Patent Application
20160149265
The present invention relates to a non-aqueous electrolyte solution for secondary batteries, and a lithium ion secondary battery.
As a solvent of a non-aqueous electrolyte solution to be used for lithium ion secondary batteries, a carbonate type solvent (such as ethylene carbonate or dimethyl carbonate) has been widely used in that it dissolves a lithium salt excellently to provide a high lithium ion conductivity, and it has a wide potential window. However, since a carbonate type solvent is flammable, use of a fluorinated solvent has been proposed as a flame retardant solvent (Patent Document 1). However, a fluorinated solvent has a low ability to dissolve a lithium salt and thus if a fluorinated solvent is used, the obtainable lithium ion secondary battery tends to have poor rate properties.
As a flame retardant non-aqueous electrolyte solution which is excellent in the battery properties (the cycle properties and the discharge capacity) and which has a high ion conductivity, the following has been proposed.
That is, a non-aqueous electrolyte solution comprising at least one fluorine-containing solvent selected from the group consisting of a fluorine-containing ether compound, a fluorine-containing chain carboxylic acid ester compound and a fluorine-containing chain carbonate compound, a cyclic carbonate compound having no fluorine atom, a cyclic carboxylic acid ester compound having no fluorine atom, and a lithium salt (Patent Document 2).
In Patent Document 2, the ion conductivity of the non-aqueous electrolyte solution is increased so as to improve the rate properties of the obtainable lithium ion secondary battery (for example, paragraph [0091]). However, according to the studies by the present inventors, even by using a non-aqueous electrolyte solution having a high ion conductivity disclosed in Examples in Patent Document 2, the rate properties of the lithium ion secondary battery are still insufficient.
Patent Document 1: JP-A-8-037024
Patent Document 2: JP-A-2008-192504
The object of the present invention is to provide a flame retardant non-aqueous electrolyte solution for secondary batteries with which a lithium ion secondary battery excellent in the rate properties can be obtained; and a safe lithium ion secondary battery excellent in the rate properties.
The present inventors have conducted extensive studies on the relation between the properties of a non-aqueous electrolyte solution and the rate properties of a lithium ion secondary battery and as a result, found that an improvement in the rate properties of a lithium ion secondary battery is significantly influenced by the lithium ion diffusion coefficient of the non-aqueous electrolyte solution, not substantially influenced by the ion conductivity of the non-aqueous electrolyte solution.
That is, the present invention provides a non-aqueous electrolyte solution for secondary batteries, comprising a lithium salt and a liquid composition, wherein
the liquid composition comprises a fluorine-containing solvent (α) containing at least one member selected from the group consisting of a fluorine-containing ether compound, a fluorine-containing chain carboxylic acid ester compound and a fluorine-containing chain carbonate compound, and a cyclic carboxylic acid ester compound,
the lithium salt contains LiPF6, and
the lithium ion diffusion coefficient of the non-aqueous electrolyte solution at 25° C. is at least 1.1×10−10 m2/s.
The liquid composition preferably has a viscosity of at most 1.7 mPa·s at 25° C.
The non-aqueous electrolyte solution preferably has a lithium salt content of from 0.7 to 1.5 mol/L.
The cyclic carboxylic acid ester compound is preferably at least one member selected from the group consisting of γ-butyrolactone, γ-valerolactone and ε-caprolactone.
The ratio of the mass of the cyclic carboxylic acid ester compound to the total mass of the non-aqueous electrolyte solution is preferably from 4 to 50 mass %.
The ratio of the mass of the fluorine-containing solvent (α) to the total mass of the non-aqueous electrolyte solution is preferably from 30 to 80 mass %.
NA/NLi i.e. the ratio of the total number of moles NA of the cyclic carboxylic acid ester compound to the total number of moles NLi of lithium atoms derived from the lithium salt is preferably from 1.5 to 7.0.
The liquid composition may further contain at least one compound (β) selected from the group consisting of a saturated cyclic carbonate compound, a saturated chain carbonate compound having no fluorine atom, a saturated cyclic sulfone compound (excluding a lithium salt) and a phosphoric acid ester compound.
That is, the liquid composition of the present invention is either one consisting solely of the fluorine-containing solvent (α) and a cyclic carboxylic acid ester, or one consisting of the fluorine-containing solvent (α), the cyclic carboxylic acid ester and the compound (β).
(NA+NB)/NLi i.e. the ratio of the sum of the total number of moles NA of the cyclic carboxylic acid ester compound and the total number of moles NB of the compound (β) to the total number of moles NLi of lithium atoms derived from the lithium salt, is preferably from 3.0 to 7.0.
The ratio of the mass of the saturated chain carbonate compound having no fluorine atom to the total mass of the non-aqueous electrolyte solution is preferably at most 30 mass %.
The ratio of the sum of the mass of the saturated cyclic carbonate compound and the mass of the saturated cyclic carbonate compound having no fluorine atom to the total mass of the non-aqueous electrolyte solution, is preferably at most 30 mass %.
The fluorine-containing solvent (α) preferably contains the fluorine-containing ether compound.
The fluorine-containing ether compound is preferably a compound represented by the following formula (1):
R1—O—R2 (1)
wherein each of R1 and R2 which are independent of each other, is a C1-10 alkyl group, a C3-10 cycloalkyl group, a C1-10 fluorinated alkyl group, a C3-10 fluorinated cycloalkyl group, a C2-10 alkyl group having at least one etheric oxygen atom, or a C2-10 fluorinated alkyl group having at least one etheric oxygen atom, provided that one or each of R1 and R2 is a C1-10 fluorinated alkyl group, a C3-10 fluorinated cycloalkyl group or a C2-10 fluorinated alkyl group having at least one etheric oxygen atom.
The compound represented by the formula (1) preferably contains at least one member selected from the group consisting of CF3CH2OCF2CHF2, CF3CH2OCF2CHFCF3, CHF2CF2CH2OCF2CHF2, CH3CH2CH2OCF2CHF2, CH3CH2OCF2CHF2 and CHF2CF2CH2OCF2CHFCF3.
The lithium ion secondary battery of the present invention comprises a positive electrode containing, as an active material, a material capable of absorbing and desorbing lithium ions, a negative electrode containing, as an active material, at least one member selected from the group consisting of metal lithium, a lithium alloy and a carbon material capable of absorbing and desorbing lithium ions, and the non-aqueous electrolyte solution for secondary batteries of the present invention.
According to the non-aqueous electrolyte solution for secondary batteries of the present invention, a lithium ion secondary battery excellent in the rate properties can be obtained. Further, the non-aqueous electrolyte solution for secondary batteries of the present invention is flame retardant.
The lithium ion secondary battery of the present invention is excellent in the rate properties and is used safely.
In this specification, a compound represented by the formula (1) will be referred to as a compound (1). The same applies to compounds represented by other formulae.
The following definitions of terms are applicable throughout description and claims.
“The non-aqueous electrolyte solution” means an electrolyte solution containing substantially no water, and even if it contains water, the amount of water is within such a range that performance degradation of a secondary battery using such a non-aqueous electrolyte solution is thereby not observed. The amount of water contained in such a non-aqueous electrolyte solution is preferably at most 500 mass ppm, more preferably at most 100 mass ppm, particularly preferably at most 50 mass ppm, based on the total mass of the non-aqueous electrolyte solution. The lower limit of the amount of water is 0 mass ppm.
“The liquid composition” contains a fluorine-containing solvent (α) and a cyclic carboxylic acid ester compound. The liquid composition may contain a compound (β).
That is, the liquid composition in the present invention is either one consisting solely of the fluorine-containing solvent (α) and the cyclic carboxylic acid ester, or one consisting of the fluorine-containing solvent (α), the cyclic carboxylic acid ester and the compound (β).
Compounds other than the lithium salt, the fluorine-containing solvent (α), the cyclic carboxylic acid ester compound and the compound (β) (that is, another solvent, additives, etc.) are defined as “other components” and are distinguished from the lithium salt and the liquid composition.
That is, the electrolyte solution in the present invention comprises the lithium salt, the fluorine-containing solvent (α) and the cyclic carboxylic acid ester and may contain the compound (β) and other components.
“The fluorine-containing ether compound” means a chain or cyclic compound having an ether bond and having a fluorine atom.
“The fluorine-containing chain carboxylic acid ester compound” means a chain compound having an ester bond in its chain structure, having no cyclic structure containing an ester bond, and having a fluorine atom.
“The fluorine-containing chain carbonate compound” means a chain compound having a carbonate bond represented by —O—C(═O)—O— in its chain structure, having no cyclic structure containing a carbonate bond, and having a fluorine atom.
“A fluorine-containing alkane compound” means a compound having at least one hydrogen atom in an alkane substituted with a fluorine atom and having remaining hydrogen atoms.
“The cyclic carboxylic acid ester compound” means a cyclic compound having an ester bond as a part of the cyclic skeleton.
“The saturated cyclic carbonate compound” means a cyclic compound having a cyclic skeleton composed of carbon atoms and oxygen atoms, having a carbonate bond represented by —O—C(═O)—O— as a part of the cyclic skeleton, and having no carbon-carbon unsaturated bond.
“The saturated chain carbonate compound having no fluorine atom” means a chain compound having a carbonate bond represented by —O—C(═O)—O— in its chain structure, having no cyclic structure having a carbonate bond, and having no fluorine atom nor carbon-carbon unsaturated bond.
“Fluorinated” and “fluorine-containing” mean that part of or all the hydrogen atoms bonded to carbon atoms are substituted with fluorine atoms.
“The fluorinated alkyl group” means a group having part of or all the hydrogen atoms in an alkyl group substituted with fluorine atoms. In a group having part of hydrogen atoms fluorinated, hydrogen atoms and fluorine atoms are present.
“A perfluoroalkyl group” means a group having all the hydrogen atoms in an alkyl group substituted with fluorine atoms.
“The carbon-carbon unsaturated bond” means a carbon-carbon double bond or a carbon-carbon triple bond.
The non-aqueous electrolyte solution for secondary batteries of the present invention (hereinafter sometimes referred to simply as a non-aqueous electrolyte solution) comprises a lithium salt and a liquid composition and as the case requires, contains another component.
The lithium ion diffusion coefficient of the non-aqueous electrolyte solution at 25° C. is at least 1.0×10−10 m2/s, preferably at least 1.5×10−10 m2/s, more preferably at least 2.0×10−10 m2/s. When the lithium ion diffusion coefficient is at least 1.1×10−10 m2/s, a lithium ion secondary battery excellent in the rate properties will be obtained. The lithium ion diffusion coefficient is preferably as high as possible, and the upper limit is not particularly limited.
The lithium ion diffusion coefficient is calculated by pulsed field gradient NMR method.
The lithium ion diffusion coefficient of the non-aqueous electrolyte solution may be adjusted e.g. by the viscosity of the liquid composition, the content of the lithium salt in the non-aqueous electrolyte solution, etc. Specifically, by decreasing the viscosity of the liquid composition, lithium ions are likely to be diffused in the non-aqueous electrolyte solution and thus the lithium ion diffusion coefficient increases. Further, by lowering the content of the lithium salt in the non-aqueous electrolyte solution, lithium ions are likely to be diffused in the non-aqueous electrolyte solution and thus the lithium ion diffusion coefficient increases.
The lower limit value for the ion conductivity at 25° C. of the non-aqueous electrolyte solution is preferably 0.40 S/m. A secondary battery using a non-aqueous electrolyte solution, of which the ion conductivity at 25° C. is less than 0.40 S/m, is inferior in output properties and thus is poor in practical applicability. When the ion conductivity at 25° C. of the non-aqueous electrolyte solution is at least 0.40 S/m, the secondary battery will be excellent in output properties.
The lithium salt is an electrolyte salt which will be dissociated in the non-aqueous electrolyte solution to supply lithium ions. The lithium salt may, for example, be LiPF6, the following compound (A) (wherein k is an integer of from 1 to 5), FSO2N(Li)SO2F, CF3SO2N(Li)SO2CF3, CF3CF2SO2N(Li)SO2CF2CF3, LiClO4, the following compound (B), the following compound (C), the following compound (D), the following compound (E) or LiBF4:
The non-aqueous electrolyte solution of the present invention contains at least LiPF6 as the lithium salt. The non-aqueous electrolyte solution may contain a lithium salt other than LiPF6 as the case requires.
LiPF6 develops a high ion conductivity when dissolved in a solvent with a high dissolving power, but is less likely to be dissolved in a fluorine-containing solvent as compared with another lithium salt such as CF3CF2SO2N(Li)SO2CF2CF3. However, the solubility of LiPF6 in a fluorine-containing solvent will be improved when LiPF6 is used in combination with a cyclic carboxylic acid ester compound. By LiPF6 being uniformly dissolved in a fluorine-containing solvent, a non-aqueous electrolyte solution having a practically sufficient ion conductivity tends to be obtained. Further, LiPF6 tends to be thermally decomposed and to lower the safety of the obtainable battery, however, by the cyclic carboxylic acid ester compound, a battery using the non-aqueous electrolyte solution using LiPF6 is less likely to undergo thermal runaway.
The compound (A) may, for example, be the following compounds (A-1) to (A-4). The compound (A) preferably contains the compound (A-2) wherein k is 2, more preferably consists solely of the compound (A-2) wherein k is 2, whereby a non-aqueous electrolyte solution with a high ion conductivity tends to be obtained.
The liquid composition comprises the fluorine-containing solvent (α) and the cyclic carboxylic acid ester compound and as the case requires, may contain the compound (β).
That is, the liquid composition in the present invention is either one consisting solely of the fluorine-containing solvent (α) and the cyclic carboxylic acid ester or one consisting of the fluorine-containing solvent (α), the cyclic carboxylic acid ester and the compound (β).
The lower limit value for the viscosity of the liquid composition at 25° C. is preferably as low as possible and is not particularly limited, and is preferably 0.6 mPa·s. The upper limit value for the viscosity of the liquid composition at 25° C. is preferably 1.7 mPa·s, more preferably 1.5 mPa·s, further preferably 1.3 mPa·s. When the viscosity of the liquid composition is at least the lower limit value, the boiling point of the obtainable electrolyte solution will not be too low, and the electrolyte solution tends to be practical. When the viscosity of the liquid composition is at most the upper limit value, the lithium ion diffusion coefficient of the non-aqueous electrolyte solution tends to be sufficiently high, and the rate properties of the obtainable lithium ion secondary battery will be further improved.
The viscosity of the liquid composition may be adjusted by the viscosities of the respective components constituting the liquid composition. For example, the viscosity can be lowered by using a solvent having a low viscosity, and the viscosity can be increased by using a solvent having a high viscosity.
The viscosity of the liquid composition is measured by a BM rotational viscometer.
The fluorine-containing solvent (α) contains at least one member selected from the group consisting of a fluorine-containing ether compound, a fluorine-containing chain carboxylic acid ester compound and a fluorine-containing chain carbonate compound and as the case requires, may contain another fluorine-containing solvent (excluding the fluorine-containing cyclic carbonate).
The fluorine-containing solvent (α) is a solvent having a fluorine atom in its molecule and is excellent in the flame retardance. As the fluorine-containing solvent (α), one type may be used alone, or two or more types may be used in combination. When two or more types of the fluorine-containing solvent (α) are to be used, their ratio may optionally be set.
The fluorine-containing solvent (α) preferably contains a fluorine-containing ether compound, whereby high solubility of the lithium salt, flame retardance and ion conductivity of the non-aqueous electrolyte solution will be achieved. The fluorine-containing ether compound is preferably the following compound (1), whereby high solubility of the lithium salt, flame retardance and ion conductivity of the non-aqueous electrolyte solution will be achieved. As the fluorine-containing ether compound, one type may be used alone, or two or more types may be used in combination. In a case where the compound (1) is contained, as the compound (1), one type may be used alone, or two or more types may be used in combination. When two or more types of the fluorine-containing ether compound are to be used, their ratio may optionally be set.
R1—O—R2 (1)
wherein each of R1 and R2 which are independent of each other, is a C1-10 alkyl group, a C3-10 cycloalkyl group, a C1-10 fluorinated alkyl group, a C3-10 fluorinated cycloalkyl group, a C2-10 alkyl group having at least one etheric oxygen atom, or a C2-10 fluorinated alkyl group having at least one etheric oxygen atom, provided that one or each of R1 and R2 is a C1-10 fluorinated alkyl group, a C3-10 fluorinated cycloalkyl group or a C2-10 fluorinated alkyl group having at least one etheric oxygen atom.
In the compound (1), each of the alkyl group and the alkyl group having an etheric oxygen atom may, for example, be a group having a straight chain structure, a branched structure or a partially cyclic structure (e.g. a cycloalkylalkyl group).
One or each of R1 and R2 is a C1-10 fluorinated alkyl group, a C3-10 fluorinated cycloalkyl group or a C2-10 fluorinated alkyl group having at least one etheric oxygen atom. When one or each of R1 and R2 is such a group, the solubility of the lithium salt in the non-aqueous electrolyte solution and the flame retardance will further improve. R1 and R2 may be the same or different.
The compound (1) is preferably a compound (1-A) wherein each of R1 and R2 is a C1-10 fluorinated alkyl group, a compound (1-B) wherein R1 is a C2-10 fluorinated alkyl group having at least one etheric oxygen atom and R2 is a C1-10 fluorinated alkyl group, or a compound (1-C) wherein R1 is a C1-10 fluorinated alkyl group and R2 is a C1-10 alkyl group, whereby an excellent solubility of the lithium salt in the liquid composition will be achieved, more preferably the compound (1-A) or the compound (1-C), particularly preferably the compound (1-A).
The total number of carbon atoms in the compound (1) is preferably from 4 to 10, more preferably from 4 to 8, since if it is too small, the boiling point will be too low, and if it is too large, the viscosity will the too high.
The molecular weight of the compound (1) is preferably from 150 to 800, more preferably from 150 to 500, particularly preferably from 200 to 500, since if it is too low, the boiling point will be too low, and if it is too high, the viscosity will be too high.
When the compound (1) has an etheric oxygen atom, the number of etheric oxygen atoms in the compound (1) is preferably from 1 to 4, more preferably 1 or 2, further preferably 1. The number of etheric oxygen atoms in the compound (1) is influential over flammability.
The fluorine content in the compound (1) is preferably at least 50 mass %, more preferably at least 60 mass %. When the fluorine content in the compound (1) is high, the flame retardance is excellent. The fluorine content is meant for the proportion of the total mass of fluorine atoms in the molecular weight.
The compound (1) is preferably a compound wherein each of R1 and R2 is a partially fluorinated alkyl group having part of hydrogen atoms in an alkyl group fluorinated, more preferably a compound wherein the terminal of one or each of R1 and R2 is —CF2H, since the solubility of the lithium salt in the liquid composition will be thereby excellent.
Specific examples of the compound (1-A) and the compound (1-B) and specific examples of the fluorine-containing ether compound other than the compound (1-A) and (1-B), may, for example, be compounds disclosed in WO2009/133899.
The compound (1) is preferably at least one member selected from the group consisting of CF3CH2OCF2CHF2, CF3CH2OCF2CHFCF3, CHF2CF2CH2OCF2CHF2, CH3CH2CH2OCF2CHF2, CH3CH2OCF2CHF2 and CHF2CF2CH2OCF2CHFCF3, particularly preferably at least one member selected from the group consisting of CF3CH2OCF2CHF2, CHF2CF2CH2OCF2CHF2 and CHF2CF2CH2OCF2CHFCF3, since the solubility of the lithium salt in the liquid composition will be thereby excellent, the flame retardance will be excellent, the viscosity will be low, and the boiling point will not be too low.
The fluorine-containing chain carboxylic acid ester compound preferably contains the following compound (3) in view of the viscosity, the boiling point, etc., more preferably consists solely of the compound (3). As the fluorine-containing chain carboxylic acid ester compound, one type may be used alone, or two or more types may be used in combination. In a case where the compound (3) is used, as the compound (3), one type may be used alone, or two or more types may be used in combination. When two or more types of the fluorine-containing chain carboxylic acid ester compound are to be used, their ratio may optionally be set.
wherein each of R3 and R4 which are independent of each other, is a C1-3 alkyl group or a C1-3 fluorinated alkyl group, provided that one or each of R3 and R4 is a C1-3 fluorinated alkyl group.
In the compound (3), the alkyl group and the fluorinated alkyl group each independently have a straight chain structure or a branched structure.
One or each of R3 and R4 is a C1-3 fluorinated alkyl group. When one or each of R3 and R4 is a C1-3 fluorinated alkyl group, the compound (3) has improved oxidation resistance and flame retardance. R3 and R4 may be the same or different.
R3 is preferably a methyl group, an ethyl group, a difluoromethyl group, a trifluoromethyl group, a tetrafluoroethyl group or a pentafluoroethyl group, more preferably a difluoromethyl group or a trifluoromethyl group, in view of the viscosity and the boiling point, or availability of the compound.
R4 is preferably a methyl group, an ethyl group, a trifluoromethyl group, a 2-fluoroethyl group, a 2,2-difluoroethyl group or a 2,2,2-trifluoroethyl group, more preferably a methyl group, an ethyl group or a 2,2,2-trifluoroethyl group, further preferably a methyl group or an ethyl group, in view of the viscosity and the boiling point, or availability of the compound.
The total number of carbon atoms in the compound (3) is preferably from 3 to 7, more preferably from 3 to 6, further preferably from 3 to 5, since if it is too small, the boiling point tends to be too low, and if it is too large, the viscosity tends to be too high.
The molecular weight of the compound (3) is preferably from 100 to 300, more preferably from 100 to 250, particularly preferably from 100 to 200, since if it is too low, the boiling point tends to be too low, and if it is too high, the viscosity tends to be too high.
The fluorine content in the compound (3) is preferably at least 25 mass %, more preferably at least 30 mass %, since the flame retardance will thereby be improved.
The compound (3) may, for example, be specifically (2,2,2-trifluoroethyl) acetate, methyl difluoroacetate, ethyl difluorotriacetate or ethyl trifluoroacetate. Among them, methyl difluoroacetate or ethyl trifluoroacetate is preferred from the viewpoint of availability and excellent battery performance such as cycle properties.
The fluorine-containing chain carbonate compound preferably contains the following compound (4), more preferably consists solely of the compound (4) in view of the viscosity, the boiling point, etc. As the fluorine-containing chain carbonate compound, one type may be used alone, or two or more types may be used in combination. When the compound (4) is contained, as the compound (4), one type may be used alone, or two or more types may be used in combination. When two or more types of the fluorine-containing chain carbonate compound are to be used, their ratio may be optionally set.
wherein each of R5 and R6 which are independent of each other, is a C1-3 alkyl group or a C1-3 fluorinated alkyl group, provided that one or each of R5 and R6 is a C1-3 fluorinated alkyl group.
In the compound (4), each of the alkyl group and the fluorinated alkyl group have a straight chain structure or a branched structure.
One or each of R5 and R6 is a C1-3 fluorinated alkyl group. When one or each of R5 and R6 is a C1-3 fluorinated alkyl group, the solubility of the lithium salt and the flame retardance will be improved. R5 and R6 may be the same or different.
The compound (4) is preferably a compound wherein each of R5 and R6 is a C1-3 fluorinated alkyl group, in view of the viscosity and the boiling point, or availability of the compound. As R5 and R6, CF3CH2— or CHF2CF2CH2— is preferred.
The total number of carbon atoms in the compound (4) is preferably from 4 to 7, since if it is too small, the boiling point tends to be too low, and if it is too large, the viscosity tends to be too high.
The molecular weight of the compound (4) is preferably from 180 to 400, more preferably from 200 to 350, particularly preferably from 210 to 300, since if it is too low, the boiling point tends to be too low, and if it is too high, the viscosity tends to be too high.
The fluorine content in the compound (4) is preferably at least 25 mass %, more preferably at least 30 mass %, since the flame retardance will thereby be improved.
The compound (4) may, for example, be specifically bis(2,2,2-trifluoroethyl) carbonate or bis(2,2,3,3-tetrafluoropropyl) carbonate. Bis(2,2,2-trifluoroethyl) carbonate is preferred from the viewpoint of the viscosity, availability and battery performance such as output properties.
The fluorine-containing solvent (α) may contain as another fluorine-containing solvent a fluorine-containing alkane compound. In a case where the fluorine-containing solvent contains a fluorine-containing alkane compound, the non-aqueous electrolyte solution has its vapor pressure suppressed, and thereby has further improved flame retardance.
The fluorine-containing alkane compound is preferably a C4-12 fluorine-containing alkane compound. When a fluorine-containing alkane compound having at least 4 carbon atoms is used, the vapor pressure of the non-aqueous electrolyte solution is low. When a fluorine-containing alkane compound having at most 12 carbon atoms is used, the solubility of the lithium salt is good.
The fluorine content in the fluorine-containing alkane compound is preferably from 50 to 80 mass %. When the fluorine content in the fluorine-containing alkane compound is at least 50 mass %, the flame retardance is excellent. When the fluorine content in the fluorine-containing alkane compound is at most 80 mass %, the solubility of the lithium salt can easily be maintained.
The fluorine-containing alkane compound is preferably a compound having a straight chain structure and may, for example, be n-C4F9CH2CH3, n-C6F13CH2CH3, n-C6F13H or n-C8F17H. As such a fluorine-containing alkane compound, one type may be used alone, or two or more types may be used in combination.
The liquid composition contains a cyclic carboxylic acid ester compound. By the cyclic carboxylic acid ester compound, the lithium salt is uniformly dissolved in the fluorine-containing solvent (α). Further, by the cyclic carboxylic acid ester compound, the non-aqueous electrolyte solution is made less reactive with the positive electrode and the negative electrode, and thermal runaway in the secondary battery is made less likely to occur. Further, when the cyclic carboxylic acid ester compound is used, as compared with a cyclic carbonate compound such as ethylene carbonate, the lithium salt solubility when used in combination with the fluorine-containing solvent (α) tends to be high, the proportion of the fluorine-containing solvent (α) in the non-aqueous electrolyte solution tends to be high and as a result, a non-aqueous electrolyte solution excellent in the frame retardance tends to be obtained.
As the cyclic carboxylic acid ester compound, one type may be used alone, or two or more types may be used in combination.
The cyclic carboxylic acid ester compound is preferably a saturated cyclic carboxylic acid ester compound containing no carbon-carbon unsaturated bond in its molecule, in view of the stability against the oxidation-reduction reaction.
The ring structure in the cyclic carboxylic acid ester compound is preferably a 4- to 10-membered ring, more preferably a 4- to 7-membered ring from the viewpoint of the stability of the structure and the viscosity. From the viewpoint of availability, a 5- or 6-membered ring is further preferred, and a 5-membered ring is particularly preferred. Further, from the viewpoint of availability, the total number of carbon atoms in the cyclic carboxylic acid ester compound is preferably from 4 to 8, more preferably 4 to 6. Further, the cyclic carboxylic acid ester is preferably composed solely of carbon atoms, hydrogen atoms and oxygen atoms, and more preferably, the portion other than the ester bond represented by a —C(═O)—O— bond contained in the ring structure, is composed solely of carbon atoms and hydrogen atoms.
The ring structure of the cyclic carboxylic acid ester compound is preferably a ring structure having one ester bond in view of the viscosity.
The cyclic carboxylic acid ester compound may be a compound having at least one of hydrogen atoms in the straight chain alkylene group substituted by a substituent. The substituent may, for example, be a fluorine atom, a chlorine atom, an alkyl group, a fluorinated alkyl group or the like. The number of carbon atoms in the alkyl group is preferably 1 or 2, and the number of carbon atoms in the fluorinated alkyl group is preferably 1 or 2.
The cyclic carboxylic acid ester compound preferably contains the following compound (5), more preferably consists solely of the following compound (5), in view of the stability against the oxidation-reduction reaction, the stability of the structure and the viscosity.
wherein each of R7 to R12 which are independent of one another, is a hydrogen atom, a fluorine atom, a chlorine atom, a C1-2 alkyl group, a C1-2 fluorinated alkyl group, or a C2-3 alkyl group having at least one etheric oxygen atom, and n is an integer of from 0 to 3. R7 to R12 may be the same or different.
As R7 to R12, a hydrogen atom, a methyl group, an ethyl group or a fluorine atom is preferred, and a hydrogen atom, a methyl group or an ethyl group is more preferred, in view of the stability against the oxidation-reduction reaction, the viscosity and availability.
n is preferably 1 to 3, more preferably 1 in view of the viscosity and availability of the compound.
The compound (5) may, for example, be a cyclic ester compound such as γ-butyrolactone, γ-valerolactone, γ-hexanolactone, δ-valerolactone or ε-caprolactone, or a compound having at least one of hydrogen atoms bonded to carbon atoms forming the ring of such a cyclic ester compound substituted by a fluorine atom, a chlorine atom, a C1-2 alkyl group, a C1-2 fluorinated alkyl group or a C2-3 alkyl group having at least one etheric oxygen atom.
As the compound (5). at least one member selected from the group consisting of γ-butyrolactone, γ-valerolactone and ε-caprolactone, is preferred, and γ-butyrolactone is more preferred, from the viewpoint of availability and since the effect to prevent thermal runaway is high.
The liquid composition preferably further contains at least one compound (β) selected from the group consisting of a saturated cyclic carbonate compound, a saturated chain carbonate compound having no fluorine atom (hereinafter sometimes referred to as a non-fluorinated saturated chain carbonate compound), a saturated cyclic sulfone compound (excluding a lithium salt) and a phosphoric acid ester compound, whereby the solubility of the lithium salt and the ion conductivity will be excellent.
The saturated cyclic carbonate compound may, for example, be propylene carbonate (PC), ethylene carbonate (EC) or 4-fluoro-1,3-dioxolan-2-one (FEC).
The non-fluorinated saturated chain carbonate compound may, for example, be dimethyl carbonate (DMC), ethyl methyl carbonate (EMC) or diethyl carbonate (DEC).
The saturated cyclic sulfolane compound may, for example, be sulfolane or 3-methylsulfolane.
The phosphoric acid ester compound may, for example, be trimethyl phosphate, triethyl phosphate or tris(2,2,2-trifluoroethyl) phosphate.
The liquid composition preferably contains the non-fluorinated saturated chain carbonate compound. When the non-fluorinated saturated cyclic carbonate compound is contained, the viscosity of the non-aqueous electrolyte solution can be lowered, and the lithium ion diffusion coefficient of the non-aqueous electrolyte solution and the ion conductivity of the non-aqueous electrolyte solution tend to be high.
The non-aqueous electrolyte solution may contain other compounds (another solvent, additives, etc.) other than the lithium salt, the fluorine-containing solvent (α), the cyclic carboxylic acid ester compound and the compound (β) as the case requires within a range not to impair the effects of the present invention.
The non-aqueous electrolyte solution may contain another solvent other than the fluorine-containing solvent (α), the fluorine-containing cyclic carboxylic acid ester compound and the compound (β).
The non-aqueous electrolyte solution may contain known additives as the case requires in order to improve the functions of the non-aqueous electrolyte solution. Such additives may, for example, be overcharge-preventing agents, dehydrating agents, deoxidizing agents, property-improving assistants and surfactants.
The overcharge-preventing agents may, for example, be an aromatic compound (such as biphenyl, an alkyl biphenyl, terphenyl, a partially hydrated product of terphenyl, cyclohexylbenzene, t-butylbenzene, t-amylbenzene, diphenyl ether or dibenzofuran), a partially fluorinated product of such an aromatic compound (such as 2-fluorobiphenyl, o-cyclohexylfluorobenzene or p-cyclohexylfluorobenzene) and a fluorine-containing anisole compound (such as 2,4-difluoroanisole, 2,5-difluoroanisole or 2,6-difluoroanisole). As the overcharge-preventing agent, one type may be used alone, or two or more types may be used in combination.
The dehydrating agents may, for example, be molecular sieves, sodium sulfate, magnesium sulfate, calcium hydride, sodium hydride, potassium hydride, and lithium aluminum hydride. The liquid composition and another solvent to be used for the non-aqueous electrolyte solution are preferably ones which have been subjected to dehydration with such a dehydrating agent, followed by rectification. Otherwise, one which has been subjected only to dehydration with such a dehydrating agent without being subjected to rectification, may be used.
Property-improving assistants are to improve the cycle properties and capacity-maintaining properties after high temperature storage.
The property-improving assistants may, for example, be a saturated carbonate (such as vinylene carbonate, vinylethylene carbonate or 4-ethynyl-1,3-dioxlan-2-one), a sulfur-containing compound (such as ethylene sulfite, 1,3-propane sultone, 1,4-butane sultone, methyl methanesulfonate, busulfan, sulfolene, dimethylsulfone, diphenylsulfone, methylphenylsulfone, dibutyl disulfide, dicyclohexyl disulfide, tetramethylthiuram monosulfide, N,N-dimethylmethane sulfonamide or N,N-diethylmethane sulfonamide), a hydrocarbon compound (such as heptane, octane or cycloheptane), and a fluorine-containing aromatic compound (such as fluorobenzene, difluorobenzene or hexafluorobenzene). As the property-improving assistant, one type may be used alone, or two or more types may be used in combination.
Surfactants are to help impregnation of the non-aqueous electrolyte solution to the electrode assembly or to separators.
The surfactants may be cationic surfactants, anionic surfactants, non-ionic surfactants or amphoteric surfactants, but anionic surfactants are preferred, since they are readily available and their surface activities are high. Further, as the surfactants, fluorine-containing surfactants are preferred, since their oxidizing resistance is high, and their cycle properties and rate properties are good. As the surfactants, one type may be used alone, or two or more types may be used in combination.
The upper limit value for the content of the lithium salt in the non-aqueous electrolyte solution is not particularly limited and is preferably 1.5 mol/L, more preferably 1.4 mol/L, further preferably 1.3 mol/L. The lower limit value for the content of the lithium salt in the non-aqueous electrolyte solution is non particularly limited, and is preferably 0.7 mol/L, more preferably 0.8 mol/L, further preferably 0.9 mol/L.
When calculated by mass, the ratio of the mass of the lithium salt to the total mass of the non-aqueous electrolyte solution is preferably from 5 to 20 mass %, more preferably from 7 to 17 mass %, further preferably from 9 to 14 mass %.
When the ratio of the lithium salt is at least the lower limit value, the ion conductivity of the non-aqueous electrolyte solution tends to be high. When the ratio of the lithium salt is at most the upper limit value, the lithium salt is readily soluble uniformly in the liquid composition, and even under a low temperature condition, the lithium salt is less likely to be precipitated. Further, the lithium ions are likely to be diffused in the non-aqueous electrolyte solution, and the lithium ion diffusion coefficient tends to be high.
The non-aqueous electrolyte solution of the present invention contains at least LiPF6 as the lithium salt. The molar ratio of LiPF6 based on the total number of moles of the lithium salt contained in the non-aqueous electrolyte solution is preferably from 40 to 100 mol %, more preferably from 50 to 100 mol %, further preferably from 65 to 100 mol %, particularly preferably from 80 to 100 mol %. When the molar ratio of LiPF6 based on the total number of moles of the lithium salt is at least the lower limit value, a highly practical non-aqueous electrolyte solution excellent in the ion conductivity tends to be obtained.
The ratio of the mass of the fluorine-containing solvent (α) to the total mass of the non-aqueous electrolyte solution is not particularly limited, however, the lower limit value for the ratio of the mass of the fluorine-containing solvent (α) to the total mass of the non-aqueous electrolyte solution is preferably 30 mass %, more preferably 40 mass %, further preferably 45 mass %. The upper limit value for the ratio of the fluorine-containing solvent (α) is preferably 80 mass %, more preferably 75 mass %, further preferably 73 mass %, particularly preferably 70 mass %.
When the ratio of the fluorine-containing solvent (α) is at least the lower limit value, the obtainable non-aqueous electrolyte solution is excellent in flame retardance, has low positive electrode reactivity and negative electrode reactivity, is less likely to undergo thermal runaway and has a high level of high voltage resistance property. When the ratio of the fluorine-containing solvent (α) is at most the upper limit value, the lithium salt can easily be uniformly dissolved, and the lithium salt is less likely to be precipitated at a low temperature.
The ratio of the mass of the fluorine-containing solvent (α) to the total mass of the liquid composition is preferably from 30 to 90 mass %, more preferably from 35 to 85 mass %, further preferably from 40 to 80 mass %, particularly preferably from 45 to 75 mass %.
When the ratio of the fluorine-containing solvent (α) is at least the lower limit value, the non-aqueous electrolyte solution is excellent in the flame retardance, has low positive electrode reactivity and negative electrode reactivity, is less likely to undergo thermal runaway and has a high level of high voltage resistance property. When the ratio of the fluorine-containing solvent (α) is at most the upper limit value, the lithium salt can easily be uniformly dissolved, and the lithium salt is less likely to be precipitated at a low temperature.
The fluorine-containing solvent (α) preferably contains the fluorine-containing ether compound, whereby high solubility of the lithium salt, and flame retardance and the ion conductivity of the non-aqueous electrolyte solution will be achieved.
The ratio of the mass of the fluorine-containing ether compound to the total mass of the fluorine-containing solvent (α) is preferably from 25 to 100 mass %, more preferably from 30 to 100 mass %, further preferably from 50 to 100 mass %, particularly preferably from 60 to 100 mass %, most preferably from 70 to 100 mass %. The fluorine-containing solvent (α) most preferably consists solely of the fluorine-containing ether compound.
The ratio of the mass of the fluorine-containing ether compound to the total mass of the non-aqueous electrolyte solution is preferably from 10 to 80 mass %. The lower limit value for the ratio of the fluorine-containing ether compound is more preferably 20 mass %, further preferably 30 mass %, particularly preferably 45 mass %. Further, the upper limit value for the ratio of the fluorine-containing ether compound is more preferably 75 mass %, further preferably 73 mass %, particularly preferably 70 mass %.
In a case where the fluorine-containing solvent (α) contains the fluorine-containing chain carboxylic acid ester compound, the ratio of the mass of the fluorine-containing chain carboxylic acid ester compound to the total mass of the fluorine-containing solvent (α) is preferably from 0.01 to 50 mass %, more preferably from 0.01 to 40 mass %, further preferably from 0.01 to 30 mass %, particularly preferably from 0.01 to 20 mass %.
In a case where the fluorine-containing solvent (α) contains the fluorine-containing chain carbonate compound, the ratio of the mass of the fluorine-containing chain carbonate compound to the total mass of the fluorine-containing solvent (α) is preferably from 0.01 to 50 mass %, more preferably from 0.01 to 40 mass %, further preferably from 0.01 to 30 mass %, particularly preferably from 0.01 to 20 mass %.
When the fluorine-containing solvent (α) contains the fluorine-containing alkane compound, the ratio of the mass of the fluorine-containing alkane compound to the total mass of the non-aqueous electrolyte solution is preferably from 0.01 to 5 mass %.
When the ratio of the fluorine-containing alkane compound is at least 0.01 mass %, the non-aqueous electrolyte solution will be excellent in the flame retardance. When the ratio of the fluorine-containing alkane is at most 5 mass %, the solubility of the lithium salt tends to be maintained.
In a case where as the fluorine-containing solvent (α), the fluorine-containing ether compound and at least one member selected from the group consisting of the fluorine-containing chain carboxylic acid ester, the fluorine-containing chain carbonate compound and the fluorine-containing alkane compound are used in combination, their ratio may optionally be set.
The ratio of the mass of the cyclic carboxylic acid ester compound to the total mass of the non-aqueous electrolyte solution is preferably from 4 to 50 mass %, more preferably from 7 to 45 mass %, further preferably from 10 to 40 mass %, particularly preferably from 15 to 35 mass %.
When the ratio of the cyclic carboxylic acid ester compound is at least the lower limit value, the non-aqueous electrolyte solution is capable of uniformly dissolving the lithium salt, has low positive electrode reactivity and negative electrode reactivity, and is less likely to undergo thermal runaway. When the ratio of the cyclic carboxylic acid ester compound is at most the upper limit value, the non-aqueous electrolyte solution is excellent in the flame retardance.
The ratio of the mass of the cyclic carboxylic acid ester to the total mass of the liquid composition is preferably from 4 to 60 mass %, more preferably from 7 to 50 mass %, further preferably from 10 to 45 mass %, particularly preferably from 15 to 40 mass %.
When the ratio of the cyclic carboxylic acid ester is at least the lower limit value, the liquid composition is excellent in the solubility, has low positive electrode reactivity and negative electrode reactivity, is less likely to undergo thermal runaway, and has a high level of high voltage resistance property. When the ratio of the cyclic carboxylic acid ester is at most the upper limit value, the liquid composition is excellent in the flame retardance.
In the non-aqueous electrolyte solution, NA/NLi, i.e. the ratio of the total number of moles NA of the cyclic carboxylic acid ester compound to the total number of moles NLi of lithium atoms derived from the lithium salt, is not particularly limited, and is preferably from 1.5 to 7.0. The lower limit value for such NA/NLi is more preferably 2, further preferably 2.5, particularly preferably 3. Further, the upper limit value for such NA/NLi is preferably 6.5, more preferably 6, further preferably 5, particularly preferably 4.5, most preferably 4.2.
When such NA/NLi is within the above range, while the lithium salt is uniformly dissolved to obtain a sufficient ion conductivity, the reactivity of the non-aqueous electrolyte solution with the positive electrode and the negative electrode can be reduced, and thermal runaway of a secondary battery can be suppressed, from the following reasons.
It is estimated that when the non-aqueous electrolyte solution is used for a secondary battery, particularly on a positive electrode, the cyclic carboxylic acid ester compound forms a stable coating film on an electrode active material, the coating film inhibits the reaction of the electrode and the non-aqueous electrolyte solution and thus suppresses thermal runaway.
It is considered that when such NA/NLi is at least the lower limit value, the non-aqueous electrolyte solution contains the cyclic carboxylic acid ester compound sufficiently, and thus the coating film is sufficiently formed to sufficiently suppress the reaction of the electrode with the non-aqueous electrolyte solution, thereby to sufficiently suppress thermal runaway. Further, the cyclic carboxylic acid ester compound is considered to have high affinity with the lithium salt and to promote dissolution of the lithium salt in the solvent. When such NA/NLi is at least the lower limit value, the lithium salt tends to be sufficiently dissolved in the solvent, whereby an electrolyte solution having a practically sufficient ion conductivity tends to be obtained.
Here, the fluorine-containing compound such as the fluorine-containing ether compound, the fluorine-containing chain carboxylic acid ester compound or the fluorine-containing chain carbonate compound is considered to have a low affinity with the lithium salt, and tends to have a very low effect to promote dissolution of the lithium salt in a solvent.
The coating film formed on the electrode active material is considered to be easily soluble in a highly polar solvent, and it is estimated that in a highly polar solvent, the coating film is dissolved even if formed, and thus formation of the coating film tends to be insufficient.
It is considered that when such NA/NLi is at most the upper limit value, the content of the cyclic carboxylic acid ester compound in the non-aqueous electrolyte solution will not be too high, the polarity of the entire non-aqueous electrolyte solution will be within an appropriate range, and thus the coating film formed on the electrode active material is less likely to be dissolved. It is considered that a sufficient coating film is maintained on the electrode active material, whereby an exothermal reaction by the electrode and the non-aqueous electrolyte solution is less likely to occur and thus thermal runaway is less likely to occur.
Further, the fluorine-containing compound such as the fluorine-containing ether compound, the fluorine-containing chain carboxylic acid ester compound or the fluorine-containing chain carbonate compound is considered to have a very low effect to dissolve the coating film since it has a low polarity. Further, by the low content of the flammable cyclic carboxylic acid ester, the flame retardance of the non-aqueous electrolyte solution will improve.
In a case where the liquid composition contains the compound (β), the ratio of the mass of the compound (β) to the total mass of the non-aqueous electrolyte solution is preferably from 0.01 to 30 mass %, more preferably from 0.1 to 20 mass %.
When the ratio of the compound (β) is at most the upper limit value, the reaction of the compound (β) and the electrode tends to be suppressed, and a non-aqueous electrolyte solution excellent in the stability will be obtained. Further, the content of the fluorine-containing solvent (α) can be increased, whereby a non-aqueous electrolyte solution excellent in the flame retardance tends to be obtained.
In a case where the liquid composition contains the saturated cyclic carbonate compound, the ratio of the mass of the saturated cyclic carbonate compound to the total mass of the non-aqueous electrolyte solution is preferably from 0.01 to 20 mass %, more preferably from 0.01 to 15 mass %, further preferably at least 0.01 mass % and less than 10 mass %, particularly preferably from 0.01 to 5 mass %.
When the ratio of the saturated cyclic carbonate compound is at most the upper limit value, the saturated cyclic carbonate compound is less likely to be reacted with the electrode, the non-aqueous electrolyte solution tends to be excellent in the stability and be excellent in the flame retardance.
In a case where the liquid composition contains the non-fluorinated saturated chain carbonate compound, the ratio of the mass of the non-fluorinated saturated chain carbonate compound to the total mass of the non-aqueous electrolyte solution is preferably from 0.01 to 30 mass %, more preferably from 0.01 to 20 mass %, further preferably from 0.01 to 15 mass %.
When the ratio of the non-fluorinated saturated chain carbonate compound is at most the upper limit value, the non-fluorinated saturated chain carbonate compound is less likely to be reacted with the electrode, and the non-aqueous electrolyte solution tends to be excellent in the stability and be excellent in the flame retardance.
In a case where the liquid composition contains the saturated cyclic carbonate compound and the non-fluorinated saturated chain carbonate compound, the ratio of the sum of the mass of the saturated cyclic carbonate compound and the mass of the non-fluorinated saturated chain carbonate compound to the total mass of the non-aqueous electrolyte solution is preferably from 0.01 to 30 mass %, more preferably from 0.01 to 15 mass %.
When the ratio of the sum of the masses is at most the upper limit value, even when the saturated cyclic carbonate compound and the non-fluorinated saturated chain carbonate compound are used, dissolution of the coating film of the cyclic carboxylic acid ester compound by a high polarity of solvent can be suppressed, the reactivity with the electrode can be suppressed, and a non-aqueous electrolyte solution having an excellent stability tends to be obtained. Further, the content of the flammable compounds can be suppressed, whereby a non-aqueous electrolyte solution having excellent flame retardance tends to be obtained.
In a case where the liquid composition contains a saturated cyclic sulfone compound, the ratio of the mass of the saturated cyclic sulfone compound to the total mass of the non-aqueous electrolyte solution is preferably from 0.01 to 20 mass %, more preferably from 0.01 to 15 mass %, further preferably from 0.01 to 10 mass %, particularly preferably from 0.01 to 5 mass %.
When the ratio of the saturated cyclic sulfone compound is at most the upper limit value, the saturated cyclic sulfone compound is less likely to be reacted with the electrode, the non-aqueous electrolyte solution tends to be excellent in the stability and be excellent in the flame retardance.
In a case where the liquid composition contains the phosphoric acid ester compound, the ratio of the mass of the phosphoric acid ester compound to the total mass of the non-aqueous electrolyte solution is preferably from 0.01 to 5 mass %.
When the ratio of the phosphoric acid ester compound is at most the upper limit value, the phosphoric acid ester compound is less likely to be reacted with the electrode, and the non-aqueous electrolyte solution tends to be excellent in the stability and be excellent in the flame retardance.
When the liquid composition contains the compound (β), the ratio of the mass of the cyclic carboxylic acid ester compound to the total mass of the cyclic carboxylic acid ester compound and the compound (β) is preferably from 30 to 100 mass %, more preferably from 35 to 100 mass %, further preferably from 40 to 100 mass %, still more preferably from 45 to 100 mass %, particularly preferably from 50 to 100 mass %.
When the ratio of the cyclic carboxylic acid ester compound is within the above range, the reactivity of the non-aqueous electrolyte solution with the positive electrode and the negative electrode can be reduced, and thermal runaway of a secondary battery can be suppressed.
In a case where the liquid composition contains the compound (β), (NA+NB)/NLi, i.e. the ratio of the sum of the total number of moles NA of the cyclic carboxylic acid ester compound and the total number of moles NB of the compound (β) to the total number of moles NLi of lithium atoms derived from the lithium salt is preferably from 3.0 to 7.0. The lower limit value for such (NA+NB)/NLi is more preferably 3.2, further preferably 3.5. Further, the upper limit value for such (NA+NB)/NLi is more preferably 6.5, further preferably 6, particularly preferably 5.5, most preferably 4.5.
The compound (β) is considered to have a high affinity with the lithium salt and to have an effect to promote dissolution of the lithium salt in a solvent, in the same manner as the cyclic carboxylic acid ester compound. When such (NA+NB)/NLi is at least the lower limit value, that is, the total amount of the compound (β) and the cyclic carboxylic acid ester compound considered to have a high effect to promote dissolution of the lithium salt is at a certain level or more relative to the amount of the lithium salt, solubility of the lithium salt in the fluorine-containing solvent (α) improves and thus the ion conductivity of the non-aqueous electrolyte solution improves, and particularly in a case where the lithium salt such as LiPF6 which is hardly soluble in the fluorinated solvent can be soluble in the fluorinated solvent, and practically sufficient ion conductivity tends to be obtained.
When the solvent has a high polarity, the coating film of the cyclic carboxylic acid ester compound formed on the electrode active material is dissolved, and formation of the coating film tends to be insufficient. The compound (β) is considered to have an effect to dissolve the coating film since it has a high polarity. When such ((NA+NB)/NLi is at most the upper limit value, that is, the total content of the compound (β) and the cyclic carboxylic acid ester compound having an effect to dissolve the coating film is at a certain level or less relative to the lithium salt, it is considered that the solubility of the coating film is low and formation of the coating film is less likely to be insufficient. Accordingly, it is estimated that the reactivity of the non-aqueous electrolyte solution with the positive electrode and the negative electrode tends to be lower, and thermal runaway of a secondary battery is less likely to occur. Further, the contents of the flammable cyclic carboxylic acid ester compound and the compound (β) in the non-aqueous electrolyte solution are reduced, whereby the flame retardance of the non-aqueous electrolyte solution will improve.
Particularly by using the lithium salt containing LiPF6 and by adjusting NA/NLi and (NA+NB)/NLi to be within the above ranges, a non-aqueous electrolyte solution having both practically sufficient ion conductivity and excellent stability with which thermal runaway is less likely to occur, tends to be obtained.
In a case where the non-aqueous electrolyte solution contains another solvent, the ratio of the sum of the mass of such another solvent and the sum of the compound (β) to the total mass of the non-aqueous electrolyte solution is preferably from 0.01 to 30 mass %, more preferably from 0.1 to 20 mass %. When the ratio of the sum of the mass of another solvent and the mass of the compound (β) is at most the upper limit value, the reaction of such another solvent and the compound (β) with the electrode is easily suppressed, and a non-aqueous electrolyte solution excellent in the stability will be obtained. Further, the content of the fluorine-containing solvent (α) can be increased, whereby a non-aqueous electrolyte solution excellent in the flame retardance tends to be obtained.
In a case where the non-aqueous electrolyte solution contains as another solvent a nitrile compound, the ratio of the mass of the nitrile compound to the total mass of the non-aqueous electrolyte solution is preferably at most 10 mass %, more preferably at most 5 mass %, further preferably at most 3 mass %, whereby a non-aqueous electrolyte solution which has lower reactivity with the positive electrode and the negative electrode and which is less likely to undergo thermal runaway tends to be obtained.
In a case where the non-aqueous electrolyte solution contains as another solvent an ether compound having no fluorine atom, the ratio of the mass of the ether compound having no fluorine atom to the mass of the non-aqueous electrolyte solution is preferably at most 10 mass %, more preferably at most 5 mass %, further preferably at most 3 mass %, particularly preferably at most 1 mass %, whereby a non-aqueous electrolyte solution which has lower reactivity with the positive electrode and the negative electrode and which is less likely to undergo thermal runaway tends to be obtained.
In a case where the non-aqueous electrolyte solution contains an overcharge-preventing agent, the ratio of the mass of the overcharge-preventing agent to the total mass of the non-aqueous electrolyte solution is preferably from 0.01 to 5 mass %.
When the ratio of the overcharge-preventing agent is within the above range, it becomes easier to prevent breakage or ignition of the secondary battery by overcharge, whereby the secondary battery can be used more safely.
In a case where the non-aqueous electrolyte solution contains a property-improving assistant, the ratio of the mass of the property-improving assistant to the total mass of the non-aqueous electrolyte solution is preferably from 0.01 to 5 mass %.
In a case where the non-aqueous electrolyte solution contains a surfactant, the ratio of the mass of the surfactant to the total mass of the non-aqueous electrolyte is preferably from 0.05 to 5 mass %, more preferably from 0.05 to 3 mass %, further preferably from 0.05 to 2 mass %.
The above-described non-aqueous electrolyte solution of the present invention is flame retardant since it contains the fluorine-containing solvent (α).
Further, in the above described non-aqueous electrolyte solution of the present invention, the lithium salt is uniformly dissolved in the fluorine-containing solvent, since the non-aqueous electrolyte solution contains the cyclic carboxylic acid ester compound although it contains the fluorine-containing solvent (α) in which a lithium salt is hardly soluble and contains LiPF6 which is very hardly soluble in the fluorine-containing solvent (α). In addition, the lithium ion diffusion coefficient of the non-aqueous electrolyte solution at 25° C. is at least 1.1×10−10 m2/s, whereby a lithium ion secondary battery excellent in the rate properties can be obtained.
The lithium ion secondary battery of the present invention comprises a positive electrode, a negative electrode and the non-aqueous electrolyte solution of the present invention.
The positive electrode may be an electrode wherein a positive electrode layer containing a positive electrode active material, a conductivity-imparting agent and a binder, is formed on a current collector.
The positive electrode active material may be any material so long as it is capable of absorbing and desorbing lithium ions. As the positive electrode active material, known positive electrode active material for conventional lithium ion secondary batteries may be employed. For example, a lithium-containing transition metal oxide, a lithium-containing transition metal composite oxide using at least one transition metal, a transition metal oxide, a transition metal sulfide, a metal oxide or an olivine type metal lithium salt may be mentioned. As the positive electrode active material, one type may be used alone, or two or more types may be used in combination.
The lithium-containing transition metal oxide may, for example, be lithium cobalt oxide, lithium nickel oxide or lithium manganese oxide.
As a metal for the lithium-containing transition metal composite oxide, Al, V, Ti, Cr, Mn, Fe, Co, Li, Ni, Cu, Zn, Mg, Ga, Zr, Si or Yb is, for example, preferred. The lithium-containing transition metal composite oxide may, for example, be lithium cobalt composite oxide such as (LiCoO2), lithium nickel composite oxide such as (LiNiO2), lithium manganese composite oxide (such as LiMnO2, LiMn2O4, Li2MnO3), a lithium ternary composite oxide such as Li(NiaCobMnc)O2 (wherein a, b, c≧0, a+b+c=1) or one having a part of the transition metal atom which mainly constitutes such a lithium transition metal composite oxide substituted by another metal such as Al, Ti, V, Cr, Mn, Fe, Co, Li, Ni, Cu, Zn, Mg, Ga, Zr, Si or Yb.
The lithium-containing transition metal composite oxide may, for example, be specifically LiMn0.5Ni0.5O2, LiMn1.8Al0.2O4, LiNi0.85Co0.10Al0.05O2, LiMn1.5Ni0.5O4, LiNi1/3Co1/3Mn1/3O2 or LiMn1.8Al0.2O4.
The transition metal oxide may, for example, be TiO2, MnO2, MoO3, V2O5, or V6O13.
The transition metal sulfide may, for example, be TiS2, FeS or MoS2.
The metal oxide may, for example, be SnO2 or SiO2.
The olivine type metal lithium salt is a substance represented by the formula LiLXxYyOzFg (wherein X is Fe(II), Co(II), Mn(II), Ni(II), V(II) or Cu(II), Y is P or Si, and L, x, y, z and g are, respectively, 0≦L≦3, 1≦x≦2, 1≦y≦3, 4≦z≦12 and 0≦g≦1) or a composite thereof.
The olivine type metal lithium salt may, for example, be specifically LiFePO4, Li3Fe2(PO4)3, LiFeP2O7, LiMnPO4, LiNiPO4, LiCoPO4, Li2FePO4F, Li2MnPO4F, Li2NiPO4F, Li2CoPO4F, Li2FeSiO4, Li2MnSiO4, Li2NiSiO4 or Li2CoSiO4.
Such a positive electrode active material having on its surface an attached substance having a composition different from the substance constituting the positive electrode active material as the main component may also be used. The surface-attached substance may, for example, be an oxide (such as aluminum oxide, silicon oxide, titanium oxide, zirconium oxide, magnesium oxide, calcium oxide, boron oxide, antimony oxide or bismuth oxide), a sulfate (such as lithium sulfate, sodium sulfate, potassium sulfate, magnesium sulfate, calcium sulfate or aluminum sulfate), or a carbonate (such as lithium carbonate, calcium carbonate or magnesium carbonate).
The amount of the surface-attached substance to the positive electrode active material is preferably at least 0.1 mass ppm and at most 20 mass %, more preferably at least 1 mass ppm and at most 10 mass %, particularly preferably at least 10 mass ppm and at most 5 mass %. By the surface-attached substance, it is possible to suppress an oxidation reaction of the non-aqueous electrolyte solution at the surface of the positive electrode active material and thereby to improve the battery life.
The positive electrode active material is preferably a lithium-containing composite oxide having an α-NaCrO2 structure as matrix (such as LiCoO2, LiNiO2 or LiMnO2) or a lithium-containing composite oxide having a spinel structure as matrix (such as LiMn2O4) since its discharge voltage is high and its electrochemical stability is high.
The conductivity-imparting agent may, for example, be a carbon material, a metal material (such as Al) or a powder of a conductive oxide.
The binder may, for example, be a resin binder (such as polyvinylidene fluoride) or a rubber binder (such as hydrocarbon rubber or fluorine-containing rubber).
The current collector may be a thin metal film composed mainly of e.g. Al.
The negative electrode may be an electrode wherein a powdery negative electrode layer containing a negative electrode active material, a conductivity-imparting agent and a binder, is formed on a current collector. In a case where the negative electrode active material can maintain the shape by itself (e.g. a thin lithium metal film), the negative electrode may be formed solely of the negative electrode active material.
The negative electrode active material may be at least one member selected from the group consisting of lithium metal, a lithium alloy and a carbon material capable of absorbing and desorbing lithium ions.
The lithium alloy may, for example, be a Li—Al alloy, a Li—Pb alloy or a Li—Sn alloy.
The carbon material may, for example, be graphite, coke or hard carbon.
As the binder and conductivity-imparting agent for the negative electrode, ones equal to those for the positive electrode may be used.
The current collector may be a thin metal film composed mainly of e.g. Cu.
Between the positive electrode and the negative electrode, a separator is interposed in order to prevent short circuiting. Such a separator may, for example, be a porous film. In such a case, the non-aqueous electrolyte solution is used as impregnated to the porous film. Further, such a porous film having the non-aqueous electrolyte solution impregnated and gelated, may be used as a gel electrolyte.
As the porous film, one which is stable against the non-aqueous electrolyte solution and is excellent in the liquid-maintaining property, may be used. The porous film is preferably a porous sheet or a non-woven fabric.
The material of the porous film may, for example, be a fluororesin (such as polyvinylidene fluoride, polytetrafluoroethylene or a copolymer of ethylene and tetrafluoroethylene), a polyimide, or a polyolefin (such as polyethylene or polypropylene), and is preferably a polyolefin in view of the oxidation resistance, air permeability, availability, etc.
The material for a battery exterior package may, for example, be nickel-plated iron, stainless steel, aluminum or its alloy, nickel, titanium, a resin material, or a film material.
The shape of the lithium ion secondary battery may be selected depending upon the particular application, and it may be a coin-form, a cylindrical form, a square form or a laminate form. Further, the shapes of the positive electrode and the negative electrode may also be suitably selected to meet with the shape of the secondary battery.
The charging voltage of the lithium ion secondary battery of the present invention is preferably at least 3.4 V, more preferably at least 4.0 V, further preferably at least 4.2 V. In a case where the positive electrode active material is a lithium-containing transition metal oxide, a lithium-containing transition metal composite oxide, a transition metal oxide, a transition metal sulfide or a metal oxide, the charging voltage is preferably at least 4.0 V, more preferably at least 4.2 V. In a case where the positive electrode active material is an olivine type metal lithium salt, the charging voltage is preferably at least 3.2 V, more preferably at least 3.4 V.
The above-described lithium ion secondary battery of the present invention, which employs the non-aqueous electrolyte solution of the present invention, is excellent in the rate properties. Further, since it employs the frame-retardant non-aqueous electrolyte solution of the present invention, it can be used safely.
Now, the present invention will be described in detail with reference to Examples, but it should be understood that the present invention is by no means restricted by the following description. Ex. 1 to 13 are Examples of the present invention, and Ex. 14 to 19 are Comparative Examples.
The viscosity was measured by a BM rotational viscometer (manufactured by Toki Sangyo Co., Ltd., RE215H) with No. 1 rotor at a number of revolutions of 300 rpm at 25° C.
The lithium ion diffusion coefficient was calculated by pulsed field gradient NMR method. For pulsed field gradient NMR measurement, ECA-600 manufactured by JEOL RESONANCE Inc. was used. The self-diffusion coefficient D in pulsed field gradient NMR method is given from the attenuation of the signal intensity I due to a change of the application conditions of pulsed field gradient as follows.
ln(I/I(0))=−Dγ2G2δ2(Δ−δ/3)
In the above formula, I(0) is the NMR peak intensity when the magnetic field gradient intensity (G)=0T, and γ, G, δ and Δ are respectively the gyromagnetic ratio of the lithium nucleus, the magnetic field gradient intensity, the magnetic field gradient pulse width and the diffusion time. Measurement was carried out with a pulse sequence of BPP-STE, with a magnetic field gradient pulse width (δ) of 6 ms for a diffusion time (Δ) of 0.1 second while the magnetic field gradient intensity (G) was changed in 12 stages from 0.05 to 0.7 T. The magnetic field gradient pulse intensity G was fine-tuned for each sample. The measurement temperature was 25° C. The sample was put into a symmetrical micro sample tube manufactured by SHIGEMI into a height of 7 mm in a glove box and subjected to measurement.
Artificial graphite (9.1 g) and carbon black (manufactured by Denki Kagaku Kogyo Kabushiki Kaisha, 0.80 g) as an electrically conductive material were mixed and stirred at a rotational speed of 2,000 rpm for one minute by means of a planetary centrifugal mixer (Awatorirentaro AR-E310, manufactured by Thinky Corporation). Then, a step of adding a 2 mass % carboxymethyl cellulose aqueous solution (9.0 g), followed by stirring at a rotational speed of 2,000 rpm for 5 minutes by means of the above mixer, was repeated twice. Then, a styrene-butadiene rubber aqueous dispersion latex binder (0.26 g) having a solid content concentration adjusted to 40 mass %, was added, followed by stirring at a rotational speed of 2,000 rpm for 5 minutes by means of the above mixer to obtain a slurry for forming an electrode.
On a copper foil having a thickness of 20 μm, the above slurry was applied in a thickness of 150 μm and dried, followed by punching out in a circular shape having a diameter of 16 mm to obtain an electrode (negative electrode) for evaluation.
A step of mixing LiCoO2 (manufactured by AGC Seimi Chemical Co. Ltd., 32.0 g) and carbon black (manufactured by Denki Kagaku Kogyo Kabushiki Kaisha, 0.80 g), followed by stirring at a rotational speed of 2,000 rpm for 30 seconds by means of a planetary centrifugal mixer (Awatorirentaro AR-E310, manufactured by Thinky Corporation), was repeated 3 times. Then, a step of adding N-methyl-2-pyrrolidone (6.0 g), followed by stirring at a rotational speed of 2,000 rpm for 5 minutes by means of the above mixer, was repeated 4 times. Then, a step of adding N-methyl-2-pyrrolidone (0.8 g), followed by stirring at a rotational speed of 2,000 rpm for 3 minutes by means of the above mixer, was repeated 3 times. Further, an N-methyl-2-pyrrolidone solution of polyvinylidene fluoride (11 mass %, 7.45 g) was added, followed by stirring at a rotational speed of 2,000 rpm for one minute by means of the above mixer to obtain a slurry. On an aluminum foil having a thickness of 20 μm, the slurry was applied and dried, followed by punching out in a circular shape having a diameter of 15 mm to obtain an electrode (positive electrode) for evaluation.
The positive electrode and the negative electrode were disposed to face each other, between the electrodes, a polyolefin type porous membrane was interposed as an electrode separator for evaluation, and the non-aqueous electrolyte solution having 2 wt % vinylene carbonate added to the non-aqueous electrolyte solution (0.1 mL) having a composition as defined in Tables 1 to 4 was used to prepare a 2032 coin cell comprising LiCoO2 electrode-graphite electrode. The non-aqueous electrolyte solution in Ex. 16, which contained vinylene carbonate, was used without addition of vinylene carbonate.
The obtained cell was charged to 3.4 V at a constant current corresponding to 0.01 C at 25° C. and further charged to 4.2 V at a current corresponding to 0.2 C, and further, charged until the current value at the charging lower limit voltage became a current corresponding to 0.02 C. Thereafter, discharging to 3.0 V was carried out at a current corresponding to 0.2 C. In each of cycles 2 to 5, charging to 4.2 V was carried out at a current corresponding to 0.2 C, and further, charging was carried out until the current value at the charging lower limit voltage became a current corresponding to 0.02 C. Thereafter, discharging to 3.0 V was carried out at a current corresponding to 0.2 C. In cycle 6, charging to 4.2 V was carried out at a current corresponding to 0.2 C, and further, charging was carried out until the current value at the charging lower limit voltage became a current corresponding to 0.02 C. Thereafter, discharging to 3.0 V was carried out at a current corresponding to 0.1 C. In cycles 7 to 11, charging was carried out at the same sequence as in cycle 6, and discharging to 3.0 V was carried out at a current corresponding to 0.1 C in cycle 7, 0.2 C in cycle 8, 0.5 C in cycle 9, 1.0 C in cycle 10, and 2.0 C in cycle 11.
The rate properties were evaluated by the average discharge voltage in cycle 11 and the retention rate of the discharge capacity in cycle 11 to the discharge capacity in cycle 8 (hereinafter sometimes referred to as the capacity retention rate).
A step of mixing artificial graphite (4.25 g) and acetylene black (0.15 g) as an electrically conductive material, followed by stirring at a rotational speed of 2,000 rpm for one minute by means of a planetary centrifugal mixer (Awatorirentaro AR-E310, manufactured by Thinky Corporation), was repeated 3 times. Then, a step of adding a 1 mass % carboxymethyl cellulose aqueous solution (4.25 g), followed by stirring at a rotational speed of 2,000 rpm for 5 minutes by means of the above mixer, was repeated twice. Further, a 1 mass % carboxymethyl cellulose aqueous solution (4.25 g) was added, followed by stirring at a rotational speed of 2,000 rpm for 10 minutes by means of the above mixer. Then, a styrene-butadiene rubber aqueous dispersion latex binder (0.13 g) having a solid content concentration adjusted to 40 mass %, was added, followed by stirring at a rotational speed of 2,000 rpm for 5 minutes by means of the above mixer to obtain a slurry for forming an electrode.
On a copper foil having a thickness of 20 μm, the above slurry was applied in a thickness of 150 μm and dried, followed by punching out in a circular shape having a diameter of 19 mm to obtain an electrode (negative electrode) for evaluation.
A negative electrode prepared by the above method was used as an electrode for evaluation, and a lithium metal foil punched into a circular shape having a diameter of 19 mm was used as a counter electrode. Between the electrodes, a polyolefin porous membrane was interposed as a separator. Further, a non-aqueous electrolyte solution having vinylene carbonate added at a concentration of 2 mass % to 0.5 mL of a carbonate non-aqueous electrolyte solution (a non-aqueous electrolyte solution having LiPF6 dissolved at a concentration of 1.0 mol/L in a mixture of ethylene carbonate and ethyl methyl carbonate in a mass ratio of 3:7, manufactured by KISHIDA CHEMICAL Co., Ltd.) was added to prepare a single electrode cell comprising graphite electrode-lithium metal foil.
The obtained single electrode cell was subjected to the following charge/discharge cycles.
In cycle 1, at 25° C., constant current charging to 0.2 V (negative electrode) was carried out at a current corresponding to 0.04 C, constant current charging to 0.05 V was carried out at a current corresponding to 0.2 C, and further constant voltage charging was carried out until the current value at the charging lower limit voltage became a current corresponding to 0.02 C. Thereafter, constant current discharging to 1.0 V was carried out at a current corresponding to 0.2 C. In cycles 2 to 4, constant current charging to 0.05 V was carried out at a current corresponding to 0.2 C, and further, constant voltage charging was carried out until the current value at the charging lower limit voltage became a current corresponding to 0.02 C. Thereafter, constant current discharging to 1.0 V was carried out at a current corresponding to 0.2 C. In cycle 5, constant current charging to 0.05 V was carried out at a current corresponding to 0.2 C. Then, the obtained single electrode cell in a charged state was disassembled in an argon atmosphere to obtain a negative electrode in a charged state. The obtained negative electrode was washed with dimethyl carbonate (2 mL) three times, vacuum dried and punched out into a circle having a diameter of 5 mm, which was put in a sealed vessel made of stainless steel (SUS), and 2 μL of the non-aqueous electrolyte solution obtained in each EX. was further put, followed by sealing to prepare an evaluation sample. Each of the obtained evaluation samples was subjected to measurement by a differential scanning calorimetry (manufactured by SII NanoTechnology Inc., DSC-6000) within a temperature range of from 50 to 350° C. at a temperature-raising rate of 5° C./min.
The negative electrode reactivity was evaluated based on “the exothermic peak temperature” and “the heating value at 200° C.”.
“The exothermic peak temperature” was a temperature at the peak top of the exothermic peak at the lowest temperature among exothermic peaks with a heating value exceeding 2,000 μW, when the heating amount at 60° C. in the above measurement was corrected to 0. The exothermic peak temperature was evaluated based on standards ⊙ (excellent): 200° C. or higher, ◯ (good): 180° C. or more and less than 200° C., Δ (poor): 150° C. or more and less than 180° C., and x (very poor): less than 150° C.
“The heating value at 200° C.” was the heating value (μW) at 200° C. when the heating amount at 60° C. in the above measurement was corrected to 0.
A step of mixing LiCoO2 (trade name: “Selion C”, manufactured by AGC Seimi Chemical Co. Ltd., 32.0 g) and carbon black (trade name: “Denka black”, manufactured by Denki Kagaku Kogyo K.K., 0.80 g), followed by stirring at a rotational speed of 2,000 rpm for one minute by means of a planetary centrifugal mixer (Awatorirentaro AR-E310, manufactured by Thinky Corporation), was repeated 3 times. Then, a step of adding N-methyl-2-pyrrolidone (7.50 g), followed by stirring at a rotational speed of 2,000 rpm for 3 minutes by means of the above mixer, was repeated 3 times. Then, a step of adding N-methyl-2-pyrrolidone (1.0 g), followed by stirring at a rotational speed of 2,000 rpm for 3 minutes by means of the above mixer, was repeated 3 times. Further, an N-methyl-2-pyrrolidone solution of polyvinylidene fluoride (11 mass %, 7.45 g) was added, followed by stirring at a rotational speed of 2,000 rpm for one minute by means of the above mixer to obtain a slurry. On an aluminum foil having a thickness of 20 μm, the above slurry was applied in a thickness of 150 μm and dried, followed by punching out in a circular shape having a diameter of 18 mm to obtain an electrode (positive electrode) for evaluation.
A positive electrode prepared by the above method was used as an electrode for evaluation, and a lithium metal foil punched into a circular shape having a diameter of 19 mm was used as a counter electrode. Between the electrodes, a polyolefin porous membrane was interposed as a separator. Further, 0.5 mL of a carbonate non-aqueous electrolyte solution (a non-aqueous electrolyte solution having LiPF6 dissolved at a concentration of 1.0 mol/L in a mixture of ethylene carbonate and ethyl methyl carbonate in a mass ratio of 3:7, manufactured by KISHIDA CHEMICAL Co., Ltd.) was added to prepare a single electrode cell comprising LiCoO2 electrode-lithium metal foil.
The obtained single electrode cell was subjected to the following charge/discharge cycles.
In cycles 1 to 4, constant current charging to 4.5 V was carried out at a current corresponding to 0.5 C, and further constant voltage charging was carried out until the current value at the charging lower limit voltage became a current corresponding to 0.02 C. Thereafter, constant current discharging to 3.0 V was carried out at a current corresponding to 0.2 C. In cycle 5, constant current charging to 4.5 V was carried out at a current corresponding to 0.5 C, and further, constant voltage charging was carried out until the current value at the charging lower limit voltage became a current corresponding to 0.02 C. Then, the obtained single electrode cell in a charged state was disassembled in an argon atmosphere to obtain a positive electrode in a charged state. The obtained positive electrode was washed with dim ethyl carbonate (2 mL) three times, vacuum dried and punched out into a circle having a diameter of 5 mm, which was put in a sealed vessel made of SUS, and 2 μL of the non-aqueous electrolyte solution obtained in each EX. was further put, followed by sealing to prepare an evaluation sample. Each of the obtained evaluation samples was subjected to measurement by a differential scanning calorimetry (manufactured by SII NanoTechnology Inc., DSC-6000) within a temperature range of from 50 to 350° C. at a temperature-raising rate of 5° C./min.
The positive electrode reactivity was measured based on “the exothermic peak temperature” and “the heating value at 200° C.” in the same manner as the evaluation of the negative electrode reactivity.
Compounds and abbreviations used in Examples are as follows.
LPF: LiPF6
LBF: LiBF4
AE3000: CF3CH2OCF2CHF2 (tradename: AE-3000, manufactured by Asahi Glass Company, Limited)
HFE458: CHF2CF2CH2OCF2CHF2
HFE5510: CHF2CF2CH2OCF2CHFCF3
MFA: methyl difluoroacetate
GBL: γ-butyrolactone
EC: ethylene carbonate
PC: propylene carbonate
DMC: dimethyl carbonate
DEC: diethyl carbonate
VC: vinylene carbonate
LPF (0.30 g) as a lithium salt was dispersed in HFE5510 (1.08 g) and AE3000 (0.61 g) as fluorine-containing ether compounds, and then, GBL (0.69 g) as a cyclic carboxylic acid ester compound and DMC (0.30 g) as a compound (β) were mixed to obtain a non-aqueous electrolyte solution 1.
The viscosity of the liquid composition, the lithium ion diffusion coefficient of the non-aqueous electrolyte solution and the rate properties of the lithium ion secondary battery are shown in Table 1. The negative electrode reactivity and the positive electrode reactivity are shown in Table 5.
A non-aqueous electrolyte solution was obtained in the same manner as in Ex. 1 except that the composition of the respective compounds such as the lithium salt was changed as identified in Tables 1 to 4. The viscosity of the liquid composition, the lithium ion diffusion coefficient of the non-aqueous electrolyte solution and the rate properties of the lithium ion secondary battery are shown in Tables 1 to 4. The negative electrode reactivity and the positive electrode reactivity are shown in Table 5.
The mass % in Tables 1 to 4 is a proportion based on 100 mass % of the entire non-aqueous electrolyte solution.
As shown in Tables 1 to 3, the lithium ion secondary battery in each of Ex. 1 to 13 which employed a non-aqueous electrolyte solution having a lithium ion diffusion coefficient of at least 1.0×10−10 m2/s was excellent in the rate properties.
Whereas as shown in Tables 3 and 4, the lithium ion secondary battery in each of Ex. 14 to 18 which employed a non-aqueous electrolyte solution having a lithium ion diffusion coefficient of less than 1.1×10−10 m2/s was inferior in the rate properties. Ex. 14 and 16 correspond to Example 14 in Patent Document 2.
Further, as shown in Table 5, the electrolyte solution in which the liquid composition contains at least one fluorine-containing solvent (α) selected from the group consisting of a fluorine-containing ether compound, a fluorine-containing chain carboxylic acid ester compound and a fluorine-containing chain carbonate compound, and a cyclic carboxylic acid ester compound, is excellent in the stability with a charging electrode. Particularly an electrolyte solution in which (NA+NB)/NLi i.e. the ratio of the sum of the total number of moles NA of the cyclic carboxylic acid ester compound and the total number of moles NB of the compound (β) to the total number of moles NLi of lithium atoms derived from the lithium salt is from 3.0 to 7.0, is remarkably excellent in the stability with the charging electrode.
The non-aqueous electrolyte solution of the present invention is useful as a non-aqueous electrolyte solution for lithium ion secondary batteries.
The lithium ion secondary battery of the present invention may be used in various applications to e.g. mobile phones, portable game devices, digital cameras, digital video cameras, electric tools, notebook computers, portable information terminals, portable music players, electric vehicles, hybrid cars, electric trains, aircrafts, satellites, submarines, ships, uninterruptible power supply systems, robots and electric power storage systems.
This application is a continuation of PCT Application No. PCT/JP2014/075134, filed on Sep. 22, 2014, which is based upon and claims the benefit of priority from Japanese Patent Application No. 2013-197587 filed on Sep. 24, 2013. The contents of those applications are incorporated herein by reference in their entireties.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013-197587 | Sep 2013 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2014/075134 | Sep 2014 | US |
| Child | 15008778 | US |