Patent Application
20060252933
The present invention relates to a Nile red luminescent compound emitting red light, a process for producing the same and a luminescent element utilizing the same. More particularly, this invention relates to a Nile red luminescent compound capable of emitting a light the color of which is nearly crimson, at a high luminance upon the application of electric energy, a novel process of producing the compound and a luminescent element utilizing the same.
For organic electroluminescent elements, which are often abbreviated to “organic Elements”, have been proposed various organic compounds.
However, compounds that are capable of emitting red light at a high luminance and endurable against heat, light, etc. have not been developed.
The objective of this invention is to provide an organic compound capable of emitting red light at a high luminance, and/or capable of emitting a light the color of which is such a red that the value on the x-axis in the CIE chromaticity is over 0.63, and further endurable against heat, light, etc. This invention also aims for providing a process for producing the organic compound and a luminescent element utilizing the compound.
In order to solve the aforementioned problems, this invention provides a Nile red luminescent compound emitting red light that has a structure represented by formula (1):
wherein R1 is a lower alkyl group having from 1 to 5 carbon atoms or benzyl group, or forms —CH2CH2—CR6R7— together with R3 (wherein the carbon atom of the —CR6R7— part is bound to the benzene fragment of chemical formula (1), each of R6 and R7 is a hydrogen atom, a lower alkyl group having from 1 to 5 carbon atoms, or benzyl group, and R6and R7maybe the same or different from each other).
R is a lower alkyl group having from 1 to 5 carbon atoms or benzyl group, or forms —CH2CH2—CR8R9— together with R5 (wherein the carbon atom of the —CR8R9— part is bound to the benzene fragment of chemical formula (1), each of R8 and R9 is a hydrogen atom, a lower alkyl group having from 1 to 5 carbon atoms, or benzyl group, and R8 and R9 maybe the same or different from each other).
R3 is a hydrogen atom, forms —CH2CH2—CR6R7— with R1, or forms with R4 a naphthalene ring including as a part thereof the benzene fragment of chemical formula (1).
R4 is a hydrogen atom, or forms with R3a naphthalene ring including as a part thereof the benzene fragment of chemical formula (1).
R is a hydrogen atom, or forms —CH2CH2—CR8R9— with R2.
X is cyano group or a fluorohydrocarbyl group.
Another solution to the above-mentioned problems is a process for producing the Nile red luminescent compound emitting red light represented by formula (1), comprising reacting a Nile red pigment compound represented by formula (2) with a halogenating agent to produce a halogenated Nile red intermediate represented by formula (3), and replacing the halogen atom with a fluorohydrocarbyl group or cyano group.
In the formula, R1, R2, R3, R4 and R5 mean the same atoms and groups as those defined above.
In the formula, R1, R2, R3, R4 and R5 mean the same atoms and groups as those defined above, and “Hal” denotes a halogen atom.
Still another solution to the above-mentioned problem is a luminescent element comprising a pair of electrodes and a light-emitting layer including the Nile red luminescent compound represented by formula (1) between the electrodes.
The Nile red luminescent compound according to the present invention is represented by formula (1):
In this formula, R1 is a lower alkyl group having 1-5 carbon atoms, or benzyl group. The lower alkyl group includes methyl group, ethyl group, a propyl group, a butyl group and a pentyl group.
R2 is a hydrogen atom or a lower alkyl group having 1-5 carbon atoms, or benzyl group. The lower alkyl group includes the same groups as R1. R1 and R2 may be the same lower alkyl group or different from each other.
Together with R3, R1 forms —CH2CH2—CR6R7— (wherein the carbon atom of the —CR6R7— part is bound to the benzene fragment of chemical formula (1), each of R6 and R7 is a hydrogen atom, a lower alkyl group having 1-5 carbon atoms, or benzyl group, and R6 and R7 may be the same or different from each other).
When R1 and R2 are lower alkyl groups, preferable —NR1R2 includes diethylamino group, di-n-propylamino group, di-i-propylamino group, a butyl group, etc.
Together with R5, R2 forms —CH2CH2—CR8R9— (wherein the carbon atom of the —CR8R9— part is bound to the benzene fragment of chemical formula (1), each of R8 and R9 is a hydrogen atom, a lower alkyl group having 1-5 carbon atoms, or benzyl group, and R8 and R9 may be the same or different from each other).
When R1 forms —CH2CH2—CR R7— with R3, and R2 forms —CH2CH2—CR8R9— with R5, formula (1) becomes the following formula (4):
In this formula (4), R4, R6, R7, R8, R9 and X denote the same as those mentioned above.
Both R3 and R4 may be hydrogen atoms, or form together a naphthalene ring including as a part thereof the benzene fragment of chemical formula (1). The red light-emitting luminescent compound that has the naphthalene ring including as a part thereof the benzene fragment formed by R3 and R4 is represented by formula (5).
In formula (5), R1, R2 and X denote the same as those mentioned above.
In formula (1), X may be a fluorohydrocarbyl group or cyano group.
The fluorohydrocarbyl group includes groups made by replacing one or more hydrogen atoms thereof with fluorine atoms. Specifically, it includes fluoro-lower-hydrocabyl groups made by replacing one or more hydrogen atoms of saturated or unsaturated hydrocarbyl groups having from 1 to 10 carbon atoms with fluorine atoms. In particular, suitable fluoro-hydrocarbyl groups are fluoro-lower-saturated-hydrocarbyl groups made by replacing one or more hydrogen atoms of saturated hydrocarbyl groups that have from 1 to 10, preferably from 1 to 5, carbon atoms with fluorine atoms. More preferable are perfluorohydrocarbyl groups made by replacing all the hydrogen atoms of saturated hydrocarbyl groups that have from 1 to 5 carbon atoms with fluorine atoms. Specific examples of the fluoro-lower-saturated-hydrocarbyl group are —CH2F, —CHF2, —CF3, —CH2CF3, —CHFCF3, —CF2CF3, —CH2CH2CF3, —CH2CHFCF3, —CH2CF2CH3, —CH2FCF2CF3, etc. Examples of the perfluoroalkyl group are —CF3, —CF2CF3, —CF2(CF2)nCF3, wherein n denotes an integer from 1 to 3. The most preferable are —CF3 and —CF2CF3.
In the Nile red luminescent compound represented by formula (1), —NR1R2 is an electron-donating group and the fluorohydrocarbyl group or cyano group represented by X is an electron attractive group, so that π electron cloud on the skeleton of the Nile red compound is extended to the substituents. Therefore, we surmise that the application of a little energy enables the luminescent compound to emit red light. The novel luminescent compound of this invention is characterized by the structure where R1—N—R2, the electron-donating group, provides the π electron cloud with electrons. Because this Nile red skeleton has an electronically stable structure and therefore the Nile red luminescent compound is chemically stable, the luminescent compound does not deteriorate even under severe environments, which is a special characteristic of the compound.
The Nile red luminescent compound emitting red light represented by formula (1) may be prepared by the following method.
The compound may be obtained by reacting a Nile red compound represented by general formula (2) with a halogenating agent.
The halogenating agent may be a common one that is able to replace hydrogen atoms on an aromatic ring with halogen atoms. Specific examples of the halogenating agent are sulfuryl chloride, phosphorus pentachloride, etc. when hydrogen atoms on an aromatic ring are replaced with chlorine atoms. Generally, when hydrogen atoms on an aromatic ring are replaced with halogen atoms, an imido-N-halosuccinate such as an imido-N-bromosuccinate, and a dialkyl halomalonate such as a dialkyl bromomalonate may be used.
The Nile red compound represented by formula (2) and the halogenating agent react easily by heating them in a solvent. The solvent includes acetic anhydride, acetic acid, an acid anhydride having not more than 5 carbon atoms, an aromatic solvent such as benzene or toluene, a chlorinated solvent such as dichloromethane or chloroform, a dioxane, etc. The reaction temperature usually ranges between 0 and 250° C., preferably between 20 and 170° C. After the reaction, purification and separation by an ordinary method will provide the targeted halogenated Nile red intermediate represented by formula (3).
In formula (3), R1, R2, R3, R4 and R5 mean the same atoms and groups as those defined above, and “Hal” denotes a halogen atom.
The halogenated Nile red intermediate is converted to the Nile red luminescent compound represented by formula (1) by replacing the halogen atom thereof with the halohydrocarbyl group or cyano group.
To introduce the halohydrocarbyl group into the intermediate, a method of reacting the intermediate with a metal perfluorohydrocarbyl reagent, which is generated in the reaction system, such as a copper perfluoroalkyl reagent, a method of generating a perfluoroalkyl radical, which is followed by the reaction with the halogenated Nile red intermediate, a method of dehydration by adding a metal perfluoroalkyl reagent, such as a Grignard reagent, a lithium reagent, or an aluminum reagent, to a carbonyl compound, or other methods may be employed. Although the halogen atom “Hal” of the intermediate may be any one of iodine, bromine, fluorine, and chlorine, the employment of iodine or bromine is recommended because iodine and bromine are easy to handle and the employment thereof produces the targeted with high yields.
Among the above-mentioned methods, the method of producing a copper perfluoroalkyl reagent in the reaction system from a perfluoroalkyl iodide, which is represented by the formula CmF2m+1I wherein m is an integer from 1 to 20, preferably from 1 to 10, more preferably from 1 to 5, and copper powder, which is followed by the reaction of this copper perfluoro alkyl reagent with the halogenated Nile red intermediate represented by formula (3) is preferable. The raw materials for this method are not expensive, and easy to obtain and handle. Moreover, the yield of the reaction product is high.
The introduction of a cyano group into the halogenated Nile red intermediate represented by formula (3) is suitably carried out by reacting the intermediate with a transition metal cyanide. The cyanidation reaction is usually done in a polar aprotic solvent, examples of which are aromatic amines such as pyridine or quinoline, dimethylformamide (DMF), N-methyl-pyrrolidone, hexamethylphosphoric triamide (HMPA), etc.
The halogenated Nile red intermediate can be easily produced only by heating a mixture of the Nile red compound and the halogenating agent. Furthermore, the introduction of a cyano group or a fluorohydrocarbyl group into the intermediate proceeds quickly by heating. Therefore, this simple production method of the Nile red luminescent compound emitting red light is an industrial method.
The luminescent element according to the present invention will be explained hereinafter.
When the luminescent element shown in
Examples of the blue light-emitting compound are diphenylvinyl biphenol compounds emitting blue light and stilbene compounds emitting blue light. A preferable diphenylvinyl biphenol compound emitting blue light is DPVBi represented by formula (10).
For the green light-emitting compound is suitable a coumarin compound emitting green light, an indophenol compound emitting green light, or an indigo compound emitting green light. The coumarin compound represented by formula (11) is preferable among them.
Upon the application of an electric field between the transparent electrode 2 and the electrode layer 4, electrons are injected from the electrode layer 4 and positive holes are injected from the transparent electrode 2. In the light-emitting layer 3, the electrons are recombined with positive holes, which causes the energy level to return to the valence band from the conduction band. This transition of the energy level is accompanied by emission of the energy differential as light.
The luminescent element A shown in
As understood from the foregoing, when the light-emitting layer of the luminescent element A includes the Nile red luminescent compound emitting red light of the present invention and not the blue light-emitting compound or the green light-emitting compound, the luminescent element A emits clear red light.
The luminescent element A may also be shaped into a tubular light emitter comprising a tubularly shaped substrate 1, a transparent electrode 2 placed on the inside surface of the substrate 1, a light emitting layer 3 and an electrode layer 4 placed on the transparent electrode 2 in this order. Because this luminescent element A does not include mercury, it is an ecological light source and maybe a substitute for conventional fluorescent lamps.
For the substrate 1 may be used any known substrate, as long as the transparent electrode 2 can be formed on the surface of the substrate. Examples of the substrate 1 are a glass substrate, a plastic sheet, a ceramic substrate, and a metal substrate, the surface of which is insulated, for example, by forming an insulating layer thereon.
When the substrate 1 is opaque, the luminescent element, which includes the blue light-emitting compound, the green light-emitting compound and the Nile red luminescent compound of the present invention, is a single-faced illuminator that emits white light from one side of the element. On the other hand, when the substrate 1 is transparent, the luminescent element is a double-faced illuminator that emits white light from both of the substrate 1 and the surface layer opposite to the substrate.
For the transparent electrode 2, various materials may be employed, as long as their work functions are large, they are transparent, and they can function as a cathode and inject holes to the light-emitting layer 3 when voltage is applied thereto. Specifically, the transparent electrode 2 may be made of a transparent inorganic conductive material of ITO, In2O3, SnO2, ZnO, CdO, etc. and derivatives thereof, or an electrically conductive high polymer such as polyaniline.
The transparent electrode 2 maybe formed on the substrate 1 by chemical vapor phase deposition, spray pyrolysis, high-vacuum metal deposition, electron beam deposition, sputtering, ion beam sputtering, ion plating, ion-assisted deposition, and other methods.
When the substrate is made of an opaque material, the electrode formed on the substrate need not be transparent.
The light-emitting layer 3 includes the Nile red luminescent compound of the present invention when the layer 3 is intended to emit red light. It includes a blue light-emitting compound and a green light-emitting compound in addition to the Nile red luminescent compound of the present invention when it is intended to emit white light. The light-emitting layer 3 may be a high polymer film prepared by dispersing the Nile red luminescent compound emitting red light of the present invention, or a blue light-emitting compound, a green light-emitting compound and the Nile red luminescent compound of the present invention in a high polymer. Also, the light-emitting layer 3 may be a deposited film which is prepared by depositing the Nile red luminescent compound of the present invention, or a blue light-emitting compound, a green light-emitting compound and the Nile red luminescent compound of the present invention on the transparent electrode 2.
Examples of the high polymer for the high polymer film are a polyvinyl carbazole, a poly(3-alkylthiophen), apolyimide including an arylamide, a polyfluorene, a polyphenylene vinylene, poly-α-methylstyrene, and a copolymer of vinylcarbazole and α-methylstyrene. Among them, a polyvinyl carbazole is preferable.
The amount of the Nile red luminescent compound emitting red light, or that of a blue light-emitting compound, a green light-emitting compound and the Nile red luminescent compound in the high polymer film is, typically, 0.01 to 2 weight %, preferably, 0.05 to 0.5 weight %.
The thickness of the high polymer film ranges, typically, between 30 nm and 500 nm, preferably between 100 nm and 300 nm. When the thickness is too small, the amount of the emitted light maybe insufficient. On the other hand, when the thickness is too large, voltage required to drive the element may be too high, which is not desirable. Besides, the large thickness may reduce the flexibility of the element necessary to shape a planar, tubular, curved or ring article.
A typical example of forming the high polymer film on the transparent electrode may be the application of a solution of the Nile red luminescent compound or the mixture of a blue light-emitting compound, a green light-emitting compound and the Nile redluminescent compound dissolved in a suitable solvent onto the transparent electrode. The application method includes, for example, a spin cast method, a coating method, a dip method, etc.
When the light-emitting layer 3 is made of a deposited film, the thickness of the film is typically 0.1 to 100 nm, although it varies depending on the structure of the light-emitting layer 3. When the thickness is too small or too large, the deposited film layer will have the same problems as the high polymer film layer described above.
For the electrode layer 4 may be employed a material having a small work function. Examples of the material are elementary metals and metallic alloys, such as MgAg, aluminum alloy, metallic calcium, etc. A preferable electrode layer 4 is made of an alloy of aluminum and a small amount of lithium. This electrode may easily be formed on the surface of light-emitting layer 3, which, in turn, has been formed on substrate 1, by the technique of metal deposition.
When either of the deposition or the application is employed for the formation of the light-emitting layer, a buffer layer should be inserted between the electrode layer and the light-emitting layer.
Materials for the buffer layer are, for example, an alkaline metal compound such as lithium fluoride, an alkaline earth metal compound such as magnesium fluoride, an oxide such as an aluminum oxide, and 4,4′-biscarbazole biphenyl(Cz-TPD). Also, materials for forming a buffer layer between the cathode made of ITO, etc. and the organic layer are, for example, m-MTDATA (4,4′,4″-tris(3-methylphenyl-phenylamino)triphenylamine), phthalocyanine, polyaniline, and polythiophene derivatives, and inorganic oxides such as molybdenum oxide, ruthenium oxide, vanadium oxide and lithium fluoride. When the materials are suitably selected, these buffer layers can lower the driving voltage of the organic EL element, which is the luminescent element, improve the quantum efficiency of luminescence, and achieve an increase in the luminance of the emitted light.
Next, the second example of the luminescent element according to this invention is shown in
As shown in
The substrate 1, the transparent electrode 2 and the electrode layer 4 are the same as those explained for the luminescent element A in
The light-emitting layer of the luminescent element B comprises the light-emitting sublayers 3a and 3b. The light-emitting sublayer 3a is a deposited film including light-emitting compounds. The light-emitting sublayer 3b is a DPVBi layer that functions as a host.
Examples of the hole-transporting substance included in the hole-transporting layer 5 are a triphenylamine compound such as N,N′-diphenyl-N,N′-di(m-tolyl) -benzidine (TPD) and a -NPD, a hydrazon compound, a stilbene compound, a heterocyclic compound, a π electron star burst positive hole transporting substance, etc.
Examples of the electron-transporting substance included in the electron-transporting layer 6 are an oxadiazole derivative such as 2-(4-tert-butylphenyl)-5-(4-biphenyl)-1,3,4-oxadiazole and 2,5-bis(1-naphthyl)-1,3,4-oxadiazole, and2,5-bis (5′-tert-butyl-2′-benzoxazolyl) thiophene. Also, a metal complex material such as quinolinol aluminum complex (Alq3), benzoquinolinol beryllium complex (Bebq2) may be used suitably.
The luminescent element B shown in
The thickness of each layer is the same as that of the corresponding layer in a known multi-layer organic EL element.
The luminescent element B in
The third example of the luminescent element of this invention is shown in
The luminescent element C shown in
The luminescent element C functions in the same way as the luminescent element B.
Another example of the luminescent element of this invention is shown in
An example of the luminescent elements, other than those shown in
The electron-transporting layer typically comprises 50-80% by weight of apolyvinyl carbazole (PVK), 5-40% by weight of an electron-transporting luminescent agent, and 0.01-20% by weight of the Nile red luminescent compound of the present invention. A composition within these ranges results in the emission of red light at a strong luminance.
Also, it is preferred if the light-emitting layer includes, as a sensitizing agent, rubrene, especially both of rubrene and Alq3.
A red light-emitting element utilizing the Nile red luminescent compound emitting red light of the present invention, or a white light-emitting element utilizing a blue light-emitting compound, a green light-emitting compound and the Nile red luminescent compound of the present invention may generally be used for an organic EL element driven by direct current, and also by pulses and alternating current.
The present invention will be explained in more detail by means of examples hereinafter. Needless to say, the present invention is not limited to the examples.
<Synthesis of a Brominated Nile Red Intermediate>
5.0 g (15.7 mmol) of Nile red, 5.63 g (23.6 mmol) of diethyl bromomalonate, and 250 ml of acetic anhydride were placed in a 500 ml pear-shaped flask. The solution in the pear-shaped flask was heated in a silicone oil bath to 135° C. and allowed to react for 2.5 hours at around this temperature. Acetic anhydride was distilled away with an evaporator and solids were obtained. A column, which had been filled with silica gel, was charged with the solids, and the solids were purified with benzene as a developer. 200 mg of a deep green solid matter was obtained. The yield was 3.2%. The melting point of the solid matter was 204-205° C. An IR spectrum of this deep green solid matter is shown in
Calculated values: C: 60.47, H: 4.31, N: 7.05, O: 8.05, Br: 20.11
Found values: C: 59.19, H: 4.24, N: 6.43, O: 8.36, Br: 21.61
Based on these results, the deep green solid matter was identified as a Nile red luminescent compound emitting red light that had the structure represented by formula (6).
The brominated Nile red intermediate can also be synthesized by reacting Nile red with N-bromosuccinimide. Generally, N-bromosuccinimide is known as a good brominating agent that is able to replace a hydrogen atom of allyl with a high yield.
In the followings, an example of producing the brominated Nile red intermediate represented by formula (6) by using N-bromosuccinimide will be shown.
10.0 g (31.4 mmol) of Nile red, 6.20 g (34.8 mmol) of N-bromosuccinimide, 0.10 g of AIBN, and 780 ml of carbon tetrachloride were placed in a 2000 ml flask. The solution in the flask was heated in a silicone oil bath to 100° C. and allowed to react for 2 hours at around this temperature. Carbon tetrachloride was distilled away with an evaporator, and solids were obtained. The solids were purified by a column chromatography that used chloroform for the developer. The purified was further recrystallized in toluene. 5.1 g of a deep green solid matter was obtained. The yield was 41%. The melting point of the solid matter was204-205° C. The employment of N-bromosuccinimide made it possible to produce the Nile red intermediate with that high yield.
<Introduction of Trifluoromethyl Group>
In a 50 ml auto clave made of stainless steel, with a stirrer, a thermometer and a heating bath were placed 1.0 g (16.0 mmol) of copper powder that had been prepared from copper sulfate, 10 ml of dimethylformamide (DMF), which had been dried so that it contained not more than 3.0% by weight of water, and 1.98 g (5.0 mmol) of the brominated Nile red intermediate represented by formula (6) in a nitrogen atmosphere. Then the autoclave was cooled to −35° C., and 1.37 g (7.0 mmol) of trifluoromethyl iodide was also introduced into the autoclave. The mixture in the autoclave was stirred at a heated temperature of 130 to 140° C. for 20 hours. Upon the termination of the reaction, the reaction product was cooled to room temperature. 20 ml of water and 15 ml of toluene were added to the cooled product, and the obtained mixture was filtered so that insoluble matters such as copper bromide were removed. Then, the organic phase was separated from the filtrate, and the separated organic liquid was washed with 30 ml of water. The washed was dried with anhydrous sodium sulfate, the dried was filtered, and the separated filtrate was concentrated with an evaporator. The obtained crude product was purified by a column chromatography that used chloroform for the developer. 1.39 g of a trifluoromethyl group-introduced product was obtained. The yield was 72%.
The obtained product, which was a solid matter, was purified by sublimation with a TRS-LSS apparatus produced by ULVAC-RIKO, Inc. (temperature of the high-temperature part: 190° C., temperature of the low-temperature part: 125° C., pressure: 0.5 Pa). Deep green crystals were obtained. The melting point of the crystals was from 234 to 236° C. The fluorescence spectrum of this product was measured with a model F-4500 spectrofluorophotometer (exciting wavelength: 365 nm, solvent: dioxane, concentration: 0.05% by weight). The wavelength of the maximum emission was 607.2 nm. The measured spectrum is shown in
The results of elemental analysis of these deep green crystals are as follows.
Calculated values: C: 65.28, H: 4.43, N: 7.25, O: 8.28, F: 14.75
Found values: C: 64.98, H: 4.36, N: 7.35, O: 8.33, F: 14.80
Based on these results, the deep green crystals were identified as a Nile red luminescent compound emitting red light that had the structure represented by formula (7).
As understood from
<Introduction of Cyano Group>
In a 50 ml pear-shaped flask with a condenser were placed 0.27 g (3.0 mmol) of copper cyanide, 10 ml of dimethylformamide (DMF), which had been dried so that it contained not more than 3.0% by weight of water, and 1 g (2.52 mmol) of the brominated Nile red intermediate represented by formula (6). The mixture in the pear-shaped flask was refluxed with stirring for 4 hours. After the termination of the reaction was confirmed by thin-layer chromatography, the reaction product liquid was poured into a mixture of 10 ml of water and 3 ml of ethylenediamine. This mixture including the reaction product was extracted twice, each time with 10 ml of dichloromethane. Then, the obtained organic liquid was washed twice, each time with 10 ml of a saturated solution of salt. The washed was dried with anhydrous sodium sulfate, and the dried was filtered, so that the filtrate was separated. The solvent of the filtrate was distilled away under reduced pressure with an evaporator. The concentrated crude product was purified by a column chromatography that used silica gel for the filler. 0.76 g of crude crystals of a cyanide product was obtained. The yield was 88%.
The obtained crude crystals were purified by sublimation with a TRS-lSS apparatus produced by ULVAC-RIKO, Inc. (temperature of the high-temperature part: 250° C., temperature of the low-temperature part: 150° C., pressure: 0.5 Pa). Deep green crystals were obtained. The melting point of the crystals was from 263 to 265° C. The fluorescence spectrum of this product was measured with a model F-4500 spectrofluorophotometer (exciting wavelength: 365 nm, solvent: dioxane, concentration: 0.05% by weight). The wavelength of the maximum emission was 629.8 nm. The measured spectrum is shown in
The results of elemental analysis of the deep green crystals are as follows.
Calculated values: C: 73.45, H: 4.99, N: 12.24, O: 9.32
Found values: C: 73.22, H: 4.95, N: 12.31, O: 9.44
Based on these results, the deep green crystals were identified as a Nile red luminescent compound emitting red light that has the structure represented by formula (8).
This invention can provide a novel Nile red luminescent compound capable of emitting at a high luminance a light that has a peak wavelength the color of which is very closer to crimson, and of enduring heat and light. Conventional technologies could not realize such luminescent compounds.
This invention can also provide a novel Nile red luminescent compound, from which a luminescent element emitting white light can be prepared.
Furthermore, this invention can provide an industrial process for easily producing the Nile red luminescent compound.
Still further, this invention can provide an EL element, the light-emitting layer of which contains the novel Nile red luminescent compound, capable of emitting a crimson light at a high luminance. Also, when the light-emitting layer includes a green light-emitting compound and a blue light-emitting compound together with the Nile red luminescent compound, a luminescent element emitting white light can be provided.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2003-025188 | Jan 2003 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP04/00771 | 1/28/2004 | WO | 6/20/2006 |