Non-magnetic particles for non-magnetic undercoating layer of magnetic recording medium, non-magnetic undercoating layer containing the same, and magnetic recording medium having the undercoating layer

BACKGROUND OF THE INVENTION
The present invention relates to non-magnetic particles for a non-magnetic undercoating layer of a magnetic recording medium, a non-magnetic undercoating layer containing such non-magnetic particles, and a magnetic recording medium having such an undercoating layer.
With a development of miniaturized and lightweight video or audio magnetic recording and reproducing apparatuses for long-time recording, magnetic recording media such as a magnetic tape and magnetic disk have been strongly required to have a higher performance, namely, a higher recording density and to reduce the noise level.
Especially, video tapes are required to have a higher picture quality, and the frequencies of carrier signals recorded in recent video tapes are higher than those recorded in conventional video tapes. In other words, the signals in the shortwave region have come to be used, and as a result, the magnetization thickness (magnetization depth) from the surface of a magnetic tape has come to be remarkably small (shallow).
With respect to signals having a short wavelength, efforts have also been made to improve the high output characteristics, especially, the S/N ratio, as described in the following literature. For example, Development of magnetic Materials and Technique for High Dispersion of magnetic Powder, published by Kabushiki Kaisha Sogo Gijutsu Center (1982) described on page 74, " . . . in the recording and reproducing characteristics, technical problems in designing a magnetic coating layer so as to produce a high recording density by achieving various requirements in electromagnetic conversion property such as a reduction in the noise level, improvement of the S/N ratio, the sensitivity and the frequency characteristics, and a reduction in the output fluctuation, are (1) to improve the uniform dispersibility of magnetic particles and the magnetic orientation, (2) to increase the packing ratio of magnetic particles in a coating film and (3) to provide a coating film with an excellent surface smoothness and a uniform thickness . . . ", and on page 312, " . . . the conditions for high-density recording in a coating-type tape are that the noise level is low with respect to signals having a short wavelength and that the high output characteristics are maintained. To satisfy these conditions, it is necessary that the tape has large coercive force (Hc) and residual magnetization (Br), . . . and the coating film has a smaller thickness . . . ".
Development of a thinner film for a magnetic recording layer has caused some problems.
Firstly, it is necessary to make a magnetic recording layer smooth and to remove the non-uniformity of thickness thereof. As well known, in order to obtain a smooth magnetic recording layer having a uniform thickness, the surface of the base film must also be smooth. This fact is described on pages 180 and 181 of Material for Synthetic Technology-Causes of Abrasion of Magnetic Tape and Head Running System and Measures for Solving the Problem (hereinunder referred to as "Materials for Synthetic Technology)" (1987), published by the publishing department of Technology Information Center, " . . . the surface roughness of a hardened magnetic layer depends on the surface roughness of the base film (back surface roughness) so largely as to be approximately proportional, . . . since the magnetic layer is formed on the surface of the base film, the more smooth the surface of the base film is, the more uniform and larger head output is obtained and the more the S/N ratio is improved".
Secondly, a problem in the strength of a base film has been caused with a tendency of the reduction in the thickness of a base film in response to the demand for a thinner magnetic layer. This fact is described, for example, on page 77 of the above-described Development of Magnetic Materials and Technique for High Dispersion of Magnetic Powder, " . . . Higher recording density is a large problem assigned to the present magnetic tape. This is important in order to shorten the length of the tape so as to miniaturize a cassette and to enable long-time recording. For this purpose, it is necessary to reduce the thickness of a base film . . . . With the tendency of reduction in the film thickness, the stiffness of the tape also reduces to such an extent as to make smooth travelling in a recorder difficult. Therefore, improvement of the stiffness of a video tape both in the longitudinal direction and in the transverse direction is now strongly demanded . . . "
Thirdly, there is a problem of too large a light transmittance caused by ultra-fine magnetic particles and a thin magnetic recording layer. Travel of a magnetic recording medium such as a magnetic tape, especially, a video tape is stopped when the video deck detects a portion of the magnetic recording medium at which the light transmittance is large. If the light transmittance of the whole part of a magnetic recording layer is made large by the production of a thinner magnetic recording medium or the ultra-fine magnetic particles dispersed in the magnetic coating layer, it is difficult to detect the portion having a large light transmittance by a video deck. As a measure for reducing the light transmittance of the magnetic coating layer, carbon black or the like is added to the magnetic recording layer. It is, therefore, essential to add carbon black or the like to a magnetic coating layer in the present video tapes.
However, addition of non-magnetic particles such as carbon black not only impairs the enhancement of the recording density but also reduces the magnetization thickness from the surface of the magnetic tape. It is, therefore, unfavorable to add non-magnetic particles to a magnetic coating layer.
To solve this problem, a magnetic recording medium having a base film composed of a non-magnetic substrate and an undercoating layer containing non-magnetic particles has been proposed.
For example, Japanese Patent Application Laid-Open (KOKAI) No. 63-187418 (1988) proposes a magnetic recording medium comprising a non-magnetic substrate, at least one undercoating layer obtained by dispersing non-magnetic particles in a binder, and a magnetic coating layer obtained by dispersing ferromagnetic particles in a binder, wherein the ferromagnetic particles are ferromagnetic iron oxide particles, ferromagnetic cobalt-modified iron oxide particles or ferromagnetic alloy particles, the average major axis diameter of the ferromagnetic particles measured through a transmission electron microscope is less than 0.30 .mu.m and the crystalline size thereof by X-ray diffraction is less than 300 .ANG..
According to the specification thereof, the non-magnetic particles used for the undercoating layer are carbon black, graphite, titanium oxide, barium sulfate, ZnS, MgCO.sub.3, ZnO, CaO, .gamma.-iron oxide, tungsten disulfite, molybdenum disulfite, boron nitride, MgO, SnO.sub.2, SiO.sub.2, Cr.sub.2 O.sub.3, a-Al.sub.2 O.sub.3, SiC, cerium oxide, corundum, synthetic diamond, .alpha.-iron oxide, garnet, quartzite, silicon nitride, silicon carbide, molybdenum carbide, boron carbide, tungsten carbide, titanium carbide, tripoli, diatomaceous, dolomite or the like. Among these, inorganic particles such as carbon black, CaCO.sub.3, titanium oxide, barium sulfate, .alpha.-Al.sub.2 O.sub.3, .alpha.-iron oxide, .gamma.-iron oxide and polymer particles such as polyethylene particles are preferable. The particle diameter of such non-magnetic particles is 1 to 1000 m.mu. in the case of granular particles, and 100 m.mu. to 5.mu. in major axis diameter and 1 to 1000 m.mu. in minor axis diameter in the case of acicular particles.
However, as a result of examination of the above-described non-magnetic particles by the present inventors, it has been found that the surface smoothness and the strength are unsatisfactory not only when granular non-magnetic particles are used but also when acicular non-magnetic particles are used.
Japanese Patent Application Laid-Open (KOKAI) No. 4-167225 (1992) proposes a magnetic recording medium produced by forming a magnetic coating layer on the surface of a non-magnetic substrate through an undercoating layer which contains acicular particles having an aspect ratio of more than 3.0 in a resin binder hardened when irradiated with an electromagnetic wave such as radioactive rays and ultraviolet rays.
However, in the case of using acicular .alpha.-FeOOH particles, which are described as the acicular particles in examples thereof, since much crystal water is contained in the surfaces of acicular .alpha.-FeOOH particles, the conformity of the particles with a binder resin and a solvent is so poor that the desired dispersibility is not obtained.
Japanese Patent Application Laid-Open (KOKAI) No. 4-325915 (1992) proposes a magnetic recording medium produced by coating on a non-magnetic substrate with an undercoating layer at least containing non-magnetic particles and a binder, and coating on the undercoating layer in the moistened state with an upper magnetic coating layer containing ferromagnetic particles and a binder, wherein an aspect ratio of the non-magnetic particles is not less than 2.5, the thickness of the upper magnetic coating layer in the dried state is not more than 1 .mu.m and the average particle diameter of the ferromagnetic particles having the major axis diameter is not more than 0.3 .mu.m.
As examples of preferred acicular non-magnetic particles are exemplified non-magnetic metals such as Cu, Cr, Ag, Al, Ti and W and the oxides thereof such as Al.sub.2 O.sub.3 (.alpha.,.gamma.), Cr.sub.2 O.sub.3, .alpha.-ferrite, goethite, SiO.sub.2 (including glass), ZrO.sub.2, CeO.sub.2 and TiO.sub.2 (rutile, anatase), and as examples of scaly non-magnetic particles, graphite, mica, boron nitride, etc. are exemplified.
Even when acicular non-magnetic particles such as .alpha.-ferrite which are described in Japanese Patent Application Laid-Open (KOKAI) No. 4-325915 (1992) are used, it is difficult to obtain the desired dispersibility, so that the surface smoothness and the strength of such a magnetic medium having a non-magnetic undercoat layer are insufficient.
Use of coated .alpha.-Fe.sub.2 O.sub.3 is proposed in Japanese Patent Application Laid-Open (KOKAI) No. 62-295217 (1987). It discloses a magnetic recording medium comprising a substrate and a magnetic coating layer containing magnetic particles and a binder, wherein the magnetic coating layer contains .alpha.-Fe.sub.2 O.sub.3 particles which are coated with a compound containing at least one selected from the group consisting of Si, Cr and Al.
Use of coated .alpha.-Fe.sub.2 O.sub.3, however, not only impairs the improvement of the recording density in the same way as addition of non-magnetic carbon black, but also impairs the reduction in the thickness of the film. As described above, the magnetization thickness from the surface of the magnetic tape is reduced and the reduction in the thickness of the film is insufficient.
In addition, in Japanese Patent Application Laid-Open (KOKAI) No. 62-295217 (1987), there is no description of the formation of a non-magnetic undercoating layer on the non-magnetic substrate. Also, there is no description which motivates the addition of non-magnetic particles composed of .alpha.-Fe.sub.2 O.sub.3 particles which are coated with a compound containing at least one selected from the group consisting of Si, Cr and Al to a non-magnetic undercoating layer. In other words, there is no description which motivates a combination of Japanese Patent Application Laid-Open (KOKAI) Nos. 63-187418 (1988), 4-167225 (1992) and 4-325915 (1992). That is, Japanese Patent Application Laid-Open (KOKAI) No. 62-295217 (1987) describes the addition of coated .alpha.-Fe.sub.2 O.sub.3 particles to a magnetic coating layer only in order to provide the magnetic coating layer with an excellent wear resistance and an appropriate magnetic head-abrasive property.
Accordingly, non-magnetic particles which impart to an undercoating layer excellent properties such as an excellent surface smoothness and a high strength, a non-magnetic undercoating layer having an excellent surface smoothness and a high strength so as to provide such a magnetic recording medium and a magnetic recording medium having a small light transmittance, an excellent surface smoothness and a uniform thickness are now strongly demanded.
As a result of studies undertaken by the present inventors so as to achieve such demands, it has been found that by making non-magnetic particles obtained by coating acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles with at least one selected from the group consisting of an Al compound, a silane coupling agent, a titanate coupling agent, a aluminate coupling agent and a zirconate coupling agent, contain in a non-magnetic undercoating layer for a magnetic recording medium, it is possible to produce a magnetic recording medium which has a base film having a strength high enough as a base film for a magnetic recording medium and an excellent surface smoothness, and which has a small light transmittance, a high smoothness and a uniform thickness. On the basis of this finding, the present invention has been achieved.
SUMMARY OF THE INVENTION
It is an object of the present invention to provide non-magnetic particles which impart to a non-magnetic undercoating layer for a magnetic recording medium an excellent surface smoothness and a high strength.
It is another object of the present invention to provide a magnetic recording medium having a small light transmittance, an excellent smoothness and a uniform thickness.
In a first aspect of the present invention, there are provided non-magnetic particles for a non-magnetic undercoating layer of a magnetic recording medium, comprising acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with at least one selected from the group consisting of an Al compound, a silane coupling agent, a titanate coupling agent, an aluminate coupling agent and a zirconate coupling agent.
In a second aspect of the present invention, there is provided a non-magnetic undercoating layer for a magnetic recording medium, which is formed on a non-magnetic substrate, comprising non-magnetic particles composed of acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with at least one selected from the group consisting of an Al compound, a silane coupling agent, a titanate coupling agent, an aluminate coupling agent and a zirconate coupling agent; and a binder resin.
In a third aspect of the present invention, there is provided a magnetic recording medium comprising a base film composed of a non-magnetic substrate, and an undercoating layer formed on the non-magnetic substrate and containing non-magnetic particles which are composed of acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with at least one selected from the group consisting of an Al compound, a silane coupling agent, a titanate coupling agent, an aluminate coupling agent and a zirconate coupling agent, and a binder resin; and a magnetic coating layer containing magnetic particles and a binder resin.
DETAILED DESCRIPTION OF THE INVENTION
The precursor particles for the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles used in the present invention are acicular or spindle-shaped goethite particles generally produced by (1) a process of acicular goethite particles by oxidizing a suspension containing colloidal ferrous hydroxide particles and having a pH of not less than 11 which is obtained by adding not less than an equivalent of an alkali hydroxide solution to an aqueous ferrous salt solution, by passing an oxygen-containing gas thereinto at a temperature of not higher than 80.degree. C.; (2) a process of producing spindle-shaped goethite particles by oxidizing a suspension containing FeCO.sub.3 which is obtained by reacting an aqueous ferrous salt solution with an aqueous alkali carbonate solution, by passing an oxygen-containing gas thereinto; (3) a process of producing acicular goethite particles by oxidizing a ferrous salt solution containing colloidal ferrous hydroxide or a precipitate containing iron, obtained by adding less than an equivalent of an alkali hydroxide solution or an alkali carbonate solution to an aqueous ferrous salt solution, by passing an oxygen-containing gas thereinto to produce acicular goethite seed particles; adding not less than an equivalent of an alkali hydroxide solution to the aqueous ferrous salt solution containing the acicular goethite seed particles, and growing the acicular goethite seed particles by passing an oxygen-containing gas into the aqueous ferrous salt solution; and (4) a process of producing acicular or spindle-shaped goethite particles by oxidizing a ferrous salt solution containing colloidal ferrous hydroxide or a precipitate containing iron, obtained by adding less than an equivalent of an alkali hydroxide solution or an alkali carbonate solution to an aqueous ferrous salt solution, by passing an oxygen-containing gas thereinto to produce acicular goethite seed particles, and growing the acicular goethite seed particles in an acidic or neutral region. The thus obtained precursor particles are heated and dehydrated and if necessary, then heat-treated, thereby obtaining the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles according to the present invention. Also, the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles of the present invention are directly produced by oxidizing a solution containing FeCO.sub.3 passing an oxygen-containing gas (refer to Japanese Patent Application Laid-Open (KOKAI) Nos. 61-14138 (1986), 61-14138 (1981), 62-128927 (1982) and 62-128930 (1982)
Elements other than Fe such as Ni, Zn, P and Si which are generally added in order to enhance properties of the particles may be added during the reaction for producing the goethite particles.
By dehydrating the acicular or spindle-shaped goethite particles as the precursor particles at a temperature of 200.degree. to 500.degree. C. and heat-treating (annealing) the dehydrated particles, if necessary, at a temperature of 350.degree. to 800.degree. C., acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles are obtained.
There is no problem even if there is a sintering preventive such as P, Si, B, Zr and Sb on the surface of the acicular or spindle-shaped goethite particles.
By heat-treating (annealing) the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles at a temperature of 350.degree. to 800.degree. C., due to the heat-melting the surfaces of the particles, the pores in the surfaces of the dehydrated acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles are filled in, and a smooth surface is obtained.
The coated acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles in the present invention are obtained by dispersing the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles obtained by the above-mentioned process in a solution containing an Al compound to form a suspension, or by dispersing the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles in an aqueous solution to form a suspension and adding an Al compound to the suspension, while adjusting the pH so as to coat the surfaces of the particles with the Al compound, filtering, washing with water, drying, pulverizing, and further, if necessary, deaerating and consolidating, thereby obtaining the coated particles.
As the Al compound in the present invention, aluminum salts such as aluminum acetate, aluminum sulfate, aluminum chloride and aluminum nitrate and alkali aluminates such as soda aluminate are usable.
Also, the dehydrated (and annealed) acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles are coated with at least one coupling agent selected from the group consisting of a silane coupling agent, a titanate coupling agent, an aluminate coupling agent and a zirconate coupling agent. As a method of coating the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles with a coupling agent, there are (i) a dry process of adding a coupling agent as it is to the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles, and co-mixing the resultant mixture by a mixer which enables the whole amount of added coupling agent to be adsorbed on the surfaces of the particles, and (ii) a wet process such as a process of adding the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles and a coupling agent to a solution composed of water as a liquid dispersion medium, stirring the resultant mixture, adjusting the pH by adding an aqueous acid or alkali solution thereto and drying the mixture, and a process of adding the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles and a coupling agent to a solution composed of an organic solvent as a liquid dispersion medium, stirring the resultant mixture and drying the mixture.
As the mixer used in the present invention, Henschel mixer, ball mill, atomizer colloid mill, edge runner, Simpson mix muller, multimuller, Stotz mill, back flow mixer, Irich mill, wet pan mill, melanger, whirl mill and quick mill are usable.
The concentration of the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles dispersed in the liquid dispersion medium is 5 to 20 wt %. If the concentration exceeds 20 wt %, the viscosity of the suspension is too high for sufficient mixing and uniform surface treatment. On the other hand, if the concentration is less than 5 wt %, the amount of medium filtered is too large for industrial advantage.
In the case of using water as the liquid dispersion medium and a water-soluble titatnate coupling agent as the coupling agent, after the coupling agent is added in the form of an aqueous solution and the resultant dispersion is stirred, the pH thereof is adjusted to the range of 6.0 to 8.0 by adding an aqueous acid or alkali solution.
As the water-soluble titanate coupling agent, triethanol amine titanate chelate, lactic acid titanate chelate, and isopropyltri(N-aminoethyl.aminoethyl) titanate are usable.
As the aqueous solutions used for adjusting the pH, in case of an alkali region, aqueous acid solutions such as acetic acid, hydrochloric acid and sulfuric acid may be exemplified, and in case of an acidic region, aqueous alkali solutions such as NH.sub.4 OH, NaOH, KOH and Na.sub.2 CO.sub.3 may be exemplified.
Aqueous acetic acid solution and aqueous NH.sub.4 OH solution are preferable, because the pH adjuster does not remain on the surfaces of the particles after drying.
If the pH is less than 6.0, an acid radical sometimes unfavorably remains on the surface of the particles. If the pH exceeds 8.0, there is a fear of a titanate coupling agent being decomposed.
In the present invention, when an organic solvent is used as the liquid dispersion medium and at least one coupling agent selected from the group consisting of a silane coupling agent, a titanate coupling agent, an aluminate coupling agent and a zirconate coupling agent which are soluble to the organic solvent, is used, the adjustment of the pH is not necessary.
As examples of the silane coupling agent, the titanate coupling agent, the aluminate coupling agent and the zirconate coupling agent used when an organic solvent is used as the liquid dispersion medium, the following known coupling agents may be cited.
As the silane coupling agents, vinyltriethoxysilane, vinyltrimethoxysilane, vinyltrichlorosilane, vinyltris(.beta.-methoxyethoxy)silane, .gamma.-(methacryloxypropyl)trimethoxysilane, .gamma.-aminopropyltrimethoxysilane, N-.beta.-(aminoethyl).gamma.-aminopropyltrimethoxysilane, .beta.-(3,4epoxycyclohexyl)ethyl trimethoxysilane, .gamma.-glycidoxypropyltrimethoxysilane and .gamma.-mercaptopropyltrimethoxysilane may be exemplified.
As the titanate coupling agents, isopropyltristearoyl titanate, isopropyltris (dioctylpyrophosphate) titanate, isopropyltri (N-aminoethyl.aminoethyl)titanate, tetraoctylbis (ditridecyl phosphate) titanate, tetra (2-2-diallyloxymethyl-1-butyl)bis(ditridecyl)phosphate titanate, bis(dioctylpyrophosphate) oxyacetate titanate and bis(dioctylpyrophosphate) ethylenetitanate may be exemplified.
As the aluminate coupling agents, acetoalkoxyaluminum diisopropylate, aluminum diisopropoxymonoethyl acetoacetate, aluminumtrisethyl acetoacetate and aluminumtrisacetyl acetonate may be exemplified.
As the zirconate coupling agents, zirconiumtetrakis acetylacetonate, zirconiumdibuthoxybis acetylacetonate, zirconiumtetrakisethyl acetoacetate, zirconiumtributhoxymonoethyl acetoacetate and zirconiumtributhoxy acetoacetonate may be exemplified.
As the organic solvent, all organic solvents which can solve the coupling agent are usable. For example, alcohols such as methanol, ethanol and propanol, ketones such as methylethyl ketone, methylisobutyl ketone and cyclohexanone, aromatic hydrocarbons such as toluene, xylene and benzene, and esters such as methyl acetate, ether acetate, propyl acetate and butyl acetate are usable.
When two or more coupling agents are used for coating the particles, the order of addition is not restricted. They may also be added simultaneously.
The amount of Al compound added is 0.01 to 50.00 parts by weight, preferably 0.05 to 20.0 parts by weight, more preferably 0.1 to 10 parts by weight based on 100 parts by weight of acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles. If the amount is less than 0.01 part by weight, the dispersion thereof in the binder resin is insufficient, while the amount exceeding 50.00 parts by weight is unfavorable, because Al compounds floating outside the surfaces of the particles interact.
In the present invention, it is preferable to coat the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles with an aluminum compound, because when the coated acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles are dispersed in the binder resin for forming an undercoating layer, the conformity of the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles with the binder resin is good and the desired dispersibility is easy to obtain.
The amount of coupling agent added is 0.01 to 50 parts by weight, preferably 0.01 to 20 parts by weight, more preferably 0.05 to 10 parts by weight based on 100 parts by weight of acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles. If the amount is less than 0.01 part by weight, the advantages aimed at in the present invention are not obtained. Even if the amount exceeds 50 wt %, the advantages aimed at in the present invention are obtained, but since the amount of coupling agent treated is more than the amount corresponding to the adsorption by a monolayer, the advantage aimed at in the present invention become saturated.
The acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with the coupling agent may be subjected to a treatment such as deaeration, and the mixer such as those described in the dry process (i) is preferably used.
It is more preferable in the present invention to use as precursor particles acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with an Al compound when coating on acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles with a coupling agent.
It is also possible to coat on the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles with at least one selected from the group consisting of Si, P, Ti, Mn, Ni, Zn, Zr, Sn and Sb compounds together with an Al compound, or to coat on the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with Al compound, with at least one selected from the group consisting of Si, P, Ti, Mn, Ni, Zn, Zr, Sn and Sb compounds. The amount of compound which coats on the surface of the acicular or spindle-shaped (.alpha.-Fe.sub.2 O.sub.3 particles or the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with Al compound, is 0.01 to 50.00 parts by weight, preferably 0.05 to 20.0 parts by weight, more preferably 0.1 to 10.0 parts by weight based on 100 parts by weight of the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles or the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with Al compound. If the amount is less than 0.01 part by weight, the dispersion in the binder resin is insufficient, while the amount exceeding 50.00 parts by weight is unfavorable, because the compounds floating outside the surfaces of the particles interact. The total amount of the coating compounds such as Al, Si, P, Ti, Mn, Ni, Zn, Zr, Sn and Sb compounds in the coated acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles in the present invention is 0.01 to 50.0 wt %, preferably 0.05 to 20.0 wt % more preferably 0.1 to 10.0 wt %.
The average major axis diameter of the coated acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles in the present invention is 0.05 to 0.25 .mu.m, preferably 0.1 to 0.25 .mu.m, the minor axis diameter thereof is 0.010 to 0.035 .mu.m, preferably 0.015 to 0.030 .mu.m, the particle size distribution thereof in geometrical standard deviation is not more than 1.40, preferably not more than 1.39 and the aspect ratio (major axis diameter/minor axis diameter) thereof is 2 to 20 preferably 3 to 17.
If the average major axis diameter is less than 0.05 .mu.m, the dispersion in the binder is difficult. On the other hand, if the average major axis diameter exceeds 0.25 .mu.m, the particle size is so large as to impair the surface smoothness.
If the average minor axis diameter is less than 0.010 .mu.m, the dispersion in the binder is unfavorably difficult. On the other hand, if the average minor axis diameter exceeds 0.035 .mu.m, the particle size is so large as to impair the surface smoothness.
If the particle size distribution in geometrical standard deviation exceeds 1.40, the coarse particles exert deleterious influence on the surface smoothness of the coated film.
If the aspect ratio is less than 2, it is difficult to provide the coated film with the desired strength. On the other hand, if the aspect ratio exceeds 20, the interaction between the particles increases so much as to exert deleterious influence on the dispersion.
As the binder resin in the present invention, resins which are at present generally used for the production of a magnetic recording medium are usable. For example, vinyl chloride-vinyl acetate copolymer, urethane resin, vinyl chloride-vinyl acetate-urethane maleate elastomer, butadiene-acrylonitrile copolymer, polyvinyl butyral, cellulose derivative such as nitrocellulose, polyester, synthetic rubber resin such as polybutadiene, epoxy resin, polyamide, polyisocyanate, electron radiation curing acryl urethane resin and mixtures thereof may be exemplified. Each of these resin binders may contain a polar group such as --OH, --COOH, --SO.sub.3 M, --OPO.sub.2 M.sub.2 and --NH.sub.2, wherein M represents H, Na or K.
A non-magnetic undercoating layer for a magnetic recording medium according to the present invention is obtained by forming a coating-film composition which contains coated acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles and a binder resin, on the surface of a non-magnetic substrate. The amount of non-magnetic particles in the undercoating layer is 65 to 95 wt %, preferably 70 to 90 wt %.
It is possible to add a lubricant, an abrasive, an antistatic agent, etc. which are generally used for the production of a magnetic recording medium, to the non-magnetic undercoating layer.
As the non-magnetic substrate, the following materials which are at present generally used for the production of a magnetic recording medium are usable. For example, a synthetic resin film such as polyethylene terephthalate, polyethylene, polypropylene, polycarbonate, polyethylene naphthalate, polyamide, polyamideimide and polyimide; film, foil and plate of a metal such as aluminum and stainless steel; and various kinds of paper may be exemplified. The thickness of the non-magnetic substrate is not restricted, but the thickness thereof is preferably 1 to 20 .mu.m.
The thickness of the undercoating layer obtained by coating on a non-magnetic substrate with a coating-film composition and drying the coating composition is 1 to 10 .mu.m, preferably 2 to 4 .mu.m. If the thickness is less than 1 .mu.m, not only it is impossible to improve the surface roughness of the base film composed of the non-magnetic substrate and the non-magnetic undercoating layer, but also the strength is insufficient. Even if the thickness exceeds 10 .mu.m, the desired properties are obtained, but in order to obtain a thin magnetic recording medium, it is preferable to forn an undercoating layer of not more than 10 .mu.m in thickness.
A magnetic recording medium of the present invention is obtained by forming a magnetic coating layer on the non-magnetic undercoating layer for a magnetic recording medium according to the present invention by coating the non-magnetic undercoating layer with a coating-film composition containing non-magnetic particles and a binder resin.
It is possible to add to the non-magnetic undercoating layer, a lubricant, an abrasive, an antistatic agent, etc. which are generally used for the production of a magnetic recording medium.
As the magnetic particles in the magnetic coating (recording) layer are usable magnetic oxide iron particles such as maghemite particles; magnetite particles; berthollide particles as an intermediate oxide of maghemite and magnetite; magnetic iron oxide particles containing an element(s) other than Fe such as Co, Al, Ni, P, Zn, Si and B; magnetic iron oxide particles obtained by coating the magnetic iron oxide particles containing other element(s) with Co, Co and Fe or the like; magnetic metal particles containing iron as the main ingredient; magnetic iron-based alloy particles containing elements other than iron such as Co, Al, Ni, P, Zn, Si, B or the like; plate-like Ba ferrite particles; and plate-like composite ferrite particles containing divalent metal such as Co, Ni and Zn and a quadrivalent metal such as Ti, Sn and Zr as coercive force reducing agents. The shape of the magnetic particles is not specified and, for example, acicular, spindle-shaped, cubic and plate-like particles are usable.
As the binder resin in the magnetic recording layer, the same resin as that used in the formation of the undercoating layer may be used. The thickness of the magnetic coating layer is 0.1 to 4.0 .mu.m, preferably 0.2 to 2.5 .mu.m.
The non-magnetic undercoating layer for a magnetic recording medium according to the present invention is excellent in the surface smoothness and the strength, so that it is possible to obtain a thin magnetic recording layer having a small light transmittance, an excellent surface smoothness and a uniform thickness when a magnetic recording medium is produced by sandwiching the non-magnetic undercoating layer composed of a coating-film composition containing non-magnetic particles and a binder resin, between the non-magnetic substrate and magnetic coating layer.
The reason why the non-magnetic undercoating layer for a magnetic recording medium according to the present invention is excellent in the surface smoothness and the strength is as follows.
It is possible to orient the acicular or spindle-shaped particles at the time of coating, on the surface of a non-magnetic substrate, and the oriented acicular or spindle-shaped particles make the light transmittance of the coating layer small, and enhance the surface smoothness and the strength thereof, as described on p. 339 of Materials for Synthetic Technology, " . . . Pigment particles such as acicular-shaped .alpha.-Fe.sub.2 O.sub.3 particles which are regarded as rod-like particles, are oriented in parallel to the surface of a substrate when coated with the pigment particles in such a manner that a shearing force is applied thereto . . . The rod-like particles which are oriented parallel to the surface of the substrate have larger hiding power and gloss, and smaller light or gas transmittance than rod-like particles which are oriented vertical to the surface of the substrate. The difference in the orientation of the pigment particles also influences the mechanical properties of the coating film. That is, the closer to the horizontal orientation to the surface of the substrate, the higher the strength is and the smaller the elongation is."
However, the dispersibility of the acicular or spindle-shaped particles is a problem, as described on p. 343 of Materials for Synthetic Technology, " . . . If the dispersibility of the magnetic particles is poor, not only is the surface smoothness deteriorated but also the orientation is influenced so that the magnetic characteristics are deteriorated . . . "
As a result of examination of various non-magnetic acicular or spindle-shaped particles which can enhance the surface smoothness and the strength, it is considered by the present inventors that by using the same iron oxide particles as the magnetic particles used in the magnetic recording layer as the non-magnetic particles for the undercoating layer for a magnetic recording medium, the conformity with a binder resin is enhanced when coated on the base film, and that the adhesiveness and the durability are also increased. For this reason, acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles are selected as the non-magnetic particles.
However, since it is impossible to obtain a sufficient orientation, an excellent surface smoothness or an adequate strength by coating on the non-magnetic substrate with a composition obtained by dispersing acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles in a resin binder, various studies have been undertaken in order to make acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles which are easy to disperse in the binder resin. As a result, it has been found that the desired properties are obtained by using acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with at least one selected from the group consisting of an Al compound, a silane coupling agent, a titanate coupling agent, an aluminate coupling agent and a zirconate coupling agent.
Namely, the dispersibility of the thus-obtained coated non-magnetic acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles in the coating-film composition is improved, and when the non-magnetic substrate is coated with the coating-film composition, the mechanical orientation on the non-magnetic substrate is smooth, so that the non-magnetic undercoating layer for a magnetic recording medium obtained has an excellent surface smoothness and a high strength.
That is, such a good result is obtained because the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with an Al compound and/or the above-described coupling agent improves the conformity with the binder resin and, hence, the dispersibility and orientation. In addition, it is considered that since the surface activity of the coated non-magnetic acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles is reduced by the Al compound and/or the coupling agent present on the surfaces of the particles, the solvent present in the neighborhood of the surface of the particles is severable therefrom, and as a result, the solvent is sufficiently removed from the dried coating film and the amount of remaining carbon is reduced, which are considered to exert favorable influence on the surface smoothness and the strength.
It has also been found that in the case where the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles coated with an Al compound is further coated with the above-described coupling agent, more excellent advantages are obtained and the conformity with the binder resin is further improved.
The average major axis diameter of the non-magnetic particles in the present invention is 0.05 to 0.25 .mu.m, preferably 0.1 to 0.25 .mu.m; the average minor axis diameter is 0.010 to 0.035 .mu.m, preferably 0.015 to 0.030 .mu.m; the aspect ratio (average major axis diameter/average minor axis diameter) is 2 to 20, preferably 3 to 17; the particle size distribution thereof in geometrical standard deviation is not more than 1.40, preferably not more than 1.39; the BET specific surface area is not more than 70 m.sup.2 /g, preferably not more than 51.0 m.sub.2 /g; the specific resistance to filtration (.alpha.V) is not more than 10.sub.13 m/kg, preferably not more than 10.sub.12 m/kg; and the amount of carbon remaining after the solvent is removed is not more than 0.5 wt %, preferably not less than 0.45 wt %.
In the non-magnetic undercoating layer of the present invention, the gloss (45.degree.) of the coating film is not less than 160%, preferably not less than 165%; the surface roughness (Ra) is not more than 17 nm, preferably not more than 15 nm; and the Young's modulus (relative value) is not less than 100, preferably not less than 110.
In the magnetic recording medium of the present invention, the coercive force (Hc) is not less than 500 Oe, preferably not less than 600 Oe; the squareness is not less than 0.85, preferably not less than 0.87; the gloss (45.degree.) is not less than 170%, preferably not less than 175%; the surface roughness (Ra) is not more than 10 nm, preferably not more than 8 nm; the Youngg's modulus (relative value) is not less than 120, preferably not less than 125; and the linear absorption coefficient is not less than 1.15 .mu.m.sup.-1, preferably not less than 1.20 .mu.m.sup.-1.
The non-magnetic undercoating layer for a magnetic recording medium, which contains non-magnetic particles is excellent in the strength and the surface properties as a base film. Therefore, a magnetic recording medium having this non-magnetic undercoating layer has a small light transmittance, a smooth surface and a uniform thickness.
In addition, by coating the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles with the Al compound and/or the above-described coupling agent, the filtration properties after the coating and washing treatments are improved, so that the operability is greatly improved.

EXAMPLES
The present invention will now be described in more detail with reference to the following examples and comparative examples.
The average major axis diameter, the average minor axis diameter and the aspect ratio of the particles in each of the following examples and comparative examples are expressed by the average values measured in electron microphotographs.
The particle size distribution of the particles is expressed by the geometrical standard deviation (.sigma.g) obtained by the following method. The major axis diameters of 350 particles in an electron microphotograph of 120,000 magnification were measured. The actual major axis diameters of the particles and the number thereof were obtained from the calculation on the basis of the measured values. In logarithmico-normal probability paper, the major axis diameters are plotted at regular intervals on the abscissa-axis and the accumulative number of particles belonging to each interval of the major axis diameters was plotted by percentage on the ordinate-axis by a statistical technique. The major axis diameters corresponding to the number of particles of 50% and 84.13%, respectively, were read from the graph, and the geometrical standard deviation (.sigma.g) was measured from the following formula:
______________________________________Geometrical standard deviation (.delta.g) = (major axisdiameter (.mu.m) corresponding to the number of particlesof 50%) / (major axis diameter (.mu.m) corresponding to thenumber of particles of 84.13%)______________________________________
The specific surface area is expressed by the value measured by a BET method using HONOSORB MODEL MS, manufactured by Quanta Chroma Corp.
The amount of Al and the amount of each element with which the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles are coated were measured by fluorescent X-ray analysis using X-RAY SPECTROMETER No. 3134 manufactured by Rigaku Industries Corp.
The amount of removed solvent is expressed by the amount of remaining carbon (C). A sample powder was immersed adequately in a solvent (MEK), and thereafter the sample was dried at a temperature of 60.degree. C. for 24 hours. The amount of carbon (C) remaining in the dried sample powder was measured by quantitative analysis using "Carbon/Sulfur Analyzer EMIA-2200", manufactured by Kabushiki Kaisha Horiba Seisakusho. The smaller the amount of remaining carbon (C), the more preferable, because the strong interaction of the solvent is the smaller.
The amount of coupling agent with which the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles are coated, were calculated as C by measuring the carbon contained in the acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles by "Carbon/Sulfur Analyzer EMIA-2200", manufactured by Kabushiki Kaisha Horiba Seisakusho.
The gloss of the coating film was obtained by measuring the gloss at 45.degree. by "Glossmeter UGV-5D", manufactured by Suga Shikenki Co., Ltd.
The surface roughness (Ra) was expressed by the center-line average roughness of the profile curve of the surface of the coating film by using "Surfcom-575A", manufactured by Tokyo Seimitsu Co., Ltd.
The specific resistance of filtration (.alpha.V) is measured by a method described in "Manual of Filtration and Compression Techniques", published by Nikkan Kogyo Shinbunsha, pages 3-8.
Namely, the slurry of a temperature of 60.degree. C. and a concentration of 10 wt % was filtrated through a filter having a filtration area of about 123 cm.sup.2 under the filtration pressure of -500 mmHg (absolute pressure: 260 mmHg) to obtain a filtrate of the viscosity of 0.5 cps and the density of 1 g/cm.sup.3 at a room temperature. From the relationship of the amount of the filtrate and the filtration time, the specific resistance of filtration (.alpha.V) was determined.
The strength of the coating film was obtained by measuring the Youngg's modulus by using "Autograph", manufactured by Shimazu Seisakusho Ltd. The Youngg's modulus in the present invention is expressed by a relative value based on the Youngg's modulus of the commercial video tape, AV T-120 (manufactured by Victor Company of Japan, Limited).
The magnetic characteristics were measured by using "Vibration Sample Magnetometer VSM-3S-15", manufactured by Toei Kogyo Kabushiki Kaisha and applying an external magnetic field up to 10 kOe.
The light transmittance of a magnetic sheet is expressed by the linear adsorption coefficient measured by using "Photoelectric Spectrophotometer UV-2100", manufactured by Shimazu Seisakusho Ltd. The linear adsorption coefficient is defined by the following formula, and the larger the value, the more difficult it is for the magnetic sheet to transmit light.
______________________________________Linear Adsorption Coefficient (.mu.m.sup.-1) = 1 n (1/t)FT(wherein t is a light transmittance (%) at .lambda. = 900non-magnetic, and FT is a thickness (.mu.m) of the coating-filmcomposition of the film used for the measurement)______________________________________
If the linear adsorption coefficient is not less than 1.2 (film thickness: 4.0 .mu.m), it satisfies the light transmittance of not more than 0.8% determined by the VHS standard.
<Production of acicular or spindle-shaped (.alpha.-Fe.sub.2 O.sub.3 >
Examples 1 to 22 and
Comparative Examples 1 to 8
Example 1
10 kg of spindle .alpha.-FeOOH particles (average major axis diameter: 0.21 .mu.m, average minor axis diameter: 0.021 .mu.m, aspect ratio: 10.0, BET specific surface area: 110.0 m.sup.2 /g) were charged into a retort with one end open, and heated and dehydrated at a temperature of 470.degree. C. for 60 minutes in air while the container was rotated. The particles were further annealed at a temperature of 650.degree. C. for 120 minutes, thereby obtaining spindle .alpha.-Fe.sub.2 O.sub.3 particles.
The thus-obtained spindle .alpha.-Fe.sub.2 O.sub.3 particles had an average major axis diameter of 0.15 .mu.m, an average minor axis diameter of 0.025 .mu.m and a BET specific surface area of 52.5 m.sup.2 /g.
The obtained spindle .alpha.-Fe.sub.2 O.sub.3 particles were then pulverized in a dry-process by an edge runner-type pulverizer (Sand mill, manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho). The pulverized particles were stirred and mixed in water and then pulverized in a wet-process by a line mill-type pulverizer (Homomic Line Mill, manufactured by Tokushukika Kogyo Kabushiki Kaisha), thereby obtaining a suspension containing the spindle .alpha.-Fe.sub.2 O.sub.3 particles.
After adding 1320 ml (corresponding to 1.78 parts by weight (calculated as Al) based on 100 parts by weight of the spindle .alpha.-Fe.sub.2 O.sub.3 particles) of aqueous aluminum sulfate solution of 2.5 mol/l to the suspension obtained, aqueous NaOH solution of 1 mol/l was added to adjust the pH to 6.0, and the resultant mixture was stirred for 30 minutes.
After the mixture was stirred, it was filtered, washed with water and dried by an ordinary method, and then compacted by an edge runner-type pulverizer (Sand mill, manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho).
The thus-obtained spindle .alpha.-Fe.sub.2 O.sub.3 particles coated with the Al compound had an average major axis diameter of 0.15 .mu.m, an average minor axis diameter of 0.026 .mu.m, an aspect ratio of 5.8, a particle size distribution in geometrical standard deviation of 1.35 and a BET specific surface area of 51.8 m.sup.2 /g. The pH of the particles was 6.3.
The filtration characteristic was evaluated by the time which took for obtaining 200 cc of the filtrate under a negative pressure of 50 cm Hg by using No. 5 filter paper having a filtration area of 122.7 cm.sup.2. The filtration time was 2.6 minutes.
Examples 2 to 22 and Comparative Examples 1 to 8
Acicular or spindle-shaped .alpha.-Fe.sub.2 O.sub.3 particles were produced in the same way as in Example 1 except for varying the kind of particles to be coated, the kind and the amount of Al compound added, the kind and the amount of other compound added and the pH of the suspension.
The particles obtained in Examples 1 to 3 and 8 to 16 were spindle .alpha.-Fe.sub.2 O.sub.3 particles and the particles obtained in Examples 4 to 7 were acicular .alpha.-F.sub.2 O.sub.3 particles.
In Comparative Examples 5 and 6, spindle .alpha.-FeOOH particles were used as particles to be coated in place of spindle .alpha.-Fe.sub.2 O.sub.3 particles, and in Comparative Examples 7 and 8, spindle .alpha.-Fe.sub.2 O.sub.3 particles obtained by heat-treating magnetite particles were used as particles to be coated.
The main producing conditions and various properties of the products are shown in Tables 1 and 2.
<Production of non-magnetic undercoating layer for magnetic recording medium>
Examples 23 to 44 and Comparative Examples 9 to 16
Examples 23
The coated spindle .alpha.-Fe.sub.2 O.sub.3 particles obtained in Example 1 were first mixed with a binder resin and a solvent so that the solid content was 75 wt %, and the resultant mixture was kneaded for 30 minutes by a Brabender Plasti-corder. Thereafter, a predetermined amount of kneaded product was taken out and charged into a glass bottle together with glass beads and a solvent. The mixture was stirred and dispersed for 6 hours by a paint conditioner.
The final composition of the non-magnetic paint obtained was as follows:
______________________________________Al-coated spindle .alpha.-Fe.sub.2 O.sub.3 particles 100 parts by weightVinyl chloride-vinyl acetate copolymer 10 parts by weighthaving a sodium sulfonate groupPolyurethane having a carboxyl group 10 parts by weightCyclohexanone 40.9 parts by weightMethyl ethyl ketone 102.2 parts by weightToluene 61.3 parts by weight______________________________________
The non-magnetic paint obtained was applied to polyethylene terephthalate film having a thickness of 14 .mu.m so as to have a thickness of 55 .mu.m by using an applicator, and dried to obtain a sheet-like specimen.
The sheet-like specimen had a Young's modulus of 121, a gloss of 182% and a surface roughness (Ra) of 11.2 nm.
Examples 24 to 44 and Comparative Examples 9 to 16
Non-magnetic undercoating layers for a magnetic recording medium were produced in the same way as in Example 23 by using the acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particles obtained in Examples 2 to 22 and Comparative Examples 1 to 8 and acicular or spindle .alpha.-FeOOH particles obtained in Comparative Examples 5 and 6, respectively.
Various properties of the products are shown in Tables 5 and 6.
<Production of magnetic tape>
Examples 45 to 50 and Comparative Examples 17 to 20
Example 45
Co-coated magnetic iron oxide particles (average major axis diameter: 0.20 .mu.m, average minor axis diameter: 0.029 .mu.m, aspect ratio: 6.8, particle size distribution in geometrical standard deviation: 1.38, BET specific surface area: 48.2 m.sup.2 /g) were first mixed with a binder resin and a solvent so that the solid content was 76 wt %, an the resultant mixture was kneaded for 30 minutes by a Brabender Plasti-corder. Thereafter, a predetermined amount of kneaded product was taken out and charged into a glass bottle together with glass beads and a solvent. The mixture was stirred and dispersed for 6 hours by a paint conditioner.
Thereafter, an abrasive, a lubricant and a hardener were added thereto, and the resultant mixture was further stirred and dispersed for 15 minutes. The magnetic paint obtained was as follows:
______________________________________Co-coated magnetic iron oxide particles 100 parts by weightVinyl chloride-vinyl acetate copolymer 10 parts by weighthaving a sodium sulfonic acid groupPolyurethane having a sodium sulfonate 10 parts by weightgroupAbrasive 10 parts by weightLubricant 2.5 parts by weightHardener 5 parts by weightCyclohexanone 52.2 parts by weightMethyl ethyl ketone 130.5 parts by weightToluene 78.3 parts by weight______________________________________
The magnetic paint obtained was applied to the undercoat layer formed thereon in Example 23 so as to have a thickness of 15 .mu.m by using an applicator and dried to obtain a sheet-like sample.
The sheet-like sample was calendered, and cured at a temperature of 60.degree. C. for 24 hours. The sheet-like sample was then slit to a width of 0.5 inch to obtain a magnetic tape.
The magnetic tape obtained had a coercive force (Hc) of 889 Oe, a squareness of 0.89, a gloss of 178%, a surface roughness (Ra) of 6.0 nm, a Young's modulus of 133, and a linear adsorption coefficient of 1.21.
Examples 46 to 50 and Comparative Examples 17 to 20
Magnetic recording media were produced in the same way as in Example 45 by using the undercoating layers for a magnetic recording medium obtained in Examples 23, 30 and 43 and Comparative Examples 9 and 14.
Various properties of the products are shown in Table 7.
<Production of acicular or spindle .alpha.-F.sub.2 O.sub.3 >
Sample Productions 1 to 20
Sample Production 1
10 kg of spindle .alpha.-FeOOH particles (average major axis diameter: 0.21 .mu.m, average.minor axis diameter: 0.021 .mu.m, aspect ratio: 10.0, BET specific surface area: 110.0 m.sup.2 /g) were charged into a retort with one end open, and heated and dehydrated at a temperature of 470.degree. C. for 60 minutes in air, while the container was rotated. The particles were further annealed at a temperature of 650.degree. C. for 120 minutes, thereby obtaining spindle .alpha.-Fe.sub.2 O.sub.3 particles.
The thus-obtained spindle .alpha.-Fe.sub.2 O.sub.3 particles had an average major axis diameter of 0.14 .mu.m, an average minor axis diameter of 0.025 .mu.m and a BET specific surface area of 52.0 m.sup.2 /g.
Sample Productions 2 to 20
Acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particles were produced in the same way as Sample Production 1 except for varying the kind of particles to be coated.
The particles obtained in Sample Productions 1, 3 to 8 were spindle .alpha.-Fe.sub.2 O.sub.3 particles and the particles obtained in Sample Productions 2 and 9 to 12 were acicular .alpha.-Fe.sub.2 O.sub.3 particles.
In Sample Productions 17 and 18, acicular .alpha.-FeOOH particles were used as they are stand, and in Sample Productions 19 and 20, acicular .alpha.-Fe.sub.2 O.sub.3 particles obtained by heat-treating magnetite particles were used instead of acicular .alpha.-Fe.sub.2 O.sub.3 particles.
The main producing conditions and various properties of the products are shown in Tables 8 and 9.
<Coating of acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particles with Al compound etc.>
Examples 51 to 56 and Comparative Examples 21 and 22
Example 51
The spindle .alpha.-Fe.sub.2 O.sub.3 particles obtained as Sample Production 7 were then pulverized in a dry-process by an edge runner-type pulverizer (Sand mill, manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho). The pulverized particles were stirred and mixed in water and then pulverized in a wet process by a line mill-type pulverizer (Homomic Line Mill, manufactured by Tokushuki Kogyo Kabushikika Kaisha), thereby obtaining a suspension (slurry concentration: 100 g/l) containing the spindle .alpha.-Fe.sub.2 O.sub.3 particles.
After adding 463 ml (corresponding to 0.50 part by weight (calculated as Al) based on 100 parts by weight of the spindle .alpha.-Fe.sub.2 O.sub.3 particles) of an aqueous sodium aluminate solution having a concentration of 2 mol/l to the 50 l (corresponding to 5000 g calcuglated as dried particles) of the suspension obtained, an aqueous HCl solution having a concentration of 1 mol/l was added to adjust the pH to 7.0, and the resultant mixture was stirred for 30 minutes.
After the mixture was stirred, it was filtered, washed with water and dried by an ordinary method to obtain spindle .alpha.-Fe.sub.2 O.sub.3 particles coated with the Al compound.
The thus-obtained spindle .alpha.-Fe.sub.2 O.sub.3 particles coated with the Al compound had an average major axis diameter of 0.16 .mu.m, an average minor axis diameter of 0.025 .mu.m, an aspect ratio of 6.4, a particle size distribution in geometrical standard deviation of 1.34 and a BET specific surface area of 52.3 m.sup.2 /g. The pH of the powder was 7.5.
Examples 52 to 56 and Comparative Examples 21 and 22
Acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particles were produced in the same way as in Example 51 except for varying the kind of particles to be coated, the kind and the amount of Al compound added, the kind and the amount of other compound added and the pH of the suspension.
The main producing conditions and various properties of the products are shown in Table 10.
<Surface treatment of acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particles with by coupling agent>
Examples 57 to 68 and Comparative Examples 23 to 30
Example 57
1000 g of the spindle .alpha.-Fe.sub.2 O.sub.3 particles obtained as Sample Production 1 and 10 g (1.0 part by weight based on 100 parts by weight of the spindle .alpha.-Fe.sub.2 O.sub.3 particles) of y-aminopropyltrimethoxysilane (A-1100: trade name, produced by Nippon Unicar Co., Ltd.) were charged into a Henschel mixer manufactured by Mitsui Miike Kagaku Koki Kabushiki Kaisha) and the mixer was driven for 20 minutes to coat the spindle .alpha.-Fe.sub.2 O.sub.3 particles with the silane coupling agent.
The amount of silane coupling agent existent on the surface of the coated particles was 0.48 part by weight based on 100 parts by weight of the spindle .alpha.-Fe.sub.2 O.sub.3 particles. The coated particles had an average major axis diameter of 0.15 .mu.m, an average minor axis diameter of 0.026 .mu.m, an aspect ratio of 5.8, a particle size distribution in geometrical standard deviation of 1.35 and a BET specific surface area of 48.6 m.sup.2 /g.
Example 58
500 g of the acicular .alpha.-Fe.sub.2 O.sub.3 particles obtained as Sample Production 2 were dispersed in 5 liter of ethanol and 100 g (2 parts by weight based on 100 parts by weight of the acicular .alpha.-Fe.sub.2 O.sub.3 particles) of ethanol solution of 10 wt % of vinyltriethoxysilane (A-151: trade name, produced by Nippon Unicar Co., Ltd.) was added to the dispersion. The resultant mixture was stirred to coat the acicular .alpha.-Fe.sub.2 O.sub.3 particles with the silane coupling agent. The dispersion was then filtered and dried, and the particles obtained were compacted by an edge runner-type pulverizer (Sand mill, manufactured by Kabushiki Kaisha. Matsumoto Chuzo Tekkosho). Thus coated particles were obtained.
The amount of silane coupling agent existent on the surfaces of the coated particles was 1.01 parts by weight based on 100 parts by weight of the acicular .alpha.-Fe.sub.2 O.sub.3 particles. The coated particles had an average major axis diameter of 0.21 .mu.m, an average minor axis diameter of 0.031 .mu.m, an aspect ratio of 6.8, a particle size distribution in geometrical standard deviation of 1.38 and a BET specific surface area of 36.6 m.sup.2 /g.
Example 59
500 g of the spindle .alpha.-Fe.sub.2 O.sub.3 particles obtained as Sample Production 3 were dispersed in 5 liter of water and 25 g (0.5 part by weight based on 100 parts by weight of the spindle .alpha.-Fe.sub.2 O.sub.3 particles) of an aqueous solution of 10 wt % of isopropyltri (N-aminoethyl-aminoethyl) titanate (KR-44: trade name, produced by Ajinomoto Co., Ltd.) was added to the dispersion. After the resultant mixture was stirred, an aqueous NH.sub.4 OH solution was added thereto to adjust the pH to 7.0, thereby coating the spindle .alpha.-Fe.sub.2 O.sub.3 particles with the titanate coupling agent. The dispersion was then filtered, dried and the particles obtained were compacted by an edge runner-type pulverizer (Sand mill, manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho). Thus coated particles were obtained.
The amount of titanate coupling agent existent on the surface of the coated particles was 0.21 part by weight based on 100 parts by weight of the spindle .alpha.-Fe.sub.2 O.sub.3 particles. The coated particles had an average major axis diameter of 0.16 .mu.m, an average minor axis diameter of 0.026 .mu.m, an aspect ratio of 6.2, a particle size distribution in geometrical standard deviation of 1.35 and a BET specific surface area of 50.0 m.sup.2 /g.
Examples 60 to 68 and Comparative Examples 23 to 30
Acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particles coated with a coupling agent were produced in the same way as in Example 57, 58 or 59 except for varying the kind of particles to be coated, the kind and the amount of coupling agent added and the pH of the dispersion.
In Comparative Examples 23 to 30, the acicularor spindle .alpha.-Fe.sub.2 O.sub.3 particles were not coated with a coupling agent.
The main producing conditions and various properties of the products are shown in Tables 12 to 13.
<Production of non-magnetic undercoating layer for magnetic recording medium>
Examples 69 to 80 and Comparative Examples 31 to 38
Example 69
The coated spindle .alpha.-Fe.sub.2 O.sub.3 particles obtained in Example 57 were first mixed with a binder resin and a solvent so that the solid content was 75 wt %, an the resultant mixture was kneaded for 30 minutes by a Brabender Prasti-corder. Thereafter, a predetermined amount of kneaded product was taken out and charged into a glass bottle together with glass beads and a solvent. The mixture was stirred and dispersed for 6 hours by a paint conditioner. The final composition of the non-magnetic paint obtained was as follows:
______________________________________Coupling agent-coated spindle .alpha.-Fe.sub.2 O.sub.3 100 parts by weightparticlesVinyl chloride-vinyl acetate copolymer 10 parts by weighthaving a sodium sulfonate groupPolyurethane having a carboxyl group 10 parts by weightCyclohexanone 40.9 parts by weightMethyl ethyl ketone 102.2 parts by weightToluene 61.3 parts by weight______________________________________
The non-magnetic paint obtained was applied to polyethylene terephthalate film having a thickness of 14 .mu.m so as to have a thickness of 55 .mu.m by using an applicator, and dried to obtain a sheet-like sample. The sheet-like sample had a Young's modulus of 138, a gloss of 168% and a surface roughness (Ra) of 14.4 nm.
Examples 70 to 80 and Comparative Examples 31 to 38
Non-magnetic undercoating layers for a magnetic recording medium were produced in the same way as in Example 69 by using the acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particles obtained in Examples 58 to 68 and Comparative Examples 23 to 30 and acicular or spindle .alpha.-FeOOH particles in Comparative Examples 27 and 28, respectively.
Various properties of the products are shown in Tables 14 and 15.
<Production of magnetic tape>
Examples 81 to 86 and Comparative Examples 39 to 42
Example 81
Co-coated magnetic iron oxide particles (average major axis diameter: 0.20 .mu.m, average minor axis diameter: 0.029 .mu.m, aspect ratio: 6.8, particle size distribution in geometrical standard deviation: 1.38, BET specific surface area: 48.2 m.sup.2 /g) were first mixed with a binder resin and a solvent so that the solid content was 76 wt %, and the resultant mixture was kneaded for 30 minutes by a Brabender Plasti-corder. Thereafter, a predetermined amount of kneaded product was taken out and charged into a glass bottle together with glass beads and a solvent. The mixture was stirred and dispersed for 6 hours by a paint conditioner.
Thereafter, an abrasive, a lubricant and a hardener solution were added, and the mixture was further stirred and dispersed for 15 minutes. The magnetic paint obtained was as follows:
______________________________________Co-coated magnetic iron oxide particles 100 parts by weightVinyl chloride-vinyl acetate copolymer 10 parts by weighthaving a sodium sulfonate groupPolyurethane having a sodium sulfonate 10 parts by weightgroupAbrasive 10 parts by weightLubricant 2.5 parts by weightHardner 5 parts by weightCyclohexanone 52.2 parts by weightMethyl ethyl ketone 130.5 parts by weightToluene 78.3 parts by weight______________________________________
The magnetic paint obtained was applied to the non-magnetic undercoating layer formed thereon in Example 69, so as to have a thickness of 15 .mu.m by using an applicator and dried to obtain a sheet-like sample. The sheet-like sample was calendered, and cured at a temperature of 60.degree. C. for 24 hours. The sheet-like sample was then slit to a width of 0.5 inch to obtain a magnetic tape.
The magnetic tape obtained had a coercive force (Hc) of 882 Oe, a squareness of 0.88, a gloss of 172%, a surface roughness (Ra) of 7.2 nm, a Young's modulus of 147, and a linear adsorption coefficient of 1.21.
Examples 82 to 86 and Comparative Examples 39 to 42
Magnetic recording media were produced in the same way as in Example 81 by using the undercoating layers for a magnetic recording medium obtained in Examples 69, 75 and 76 and Comparative Examples 31 and 36.
Various properties of the products are shown in Table 16.
TABLE 1__________________________________________________________________________Production of acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particlesAcicular or spindle .alpha.-FeOOH BET Dehydration AnnealingExamples Major Minor specific Tem- Tem-and axis axis Aspect surface pera- pera-Comp. diameter diameter ratio area ture Time ture TimeExamples (.mu.m) (.mu.m) (-) (m.sup.2 /g) (.degree.C.) (min) (.degree.C.) (min)__________________________________________________________________________Example1 0.21 0.021 10.0 110.0 470 60 650 1202 0.21 0.021 10.0 110.0 470 60 650 1203 0.21 0.021 10.0 110.0 470 60 650 1204 0.25 0.023 10.9 75.3 470 60 650 1205 0.25 0.023 10.9 75.3 470 60 650 1206 0.30 0.026 11.5 46.2 470 60 650 1207 0.30 0.026 11.5 46.2 470 60 650 1208 0.21 0.021 10.0 110.0 470 60 650 1209 0.21 0.021 10.0 110.0 470 60 650 12010 0.21 0.021 10.0 110.0 470 60 650 12011 0.21 0.021 10.0 110.0 470 60 650 12012 0.21 0.021 10.0 110.0 470 60 650 12013 0.21 0.021 10.0 110.0 470 60 650 12014 0.21 0.021 10.0 110.0 470 60 650 12015 0.21 0.021 10.0 110.0 470 60 650 12016 0.21 0.021 10.0 110.0 470 60 650 120__________________________________________________________________________Production of coated acicular or spindle .alpha.-Fe.sub.2 O.sub.3particles Other coating compoundsCoating Al compound Amount Al pH of Ele- of pH of content sus- ment element sus- Kind (wt %) pension Kind added added pension__________________________________________________________________________Example1 Al.sub.2 (SO.sub.4).sub.3 1.78 6.0 -- -- -- --2 NaAlO.sub.2 5.00 8.0 -- -- -- --3 NaAlO.sub.2 10.00 7.0 -- -- -- --4 AlCl.sub.3 0.50 7.0 -- -- -- --5 Al.sub.2 (SO.sub.4).sub.3 5.00 7.0 -- -- -- --6 Al.sub.2 (SO.sub.4).sub.3 10.00 6.0 -- -- -- --7 Al.sub.2 (SO.sub.4).sub.3 40.00 6.0 -- -- -- --8 Al.sub.2 (SO.sub.4).sub.3 3.56 7.0 No. 3 water Si 1.0 7.0 glass9 Al.sub.2 (SO.sub.4).sub.3 3.56 7.0 No. 3 water Si 2.0 6.0 glass10 NaAlO.sub.2 5.00 7.0 No. 3 water Si 10.0 7.0 glass11 NaAlO.sub.2 5.00 7.0 No. 3 water Si 40.0 6.0 glass12 Al.sub.2 (SO.sub.4).sub.3 3.56 6.0 Sodium P 1.0 7.0 hexameta- phosphate13 NaAlO.sub.2 2.00 8.0 Titanyl Ti 5.0 7.0 sulfate14 AlCl.sub.3 5.00 7.0 Manganese Mn 3.2 7.0 sulfate15 Al.sub.2 (SO.sub.4).sub.3 4.32 8.0 Nickel Ni 5.0 7.0 sulfate16 Al.sub.2 (SO.sub.4).sub.3 3.56 7.0 Zinc Zn 4.0 7.0 sulfate__________________________________________________________________________
TABLE 2__________________________________________________________________________Production of acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particlesAcicular or spindle .alpha.-FeOOH BET Dehydration AnnealingExamples Major Minor specific Tem- Tem-and axis axis Aspect surface pera- pera-Comp. diameter diameter ratio area ture Time ture TimeExamples (.mu.m) (.mu.m) (-) (m.sup.2 /g) (.degree.C.) (min) (.degree.C.) (min)__________________________________________________________________________Example17 0.21 0.021 10.0 110.0 470 60 650 12018 0.21 0.021 10.0 110.0 470 60 650 12019 0.21 0.021 10.0 110.0 470 60 650 12020 0.21 0.021 10.0 110.0 470 60 650 12021 0.21 0.021 10.0 110.0 470 60 650 12022 0.21 0.021 10.0 110.0 470 60 650 120Comp.Example1 0.21 0.021 10.0 110.0 470 60 650 1202 0.25 0.023 10.9 75.3 470 60 650 1203 0.30 0.026 11.5 46.2 470 60 650 1204 0.21 0.021 10.0 110.0 470 60 650 1205 0.21 0.021 10.0 110.0 -- -- -- --6 0.25 0.023 10.9 75.3 -- -- -- --7 *0.17 0.12 1.4 13.8 -- -- -- --8 *0.34 0.28 1.2 6.7 -- -- -- --__________________________________________________________________________ (Note) *: Fe.sub.2 O.sub.3 particles obtained by heattreating magnetite particles were used
Production of coated acicular or spindle .alpha.-Fe.sub.2 O.sub.3particles Other coating compoundsCoating Al compound Amount Al pH of Ele- of pH of content sus- ment element sus- Kind (wt %) pension Kind added added pension__________________________________________________________________________Example17 Al.sub.2 (SO.sub.4).sub.3 3.56 7.0 Zirconium Zr 5.0 7.0 sulfate18 Al.sub.2 (SO.sub.4).sub.3 3.56 7.0 Zirconia sol Zr 5.0 7.019 Al.sub.2 (SO.sub.4).sub.3 3.56 7.0 Soda Sn 10.0 7.0 stannate20 NaAlO.sub.2 2.00 8.0 Antimony sol Sb 10.0 7.021 Al.sub.2 (SO.sub.4).sub.3 3.56 7.0 No. 3 water Si 3.0 7.0 glass + zir- Zr 2.0 7.0 conia sol22 NaAlO.sub.2 5.00 7.0 Sodium P 1.0 7.0 hexameta- Zn 1.0 7.0 phosphate + Zinc sulfateComp.Example1 -- -- -- -- -- -- --2 -- -- -- -- -- -- --3 Al.sub.2 (SO.sub.4).sub.3 0.005 7.0 -- -- -- --4 NaAlO.sub.2 80.0 7.0 -- -- -- --5 -- -- -- -- -- -- --6 -- -- -- -- -- -- --7 -- -- -- -- -- -- --8 -- -- -- -- -- -- --__________________________________________________________________________
TABLE 3______________________________________Properties of coated acicular or spindle.alpha.-Fe.sub.2 O.sub.3 particles Major Minor Geomet- BET axis axis rical specificExamples diam- diam- Aspect standard surface Aland Comp. eter eter ratio deviation area contentExamples (.mu.m) (.mu.m) (-) (.delta.g) (-) (m.sup.2 /g) (wt %)______________________________________Example1 0.15 0.026 5.8 1.35 51.8 1.782 0.14 0.026 5.4 1.34 50.1 5.013 0.16 0.028 5.7 1.36 43.2 9.894 0.20 0.030 6.7 1.38 38.9 0.495 0.21 0.032 6.4 1.37 34.6 4.986 0.24 0.033 7.3 1.36 31.3 9.917 0.25 0.034 7.9 1.37 26.5 38.808 0.15 0.026 5.8 1.35 53.6 3.569 0.15 0.026 5.8 1.34 51.5 3.5410 0.16 0.027 5.9 1.35 48.7 4.8611 0.16 0.029 5.5 1.36 59.9 4.9612 0.16 0.026 6.2 1.36 54.1 3.5613 0.15 0.026 5.8 1.35 49.8 1.9814 0.17 0.025 6.8 1.35 47.6 4.9215 0.15 0.028 5.4 1.36 48.8 4.3216 0.16 0.025 6.4 1.35 47.7 3.55______________________________________Properties of coated acicular or spindle.alpha.-Fe.sub.2 O.sub.3 particlesOther coating Filtration productivity Removalelements Resistance of solvent Al of filtration Filtration Amount of content (.alpha.V) time remaining Kind (wt %) (m/kg) (min) C (wt %)______________________________________Example1 -- -- 4.22 .times. 10.sup.11 2.6 0.4202 -- -- 8.80 .times. 10.sup.11 3.8 0.3803 -- -- 1.01 .times. 10.sup.12 7.3 0.3624 -- -- 9.87 .times. 10.sup.11 5.6 0.4505 -- -- 4.86 .times. 10.sup.11 2.8 0.3806 -- -- 5.26 .times. 10.sup.11 3.3 0.3537 -- -- 6.23 .times. 10.sup.11 3.5 0.2968 Si 0.98 8.80 .times. 10.sup.11 4.1 0.4209 Si 1.78 1.03 .times. 10.sup.12 8.2 0.39610 Si 8.85 2.42 .times. 10.sup.12 12.2 0.33311 Si 32.80 3.56 .times. 10.sup.12 13.8 0.30112 P 1.01 2.11 .times. 10.sup.11 3.1 0.45013 Ti 4.98 5.23 .times. 10.sup.11 3.8 0.42114 Mn 3.02 4.21 .times. 10.sup.11 4.2 0.37615 Ni 4.86 3.56 .times. 10.sup.11 3.1 0.39216 Zn 4.00 6.24 .times. 10.sup.11 3.9 0.415______________________________________
TABLE 4______________________________________Properties of coated acicular or spindle.alpha.-Fe.sub.2 O.sub.3 particles Minor Geomet- BETExamples Major axis rical specificand axis diam- Aspect standard surface AlComp. diameter eter ratio deviation area contentExamples (.mu.m) (.mu.m) (-) (.delta.g) (-) (m.sup.2 /g) (wt %)______________________________________Example17 0.16 0.026 6.2 1.35 49.1 3.5318 0.15 0.026 5.8 1.35 48.9 3.5219 0.18 0.027 6.7 1.36 51.1 3.5620 0.18 0.027 6.7 1.35 50.0 2.0121 0.15 0.026 5.8 1.36 46.9 3.5322 0.16 0.026 6.2 1.36 47.8 4.89Comp.Example1 0.14 0.025 5.6 1.36 52.0 --2 0.23 0.030 7.7 1.37 38.5 --3 0.26 0.034 7.6 1.38 33.6 0.0054 0.17 0.032 5.3 1.37 38.0 73.925 #0.21 0.021 10.0 1.33 -- --6 ##0.25 0.023 10.9 1.32 -- --7 0.17 0.12 1.4 1.56 13.8 --8 0.34 0.28 1.2 1.78 6.7 --______________________________________ (Note) #: Spindle FeOOH particles ##: Acicular FeOOH particles
Properties of coated acicular or spindle.alpha.-Fe.sub.2 O.sub.3 particlesOther coating Filtration productivity Removalelements Resistance of solvent Al of filtration Filtration Amount of content (.alpha.V) time remaining Kind (wt %) (m/kg) (min) C (wt %)______________________________________Example17 Zr 4.58 3.21 .times. 10.sup.11 2.6 0.41018 Zr 4.88 3.30 .times. 10.sup.11 2.2 0.39319 Sn 8.52 4.56 .times. 10.sup.11 2.8 0.26620 Sb 7.66 3.68 .times. 10.sup.11 2.1 0.40321 Si 2.96 8.91 .times. 10.sup.11 6.1 0.400 Zr 1.8922 P 0.99 9.00 .times. 10.sup.11 7.2 0.430 Zn 1.00Comp.Example1 -- -- 4.74 .times. 10.sup.13 42.0 0.5032 -- -- 5.32 .times. 10.sup.13 59.5 0.5153 -- -- 1.74 .times. 10.sup.13 25.0 0.5004 -- -- 9.32 .times. 10.sup.12 20.0 0.3215 -- -- -- -- 0.7056 -- -- -- -- 0.8117 -- -- -- -- 0.4658 -- -- -- -- 0.423______________________________________
TABLE 5______________________________________Properties of non-magnetic undercoating layer Young'sExamples Surface modulusand roughness (relativeCompar- Non- Gloss of coating value) of Thicknessative magnetic (45.degree.) film coating of coatingExamples particles (%) (Ra) (nm) film (-) film (.mu.m)______________________________________Example Example23 1 182 11.2 121 3.824 2 179 12.0 132 3.725 3 179 11.8 128 3.826 4 168 14.2 136 3.627 5 167 14.0 136 3.728 6 161 14.8 143 3.929 7 163 14.6 146 4.030 8 185 11.2 125 3.931 9 187 11.0 126 3.932 10 176 11.8 119 4.133 11 165 13.2 123 4.234 12 185 11.4 119 3.635 13 183 11.4 118 3.636 14 182 11.6 123 3.837 15 183 11.4 123 3.838 16 179 12.2 120 3.7______________________________________
TABLE 6______________________________________Properties of non-magnetic undercoating layer Young'sExamples Surface modulusand roughness (relativeCompar- Non- Gloss of coating value) of Thicknessative magnetic (45.degree.) film coating of coatingExamples particles (%) (Ra) (nm) film (-) film (.mu.m)______________________________________Example Example39 17 176 12.6 125 3.840 18 188 11.8 121 3.841 19 180 11.6 124 3.842 20 176 12.0 129 3.743 21 193 10.8 135 3.944 22 183 11.8 118 3.8Comp. Comp.Example Example 9 1 155 21.6 88 3.910 2 158 17.6 89 4.111 3 158 17.6 95 3.612 4 136 18.8 96 4.013 5 102 31.6 93 4.414 6 121 28.8 101 4.615 7 91 41.6 60 3.816 8 72 84.8 30 3.6______________________________________
TABLE 7__________________________________________________________________________Properties of magnetic tape Under-Ref- coating Coerciveerence layer force Square-Example used Magnetic particles used Hc (Oe) ness (-)__________________________________________________________________________Example Example45 23 Co-coated Fe.sub.3 O.sub.4 particles 889 0.8946 30 Major axis diameter: 0.20 .mu.m 893 0.8847 43 Minor axis diameter: 0.029 .mu.m 896 0.90Comp. Comp. Hc: 850 OeExample Example .delta.s: 81.3 emu/g17 9 Co content: 4.52 wt % 877 0.8518 14 Fe.sup.2+ 16.5tent: wt % 869 0.83Example Example48 23 Magnetic metal particles 1628 0.8849 30 Major axis diameter: 0.13 .mu.m 1611 0.8850 43 Minor axis diameter: 0.017 .mu.m 1652 0.89Comp. Comp. Hc: 1560 OeExample Example .delta.s: 128.9 emu/g19 9 BET specific 52.9 m.sup.2 /g 1590 0.8620 14 surface area: 1569 0.85 Co content: 5.9 wt % Al content: 1.1 wt % B content: 1.0 wt %__________________________________________________________________________Properties of magnetic tape Young's Surface modulus Gloss of roughness (relative Thickness magnetic of magnetic value) of of magnetic coating film coating film magnetic coating Linear (45.degree.) (%) (Ra) (nm) tape (-) film (.mu.m) absorption__________________________________________________________________________Example45 178 6.0 133 1.2 1.2146 175 6.8 136 1.4 1.2047 181 5.6 136 1.2 1.22Comp.Example17 142 11.2 108 1.4 1.0818 125 13.6 115 1.4 1.15Example48 235 5.6 128 1.4 1.3149 232 5.6 126 1.4 1.2850 238 5.2 132 1.4 1.29Comp.Example19 172 18.8 93 1.2 1.1520 150 31.6 108 1.2 1.13__________________________________________________________________________
TABLE 8__________________________________________________________________________Production of acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particlesAcicular or spindle .alpha.-FeOOH BETMajor Minor specific axis axis Aspect surface Dehydration AnnealingSamples diameter diameter ratio area Temperature Time Temperature TimeProduction (.mu.m) (.mu.m) (-) (m.sup.2 /g) (.degree.C.) (min) (.degree.C.) (min)__________________________________________________________________________1 0.21 0.021 10.0 110.0 470 60 650 1202 0.25 0.023 10.9 75.3 470 60 650 1203 0.21 0.021 10.0 110.0 470 60 650 1204 0.21 0.021 10.0 110.0 470 60 650 1205 0.21 0.021 10.0 110.0 470 60 650 1206 0.21 0.021 10.0 110.0 470 60 650 1207 0.21 0.021 10.0 110.0 470 60 650 1208 0.21 0.021 10.0 110.0 470 60 650 1209 0.25 0.023 10.9 75.3 470 60 650 12010 0.25 0.023 10.9 75.3 470 60 650 12011 0.30 0.026 11.5 46.2 470 60 650 12012 0.30 0.026 11.5 46.2 470 60 650 120__________________________________________________________________________
TABLE 9__________________________________________________________________________Production of acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particlesAcicular or spindle .alpha.-FeOOH BETMajor Minor specific axis axis Aspect surface Dehydration AnnealingSamples diameter diameter ratio area Temperature Time Temperature TimeProduction (.mu.m) (.mu.m) (-) (m.sup.2 /g) (.degree.C.) (min) (.degree.C.) (min)__________________________________________________________________________13 0.21 0.021 10.0 110.0 470 60 650 12014 0.25 0.023 10.9 75.3 470 60 650 12015 0.30 0.026 11.5 46.2 470 60 650 12016 0.21 0.021 10.0 110.0 470 60 650 12017 0.21 0.021 10.0 110.0 -- -- -- --18 0.25 0.023 10.9 75.3 -- -- -- --19 *0.17 0.12 1.4 13.8 -- -- -- --20 *0.34 0.28 1.2 6.7 -- -- -- --__________________________________________________________________________ (Note) *: Fe.sub.2 O.sub.3 particles obtained by heattreating magnetite particles were used
TABLE 10__________________________________________________________________________ Production of acicular or spindle .alpha.-Fe.sub.2 O.sub.3 particles coated with Al compound, etc Other coating compounds Coating Al compound Amount ofExamples and Particles Al pH of Ele- element pH ofComparative to be content suspension ment added suspensionExamples coated Kind (wt %) (-) Kind added (wt %) (-)__________________________________________________________________________Example Sample51 7 NaAlO.sub.2 0.50 7.0 -- -- -- --52 8 Al.sub.2 (SO.sub.4).sub.3 1.00 7.0 No. 3 water Si 2.0 6.0 glass53 9 Al.sub.2 (SO.sub.4).sub.3 2.00 8.0 -- -- -- --54 10 Al.sub.2 (SO.sub.4).sub.3 3.00 7.0 Zirconium Zr 1.0 7.0 sulfate55 11 AlCl.sub.3 5.00 6.0 -- -- -- --56 12 Al.sub.2 (SO.sub.4).sub.3 10.00 7.0 Zinc Zn 2.0 6.0 sulfateComp. 15 Al.sub.2 (SO.sub.4).sub.3 0.005 7.0 -- -- -- --Example 21Comp. 16 NaAlO.sub.2 80.00 7.0 --Example 22__________________________________________________________________________
TABLE 11______________________________________Examples Production of acicular or spindle .alpha.-Fe.sub.2 O.sub.3and particles coated with coupling agentCompar- Particlesative to be Kind of coupling AmountExamples coated agent (wt %) *Process______________________________________Example Sample57 1 .gamma.-aminopropyltri- 1.0 A methoxysilane (A-1100: trade name, produced by Nippon Unicar Co., Ltd.)58 2 Vinyltriethoxysilane 2.0 B (A-151: trade name, produced by Nippon Unicar Co., Ltd.)59 3 Isopropyltri (N-amino 0.5 C ethylaminoethyl) titanate (KR-44: trade name, produced by Ajinomoto Co., Ltd.)60 4 Acetoalkoxyaluminum 2.0 A diisopropylate (AL-M: trade name, produced by Ajinomoto Co., Ltd.)61 5 .gamma.-aminopropyltri- 5.0 A methoxysilane (A-1100: trade name, produced by Nippon Unicar Co., Ltd.)62 6 .gamma.-glycidoxypropyltri- 0.1 A methoxysilane (A-187: trade name, produced by Nippon Unicar Co., Ltd.) Exampleaminopropyltri- .gamma. 2.0 B methoxysilane (A-1100: trade name, produced by Nippon Unicar Co., Ltd.)glycidoxypropyltri-mma. 3.0 A methoxysilane (A-187: trade name, produced by Nippon Unicar Co., Ltd.)aminopropyltri- .gamma. 2.0 A methoxysilane (A-1100: trade name, produced by Nippon Unicar Co., Ltd.)aminopropyltri- .gamma. 3.0 B methoxysilane (A-1100: trade name, produced by Nippon Unicar Co., Ltd.)67 55 Isopropyltri(N-amino- 5.0 A ethylaminoethyl)- titanate (KR-44: trade name, produced by Ajinomoto Co., Ltd.)68 56 Isopropyltri(N-amino- 2.0 A ethylaminoethyl)- titanate (KR-44: trade name, produced by Ajinomoto Co., Ltd.)______________________________________ (Note) *: Process A: Dry process Process B: Wet process using organic solvent as liquid dispersion medium Process C: Wet process using water as liquid dispersion medium
TABLE 12__________________________________________________________________________Properties of coated acicular or spindle .alpha.-Fe.sub.2 O.sub.3particles Amount BET ofExamples Major Minor Geometrical specific Other coating couplingand axis axis Aspect standard surface Al elements agent (CComp. diameter diameter ratio deviation area content Content content)Examples (.mu.m) (.mu.m) (-) (.delta.g) (-) (m.sup.2 /g) (wt %) Element (wt %) (wt %)__________________________________________________________________________Example57 0.15 0.026 5.8 1.35 48.6 -- -- -- 0.4858 0.21 0.031 6.8 1.38 36.6 -- -- -- 1.0159 0.16 0.026 6.2 1.35 50.0 -- -- -- 0.2160 0.15 0.026 5.8 1.36 47.5 -- -- -- 1.3561 0.15 0.025 6.0 1.35 45.2 -- -- -- 2.4462 0.16 0.026 6.2 1.36 51.0 -- -- -- 0.04663 0.15 0.026 5.8 1.36 49.1 0.50 -- -- 0.9864 0.15 0.025 6.0 1.34 48.5 1.00 Si 1.98 1.3765 0.21 0.030 7.0 1.39 37.4 1.96 -- -- 0.9766 0.21 0.030 7.0 1.38 35.8 2.98 Zr 1.00 1.4667 0.25 0.033 7.6 1.39 28.6 4.89 -- -- 2.1668 0.25 0.034 7.4 1.38 29.2 9.93 Zn 1.95 0.86__________________________________________________________________________
TABLE 13__________________________________________________________________________Properties of coated acicular of spindle .alpha.-Fe.sub.2 O.sub.3particles AmountSample BET ofExamples or Major Minor Geometrical specific Other coating couplingand particles axis axis Aspect standard surface Al elements agent (CComp. to be diameter diameter ratio deviation area content Content content)Examples coated (.mu.m) (.mu.m) (-) (.delta.g) (-) (m.sup.2 /g) (wt %) Element (wt %) (wt %)__________________________________________________________________________Comp.Example Sample23 13 0.14 0.025 5.6 1.36 52.0 -- -- -- --24 14 0.23 0.030 7.7 1.37 38.5 -- -- -- --25 17 #0.21 0.021 10.0 1.33 -- -- -- -- --26 18 ##0.25 0.023 10.9 1.32 -- -- -- -- --27 19 0.17 0.12 1.4 1.56 13.8 -- -- -- --28 20 0.34 0.28 1.2 1.78 6.7 -- -- -- --__________________________________________________________________________ (Note) #: Spindle FeOOH particles ##: Acicular FeOOH particles
TABLE 14______________________________________Properties of non-magnetic undercoat layer Young'sExamples Surface modulusand roughness (relativeCompar- Non- Gloss of coating value) of Thicknessative magnetic (45.degree.) film coating of coatingExamples particles (%) (Ra) (nm) film (-) film (.mu.m)______________________________________Example Example69 57 168 14.4 138 4.070 58 164 13.6 143 3.871 59 160 14.8 132 4.172 60 168 14.2 140 3.773 61 171 12.8 142 3.674 62 162 15.2 116 3.575 63 179 12.0 156 4.076 64 189 10.2 156 3.877 65 180 11.6 146 3.578 66 193 9.8 161 3.679 67 172 12.2 145 3.980 68 183 10.8 149 4.0______________________________________
TABLE 15______________________________________Properties of non-magnetic undercoat layer Young'sExamples Surface modulusand roughness (relativeCompar- Non- Gloss of coating value) of Thicknessative magnetic (45.degree.) film coating of coatingExamples particles (%) (Ra) (nm) film (-) film (.mu.m)______________________________________Comp. Comp.Example Example29 23 155 21.6 88 3.930 24 158 17.6 89 4.131 25 102 31.6 93 4.432 26 121 28.8 101 4.633 27 91 41.6 60 3.834 28 72 84.8 30 3.6______________________________________
TABLE 16__________________________________________________________________________Properties of magnetic tape Under-Ref- coating Coerciveerence layer force Square-Example used Magnetic particles used Hc (Oe) ness (-)__________________________________________________________________________Example Example81 69 Co-coated Fe.sub.3 O.sub.4 particles 882 0.8882 75 Major axial diameter: 0.20 .mu.m 889 0.8883 76 Minor axial diameter: 0.029 .mu.m 892 0.89Comp. Comp. Hc: 850 OeExample Example .delta.s: 81.3 emu/g35 29 Co content: 4.52 wt % 877 0.8536 32 Fe.sup.2+ content: 16.5 wt % 869 0.83Example Example84 69 Magnetic metal particles 1620 0.8885 75 Major axial diameter: 0.13 .mu.m 1636 0.8986 76 Minor axial diameter: 0.017 .mu.m 1662 0.90Comp. Comp. Hc: 1560 OeExample Example .delta.s: 128.9 emu/g37 29 BET specific surface 52.9 m.sup.2 /g 1590 0.8638 32 area: 1569 0.85 Co content: 5.9 wt % Al content: 1.1 wt % B content: 1.0 wt %__________________________________________________________________________Properties of magnetic tape Surface roughness Young's of modulus Thickness Gloss of magnetic (relative of magnetic coating value) of magnetic coating film film magnetic coating Linear (45.degree.) (%) (Ra) (nm) tape (-) film (.mu.m) absorption__________________________________________________________________________Example81 172 7.2 147 1.2 1.2182 176 6.6 160 1.2 1.2083 180 6.0 163 1.4 1.22Comp.Example35 142 11.2 108 1.4 1.0836 125 13.6 115 1.4 1.15Example84 230 5.6 142 1.2 1.2985 235 5.2 158 1.2 1.3586 236 5.0 162 1.2 1.34Comp.Example37 172 18.8 93 1.2 1.1538 150 31.6 108 1.2 1.13__________________________________________________________________________

Number	Name	Date
4076890	Yamada	Feb 1978
4789581	Nakamura	Dec 1988
4863793	Ogawa et al.	Sep 1989
5035948	Saito	Jul 1991
5089317	Noguchi	Feb 1992
5219652	Shimasoho	Jun 1993

Number	Date	Country
62-295217	Dec 1987	JPX
63-187418	Aug 1988	JPX
4-167225	Jun 1992	JPX
4-325915	Nov 1992	JPX

Non-magnetic particles for non-magnetic undercoating layer of magnetic recording medium, non-magnetic undercoating layer containing the same, and magnetic recording medium having the undercoating layer

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (6)

Foreign Referenced Citations (4)