Patent Application
20090298996
The present invention refers to rheology modifiers and to mixtures of rheology modifiers for modifying the rheological behaviour of coating compositions, to coating compositions containing these rheology modifiers and to substrates coated with these coating compositions. It also refers to processes for the preparation of the rheology modifiers and the coating compositions and to processes for coating the substrates.
Coating compositions for coating a substrate usually include a rheology modifier in order to adapt the rheological behaviour of the coating color (synonymous to coating composition) to the coating device and coating conditions. Traditional coating techniques such as blade coating and roll coating require coating compositions of relatively high “low shear viscosity” (synonymous to Brookfield viscosity) and low “apparent high shear viscosity”. Curtain coating, a relatively recent coating technique, involves adding the coating composition as a falling thin curtain onto the substrate. This method requires coating compositions of relatively low “low shear viscosity”, but high “apparent extensional viscosity” (synonymous to high stretchability), as the coating composition curtain should not break especially when the substrate moves at high speed.
Rheology modifiers are usually polymers. Whereas many rheology modifiers, which in a coating composition exhibit high “low shear viscosity” and low “apparent high shear viscosity”, and thus are suitable for traditional coating techniques, are known, rheology modifiers, which as aqueous solution exhibit high “apparent extensional viscosity” and are thus suitable for curtain coating, are rare.
One rheology modifier, that is commercially available and is capable of providing aqueous solutions of high “apparent extensional viscosities”, is Sterocoll® BL, sold by BASF. The disadvantage of this rheology modifier is that it is only obtainable as an inverse (water-in-oil) emulsion. Inverse emulsions are unstable as the phases can easily separate and prone to freezing, which can cause the formation of undissolved gel particles. Therefore, inverse emulsions require additional equipment such as mixing or heating devices when stored, transported or added into the coating composition and thus are difficult to handle. In addition, inverse emulsions generate oil waste, and thus for environmental reasons demand a special clean-up after use.
It is a first object of the present invention to provide a rheology modifier for coating compositions, which is capable of providing aqueous solutions of high “apparent extensional viscosities”, and which is easy to handle and does not cause environmental problems.
This object is solved by the rheology modifiers of claim 1, the processes of claims 4, 5 and 7, the coating composition of claim 6 and the substrate of claim 11.
In some coating processes for preparing coated paper, which include blade coating operations, coating compositions of a higher than usual low “apparent high shear viscosity” are required. Coating compositions having a high amount of polyvinyl alcohol as co-binder are known to fulfill this requirement. However, when waste paper coated with these compositions is recycled, a paper stock containing sticky material of light colour, so-called “white pitch”, is obtained resulting in “white pitch” throughout the paper machine and in low-quality paper. As a consequence, the machine has to be stopped and cleaned, and in order to avoid further formation of “white pitch” an increased demand of chemicals, for example fixatives, in the wet end is needed.
In some cases, the formation of “white pitch” is related to the presence of polyvinyl alcohol in the paper stock as discussed in Teirfolk, J.-E, Hossenlopp, C., Castaing, J.-C., “Interactions between latex, calcium ions and polyvinyl alcohol”, PTS-Streicherei-Symposium, 2001.
Therefore, it is a second object of the present invention to provide a rheology modifier for coating compositions, which is capable of forming coating compositions of higher than usual low “apparent high shear viscosity” without requiring the presence of high amounts of polyvinyl alcohol as co-binder.
This object is solved by the mixture of rheology modifiers of claim 14, the processes of claims 18 and 20, the coating composition of claim 19 and the substrate of claim 24.
The rheology modifiers of the first aspect of present invention are water-soluble polymers having a weight average molecular weight (Mw) of at least 1'000'000 g/mol and an intrinsic viscosity of at least 2.5 dl/g, both as determined by size exclusion chromatography, and the rheology modifiers are in the form of solid particles.
Preferably, the polymers have a weight average molecular weight (Mw) of at least 2'000'000 g/mol and an intrinsic viscosity of at least 3.5 dl/g, both as determined by size exclusion chromatography. More preferably, the polymers have a weight average molecular weight (Mw) of at least 2'500'000 g/mol and an intrinsic viscosity of at least 4.5 dl/g, both as determined by size exclusion chromatography.
Preferably, the solid particles are beads. Preferably, the beads have a diameter in the range of 1 to 1000 μm, more preferably, of 100 to 400 μm.
Water-soluble means that at least 1 g of polymer dissolves in 100 g water to form a viscous solution.
Preferably, the polymers are composed of monomer units derived from
(i) at least one monomer of formula I
Examples of C1-6-alkyl are methyl, ethyl, propyl, isopropyl, butyl, sec-butyl, tert-butyl, isobutyl, pentyl and hexyl. Examples of C5-8-cycloalkyl are cyclopentyl, cyclohexyl and cycloheptyl. Examples of 5- or 7-membered heterocyclic rings are morpholino, pyrrolidino and piperidino. Examples of aryl are phenyl and substituted phenyl such as tolyl. Examples of halogen are bromine and chlorine. Examples of C1-4-alkoxy are methoxy, ethoxy, propoxy, isopropoxy, butoxy, sec-butoxy, tert-butoxy and isobutoxy. Examples of mono- or diC1-4-alkylamino are N-methylamino, N,N-ethylmethylamino, N,N-diethylamino, N,N-dipropylamino, N-isopropylamino and N,N-dibutylamino.
Examples of monomers of formula (I) are (meth)acrylamide, N,N-dimethyl(meth)acrylamide, N,N-diethyl(meth)acrylamide, N-isopropyl(meth)acrylamide.
Preferably, R1 and R2 can be the same or different and are hydrogen or C1-4-alkyl, whereby C1-4-alkyl may be substituted with amino or mono- or diC1-4-alkylamino, and
R3 and R4 can be the same or different and are hydrogen, C1-4-alkyl or NHCOC1-4-alkyl, whereby C1-4-alkyl may be substituted with amino or mono- or diC1-4-alkylamino.
Examples of C1-4-alkyl are methyl, ethyl, propyl, isopropyl, butyl, sec-butyl, tert-butyl, and isobutyl.
More preferably, R1 and R2 can be the same or different and are hydrogen or C1-4-alkyl, and R3 and R4 can be the same or different and are hydrogen or C1-4-alkyl.
Even more preferably, R1 and R2 are hydrogen, and R3 and R4 are the same or different and are hydrogen or C1-4-alkyl.
Most preferably, R1, R2, R3 and R4 are hydrogen.
Any suitable other ethylenically unsaturated monomer can be used. Examples of other ethylenically unsaturated monomers are acrylic monomers, styrene monomers, vinyl monomers, maleic monomers and allyl monomers.
Examples of acrylic monomers are (meth)acrylic acid or salts thereof, (meth)acrylamide, (meth)acrylonitrile, C1-6-alkyl(meth)acrylates such as ethyl(meth)acrylate, butyl (meth)acrylate or hexyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, di(C1-4-alkylamino)C1-6-alkyl(meth)acrylates such as dimethylaminoethyl acrylate or diethylaminoethyl acrylate, amides formed from di(C1-4-alkylamino)C1-6-alkylamines and (meth)acrylic acid and C1-4-alkyl halide adducts thereof.
Examples of styrene monomers are styrene, 4-methylstyrene and 4-vinylbiphenyl. Examples of vinyl monomers are vinyl alcohol, vinyl chloride, vinylidene chloride, vinyl isobutyl ether and vinyl acetate. Examples of olefin monomers are ethylene, propylene, butadiene and isoprene and chlorinated or fluorinated derivatives thereof such as tetrafluoroethylene. Examples of maleic monomers are maleic acid, maleic anhydride and maleimide. An example of an allyl monomer is diallyldimethylammonium chloride.
Preferably, the optional other ethylenically unsaturated monomers comprise at least one monomer of formula II
whereby
R5 and R6 can be the same or different and are hydrogen, C1-6-alkyl, C5-8-cycloalkyl, halogen, aryl or NHCOC1-4-alkyl, whereby C1-6-alkyl may be substituted with amino, hydroxyl, halogen, C1-4-alkoxy, aryl or mono- or diC1-4-alkylamino, and
M is hydrogen, ammonium, mono-, di-, tri- or tetraC1-4-alkylammonium, alkali metal or earth alkaline metal.
Examples of mono-, di-, tri- or tetraC1-4-alkylammonium are N-ethylammonium, N,N-diethylammonium and N,N,N-tributylammonium. Examples of alkali metals are sodium, potassium and lithium. Examples of earth alkaline metals are magnesium and calcium.
Examples of monomers of formula (II) are (meth)acrylic acid, ammonium (meth)acrylate, sodium (meth)acrylate.
Preferably, R5 and R6 can be the same or different and are hydrogen, C1-4-alkyl or NHCOC1-4-alkyl, and M is hydrogen, ammonium, mono-, di-, tri- or tetraC1-4-alkylammonium, alkali metal or earth alkaline metal.
More preferably, R5 and R6 are the same or different and are hydrogen or C1-4-alkyl, and M is hydrogen, ammonium, or alkali metal. Most preferably, R5 and R6 are hydrogen, and M is hydrogen, ammonium, or alkali metal.
Preferably, the polymers are obtainable by polymerisation of at least one monomer of formula (I) and at least one monomer of formula (II).
Preferably the molar ratio of monomers of formula (I)/monomers of formula (II) is from 90:1 to 1:90, more preferably it is from 10:1 to 1:10, even more preferably, it is from 5:1 to 1:5, and most preferably it is from 1:1 to 1:5.
Also part of the first aspect of the invention is a process for preparing the rheology modifiers of the present invention, which comprises the steps of
It is possible to start the distillation of water already during step (iii).
Examples of water-immiscible solvent are mineral oils or hydrocarbon liquids such as Exxsol® D40 or Isopar® G, hydrophobic carboxylic acid esters such as dibutyl phthalate or dioctyl phthalate, fatty acid triglycerides such as soyabean oil or sunflower oil, and silicone oils.
Preferably, the water-immiscible solvent is a mineral oil or hydrocarbon liquid.
The initiator can be a peroxide, a persulfate, an azo compound, a redox couple or mixtures thereof.
Examples of peroxides are hydrogen peroxide, potassium peroxide, tert-butyl peroxide, tert-butyl hydroperoxide, cumene hydroperoxide and benzoyl peroxide. Examples of persulfates are ammonium, sodium or potassium persulfate. Examples of azo compounds are 2,2-azobisisobutyronitrile, 4,4′-azobis(4-cyanovaleric acid) and 2,2′-azobis(N,N′-dimethyleneisobutyramidine) dihydrochloride, 1,1′-azobis(cyclohexanecarbonitrile) and 2,2′-azobis(2-amidinopropane) dihydrochloride. Redox couples consist of an oxidizing agent and a reducing agent. The oxidizing agent can be one of the above listed peroxides, persulfates, sulfates or azo compounds, or an alkali metal chlorate or bromate. Examples of reducing agents are ascorbic acid, glucose or ammonium or alkali metal hydrogen sulfite, sulfite, thiosulfate or sulfide, or ferrous ammonium sulfate.
Preferably, the initiator is a mixture of a redox couple and one or more initiators selected from the group consisting of peroxides, persulfates and azo compounds.
More preferably, the initiator is a mixture of a redox couple, wherein the oxidizing agent is selected from the group consisting of peroxides and alkali metal bromates, and the reducing agent is selected from the group consisting of ammonium or alkali metal hydrogen sulfite, sulfite, thiosulfate or sulfide, or ferrous ammonium sulfate, with one or more azo compound initiators.
Even more preferably, the initiator is a mixture of a redox couple, wherein the oxidizing agent is a peroxide and the reducing agent is an alkali metal hydrogen sulfite or sulfite, with one or more azo compound initiators.
Most preferably, the initiator is a mixture of a redox couple, wherein the oxidizing agent is tert-butylhydroperoxide and the reducing agent is sodium sulfite, and 2,2′-azobis(2-amidinopropane) dihydrochloride as azo compound initiator.
Preferably, the polymerization is performed in the presence of a chain transfer agent.
Examples of chain transfer agents are sodium hypophosphite, mercapto ethanol, thioglycolic acid, formic acid and malic acid. A preferred chain transfer agent is sodium hypophosphite.
Preferably, the polymerization is performed in the presence of a polymeric stabilizer and/or a sequesterant agent.
Examples of polymeric stabilizer are C1-20-alkyl(metha)acrylate (meth)acrylic acid copolymers. Examples of C1-20-alkyl are methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, myristyl and stearyl. A preferred polymeric stabilizer is stearyl methacrylate:methacrylic acid copolymer.
Examples of sequesterant agents are ethylenediaminetetraacetic acid and diethylenetriaminepentaacetic acid, penta sodium salt.
Preferably, the ratio of water-immiscible solvent/water is between 10:1 and 1:10, more preferably, it is between 5:1 and 1:5, most preferably, it is between 4:1 and 1:1.
Preferably, the concentration of monomer or monomers in the aqueous phase is between 0.1 and 20 mol/L, more preferably, it is between 1 and 15 mol/L, most preferably, it is between 7 and 12 mol/L.
Preferably, the molar ratio of initiator or initiators/monomer or monomers is between 0.0001% and 1%, more preferably, it is between 0.001% and 0.1%, most preferably, it is between 0.01% and 0.05%.
Preferably, the molar ratio of chain transfer agent/monomer or monomers is between 0.001% and 10%, more preferably, it is between 0.01% and 1%, most preferably it is between 0.2% and 0.6%.
Preferably, the pH of the aqueous phase is 3 to 10, more preferably, 4 to 8, most preferably, 5 to 7.
Also part of the first aspect of the invention is a process for preparing a coating composition which comprises the steps of
Preferably, the rheology modifiers of step (i) is mixed with a binder, a pigment, a carrier solvent and optional additives in order to form a coating composition.
Any suitable binder or binder mixtures can be used. Examples of binders are styrene-butadiene (SB) copolymer, styrene-acrylate (SA) copolymer, styrene-butadiene-acrylonitrile copolymer, styrene-acrylate-acrylonitrile copolymer, styrene-butadiene-acrylate-acrylonitrile copolymer, styrene-maleic anhydride copolymer, styrene-acrylate-maleic anhydride copolymer, polysaccharides, proteins, polyvinyl pyrrolidone, polyvinyl alcohol, polyvinyl acetate, natural polymers such as starch, cellulose or protein and cellulose derivatives such as carboxymethylcellulose (CMC).
Preferred binders are styrene-butadiene (SB) copolymer, styrene-acrylate (SA) copolymer and polyvinyl alcohol and mixtures thereof.
Any suitable pigment or pigment mixture can be used. Examples of pigments are clay (or kaolin), calcined clay (or kaolin), ground calcium carbonate (GCC), precipitated calcium carbonate (PCC), titanium dioxide, satin white, zinc oxide, barium sulfate, gypsum, silica, alumina trihydrate, talc, mica and diatomaceous earth.
An example of a carrier solvent is water. The binder and/or the pigment can be employed as aqueous solutions or dispersions, e.g. the binder may be employed as latex, so that the addition of further water may not be necessary.
Examples of optional additives are optical brighteners, surfactants, dispersants, biocides, defoamers, lubricants, crosslinkers (also called insolubilisers), additional rheology modifiers, water retention agents and dyes.
An example of an optical brightener is diaminostilbenedisulfonic acid as sold for example under the tradename Ciba® Tinopal® UP. An example of a surfactant is sodium dialkylsulphosuccinate as sold for example under the tradename Aerosol OT, or alkoxylated fatty acids as sold for example under the tradename Invadine PF. Examples of dispersants are sodium salts of acrylic polymers, as sold for example under the tradename Ciba® Dispex® N40. An example of a biocide is glutaraldehyde as sold for example under the tradename PRIOR 850. Examples of defoamers are polyether derivatives of aliphatic alcohols as sold for example under the tradename Afranil® F. An example of a lubricant is calcium stearate as sold for example under the tradename Ciba® Raisacoat® CAS50. An example of a crosslinker is ammonium zirconium carbonate as sold for example under the tradename Ciba® Raisacoat® AZ20. Examples of additional rheology modifiers are xanthan gum, methylcellulose, hydroxypropyl methylcellulose, or acrylic polymers such as sold for example under the tradename Ciba® Rheovis® CTE-407. An example of a water retention agent is sodium alginate. Examples of dyes are organic pigment dyes, respectively anionic direct dyes as sold for example under the tradenames Ciba® Irgalite® and Ciba® Pergasol®.
Preferably the pH of the coating composition is in the range of 6.5 to 10.5, more preferably 7 to 10, most preferably 7.5 to 9.5.
The amount of solids in the coating composition can be 10 to 90%, preferably 20 to 80%, more preferably 30 to 70%, most preferably 50 to 70%, by weight based on the weight of the composition.
The amount of pigment can be from 1 to 90%, preferably from 20 to 80%, more preferably 30 to 70%, most preferably from 40 to 60% by weight based on the weight of the composition.
The amount of rheology modifier of the present invention can be from 0.001 to 5, preferably from 0.01 to 3, more preferably from 0.05 to 1 dry weight parts per 100 dry weight parts pigment.
The amount of binder can be from 1 to 60, preferably from 3 to 30, more preferably from 10 to 20 dry weight parts per 100 dry weight parts pigment.
The amount of optional other components can be from 0 to 10, preferably from 0.5 to 4 dry weight parts per 100 dry weight parts pigment.
Also part of the first aspect of the invention is a coating composition obtainable by above process.
Another part of the first aspect of the present invention is a process for coating a substrate comprising the steps of
The substrate can be a sheet or any other three dimensional object and it can have an even or uneven surface. The substrate can be made from paper, cardboard, metal, wood, textiles, glass, ceramics and/or polymers. Examples of polymers are polyethylene terephthalate, low density-polyethylene, polypropylene, biaxially orientated polypropylene, polyether sulfone, polyvinyl chloride polyester and polystyrene. Preferably, the substrate is made from paper, cardboard or polymer. More preferably, the substrate is paper.
The coating composition can be applied by any suitable method such as blade, roll, spray or curtain coating. Preferably the coating composition is applied by curtain coating onto the substrate.
Another part of the first aspect of the invention are substrates coated by the above process.
Also part of the first aspect of the present invention is the use of the rheology modifiers of the first aspect of the present invention for coating operations, especially for curtain coating operations.
Aqueous solutions of the rheology modifiers of the first aspect of the present invention show a high “apparent extensional viscosity” and a low “low shear viscosity” (synonymous to Brookfield viscosity) when the concentration of the rheology modifier is low and a low “apparent extensional viscosity” and a high “low shear viscosity” (synonymous to Brookfield viscosity) when the concentration of the rheology modifier is high. So, depending on the concentration, these rheology modifiers can be used for all kind of coating methods, such as blade, roll or curtain coating.
The rheology modifiers of the first aspect of the present invention have the advantages that they are solid polymer particles and thus very stable, easy to handle and do not require a special clean-up after use in order to avoid environmental problems. In addition, they can be either used as solid particles or readily dissolved in water just before use.
The mixtures of rheology modifiers of the second aspect of the present invention comprise a first rheology modifier, which is a water-soluble polymer having a weight average molecular weight (Mw) of at least 1'000'000 g/mol and an intrinsic viscosity of at least 2.5 dl/g, both as determined by size exclusion chromatography, and a second rheology modifier, which has a weight average molecular weight of from 2'000 g/mol to 800'000 g/mol, as determined by size exclusion chromatography.
Preferably, the first rheology modifier is a polymer having a weight average molecular weight (Mw) of from 1'000'000 g/mol to 2'500'000 g/mol and an intrinsic viscosity of from 2.5 to 5.0 dl/g, both as determined by size exclusion chromatography. More preferably, the first rheology modifier is a polymer having a weight average molecular weight (Mw) of from 1'00'000 g/mol to 1'500'000 g/mol, and an intrinsic viscosity of from 2.5 to 4.5 dl/g, both as determined by size exclusion chromatography.
Preferably, the first rheology modifier is a polymer composed of monomer units derived from
(i) at least one monomer of formula I
Examples of C1-4-alkyl are methyl, ethyl, propyl, isopropyl, butyl, sec-butyl, tert-butyl, and isobutyl. Examples of C1-6-alkyl are methyl, ethyl, propyl, isopropyl, butyl, sec-butyl, tert-butyl, isobutyl, pentyl and hexyl. Examples of C5-8-cycloalkyl are cyclopentyl, cyclohexyl and cycloheptyl. Examples of 5- or 7-membered heterocyclic rings are morpholino, pyrrolidino and piperidino. Examples of aryl are phenyl and substituted phenyl such as tolyl. Examples of halogen are bromine and chlorine. Examples of C1-4-alkoxy are methoxy, ethoxy, propoxy, isopropoxy, butoxy, sec-butoxy, tert-butoxy and isobutoxy. Examples of mono- or diC1-4-alkylamino are N-methylamino, N,N-ethylmethylamino, N,N-diethylamino, N,N-dipropylamino, N-isopropylamino and N,N-dibutylamino.
Examples of monomers of formula (I) are (meth)acrylamide, N,N-dimethyl(meth)acrylamide, N,N-diethyl(meth)acrylamide, N-isopropyl(meth)acrylamide.
Preferably, R1 and R2 can be the same or different and are hydrogen or C1-4-alkyl, whereby C1-4-alkyl may be substituted with amino or mono- or diC1-4-alkylamino, and
R3 and R4 can be the same or different and are hydrogen, C1-4-alkyl or NHCOC1-4-alkyl, whereby C1-4-alkyl may be substituted with amino or mono- or diC1-4-alkylamino.
More preferably, R1 and R2 can be the same or different and are hydrogen or C1-4-alkyl, and R3 and R4 can be the same or different and are hydrogen or C1-4-alkyl.
Even more preferably, R1 and R2 are hydrogen, and R3 and R4 are the same or different and are hydrogen or C1-4-alkyl.
Most preferably, R1, R2, R3 and R4 are hydrogen.
Any suitable other ethylenically unsaturated monomer can be used. Examples of other ethylenically unsaturated monomers are acrylic monomers, styrene monomers, vinyl monomers, maleic monomers and allyl monomers.
Examples of acrylic monomers are (meth)acrylic acid or salts thereof, (meth)acrylamide, (meth)acrylonitrile, C1-6-alkyl(meth)acrylates such as ethyl(meth)acrylate, butyl (meth)acrylate or hexyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, di(C1-4-alkylamino)C1-6-alkyl(meth)acrylates such as dimethylaminoethyl acrylate or diethylaminoethyl acrylate, amides formed from di(C1-4-alkylamino)C1-6-alkylamines and (meth)acrylic acid and C1-4-alkyl halide adducts thereof.
Examples of styrene monomers are styrene, 4-methylstyrene and 4-vinylbiphenyl. Examples of vinyl monomers are vinyl alcohol, vinyl chloride, vinylidene chloride, vinyl isobutyl ether and vinyl acetate. Examples of olefin monomers are ethylene, propylene, butadiene and isoprene and chlorinated or fluorinated derivatives thereof such as tetrafluoroethylene. Examples of maleic monomers are maleic acid, maleic anhydride and maleimide. An example of an allyl monomer is diallyldimethylammonium chloride.
Preferably, the optional other ethylenically unsaturated monomers comprise at least one monomer of formula II
whereby
R5 and R6 can be the same or different and are hydrogen, C1-6-alkyl, C5-8-cycloalkyl, halogen, aryl or NHCOC1-4-alkyl, whereby C1-6-alkyl may be substituted with amino, hydroxyl, halogen, C1-4-alkoxy, aryl or mono- or diC1-4-alkylamino, and
M is hydrogen, ammonium, mono-, di-, tri- or tetraC1-4-alkylammonium, alkali metal or earth alkaline metal.
Examples of mono-, di-, tri- or tetraC1-4-alkylammonium are N-ethylammonium, N,N-diethylammonium and N,N,N-tributylammonium. Examples of alkali metals are sodium, potassium and lithium. Examples of earth alkaline metals are magnesium and calcium.
Examples of monomers of formula (II) are (meth)acrylic acid, ammonium (meth)acrylate, sodium (meth)acrylate.
Preferably, R5 and R6 can be the same or different and are hydrogen, C1-4-alkyl or NHCOC1-4-alkyl, and M is hydrogen, ammonium, mono-, di-, tri- or tetraC1-4-alkylammonium, alkali metal or earth alkaline metal.
More preferably, R5 and R6 are the same or different and are hydrogen or C1-4-alkyl, and M is hydrogen, ammonium, or alkali metal. Most preferably, R5 and R6 are hydrogen, and M is hydrogen, ammonium, or alkali metal.
Preferably, the polymers are obtainable by polymerisation of at least one monomer of formula (I) and at least one monomer of formula (II).
Preferably the molar ratio of monomers of formula (I)/monomers of formula (II) is from 90:1 to 1:90, more preferably it is from 10:1 to 1:10, even more preferably, it is from 5:1 to 1:5, and most preferably it is from 1:1 to 1:5.
Preferably, the second rheology modifier has a weight average molecular weight of from 2'000 g/mol to 500'000 g/mol, more preferably, from 10'000 to 250'000 g/mol, most preferably from 50'000 to 150'000 g/mol.
The second rheology modifier is preferably prepared from a monomer mixture comprising at least one acrylic monomer. In particular, it is formed from a monomer mixture comprising an acidic acrylic monomer and a monomer having a hydrophobic side chain. Examples of acidic acrylic monomers are acrylic acid and methacrylic acid. Examples of monomers having a hydrophobic side chain are steareth 10 mole ethoxylate allyl ether and steareth 25 mole ethoxylate methacrylate. Preferably, the monomer mixture comprises from 10 to 90%, more preferably from 20 to 80%, most preferably from 30 to 70% by weight of the acidic acrylic monomer based on the weight of all monomers. Preferably, the monomer mixture comprises from 0.01 to 40%, more preferably from 0.01 to 30%, most preferably from 0.01 to 20% by weight of the monomer having at least one hydrophobic side chain based on the weight of all monomers. A particular preferred second rheology modifier is prepared from ethyl acrylate/methacrylic acid/steareth 10 mole ethoxylate allyl ether in a weight ratio of 50/40/10.
Also part of the second aspect of the invention is a process for preparing a coating composition which comprises the steps of
The examples of binders, pigments, carrier solvents and optional additives given for the first aspect of the invention apply also here.
Preferably the pH of the coating composition is in the range of 6.5 to 10.5, more preferably 7 to 10, most preferably 7.5 to 9.5.
The amount of solids in the coating composition can be 20 to 95%, preferably 30 to 90%, more preferably 40 to 85%, most preferably 60 to 80%, by weight based on the weight of the composition.
The amount of pigment can be from 1 to 90%, preferably from can be 20 to 95%, preferably 30 to 90%, more preferably 40 to 85%, most preferably 60 to 80%, by weight based on the weight of the composition.
The amount of the first rheology modifier of the mixture of rheology modifiers of the second aspect of the invention can be from 0.001 to 5, preferably from 0.01 to 3, more preferably from 0.03 to 0.5 dry weight parts per 100 dry weight parts pigment.
The amount of the second rheology modifier of the mixture of rheology modifiers of the second aspect of the invention can be from 0.001 to 5, preferably from 0.01 to 3, more preferably from 0.03 to 0.5 dry weight parts per 100 dry weight parts pigment.
The amount of binder can be from 1 to 60, preferably from 3 to 30, more preferably from 5 to 15 dry weight parts per 100 dry weight parts pigment.
The amount of optional other components can be from 0 to 10, preferably from 0.5 to 4 dry weight parts per 100 dry weight parts pigment.
Also part of the second aspect of the invention is a coating composition obtainable by above process.
Another part of the second aspect of the present invention is a process for coating a substrate comprising the steps of
The examples for a substrate given for the first aspect of the invention apply accordingly to the second aspect of the invention.
Another part of the second aspect of the invention are substrates coated by the above process.
Also part of the second aspect of the present invention is the use of the rheology modifiers of the present invention for coating operations, especially for blade coating operations.
Another part of the second aspect of the present invention is a method for reducing white pitch in the production of coated paper comprising the step of coating the paper with a coating composition comprising the mixture of rheology modifiers of the second aspect of the present invention.
An advantage of the mixture of rheology modifiers of the second aspect of the present invention is that in processes for preparing paper, which involve blade coating operations and require coating compositions of higher than usual low “apparent high shear viscosity” only a reduced amount of polyvinyl alcohol is required to achieve the desired coating composition of higher than usual low “apparent high shear viscosity”. Thus, when recycling paper coated with these composition, the formation of “white pitch” caused by the presence of polyvinyl alcohol in the wet end is reduced.
A 25% by weight solution of stearyl methacrylate:methacrylic acid copolymer in Exxsol® D40 (3.6 g) is dissolved in Exxsol® D40, a hydrocarbon solvent, (300 g) and the obtained solution is sparged with nitrogen for 30 minutes. A monomer solution is prepared by dissolving acrylamide (81 g, 1.14 mol) and a 1% by weight aqueous solution of ethylenediaminetetraacetic acid (5.4 g) in water (93.6 g) and adjusting the pH to 6.0. A 10% by weight aqueous solution of sodium hypophosphite (0.9 mL), a 2% by weight solution of 2,2′-azobis(2-amidinopropane) dihydrochloride (1.8 mL) and a 1% aqueous solution of sodium sulfite (1.8 mL) are added to the monomer solution. The thus obtained solution is added to the sparged hydrocarbon solvent and a nitrogen atmosphere is maintained. The stirrer speed is adjusted to give droplets of approximately 250 μm. A 1% by weight aqueous solution of tert-butyl hydroperoxide (0.9 mL) is added to the mixture to start the polymerization. The polymerization is allowed to exotherm. After polymerization, water is removed by distillation. After cooling the polymer beads are separated by filtration and dried to remove residual solvent at 40° C. The obtained polymer beads (100% of the monomer units derived from acrylamide) have an average diameter of 250 μm.
Polymer beads are prepared as described in example 1, except that the amount of the 10% by weight aqueous solution of sodium hypophosphite is 1.8 mL. The obtained polymer beads (100% of the monomer units derived from acrylamide) have an average diameter of 250 μm.
Polymer beads are prepared as described in example 1, except that the amount of the 10% by weight aqueous solution of sodium hypophosphite is 3.6 mL. The obtained polymer beads (100% of the monomer units derived from acrylamide) have an average diameter of 250 μm.
Polymer beads are prepared as described in example 1, except that the monomer solution is prepared by dissolving acrylamide (56.7 g, 0.8 mol), acrylic acid (18.6 g, 0.26 mol), sodium hydroxide (10.3 g) and a 1% by weight aqueous solution of ethylenediaminetetraacetic acid (5.4 g) in water (93.6 g) and adjusting the pH to 6.0. The obtained polymer beads (75% of the monomer units are derived from acrylamide and 25% from sodium acrylate) have an average diameter of 250 μm.
Polymer beads are prepared as described in example 2, except that the amount of the 10% by weight aqueous solution of sodium hypophosphite is 1.8 mL. The obtained polymer beads (75% of the monomer units are derived from acrylamide and 25% from acrylic acid) have an average diameter of 250 μm.
Polymer beads are prepared as described in example 2, except that the amount of the 10% by weight aqueous solution of sodium hypophosphite is 3.6 mL. The obtained polymer beads (75% of the monomer units are derived from acrylamide and 25% from acrylic acid) have an average diameter of 250 μm.
Polymer beads are prepared as described in example 1, except that the monomer solution is prepared by dissolving acrylamide (14.4 g, 0.2 mol), acrylic acid (44.1 g, 0.61 mol), sodium hydroxide (24.5 g) and a 1% by weight aqueous solution of ethylenediaminetetraacetic acid (5.4 g) in water (91.6 g) and adjusting the pH to 6.0. The obtained polymer beads (25% of the monomer units are derived from acrylamide and 75% from sodium acrylate) have an average diameter of 250 μm.
Polymer beads are prepared as described in example 4, except that the amount of the 10% by weight aqueous solution of sodium hypophosphite is 1.8 mL. The obtained polymer beads (25% of the monomer units are derived from acrylamide and 75% from acrylic acid) have an average diameter of 250 μm.
Polymer beads are prepared as described in example 4, except that the amount of the 10% by weight aqueous solution of sodium hypophosphite is 3.6 mL. The obtained polymer beads (25% of the monomer units are derived from acrylamide and 75% from acrylic acid) have an average diameter of 250 μm.
The number average molecular weight (Mn), the weight average molecular weight (Mw) and the intrinsic viscosity (IV) are determined by size exclusion chromatography (detector: Viscotec TDA three array detector (refractive index-, viscometer- and RALS (90°)/LALS (7°) light scattering detector); column: 2×Viscogel GMPWXL+precolumn; pump: Viscotec VE 20002 GPC eluent/sample module; eluent: 0.2 M sodium nitrate, 0.8 mL/min; temperature: 35° C. (columns+detectors); calibration: narrow polyethylene oxide standard).
The “low shear viscosity” of aqueous solutions of polymer beads at 30 g, 60 g and 90 g, respectively, beads per litre water is measured using a Brookfield viscometer (100 rpm and 25° C.).
The results are shown in
One can see that the rheology modifiers of examples 1 to 6 show “low shear viscosities”, which are comparable to the “low shear viscosities” of the rheology modifiers obtained in comparative examples 1 to 3.
The “normalized diameter” of aqueous solutions of the polymer beads at 30 g beads per litre water is measured using a CaBER 1 instrument, which is an extensional rheometer sold by Thermo Haake (plates diameter 6 mm; start height 2.5 mm; end height 7.85 mm; hencky strain 1.14). The normalized diameter is the filament diameter (as a function of time)/initial filament diameter. The break-up time, i.e. the time at which the normalized diameter is 0, is related to the apparent extensional viscosity. The higher the break-up time, the higher is the “apparent extensional viscosity”.
The results are shown in
One can see that the rheology modifiers of examples 1 to 6 show “apparent extensional viscosities”, which are considerable higher than the “apparent extensional viscosities” of the rheology modifiers obtained in comparative examples 1 to 3. Among the rheology modifiers of examples 1 to 6, the rheology modifiers of examples 2, 4 and 5 yield the highest “apparent extensional viscosities”. The highest “apparent extensional viscosity” is obtained with the rheology modifier of example 4.
The rheology modifiers obtained in examples 1 to 6 are dissolved in water at 30 g beads per litre of water, and varying amounts (0.5 to 0.2 dry weight parts of polymer beads) of these solutions are added to a mixture of 100 dry weight parts ground calcium carbonate, and 17.5 dry weight parts of Ciba® Latexia® 301, a styrene butadiene latex, in water to give a coating composition having a solid content of 60% by weight based on the weight of the composition. The pH is adjusted to 9.0.
0.1 dry weight parts Sterocoll® BL, an inverse (water-in-oil) emulsion of a rheology modifier, is added to a mixture of 100 dry weight parts ground calcium carbonate, and 17.5 dry weight parts DL 936, a styrene butadiene latex, in water to give a coating composition having a solid content of 60% by weight based on the weight of the composition. The pH is adjusted to 9.0.
0.1 dry weight parts Sterocoll® BL, an inverse (water-in-oil) emulsion of a rheology modifier, is added to a mixture of 100 dry weight parts ground calcium carbonate, and 17.5 dry weight parts of Ciba® Latexia® 301, a styrene butadiene latex in water to give a coating composition having a solid content of 60% by weight based on the weight of the composition. The pH is adjusted to 9.0.
The low shear viscosities of the coating compositions are measured using a Brookfield viscometer (100 rpm and 25° C.).
One can see that “low shear viscosities” comparable to those of the coating compositions containing Sterocoll® BL (comparative examples 4 and 5) can be achieved with the coating compositions of example 7 containing the rheology modifiers of examples 1 to 6. The rheology modifiers of examples 4, 5 or 6 even yield coating compositions of comparable “low shear viscosities” at lower dosages compared to Sterocoll® BL.
Water retention properties (g released water/m2 base paper) of the coating compositions are measured following test method TAPPI T 701 pm-01 using an AA GWR water retention meter by determining the amount of continuous phase removed through a membrane filter (non-hydroscopic polycarbonate filter with 5 μm mean pore size) from the coating into base paper (chromatography paper with basis weight 413 g/m2) within 2 minutes and under hydrostatic pressure of 2 bars.
The measurement is performed on those coating compositions of example 7 having comparable “low shear viscosities” to the coating composition of comparative example 5.
The lower the “water loss” value, the higher is the water retention. One can see that the water retention properties of the coating compositions of example 7 containing the rheology modifiers of examples 1 to 6, are comparable to those of the coating composition containing Sterocoll® BL (comparative example 5). Among the rheology modifiers of examples 1 to 6, the rheology modifier of example 4 yields the best water retention properties.
It was not possible to measure the apparent extensional viscosities of the coating compositions due to irreproducible results.
An aqueous emulsion polymer composed of ethyl acrylate/methacrylic acid/steareth 10 mole ethoxylate allyl ether in a weight ratio of 50/40/10 is prepared in analogy to example 1 of WO 04/076743.
Following coating compositions having a pH of 9.0 and various solid contents (68.0 to 69.6% by weight) are prepared.
The “apparent high shear viscosities” of the coating compositions having a solid content of 68.5% by weight are measured using an ACAV A4 viscometer.
The “apparent high shear viscosities” are shown in
The coating compositions of examples 9 to 11 containing the rheology modifiers of examples 1 or 2 and the rheology modifier of example 7 as second rheology modifier and only 0.6 dry weight parts of polyvinyl alcohol, yield higher than usual “apparent high shear viscosities”. A particular higher than usual “apparent high shear viscosity” is obtained with the coating composition of example 9 containing 0.1 dry weight parts of the rheology modifier of example 1 and 0.06 dry weight parts of the rheology modifier of example 8 as additional rheology modifier, followed by the coating composition of example 10.
The water retention properties are determined as described for the coating compositions of example 7 and comparative examples 4 and 5.
The water retention properties are shown in
| Number | Date | Country | Kind |
|---|---|---|---|
| 05108440.8 | Sep 2005 | EP | regional |
| 06117808.3 | Jul 2006 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2006/065951 | 9/4/2006 | WO | 00 | 8/11/2009 |