The present invention refers to medical devices comprising a non-metallic micro tube containing FRP (fiber reinforced polymer), especially to respective tubings, used for constructing catheters like balloon dilation catheters, stent delivery catheters, guiding catheters and diagnostic catheters.
Angioplasty is an efficient and successful method of opening stenosis in the vascular system. In a popular form of angioplasty, a balloon catheter is advanced through the vascular system until the balloon, which is carried at the distal end of a catheter shaft, and which may carry an expandable stent, is positioned across the stenosis or damaged vessel. By inflating the balloon pressure is applied to the obstruction, which is moved by pressing it against the inner wall of the vessel, whereby the vessel is opened for improved flow. Due to the expansion of the balloon, the stent, which—if used—is situated on the balloon, is also expanded for aiding in repairing the vessel wall and hindering obstruction. As a last step the stent is then released by deflating the balloon reducing its circumference until refolding of the balloon occurs followed by removal of the balloon and catheter from the vessel along a guide wire.
There are various types of balloon catheters. One type is fed over a guide wire (i.e., “over-the-wire” catheters) and another type serves as its own guide wire (“fixed-wire” catheters). There have been developments of variations of these two basic types: the so-called “rapid exchange “type, “innerless” catheters, and others.
In another popular form of angioplastie selfexpanding stents are delivered to the target site in a vessel via a self-expanding stent delivery catheter. Usually the stent is covered by a sheath to keep it in the contracted configuration on the catheter until it reaches the target side. The sheath is then retracted in order to release the stent and the catheter is subsequently removed from the vessel.
If a catheter, like a balloon catheter, is used in percutaneous transluminal angioplasty (PTA) or percutaneous transluminal coronary angioplasty (PTCA), it is typically advanced through a guide catheter to a preselected vessel location, such as the aorta, for example. Using an imaging technique like fluoroscopy or MRI, the surgeon advances the catheter until the balloon is located across the stenosis or obstruction. This may involve the use of a guide wire over which the catheter is moved or alternatively the catheter may act as its own guide wire. Besides the fact that a smooth advancement in the vessels is in itself very advantageously, a possible origin of trouble arriving from this advancement of the catheter is the friction between the wire and the inner lumen of the catheter when guiding the catheter along the wire. As the movement in the vessels is highly difficult and a task requiring great handling skills any resistance in addition to those unavoidable due to the nature of the vessels being penetrated is strictly unwanted. Accordingly besides smoothness of the catheter (tip) itself a smooth movement of the wire inside the catheter avoiding as much friction as possible is highly desired. However, on the other hand the catheter needs sufficient pushability in order to advance the catheter over for example a stenosis in the vessel.
In order to address these conflictive needs, high flexibility and high pushability, many catheters, in particular PTA or PTCA catheters include a proximal portion that is relatively stiff, conventionally made from a stainless steel hypotube and a transition to a relatively soft and flexible distal portion of the catheter conventionally made from polymeric materials like PEBAX or Nylon.
Further, diagnostic catheters which are commonly used to facilitate the diagnosis of vascular diseases such as coronary artery disease and peripheral vascular disease and guide catheters which are commonly used to facilitate advancement of a PTA or PTCA catheter to the treatment site within the vessel when treating vascular diseases, commonly include a metallic braid reinforcement layer disposed between an inner layer and an outer layer. The braid reinforcement provides torsional rigidity, column strength, kink resistance, as well as radiopacity and is conventionally made from stainless steel wire.
However, a major drawback of these conventional braid reinforcement materials and hypotube materials such as stainless steel is their incompatibility with MRI (magnetic resonance imaging) due to their ferro-magnetic properties. MRI has become a standard in non-invasive diagnostic imaging and it is expected that MRI will be used in the future also for endovascular diagnosis and even treatment. The benefit for the patient compared to currently used x-ray angiogram is the absence of γ ray exposure and the use of less impacting contrast media.
Therefore, there is a clear need for improved high strength materials especially tubes for medical devices that allow use of these medical devices for effective treatment of the patient. There is a strong need for biocompatible and MRI compatible materials providing sufficient strength and elasticity.
The present invention provides medical devices comprising a non-metallic micro tube containing FRP (Fiber Reinforced Polymer) or continuous-fiber-reinforced implantable-grade polymer. The present invention particularly refers to MRI compatible tubings, used for constructing catheters like balloon dilation catheters, stent delivery catheters, guiding catheters and diagnostic catheters. Just as a clarification it should be made clear that this said micro tube is not meant to be a balloon or an inflatable member and thus is non-inflatable.
The invention further provides dual layer, trilayer or multilayer non-metallic micro tubes and methods for production thereof. In one embodiment the non-metallic microtube comprises PEEK (Polyetheretherketone) Polymer and Fiber Reinforced Polymer (FRP) containing continuous reinforced fiber material. The polymer used for at least one of the FRPs may be a thermoplastic or thermoset polymeric material.
In another embodiment of the present invention the non-metallic microtube comprises Fiber Reinforced PEEK (Polyetheretherketone) Polymer
In one embodiment of the present invention the non-metallic microtube further comprises polytetrafluoroethylene (PTFE) Teflon.
In a further embodiment the non-metallic microtube comprises PEEK, FRP, and PTFE.
These non-metallic microtubes according to the present invention can be used for a catheter shafts or other tubular catheter components and compare favorably with metallic alternatives. The mechanical properties of these continuous reinforced micro tubes are comparable to those of metallic materials of a similar dimension and outline while still having the advantage of their respective basic polymer.
The present invention provides medical devices comprising a non-metallic micro tube containing continuous-fiber-reinforced implantable-grade polymer. The present invention particularly refers to MRI compatible tubings, used for constructing catheters like balloon dilation catheters, stent delivery catheters, guiding catheters and diagnostic catheters. As said above and as a major embodiment said micro tube (non-metallic micro tube) is neither a balloon nor an inflatable member and thus is non-inflatable.
The present invention is directed to a medical device comprising a non-metallic microtube, the non-metallic microtube comprising FRP (Fiber Reinforced Polymers). Usually, and as the major embodiment the invention is thus also directed to a medical device comprising a non-metallic, non-inflatable microtube, the non-metallic, non-inflatable microtube comprising FRP (Fiber Reinforced Polymers).
In one embodiment, the non-metallic microtube comprising FRP are MRI compatible tubings.
In one embodiment the medical devices are MRI compatible medical devices. The medical devices particularly include catheters like balloon dilatation catheters, stent delivery catheters, guiding catheters and diagnostic catheters.
FRP (Fiber Reinforced Polymers) are defined as a polymeric material in which fibers or fiber filaments, selected from long or short, non-continuous or continuos fibers, are embedded reinforcing the polymer, especially an implantable-grade polymer. Examples could include fiber glass (glass reinforced polymer) or especially CRP (Carbon Reinforced Polymer or Carbon fiber Reinforced Polymer) (see below). FRPs are typically organized in a laminate structure, embedded within a thin layer of light polymer matrix material. The fibres provide the strength and stiffness, while the polymer binds and protects the fibers from damage, and transfers the stresses between fibers.
The embedded fibers or fiber filaments in the FRPs of the microtubes of the medical devices according to the present invention are derived from natural sources or preferably are synthetic material. Non-limiting examples include aramid, boron, glass (fiberglass) or carbon fibers; or also carbon-fiber and PEEK combined to form single filaments. Possibly the fibers are mixed with one another or with Kevlar or Aluminium fibers which could possibly also be used alone. If in a preferred embodiment carbon fibers are used the FRP is then called CRP (Carbon Reinforced Polymer or Carbon fiber Reinforced Polymer). Carbon (fiber) reinforced polymer is a fiber reinforced polymer in which the polymer is as non-limiting examples selected from epoxy, or other polymers, such as polyester, vinyl ester or nylon; preferably epoxy.
All the different fibers mentioned above can be applied as single or multiple elements, alone or in combinations of any or all of the above mentioned fibers depending on the application of specific requirements for the medical device.
In a preferred embodiment, the embedded fiber filaments consist of carbon fibers, or carbon fiber and PEEK are combined to form single filaments.
The polymeric material of the FRPs of the micro tubes of the medical devices according to the present invention used are including Polyester, Epoxy or Nylon or especially PEEK or (other) (suitable) pseudo-thermoplastic.
The polymers used for the microtubes of the medical devices according to the present invention are standard polymers preferably suitable for medical devices. Non-limiting examples include Polyester, Epoxy, Vinyl Ester or Nylon or especially PEEK or (other) pseudo-thermoplastic. Suitable pseudo-thermoplastics are pseudo-thermoplastics which have a high thermal index and whose properties can be maintained during a continuous service temperature of 450° F. (232° C.) or for short excursions as high as 900° F. (482° C.). Non limiting examples of suitable pseudo-thermoplastics are polyimides or loaded polyimides such as e.g. carbon loaded polyimide; or include Polyetheretherketone—PEEK, ENSIFONE® PSU (Polysulfonel, RILSAN®AESNO Nylon 12, TROGAMID®, CELAZOLE® PBI—[meltprocessable grades], Ultem 1000 polyetherimide (PEI) or others. Generally these polymers are rigid, high-strength, semi-tough thermoplastics that have high heat deflection temperatures and maintain their mechanical properties over a wide temperature range.
In a further embodiment the non-metallic microtube comprises fiber reinforced PEEK or fiber-reinforced pseudothermoplastic, most preferably carbo-fiber reinforced PEEK as FRP.
In one embodiment the non-metallic microtube comprises pseudothermoplastic, especially polyimide, preferably fiber-reinforced polyimide.
The non-metallic tube according to the present invention further may comprise PTFE.
In one embodiment of the present invention the fibers of the FRP are embedded in a preferential direction or preferential directions or orientation. In one embodiment the fibers in at least one FRP comprised in a non-metallic hypotube are directionally orientated, with “directionally orientated” meaning that the fibers in the FRP are embedded in a preferential direction or—if there are more than one layer of fibers—in preferential directions or orientations while each single layer still has the fibers unidirectionally orientated. In one embodiment the fibers of an FRP comprised in a non-metallic hypotube are unidirectionally orientated. In another embodiment, the non-metallic hypotube comprises a first layer of FRP which has unidirectionally orientated fibers in a first direction and a second layer of FRP which has unidirectionally orientated fibers in a second direction. By embedding the fibers or fiber filaments preferentially unidirectionally aligned into the microtube the heterogeneous materials are no longer isotropic but have preferential directions depending on the orientation of the fibers.
In one embodiment of the present invention the non-metallic microtube of the medical device has two—preferably different—layers of polymeric material, i.e. is dual layered, or has at least two layers of polymeric material or has optionally three or more layers of polymeric material.
In one preferred embodiment the medical device comprises a non-metallic microtube that has two layers, wherein the inner layer of the microtube is made from fiber reinforced PEEK or a pseudothermoplastic and the outer layer is made from PTFE.
In another preferred embodiment of the present invention the medical device comprises a non-metallic microtube that has three—preferably different—layers of polymeric material, i.e. is trilayered. In one preferred embodiment the inner layer of the microtube is made from PEEK or a pseudothermoplastic, the intermediate layer is made from FRP and the outer layer is made from PTFE. In this embodiment the intermediate layer is preferably made from carbon reinforced polymer (CRP).
In further embodiments of the present invention the non-metallic tube may further comprise an outer layer comprising a functional coating to act as a biointerface and aid blood-foreign material interaction between the device and the blood fluid contact surface, or form a lubricious barrier to aid movement through the conduits of the vasculature.
Referring now to the embodiments depicted in
In one embodiment as depicted in
In a preferred embodiment of the present invention the non-metallic microtube has an inner layer made of PEEK, and an intermediate layer made of a tube made from CRP (Carbon Reinforced Polymer) with the fiber filaments in a preferential direction or orientation which is coated on its outside with Teflon polytetrafluoroethylene (PTFE) to result in the outer layer.
In an alternative embodiment of the present invention as depicted in
The present invention is further directed to methods of manufacturing medical devices comprising non-metallic microtubes, the method comprising the steps of a) extruding a first material over a mandrel to form the inner layer; b) applying a second material over the first material. As said above and as a major embodiment said micro tube is neither a balloon nor an inflatable member and thus is non-inflatable. Accordingly—usually and as the major embodiment—these methods of manufacturing medical devices comprising non-metallic, non-inflatable microtubes comprise the steps of a) extruding a first material over a mandrel to form the inner layer; b) applying a second material over the first material.
In one embodiment of the present invention the method for manufacture further comprises the step of c) subjecting the outer surface of the inner layer to a surface treatment before application of the second material.
In a preferred embodiment of the present invention the method for manufacture further comprises the step of d) precision grinding of the dual layer tube.
In yet a preferred embodiment the method for manufacture further comprises the step of e) applying a third material over the second material.
The multi layer non-metallic micro tube according to the present invention may be processed using conventional and understood thermoplastic processing equipment and techniques such as for example but not limitation injection molding, extrusion, pultrusion, compression molding, powder coating, spraying and dip coating.
Referring now back to
In one embodiment of the present invention represented in
In one embodiment of the present invention the surface of the PEEK is subjected to a surface treatment to aid adhesion of the second layer and to prevent delaminating and fatigue crack. Suitable surface treatments include but are not limited to chemical etching, abrading, addition of an adhesive, and plasma surface preparations.
In a next step of manufacturing a medical device comprising a microtube, the second layer 120 consisting of a continuous fiber reinforced polymer with continuous reinforced fiber filaments embedded in the polymer matrix in a preferential direction or orientation is then applied over the top of the first layer 110.
In one embodiment of the present invention the second layer 120 consisting of a continuous fiber reinforced polymer is applied over the top of the first layer in a thickness greater than required for the finished sub-assembly. In this embodiment the entire sub-assembly consisting of the two layers is then parallel precision ground across its entire length to a pre defined and optimal outside diameter.
The top layer or third layer 130 may be made from Teflon, ie. PTFE and is applied over the second layer 120 in any thickness desired by for example but not limitation by dipping, spraying, extruding, pultruding, compression molding, or powder coating. In a very preferred embodiment, small uncoated segments 101, 102, and 103 are left uncoated, these small segments representing bonding regions for example but not limited to proximal shaft markers in the appropriate positions 103, or at the ends 101, 102 for attachment of further distal and proximal components, like e.g. a catheter balloon if the medical device comprising this microtube is a balloon dilatation catheter.
In another embodiment of the present invention represented in
As explained in the first embodiment, the top layer or second layer 240 of the microtube 200 of the second embodiment depicted in
The present invention is further directed to the use of a medical device according to the present invention for the treatment of a disease, especially a cardiovascular disease, especially a stenosis.
While preferred illustrative embodiments of the invention are described above, it will be apparent to one skilled in the art that various changes and modifications may be made therein without departing from the invention. The appended claims are intended to cover all such changes and modifications that fall within the true spirit and scope of the invention.
Number | Date | Country | Kind |
---|---|---|---|
09009923.5 | Jul 2009 | EP | regional |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/EP2010/004678 | 7/30/2010 | WO | 00 | 5/3/2012 |