The invention relates to a can body for a two-piece beverage container. More particularly, the present invention is directed to a can body having a novel necked in upper portion with threads and a method for making the can body.
Two-piece cans are the most common type of metal containers used in the beer and beverage industry. They are usually formed of aluminum or tin-plated steel. The two-piece can consists of a first cylindrical can body portion having an integral bottom end wall and a second, separately-formed, top end panel portion which, after the can has been filled, is double-seamed thereon to close the open upper end of the container.
An important competitive objective is to reduce the total can weight as much as possible while maintaining its strength and performance in accordance with industry requirements. For pressurized contents such as soft drinks or beer, the end panel must be made of a metal thickness gauge that is on the order of at least twice the thickness of the side wall. Accordingly, to minimize the overall container weight the second end panel should be diametrically as small as possible and yet maintain the structural integrity of the container, the functionality of the end, and also the aesthetically-pleasing appearance of the can.
Beer and beverage marketers have preferred a neck construction having a relatively smooth neck shape between the opening and the diameter can body sidewall. This smooth can neck construction was made by a spin necking process, and apparatus as shown, for example, in U.S. Pat. Nos. 4,058,998 and 4,512,172.
More recently, U.S. Pat. No. 5,497,900 described a die necking method for necking can bodies. The method of the '900 patent contemplates forming a cylindrical neck portion adjacent the cylindrical open end of a container so that the cylindrical neck merged with the cylindrical side wall through a generally smoothly tapered neck portion. The tapered neck portion between the cylindrical neck portion and the cylindrical container side wall initially is defined by a lower, generally arcuate segment having a relatively large internal curvature at the upper end of the cylindrical side wall and an upper, generally arcuate segment having a relatively large external curvature at the lower end of the reduced cylindrical neck. A further tapered portion is then formed at the open end and is forced downwardly while the cylindrical neck is further reduced. The further tapered portion freely integrates with the second arcuate segment which is reformed and the tapered portion is extended. This process is repeated sequentially until the cylindrical neck is reduced to the desired diameter and a smoothly tapered necked-in portion is formed on the end of the side wall. In each necking operation, the tapered portion is not constrained by the die and is freely formed without regard to the specific dimensions of the die transition zone.
The container that is formed by the above die necking process has an aesthetically-pleasing appearance, greater strength and crush resistance and is devoid of the scratches or wrinkles in the neck produced in a spin necking operation. Similar methods are still used today.
More recently, metal beer and beverage containers have produced metal cans to resemble glass bottles. U.S. Pat. Nos. 5,293,765 and 5,822,843 disclose methods and apparatuses for manufacturing threaded aluminum containers which resemble bottles.
One of the drawbacks of producing metal bottles is that the container manufacturer must build new facilities to produce the metal bottle or retrofit current facilities with new tooling to manufacture the metal bottles. Furthermore, the metal bottles are purported to use more than three times the metal used to make an aluminum can.
The present invention is provided to solve the problems discussed above and other problems, and to provide advantages and aspects not provided by prior metal bottles of this type. A full discussion of the features and advantages of the present invention is deferred to the following detailed description, which proceeds with reference to the accompanying drawings.
One embodiment of the present invention is directed to a metal container. The metal container comprises a lower portion and an upper portion. The lower portion comprises an enclosed bottom and a cylindrical sidewall extending upwardly from the enclosed bottom portion having a diameter. The cylindrical sidewall is centered about a longitudinal axis. The upper portion comprises a circumferential shoulder portion, a circumferential neck, and an open end. The circumferential shoulder portion is integral with an uppermost portion of the cylindrical side wall. The circumferential shoulder is smoothly tapered radially inwardly and has a radius of curvature greater than 0.500 inches (1.27 cm). The circumferential neck extends upwardly and radially inwardly from an uppermost portion of the circumferential shoulder. The open end is connected to the circumferential neck. The open end has threads for threadable attachment to a closure member.
In one aspect the first embodiment, circumferential neck is substantially flat.
In another aspect of the first embodiment, a transition region between the circumferential shoulder and the circumferential neck is substantially flat.
In another aspect of the first embodiment, a height of the upper portion is less than 2.6 inches (6.6 cm).
In another aspect of the first embodiment, a height of the metal container is less than 6.3 inches (16.0 cm).
In another aspect of the first embodiment, the radius of curvature of the circumferential shoulder is between 0.500 inches (1.27 cm) and 1.500 inches (3.81 cm).
In another aspect of the first embodiment, the radius of curvature of the circumferential shoulder is between 0.500 inches (1.27 cm) and 1.100 inches (2.79 cm).
In another aspect of the first embodiment, the radius of curvature of the circumferential shoulder is about 1.00 inches (2.54 cm).
In another aspect of the first embodiment, the radius of curvature of the circumferential shoulder is about 0.62 inches (1.57 cm).
In another aspect of the first embodiment, the angle of the circumferential neck is between 20 and 37 degrees.
In another aspect of the first embodiment, the angle of the circumferential neck is about 22 degrees.
In another aspect of the first embodiment, the angle of the circumferential neck is about 35 degrees.
In another aspect of the first embodiment, the upper portion further comprises a second circumferential shoulder portion integral with an uppermost portion of the circumferential neck. The second circumferential shoulder has a lower concave bend joined to an upper convex bend by an upwardly extending intermediate segment.
In another aspect of the first embodiment, the second circumferential neck is directly connected to the open end.
In another aspect of the first embodiment, the circumferential neck comprises a first radially compressed tapered portion having a single compressed lower segment, and a second further radially compressed tapered portion extending from an upper part of the first tapered portion. The second tapered portion is disposed between the first tapered portion and the open end of the metal container.
In another aspect of the first embodiment, metal container further comprises a containment space for holding a liquid. The containment space has a volume of at least 10 ounces (0.30 liters).
In another aspect of the first embodiment, the metal container further comprises a containment space for a holding a liquid. The containment space has a volume of at least 14 ounces (0.41 liters).
A second embodiment of the present invention is directed to a metal container. The metal container comprises a lower portion and an upper portion. The lower portion comprises an enclosed bottom and a cylindrical sidewall extending upwardly from the enclosed bottom portion having a diameter. The cylindrical sidewall is centered about a longitudinal axis. The upper portion comprises a circumferential shoulder, a substantially flat circumferential neck, and an open end. The circumferential shoulder portion is integral with an uppermost portion of the cylindrical side wall. The circumferential shoulder is smoothly tapered radially inwardly and has a radius of curvature greater than 0.500 inches (1.27 cm). The substantially flat circumferential neck is integral with an uppermost portion of the circumferential neck. The neck extends upwardly and radially inwardly from an uppermost portion of the circumferential shoulder, wherein a transition region between the neck and the shoulder is substantially flat. The open end is connected to the circumferential neck. The open end has threads for threadable attachment to a closure member.
A third embodiment of the present invention is directed to a metal container. The metal container comprises a lower portion and an upper portion. The lower portion comprises an enclosed bottom and a cylindrical sidewall extending upwardly from the enclosed bottom portion having a diameter. The cylindrical sidewall is centered about a longitudinal axis. The upper portion comprises a circumferential shoulder, a circumferential neck, and an open end. The circumferential shoulder portion is integral with an uppermost portion of the cylindrical side wall. The circumferential shoulder is smoothly tapered radially inwardly and has a radius of curvature greater than 0.500 inches (1.27 cm). The circumferential neck extends upwardly and radially inwardly from an uppermost portion of the circumferential shoulder. The open end is connected to the circumferential neck. The open end having threads for threadable attachment to a closure member. The upper and lower portions define a containment space for holding between about 10 (0.30 liters) and about 14 ounces (0.41 liters) of liquid.
Another embodiment of the present invention is directed to a method and apparatus for producing the containers described herein.
Other features and advantages of the invention will be apparent from the following specification taken in conjunction with the following drawings.
To understand the present invention, it will now be described by way of example, with reference to the accompanying drawings in which:
While this invention is susceptible of embodiments in many different forms, there is shown in the drawings and will herein be described in detail preferred embodiments of the invention with the understanding that the present disclosure is to be considered as an exemplification of the principles of the invention and is not intended to limit the broad aspect of the invention to the embodiments illustrated.
The present invention is directed to two-piece metal containers having threads for threadable attachment of a closure member, such as a threaded cap, to the open end of the metal container.
It is believed that advantages of the metal containers described herein are increased strength through geometric design and improved processing by allowing existing manufacturing facilities to, for the most part, process the threaded metal containers. The applicants further believe that the container described herein has an aesthetically-pleasing appearance, greater strength, and crush resistance. Metal usage may also be reduced by increasing the strength of the container so that required strength is achieved through geometric design rather than increased metal volume, especially thickness. Metal usage is is further decreased by decreasing the size of the open end thereby decreasing the size of the can end required to seal the open end.
Referring to
The lower portion 12 includes an enclosed bottom 16 and a cylindrical sidewall 18 extending upwardly from the enclosed bottom portion 16.
The bottom 16 has a dome-shaped center panel 17 surround by a generally a circumferential annular support 20. An outer wall 22 extends radially outwardly and upwardly relative to the annular support 20 and joins the bottom 16 with the lowermost portion of the cylindrical sidewall 18.
The cylindrical sidewall 18 is centered about the longitudinal axis 24. In the embodiments illustrated the sidewall 18 is smooth and flat. However, one ordinary skilled in the art would appreciated that any one of a number of forming techniques could be employed to impart a shape and/or texture to the sidewall 18. For instance, the interior of the sidewall 18 could be forced outwardly by a fluid pressure or forming segments, laser treatment could be employed to etch or otherwise mark the sidewall 18, and/or flutes or other designs may be imparted onto the sidewall 18 through mechanical deformation of the sidewall 18.
The upper portion 14 includes a circumferential shoulder portion 26. The shoulder 26 has a convexly curved appearance when viewed from a vantage point external to the container 10. The shoulder 26 has a lowermost point integral with an uppermost portion of the cylindrical sidewall 18. The transition point between the sidewall 18 and shoulder 26 is at a point where the can body 10 begins to curve radially inwardly. Stated another way, the diameter of the container body 10 begins to decrease at the point where the shoulder 26 begins and the sidewall 26 ends.
It is believed that the radius of curvature of the shoulder 26 is important for the aesthetic appearance of the container 10 as well as for the strength of the container 10. It is further believed that these characteristics differentiate the present embodiments for prior art containers of this type. For instance, in the embodiments illustrated, a radius of curvature of the shoulder RS is greater than 0.500 inches (1.27 cm), preferably 0.500 (1.27 cm) to 1.500 inches (3.81 cm), more preferably 0.500 inches (1.27 cm) to 1.100 inches (2.79 cm). In the embodiment illustrated in
The shoulder 26 has a smoothly tapered appearance. This appearance is achieved through a die forming technique similar to the die forming technique disclosed in commonly assigned U.S. Pat. No. 5,497,900 which is hereby incorporated by reference as if fully set forth herein. The smoothly tapered appearance differs from containers produced using alternative methods like spin-necking in that the radius of curvature is much greater so that wrinkles and scratches are avoided as is the unsightliness of an abrupt reduction in the diameter of the container caused by a sharp corner or bend at the shoulder. Thus, a vertical length of the shoulder 26, parallel to the longitudinal axis, is greater than the vertical length of shoulders produced through other forming techniques.
The upper portion 14 further includes an inwardly tapered circumferential neck 28. The neck 28 has a lowermost portion integral with an uppermost portion of the shoulder 26. Thus, the neck 28 functions to further decrease the diameter of the container 10 along the vertical length of the neck 28. The neck 28 is preferentially substantially flat, i.e. primarily free of an arc-shape design, although it may have some discontinuity formed during production. An angle θ of the neck 28, measured from a vertical axis parallel to the longitudinal axis, is greater than 10 degrees, preferably 15 to 60 degrees, and more preferably 20 to 37 degrees. The embodiment illustrated in
The upper portion 14 also includes a second circumferential shoulder 30 located above the neck 28. This second shoulder 30 is integral with an uppermost portion of the neck 28. This shoulder 30 has a lower concave bend joined to an upper convex bend by an upwardly extending intermediate segment 32. Thus, the second shoulder 30 extends the height of the container 10 as it further decreases the diameter of the container 10, though to a lesser extent than the first shoulder 26.
The upper portion 14 further includes an open end 34. The open end 34 has a thread arrangement 36 for attachment to a closure member, such as a cap. The thread arrangement 36 includes a capper clearance 38 integral with an uppermost portion of the second shoulder 30. The capper clearance 38 receives a radially innermost portion of a cap threadably attached to the container utilizing the thread arrangement 36.
A threaded portion 40 is integral with an uppermost portion of the capper clearance 38. The threaded portion 40 includes a male thread 42 having a thread pitch of about 0.125±005 inches. The male thread 42 has upper and lower thread angles φ1,φ2. The upper thread angle φ1 is measured upwardly from a horizontal axis. The upper thread angle φ1 is generally between 30 degrees and 70 degrees, more preferably between about 33 degrees to about 60 degrees, and most preferably either 34 degrees±0.5 degrees as illustrated in
The container opening 46 is defined by a curl 48. The curl 48 has an upper surface 50 which may be curved as shown if
Referring to
The shallow cups 120 are transferred continuously to one or more bodymaker stations 124. Each bodymaker station 124 includes tooling for drawing and thinning the shallow cups 120 to form thin-walled tubular can bodies 128 having an open end and an opposing closed end. Each bodymaker station 124 contains a tool called a punch, which forms the shape of the can body 128 by forcing the cup 120 through a series of progressively smaller circular ironing rings. This action draws the metal up the sides of the punch, ironing it into a can body 128. As the cup 120 is forced through the rings, its diameter is reduced, its walls are thinned and its height is increased. At the end of the punch stroke, the bottom is formed into a dome shape that strengthens the bottom of the can body 128. During this process, referred to as wall ironing, the metal must be lubricated to reduce frictional heat.
The thin-walled, tubular can bodies 128 are transferred from the bodymakers 124 to trimmer stations 132. The trimmer station includes a knife for shearing excess material about the open ends of the tubular can bodies 128. This process adapts the can bodies 128 to a uniform, predetermined height.
The can bodies 128 are then continuously transferred to a washer station 140. The washer 136 removes the forming lubricants before the application of outside decoration (or label) and inside protective coating. The washed can bodies are discharged through a dryer station 144 where the can bodies 128 are dried with forced hot air.
Depending on end user requirements, a base layer of coating can be applied to the outer surface of the can bodies 128 at a base coater station 148. The base coating layer is generally a white or clear base coat. A base coat dryer station 152 may be provided for curing the base coat layer.
The can bodies 128 are then continuously transferred to a decorative coating station 156. The decorative coating station 156 applies a decorative layer of coating (ink) to the outer surface of the thin-walled tubular can bodies 128. The inked can bodies 128 move to a rotating varnish application roll that applies a clear coating over the entire outer sidewall. The clear coating protects the ink from scratching and contains lubricants that facilitate can conveying.
The can bodies 128 are transferred from the decorator 156 onto a pin (so that only the inside surface is contacted) and is conveyed through a decorator coating, or “pin,” oven/drier station 160 where the ink is dried with forced hot air.
Following application and curing of the exterior decorative layer, the can bodies 128 are conveyed to an inner surface coater station 164. This station 164 includes a bank of spray machines that spray the inner surfaces of the can bodies 128 with an epoxy-based organic protective coating. The inside coating is also cured by forced hot air at another dryer station 168. The coating prevents the beverage from contacting or reacting with the metal of the inner surface of the can body 128.
The can bodies may be palletized at this point and transferred to another location or separate manufacturing line for further processing. Alternatively, the can bodies can continue to be processed in-line. In either case, the processing continues as described below.
After the can bodies 128 leave the drier station 168, they pass through a lubricator station that applies a thin film of lubricant to the exterior of the top (open end) where a neck and a flange will be formed. A necker station 176 reduces the diameter of the open ends of the can bodies 128, and gives the cans the characteristic neck shape. Here, the diameter of the top of the can is reduced or “necked-in.” The necking station includes a plurality of necking modules.
At each module, an open end of the unfinished can body is necked-in or the inwardly-tapered portion is reshaped. A small overlap is created between a previously necked-in portion while the overall necked-in portion is extended and axially enlarged and small segments of reduction are taken so that the various operations blend smoothly into the finished necked-in portion. The resultant necked-in portion has a rounded shoulder on the end of the cylindrical side wall which merges with an inwardly-tapered annular straight neck segment through an arcuate portion, as described above. The opposite end of the annular straight segment merges with the open end through a second arcuate segment.
Prior to this stage of the processing, the unfinished can body has a thickened portion adjacent its upper open end. As the open end of the container is moved into engagement with a necking die, the forming angle in the die results in large radial forces on the container wall and small axial forces so that there is radial compression of the wall of the container.
As illustrated in
The left side portion of
The transition zone or intermediate surface 204 has a first arcuate surface segment A1 at the end of the first cylindrical wall portion 202 which has a radius of about 0.220 inch and a second arcuate surface segment R1 at the end of the second cylindrical wall portion 205 which has a radius of about 0.120 inch.
As the container 10 is moved upwardly into the die element 130A, as depicted on the right-hand side of
In the first necking module, the diameter of the container 10 is reduced only a very small amount while the portion of the can body to be necked is conditioned for subsequent operations. In other words, a form control operation is performed on the ultimate neck portion to prepare the container for subsequent operations.
This is accomplished by tightly controlling the dimensions and tolerances of reduced cylindrical surface 205 of die 130A and the external surface diameter of the forming sleeve or element 150A. The external diameter of sleeve or element 150A is equal to the internal diameter of cylindrical surface 205 less two times the thickness of the container side wall (t) with a maximum of 10% clearance of the wall thickness. By thus tightly controlling these dimensions, dents or imperfections in the container are removed or minimized, and also any variations in wall thickness around the perimeter of the neck are reduced to provide concentricity of the side wall of the container with the die.
Also, as mentioned above, during the movement of container 10 from the position illustrated at the left of
At the first forming station, the die element 130A forms the container 10 to have a shoulder 211 between a cylindrical side wall 210 and a reduced cylindrical neck 212; the shoulder 211, at this point, includes first and second arcuate segments CA1, CR1, respectively.
After the first necking operation is completed, the partially-necked container 10 exits therefrom and is fed to the second necking module. In the second necking operation, the necked-in portion is axially elongated while the reduced cylindrical neck portion 212 is further reduced in diameter by compression of the metal therein. This is accomplished by a second necking die 130B (
Referring to
As the container is moved from the left-hand position, shown in
In the second necking operation, the diameter of the reduced cylindrical neck is reduced, while the metal is further radially compressed therein. In the second necking die 130B, the forming angle described above is defined by the arcuate surface segment R2. It will be noted that the lower segment of the shoulder adjacent the cylindrical sidewall remains substantially unchanged while the upper part is reformed and the tapered portion is axially elongated.
During the second operation, a second tapered portion is essentially freely formed in the reduced cylindrical neck being free of the die at its lower end and this second tapered portion is forced along the reduced neck portion until it integrates with the arcuate segment CR1 of the first tapered portion. During this second operation, the lower part of the first tapered portion remains essentially unchanged while the second tapered portion combines and blends with the first tapered portion to produce an extension thereof and part of the finished shoulder.
It will be appreciated that the necking operation performed at each of the various modules is somewhat repetitive. It should be appreciated that, in fact, each module performs a part, and not all, of the necked-in portion while the cylindrical neck is sequentially and progressively reduced in diameter. That is, each module adds to and at least partially reforms and extends the necked-in portion produced on the container by the previous operation.
At each subsequent station, the cylindrical neck is compressed and reduced while the existing tapered or necked-in portion is partially reformed and axially elongated or extended to produce a small annular inwardly-tapered portion between the upper and lower arcuate segments described above.
Thus, the necking operation forms a smooth tapered necked-in portion between the container side wall and the reduced diameter cylindrical neck. This necked-in portion or taper includes a first arcuate segment integral with the side wall and a second arcuate segment integral with the reduced cylindrical neck. During the necking operation, the neck, comprising the reduced diameter cylindrical neck and the necked-in portion, is formed in segments while the axial dimension is increased and the cylindrical neck is further reduced in diameter and in axial length while a rounded shoulder is formed at the end of the side wall. At the same time, a straight tapered wall section or segment is created in the necked-in or tapered portion.
In each of the necking modules, the principal forces applied to the upper portion of the can body, which includes the first shoulder, the tapered neck, and the open end, are radially inwardly-directed forces and therefore the metal is primarily compressed and localized bending is minimized. The tapered portion is allowed to determine its profile because it is not constrained by the die below the contact area and is thus not dependent on the configuration of the lower portion of the transition zone of the die. Of course, the forming sleeve or element 150 will direct the upper edge of the container 16 into the annular slot defined between the forming sleeve or element and the reduced cylindrical portion of the die 130. Stated another way, the forming element 150 which engages the inner surface of the container 16 provides a guiding function or form control function.
The resultant can body comprises a cylindrical side wall extending from an integral bottom end wall, a single smooth necked in shoulder portion at an end of the cylindrical side wall, a single inwardly tapered annular straight segment extending from the shoulder between the sidewall and an open end of the can body. The inwardly tapered annular straight segment comprises a first radially compressed tapered portion having a single compressed lower segment, and a second further radially compressed tapered portion extending from an upper part of the first tapered portion. The second tapered portion is disposed between the first tapered portion and the open end. Subsequent necking modules would result in additional tapered portions. Thus, a plurality of tapered portions will be produced, preferably between eighteen and thirty-nine in number. More preferably a trim operation occurs after an eighteenth necking operation; a second trim operation and an expansion operation are carried out after the thirty-first necking operation; threads are produced in a threading operation after a thirty-fifth necking operation, and the end curl is provided in a curling operation which takes place after a thirty-ninth necking operation. This is all done on the necking station as a continuous sequence.
As stated before, method can be carried out on-line for a continuous sequence from cupping to finished threaded can body. Alternatively, the can bodies of the present invention are not flanged at the necking station, and may be removed from the typical process after the drying station 168.
While the specific embodiments have been illustrated and described, numerous modifications come to mind without significantly departing from the spirit of the invention, and the scope of protection is only limited by the scope of the accompanying Claims.
This application is a continuation-in-part application of currently U.S. Design Application. No. 29/262,849, filed Jul. 12, 2006, now U.S. Pat. No. D554,000 S, which is hereby incorporated by reference as if fully set forth herein.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1443682 | Gueritey | Jan 1923 | A |
| 1621487 | Aulbach | Mar 1927 | A |
| 2195257 | Paris | Mar 1940 | A |
| 2337616 | McManus et al. | Dec 1943 | A |
| 2384810 | Calleson et al. | Sep 1945 | A |
| 3995572 | Saunders | Dec 1976 | A |
| D245964 | Sexton et al. | Oct 1977 | S |
| D246030 | Sexton et al. | Oct 1977 | S |
| D246229 | Saunders | Nov 1977 | S |
| D247772 | Sexton, Jr. | Apr 1978 | S |
| D250933 | Saunders | Jan 1979 | S |
| D271281 | Abbott et al. | Nov 1983 | S |
| D271854 | Berry | Dec 1983 | S |
| 4441354 | Bodega | Apr 1984 | A |
| D275834 | Slade | Oct 1984 | S |
| 4643330 | Kennedy | Feb 1987 | A |
| D290811 | Cleveland, Jr. | Jul 1987 | S |
| 4844270 | Coffman | Jul 1989 | A |
| 4892214 | Hamaguchi et al. | Jan 1990 | A |
| D319580 | Cassai et al. | Sep 1991 | S |
| 5052576 | Budenbender | Oct 1991 | A |
| 5061140 | Hamaguchi et al. | Oct 1991 | A |
| D327218 | Nickerson | Jun 1992 | S |
| 5135124 | Wobser | Aug 1992 | A |
| 5190181 | Budenbender | Mar 1993 | A |
| 5293765 | Nussbaum-Pogacnik | Mar 1994 | A |
| 5355710 | Diekhoff | Oct 1994 | A |
| D353771 | Klitsner | Dec 1994 | S |
| 5448903 | Johnson | Sep 1995 | A |
| D369977 | Sexton, Jr. | May 1996 | S |
| D371075 | Stonehouse | Jun 1996 | S |
| 5557963 | Diekhoff | Sep 1996 | A |
| 5572893 | Goda et al. | Nov 1996 | A |
| 5605248 | Jentzsch | Feb 1997 | A |
| 5660301 | Kaplowitz | Aug 1997 | A |
| D384888 | Diekhoff | Oct 1997 | S |
| 5704240 | Jordan | Jan 1998 | A |
| 5711447 | Plester | Jan 1998 | A |
| 5713235 | Diekhoff | Feb 1998 | A |
| 5718352 | Diekhoff et al. | Feb 1998 | A |
| 5778723 | Diekhoff | Jul 1998 | A |
| 5822843 | Diekhoff et al. | Oct 1998 | A |
| 5875909 | Guglielmini | Mar 1999 | A |
| 5881907 | Schutz | Mar 1999 | A |
| 6010026 | Diekhoff et al. | Jan 2000 | A |
| 6010028 | Jordan et al. | Jan 2000 | A |
| 6105807 | McCrossen | Aug 2000 | A |
| D432015 | Holiday | Oct 2000 | S |
| D434323 | Pattinson | Nov 2000 | S |
| D434608 | Hansen | Dec 2000 | S |
| D437233 | Gibert | Feb 2001 | S |
| 6206222 | Cudzik | Mar 2001 | B1 |
| D444385 | Dixon | Jul 2001 | S |
| D451027 | Dugrot | Nov 2001 | S |
| 6463776 | Enoki et al. | Oct 2002 | B1 |
| 6499329 | Enoki et al. | Dec 2002 | B1 |
| 6543636 | Flecheux et al. | Apr 2003 | B1 |
| 6761280 | Zonker et al. | Jul 2004 | B2 |
| 6779677 | Chupak | Aug 2004 | B2 |
| 6857304 | Enoki | Feb 2005 | B2 |
| D503343 | Canino | Mar 2005 | S |
| 6907653 | Chupak | Jun 2005 | B2 |
| 6959830 | Kanou et al. | Nov 2005 | B1 |
| 7014060 | Richardson | Mar 2006 | B2 |
| 7152766 | Walsh et al. | Dec 2006 | B1 |
| D549595 | Lowther, Sr. et al. | Aug 2007 | S |
| D570228 | van Dam | Jun 2008 | S |
| 20010040167 | Flecheux et al. | Nov 2001 | A1 |
| 20050205575 | Kobayashi et al. | Sep 2005 | A1 |
| 20060011633 | Cook et al. | Jan 2006 | A1 |
| Number | Date | Country |
|---|---|---|
| 376464 | Nov 1931 | BE |
| 678389 | Jan 1964 | CA |
| 4439464 | May 1996 | DE |
| 19513886 | Oct 1996 | DE |
| 29512058 | Dec 1996 | DE |
| 19806481 | Aug 1998 | DE |
| 19722628 | Dec 1998 | DE |
| 0281543 | Sep 1988 | EP |
| 0182646 | Mar 1989 | EP |
| 0380662 | Aug 1990 | EP |
| 0510291 | Oct 1992 | EP |
| 0512131 | Nov 1992 | EP |
| 0537773 | Apr 1993 | EP |
| 0549987 | Jul 1993 | EP |
| 0581568 | Feb 1994 | EP |
| 0667299 | Aug 1995 | EP |
| 0693434 | Jan 1996 | EP |
| 0743260 | Nov 1996 | EP |
| 0864385 | Sep 1998 | EP |
| 1134046 | Sep 2001 | EP |
| 1136154 | Sep 2001 | EP |
| 1459997 | Sep 2004 | EP |
| 1468925 | Oct 2004 | EP |
| 633497 | Jan 1928 | FR |
| 2688431 | Sep 1993 | FR |
| 2708252 | Feb 1995 | FR |
| 2330548 | Apr 1999 | GB |
| 3000547 | Jan 2002 | GB |
| 458853 | Mar 1951 | IT |
| 01210136 | Aug 1989 | JP |
| 11139438 | May 1999 | JP |
| 2001090898 | Apr 2001 | JP |
| 2002037442 | Feb 2002 | JP |
| 2002137032 | May 2002 | JP |
| 2003-181577 | Jul 2003 | JP |
| 2003-290854 | Oct 2003 | JP |
| 2007-039095 | Feb 2007 | JP |
| 50159 | May 2001 | RU |
| 59523 | Jul 2006 | RU |
| 9111274 | Aug 1991 | WO |
| 9615865 | May 1996 | WO |
| 9616754 | Jun 1996 | WO |
| 9742091 | Nov 1997 | WO |
| 9806636 | Feb 1998 | WO |
| 9918013 | Apr 1999 | WO |
| 9932363 | Jul 1999 | WO |
| WO-9932363 | Jul 1999 | WO |
| 9943558 | Sep 1999 | WO |
| 9946176 | Sep 1999 | WO |
| 9948764 | Sep 1999 | WO |
| 0115829 | Mar 2001 | WO |
| 03047991 | Jun 2003 | WO |
| 2005108216 | Nov 2005 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20080011702 A1 | Jan 2008 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 29262849 | Jul 2006 | US |
| Child | 11676617 | US |