Patent Grant
10888850
Catalyst compositions, catalyst precursor compositions, and corresponding methods suitable for hydroprocessing of distillate boiling range feeds are provided, such as distillate boiling range feeds suitable for fuels production.
The requirements for production of diesel boiling range fuels can potentially vary during the course of a year. During summer months, a primary goal of hydroprocessing can be reduction of sulfur and/or nitrogen content of diesel boiling range fuels in order to satisfy regulatory requirements. Sulfur reduction can also be important during winter months, but an additional consideration can be improving the cold flow properties of the diesel boiling range fuels. Dewaxing of diesel boiling range fractions can be used to provide improved cold flow properties, but this can also result in loss of product yield. Methods which can allow for improved production of diesel boiling range fuels while maintaining or improving the yield of such fuels can therefore be desirable.
U.S. Pat. No. 8,394,255 describes methods for integrated hydrocracking and dewaxing of a feed under sour conditions for formation of diesel and lubricant boiling range fractions.
U.S. Provisional Patent Application No. 62/270,213 describes base metal dewaxing catalysts, methods for making the base metal dewaxing catalysts, and methods for performing dewaxing using such catalysts.
U.S. Provisional Patent Application No. 62/270,234 describes methods for dewaxing distillate boiling range feeds, such as distillate boiling range feeds suitable for fuels production.
In various aspects, a catalyst precursor is provided comprising at least one noble metal, at least one Group 6 metal, at least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, and a dispersion agent supported on a support comprising a zeolitic framework structure. The catalyst precursor can have a molar ratio of the least one Group 8-10 base metal to the at least one Group 6 metal of about 0.1 to about 10 and a molar ratio of the dispersion agent to the least one Group 8-10 base metal of about 0.5 to about 10
In some aspects, the zeolitic framework structure can comprise an MEL framework structure, such as ZSM-11. In some aspects, the MEL framework structure can comprise a molar ratio of silica to alumina of about 35 to about 55 and/or an alpha value of at least about 380 and/or a total surface area of at least about 350 m2/g. In other aspects, the zeolitic framework structure can comprise ZSM-48, ZSM-11, a zeolitic framework structure having a 10-member ring as a largest pore channel, or a combination thereof.
In some aspects, the catalyst precursor can comprise less than about 2.0 wt % of the at least one noble metal and about 2.0 wt % to about 30 wt % of the at least one Group 6 metal and the at least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, based on a weight of the catalyst precursor. The at least one noble metal optionally comprises Pt, Ru, Os, Rh, Ir, or a combination thereof. The at least one Group 8-10 base metal can comprise Ni, Co or a combination thereof. The at least one Group 6 metal can comprise W, Mo, or a combination thereof.
In some aspects, the dispersion agent can comprise a compound having 2-10 carbon atoms and a carbon atom to oxygen atom ratio of about 0.6 to about 2.0. The dispersion agent can comprise a glycol, a carboxylic acid, or a combination thereof. For example, the dispersion agent can comprise citric acid, gluconic acid, nitrilotriacetic acid, ethylene glycol, or a combination thereof.
In some aspects, the support can further comprise a binder selected from the group consisting of an active or inactive material, an inorganic material, a clay, alumina, silica, silica-alumina, titania, zirconia, or a combination thereof. The alumina binder can optionally have a surface area of about 150 m2/g or less.
In other aspects, a method of forming a composition is provided. The method can be suitable, for example, for forming a catalyst precursor according to the above aspects. The method can include impregnating a support comprising a zeolitic framework structure with a first impregnation solution comprising at least one Group 6 metal salt, at least one Group 8-10 base metal salt, preferably at least one non-noble Group 8-10 base metal salt, and a dispersion agent to form a catalyst precursor. The resulting impregnated support can then be dried at a temperature of about 80° C. to about 200° C. The dried impregnated support can then be impregnated with a second impregnation solution comprising at least one noble metal salt to form a catalyst precursor. The resulting catalyst precursor can then be dried at a temperature of about 80° C. to about 200° C. In some aspects, the method can further include sulfiding the catalyst precursor under effective sulfiding conditions to form a dewaxing catalyst. In some aspects, the catalyst precursor can be sulfided without prior calcining of the catalyst precursor.
In some aspects, the catalyst precursor can have a molar ratio of the least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, to the at least one Group 6 metal of about 0.1 to about 10. In some aspects, the catalyst precursor can have a molar ratio of the dispersion agent to the least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, of about 0.5 to about 10.
In still other aspects, a method for treating a distillate boiling range feed is provided. The method can include exposing a distillate boiling range feed to a dewaxing catalyst under effective hydroprocessing conditions, the dewaxing catalyst comprising at least one noble metal sulfide, at least one Group 6 metal sulfide, at least one Group 8-10 base metal sulfide, preferably at least one non-noble Group 8-10 base metal sulfide. The dewaxing catalyst can be formed, for example, by sulfiding a catalyst precursor according to the above aspects. In some aspects, the dewaxing catalyst can be formed by impregnating a support comprising a zeolitic framework structure with a first impregnation solution comprising at least one Group 6 metal salt, at least one Group 8-10 base metal salt, preferably at least one non-noble Group 8-10 base metal salt, and a dispersion agent to form a catalyst precursor. The dispersion agent can comprise a compound having 2-10 carbon atoms and/or a carbon atom to oxygen atom ratio of about 0.6 to about 2.0. The resulting impregnated support can then be dried at a temperature of about 80° C. to about 200° C. The dried impregnated support can then be impregnated with a second impregnation solution comprising at least one noble metal salt to form a catalyst precursor. The resulting catalyst precursor can then be dried at a temperature of about 80° C. to about 200° C. The dried catalyst precursor can then be sulfided under effective sulfiding conditions. In some aspects, the catalyst precursor can be sulfided without prior calcining of the catalyst precursor
In some aspects, the catalyst precursor can have a molar ratio of the least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, to the at least one Group 6 metal of about 0.1 to about 10. In some aspects, the catalyst precursor can have a molar ratio of the dispersion agent to the least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, of about 0.5 to about 10.
In some aspects, the effective hydroprocessing conditions comprise at least one of effective hydrotreating conditions and effective catalytic dewaxing conditions. In some aspects, the method can further comprise exposing the distillate boiling range feed to a hydrotreating catalyst.
Overview
In various aspects, methods, catalysts, and corresponding catalyst precursors are provided for performing dewaxing of diesel boiling range fractions. The dewaxing, such as trim dewaxing, can allow for production of diesel boiling range fuels with improved cold flow properties at desirable yields. The catalysts and/or catalyst precursors can correspond to supported base metal catalysts and/or catalyst precursors that include at least one noble metal, at least one Group 6 metal (corresponding to Column 6 of IUPAC periodic table) along with at least one Group 8-10 base metal (corresponding to Columns 8-10 of IUPAC periodic table), preferably a non-noble Group 8-10 base metal. The support can correspond to a zeolitic support (optionally including a separate binder), such as a support including a zeolitic framework structure having a 10-member ring pore channel as a largest pore channel. Examples of suitable zeolitic framework structures can include, but are not limited to, MEL (ZSM-11), MRE (ZSM-48), and MTT (ZSM-23). The catalysts can be formed, for example, by impregnating a support including a zeolitic framework structure with a first impregnation solution that also includes a dispersion agent and a second impregnation solution that includes at least one noble metal.
Introducing a dewaxing catalyst into a distillate hydrotreating environment can pose a variety of challenges. Conventional base metal dewaxing catalysts can have a reduced activity for heteroatom removal (e.g., sulfur, nitrogen) and/or reduced distillate selectivity, as compared to a hydrotreating catalyst. As a result, introducing a conventional dewaxing catalyst into an existing hydrotreatment reactor can require selection of less challenging feeds, a reduction in the amount of feed treated and distillate produced, and/or an increase in the required severity of the hydrotreatment reaction conditions. Alternatively, if a noble metal dewaxing catalyst is used as part of the catalyst bed in a hydrotreatment reactor, heteroatom removal is further reduced and dewaxing activity suppression can occur due to the presence of H2S and NH3 formed during hydrotreatment. This can require increasing the reactor temperature to a higher temperature to achieve desired cold flow properties and sulfur levels, leading to shorter run lengths and additional feed conversion and corresponding yield loss.
It has been unexpectedly discovered that the difficulties in replacing conventional hydrotreating catalyst with a dewaxing catalyst can be at least partially mitigated by using a supported noble metal- and base metal-containing dewaxing catalyst that includes a noble metal in addition to at least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, and at least one Group 6 metal as supported metals. Using a dewaxing catalyst with a supported noble metal, supported Group 8-10 base metal, preferably a supported non-noble Group 8-10 base metal, and supported Group 6 metal can reduce or minimize the difference in desulfurization and/or denitrogenation activity between a conventional base metal hydrotreating catalyst and a base metal dewaxing catalyst. Reducing or minimizing this difference in activity can, for example, allow for inclusion of dewaxing catalyst in a distillate hydrotreating environment while maintaining a more desirable feed space velocity for a given target heteroatom content in the hydrotreated effluent. Indeed, the use of a noble metal in addition to a non-noble Group 8-10 base metal and a Group 6 metal results in a dewaxing catalyst having an increased desulfurization and/or denitrogenation activity that is considered more than additive. Without being bound by any particular theory, it is believed that the presence of a noble metal in the catalyst creates an enhanced hydrogen spillover effect whereby the noble metal can split H2 molecules and increase hydrogen transfer during hydrotreating. Furthermore, this combination of a noble metal, a non-noble Group 8-10 base metal and a Group 6 metal results in a dewaxing catalyst having enhanced dewaxing activity even when used in the presence of a sulfur-containing feed. This enhanced dewaxing activity is unexpected because a person of ordinary skill in the art would expect poisoning of the noble metal to occur due to sulfur present in the feed thereby inhibiting dewaxing activity of the catalyst.
In various aspects, the noble metal and base metal dewaxing catalyst can be made using a dispersion agent during impregnation of the base metals onto the support to form a catalyst precursor. Without being bound by any particular theory, it is believed that the dispersion agent can increase dispersion of the base metals on the surface of the support and/or within the pore network of the zeolitic framework structure so that an increased number of active sites are available for reaction. Without being bound by any particular theory, it is believed that the dispersion agent can allow impregnated metals that are supported on a catalyst precursor to be present in a form where the metals are complexed by the dispersion agent. The complexed metals in the catalyst precursor can then be converted to metal sulfides, optionally without passing through an intermediate metal oxide state. This is in contrast to metals supported on a conventional catalyst, where the metals can typically be in oxide form prior to sulfidation.
In this discussion, the terms “catalyst” and “catalyst precursor” are both used. During formation of a dewaxing catalyst, a support can initially be formed that includes metals and a dispersion agent that are supported on the support. After drying, the metals and dispersion agent can remain supported on the support, with the metals being complexed by the dispersion agent. At this stage, the composition corresponds to/is defined as a “catalyst precursor” for purposes of the claims below. Prior to use for dewaxing (and/or other hydroprocessing), the catalyst precursor can be sulfided, which converts the metals to metal sulfides. The sulfiding process can also remove the dispersion agent from the support. After sulfidation, the composition corresponds to/is defined as a “catalyst” for purposes of the claims below. It is noted that to simplify the language used for describing synthesis of a catalyst, the term “catalyst” may be used informally to refer to compositional states prior to sulfidation, even though the “catalyst” corresponds to only the final sulfided composition.
Noble Metal Containing Dewaxing Catalyst and Methods of Making Said Catalyst
In various aspects, a dewaxing catalyst can be formed using a support comprising one or more zeolites. Examples of suitable zeolites include, but are not limited to, zeolitic framework structures having a 10-member ring pore channel as the largest pore size channel in the framework structure. Optionally, the largest pore size channel can be a 1-D channel, 2-D channel or a 3-D channel. Suitable framework structure types can include, but are not limited to, a) zeolites where the largest pore size channel has a pore size from about 4.8 Angstroms to about 6.0 Angstroms; b) zeolites where the largest pore size channel corresponds to a 10 member ring; c) zeolitic framework structures of framework type MRE, MEL, MTT, EUO, AEL, AFO, SFF, STF, or TON; d) zeolites having the zeolite structure corresponding to ZSM-11 and/or having the disordered zeolite structure corresponding to ZSM-48; or e) combinations thereof.
In various aspects, the zeolitic framework structure can comprise an MEL framework structure, the zeolitic framework structure further comprising a) a molar ratio of silica to alumina of about 35 to about 55; b) an alpha value of at least about 380; c) a total surface area of at least about 350 m2/g, or d) a combination thereof.
In this discussion and the claims below, a zeolite is defined to refer to a crystalline material having a porous framework structure built from tetrahedra atoms connected by bridging oxygen atoms. Examples of known zeolite frameworks are given in the “Atlas of Zeolite Frameworks” published on behalf of the Structure Commission of the International Zeolite Association”, 6th revised edition, Ch. Baerlocher, L. B. McCusker, D. H. Olson, eds., Elsevier, New York (2007) and the corresponding web site, http://www.iza-structure.org/databases/. Under this definition, a zeolite can refer to aluminosilicates having a zeolitic framework type as well as crystalline structures containing oxides of heteroatoms different from silicon and aluminum. Such heteroatoms can include any heteroatom generally known to be suitable for inclusion in a zeolitic framework, such as gallium, boron, germanium, phosphorus, zinc, antimony, tin, and/or other transition metals that can substitute for silicon and/or aluminum in a zeolitic framework.
Catalysts can be self-bound and/or can be optionally bound with a separate binder or matrix material prior to use. Binders can be resistant to temperatures of the use desired and are attrition resistant. Binders may be catalytically active or inactive and include other zeolites, other inorganic materials such as clays and metal oxides such as alumina, silica, silica-alumina, titania and zirconia. Clays may be kaolin, bentonite and montmorillonite and are commercially available. They may be blended with other materials such as silicates. Other binary porous matrix materials in addition to silica-aluminas include materials such as silica-magnesia, silica-thoria, silica-zirconia, silica-beryllia and silica-titania. Ternary materials such as silica-alumina-magnesia, silica-alumina-thoria and silica-alumina-zirconia can also be suitable for use as binders. The matrix can be in the form of a co-gel. In some aspects, dewaxing catalysts can be formulated using a low surface area binder, a low surface area binder represents a binder with a surface area of about 150 m2/g or less, or about 130 m2/g or less, or about 100 m2/g or less, or about 80 m2/g or less, or about 70 m2/g or less.
The amount of zeolite in a support including a binder can be from about 30 wt % zeolite to about 100 wt % zeolite relative to the combined weight of binder and zeolite. For example, the amount of zeolite can be about 30 wt % to about 100 wt %, or about 30 wt % to about 90 wt %, or about 30 wt % to about 80 wt %, or about 30 wt % to about 70 wt %, or about 50 wt % to about 100 wt %, or about 50 wt % to about 90 wt %, or about 50 wt % to about 80 wt %, or about 50 wt % to about 70 wt %, or about 60 wt % to about 90 wt %, or about 60 wt % to about 80 wt %, or about 60 wt % to about 70 wt %.
After combining a zeolite with any optional binder, the zeolite can be extruded to form support particles. Alternatively, support particles may be formed by any other convenient method. After forming support particles, the support particles can be impregnated with the base metal salts using an impregnation solution that also includes a dispersion agent.
Impregnation, such as impregnation by incipient wetness or ion exchange in solution, is a commonly used technique for introducing metals into a catalyst that includes a support. During impregnation, a support is exposed to a solution containing a salt of the metal for impregnation. There are many variables that can affect the dispersion of the metal salt during impregnation, including the concentration of the salt, the pH of the salt solution, the point of zero charge of the support material, but not excluding other variables that may also be important during incipient wetness or ion exchange impregnation. Multiple exposure steps can optionally be performed to achieve a desired metals loading on a catalyst. After impregnating a support with a metal salt, the support can be dried to remove excess water. The drying can be performed under any convenient atmosphere, such as air, at a temperature from about 80° C. to about 200° C. Optionally but preferably, the catalyst is not calcined prior to sulfidation.
In various aspects, a catalyst/catalyst precursor can include at least one noble metal and at least one base metal from Group 8-10 (Columns 8-10 of IUPAC periodic table; also known as a Group VIII metal) as hydrogenation or catalytic metals. Examples of suitable noble metals include Pt, Pd, Rh, Ir, Ru, Os, Ag, Au and combinations thereof. Examples of suitable Group 8-10 base metals include noble and non-noble metals. Preferably, the Group 8-10 base metal may be a non-noble metal, such as Co, Ni, Fe and combinations thereof. Preferably, the at least one noble metal can be Pt, Ru, Os, Rh, Ir and combinations thereof, and the at least one Group 8-10 base metal can be Ni and/or Co. A catalyst/catalyst precursor can further include at least one Group 6 metal (Column 6 of IUPAC periodic table; also known as a Group VI metal) as a hydrogenation metal, preferably Mo and/or W. In some optional aspects, other metal salts for impregnation as hydrogenation or catalytic metals can generally correspond to salts of metals from Groups 6-12 (Columns 6-12 IUPAC periodic table), preferably additional salts of metals from Group 6 and 8-10.
After drying of the impregnated support (which corresponds to a catalyst precursor), the amount of hydrogenation metals (e.g., Group 6 metal and/or non-noble Group 8-10 base metal) on the support may range from about 1.0 wt % to about 30 wt %, based on weight of the catalyst precursor. For example, the amount of hydrogenation metals (e.g., Group 6 metal and/or non-noble Group 8-10 base metal) can be about 1.0 wt % to about 30 wt %, or about 1.0 wt % to about 25 wt %, or about 1.0 wt % to about 20 wt %, or about 1.0 wt % to about 15 wt %, or about 1.0 wt % to about 12 wt %, or about 3.0 wt % to about 30 wt %, or about 3.0 wt % to about 25 wt %, or about 3.0 wt % to about 20 wt %, or about 3.0 wt % to about 15 wt %, or about 3.0 wt % to about 12 wt %, or about 5.0 wt % to about 30 wt %, or about 5.0 wt % to about 25 wt %, or about 5.0 wt % to about 20 wt %, or about 5.0 wt % to about 15 wt %, or about 5.0 wt % to about 12 wt %, or about 10 wt % to about 30 wt %, or about 10 wt % to about 25 wt %, or about 10 wt % to about 20 wt %, or about 10 wt % to about 15 wt %. In particular, the amount of hydrogenation metals (e.g., Group 6 metal and/or non-noble Group 8-10 base metal) can be about 1.0 wt % to 30 wt %, or about 5.0 wt % to about 30 wt %, or about 5 wt % to about 20 wt %, or about 10 wt % to about 25 wt %. Suitable metal salts can include typical salts used for aqueous impregnation of support particles for catalysts. In particular embodiments, the amount of Group 6 metal on the support may range from about 1.0 wt % to about 30 wt %, based on weight of the catalyst precursor, for example, about 1.0 wt % to about 25 wt %, or about 1.0 wt % to about 20 wt %, or about 1.0 wt % to about 15 wt %, or about 3.0 wt % to about 30 wt %, or about 3.0 wt % to about 25 wt %, or about 3.0 wt % to about 20 wt %, or about 3.0 wt % to about 15 wt %, or about 5.0 wt % to about 30 wt %, or about 5.0 wt % to about 25 wt %, or about 5.0 wt % to about 20 wt %, or about 5.0 wt % to about 15 wt %. In other particular embodiments, the amount of non-noble Group 8-10 metal on the support may range from about 1.0 wt % to about 20 wt %, based on weight of the catalyst precursor, for example, about 1.0 wt % to about 15 wt %, or about 1.0 wt % to about 10 wt %, or about 1.0 wt % to about 5.0 wt %, or about 2.0 wt % to about 20 wt %, or about 2.0 wt % to about 15 wt %, or about 2.0 wt % to about 10 wt %, or about 2.0 wt % to about 5.0 wt %.
Additionally or alternatively, the catalyst precursor may advantageously include a lower amount of noble metal (e.g., Pt, Ru, Os, Rh, Ir), for example, less than about 5.0 wt %, or less than about 2.0 wt %, or less than about 1.0 wt %, or less than about 0.50 wt %, or less than about 0.20 wt %, or less than about 0.050 wt % based on a weight of the catalyst precursor. In other aspects, the catalyst precursor may include a noble metal (e.g., Pt, Ru, Os, Rh, Ir) in amount of about 0.010 wt % to about 5.0 wt %, or about 0.010 wt % to about 2.0 wt %, or about 0.010 wt % to about 1.0 wt %, or about 0.010 wt % to about 0.50 wt %, or about 0.010 wt % to about 0.20 wt %, or about 0.010 wt % to about 0.050 wt %, or about 0.050 wt % to about 5.0 wt %, or about 0.050 wt % to about 2.0 wt %, or about 0.050 wt % to about 1.0 wt %, or about 0.050 wt % to about 0.50 wt %, or about 0.050 wt % to about 0.20 wt. In further aspects, the amount of at least one Group 6 metal (e.g., Mo and/or W) and at least one Group 8-10 base metal (e.g., Ni and/or Co) based on a weight of the catalyst precursor can be about 1.0 wt % to about 30 wt %, or about 1.0 wt % to about 25 wt %, or about 1.0 wt % to about 20 wt %, or about 1.0 wt % to about 15 wt %, or about 1.0 wt % to about 12 wt %, or about 3.0 wt % to about 30 wt %, or about 3.0 wt % to about 25 wt %, or about 3.0 wt % to about 20 wt %, or about 3.0 wt % to about 15 wt %, or about 3.0 wt % to about 12 wt %, or about 5.0 wt % to about 30 wt %, or about 5.0 wt % to about 25 wt %, or about 5.0 wt % to about 20 wt %, or about 5.0 wt % to about 15 wt %, or about 5.0 wt % to about 12 wt %, or about 10 wt % to about 30 wt %, or about 10 wt % to about 25 wt %, or about 10 wt % to about 20 wt %, or about 10 wt % to about 15 wt %. In particular, the amount of hydrogenation metals can be about 1.0 wt % to 30 wt %, or about 5.0 wt % to about 30 wt %, or about 5 wt % to about 20 wt %, or about 10 wt % to about 25 wt %.
In aspects where at least one Group 6 metal is also included on the catalyst/catalyst precursor, the molar ratio of the at least one non-noble Group 8-10 base metal to the at least one Group 6 metal can be from about 0.1 to about 10, or about 0.1 to about 8.0, or about 0.1 to about 6.0, or about 0.1 to about 4.0, or about 0.1 to about 2.0, or about 0.1 to about 1.0, or about 0.1 to about 0.6, or about 0.2 to about 10, or about 0.2 to about 8.0, or about 0.2 to about 6.0, or about 0.2 to about 4.0, or about 0.2 to about 2.0, or about 0.2 to about 1.0, or about 0.2 to about 0.6. For example, if Ni is the non-noble Group 8-10 base metal and Mo is the Group 6 metal, the molar ratio of Ni to Mo can be from about 0.1 to about 10, or about 0.1 to about 6.0, about 0.1 to 2.0, or about 0.1 to about 1.0, or about 0.2 to about 1.0, or about 0.2 to about 0.6. Without being bound by any particular theory, the molar ratio of the base metals can be selected so that during hydroprocessing using the catalyst, a substantial amount of heteroatom removal occurs via both a hydrogenation mechanism (as can be catalyzed by Ni) and a hydrogenolysis mechanism (as can be catalyzed by Co).
In addition to water soluble metal salts, the impregnation solution can also include one or more dispersion agents. A dispersion agent can be an organic compound comprising 2 to 10 carbons and having a ratio of carbon atoms to oxygen atoms of about 2 to about 0.6. Optionally, the dispersion agent can be a carboxylic acid. Examples of suitable dispersion agents include glycols (e.g., ethylene glycol) and carboxylic acids, such as citric acid and gluconic acid. Optionally, the dispersion agent can be an amine or other nitrogen-containing compound, such as nitrilotriacetic acid. Without being bound by any particular theory, it is believed that the dispersion agent can be removed from the catalyst precursor/catalyst during heating, calcination, and/or sulfidation steps that are performed after impregnation to form metal oxides and/or metal sulfides. In aspects where only drying of a catalyst precursor is performed prior to sulfidation, the metals on the catalyst precursor can be converted from metals complexed by the dispersion agent to metal sulfides during sulfidation without necessarily forming an intermediate metal oxide. It is believed that the dispersion agent can assist with modifying the distribution of metals across the catalyst support, which can facilitate the improved heteroatom removal activity described herein. In some aspects, the complex formed between the dispersion agent and the metal can correspond to a complex between an anion formed from the dispersion agent (such as by loss of an acidic proton) and a metal cation. References herein to a molar ratio of dispersion agent to metal are defined to include aspects where the dispersion agent is in the form of an anion derived from the dispersion agent.
In some aspects, the molar ratio of dispersion agent to total metals in the catalyst precursor can be about 0.1 to 10.0, or about 0.1 to 5.0, or about 0.1 to 7.0, or about 0.1 to 5.0, or about 0.1 to 4.0, or about 0.1 to 2.0, or about 0.1 to 1.0, or about 0.2 to 10, or about 0.2 to 7.0, or about 0.2 to 5.0, or about 0.2 to 4.0, or about 0.2 to 2.0, or about 0.2 to 1.0, or about 0.3 to 10, or about 0.3 to about 7.0, or about 0.3 to 5.0, or about 0.3 to 4.0, or about 0.3 to 2.0, or about 0.3 to 1.0, or about 0.4 to 10, or about 0.4 to 7.0, or about 0.4 to 5.0, or about 0.4 to 4.0, or about 0.4 to 2.0, or about 0.4 to 1.0. Additionally or alternately, the molar ratio of dispersion agent to total non-noble Group 8-10 metals in the catalyst precursor can be about 0.5 to 10, or about 0.5 to 5.0, or about 0.5 to 5.0, or about 0.5 to 4.0, or about 0.5 to 3.0, or about 1.0 to 10, or about 1.0 to 7.0, or about 1.0 to 5.0, or about 1.0 to 4.0, or about 1.0 to 3.0.
After impregnating a support to form a catalyst precursor, the catalyst precursor can be at least partially dried, such as by drying at a temperature of about 80° C. to about 200° C. Under these conditions, the dispersion agent can remain on the catalyst precursor, so that hydrogenation metals that are complexed by the dispersion agent can remain in a complexed form. Optionally, a portion of the hydrogenation metals on the catalyst precursor can be in an oxide form. In some aspects, a ratio of hydrogenation metals on the catalyst precursor in oxide form to hydrogenation metals on the catalyst precursor that are complexed by the dispersion agent can be 0.2 or less, or 0.1 or less, such as down to having substantially no supported metals in oxide form.
In various aspects, a catalyst precursor can be formed by impregnating a support with one or more impregnations solutions. For example, a catalyst precursor can be formed by impregnating a support as described herein, e.g., comprising a zeolitic framework structure, with a first impregnation solution comprising at least one Group 6 metal salt (e.g., a W salt), at least one Group 8-10 base metal salt, preferably at least one non-noble Group 8-10 base metal salt (e.g., Ni salt and/or Co salt), and a dispersion agent to form an impregnated support. The dispersion agent can comprise a compound having 2-10 carbon atoms and a carbon atom to oxygen atom ratio of about 0.6 to about 2.0. The impregnated support can be dried at a temperature of about 80° C. to about 200° C. Then the dried impregnated support can be impregnated with a second impregnation solution comprising at least one noble metal salt (e.g., a Pt salt, a Ru salt, an Os salt, a Rh salt, an Ir salt) to form a catalyst precursor as described herein. The catalyst precursor can be dried at a temperature of about 80° C. to about 200° C.
The catalyst precursor can correspond to a catalyst support as described herein with impregnated metals that are complexed by a dispersion agent as described herein. The amount of dispersion agent in the impregnation solution can be selected based on the amount of metal in the solution. In some aspects, the molar ratio of dispersion agent to total metals in the solution can be about 0.1 to 10.0, or about 0.1 to 5.0, or about 0.1 to 7.0, or about 0.1 to 5.0, or about 0.1 to 4.0, or about 0.1 to 2.0, or about 0.1 to 1.0, or about 0.2 to 10, or about 0.2 to 7.0, or about 0.2 to 5.0, or about 0.2 to 4.0, or about 0.2 to 2.0, or about 0.2 to 1.0, or about 0.3 to 10, or about 0.3 to about 7.0, or about 0.3 to 5.0, or about 0.3 to 4.0, or about 0.3 to 2.0, or about 0.3 to 1.0, or about 0.4 to 10, or about 0.4 to 7.0, or about 0.4 to 5.0, or about 0.4 to 4.0, or about 0.4 to 2.0, or about 0.4 to 1.0. Additionally or alternately, the molar ratio of dispersion agent to total non-noble Group 8-10 metals in the solution can be about 0.5 to 10, or about 0.5 to 5.0, or about 0.5 to 5.0, or about 0.5 to 4.0, or about 0.5 to 3.0, or about 1.0 to 10, or about 1.0 to 7.0, or about 1.0 to 5.0, or about 1.0 to 4.0, or about 1.0 to 3.0.
After forming a catalyst precursor with supported noble and base metals, the noble and base metals may be sulfided prior to use to form a sulfided metal catalyst. The sulfidation of the metals can be performed by any convenient method, such as gas phase sulfidation or liquid phase sulfidation. Sulfidation is generally carried out by contacting a catalyst precursor (such as a catalyst precursor that includes metals complexed by a dispersion agent and/or metals in the form of metal oxides) with a sulfur containing compound, such as elemental sulfur, hydrogen sulfide or polysulfides. Hydrogen sulfide is a convenient sulfidation agent for gas phase sulfidation, and can be incorporated into a gas phase sulfidation atmosphere containing hydrogen in an amount of about 0.1 wt % to 10 wt %. Sulfidation can also be carried out in the liquid phase utilizing a combination of a polysulfide, such as a dimethyl disulfide spiked hydrocarbon stream, and hydrogen. The sulfidation can be performed at a convenient sulfidation temperature, such as a temperature from 150° C. to 500° C. The sulfidation can be performed at a convenient sulfidation pressure, such as a pressure of 100 psig to 1000 psig or more. The sulfidation time can vary depending on the sulfidation conditions, so that sulfidation times of 1 hour to 72 hours can be suitable. The resulting catalyst may also be steamed prior to use. In various aspects, the catalyst precursor can be sulfide without prior calcining of the catalyst precursor.
Processing Using Noble Metal Containing Dewaxing Catalyst—Feedstock
The noble metal containing dewaxing catalyst described herein can be used for dewaxing of various feeds, such as diesel boiling range feeds, distillate boiling range feeds, and/or lubricant boiling range feeds. One way of defining a feedstock is based on the boiling range of the feed. One option for defining a boiling range is to use an initial boiling point for a feed and/or a final boiling point for a feed. Another option, which in some instances may provide a more representative description of a feed, is to characterize a feed based on the amount of the feed that boils at one or more temperatures. For example, a “T5” boiling point for a feed is defined as the temperature at which 5 wt % of the feed will boil off. Similarly, a “T95” boiling point is a temperature at 95 wt % of the feed will boil. A suitable ASTM method can be used for characterization of boiling points (including fractional boiling points), such as ASTM D2887.
As defined herein, a diesel boiling range feed can have a boiling range based on a T5 distillation point and/or a T10 distillation point, and a T95 distillation point and/or a T90 distillation point. In various aspects, a diesel boiling range feed or fraction is defined as a feed or fraction with a T5 distillation point of at least 177° C. and a T95 distillation point of 371° C. or less, or a T5 distillation point of at least 177° C. and a T90 distillation point of 371° C. or less, or a T10 distillation point of at least 177° C. and a T95 distillation point of 371° C. or less, or a T10 distillation point of at least 177° C. and a T90 distillation point of 371° C. or less. Additionally or alternately, a diesel boiling range fraction within a feed can be defined as the portion of a feed having a boiling range from 177° C. (as an initial boiling point) to 371° C. (as a final boiling point). As defined herein, a lubricant boiling range feed can having a boiling range based on a T5 distillation point and/or a T10 distillation point, and a T95 distillation point and/or a T90 distillation point. In various aspects, a lubricant boiling range feed or fraction is defined as a feed or fraction with a T5 distillation point of at least 371° C. and a T95 distillation point of 510° C. or less, or a T5 distillation point of at least 371° C. and a T90 distillation point of 510° C. or less, or a T10 distillation point of at least 371° C. and a T95 distillation point of 510° C. or less, or a T10 distillation point of at least 371° C. and a T90 distillation point of 510° C. or less. Additionally or alternately, a lubricant boiling range fraction within a feed can be defined as the portion of a feed having a boiling range from 371° C. (as an initial boiling point) to 510° C. (as a final boiling point). As defined herein, a distillate boiling range can be defined that represents a combination of the diesel and lubricant boiling ranges. Thus, a distillate boiling range feed can be defined as a feed or fraction with a T5 distillation point of at least 177° C. and a T95 distillation point of 510° C. or less, or a T5 distillation point of at least 177° C. and a T90 distillation point of 510° C. or less, or a T10 distillation point of at least 177° C. and a T95 distillation point of 510° C. or less, or a T10 distillation point of at least 177° C. and a T90 distillation point of 510° C. or less. Additionally or alternately, a distillate boiling range fraction within a feed can be defined as the portion of a feed having a boiling range from 177° C. (as an initial boiling point) to 510° C. (as a final boiling point).
A wide range of petroleum and chemical feedstocks can be hydroprocessed in reaction systems that include a dewaxing catalyst formed using a plurality of structure directing agents. Suitable feedstocks include whole and reduced petroleum crudes, atmospheric and vacuum residua, propane deasphalted residua, e.g., brightstock, cycle oils, FCC tower bottoms, gas oils, including vacuum gas oils and coker gas oils, light to heavy distillates including raw virgin distillates, hydrocrackates, hydrotreated oils, slack waxes, Fischer-Tropsch waxes, raffinates, and mixtures of these materials.
In embodiments involving an initial sulfur removal stage prior to hydrocracking, the sulfur content of the feed can be at least 300 ppm by weight of sulfur, or at least 1000 wppm, or at least 2000 wppm, or at least 4000 wppm, or at least 10,000 wppm, or at least 20,000 wppm. In other embodiments, including some embodiments where a previously hydrotreated and/or hydrocracked feed is used, the sulfur content can be 2000 wppm or less, or 1000 wppm or less, or 500 wppm or less, or 100 wppm or less.
In some aspects, a dewaxing catalyst as described herein including at least one noble metal, at least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, and at least one Group 6 metal can be used to provide an improved amount of hydrotreating activity (desulfurization activity and/or denitrogenation activity) when exposed to a diesel and/or lubricant boiling range feed under effective dewaxing conditions and/or effective hydrotreating conditions. The dewaxing catalyst including at least one noble metal, at least one Group 8-10 base metal, preferably least one non-noble Group 8-10 base metal, and at least one Group 6 metal can further provide a comparable level of cloud point reduction under such conditions. Effective conditions for catalytic dewaxing and hydrotreating are described in greater detail below. Optionally, additional benefit in hydrotreating activity can be obtained when the dewaxing catalyst comprises a low surface area binder, such as a low surface area alumina binder. Optionally, additional benefit in hydrotreating activity can be obtained by performing dewaxing and/or hydrotreatment at higher temperatures, such as at least about 680° F. (360° C.), or at least about 700° F. (371° C.), or at least about 716° F. (380° C.). In combination with typical end of run temperatures, the additional benefit in cloud point reduction can be achieved for dewaxing temperatures of about 340° C. to about 450° C., or about 360° C. to about 450° C., or about 360° C. to about 425° C., or about 370° C. to about 450° C., or about 370° C. to about 425° C., or about 380° C. to about 450° C., or about 380° C. to about 425° C.
For reaction system configurations where a diesel boiling range product is produced based in part on exposure of a feed to a base metal dewaxing catalyst, the diesel boiling range product can have a cloud point of about −10° C. or less, or about −20° C. or less, or about −30° C. or less, or about −40° C. or less. Additionally or alternately, the diesel boiling range product can have a sulfur content of about 100 wppm of sulfur or less, or about 50 wppm or less, or about 25 wppm or less, or about 15 wppm or less. Additionally or alternately, the diesel boiling range product can have a nitrogen content of about 100 wppm of nitrogen or less, or about 50 wppm or less, or about 25 wppm or less, or about 15 wppm or less.
Examples of Reaction Systems for Hydroprocessing
In the discussion herein, a stage can correspond to a single reactor or a plurality of reactors. Optionally, multiple parallel reactors can be used to perform one or more of the processes, or multiple parallel reactors can be used for all processes in a stage. Each stage and/or reactor can include one or more catalyst beds containing hydroprocessing catalyst. Note that a “bed” of catalyst in the discussion below can refer to a partial physical catalyst bed. For example, a catalyst bed within a reactor could be filled partially with a hydrocracking catalyst and partially with a dewaxing catalyst as described herein. For convenience in description, even though the two catalysts may be stacked together in a single catalyst bed, the hydrocracking catalyst and dewaxing catalyst as described herein can each be referred to conceptually as separate catalyst beds.
In the discussion herein, reference will be made to a hydroprocessing reaction system. The hydroprocessing reaction system corresponds to the one or more stages, such as two stages and/or reactors and an optional intermediate separator, that are used to expose a feed to a plurality of catalysts under hydroprocessing conditions. The plurality of catalysts can be distributed between the stages and/or reactors in any convenient manner, with some preferred methods of arranging the catalyst described herein.
Various types of hydroprocessing can be used in the production of distillate fuels and/or lubricant base oils. In some aspects, diesel boiling range fuel products can be formed by exposing a diesel and/or distillate boiling range feed to hydrotreating catalyst and a dewaxing catalyst as described herein under effective hydrotreating conditions. Optionally, the hydrotreating catalyst and the dewaxing catalyst can be located in the same reactor. Optionally, the hydrotreating catalyst and the dewaxing catalyst as described herein can be located within the same catalyst bed in a reactor. Optionally, the effluent (or at least a portion thereof) from exposing the feed to the hydrotreating catalyst and the dewaxing catalyst as described herein can be exposed to an aromatic saturation catalyst. This type of configuration can allow for production of a diesel boiling range product with reduced sulfur content, reduced nitrogen content, and/or improved cold flow properties.
In other aspects, diesel boiling range fuel products can be formed by exposing a diesel and/or distillate boiling range feed to hydrotreating catalyst under effective hydrotreating conditions and a dewaxing catalyst as described herein under effective dewaxing conditions. Optionally, the hydrotreating catalyst and the dewaxing catalyst as described herein can be located in the same reactor. Optionally, the effluent (or at least a portion thereof) from exposing the feed to the hydrotreating catalyst and the dewaxing catalyst as described herein can be exposed to an aromatic saturation catalyst. This type of configuration can allow for production of a diesel boiling range product with reduced sulfur content, reduced nitrogen content, and/or improved cold flow properties.
In still other aspects, diesel boiling range products and lubricant boiling range products can be formed by exposing a lubricant and/or distillate boiling range feed to hydrotreating catalyst under effective hydrotreating conditions; hydrocracking catalyst under effective hydrocracking conditions; and a dewaxing catalyst as described herein under effective dewaxing conditions. Optionally, a separation can be performed on hydrotreated effluent and/or hydrocracked effluent prior to at least one additional stage of hydrotreatment and/or hydrocracking. This separation can correspond to a separation to remove light ends (C4−), or this separation can also allow for separation of any fuels boiling range material formed during the exposure to the hydrotreating and/or hydrocracking catalyst(s). Optionally, a separation can be performed on hydrotreated effluent and/or hydrocracked effluent prior to at least one stage of catalytic dewaxing. This separation can correspond to a separation to remove light ends (C4−), or this separation can also allow for separation of any fuels boiling range material formed during the exposure to the hydrotreating and/or hydrocracking catalyst(s). Optionally, the effluent (or at least a portion thereof) from exposing the feed to the dewaxing catalyst as described herein can be exposed to an aromatic saturation catalyst. This type of configuration can allow for production of diesel boiling range product and/or lubricant boiling range product with reduced sulfur content, reduced nitrogen content, and/or improved cold flow properties.
After passing through separator 120, the remaining portion 125 of the effluent can be passed into a second reactor (or reactors) 130. In the example shown in
In some alternative aspects, a reaction system for fuels production can include fewer reactors and/or stages than the system shown in
Hydrotreatment Conditions
Hydrotreatment can typically be used to reduce the sulfur, nitrogen, and aromatic content of a feed. The catalysts used for hydrotreatment can include conventional hydroprocessing catalysts, for example those that comprise at least one non-noble Group 8-10 metal (Columns 8-10 of IUPAC periodic table), such as Fe, Co, and/or Ni, optionally Co and/or Ni; and at least one Group 6 metal (Column 6 of IUPAC periodic table), such as Mo and/or W. Such hydroprocessing catalysts optionally include transition metal sulfides that are impregnated or dispersed on a refractory support or carrier such as alumina and/or silica. The support or carrier itself typically has no significant/measurable catalytic activity. Substantially carrier- or support-free catalysts, commonly referred to as bulk catalysts, generally have higher volumetric activities than their supported counterparts.
The conventional hydrotreating catalysts can either be in bulk form or in supported form. In addition to alumina and/or silica, other suitable support/carrier materials can include, but are not limited to, zeolites, titania, silica-titania, and titania-alumina. Suitable aluminas are porous aluminas such as gamma or eta having average pore sizes from 50 to 200 Å, or 75 to 150 Å; a surface area from 100 to 300 m2/g, or 150 to 250 m2/g; and a pore volume of from 0.25 to 1.0 cm3/g, or 0.35 to 0.8 cm3/g. More generally, any convenient size, shape, and/or pore size distribution for a catalyst suitable for hydrotreatment of a distillate (including lubricant base oil) boiling range feed in a conventional manner may be used. It is noted that more than one type of hydroprocessing catalyst can be used in one or multiple reaction vessels.
In the hydrotreating catalysts, the at least one non-noble Group 8-10 metal, in oxide form, can be present in an amount ranging from 2 wt % to 40 wt %, or from 4 wt % to 15 wt %. The at least one Group 6 metal, in oxide form, can be present in an amount ranging from 2 wt % to 70 wt %, or for supported catalysts from 6 wt % to 40 wt % or from 10 wt % to 30 wt %. These weight percents are based on the total weight of the catalyst. Suitable metal catalysts can include cobalt/molybdenum (1-10% Co as oxide, 10-40% Mo as oxide), nickel/molybdenum (1-10% Ni as oxide, 10-40% Co as oxide), or nickel/tungsten (1-10% Ni as oxide, 10-40% W as oxide) on alumina, silica, silica-alumina, or titania.
The hydrotreatment is carried out in the presence of hydrogen. A hydrogen stream is, therefore, fed or injected into a vessel or reaction zone or hydroprocessing zone in which the hydroprocessing catalyst is located. Hydrogen, which is contained in a hydrogen “treat gas,” is provided to the reaction zone. Treat gas can be either pure hydrogen or a hydrogen-containing gas, which is a gas stream containing hydrogen in an amount that is sufficient for the intended reaction(s), optionally including one or more other gasses (e.g., nitrogen and light hydrocarbons such as methane), and which will not adversely interfere with or affect either the reactions or the products. Impurities, such as H2S and NH3 are undesirable and would typically be removed from the treat gas before it is conducted to the reactor. In aspects where the treat gas stream introduced into a reaction stage contains components other than hydrogen, the treat gas can contain at least 50 vol. %, or at least 75 vol. % hydrogen, or at least 90 vol % hydrogen, or at least 95 vol % hydrogen, or at least 99 vol % hydrogen.
Hydrotreating conditions can include temperatures of 200° C. to 450° C., or 315° C. to 425° C.; pressures of 250 psig (1.8 MPag) to 5000 psig (34.6 MPag) or 300 psig (2.1 MPag) to 3000 psig (20.7 MPag); and liquid hourly space velocities (LHSV) of 0.1 hr−1 to 10 hr−1; and hydrogen treat rates of 100 scf/B (17.8 m3/m3) to 10,000 scf/B (1781 m3/m3), or 500 (89 m3/m3) to 10,000 scf/B (1781 m3/m3). Hydrogen can be supplied co-currently with the input feed to the hydrotreatment reactor and/or reaction zone or separately (and optionally counter-current) via a separate gas conduit to the hydrotreatment zone.
Hydrocracking Conditions
In various aspects, the reaction conditions in the reaction system can be selected to generate a desired level of conversion of a feed. Conversion of the feed can be defined in terms of conversion of molecules that boil above a temperature threshold to molecules below that threshold. The conversion temperature can be any convenient temperature, such as 700° F. (371° C.). In an aspect, the amount of conversion in the stage(s) of the reaction system can be selected to enhance diesel production while achieving a substantial overall yield of fuels. The amount of conversion can correspond to the total conversion of molecules within any stage of the fuels hydrocracker or other reaction system that is used to hydroprocess the lower boiling portion of the feed from the vacuum distillation unit. Suitable amounts of conversion of molecules boiling above 700° F. to molecules boiling below 700° F. include converting at least 25% of the 700° F.+ portion of the feedstock to the stage(s) of the reaction system, or at least 40% of the 700° F.+ portion, or at least 50%, or at least 60%, or at least 70%, or at least 75%. Additionally or alternately, the amount of conversion for the reaction system can be 85% or less, or 80% or less, or 75% or less, or 70% or less, or 60% or less, or 50% or less. Each of the above lower bounds on the amount of conversion is explicitly contemplated in conjunction with each of the above upper bounds. Still larger amounts of conversion may also produce a suitable hydrocracker bottoms for forming lubricant base oils, but such higher conversion amounts will also result in a reduced yield of lubricant base oils. Reducing the amount of conversion can increase the yield of lubricant base oils, but reducing the amount of conversion to below the ranges noted above may result in hydrocracker bottoms that are not suitable for formation of Group II, Group II+, or Group III lubricant base oils.
In order to achieve a desired level of conversion, a reaction system can include at least one hydrocracking catalyst. Hydrocracking catalysts typically contain sulfided base metals on acidic supports, such as amorphous silica alumina, cracking zeolites such as USY, or acidified alumina. Often these acidic supports are mixed or bound with other metal oxides such as alumina, titania or silica. Examples of suitable acidic supports include acidic molecular sieves, such as zeolites or silicoaluminophophates. One example of suitable zeolite is USY, such as a USY zeolite with cell size of 24.25 Angstroms or less. Additionally or alternately, the catalyst can be a low acidity molecular sieve, such as a USY zeolite with a Si to Al ratio of at least 20, and preferably at least 40 or 50. Zeolite Beta is another example of a potentially suitable hydrocracking catalyst. Non-limiting examples of metals for hydrocracking catalysts include metals or combinations of metals that include at least one Group 8-10 metal (Columns 8-10 on the IUPAC periodic table), such as nickel, nickel-cobalt-molybdenum, cobalt-molybdenum, nickel-tungsten, nickel-molybdenum, and/or nickel-molybdenum-tungsten. Additionally or alternately, hydrocracking catalysts with noble metals can also be used. Non-limiting examples of noble metal catalysts include those based on platinum and/or palladium. Support materials which may be used for both the noble and non-noble metal catalysts can comprise a refractory oxide material such as alumina, silica, alumina-silica, kieselguhr, diatomaceous earth, magnesia, zirconia, or combinations thereof, with alumina, silica, alumina-silica being the most common (and preferred, in one embodiment).
In various aspects, the conditions selected for hydrocracking for fuels production and/or lubricant base stock production can depend on the desired level of conversion, the level of contaminants in the input feed to a hydrocracking stage, and potentially other factors. For example, hydrocracking conditions in a first stage (such as a sour stage) and/or a second stage (such as a sweet stage) can be selected to achieve a desired level of conversion in the reaction system. A hydrocracking process in the first stage (or otherwise under sour conditions) can be carried out at temperatures of 550° F. (288° C.) to 840° F. (449° C.), hydrogen partial pressures of from 250 psig to 5000 psig (1.8 MPag to 34.6 MPag), liquid hourly space velocities of from 0.05 h−1 to 10 and hydrogen treat gas rates of from 35.6 m3/m3 to 1781 m3/m3 (200 SCF/B to 10,000 SCF/B). In other embodiments, the conditions can include temperatures in the range of 600° F. (343° C.) to 815° F. (435° C.), hydrogen partial pressures of from 500 psig to 3000 psig (3.5 MPag-20.9 MPag), and hydrogen treat gas rates of from 213 m3/m3 to 1068 m3/m3 (1200 SCF/B to 6000 SCF/B). The LHSV relative to only the hydrocracking catalyst can be from 0.25 h−1 to 50 h−1, such as from 0.5 to 20 h−1, and preferably from 1.0 to 4.0 h−1.
In some aspects, a portion of the hydrocracking catalyst can be contained in a second reactor stage. In such aspects, a first reaction stage of the hydroprocessing reaction system can include one or more hydrotreating and/or hydrocracking catalysts. The conditions in the first reaction stage can be suitable for reducing the sulfur and/or nitrogen content of the feedstock. A separator can then be used in between the first and second stages of the reaction system to remove gas phase sulfur and nitrogen contaminants. One option for the separator is to simply perform a gas-liquid separation to remove contaminant. Another option is to use a separator such as a flash separator that can perform a separation at a higher temperature. Such a high temperature separator can be used, for example, to separate the feed into a portion boiling below a temperature cut point, such as 350° F. (177° C.) or 400° F. (204° C.), and a portion boiling above the temperature cut point. In this type of separation, the naphtha boiling range portion of the effluent from the first reaction stage can also be removed, thus reducing the volume of effluent that is processed in the second or other subsequent stages. Of course, any low boiling contaminants in the effluent from the first stage would also be separated into the portion boiling below the temperature cut point. If sufficient contaminant removal is performed in the first stage, the second stage can be operated as a “sweet” or low contaminant stage.
Still another option can be to use a separator between the first and second stages of the hydroprocessing reaction system that can also perform at least a partial fractionation of the effluent from the first stage. In this type of aspect, the effluent from the first hydroprocessing stage can be separated into at least a portion boiling below the distillate (such as diesel) fuel range, a portion boiling in the distillate fuel range, and a portion boiling above the distillate fuel range. The distillate fuel range can be defined based on a conventional diesel boiling range, such as having a lower end cut point temperature of at least 350° F. (177° C.) or at least 400° F. (204° C.) to having an upper end cut point temperature of 700° F. (371° C.) or less or 650° F. (343° C.) or less. Optionally, the distillate fuel range can be extended to include additional kerosene, such as by selecting a lower end cut point temperature of at least 300° F. (149° C.).
In aspects where the inter-stage separator is also used to produce a distillate fuel fraction, the portion boiling below the distillate fuel fraction includes, naphtha boiling range molecules, light ends, and contaminants such as H2S. These different products can be separated from each other in any convenient manner. Similarly, one or more distillate fuel fractions can be formed, if desired, from the distillate boiling range fraction. The portion boiling above the distillate fuel range represents the potential lubricant base oils. In such aspects, the portion boiling above the distillate fuel range is subjected to further hydroprocessing in a second hydroprocessing stage.
A hydrocracking process in a second stage (or otherwise under non-sour conditions) can be performed under conditions similar to those used for a first stage hydrocracking process, or the conditions can be different. In an embodiment, the conditions in a second stage can have less severe conditions than a hydrocracking process in a first (sour) stage. The temperature in the hydrocracking process can be 40° F. (22° C.) less than the temperature for a hydrocracking process in the first stage, or 80° F. (44° C.) less, or 120° F. (66° C.) less. The pressure for a hydrocracking process in a second stage can be 100 psig (690 kPa) less than a hydrocracking process in the first stage, or 200 psig (1380 kPa) less, or 300 psig (2070 kPa) less. Additionally or alternately, suitable hydrocracking conditions for a second (non-sour) stage can include, but are not limited to, conditions similar to a first or sour stage. Suitable hydrocracking conditions can include temperatures of 550° F. (288° C.) to 840° F. (449° C.), hydrogen partial pressures of from 250 psig to 5000 psig (1.8 MPag to 34.6 MPag), liquid hourly space velocities of from 0.05 h−1 to 10 h−1, and hydrogen treat gas rates of from 35.6 m3/m3 to 1781 m3/m3 (200 SCF/B to 10,000 SCF/B). In other embodiments, the conditions can include temperatures in the range of 600° F. (343° C.) to 815° F. (435° C.), hydrogen partial pressures of from 500 psig to 3000 psig (3.5 MPag-20.9 MPag), and hydrogen treat gas rates of from 213 m3/m3 to 1068 m3/m3 (1200 SCF/B to 6000 SCF/B). The liquid hourly space velocity can vary depending on the relative amount of hydrocracking catalyst used versus dewaxing catalyst. Relative to the combined amount of hydrocracking and dewaxing catalyst, the LHSV can be from 0.2 h−1 to 10 h−1, such as from 0.5 h−1 to 5 h−1 and/or from 1 h−1 to 4 h−1. Depending on the relative amount of hydrocracking catalyst and dewaxing catalyst used, the LHSV relative to only the hydrocracking catalyst can be from 0.25 h−1 to 50 h−1, such as from 0.5 to 20 h−1, and preferably from 1.0 h−1 to 4.0 h−1.
In still another embodiment, the same conditions can be used for hydrotreating and hydrocracking beds or stages, such as using hydrotreating conditions for both or using hydrocracking conditions for both. In yet another embodiment, the pressure for the hydrotreating and hydrocracking beds or stages can be the same.
Catalytic Dewaxing Process
In some aspects, a dewaxing catalyst as described herein including at least one noble metal, at least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, and at least one Group 6 metal can be included in the same stage and/or the same reactor and/or the same bed as a hydrotreating catalyst. The dewaxing catalyst can be mixed with the hydrotreating catalyst and/or the dewaxing catalyst can be downstream (within the same bed or in a different bed) relative to at least a portion of the hydrotreating catalyst or relative to substantially all of the hydrotreating catalyst.
In other aspects, a dewaxing catalyst including at least one noble metal, at least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, and at least one Group 6 metal can be located in a bed downstream from any hydrocracking catalyst stages and/or any hydrocracking catalyst present in a stage. This can allow the dewaxing to occur on molecules that have already been hydrotreated or hydrocracked to remove a significant fraction of organic sulfur- and nitrogen-containing species. The dewaxing catalyst can be located in the same reactor as at least a portion of the hydrocracking catalyst in a stage. Alternatively, the effluent from a reactor containing hydrocracking catalyst, possibly after a gas-liquid separation, can be fed into a separate stage or reactor containing the dewaxing catalyst. In still other aspects, dewaxing catalyst can be used in a catalyst bed prior to (i.e., upstream relative to the process flow) at least one bed of hydrotreating and/or hydrocracking catalyst.
In various aspects, at least a portion of the dewaxing catalyst can correspond to the dewaxing catalyst including at least one noble metal, at least one Group 8-10 base metal, preferably at least one non-noble Group 8-10 base metal, and at least one Group 6 metal as described herein. Such a dewaxing catalyst can be used alone, or in conjunction with one or more other additional dewaxing catalysts.
Additional suitable dewaxing catalysts can include molecular sieves such as crystalline aluminosilicates (zeolites). In an embodiment, the molecular sieve can comprise, consist essentially of, or be ZSM-5, ZSM-11, ZSM-22, ZSM-23, ZSM-35, ZSM-48, zeolite Beta, TON (Theta-1), or a combination thereof, for example ZSM-23 and/or ZSM-48, or ZSM-48 and/or zeolite Beta. Optionally, molecular sieves that are selective for dewaxing by isomerization as opposed to cracking can be used, such as ZSM-48, zeolite Beta, ZSM-23, or a combination thereof. Additionally or alternately, the molecular sieve can comprise, consist essentially of, or be a 10-member ring 1-D molecular sieve. Examples include EU-1, ZSM-35 (or ferrierite), ZSM-11, ZSM-57, NU-87, SAPO-11, ZSM-48, ZSM-23, and ZSM-22; for example EU-2, EU-11, ZBM-30, ZSM-48, or ZSM-23; such as ZSM-48. Note that a zeolite having the ZSM-23 structure with a silica to alumina ratio of from 20:1 to 40:1 can sometimes be referred to as SSZ-32. Other molecular sieves that are isostructural with the above materials include NU-10, EU-13, KZ-1, and NU-23. Optionally, the additional dewaxing catalyst(s) can include a binder for the molecular sieve, such as alumina, titania, silica, silica-alumina, zirconia, or a combination thereof, for example alumina and/or titania or silica and/or zirconia and/or titania.
In some aspects, the additional dewaxing catalyst(s) used in processes according to the invention can be catalysts with a low ratio of silica to alumina. For example, for ZSM-48, the ratio of silica to alumina in the zeolite can be less than 200:1, such as less than 110:1, or less than 100:1, or less than 90:1, or less than 75:1. In various embodiments, the ratio of silica to alumina can be from 50:1 to 200:1, such as 60:1 to 160:1, or 70:1 to 100:1.
In various aspects, the additional dewaxing catalyst(s) can further include a metal hydrogenation component. The metal hydrogenation component can typically be a Group 6 and/or a Group 8-10 metal, such as a Group 8-10 noble metal. For example, the metal hydrogenation component can be Pt, Pd, or a mixture thereof. In an alternative aspect, the metal hydrogenation component can be a combination of a non-noble Group 8-10 metal with a Group 6 metal. Suitable combinations can include Ni, Co, or Fe with Mo or W, preferably Ni with Mo or W.
The metal hydrogenation component may be added to an additional catalyst in any convenient manner. One technique for adding the metal hydrogenation component is by incipient wetness. For example, after combining a zeolite and a binder, the combined zeolite and binder can be extruded into catalyst particles. These catalyst particles can then be exposed to a solution containing a suitable metal precursor. Alternatively, metal can be added to the catalyst by ion exchange, where a metal precursor is added to a mixture of zeolite (or zeolite and binder) prior to extrusion.
The amount of metal in an additional dewaxing catalyst can be at least 0.1 wt % based on catalyst, or at least 0.15 wt %, or at least 0.2 wt %, or at least 0.25 wt %, or at least 0.3 wt %, or at least 0.5 wt % based on catalyst. The amount of metal in the catalyst can be 20 wt % or less based on catalyst, or 10 wt % or less, or 5 wt % or less, or 2.5 wt % or less, or 1 wt % or less. For aspects where the metal is Pt, Pd, another Group 8-10 noble metal, or a combination thereof, the amount of metal can be from 0.1 to 5 wt %, preferably from 0.1 to 2 wt %, or 0.25 to 1.8 wt %, or 0.4 to 1.5 wt %. For embodiments where the metal is a combination of a non-noble Group 8-10 metal with a Group 6 metal, the combined amount of metal can be from 0.5 wt % to 20 wt %, or 1 wt % to 15 wt %, or 2.5 wt % to 10 wt %.
The additional dewaxing catalysts useful in processes according to the invention can also include a binder. In some aspects, the dewaxing catalysts can be formulated using a low surface area binder, a low surface area binder represents a binder with a surface area of 100 m2/g or less, or 80 m2/g or less, or 70 m2/g or less. The amount of zeolite in a catalyst formulated using a binder can be from 30 wt % zeolite to 90 wt % zeolite relative to the combined weight of binder and zeolite. Preferably, the amount of zeolite is at least 50 wt % of the combined weight of zeolite and binder, such as at least 60 wt % or from 65 wt % to 80 wt %. Optionally, the dewaxing catalyst can include a binder for the molecular sieve, such as alumina, titania, silica, silica-alumina, zirconia, or a combination thereof. In a preferred embodiment, the binder can be alumina. In another embodiment, the binder can be alumina, titania, or a combination thereof. In still another embodiment, the binder can be titania, silica, zirconia, or a combination thereof.
A zeolite can be combined with binder in any convenient manner. For example, a bound catalyst can be produced by starting with powders of both the zeolite and binder, combining and mulling the powders with added water to form a mixture, and then extruding the mixture to produce a bound catalyst of a desired size. Extrusion aids can also be used to modify the extrusion flow properties of the zeolite and binder mixture.
Process conditions in a catalytic dewaxing zone can include a temperature of from 200 to 450° C., preferably 270 to 400° C., a hydrogen partial pressure of from 1.8 MPag to 34.6 MPag (250 psig to 5000 psig), preferably 4.8 MPag to 20.7 MPag, and a hydrogen treat gas rate of from 35.6 m3/m3 (200 SCF/B) to 1781 m3/m3 (10,000 scf/B), preferably 178 m3/m3 (1000 SCF/B) to 890.6 m3/m3 (5000 SCF/B). In still other embodiments, the conditions can include temperatures in the range of 600° F. (343° C.) to 815° F. (435° C.), hydrogen partial pressures of from 500 psig to 3000 psig (3.6 MPag-20.7 MPag), and hydrogen treat gas rates of from 213 m3/m3 to 1068 m3/m3 (1200 SCF/B to 6000 SCF/B). These latter conditions may be suitable, for example, if the dewaxing stage is operating under sour conditions. The liquid hourly space velocity (LHSV) can be from 0.2 h−1 to 10 such as from 0.5 h−1 to 5 and/or from 1 h−1 to 4 h−1.
Additionally or alternately, the conditions for dewaxing can be selected based on the conditions for a preceding reaction in the stage, such as hydrocracking conditions or hydrotreating conditions. Such conditions can be further modified using a quench between previous catalyst bed(s) and the bed for the dewaxing catalyst. Instead of operating the dewaxing process at a temperature corresponding to the exit temperature of the prior catalyst bed, a quench can be used to reduce the temperature for the hydrocarbon stream at the beginning of the dewaxing catalyst bed. One option can be to use a quench to have a temperature at the beginning of the dewaxing catalyst bed that is the same as the outlet temperature of the prior catalyst bed. Another option can be to use a quench to have a temperature at the beginning of the dewaxing catalyst bed that is at least 10° F. (6° C.) lower than the prior catalyst bed, or at least 20° F. (11° C.) lower, or at least 30° F. (16° C.) lower, or at least 40° F. (21° C.) lower.
As still another option, the dewaxing catalyst in the final reaction stage can be mixed with another type of catalyst, such as hydrotreating catalyst, in at least one bed in a reactor. As yet another option, a hydrocracking catalyst and a dewaxing catalyst can be co-extruded with a single binder to form a mixed functionality catalyst.
Hydrofinishing and/or Aromatic Saturation Process
In some aspects, a hydrofinishing and/or aromatic saturation stage can also be provided. The hydrofinishing and/or aromatic saturation can occur after the last hydrocracking or dewaxing stage. The hydrofinishing and/or aromatic saturation can occur either before or after fractionation. If hydrofinishing and/or aromatic saturation occurs after fractionation, the hydrofinishing can be performed on one or more portions of the fractionated product, such as being performed on the bottoms from the reaction stage (i.e., the hydrocracker bottoms). Alternatively, the entire effluent from the last hydrocracking or dewaxing process can be hydrofinished and/or undergo aromatic saturation.
In some situations, a hydrofinishing process and an aromatic saturation process can refer to a single process performed using the same catalyst. Alternatively, one type of catalyst or catalyst system can be provided to perform aromatic saturation, while a second catalyst or catalyst system can be used for hydrofinishing. Typically a hydrofinishing and/or aromatic saturation process will be performed in a separate reactor from dewaxing or hydrocracking processes for practical reasons, such as facilitating use of a lower temperature for the hydrofinishing or aromatic saturation process. However, an additional hydrofinishing reactor following a hydrocracking or dewaxing process but prior to fractionation could still be considered part of a second stage of a reaction system conceptually.
Hydrofinishing and/or aromatic saturation catalysts can include catalysts containing Group 6 metals, Group 8-10 metals, and mixtures thereof. In an embodiment, preferred metals include at least one metal sulfide having a strong hydrogenation function. In another embodiment, the hydrofinishing catalyst can include a Group 8-10 noble metal, such as Pt, Pd, or a combination thereof. The mixture of metals may also be present as bulk metal catalysts wherein the amount of metal is 30 wt. % or greater based on catalyst. Suitable metal oxide supports include low acidic oxides such as silica, alumina, silica-aluminas or Mania, preferably alumina. The preferred hydrofinishing catalysts for aromatic saturation will comprise at least one metal having relatively strong hydrogenation function on a porous support. Typical support materials include amorphous or crystalline oxide materials such as alumina, silica, and silica-alumina. The support materials may also be modified, such as by halogenation, or in particular fluorination. The metal content of the catalyst is often as high as 20 weight percent for non-noble metals. In an embodiment, a preferred hydrofinishing catalyst can include a crystalline material belonging to the M41S class or family of catalysts. The M41S family of catalysts are mesoporous materials having high silica content. Examples include MCM-41, MCM-48 and MCM-50. A preferred member of this class is MCM-41. If separate catalysts are used for aromatic saturation and hydrofinishing, an aromatic saturation catalyst can be selected based on activity and/or selectivity for aromatic saturation, while a hydrofinishing catalyst can be selected based on activity for improving product specifications, such as product color and polynuclear aromatic reduction.
Hydrofinishing conditions can include temperatures from 125° C. to 425° C., preferably 180° C. to 280° C., a hydrogen partial pressure from 500 psig (3.4 MPa) to 3000 psig (20.7 MPa), preferably 1500 psig (10.3 MPa) to 2500 psig (17.2 MPa), and liquid hourly space velocity from 0.1 hr−1 to 5 hr−1 LHSV, preferably 0.5 hr−1 to 2.0 hr−1. Additionally, a hydrogen treat gas rate of from 35.6 m3/m3 to 1781 m3/m3 (200 SCF/B to 10,000 SCF/B) can be used.
In some optional aspects where the feed includes a lubricant boiling range portion (i.e., a portion of the feed has a boiling point greater than 371° C.), after hydroprocessing the bottoms from the hydroprocessing reaction system can have a viscosity index (VI) of at least 95, such as at least 105 or at least 110. In such optional aspects, the amount of saturated molecules in the bottoms from the hydroprocessing reaction system can be at least 90%, while the sulfur content of the bottoms is less than 300 wppm. Thus, in such optional aspects, the bottoms from the hydroprocessing reaction system can be suitable for use as a Group II and/or Group III lubricant base oil.
The following examples use bound ZSM-11 (a catalyst support including an MEL framework structure) to illustrate the benefits of using a base metal dewaxing catalyst including two or more Group 8-10 base metals. However, it is understood that other catalyst supports with different zeolitic framework structures, such as ZSM-48 (MRE), can be used as a zeolitic support in a catalyst including two or more Group 8-10 base metals.
A mixture was prepared from about 8250 g of water, about 1540 g of tetra-n-butylammonium bromide (50% solution) as a structure directing agent or template, about 2750 g of Ultrasil silica, about 1010 g of aluminum sulfate solution (47%), about 880 g of 50% sodium hydroxide solution, and about 30 g of ZSM-11 seeds. The mixture had the following molar composition:
The mixture was reacted at about 250° F. (121° C.) in a 5-gal autoclave with stirring at about 350 RPM for 120 hours. The product was filtered, washed with deionized (DI) water and dried at about 250° F. (120° C.). The XRD pattern of the as-synthesized material showed the typical pure phase of ZSM-11 topology. The SEM of the as-synthesized material showed morphology of agglomerates composed of small crystallites with size of <0.05 micron. The as-synthesized crystals were converted into the hydrogen form by three ion exchanges with ammonium nitrate solution at room temperature, followed by drying at about 250° F. (120° C.) and calcination at about 1000° F. (540° C.) for 6 hours. The resulting MA-ZSM-11 crystals had a SiO2/Al2O3 molar ratio of ˜45; a total surface area (total SA=micropore SA+mesopore SA) of 481 m2/g (364 m2/g micropore+117 m2/g mesopore); hexane sorption of about 96.9 mg/g; and an Alpha value of about 750.
65 parts (basis: calcined ˜538° C.) of ZSM-11 crystal with silica/alumina molar ratio of ˜45/1 (Example 1) were mixed with about 35 parts of pseudoboehmite alumina (basis: calcined ˜538° C.) in a Simpson muller. Sufficient water was added to produce an extrudable paste on a 2″ Bonnot extruder. The mix of ZSM-11, pseudoboehmite alumina, and water containing paste was extruded and dried in a hotpack oven at ˜121° C. overnight. The dried extrudate was calcined in nitrogen at ˜538° C. to decompose and remove the organic template. The N2 calcined extrudate was humidified with saturated air and exchanged with 1 N ammonium nitrate to remove sodium (spec: <500 ppm Na). After ammonium nitrate exchange, the extrudate was washed with deionized water to remove residual nitrate ions prior to drying. The ammonium exchanged extrudate was dried at ˜121° C. overnight and calcined in air at ˜538° C. Several extrusions were made with varying zeolite/binder ratios. Catalyst 2a corresponded to a 65/35 ratio of zeolite to alumina described above. Catalyst 2b corresponded to a 50/50 ratio of zeolite to alumina. Catalyst 2c corresponded to a 35/65 ratio. Catalyst 2d corresponded to a 80/20 ratio of zeolite to alumina. Catalyst 2e corresponded to a 90/10 ratio of zeolite to alumina. Catalyst 2f corresponded to a 65/35 ratio of an alternative alumina binder (Catapal® 200) with a lower surface area than the pseudoboehmite binder (Versal™ 300) used for Catalysts 2a-2e. The Alpha and BET N2 porosity data for these catalysts are summarized in Table 2 below.
Extrudates similar to those made in Example 2 were used as supports for noble and base metals. The extrudates included an alumina (Versal™ 300) binder. The absorption capacity of the extrudates was estimated using deionized water. The Ni, Mo, and Pt precursor compounds used in the catalyst preparations were nickel carbonate hydroxide tetrahydrate, ammonium heptamolybdate tetrahydrate, and tetra-amine platinum nitrate, respectively. Citric acid was included in the impregnation solution as a dispersion agent. The absorption capacity of the extrudate was measured as ˜0.60 cc/g. The volume of the first impregnation solution was targeted as ˜90% of the absorption capacity of the extrudates. To avoid damaging the extrudates during impregnation, the extrudates were humidified with air bubbling through a water bath at room temperature (˜18° C.-25° C.) for ˜16 hours.
To make the noble metal and base metal containing catalyst precursor, about 5.38 g of citric acid (citric acid: Ni=˜2.0) was dissolved in ˜7.0 g of deionized water to form a citric acid solution. The citric solution was heated up to ˜60° C. while stirring. About 1.6456 g of nickel carbonate hydroxide tetrahydrate (2 NiCO3.3Ni(OH)2.4H2O) and 6.263 g of ammonium heptamolybdate tetrahydrate ((NH4)6Mo7O244H2O) were added into the citric acid solution to form the first impregnation solution. The first impregnation solution was stirred until the solution was clear. The first impregnation solution was then cooled to room temperature (˜18° C.-25° C.). These amounts yielded a first impregnation solution with an Ni:Mo molar ratio of ˜0.40 and a citric acid:Ni molar ratio of ˜2.0.
The total solution volume of the first impregnation solution was adjusted with deionized water to achieve the desired volume for impregnation (˜10.8 ml), and the first impregnation solution was impregnated onto ˜20.0 g of the extrudate from Example 2 to form an impregnated support. After this first impregnation, the impregnated support was dried in air at ˜120° C. for ˜16 hrs to form a dried impregnated support.
A second impregnation solution was prepared by adding ˜6 g of deionized water to ˜0.6823 g of tetra-amine platinum nitrate solution (containing ˜0.02422 g of Pt; 3.55 wt % Pt). The second impregnation solution was impregnated onto the dried impregnated support (3.4% Ni+14% Mo/ZSM-11/Al2O3) to form a catalyst precursor. The catalyst precursor remained at room temperature (˜18° C.-25° C.) for ˜60 minutes to reach equilibrium. Then the catalyst precursor was dried in air at ˜120° C. for ˜16 hrs. The catalyst precursor was then stored in a sealed vessel to prevent absorption of moisture from the air. It is noted that a subsequent calcination was not performed after drying. The resulting catalyst included about 0.10 wt % Pt, about 3.4 wt % Ni, and about 14 wt % Mo on the zeolite support relative to the total weight of the catalyst precursor.
Extrudates similar to those made in Example 2 were also used as supports to make a supported NiMo catalyst precursor using methods and reagents similar to those described for the PtNiMo catalyst precursor. The resulting NiMo catalyst precursor included about 3.4 wt % Ni and about 14 wt % Mo on the zeolite support relative to the total weight of the catalyst precursor.
To make the NiMo base metal catalyst precursor, about 134.5 g of citric acid was dissolved in 378.6 g of deionized water, and the citric acid solution was heated up to ˜60° C. while stirring. Once the solution was clear and at ˜60° C., about 41.1 g of nickel carbonate hydroxide tetrahydrate (2 NiCO3.3Ni(OH)2.4H2O) was slowly added into the citric acid solution. This was followed by the addition of ˜156.6 g of ammonium heptamolybdate tetrahydrate ((NH4)6Mo7O244H2O). The solution was stirred until the solution was clear. The solution was then cooled to room temperature (˜18° C.-25° C.). These amounts yielded a solution with a citric acid/Ni molar ratio of ˜2.0. The solution was then used to impregnate 500 g of extrudates (ZSM-11/Al2O3) using a large impregnation cone. The solution was sprayed into the cone for about 20 minutes while rotating the cone at ˜2 RPM. After all of the solution was applied, the extrudates in the cone were tumbled for another 30 minutes at ˜2 RPM. The resulting precursor catalyst was then dried for 1 hour in air at ˜120° C.
Table 3 provides additional description of the base metal catalyst precursors.
The catalyst precursors from Example 3 were sulfided to form catalysts and evaluated for heteroatom removal cloud point reduction of a distillate feed in a tri-phase fixed bed reactor. For the evaluation, the catalyst precursors were sized and loaded into the reactor as 14/20 mesh particles. The reactor was placed in a sandbath to provide isothermal operating conditions. After loading, the catalyst precursors were dried for 2 hours under flowing N2 at ˜110° C. and ˜600 psig (˜4.1 MPag), followed by holding the reactor at ˜110° C. and ˜4.1 MPag of H2 for roughly 2 hours. Following drying, the sulfidation process to form catalyst from the catalyst precursor was started by performing catalyst precursor wetting at 110° C., 1000 psig (˜6.9 MPag), and 2250 SCF/B (˜400 Nm3/m3) of H2 with a light gas oil feed. This was followed by heating the reactor to 204° C., at which point the feed was switched to a spiked light gas oil containing 2.5 wt % sulfur (spiking was performed with dimethyldisulfide) at a LHSV of 2.0 hr−1 while maintaining the H2 treat gas flow at ˜400 Nm3/m3. After introducing the spiked light gas oil, the reactor was heated to ˜250° C. at a rate of ˜28° C./hr under the same liquid and gas flow rates and held for at least ˜8 hours. The temperature was then ramped to ˜320° C. at ˜28° C./hr and held at that temperature for roughly 5 hours.
After this final temperature hold, a distillate feed for processing was introduced into the reactor. Table 4 shows the properties of the distillate feed for processing.
The performance of the sulfided catalysts formed from the catalyst precursors in Example 3 was evaluated based on activity for sulfur removal, nitrogen removal, and cloud point reduction. With regard to sulfur removal,
The PtNiMo catalyst also exhibited greater activity for nitrogen removal.
Based on
A catalyst precursor comprising: at least one noble metal, at least one Group 6 metal, at least one non-noble Group 8-10 base metal and a dispersion agent supported on a support comprising a zeolitic framework structure, wherein the catalyst precursor has a molar ratio of the least one non-noble Group 8-10 base metal to the at least one Group 6 metal of about 0.1 to about 10 (or about 0.1 to about 5.0 or about 0.1 to about 1.0) and a molar ratio of the dispersion agent to the least one Group 8-10 base metal about 0.5 to about 10 (or about 0.5 to about 4.0).
A method of forming a composition, comprising: impregnating a support comprising a zeolitic framework structure with a first impregnation solution comprising at least one Group 6 metal salt, at least one non-noble Group 8-10 base metal salt, and a dispersion agent, the dispersion agent comprising a compound having 2-10 carbon atoms and a carbon atom to oxygen atom ratio of about 0.6 to about 2.0 to form an impregnated support; drying the impregnated support at a temperature of about 80° C. to about 200° C.; impregnating the dried impregnated support with a second impregnation solution comprising at least one noble metal salt to form a catalyst precursor; and drying the catalyst precursor at a temperature of about 80° C. to about 200° C.
The method of forming a composition of Embodiment 2, wherein the catalyst precursor has a molar ratio of the least one non-noble Group 8-10 base metal to the at least one Group 6 metal of about 0.1 to about 10 (or about 0.1 to about 5.0 or about 0.1 to about 1.0) and a molar ratio of the dispersion agent to the least one Group 8-10 base metal about 0.5 to about 10 (or about 0.5 to about 4.0).
The method of forming a composition of Embodiment 2 or 3, wherein the at least one Group 6 metal salt comprises a W salt, a Mo salt, or a combination thereof, the at least one non-noble Group 8-10 metal salt comprise an Ni salt, a Co salt or a combination thereof, and the at least one noble metal salt comprise a Pt salt, a Ru salt, an Os salt, a Rh salt, an Ir salt, or a combination thereof.
The method of forming a composition of any of Embodiments 2 to 4, the method further comprising sulfiding the catalyst precursor under effective sulfiding conditions to form a dewaxing catalyst.
The catalyst precursor or method of forming a composition of any of the above embodiments, wherein the zeolitic framework structure comprises an MEL framework structure, the MEL framework structure optionally comprising ZSM-11, the MEL framework structure optionally comprising a) a molar ratio of silica to alumina of about 35 to about 55; b) an alpha value of at least about 380; c) a total surface area of at least about 350 m2/g, or d) a combination thereof.
The catalyst precursor or method of forming a composition of any of Embodiments 1-5, wherein the zeolitic framework structure comprises ZSM-48, ZSM-11, a zeolitic framework structure having a 10-member ring as a largest pore channel, or a combination thereof.
The catalyst precursor or method of forming a composition of any of the above embodiments, wherein the catalyst precursor comprises less than about 2.0 wt % of the at least one noble metal and about 2.0 wt % to about 30 wt % of the at least one Group 6 metal and the at least one non-noble Group 8-10 base metal based on a weight of the catalyst precursor, wherein the at least one noble metal optionally comprises Pt, Ru, Os, Rh, Ir, or a combination thereof, the at least one Group 6 metal optionally comprises W, Mo, or a combination thereof, and the at least one non-noble Group 8-10 base metal optionally comprises Ni, Co or a combination thereof.
The catalyst precursor or method of forming a composition of any of the above embodiments, wherein the dispersion agent comprises a compound having 2-10 carbon atoms and a carbon atom to oxygen atom ratio of about 0.6 to about 2.0.
The catalyst precursor or method of forming a composition of any of the above embodiments, wherein the dispersion agent comprises a glycol, a carboxylic acid, or a combination thereof; or wherein the dispersion agent comprises citric acid, gluconic acid, nitrilotriacetic acid, ethylene glycol, or a combination thereof.
The catalyst precursor or method of forming a composition of any of the above embodiments, wherein the support further comprises a binder selected from the group consisting of an active or inactive material, an inorganic material, a clay, alumina, silica, silica-alumina, titania, zirconia, or a combination thereof.
A method for treating a distillate boiling range feed, comprising: exposing a distillate boiling range feed to a dewaxing catalyst under effective hydroprocessing conditions, the dewaxing catalyst comprising at least one noble metal sulfide, at least one Group 6 metal sulfide, at least one non-noble Group 8-10 base metal sulfide; the dewaxing catalyst being formed by: impregnating a support comprising a zeolitic framework structure with a first impregnation solution comprising at least one Group 6 metal salt, at least one non-noble Group 8-10 base metal salt, and a dispersion agent, the dispersion agent comprising a compound having 2-10 carbon atoms and a carbon atom to oxygen atom ratio of about 0.6 to about 2.0 to form an impregnated support; drying the impregnated support at a temperature of about 80° C. to about to 200° C.; impregnating the dried impregnated support with a second impregnation solution comprising at least one noble metal salt to form a catalyst precursor; drying the catalyst precursor at a temperature of about 80° C. to about 200° C.; and sulfiding the dried catalyst precursor under effective sulfiding conditions.
The method of Embodiment 12, wherein the dewaxing catalyst has a molar ratio of the least one non-noble Group 8-10 base metal to the at least one Group 6 metal of about 0.1 to about 10 (or about 0.1 to about 5.0 or about 0.1 to about 1.0) and a molar ratio of the dispersion agent to the least one Group 8-10 base metal about 0.5 to about 10 (or about 0.5 to about 4.0) prior to the sulfiding.
The method of any of Embodiments 11-13, wherein the effective hydroprocessing conditions comprise at least one of effective hydrotreating conditions and effective catalytic dewaxing conditions; wherein the method further comprises exposing the distillate boiling range feed to a hydrotreating catalyst; or a combination thereof.
The method of any of Embodiments 5-14, wherein the catalyst precursor is sulfided without prior calcining of the catalyst precursor.
A method for treating a distillate boiling range feed, comprising: exposing a distillate boiling range feed to a dewaxing catalyst under effective hydroprocessing conditions, the dewaxing catalyst comprising at least one noble metal sulfide, at least one Group 6 metal sulfide, and at least one non-noble Group 8-10 base metal sulfide; the dewaxing catalyst being formed by a) the method of forming a composition according to any of Embodiments 5-10 or b) by sulfiding a catalyst precursor according to any of Embodiments 1 and 6-10 under effective sulfiding conditions, the catalyst precursor optionally being sulfided without prior calcining of the catalyst precursor.
A method for treating a distillate boiling range feed, comprising: exposing a distillate boiling range feed to a hydrotreating catalyst under effective hydroprocessing conditions to form a hydrotreated effluent; and exposing at least a portion of the hydrotreated effluent to a dewaxing catalyst under effective hydroprocessing conditions, the dewaxing catalyst comprising at least one noble metal sulfide, at least one Group 6 metal sulfide, at least one non-noble Group 8-10 base metal sulfide; the dewaxing catalyst being formed by a) the method of forming a composition according to any of Embodiments 5-10 or b) by sulfiding a catalyst precursor according to any of Embodiments 1 and 6-10 under effective sulfiding conditions, the catalyst precursor optionally being sulfided without prior calcining of the catalyst precursor.
Although the present invention has been described in terms of specific embodiments, it is not so limited. Suitable alterations/modifications for operation under specific conditions should be apparent to those skilled in the art. It is therefore intended that the following claims be interpreted as covering all such alterations/modifications as fall within the true spirit/scope of the invention.
This application claims priority to U.S. Provisional Application Ser. No. 62/501,866 filed May 5, 2017, which is herein incorporated by reference in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4568450 | Ting et al. | Feb 1986 | A |
| 8288305 | Bai | Oct 2012 | B2 |
| 8394255 | McCarthy et al. | Mar 2013 | B2 |
| 20090071875 | Kato | Mar 2009 | A1 |
| 20110105302 | Burton | May 2011 | A1 |
| 20110315599 | Prentice | Dec 2011 | A1 |
| 20150126791 | Kijlstra et al. | May 2015 | A1 |
| 20150158018 | Zhan | Jun 2015 | A1 |
| 20150273447 | Jongkind et al. | Oct 2015 | A1 |
| 20170175011 | McCarthy et al. | Jun 2017 | A1 |
| 20170175015 | Podsiadlo et al. | Jun 2017 | A1 |
| Number | Date | Country |
|---|---|---|
| 0155822 | Sep 1985 | EP |
| 1 880 760 | Jan 2008 | EP |
| 2 072 127 | Jun 2009 | EP |
| WO 2013152577 | Oct 2013 | WO |
| 2017112558 | Jun 2017 | WO |
| 2017112558 | Jun 2017 | WO |
| Entry |
|---|
| The International Search Report and Written Opinion of PCT/US2018/029517 dated Oct. 1, 2018. |
| Marin-Rosas, “Middle Distillate Hydrotreatment Zeolite Catalysts Containing Pt/Pd or Ni”, Dissertation, 2006, Texas A&M University, retrieved from the internet Oct. 15, 2018, https://oaktrust.library.tamu.edu/bitstream/handle/1969.1/ETD-TAMU-1066/Marin-Rosas-Dissertation.pdf?sequence=1&isAllowed=y. |
| Database of Zeolite Structures, Structure Commission of the International Zeolite Association, Jun. 27, 2018, www.iza-structure.org/databases. |
| Number | Date | Country | |
|---|---|---|---|
| 20180318811 A1 | Nov 2018 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62501866 | May 2017 | US |