Non-chromate protective coating for iron and iron alloys and coating solution

Information

  • Patent Grant
  • 6582530
  • Patent Number
    6,582,530
  • Date Filed
    Thursday, September 5, 2002
    22 years ago
  • Date Issued
    Tuesday, June 24, 2003
    21 years ago
Abstract
A non-chromate protective coating and coating solution useful for coating iron and iron alloys, particularly steel, includes V2O5, Ce2(MoO4)3 or SrWO4 as a corrosion inhibitive component
Description




BACKGROUND OF THE INVENTION




The present invention relates to a non-chromate protective coating solution and a result coating composition particularly useful as a protective coating on iron and iron alloys.




Chromate-based high temperature aluminum coatings have been used to protect steel components such as, for example, compressor discs from high temperature and atmosphere corrosion damage. While the chromate based aluminum coatings are highly effective, such coatings have lost favor due to health concerns associated with the use of hexavalent chromium.




Naturally, it would be highly desirable to provide a non-chromate protective coating for metal, particularly iron and iron alloys including steel, which would meet industry demands with respect to high temperature and atmospheric corrosion damage protection.




SUMMARY OF THE INVENTION




Accordingly, it is an object of the present invention to provide a non-chromate protective coating for a metal substrate. It is a further object of the present invention to provide a non-chromate protective coating for iron and iron alloy substrates.




It is a still further object of the present invention to provide a non-chromate protective coating solution for forming the non-chromate protective coating.




The foregoing objects or advantages are attained by the present invention.




In accordance with the present invention, a non-chromate protective coating solution comprises from 25 to 75 wt. % H


2


O; from 10 to 20 wt. % H


3


PO


4


; from 2 to 10 wt. % MgO; from 10 to 50 wt. % Al; and from 0.5 to 10 wt. % of a metal oxide selected from the group consisting of V


2


O


5


, Ce


2


(MoO


4


)


3


and SrWO


4


. The non-chromate protective coating solution has a pH of between 2.5 to 5.0.




The resulting non-chromate protective coating comprises from 15 to 40 wt. % H


3


PO


4


; from 3 to 20 wt. % MgO; from 20 to 75 wt. % Al; and from 1.0 to 20 wt. % of a metal oxide selected from the group consisting of V


2


O


5


, Ce


2


(MoO


4


)


3


and SrWO


4


.




Other details of the non-chromate protective coating and coating solution of the present invention are set forth in the following detailed description and example.




DETAILED DESCRIPTION




The present invention relates to a non-chromate protective coating and coating solution particularly useful for coating iron and iron alloys, particularly steel. In accordance with the present invention, the non-chromate protective coating comprises from 15 to 40 wt. % H


3


PO


4


; from 3 to 20 wt. % MgO; from 20 to 75 wt. % Al; and from 1.0 to 20 wt. % of a metal oxide selected from the group consisting Of V


2


O


5


, Ce


2


(MoO


4


)


3


and SrWO


4


When V


2


O


5


is employed as the metal oxide, the preferred non-chromate protective coating comprises from 15 to 25 wt. % H


3


PO


4


; from 3 to 10 wt. % MgO; from 30 to 60 wt. % Al; an d from 1 to 5 wt. % V


2


O


5


. When the preferred metal oxide is Ce


2


(MoO


4


)


3


, the preferred non-chromate coating composition comprises from 13 to 20 wt. % H


3


PO


4


; from 3 to 10 wt. % MgO; from 35 to 70 wt. % Al; and from 7 to 20 wt. % Ce


2


(MoO


4


)


3


. When the preferred metal oxide is SrWO


4


, the preferred non-chromate protective coating composition comprises from 13 to 20 wt. % H


3


PO


4


; from 3 to 10 wt. % MgO; from 35 to 70 wt. % Al; and from 7 to 20 wt. % SrWO


4


. The non-chromate protective coating of the present invention is particularly useful for coating iron and iron alloys, particularly steel.




The non-chromate protective coating solution used to produce the protective coating of the present invention comprises from 25 to 75 wt. % H


2


O; from 5 to 20 wt. % H


3


PO


4


; from 2 to 10 wt. % MgO; from 10 to 50 wt. % Al; and from 0.5 to 10 wt. % of a metal oxide selected from the group consisting of V


2


O


5


, Ce


2


(MoO


4


)


3


and SrWO


4


. When V


2


O


5


is employed as the preferred metal oxide, the coating solution comprises from 50 to 75 wt. % H


2


O; from 10 to 14 wt. % H


3


PO


4


; from 2 to 5 wt. % MgO; from 15 to 35 wt. % Al; and from 0.5 to 2 wt. % V


2


O


5


. When Ce


2


(MoO


4


) 3 is employed as the preferred metal oxide, the protective coating solution comprises from 50 to 75 wt. % H


2


O; from 8 to 12 wt. % H


3


PO


4


; from 2 to 5 wt. % MgO; from 20 to 40 wt. % Al; and from 5 to 10 wt. % Ce


2


(MoO


4


)


3


. When SrWO4 is employed as the preferred metal oxide, the protective coating solution comprises from 50 to 75 wt. % H


2


O; from 8 to 12 wt. % H


3


PO


4


; from 2 to 5 wt. % MgO; from 20 to 40 wt. % Al; and from 5 to 10 wt. % SrWO


4


. It is preferred that the coating solutions have a pH of between about 2.5 to 5.0 preferably between about 3.0 to 4.0. The metal substrate is coated with the solution by processes well known in the art.











The effectiveness of the protective coatings in accordance with the present invention when compared to chromated coatings is demonstrated in the following example.




EXAMPLE




Four carbon steel panels were used as a substrate material. Prior to coating of the panels, each panel was grit blasted, rinsed with deionized water and dried. The coating mixtures were applied to one side of the panels by a paintbrush. The panels were allowed to air dry horizontally overnight. The panels were then additionally dried in an oven at 176° F. for thirty minutes and thereafter cured in a furnace at 625° F. for one hour.




One of the four panels was coated with a solution containing hexavalent chromium. The remaining three panels were coated with protective coating solutions in accordance with the present invention. The coating formulations are presented hereinbelow in Table 1 along with observations made during the preparation of the coating solutions.




















TABLE 1











Al












For-




H


3


PO


4






104




MgO




CrO


3






V


2


O


5






Ce(MoO


4


)


3






SrWO


4








mula




ml




g




g




g




g




g




g




pH











1




10.26




40.02




4.04




5.01







3.0






2




10.26




40.02




4.04





1.09






4.0






3




10.26




40.02




4.04






9.51





5.0






4




10.26




40.02




4.04







8.39




4.5














In order to test the corrosion resistance of the coated panels, a solution was prepared using a mixture of technical grade sulfuric and nitric acids in a volume ratio of 3:1 and diluted with deionized water to a pH of three. Sodium chloride was then added to the solution in an amount of 2500 ppm. The solution simulates a corrosive condensate found in certain service environments, such as those experienced by compressor discs. A diamond-tipped marking tool was used to scribe an “X” from corner to corner through the coating on each coupon. The scribed coupons were then submerged for 15 minutes in the test solution, air dried for one hour, and thereafter put in a furnace at 800° F. for two hours. Finally the coupons were placed for twenty hours in a desiccator at 100% humidity. This sequence was repeated and the coatings were evaluated after 5 test cycles. The observations are set forth hereinbelow in Table 2.















TABLE 2













Observations
















Quality of coating before




Coupons after 5 test




Coupon ratings






Formula




testing




cycles




(1 = best)









1




Smooth surface and consistent




No corrosion




1






(Cra


3


)




coating thickness






2




Smooth surface and consistent




No corrosion in the




2






(V


2


O


5


)




coating thickness




field. Some corrosion in








the lower part of one








scribe.






3




Smooth surface and consistent




No corrosion in the




3






(Ce


2


(MoO


4


)


3


)




coating thickness




field. Corrosion in the








lower part of the








scribes.






4




Smooth surface and consistent




No corrosion in the




3






(SrWO


4


)




coating thickness




field. Corrosion in the








lower part of the








scribes.














As can be seen from Table 2, V


2


O


5


preformed as the best non-chromated metal oxide. While Ce(MoO


4


)


3


and SrWO


4


did not perform to the level of V


2


O


5


, their performance was acceptable.




It is to be understood that the invention is not limited to the illustrations described and shown herein, which are deemed to be merely illustrative of the best modes of carrying out the invention, and which are susceptible of modification of form, size, arrangement of parts and details of operation. The invention rather is intended to encompass all such modifications which are within its spirit and scope as defined by the claims.



Claims
  • 1. A non-chromate protective coating solution comprising:from 25 to 75 wt. % H2O; from 5 to 20 wt. % H3PO4; from 2 to 10 wt. % MgO; from 10 to 50 wt. % Al; and from 0.5 to 10 wt. % of a metal oxide selected from the group consisting of V2O5, Ce2(MoO4)3 and SrWO4.
  • 2. A non-chromate protective coating solution according to claim 1 comprising:from 50 to 75 wt. % H2O; from 10 to 14 wt. % H3PO4; from 2 to 5 wt. % MgO; from 15 to 35 wt. % Al; and from 0.5 to 2 wt. % V2O5.
  • 3. A non-chromate protective coating solution according to claim 1 comprising:from 50 to 75 wt. % H2O; from 8 to 12 wt.% H3PO4; from 2 to 5 wt. % MgO; from 20 to 40 wt. % Al; and from 5 to 10 wt. % Ce2(MoO4)3.
  • 4. A non-chromate protective coating solution according to claim 1 comprising:from 50 to 75 wt. % H2O; from 8 to 12 wt. % H3PO4; from 2 to 5 wt. % MgO; from 20 to 40 wt. % Al; and from 5 to 10 wt. % SrWo4.
  • 5. A non-chromate protective coating solution according to one of claim 1, 2, 3 or 4 wherein the solution has a pH of between 2.5 to 5.0.
  • 6. A non-chromate protective coating solution according to one of claim 1, 2, 3 or 4 wherein the solution has a pH of between 3.0 to 4.0.
  • 7. A composite comprising a metal substrate coated with a non-chromate protective coating, said non-chromate protective coating comprising:from 15 to 40 wt. % H3PO4; from 3 to 20 wt. % MgO; from 20 to 75 wt. % Al; and from 1.0 to 20 wt. % of a metal oxide selected from the group consisting Of V2O5, Ce2(MoO4)3 and SrWO4.
  • 8. A composite according to claim 7, wherein said non-chromate protective coating comprising:from 15 to 25 wt. % H3PO4; from 3 to 10 wt. % MgO; from 30 to 60 wt. % Al; and from 1 to 5 wt. % V2O5.
  • 9. A composite according to claim 7, wherein said non-chromate protective coating comprising:from 13 to 20 wt. % H3PO4; from 3 to 10 wt. % MgO; from 35 to 70 wt. % Al; and from 7 to 20 wt. % Ce2(Mo04)3.
  • 10. A composite according to claim 7, wherein said non-chromate protective coating comprising:from 13 to 20 wt. % H3PO4; from 3 to 10 wt. % MgO; from 35 to 70 wt. % Al; and from 7 to 20 wt. % SrWO4.
  • 11. A composite according to one of claim 7, 8, 9 or 10, wherein said metal substrate is selected from the group consisting of iron and iron alloys.
US Referenced Citations (6)
Number Name Date Kind
4347085 Haselkorn et al. Aug 1982 A
5279649 Stetson et al. Jan 1994 A
5279650 Stetson et al. Jan 1994 A
5652064 Mosser et al. Jul 1997 A
5968240 Myers et al. Oct 1999 A
6368394 Hughes et al. Apr 2002 B1