Patent Application
20080128274
Embodiments are generally related to gas sensors. Embodiments are also related to the field of NOx sensors using nano-crystalline CeO2. Embodiments are additionally related to CeO2 (MOS) NOx sensors for high temperature applications.
The role of gases and the measurement of their concentration have always received wide spread applications in many fields of science and technology. This has resulted in an increasing demand for small scale solid-state sensors. NOx sensors for automotive exhaust gas environments are of great interest because of high expectations of nanostructured materials and ever increasing demands on emission control legislations. The sensitivity of a gas sensor is defined as the ratio of the resistance of the sensor element in air to the resistance of the sensor element in the test gas atmosphere (S=Rair/Rgas).
Many processes and devices have been used for sensing exhaust gases from automobile engines. NOx is one of the unwanted exhaust gases which pollute the environment. NOx is a term used to describe the total oxides of nitrogen, which are commonly estimated from the measured NO, based on the assumption that the total NOx is (combination of NO and NO2 with varying concentrations depend upon the engine conditions ranging from 40% to 5% for NO2 and 60% to 95% of NO). This assumption is generally acceptable when combustion exhaust gases are measured at the outlet of a combustion system and the oxygen concentration is low. If the measurement is made at the exhaust outlet or in the atmosphere, the NO2 is likely much higher than total 5% of the total NOx.
Measurement of NO and NO2 is recommended for accurate total NOx formation. NOx is important to measure because of reactions involving volatile organic compounds (VOCs) with nitrogen oxides (NOx) in the presence of sunlight form ozone in the atmosphere. Ground-level ozone and NOx for example, causes throat irritation, congestion, chest pains, nausea and labored breathing. Ozone can also aggravate respiratory conditions, such as chronic lung and heart diseases, allergies and asthma. Additionally, Ozone ages the lungs and may contribute to various types of lung diseases.
NOx is found in emissions from aircraft, automobiles and industrial factories and contributes to the production of acid rain, smog, and the depletion of the ozone layer. With the increase in the number of vehicles traveling the earth, the amount of NOx produced is also increasing, thereby causing a dangerous situation for the environment. Therefore, a reliable NOx sensor to monitor and control emissions while exposed to the harsh conditions is needed.
The development of gas sensor devices with optimized selectivity and sensitivity has been gaining prominence in recent years. The use of semiconductor fabrication line is the preferred manufacturing process because of the potential to reduce cost. However fundamental materials and processing issues which are critical for high performance gas sensors need to be addressed. Among the new technologies a nano-crystalline material offers immense promise for improved sensitivity.
Nano-crystalline materials are currently receiving a great deal of attention due to their unique physical properties, which derive from their nanometer scaled sizes. In nano-sized materials, for example, the surface to bulk ratio is much greater than coarse materials, so that the surface properties become paramount, which makes them particularly appealing in applications, such as gas sensors, where nano-sized properties can be exploited. Grain size reduction, for example, is one of the main factors for enhancing the gas sensing properties of semiconducting oxides. It is believed that improved sensing technologies can therefore be configured and developed by taking advantage of recent advances in nano-sized materials.
The following summary is provided to facilitate an understanding of some of the innovative features unique to the embodiments disclosed and is not intended to be a full description. A full appreciation of the various aspects of the embodiments can be gained by taking the entire specification, claims, drawings, and abstract as a whole.
It is, therefore, one aspect of the present invention to provide for an improved NOx sensor to monitor and control emissions when exposed to harsh conditions.
It is another aspect of the present invention to provide for a gas sensor that utilizes nano-sized CeO2 particles to detect NOx and study the cross sensitivity for oxygen, unburnt hydrocarbons, CO and CO2.
The aforementioned aspects and other objectives and advantages can now be achieved as described herein. CeO2 nano-crystalline powders are synthesized by employing sol-gel, co-precipitation as well as chemical vapor synthesis (CVS). Such powders are used for configuring thin films of CeO2 on platinum inter digital comb type electrodes performed on alumina substrates to form a sensor thereof. On the other side of the sensor, a platinum heater is provided to maintain the sensor at high temperatures. The nano powders obtained by the above said methods are dispersed on these substrates by dip coating, or screen printing by adding the appropriate binders for making thin and thick films. Dispersing the nano-crystalline powders in organic solvents and by employing electrophoresis techniques, thin films also can be fabricated.
Sintering is carried out to enhance the adherence of these films to the substrate. Thick films are also prepared by using screen printing techniques of CeO2 in association with an appropriate binder and sintered at higher temperatures. Such films can be impregnated with 2% platinum particles. The gas sensing properties of NOx can be carried out using a test apparatus, which can indicated that the sensitivity for 2500 pm of NO and NO2 is approximately 250% and the response and recovery time are less than four seconds for the same concentration. The uniqueness of the disclosed technique and device stems from the control of the particle size and shape. Especially with chemical vapor synthesis, the particle size can be controlled up to 8 to 10 nm. Higher particle sizes are also easily achieved.
The accompanying figures, in which like reference numerals refer to identical or functionally-similar elements throughout the separate views and which are incorporated in and form a part of the specification, further illustrate the embodiments and, together with the detailed description, serve to explain the embodiments disclosed herein.
The particular values and configurations discussed in these non-limiting examples can be varied and are cited merely to illustrate at least one embodiment and are not intended to limit the scope thereof.
Referring to
Current voltage properties can be measured using a high voltage source 170 (e.g., a power supply). A stand 150 can also be provided upon which the two-way gas valve 140 and gas sensor 160 are connected. The conductance of the sensor 160 can be measured with a digital multimeter 180 that is connected electrically to the high voltage source 170 and also to a computer 190. The change in resistance can be simultaneously monitored by the digital multimeter 180. The apparatus 100 also includes the control computer 190, which is generally operable to control and manage the overall operation of the testing apparatus 100.
Referring to
Referring to
Referring to
A heating element is used to regulate the sensor temperature, since the finished sensors exhibit different gas response characteristics at different temperature ranges. This heating element can be a platinum or platinum alloy wire, a resistive metal oxide, or a thin layer of deposited platinum. The sensor element 200 can then be processed at a specific high temperature, which determines the specific characteristics of the finished sensor. In the presence of gas, the metal oxide causes the gas to dissociate into charged ions or complexes, which results in the transfer of electrons. The built-in platinum heater 240 thus heats the metal oxide material to an operational temperature range that is optimal for gas to be detected, and can optionally be regulated and controlled by a specific circuit. This specific circuit can be a chip (Application-Specific Integrated Circuit, ASIC) which can control sensor temperature through an independent measurement and heating mechanism of the micro heater present inside the chip.
Referring to
Next, as indicated at block 350, a sintering operation can be carried out to enhance the adherence of these films to the substrate. The difficulty of sintering of CeO2 (as the sintering temperature of CeO2 is beyond 1600 C) is solved by adding inorganic binders mixing (5%) with CeO2. Thick films can also be prepared using a screen printing technique of CeO2 with an appropriate binder and sintered at high temperatures. The cross sensitivity of other gases (e.g., hydrocarbons, CO, CO2 etc) can be checked thoroughly by adding a catalytic metal such as platinum 360 as depicted block 360. The cross sensitivity can thus be reduced to specified limits.
Referring to
In such an application, the sensor may produce a sensitivity of 200% with respect to a change of resistance for 2500 ppm of NO and NO2. The particle size effect begins to occur below 50 nm with an order of magnitude increase in sensitivity for particles in 20 to 30 nm range. This particle size effect is due, in part, to an increase in the surface area since. In this range, a large fraction of the atoms (e.g., up to 50) are generally present at the surface or the interface region so that the structure and properties are different from that of the bulk material. However, the main effect is associated with the depth of the surface space charge region affected by gas adsorption in relation to the particle size. By employing a sol-gel process, for example, a 20 nm size of CeO2 can be obtained. Such nano-powders are preferably mixed with adequate (5 to 10 wt %) amounts of ethylene glycol and the paste is then applied on to the platinum electrodes on an alumina substrate. The other method employed is by adding an appropriate amount (5 to 20% by wt) of binder ink making the printable ink for screen printing to be used for thick film sensor production.
The sensor described herein is very simple to fabricate and possesses a fast response and recovery for the NOx gas because of the presence of the nano-sized particles. Such benefits can be achieved due to the large surface area and reactive nature of the nano-crystalline powders. The cost of the sensor is relatively inexpensive, because large scale manufacturing processes such as screen printing can be employed. The electronics used to measure conductivity change are also much less complex and generally inexpensive. Cerium oxide in a thick film form, for example, can also be prepared using nanopowders and tested for NOx sensing. The methodology and device disclosed herein therefore uses nano-sized CeO2 particles to detect NO and NO2 and employs nano-crystalline powders of CeO2 to configure thin films on Platinum comb type electrodes preformed on alumina substrates.
It will be appreciated that variations of the above-disclosed and other features and functions, or alternatives thereof, may be desirably combined into many other different systems or applications. Also that various presently unforeseen or unanticipated alternatives, modifications, variations or improvements therein may be subsequently made by those skilled in the art which are also intended to be encompassed by the following claims.