Patent Grant
8053096
Magnetic thin-film media, wherein a fine grained polycrystalline magnetic alloy layer serves as the active recording medium layer, are generally classified as “longitudinal” or “perpendicular,” depending on the orientation of the magnetization of the magnetic domains of the grains of the magnetic material. In longitudinal media (also often referred as “conventional” media), the magnetization in the bits is flipped between lying parallel and anti-parallel to the direction in which the head is moving relative to the disc.
Perpendicular magnetic recording media are being developed for higher density recording as compared to longitudinal media. The thin-film perpendicular magnetic recording medium comprises a substrate and a magnetic layer having perpendicular magnetic anisotropy. In perpendicular media, the magnetization of the disc, instead of lying in the disc's plane as it does in longitudinal recording, stands on end perpendicular to the plane of the disc. The bits are then represented as regions of upward or downward directed magnetization (corresponding to the 1's and 0's of the digital data).
While perpendicular media technology provides higher areal density capability over longitudinal media, granular perpendicular magnetic recording media is being developed for further extending the areal density as compared to conventional (non-granular) perpendicular magnetic recording which is limited by the existence of strong lateral exchange coupling between magnetic grains. Granular structure provides better grain isolation through oxide segregation to grain boundary, hence enhancing grain to grain magnetic decoupling and increasing media signal to noise ratio (SNR).
A granular perpendicular magnetic layer contains magnetic columnar grains separated by grain boundaries comprising a dielectric material such as oxides, nitrides or carbides to decouple the magnetic grains. The grain boundaries having a thickness of about 2 Å to about 30 Å, provide a substantial reduction in the magnetic interaction between the magnetic grains. In contrast to conventional perpendicular media, wherein the longitudinal magnetic layer is typically sputtered at low pressures and high temperatures in the presence of an inert gas, such as argon (Ar), deposition of the granular perpendicular magnetic layer is conducted at relatively high pressures and low temperatures and utilizes a reactive sputtering technique wherein oxygen (O2), CxHy, and/or nitrogen (N2) are introduced in a gas mixture of, for example, Ar and O2, Ar and CxHy) Ar and N2, or Ar and O2, CxHy, and N2. Alternatively, oxide, carbide or nitrides may be introduced by utilizing a sputter target comprising oxides, carbides and/or nitrides which is sputtered in the presence of an inert gas (e.g., Ar), or, optionally, may be sputtered in the presence of a sputtering gas comprising O2, CxHy, and/or N2 with or without the presence of an inert gas. Not wishing to be bound by theory, the introduction of O2, CxHy, and/or N2 reactive gases, and oxides, carbides, and/or nitrides inside targets provides oxides, carbides, and/or nitrides that migrate into the grain boundaries, thereby providing a granular perpendicular structure having a reduced lateral exchange coupling between grains.
The interlayers are normally Ru and Ru alloys which grow hcp <002> orientations to serve as templates for perpendicular growth of magnetic alloys. The interlayers have a total thickness of at least 200 Å.
Under conventional process conditions, the perpendicular media structure is not “rigid” enough to survive the sheer stress caused by hard particles. This results in physical mechanical damage and accompanying irreversible magnetic damage and malfunction. In addition, the high cost of Ru makes thinner Ru-based layers desirable.
This invention relates to a perpendicular magnetic recording medium comprising a substrate and a seed layer comprising a Ni alloy.
Preferred embodiments of this invention is shown and described, simply by way of illustration of the best mode contemplated for carrying out this invention, in the following detailed description. As will be realized, this invention is capable of other and different embodiments, and its details are capable of modifications in various obvious respects, all without departing from this invention. Accordingly, the drawings and description are to be regarded as illustrative in nature and not as restrictive.
a) depicts recording media SNR vs. total thickness of Ru-based interlayers.
b) depicts BER vs. total thickness of Ru-based interlayers.
One embodiment of the invention is a perpendicular magnetic recording medium comprising a substrate and a seed layer comprising a Ni alloy. In one variation, the Ni alloy has the composition Ni100-xMx, where x has a value such that the Ni alloy has a FCC crystalline structure. Examples of M include, but are not limited to, V, Cr, W, Al, and Ta. In one variation x has a value of between 0 and about 50.
In another embodiment, a thickness of the seed layer is from about 5 to about 200 Å. In another embodiment, the recording medium further comprises one or more interlayers, wherein a total thickness of the interlayer is from about 10 to about 200 Å.
In one variation, the recording medium could further comprise one or more magnetic layers deposited on the one or more interlayers and a carbon overcoat.
Another embodiment is a method of manufacturing a magnetic recording medium comprising depositing depositing a seed layer comprising a Ni alloy.
Using a Ni alloy as a seed layer promotes perpendicular crystal growth, which allows the Ru and Ru-based alloy interlayers to have a total thickness of less than 200 Å. In addition, the perpendicular media structure becomes more “rigid” and has higher scratch resistance to hard particles.
a) and 5(b) show the effect of total Ru-based interlayer thickness on (a) media SNR and (b) BER when a Ni100-xMx seed layer is used. The interlayer thickness is the sum of thickness of low pressure and high pressure Ru and/or Ru-based layers. When using a seed layer according to one embodiment of the invention, good media SNR can be maintained with a total interlayer thickness down to as thin as 100 Å and good BER is maintained with a total interlayer thickness down to about 120 Å.
An embodiment of the media comprises, from the bottom to the top:
(1) Substrate: polished glass, glass ceramics, or Al/NiP.
(2) Adhesion layers to ensure strong attachment of the functional layers to the substrates. One can have more than one layer for better adhesion or skip this layer if adhesion is fine. The examples include Ti alloys.
(3) Soft underlayers (SUL) include various design types, including a single SUL, anti-ferromagnetic coupled (AFC) structure, laminated SUL, SUL with pinned layer (also called anti-ferromagnetic exchange biased layer), and so on. The examples of SUL materials include FexCoyBz based, and CoxZryNbz/CozZryTaz based series.
(4) Seed layer(s) comprising a Ni alloy having the composition Ni100-xMx, where M is a metal selected from V, Cr, W, Al, and Ta, and x has a value such that the Ni-alloy maintains a FCC crystalline structure. In this embodiment x may have a value of from about 0 to about 50.
(5) Interlayer(s) as a template for Co (00.2) growth. They include Ru-based materials.
(6) Oxide containing magnetic layers (M1) can be sputtered with conventional granular media targets reactively (with Ox) and/or non-reactively. Multiple layers can be employed to achieve desired film property and performance. Examples of targets are Co100-x-yPtx(MO)y and/or Co100-x-y-zPtx(X)y(MO)z series (X is the 3rd additives such as Cr, and M is metal elements such as Si, Ti and Nb). Besides oxides in M1, the list can be easily extended such that the magnetic grains in M1 can be isolated from each other with dielectric materials at grain boundary, such as nitrides (MxNy), carbon (C) and carbides (MxCy). The examples of sputter targets are Co100-x-yPtx(MN)y, Co100-x-yPtx(MC)y and/or Co100-x-y-zPtx(X)y(MN)z, Co100-x-y-zPtx(X)y(MC)z series.
(7) Non-oxide containing magnetic layers (M2): The sputter targets can be used including conventional longitudinal media alloys and/or alloy perpendicular media. Desired performance will be achieved without reactive sputtering. Single layer or multiple layers can be sputtered on the top of oxide containing magnetic layers. The non-oxide magnetic layer(s) will grow epitaxially from oxide granular layer underneath. The orientation could eventually change if these layers are too thick. The examples of these are Co100-x-y-z-αCrxPtyBz XαYβ.
(8) Cap layer, which is optional for this design. In one variation, with dense grains and grain boundary without oxygen may not be necessary. Conventional carbon and lubrication can be adapted for the embodiment of the claimed media to achieve adequate mechanical performance.
The above layered structure of an embodiment is an exemplary structure. In other embodiments, the layered structure could be different with either less or more layers than those stated above.
Instead of the optional NiP coating on the substrate, the layer on the substrate could be any Ni-containing layer such as a NiNb layer, a Cr/NiNb layer, or any other Ni-containing layer. Optionally, there could be an adhesion layer between the substrate and the Ni-containing layer. The surface of the Ni-containing layer could be optionally oxidized.
The substrates used can be Al alloy, glass, or glass-ceramic. The magnetically soft underlayers according to present invention are amorphous or nanocrystalline and can be FeCoB, FeCoC, FeCoTaZr, FeTaC, FeSi, CoZrNb, CoZrTa, etc. The seed layers and interlayer can be Cu, Ag, Au, Pt, Pd, Ru-alloy, etc. The CoPt-based magnetic recording layer can be CoPt, CoPtCr, CoPtCrTa, CoPtCrB, CoPtCrNb, CoPtTi, CoPtCrTi, CoPtCrSi, CoPtCrAl, CoPtCrZr, CoPtCrHf, CoPtCrW, CoPtCrC, CoPtCrMo, CoPtCrRu, etc., deposited under argon gas, or under a gas mixture of argon and oxygen or nitrogen. Dielectric materials such as oxides, carbides or nitrides can be incorporated into the target materials also.
Embodiments of this invention include the use of any of the various magnetic alloys containing Pt and Co, and other combinations of B, Cr, Co, Pt, Ni, Al, Si, Zr, Hf, W, C, Mo, Ru, Ta, Nb, O and N, in the magnetic recording layer.
In a preferred embodiment the total thickness of SUL could be 100 to 5000 Å, and more preferably 600 to 2000 Å. There could be a more than one soft under layer. The laminations of the SUL can have identical thickness or different thickness. The spacer layers between the laminations of SUL could be Ta, C, etc. with thickness between 1 and 50 Å. The thickness of the seed layer, ts, could be in the range of 5 Å<ts<200 Å. The thickness of an intermediate layer could be 10 to 200 Å, and more preferably about 120 Å. The thickness of the magnetic recording layer is about 50 Å to about 300 Å, more preferably 80 to 150 Å. The adhesion enhancement layer could be Ti, TiCr, Cr etc. with thickness of 10 to 50 Å. The overcoat cap layer could be hydrogenated, nitrogenated, hybrid or other forms of carbon with thickness of 5 to 100 Å, and more preferably 20 to 60 Å.
The magnetic recording medium has a remanent coercivity of about 2000 to about 10,000 Oersted, and an Mrt (product of remanance, Mr, and magnetic recording layer thickness, t) of about 0.2 to about 2.0 memu/cm2. In a preferred embodiment, the coercivity is about 2500 to about 9000 Oersted, more preferably in the range of about 4000 to about 8000 Oersted, and most preferably in the range of about 4000 to about 7000 Oersted. In a preferred embodiment, the Mrt is about 0.25 to about 1 memu/cm2, more preferably in the range of about 0.4 to about 0.9 memu/cm2.
Almost all the manufacturing of a disk media takes place in clean rooms where the amount of dust in the atmosphere is kept very low, and is strictly controlled and monitored. After one or more cleaning processes on a non-magnetic substrate, the substrate has an ultra-clean surface and is ready for the deposition of layers of magnetic media on the substrate. The apparatus for depositing all the layers needed for such media could be a static sputter system or a pass-by system, where all the layers except the lubricant are deposited sequentially inside a suitable vacuum environment.
Each of the layers constituting magnetic recording media of the present invention, except for a carbon overcoat and a lubricant topcoat layer, may be deposited or otherwise formed by any suitable physical vapor deposition technique (PVD), e.g., sputtering, or by a combination of PVD techniques, i.e., sputtering, vacuum evaporation, etc., with sputtering being preferred. The carbon overcoat is typically deposited with sputtering or ion beam deposition. The lubricant layer is typically provided as a topcoat by dipping of the medium into a bath containing a solution of the lubricant compound, followed by removal of excess liquid, as by wiping, or by a vapor lube deposition method in a vacuum environment.
Sputtering is perhaps the most important step in the whole process of creating recording media. There are two types of sputtering: pass-by sputtering and static sputtering. In pass-by sputtering, disks are passed inside a vacuum chamber, where they are deposited with the magnetic and non-magnetic materials that are deposited as one or more layers on the substrate when the disks are moving. Static sputtering uses smaller machines, and each disk is picked up and deposited individually when the disks are not moving. The layers on the disk of the embodiment of this invention were deposited by static sputtering in a sputter machine.
The sputtered layers are deposited in what are called bombs, which are loaded onto the sputtering machine. The bombs are vacuum chambers with targets on either side. The substrate is lifted into the bomb and is deposited with the sputtered material.
A layer of lube is preferably applied to the carbon surface as one of the topcoat layers on the disk.
Sputtering leads to some particulates formation on the post sputter disks. These particulates need to be removed to ensure that they do not lead to the scratching between the head and substrate. Once a layer of lube is applied, the substrates move to the buffing stage, where the substrate is polished while it preferentially spins around a spindle. The disk is wiped and a clean lube is evenly applied on the surface.
Subsequently, in some cases, the disk is prepared and tested for quality thorough a three-stage process. First, a burnishing head passes over the surface, removing any bumps (asperities as the technical term goes). The glide head then goes over the disk, checking for remaining bumps, if any. Finally the certifying head checks the surface for manufacturing defects and also measures the magnetic recording ability of the disk.
This application discloses several numerical ranges in the text and figures. The numerical ranges disclosed support any range or value within the disclosed numerical ranges even though a precise range limitation is not stated verbatim in the specification because this invention can be practiced throughout the disclosed numerical ranges. In the claims, the terms “a” and “an” mean one or more.
The above description is presented to enable a person skilled in the art to make and use the invention, and is provided in the context of a particular application and its requirements. Various modifications to the preferred embodiments will be readily apparent to those skilled in the art, and the generic principles defined herein may be applied to other embodiments and applications without departing from the spirit and scope of the invention. Thus, this invention is not intended to be limited to the embodiments shown, but is to be accorded the widest scope consistent with the principles and features disclosed herein.
The implementations described above and other implementations are within the scope of the following claims.
| Number | Name | Date | Kind |
|---|---|---|---|
| 7368185 | Hirayama et al. | May 2008 | B2 |
| 7632580 | Ikeda et al. | Dec 2009 | B2 |
| 20030170500 | Shimizu et al. | Sep 2003 | A1 |
| 20060228587 | Kuboki | Oct 2006 | A1 |
| 20060246323 | Liu et al. | Nov 2006 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20100021770 A1 | Jan 2010 | US |