Patent Application
20160244869
This application is based upon and claims the benefit of priority from Japanese Patent Application No. 2013-204786 filed on Sep. 30, 2013; the entire contents of which are incorporated herein by reference.
The present invention relates to a nitriding process method of a steel member, the method forming a nitride compound layer on a surface of the steel member by a nitriding process
Steel members such as gears used in automobile transmissions are required to be high in pitting resistance and bending fatigue strength, and to meet such requirement, increasing strength by a carburizing process or a nitriding process has been in practice as a method to strengthen steel members such as gears.
It has been conventionally known that, for improving pitting resistance and bending fatigue strength of a steel member, it is effective to generate an iron nitride compound layer whose main component is a γ′ phase, on a surface of the steel member by a nitriding process, as described in, for example, Patent Document 1.
Further, as a nitriding process method capable of making nitrogen contained in a steel member uniformly from its surface layer up to deep portion in a short time, Patent Document 2 describes that, after a nitriding process is performed in, for example, a 100% NH3 atmosphere in a heating furnace, a nitriding process is performed under a lower NH3 gas concentration than the above, for example, 50% and a 50% N2 gas concentration.
[Patent Document 1] Japanese Patent Application No. 2012-095035
[Patent Document 2] Japanese Laid-open Patent Publication No. 2007-238969
In order to generate the γ′ phase on the surface layer, it is necessary for a NH3 partial pressure in a furnace during the nitriding process to be low, but the method described in Patent Document 1 has restriction that a flow velocity of nitriding process gas in the furnace needs to be 1 m/sec or higher in order to uniformly form the nitride compound layer. Further, if a component has a complicated shape, it has been difficult to generate the nitride compound layer uniformly over positions of the component. Further, in mass production, there has been a problem about productivity due to a great thickness variation among the nitride compound layers in a lot.
Further, Patent Document 2 describes that its nitriding process method achieves the uniform nitriding in a short time, but does not mention a phase change of the compound and so on in this method.
It is an object of the present invention to provide a method of manufacturing a nitrided steel member high in pitting resistance and bending fatigue strength, the method being free from restriction of wind velocity and capable of generating a nitride compound layer having a desired phase mode, uniformly all over a component to be treated, even if it is a mass-produced component to be treated.
To solve the aforesaid problems, the present invention provides a nitriding process method of a steel member, wherein a first nitriding process step is performed in which the steel member is subjected to a nitriding process in a nitriding gas atmosphere having a nitriding potential with which a nitride compound layer having a γ′ phase or an e phase is generated, and thereafter a second nitriding process step is performed in which the steel member is subjected to a nitriding process in a nitriding gas atmosphere having a nitriding potential lower than the nitriding potential in the first nitriding process step, to thereby precipitate the γ′ phase in the nitride compound layer.
The first nitriding process step may be performed in a nitriding gas atmosphere having a 0.6 to 1.51 nitriding potential, and the second nitriding process step may be performed in a nitriding gas atmosphere having a 0.16 to 0.25 nitriding potential.
According to the present invention, it is possible to generate a nitride compound layer having a desired phase mode, uniformly all over a component to be treated, even if it is a mass-produced component to be treated, without any restriction of wind velocity, and to manufacture a nitrided steel member high in pitting resistance and bending fatigue strength.
[FIG. 1] is an explanatory view illustrating an example of the structure of a heat treatment apparatus.
[FIG. 2] is an explanatory process chart of a nitriding process.
[FIG. 3] is a chart illustrating phases of a compound which are generated depending on KN and temperature.
Hereinafter, an embodiment of the present invention will be described with reference to the drawings.
In the present invention, a steel member is subjected to a gas nitriding process, whereby an iron nitride compound layer whose main component is a γ′ phase is formed on a surface of the steel member (base metal).
A heat treatment apparatus 1, for example, illustrated in
Heaters 25 are disposed in the heating chamber 11. Nitriding process gas made up of N2 gas, NH3 gas, and H2 gas is introduced into the heating chamber 11, the nitriding process gas is heated to a predetermined temperature by the heaters 25, and the steel member loaded into the heating chamber 11 is subjected to the nitriding process. A fan 26 for stirring the process gas in the heating chamber 11 and keeping the heating temperature of the steel member uniform is fit in a ceiling of the heating chamber 11. An openable/closable intermediate door 27 is attached to an exit side (right side in
An elevator 30 which lifts up and down the case 20 housing the steel member is installed in the cooling chamber 12. An oil tank 32 storing cooling oil 31 is installed in a lower part of the cooling chamber 12. An exit food 36 including an openable/closable door 35 is attached to an exit side (right side in
In the above-described heat treatment apparatus 1, the case 20 housing the steel member is loaded into the heating chamber 11 from the loading unit 10 by a pusher or the like. Incidentally, it is preferable to pre-clean the treatment target (steel member to be nitrided) prior to the nitriding process, in order to remove dirt and oil therefrom. The pre-cleaning is preferably, for example, vacuum cleaning which degreases and dries the treatment target by dissolving and replacing oil and so on by a hydrocarbon-based cleaning liquid and vaporizing it, alkaline cleaning which degreases the treatment target by an alkaline cleaning liquid, or the like.
Then, after the case 20 housing the steel member thus pre-treated is loaded into the heating chamber 11, the process gas is introduced into the heating chamber 11. Further, the process gas introduced into the heating chamber 11 is heated to the predetermined temperature by the heaters 25, and the steel member loaded into the heating chamber 11 is subjected to the nitriding process while the process gas is stirred by the fan 26. The heat treatment apparatus in
After the temperature in the heating chamber 11 reaches the nitriding process temperature which is, for example, 600° C., a first nitriding process step is first performed in an atmosphere having a high nitriding potential KN in order to promote the initial generation of the nitride compound layer on the surface layer of the steel member. Note that the nitriding potential KN is expressed by the following well-known expression (1) using a ratio between a partial pressure P(NH3) of the NH3 gas and a partial pressure P(H2) of the H2 gas.
KN═P(NH3)/P(H2)3/2 (1)
In the step of subjecting the steel member to the nitriding process, the partial pressure P(NH3) of the NH3 gas in the heating chamber 11 and the partial pressure P(H2) of the H2 gas are controlled to predetermined ranges. It is possible to control these gas partial pressures by analyzing the NH3 gas of the atmosphere in the heating chamber 11 by an infrared absorption method and analyzing the H2 gas by a high corrosion resistance thermal conductivity method, and while analyzing their analytic values online, automatically adjusting the flow rate of the H2 gas that is to be supplied to the heating chamber 11. For example, as indicated in
After the first nitriding process step, a second nitriding process step to form the nitride compound layer having a desired phase mode is performed in an atmosphere whose nitriding potential KN is lowered. For example, as indicated in
While the nitriding process is performed, the fan in the heating chamber 11 is rotated at, for example, 1800 rpm to uniformly diffuse the nitriding process gas. The nitriding process time indicated in
Incidentally, if the steel member is made of, for example, a carbon steel material for mechanical structure or an alloy steel material for mechanical structure, the temperature in the heating chamber 22 during the nitriding process is preferably kept at 520 to 610° C., though differing depending on the member to be treated. The higher the temperature of the nitriding process, the higher productivity is, but when the temperature is higher than 610° C., softening, an increase of strain, and the like may occur in the member to be treated. When it is lower than 520° C., a formation speed of the iron nitride compound layer becomes slow, which is not preferable in view of cost. Further, as a difference between the process temperatures in the first nitriding process step and the second nitriding process step is smaller, it is possible to perform the nitriding process with the smallest possible variation in temperature among members to be treated, which makes it possible to reduce variation in nitriding quality among the members to be treated. The temperature difference between the both process steps is preferably controlled to be within 50° C., and more preferably within 30° C., and still more preferably they are the same temperature.
When the second nitriding process step is finished, a cooling step is performed.
Alternatively, for example, in the first nitriding process step, the ε+γ′ phase may be generated in the initial nitriding period under a lower temperature and a higher nitriding potential KN such as the C point in
By the nitriding process being performed under the above condition, it is possible to obtain a nitrided steel member having, on its surface, the iron nitride compound layer whose main component is the γ′ phase. The steel member thus obtained has increased strength with a nitrogen diffusion layer and a nitride being formed therein, and has sufficient pitting resistance and bending fatigue strength with the γ′ phase-rich iron nitride compound layer being formed on its surface.
In the present invention, without performing the nitriding process under a low NH3 partial pressure ratio for a long time or without controlling the wind velocity as has been done in a conventional nitriding process method, the initial generation of the nitride compound layer is promoted by increasing the NH3 partial pressure ratio in the initial period of the nitriding process, and the mode of the nitride compound is controlled by thereafter performing the nitriding process under the decreased NH3 partial pressure ratio. Consequently, it is possible to produce the compound layer having a desired phase mode over the positions of the component to be treated uniformly and in a large amount, without any restriction of the wind velocity.
Further, as compared with carburizing and carbonitriding processes, the nitriding process of the present invention causes only a small strain amount since it is a process at an austenite transformation temperature or lower. Further, since a quenching step indispensable in the carburizing and carbonitriding processes can be dispensed with, a strain variation amount is also smaller. As a result, it is possible to obtain the nitrided steel member high in strength and low in strain.
Hitherto, a preferred embodiment of the present invention has been described, but the present invention is not limited to such an example. It would be obvious for those skilled in the art to think of various change examples or modification examples within the scope of the technical idea described in the claims, and these examples are naturally construed as being included in the technical range of the present invention.
Ring gears in a cylindrical shape and ring gears in a bottomed cylindrical shape which are steel members were used as treatment targets, and they were subjected to a nitriding process.
In an example 1 and a comparative example 1, the ring gears in the cylindrical shape were subjected to the nitriding process. An eight-tier jig was used, the number of the members loaded thereon was 320, and they were loaded in a flat manner In the example 1, a nitriding process was performed in which the first nitriding process step is performed in an atmosphere of KN=1.03 for ten minutes, and the second nitriding process step was performed in an atmosphere of KN=0.24 for 110 minutes. In the comparative example 1, a nitriding process was performed in an atmosphere of KN=0.25 for 120 minutes. Conditions and results of the nitriding processes are presented in Table 1. Note that a temperature condition was set as indicated in
In the steel member subjected to the nitriding process by the present invention, the generated γ′ phase-rich nitride compound layer preferably has a 4 to 16 μm thickness. When the thickness is less than 4 μm, fatigue strength is not improved sufficiently due to too small a thickness. On the other hand, when the thickness is over 16 μm, since a nitrogen diffusion speed in the γ′ phase becomes slow, the nitrogen concentration in the γ′ phase becomes high and a ratio of the e phase increases, so that the whole nitride compound layer becomes brittle to be easily peeled off, and an improvement of the fatigue strength cannot be expected. A process capability index Cp(6σ) of the example 1 which was calculated when 4 to 16 μm in this preferable range were set as an upper limit value and a lower limit value turned out to be 3.45, which is far higher than that of the comparative example 1. The process capability index is process capability expressed as a numeric value, and is a value equal to a standard width divided by 6σ (σ: standard deviation). If Cp≧1.33, the process capability is sufficient, and 99.9% or more of products are up to standard.
In examples 2 to 8 and a comparative example 2, the ring gears in the bottomed cylindrical shape were subjected to a nitriding process. An eight-tire jig was used and the number of the members loaded thereon was 320, and they were loaded with their bottoms downward. In the examples 2 to 8, a flow rate of NH3 gas was set to 120 L/min and 60 L/min in the first nitriding process step and the second nitriding process step respectively, and a flow rate of H2 gas was adjusted, whereby KN was controlled to fall within a 0.60 to 1.51 range in the first nitriding process step, and KN was controlled to fall within a 0.16 to 0.25 range in the second nitriding process step. The first and second nitriding process steps in the examples 2 to 8 were performed for 60 minutes each. In the comparative example 2 as in the comparative example 1, the nitriding process was performed in an atmosphere of KN=0.25 for 120 minutes. Conditions and results of the nitriding processes are presented in Table 2. Note that a temperature condition was set as in
In all of the examples 2 to 8, it was possible to obtain a 40% γ′ phase or more, and a process capability index Cp(6σ) fell within a 1.57 to 2.82 range. On the other hand, in the comparative example 2, a thickness variation of the compound layer in a lot was not up to standard, and the products were of no industrial value. Further, in the comparative example 1, since the rings have a simple shape, a wind velocity in a furnace was sound, but the examples of the present invention have higher industrial reliability.
As described above, according to the examples of the present invention, it was possible to obtain nitrided steel members which were strengthened with a nitrogen diffusion layer and a nitride being formed in each of them, and which had sufficient pitting resistance and bending fatigue strength with a γ′ phase-rich iron nitride compound layer being formed on a surface of each of them. Further, since the nitriding process is performed at an austenite transformation temperature or lower, a strain amount is small, and in addition since a quenching step can be dispensed with, a strain variation amount is also small. Therefore, by carrying out the present invention, it was possible to obtain a nitrided steel member high in strength and low in strain.
The present invention is useful for steel nitriding technology.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013-204786 | Sep 2013 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2014/076178 | 9/30/2014 | WO | 00 |