C. As a further example, it may be heated to about 800° C. to about 1000° C., about 850° C. to about 950° C., or about 900° C. The carbon-comprising polymer may be heated for a duration of about 30 minutes to about 5 hours, about 1 hour to about 3 hours, or about 2 hours. The heating may be done in the presence of an inert gas, such as neon, argon, krypton, or xenon.
As illustrated in a step 1908, such methods may also optionally include disposing a Si-based layer 154 (e.g., crystalline Si and/or amorphous Si) on the nanoscale scaffold 152, prior to disposing the carbon-comprising polymer, in which case the carbon-comprising polymer is disposed on the Si-based layer 154.
As described herein, in the Examples set forth below, and in Provisional Patent Application No. 61/179,663, filed May 19, 2009, the disclosure of which is incorporated by reference herein in its entirety, the present invention overcomes the limitations of bulk silicon and harnesses the high charge capacity of silicon in the form of nanowires. The nanowires suitably have diameters in the 10's of nanometer range, and aspect ratios of about 1000. The nanowires are able to absorb the large volume changes caused by lithiation and de-lithiation during charging and discharging without losing their structural integrity.
The following Examples describe silicon nanowire (Si NW) performance in practice. For implementation in Li-ion batteries, the Si NWs are suitably used as a low-volume (about 5-30 weight %) filler in anodes. This approach allows for easy integration into existing product lines while still providing a significant boost in performance. An addition of 10% by weight of SiNW has been found to result in a battery anode capacity boost of about 30%-50%.
It will be readily apparent to one of ordinary skill in the relevant arts that other suitable modifications and adaptations to the methods and applications described herein can be made without departing from the scope of the invention or any embodiment thereof. Having now described the present invention in detail, the same will be more clearly understood by reference to the following examples, which are included herewith for purposes of illustration only and are not intended to be limiting of the invention.
Vapor-liquid-solid (VLS) methods are utilized for growing Si nanowires. The wires are single crystalline with diameters between about 20 nm and about 200 nm and lengths between about 1 μm and about 50 μm. The growth processes allow for high degrees of freedom in the design of shape, size, composition etc. For example, nanowires are able to be manufactured that are substantially straight and with a yield of greater than about 99% (see
The methods of the present invention can be utilized to prepare silicon nanowires on a variety of different substrate materials and form factors. For use as an additive to battery slurries, nanowires are suitably grown onto carbon black, graphite or on loose graphene nanosheet powder surfaces. In all three cases, it is very straightforward to mix the substrate/Si nanowire compositions/additives into anode materials. As described throughout, growing Si nanowires on graphene or carbon powders allows the structures to accommodate the large volume change during lithiation and delithiation of Si materials. Thus, the Si nanowire materials can be utilized directly in graphite based inks or slurries.
Carbon black is an effective growth substrate for the nanowires as well as a suitable matrix material for a battery anode, and can easily be integrated into slurry formulations. The nanowires can be grown on carbon black, as well as on other substrates, in densities that can be adjusted in a wide range and thus tailored to the desired performance characteristics.
The micrographs in
These protrusions in thin film material result in a reduction of the conductivity of the Si material itself, and hence decrease the capacity of Si material over cycling. However, in the case of Si core nanowires coated with a C shell, these protrusions provide the benefit of creating more surface area and even shorter diffusion paths for the lithium ions as compared to a smooth nanowire. In addition, loss in electronic conductivity is avoided by the presence of carbon on the wire surface and carbon powders or graphite powders in the electrode. This extra surface area provides an increase, rather than a decrease, in the capacity of a battery anode containing Si nanowires of the present invention with increasing number of charge cycles.
Nanowires provide a continuous electronic conduction path that does not appear to be achieved at the same level with spherical nanoparticles. Spheres by their very nature only have a limited number of sphere-to-sphere point contacts that contribute to electronic conductivity. Nanowires also provide an additional degree of freedom in adjusting the porosity.’
Capacity of Si Nanowires on a Stainless Steel Electrode with Lithium Foil Counter Electrode
In order to measure the charge capacity and cycle efficiency of Si nanowires, the nanowires were grown on a steel substrate as an anode, and used in conjunction with lithium foil as the counter electrode.
These measurements clearly demonstrate the theoretical charge capacity can be demonstrated with 40 nm thick wires. As described below, these Si nanowires have been used to develop an electrode that provides an enhanced capacity that can be maintained for 80 cycles without little to no reduction.
Comparison of Silicon Nanowires with Silicon Thin Films and Powder
Si nanowires behave quite differently than Si thin films, bulk Si, or Si powders. When silicon nanowires are produced on a stainless steel substrate, a thin layer of silicon is also produced on the stainless substrate between the bases of the nanowires. The measurements provided herein therefore contain contributions from both the nanowires and the Si thin film.
A distinctly different behavior can be seen in
A carbon coating suitably improves the conductivity of Si nanowires and the ability to integrate the Si nanowires into carbon-based slurries for lithium-ion batteries. A carbon-based polymer (such as, SBR, CMC, PVDF, etc.) is typically used as a binder in the battery slurries. In embodiments, the binder is used as a carbon source for carbon coating on the Si nanowires. Carbonizing the carbon-based polymer to form a carbon coating on Si nanowires may also improve the interaction between the carbon-based polymer and the carbon coating on the Si nanowires.
Si nanowires that have a carbon coating (e.g., a surface layer of carbon or a carbon shell) show a better cycling performance when used in a lithium-ion battery. The improved performance may be due to formation of passivating films on the surface of electrode materials, especially for Si and carbon-coated Si.
To approximate commercial battery formulations and for purposes of a baseline and control, a mixture of 80% graphite with 10% carbon and 10% PVDF (Li-G-C-PVDF) was utilized as a battery slurry. To determine the capacity of the nanowire materials of the present invention, 10% of the graphite was replaced with 10% Si Nanowire material (Li-SiNW-G-C-PVDF).
As described herein, suitably the nanowires of the additives of the present invention are arranged in an interwoven, interleaving or overlapping network. For an efficient battery design, however, it is important to uniformly distribute carbon as well as the binder (e.g., conductive polymer or “polymer binder”). In order to demonstrate the uniform distribution of polymer, lead (Pb)-stained NAFION® was used as a model substance that could be tracked using Energy Dispersive X-Ray (EDX) analysis.
Heat-treated battery electrodes may improve binder distribution and, therefore, may lead to better cycling. In one example, a foil with PVDF-SiNW-graphite-conductive carbon black was heated at 300° C. under 4% hydrogen in Argon for 8 hours. The melting point of PVDF is about 160° C. The onset temperature of PVDF decomposition is higher than 350° C., so 300° C. is an effective temperature for heat treatments of embodiments of the present invention.
Heat-treated Si nanowire-graphite-PVDF electrodes may improve adhesion to the current collector (e.g., Cu) and, more importantly, may make a relatively dense/uniform coating layer. The improved adhesion of the coating layers on the current collector may lead to better cycling performance. In addition, a better interaction between the binder and active material powders may also result in reduced changes in the solid electrolyte interphase (SEI), which also influences cycling performances.
Manufacturing and Integration into Existing Slurry Preparations
As described herein, Si nanowires can be disposed on a number of substrates. Using the methods described throughout, nanowire diameter (e.g., 20-200 nm), length (e.g., to about 50 um), taper (usually targeted to be zero), size distribution (>+/−20% full width at half-maximum), and doping (if desired), over a wide range and with high yield, can be readily controlled. Nanowires with Si cores and SiC shells with adjustable core/shell ratios and graphitic surface layers can be readily produced. Production output has been scaled-up by 100× from the lab scale and successfully tested in a prototype for a manufacturing line designed for high volume (50 tons of Si NWs per year) production.
An exemplary manufacturing process is shown in
Exemplary embodiments of the present invention have been presented. The invention is not limited to these examples. These examples are presented herein for purposes of illustration, and not limitation. Alternatives (including equivalents, extensions, variations, deviations, etc., of those described herein) will be apparent to persons skilled in the relevant art(s) based on the teachings contained herein. Such alternatives fall within the scope and spirit of the invention.
All publications, patents and patent applications mentioned in this specification are indicative of the level of skill of those skilled in the art to which this invention pertains, and are herein incorporated by reference to the same extent as if each individual publication, patent or patent application was specifically and individually indicated to be incorporated by reference.
This application is a continuation of U.S. patent application Ser. No. 12/783,243, filed May 19, 2010, which claims the benefit of U.S. Provisional Application Nos. 61/179,663, entitled “Nanowire Enabled Battery Technology”, filed May 19, 2009, 61/221,392 entitled “Nanostructured Materials For Battery Applications”, filed Jun. 29, 2009, and 61/255,732 entitled “Nanostructured Materials For Battery Applications”, filed Oct. 28, 2009, which are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61179663 | May 2009 | US | |
| 61221392 | Jun 2009 | US | |
| 61255732 | Oct 2009 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12783243 | May 2010 | US |
| Child | 16599795 | US |