Patent Grant
10633463
This invention relates to a non-phthalate catalyst system with a novel external electron donor for olefin polymerization.
Phthalate-based catalysts have been widely used in the commercial production of polypropylene worldwide. Extensive research and development have shown that the use of certain alkoxysilanes as external donors leads to optimum performance of phthalate-based catalysts (Kissin, Alkene Polymerizations with Transition Metal Catalysts, Studies in Surface Science and Catalysis 173: 224-243 (Elsevier, Amsterdam, 2007); Pasquini, Polypropylene Handbook (2nd Ed., Hanser Publishers, Munich, 2005); Moore, The Rebirth of Polypropylene: Supported Catalysts (Hanser Publishers, Munich, 1998)). The use of these silane donors allows for the production of a wide range of polypropylene products, due to the varied effect of these donors on the hydrogen response (characterized by melt flow rate (MFR)), isotacticity (characterized by % xylene solubles (% XS) or the isotactic pentad contents (mmmm) of the xylene-insoluble fraction (XI)), and molecular weight distribution (MWD).
Yet the use of these phthalate-based catalysts has caused regulatory and human health and safety concerns. Non-phthalate catalysts have been evaluated as replacements for the phthalate-based systems. However, the current non-phthalate catalysts generally do not match the performance of the phthalate systems.
Non-phthalate catalysts have certain limitations compared to the phthalate systems, for instance, very high initial activity, fast decay of polymerization activity, insufficient catalyst activity or low gas phase activity in sequential polymerization process for impact copolymer production. Additionally, non-phthalate catalysts often exhibit one or more of the following characteristics: low hydrogen response (characterized by low MFR) and low isotacticity. These limitations of the non-phthalate catalysts often render the properties of the polymers made with non-phthalate systems poorer than those of the polymers made with the phthalate-based catalysts.
There thus remains a need in the art to improve the technology of these non-phthalate catalyst systems to overcome the above-described limitations in the non-phthalate catalyst systems. This invention answers that need.
One aspect of the invention relates to a non-phthalate catalyst system for olefin polymerization. The non-phthalate catalyst system comprises (a) a solid Ziegler-Natta catalyst composition comprising a transition metal, a Group 2 metal, and one or more halogens; and one or more internal electron donor compounds; and (b) one or more external electron donor compounds.
The internal electron donor compound is i) a diether compound having a formula of
ii) a diester compound having a formula of
iii) a cyclic diester compound having a formula of
or iv) a succinate compound having a formula of
In these formulas, each of R1 and R2 is independently H or an alkyl, cycloalkyl, aryl, or aralkyl group, each having from 1 to 18 carbon atoms; or, R1 and R2 together form one or more saturated or unsaturated mono- or poly-cyclic structures. Each R3 is independently an alkyl, aryl, or aralkyl group having from 1 to 18 carbon atoms. Each R4 is H or R3. Each R5 is independently a C1 to C18 hydrocarbyl group which can optionally form one or more saturated or unsaturated mono- or poly-cyclic structures. Each of R6 and R7 is independently H or a C1 to C18 hydrocarbyl group; or, R6 and R7 together form one or more saturated or unsaturated mono- or poly-cyclic structures. Each R8 is independently absent, H, or a C1 to C18 hydrocarbyl group. Each R9 is independently H, halogen, or a C1 to C18 hydrocarbyl group. Each R10 is independently a C1 to C20 hydrocarbyl group. Each of R11 and R12 is independently R9 or —COOR10, provided that at least one of R11 and R12 is —COOR10. Each of R13 and R14 is independently a C1 to C18 hydrocarbyl group. The integer m is 0 or 1. The integer p ranges from 1 to 6. Each of R1, R2, R3, R4, R5, R6, R7, R8, R9, R13, and R14 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group.
The external electron donor compound is i) a triester compound having a formula of
ii) a diester compound having a formula of
or iii) an oxo-substituted diester compound having a formula of
In these formulas, X is CH2 or O. Each R is independently a C1-C10 hydrocarbyl group. Each R′ is independently H or R. Each n is independently an integer from 1 to 4. The integer n′ ranges from 0 to 4.
Another aspect of the invention relates to a non-phthalate catalyst system for olefin polymerization. The non-phthalate catalyst system comprises (a) a solid Ziegler-Natta catalyst composition comprising a transition metal, a Group 2 metal, and one or more halogens; and one or more internal electron donor compounds; and (b) one or more external electron donor compounds.
The internal electron donor compound is i) a diester compound having a formula of
or ii) a cyclic diester compound having a formula of
In these formulas, each R5 is independently a C1 to C18 hydrocarbyl group which can optionally form one or more saturated or unsaturated mono- or poly-cyclic structures. Each R17 is independently H, halogen, or C1 to C18 hydrocarbyl group which can optionally form one or more saturated or unsaturated cyclic structures with the phenyl group it is attached to. Each R9 is independently H, halogen, or C1 to C18 hydrocarbyl group. Each R10 is independently C1 to C20 hydrocarbyl group. Each of R11 and R12 is independently R9 or —COOR10, provided that at least one of R11 and R12 is —COOR10. Each m′ is independently an integer from 0 to 5. The integer p ranges from 1 to 6. Each of R5, R9, and R17 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group.
The external electron donor compound has a formula of
wherein the external electron donor compound does not contain an alkoxysilane compound. In formula VIII, each R is independently a C1 to C10 hydrocarbyl group, and can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group. R′ is H or R. The integer n ranges from 1 to 10.
Another aspect of the invention relates to a process for preparing a polyolefin. The process comprises polymerizing one or more olefins, in the presence of the non-phthalate catalyst system under reaction conditions sufficient to form the polyolefin. The non-phthalate catalyst system may be any non-phthalate catalyst system described herein.
This invention relates to a non-phthalate catalyst system capable to produce polyolefins with good catalyst activity, high isotacticity, and increased hydrogen response. Previously, non-phthalate catalyst systems have typically focused on using conventional alkoxysilane external donors. However, the non-phthalate catalysts often respond poorly to the changes in the type of conventional alkoxysilane external donors used, and the conventional alkoxysilane external donors generally have little modifying effect on the performance of the non-phthalate catalysts and the resulting polymer properties. In this invention, the inventors have discovered a series of novel catalyst/non-silane external donor systems that are chemically different from catalyst/alkoxysilane external donor systems. These non-silane external donors can modify the non-phthalate catalysts more significantly than the well-known alkoxysilane external donors and, thus, significantly improving the performance of the resulting polymer.
One aspect of the invention relates to a non-phthalate catalyst system for olefin polymerization. The non-phthalate catalyst system comprises (a) a solid Ziegler-Natta catalyst composition comprising a transition metal, a Group 2 metal, and one or more halogens; and one or more internal electron donor compounds; and (b) one or more external electron donor compounds.
The internal electron donor compound is i) a diether compound having a formula of
ii) a diester compound having a formula of
iii) a cyclic diester compound having a formula of
or iv) a succinate compound having a formula of
In these formulas, each of R1 and R2 is independently H or an alkyl, cycloalkyl, aryl, or aralkyl group, each having from 1 to 18 carbon atoms; or, R1 and R2 together form one or more saturated or unsaturated mono- or poly-cyclic structures. Each R3 is independently an alkyl, aryl, or aralkyl group having from 1 to 18 carbon atoms. Each R4 is H or R3. Each R5 is independently a C1 to C18 hydrocarbyl group which can optionally form one or more saturated or unsaturated mono- or poly-cyclic structures. Each of R6 and R7 is independently H or a C1 to C18 hydrocarbyl group; or, R6 and R7 together form one or more saturated or unsaturated mono- or poly-cyclic structures. Each R8 is independently absent, H, or a C1 to C18 hydrocarbyl group. Each R9 is independently H, halogen, or a C1 to C18 hydrocarbyl group. Each R10 is independently a C1 to C20 hydrocarbyl group. Each of R11 and R12 is independently R9 or —COOR10, provided that at least one of R11 and R12 is —COOR10. Each of R13 and R14 is independently a C1 to C18 hydrocarbyl group. The integer m is 0 or 1. The integer p ranges from 1 to 6. Each of R1, R2, R3, R4, R5, R6, R7, R8, R9, R13, and R14 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group.
The external electron donor compound is i) a triester compound having a formula of
ii) a diester compound having a formula of
or iii) an oxo-substituted diester compound having a formula of
In these formulas, X is CH2 or O. Each R is independently a C1-C10 hydrocarbyl group. Each R′ is independently H or R. Each n is independently an integer from 1 to 4. The integer n′ ranges from 0 to 4.
Solid Ziegler-Nata Catalyst Composition
Catalyst systems for the stereospecific polymerization of olefins are well known in the art. The most common type of catalyst system is the Ziegler-Natta family, which comprises a solid catalyst composition containing a Ziegler-Natta procatalyst composition, an internal electron donor, and an external electron donor.
Any Ziegler-Natta procatalyst known in the art may be used in the non-phthalate catalyst system. For instance, the Ziegler-Natta procatalyst composition typically contains a transition metal compound and a Group 2 metal compound. The transition metal compound may be a solid complex derived from a transition metal compound, for example, titanium-, zirconium-, chromium- or vanadium-hydrocarbyloxides, hydrocarbyls, halides, or mixtures thereof. In a typical Ziegler-Natta procatalyst composition, the transition metal is titanium, the Group 2 metal is magnesium, and the halogen is chloride.
The transition metal compound may have the general formulas of TrXx or Tr(OQ)gX4-g. Tr is the transition metal, for instance, Tr may be a Group 4, 5, or 6 metal. In one embodiment, Tr is a Group 4 metal, such as titanium. In another embodiment, Tr is Group 5 metal, such as vanadium. Each Q independently represents a hydrocarbon group, such as a C1-C10 alkyl group. X represents a halogen atom, such as chloride, bromide, or iodide; x is an integer from 3 to 4; and g is an integer from 0 to 4. Exemplary transition metal compounds include titanium trihalides such as TiCl3, TiBr3, and TiI3; titanium tetrahalides such as TiCl4, TiBr4, and TiI4; alkoxytitanium trihalides such as Ti(OCH3)Cl3, Ti(OC2H5)Cl3, Ti(OC4H9)Cl3, Ti(OC2H5)Br3, and Ti(OC4H9)Br3; dialkoxytitanium dihalides such as Ti(OCH3)2Cl2, Ti(OC2H5)2Cl2, Ti(OC4H9)2Cl2 and Ti(OC2H5)2Br2; trialkoxytitanium monohalides such as Ti(OCH3)3Cl, Ti(OC2H5)3Cl, Ti(OC4H9)3Cl, and Ti(OC2H5)3Br; and tetraalkoxytitaniums such as Ti(OCH3)4, Ti(OC2H5)4 and Ti(OC4H9)4. Mixtures of two or more such transition metal compounds may be used as well. The transition metal compound may be used individually or in solutions of hydrocarbon compounds or halogenated hydrocarbons.
Suitable Group 2 metal compounds include magnesium halides, such as magnesium chloride and magnesium bromide; alkoxymagnesiums, such as ethoxymagnesium, isopropoxymagnesium, butoxymagnesium, and 2-ethylhexoxymagnesium; dialkoxymagnesiums, such as diethoxymagnesium; alkoxymagnesium halides, such as methoxymagnesium chloride, ethoxymagnesium chloride, isopropoxy magnesium chloride, butoxy magnesium chloride, and octoxy magnesium chloride; magnesium oxyhalides; dialkylmagnesiums; aryloxymagnesiums, such as phenoxymagnesium and methylphenoxy magnesium chloride; and carboxylates of magnesium, such as magnesium laurate and magnesium stearate. These magnesium compounds may be in the liquid or solid state. Typically, the Group 2 metal compound is magnesium dichloride.
Internal Donor
The Ziegler-Natta procatalyst composition includes an internal electron donor. The internal electron donor provides tacticity control and catalyst crystallite sizing. Suitable internal electron donors include diethers, diesters, cyclic diesters, and succinates, and combinations thereof.
As used herein, a “hydrocarbyl” is a linear or branched aliphatic radical, such as alkyl, alkenyl, and alkynyl; alicyclic radical, such as cycloalkyl, cycloalkenyl; aromatic radical, such as monocyclic or polycyclic aromatic radical; as well as combinations thereof, such as alkaryl and aralkyl.
i) Diether Compound
The internal electron donor can be a diether compound, such as a 1,3-diether having a formula of
Each of R1 and R2 is independently H or an alkyl, cycloalkyl, aryl, or aralkyl group, each having from 1 to 18 carbon atoms; or, R1 and R2 together form one or more saturated or unsaturated mono- or poly-cyclic structures. Each R3 is independently an alkyl, aryl, or aralkyl group having from 1 to 18 carbon atoms. Each R4 is H or R3. The alkyl, cycloalkyl, and aryl for each R group can be further substituted with one or more of alkyl, cycloalkyl, aryl, or halogen groups. Each of R1, R2, R3, and R4 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group. Typically, R1 and R2 are each independently H, C1-C6 alkyl, C2-C10 mono- or di-cycloalkyl, phenyl, benzyl, or naphthyl; R3 is a C1-C6 alkyl such as methyl; and R4 is hydrogen.
In some embodiments, when one of R1 and R2 is hydrogen, the other can be ethyl, butyl, 2-ethylhexyl, cyclohexylethyl, diphenylmethyl, p-chlorophenyl, 1-naphthyl, or 1-decahydronaphthyl. In some embodiments, when one of R1 and R2 is methyl, ethyl, or propyl; the other can be ethyl, propyl, butyl, pentyl, 2-ethylhexyl, cyclopentyl, cyclohexyl, methylcyclohexyl, phenyl, or benzyl. In some embodiments, both R1 and R2 can be ethyl, propyl, isopropyl, butyl, pentyl, phenyl, benzyl, cyclohexyl, or cyclopentyl. Exemplary diether compounds include, but are not limited to, 2-(2-ethylhexyl)-1,3-dimethoxypropane, 2-isopropyl-1,3-dimethoxypropane, 2-butyl-1,3-dimethoxypropane, 2-sec-butyl-1,3-dimethoxypropane, 2-cyclohexyl-1,3-dimethoxypropane, 2-phenyl-1,3-dimethoxypropane, 2-tert-butyl-1,3-dimethoxypropane, 2-cumyl-1,3-di4methoxypropane, 2-(2-phenylethyl)-1,3-dimethoxypropane, 2-(2-cyclohexylethyl)-1,3-dimethoxypropane, 2-(p-chlorophenyl)-1,3-dimethoxypropane, 2-(diphenylmethyl)-1,3-dimethoxypropane, 2 (1-naphthyl)-1,3-dimethoxypropane, 2(p-fluorophenyl)-1,3-dimethoxypropane, 2(1-decahydronaphthyl)-1,3-dimethoxypropane, 2(p-tert-butylphenyl)-1,3-dimethoxypropane, 2,2-dicyclohexyl-1,3-dimethoxypropane, 2,2-diethyl-1,3-dimethoxypropane, 2,2-dipropyl-1,3-dimethoxypropane, 2,2-dibutyl-1,3-dimethoxypropane, 2,2-diethyl-1,3-diethoxypropane, 2,2-dicyclopentyl-1,3-dimethoxypropane, 2,2-dipropyl-1,3-diethoxypropane, 2,2-dibutyl-1,3-diethoxypropane, 2-methyl-2-ethyl-1,3-dimethoxypropane, 2-methyl-2-propyl-1,3-dimethoxypropane, 2-methyl-2-benzyl-1,3-dimethoxypropane, 2-methyl-2-phenyl-1,3-dimethoxypropane, 2-methyl-2-cyclohexyl-1,3-dimethoxypropane, 2-methyl-2-methylcyclohexyl-1,3-dimethoxypropane, 2,2-bis(p-chlorophenyl)-1,3-dimethoxypropane, 2,2-bis(2-phenylethyl)-1,3-dimethoxypropane, 2,2-bis(2-cyclohexylethyl)-1,3-dimethoxypropane, 2-methyl-2-isobutyl-1,3-dimethoxypropane, 2-methyl-2-(2-ethylhexyl)-1,3-dimethoxypropane, 2,2-bis(2-ethylhexyl)-1,3-dimethoxypropane, 2,2-bis(p-methylphenyl)-1,3-dimethoxypropane, 2-methyl-2-isopropyl-1,3-dimethoxypropane, 2,2-diisobutyl-1,3-dimethoxypropane, 2,2-diphenyl-1,3-dimethoxypropane, 2,2-dibenzyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclopentyl-1,3-dimethoxypropane, 2,2-bis(cyclohexylmethyl)-1,3-dimethoxypropane, 2,2-diisobutyl-1,3-diethoxypropane, 2,2-diisobutyl-1,3-dibutoxypropane, 2-isobutyl-2-isopropyl-1,3-dimetoxypropane, 2,2-di-sec-butyl-1,3-dimetoxypropane, 2,2-di-tert-butyl-1,3-dimethoxypropane, 2,2-dineopentyl-1,3-dimethoxypropane, 2-iso-propyl-2-isopentyl-1,3-dimethoxypropane, 2-phenyl-2-benzyl-1,3-dimetoxypropane, 2-cyclohexyl-2-cyclohexylmethyl-1,3-dimethoxypropane. Mixtures of two or more such diether compounds may be used as well.
In some embodiments, R1 and R2 together form one or more unsaturated mono- or poly-cyclic structures, such as cyclopentadiene. The resulting diether compound has a formula of
R3 and R4 are defined as above. Each R1′ is independently H, halogen, or an alkyl, cycloalkyl, aryl, or aralkyl group, each having from 1 to 18 carbon atoms; or, two or more of R1′, together with the pentadiene ring, form fused di- or tri-cyclic structures. The alkyl, cycloalkyl, and aryl for each R1′ group can be further substituted with one or more of alkyl, cycloalkyl, aryl, or halogen groups. Each R1′ and its substituent group can optionally contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms. The integer r ranges from 0 to 4. Typically, R3 is a C1-C6 alkyl such as methyl; and R4 is hydrogen. Typically, each R1′ is H, halogen such as fluoro or chloro; C1-C6 alkyl; C2-C6 cycloalkyl; phenyl; or two of the R1′ groups form an indene with the pentadiene ring. Exemplary pentadiene- or indiene-containing compounds are 1,1-bis(methoxymethyl)-cyclopentadiene; 1,1-bis(methoxymethyl)-2,3,4,5-tetramethylcyclopentadiene; 1,1-bis(methoxymethyl)-2,3,4,5-tetraphenylcyclopentadiene; 1,1-bis(methoxymethyl)-2,3,4,5-tetrafluorocyclopentadiene; 1,1-bis(methoxymethyl)-3,4-dicyclopentylcyclopentadiene; 1,1-bis(methoxymethyl)indene; 1,1-bis(methoxymethyl)-2,3-dimethylindene; 1,1-bis(methoxymethyl)-4,5,6,7-tetrahydroindene; 1,1-bis(methoxymethyl)-2,3,6,7-tetrafluoroindene; 1,1-bis(methoxymethyl)-4,7-dimethylindene; 1,1-bis(methoxymethyl)-3,6-dimethylindene; 1,1-bis(methoxymethyl)-4-phenylindene; 1,1-bis(methoxymethyl)-4-phenyl-2-methylindene; 1,1-bis(methoxymethyl)-4-cyclohexylindene; 1,1-bis(methoxymethyl)-7-(3,3,3-trifluoropropyl)indene; 1,1-bis(methoxymethyl)-7-trimethyilsilylindene; 1,1-bis(methoxymethyl)-7-trifluoromethylindene; 1,1-bis(methoxymethyl)-4,7-dimethyl-4,5,6,7-tetrahydroindene; 1,1-bis(methoxymethyl)-7-methylindene; 1,1-bis(methoxymethyl)-7-cyclopentylindene; 1,1-bis(methoxymethyl)-7-isopropylindene; 1,1-bis(methoxymethyl)-7-cyclohexylindene; 1,1-bis(methoxymethyl)-7-tert-butylindene; 1,1-bis(methoxymethyl)-7-tert-butyl-2-methylindene; 1,1-bis(methoxymethyl)-7-phenylindene; 1,1-bis(methoxymethyl)-2-phenylindene; 1,1-bis(methoxymethyl)-1H-benz[e]indene; and 1,1-bis(methoxymethyl)-1H-2-methylbenz[e]indene. Mixtures of two or more such diether compounds may be used as well.
Alternatively, two or more of R1′ groups, together with the pentadiene ring, form fused di- or tri-cyclic structures, such as fluorene. The resulting diether compound has a formula of
R3 and R4 are defined as above. Each R15 is independently H, halogen, or an alkyl, cycloalkyl, aryl, alkylaryl, or aralkyl group, each having from 1 to 18 carbon atoms; or one or more R15 groups, together with the benzene ring, form fused rings. The integer q ranges from 0 to 4. The symbol “” in the formula refers to a saturated bond or unsaturated bond. Typically, R15 is H; halogen such as fluoro or chloro; C1-C6 alkyl; C2-C6 cycloalkyl; or two or more R15 form benzofluorene with the benzene ring(s). Exemplary fluorene-containing diether compounds are 9,9-bis(methoxymethyl)fluorene; 9,9-bis(methoxymethyl)-2,3,6,7-tetramethylfluorene; 9,9-bis(methoxymethyl)-2,3,4,5,6,7-hexafluorofluorene; 9,9-bis(methoxymethyl)-2,3-benzofluorene; 9,9-bis(methoxymethyl)-2,3,6,7-dibenzofluorene; 9,9-bis(methoxymethyl)-2,7-diisopropylfluorene; 9,9-bis(methoxymethyl)-1,8-dichlorofluorene; 9,9-bis(methoxymethyl)-2,7-dicyclopentylfluorene; 9,9-bis(methoxymethyl)-1,8-difluorofluorene; 9,9-bis(methoxymethyl)-1,2,3,4-tetrahydrofluorene; 9,9-bis(methoxymethyl)-1,2,3,4,5,6,7,8-octahydrofluorene; and 9,9-bis(methoxymethyl)-4-tert-butylfluorene. A typical fluorene-containing diether compound is 9,9-bis(methoxymethyl)fluorene. Mixtures of two or more such diether compounds may be used as well.
ii) Diester Compound
The internal electron donor can be a diester compound having a formula of
Each R5 is independently a C1 to C18 hydrocarbyl group which can optionally form one or more saturated or unsaturated mono- or poly-cyclic structures. Each of R6 and R7 is independently H or a C1 to C18 hydrocarbyl group; or, R6 and R7 together form one or more saturated or unsaturated mono- or poly-cyclic structures. Each R8 is independently absent, H, or a C1 to C18 hydrocarbyl group. The integer m is 0 or 1. Each of R5, R6, R7, and R8 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group.
R5 can be a C1 to C18 alkyl such as C1 to C10 alkyl; C2 to C18 alkenyl such as C2 to C8 alkenyl; C3 to C18 cycloalkyl such as C5 to C6 cycloalkyl; C3 to C18 cycloalkenyl such as C5 to C6 cycloalkenyl; aryl such as phenyl; heteroaryl, e.g., 5- or 6-membered ring heteroaryl, containing one or more heteroatoms N, O, or S, such as furanyl; each of these groups can be further substituted by one or more halogen atoms such as chloro or fluoro, C1-C10 alkyl, or C1-C10 alkyoxy. Each of R6 and R7 can be independently C1-C15 alkyl (e.g., C1-C10 alkyl or C1-C6 alkyl), C6-C14 aryl (e.g., phenyl), C3-C15 cycloalkyl (e.g., C5-C6 cycloalkyl), C7-C15 arylalkyl (e.g., C7-C12 aralkyl), or C7-C15 alkylaryl (e.g., C7-C12 alkylaryl). Each R8 can be independently absent, hydrogen, C1-C15 alkyl (e.g., C1-C10 alkyl or C1-C6 alkyl), C2 to C18 alkenyl (e.g., C2 to C8 alkenyl), C6-C14 aryl (e.g., phenyl, naphthyl, or halophenyl), C3-C15 cycloalkyl (e.g., C5-C6 cycloalkyl), C7-C15 arylalkyl (e.g., C7-C12 aralkyl), or C7-C15 alkylaryl (e.g., C7-C12 alkylaryl).
In some embodiments, m is 1. The diester compound has a formula of:
R5, R6, R7, and R8 are defined as above. In certain embodiments, each R5 is independently an aryl. For instance, the diester compound can have a formula of:
Each R16 is independently H, halogen, or a C1 to C18 hydrocarbyl group which can optionally form one or more saturated or unsaturated cyclic structures with the phenyl group it attaches to. Each R16 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group. For instance, each R16 can be independently H, halogen, a C1-C15 alkyl (e.g., C1-C10 alkyl or C1-C6 alkyl), C1-C15 alkoxy (e.g., C1-C10 alkoxy or C1-C6 alkoxy), C6-C14 aryl (e.g., phenyl), C3-C15 cycloalkyl, C7-C15 arylalkyl (e.g., C7-C12 aralkyl), or C7-C15 alkylaryl (e.g., C7-C12 alkylaryl). Exemplary R16 groups are H, halogen such as chloro or fluoro, a C1-C6 alkyl, C1-C6 alkoxy, phenyl, C7-C12 aralkyl, or C7-C12 alkylaryl. Each m′ is independently an integer from 0 to 5, for instance, from 0 to 3. Exemplary R6 and R7 groups are C1-C6 alkyl, phenyl, C5-C6 cycloalkyl, C7-C12 arylalkyl, or C7-C12 alkylaryl. Exemplary R8 groups are hydrogen; C1-C6 alkyl; C2 to C8 alkenyl; phenyl, naphthyl, or halophenyl; C5-C6 cycloalkyl; C7-C12 arylalkyl; or C7-C12 alkylaryl.
Exemplary diester compounds for formula IIb are 2,4-pentanediol dibenzoate, 3-methyl-2,4-pentanediol dibenzoate, 3-ethyl-2,4-pentanediol dibenzoate, 3-n-propyl-2,4-pentanediol dibenzoate, 3-i-propyl-2,4-pentanediol dibenzoate, 3-n-butyl-2,4-pentanediol dibenzoate, 3-i-butyl-2,4-pentanediol dibenzoate, 3-t-butyl-2,4-pentanediol dibenzoate, 3-n-pentyl-2,4-pentanediol dibenzoate, 3-i-pentyl-2,4-pentanediol dibenzoate, 3-cyclopentyl-2,4-pentanediol dibenzoate, 3-cyclohexyl-2,4-pentanediol dibenzoate, 3-phenyl-2,4-pentanediol dibenzoate, 3-(2-naphtyl)-2,4-pentanediol dibenzoate, 3-allyl-2,4-pentanediol dibenzoate, 3,3-dimethyl-2,4-pentanediol dibenzoate, 3-ethyl-3-methyl-2,4-pentanediol dibenzoate, 3-methyl-3-i-propyl-2,4-pentanediol dibenzoate, 3,3-diisopropyl-2,4-pentanediol dibenzoate, 3-i-pentyl-2-i-propyl-2,4-pentanediol dibenzoate, 3,5-heptanediol dibenzoate, 4,6-nonanediol dibenzoate, 2,6-dimethyl-3,5-heptanediol dibenzoate, 5,7-undecanediol dibenzoate, 2,8-dimethyl-4,6-nonanediol dibenzoate, 2,2,6,6,tetramethyl-3,5-hetanediol dibenzoate, 6,8-tridecanediol dibenzoate, 2,10-dimethyl-5,7-undecanediol dibenzoate, 1,3-dicyclopentyl-1,3-propanediol dibenzoate, 1,3-dicyclohexyl-1,3-propanediol dibenzoate, 1,3-diphenyl-1,3-propanediol dibenzoate, 1,3-bis(2-naphtyl)-1,3-propanediol dibenzoate, 2,4-hexanediol dibenzoate, 2,4-heptanediol dibenzoate, 2-methyl-3,5-hexanediol dibenzoate, 2,4-octanediol dibenzoate, 2-methyl-4,6-heptanediol dibenzoate, 2,2-dimethyl-3,5-hexanediol dibenzoate, 2-methyl-5,7-octanediol dibenzoate, 2,4-nonanediol dibenzoate, 1-cyclopentyl-1,3-butanediol dibenzoate, 1-cyclohexyl-1,3-butanediol dibenzoate, 1-phenyl-1,3-butanediol dibenzoate, 1-(2-naphtyl)-1,3-butanediol dibenzoate, 2,4-pentanediol-bis(4-methylbenzoate), 2,4-pentanediol-bis(3-methylbenzoate), 2,4-pentanediol-bis(4-ethylbenzoate), 2,4-pentanediol-bis(4-n-propylbenzoate), 2,4-pentanediol-bis(4-n-butylbenzoate), 2,4-pentanediol-bis(4-i-propylbenzoate), 2,4-pentanediol-bis(4-i-butylbenzoate), 2,4-pentanediol-bis(4-t-butylbenzoate), 2,4-pentanediol-bis(4-phenylbenzoate), 2,4-pentanediol-bis(3,4-dimethylbenzoate), 2,4-pentanediol-bis(2,4,6-trimethylbenzoate), 2,4-pentanediol-bis(2,6-dimethylbenzoate), 2,4-pentanediol-di-(2-naphthoate), 3-methyl-2,4-pentanediol-bis(4-n-propylbenzoate), 3-i-pentyl-2,4-pentanediol-bis(4-n-propylbenzoate), 1,1,1,5,5,5-hexafluoro-2,4-pentanediol-bis(4-ethylbenzoate), 1,1,1-trifluoro-2,4-pentanediol-bis(4-ethylbenzoate), 1,3-bis(4-chlorophenyl)-1,3-propanediol-bis(4-ethylbenzoate), pentafluorophenyl)-1,3-butanediol-bis(4-ethylbenzoate), 1,1-difluoro-4-phenyl-2,4-butandiol-bis(4-n-propylbenzoate), 1,1,1-trifluoro-5,5-dimethyl-2,4-hexandiol-bis(4-n-propylbenzoate), 1,1,1-trifluoro-4-(2-furyl)-2,4-butandiol-bis(4-n-propylbenzoate), 1,1,1-trifluoro-4-phenyl-2,4-butandiol-bis(4-n-propylbenzoate), 1,1,1-trifluoro-4-(2-thienyl)-2,4-butandiol-bis(4-n-propylbenzoate), 1,1,1-trifluoro-4-(4-chloro-phenyl)-2,4-butandiol-bis(4-n-propylbenzoate), 1,1,1-trifluoro-4-(2-naphtyl)-2,4-butandiol-bis(4-n-propylbenzoate), and 3-chloro-2,4-pentandiol-bis(4-n-propylbenzoate).
In some embodiments, m is 0, and R6 and R7 can form one or more saturated or unsaturated mono- or poly-cyclic structures. For instance, R6 and R7 can form an aryl group having the formula of:
R5 is defined as above. In certain embodiments, both R5 groups are an aryl. For instance, the diester compound can have a formula of:
Each of R16 and R17 is independently H, halogen, or a C1 to C18 hydrocarbyl group which can optionally form one or more saturated or unsaturated cyclic structures with the phenyl group it attaches to. Each of R16 and R17 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group. For instance, each of R16 and R17 can be independently H, halogen (e.g., chloro or fluoro), or a C1-C15 alkyl (e.g., C1-C10 alkyl or C1-C6 alkyl), C1-C15 alkoxy (e.g., C1-C10 alkoxy or C1-C6 alkoxy), C6-C14 aryl (e.g., phenyl), C3-C15 cycloalkyl, C7-C15 arylalkyl (e.g., C7-C12 aralkyl), or C7-C15 alkylaryl (e.g., C7-C12 alkylaryl). Exemplary R16 and R17 groups are H, halogen such as chloro or fluoro, a C1-C6 alkyl, C1-C6 alkoxy, phenyl, C7-C12 aralkyl, or C7-C12 alkylaryl. Each m′ is independently an integer from 0 to 5, for instance, from 0 to 3. Exemplary compounds for formula lid include those containing one or two R17 groups and one R16 on each benzoate moiety. For instance, exemplary compounds for formula IId can contain two R17 groups, one at para-position and one at ortho-position to the —O—C(O)— group; and can contain one R16 on each benzoate moiety, each at para-position to the —C(O)—O— group. A typical compound for formula IId is 5-(tert-butyl)-3-methyl-1,2-phenylene dibenzoate.
In some embodiments, m is 1, R8 is absent, and R6 and R7 can form a fused ring structure. For instance, R6 and R7 can form a naphthalene group, forming a 1,8-naphthalene diester compound having the formula of:
R5 is defined as above. Each R17 is independently H, halogen, or a C1 to C18 hydrocarbyl group which can optionally form one or more saturated or unsaturated cyclic structures with the phenyl group it attaches to. Each R17 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group. For instance, each R17 can be independently H, halogen (e.g., chloro or fluoro), or a C1-C15 alkyl (e.g., C1-C10 alkyl or C1-C6 alkyl), C1-C15 alkoxy (e.g., C1-C10 alkoxy or C1-C6 alkoxy), C6-C14 aryl (e.g., phenyl), C3-C15 cycloalkyl, C7-C15 arylalkyl (e.g., C7-C12 aralkyl), or C7-C15 alkylaryl (e.g., C7-C12 alkylaryl). Exemplary R17 groups are H, halogen such as chloro or fluoro, a C1-C6 alkyl, C1-C6 alkoxy, phenyl, C7-C12 aralkyl, or C7-C12 alkylaryl. Each m′ is independently an integer from 0 to 5, for instance, from 0 to 3.
In formula IIe, exemplary R5 groups are C1-C10 alkyl; C2-C10 alkenyl; C5-C6 cycloalkyl; C5-C6 cycloalkenyl; aryl such as phenyl; or heteroaryl, e.g., 5- or 6-membered ring heteroaryl, containing one or more heteroatoms N, O, or S, such as furanyl; each of these groups can be further substituted by one or more halogen atoms such as chloro or fluoro, C1-C10 alkyl, or C1-C10 alkyoxy. R5 may be the same or different.
In certain embodiments, both R5 groups are an aryl. For instance, the 1,8-napthalene diester compound can have a formula of:
The definition of R16 is the same as the definition of R17, which is defined above. The integer m′ is defined as above. Exemplary 1,8-napthalene diester compounds for formula IIf are 1,8-naphthyl dibenzoate; 1,8-naphthyl di-4-methylbenzoate; 1,8-naphthyl di-3-methylbenzoate; 1,8-naphthyl di-2-methylbenzoate; 1,8-naphthyl di-4-ethylbenzoate; 1,8-naphthyl di-4-n-propylbenzoate; 1,8-naphthyl di-4-isopropylbenzoate; 1,8-naphthyl di-4-n-butylbenzoate; 1,8-naphthyl di-4-isobutylbenzoate; 1,8-naphthyl di-4-t-butylbenzoate; 1,8-naphthyl di-4-phenylbenzoate; 1,8-naphthyl di-4-fluorobenzoate; 1,8-naphthyl di-3-fluorobenzoate; 1,8-naphthyl di-2-fluorobenzoate; 1,8-naphthyl di-4-chlorobenzoate; 1,8-naphthyl di-3-chlorobenzoate; 1,8-naphthyl di-2-chlorobenzoate; 1,8-naphthyl di-4-bromobenzoate; 1,8-naphthyl di-3-bromobenzoate; 1,8-naphthyl di-2-bromobenzoate; 1,8-naphthyl di-4-cyclohexylbenzoate; 1,8-naphthyl di-2,3-dimethylbenzoate; 1,8-naphthyl di-2,4-dimethylbenzoate; 1,8-naphthyl di-2,5-dimethylbenzoate; 1,8-naphthyl di-2,6-dimethylbenzoate; 1,8-naphthyl di-3,4-dimethylbenzoate; 1,8-naphthyl di-3,5-dimethylbenzoate; 1,8-naphthyl di-2,3-dichlorobenzoate; 1,8-naphthyl di-2,4-dichlorobenzoate; 1,8-naphthyl di-2,5-dichlorobenzoate; 1,8-naphthyl di-2,6-dichlorobenzoate; 1,8-naphthyl di-3,4-dichlorobenzoate; 1,8-naphthyl di-3,5-dichlorobenzoate; and 1,8-naphthyl di-3,5-di-t-butylbenzoate. A typical diester compound for formula IIf is 1,8-naphthyl dibenzoate.
Additional exemplary 1,8-napthalene diester compounds for formula IIe are
iii) Cyclic Diester Compound
The internal electron donor can be a cyclic diester compound having a formula of
Each R9 is independently H, halogen, or a C1 to C18 hydrocarbyl group. R9 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group. For instance, R9 can be C1 to C18 alkyl such as C1 to C8 alkyl; C2 to C18 alkenyl such as C2 to C8 alkenyl; C3 to C18 cycloalkyl such as C5 to C6 cycloalkyl; aryl such as phenyl; C1 to C18 alkoxy such as C1 to C8 alkoxy; siloxy; aldehyde; or acetyl. Exemplary R9 groups are methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, n-pentyl, cyclopentyl, n-hexyl, cyclohexyl, octyl, vinyl, or phenyl. Typically, R9 is methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, or sec-butyl. Two or more R9 groups may also be bonded to each other to form a saturated or unsaturated mono- or poly-cyclic structure backbone, e.g., a fused ring and/or bridged polycyclic backbone. Exemplary fused ring and/or bridged polycyclic backbone are norbornane
and tetracyclododecene
Each R10 is independently a C1 to C20 hydrocarbyl group. For example, R10 can be a C1 to C20 alkyl, C1 to C10 alkyl, C2 to C8 alkyl, or C4 to C8 alkyl. Exemplary R10 groups are ethyl, n-propyl, isopropyl, n-butyl, isobutyl, hexyl, heptyl, octyl, 2-ethylhexyl, decyl, dodecyl, tetradecyl, hexadecyl, octadecyl, or eicosyl. Typically, R10 is n-butyl or isobutyl.
Each R11 and R12 is independently R9 or —COOR10, provided that at least one of R11 and R12 is —COOR10.
The integer p ranges from 1 to 6. For instance p can be 1, 2, 3. Typically, p is 2.
In some embodiments, the cyclic diester compound has a formula of
In formulas IIIa and IIIb, each R10 is independently a C1 to C10 alkyl, and each R9 is independently H or a C1 to C8 alkyl, C3 to C6 cycloalkyl, C2 to C6 alkenyl, or phenyl. Exemplary cyclic diester compounds for formulas Ma and IIIb are diisobutyl cyclohexane-1,2-dicarboxylate, diethyl 3-methylcyclohexane-1,2-dicarboxylate, di-n-propyl 3-methylcyclohexane-1,2-dicarboxylate, diisopropyl 3-methylcyclohexane-1,2-dicarboxylate, di-n-butyl 3-methylcyclohexane-1,2-dicarboxylate, diisobutyl 3-methylcyclohexane-1,2-dicarboxylate, dihexyl 3-methylcyclohexane-1,2-dicarboxylate, diheptyl 3-methylcyclohexane-1,2-dicarboxylate, dioctyl 3-methylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3-methylcyclohexane-1,2-dicarboxylate, didecyl 3-methylcyclohexane-1,2-dicarboxylate, diethyl 4-methylcyclohexane-1,3-dicarboxylate, diisobutyl 4-methylcyclohexane-1,3-dicarboxylate, diethyl 4-methylcyclohexane-1,2-dicarboxylate, di-n-propyl 4-methylcyclohexane-1,2-dicarboxylate, diisopropyl 4-methylcyclohexane-1,2-dicarboxylate, di-n-butyl 4-methylcyclohexane-1,2-dicarboxylate, diisobutyl 4-methylcyclohexane-1,2-dicarboxylate, dihexyl 4-methylcyclohexane-1,2-dicarboxylate, diheptyl 4-methylcyclohexane-1,2-dicarboxylate, dioctyl 4-methylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 4-methylcyclohexane-1,2-dicarboxylate, didecyl 4-methylcyclohexane-1,2-dicarboxylate, diethyl 5-methylcyclohexane-1,3-dicarboxylate, diisobutyl 5-methylcyclohexane-1,3-dicarboxylate, diethyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, di-n-propyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, diisopropyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, di-n-butyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, diisobutyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, dihexyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, diheptyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, dioctyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, didecyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, diethyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, di-n-propyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, diisopropyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, di-n-butyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, diisobutyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, dihexyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, diheptyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, dioctyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, didecyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, diethyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, di-n-propyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, diisopropyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, di-n-butyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, diisobutyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, dihexyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, dioctyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, didecyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, diethyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-n-propyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diisopropyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-n-butyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diisobutyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, dihexyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diheptyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, dioctyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, didecyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diethyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-n-propyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diisopropyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-n-butyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diisobutyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, dihexyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diheptyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, dioctyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, didecyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diethyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, di-n-propyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, diisopropyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, di-n-butyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, diisobutyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, dihexyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, diheptyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, dioctyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, dodecyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, diethyl 3-hexylcyclohexane-1,2-dicarboxylate, diisobutyl 3-hexylcyclohexane-1,2-dicarboxylate, diethyl 3,6-dihexylcyclohexane-1,2-dicarboxylate, and diisobutyl 3-hexyl-6-pentylcyclohexane-1,2-dicarboxylate. Typically, the cyclic diester compound is diisobutyl cyclohexane-1,2-dicarboxylate or diisobutyl 3,6-dimethylcyclohexane-1,2-dicarboxylate. Mixtures of two or more such cyclic diester compounds may be used as well.
iv) Succinate Compound
The internal electron donor can be a succinate compound having a formula of
Each of R13 and R14 is independently a C1 to C18 hydrocarbyl group. For instance, each of R13 and R14 can be C1 to C18 alkyl, C2 to C18 alkenyl, C3 to C18 cycloalkyl, or aryl. The alkyl, alkenyl, cycloalkyl, and aryl for each R group can be further substituted with one or more of alkyl, cycloalkyl, aryl, or halogen groups. Each of R13 and R14 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group. Typically, R13 is C1 to C6 alkyl, C5-C6 cycloalkyl, phenyl, fluorenyl; each of these groups can be optionally substituted with one or more of C1 to C6 alkyl, C5-C6 cycloalkyl, phenyl, or halogen atoms such as fluoro or chloro. Typically, R14 is C1 to C6 alkyl.
Exemplary succinate compounds are diethyl 2-sec-butyl-3-methylsuccinate, diethyl 2-(3,3,3-trifluoropropyl)-3-methylsuccinate, diethyl 2,3-bis(2-ethylbutyl) succinate, diethyl 2,3-diethyl-2-isopropylsuccinate, diethyl 2,3-diisopropyl-2-methylsuccinate, diethyl 2,3-dicyclohexyl-2-methylsuccinate, diethyl 2,3-dibenzylsuccinate, diethyl 2,3-diisopropylsuccinate, diethyl 2,3-bis (cyclohexylmethyl)succinate, diethyl 2,3-di-t-butylsuccinate, diethyl 2,3-diisobutylsuccinate, diethyl 2,3-dineopentylsuccinate, diethyl 2,3-diisopentylsuccinate, diethyl 2,3-(1-trifluoromethyl-ethyl)succinate, diethyl 2-(9-fluorenyl)succinate, diethyl 2-isopropyl-3-isobutylsuccinate, diethyl 2-t-butyl-3-isopropylsuccinate, diethyl 2-isopropyl-1,3-cyclohexylsuccinates diethyl 2-isopentyl-3-cyclohexylsuccinate, diethyl 2-cyclohexyl-3-cyclopentylsuccinate, diethyl 2,2,3,3-tetramethylsuccinate, diethyl 2,2,3,3-tetraethylsuccinate, diethyl 2,2,3,3-tetra-n-propylsuccinate, diethyl 2,3-diethyl-2,3-diisopropylsuccinate, diisobutyl 2,3-bis(trimethylsilyl)succinate, diisobutyl 2-sec-butyl-3-methylsuccinate, diisobutyl 2-(3,3,3-trifluoropropyl)-3-methylsuccinate, diisobutyl 2,3-bis(2-ethylbutyl)succinate, diisobutyl 2,3-diethyl-2-isopropylsuccinate, diisobutyl 2,3-diisopropyl-2-methylsuccinate, diisobutyl 2,3-dicyclohexyl-2-methylsuccinate, diisobutyl 2,3-dibenzylsuccinate, diisobutyl 2,3-diisopropylsuccinate, diisobutyl 2,3-bis(cyclohexylmethyl)succinate, diisobutyl 2,3-di-t-butylsuccinate, diisobutyl 2,3-diisobutylsuccinate, diisobutyl 2,3-dineopentylsuccinate, diisobutyl 2,3-diisopentylsuccinate, diisobutyl 2,3-bis(3,3,3-trifluoropropyl)succinate, diisobutyl 2,3-di-n-propylsuccinate, diisobutyl 2-(9-fluorenyl)succinate, diisobutyl 2-isopropyl-3-isobutylsuccinate, diisobutyl 2-t-butyl-3-isopropylsuccinate, diisobutyl 2-isopropyl-3-cyclohexylsuccinate, diisobutyl 2-isopentyl-3-cyclohexylsuccinate, diisobutyl 2-n-propyl-3-(cyclohexylmethyl)succinate, diisobutyl 2-cyclohexyl-3-cyclopentylsuccinate, diisobutyl 2,2,3,3-tetramethylsuccinate, diisobutyl 2,2,3,3-tetraethylsuccinate, diisobutyl 2,2,3,3-tetra-n-propylsuccinate, diisobutyl 2,3-diethyl-2,3-diisopropylsuccinate, dineopentyl 2,3-bis(trimethylsilyl)succinate, dineopentyl 2,2-di-sec-butyl-3-methylsuccinate, dineopentyl 2-(3,3,3-trifluoropropyl)-3-methylsuccinate, dineopentyl 2,3 bis-(2-ethylbutyl)succinate, dineopentyl 2,3-diethyl-2-isopropylsuccinate, dineopentyl 2,3-diisopropyl-2-methylsuccinate, dineopentyl 2,3-dicyclohexyl-2-methylsuccinate, dineopentyl 2,3-dibenzylsuccinate, dineopentyl 2,3-diisopropylsuccinate, dineopentyl 2,3-bis-(cyclohexylmethyl)succinate, dineopentyl 2,3-di-t-butylsuccinate, dineopentyl 2,3-diisobutylsuccinate, dineopentyl 2,3-dineopentylsuccinate, dineopentyl 2,3-diisopentylsuccinate, dineopentyl 2,3-bis(3,3,3-trifluoropropyl)succinate, dineopentyl 2,3-n-propylsuccinate, dineopentyl 2-(9-fluorenyl)succinate, dineopentyl 2-isopropyl-3-isobutylsuccinate, dineopentyl 2-t-butyl-3-isopropylsuccinate, dineopentyl 2-isopropyl-3-cyclohexylsuccinate, dineopentyl 2-isopentyl-3-cyclohexylsuccinate, dineopentyl 2-n-propyl-3-(cyclohexylmethyl)succinate, dineopentyl 2-cyclohexyl-3-cyclopentylsuccinate, dineopentyl 2,2,3,3-tetramethylsuccinate, dineopentyl 2,2,3,3-tetra-ethylsuccinate, dineopentyl 2,2,3,3-tetra-n-propylsuccinate, dineopentyl 2,3-diethyl-2,3-diisopropylsuccinate, diethyl 1,2-cyclohexanedicarboxylate, and diethyl norbornene-2,3-dicarboxylate. Typically, the succinate compound is diethyl 2,3-diisopropylsuccinate. Mixtures of two or more such succinate compounds may be used as well.
Preparation of Solid Ziegler-Nata Catalyst Composition
The solid Ziegler-Nata procatalyst composition can be carried out by various methods known to one skilled in the art. For instance, the titanium compound, the magnesium dichloride in an anhydrous state, and the electron donor compounds can be milled together under conditions in which activation of the magnesium dichloride occurs. The product can be treated one or more times with an excess of TiCl4 at a temperature about 80 to 135° C., followed by washings with hydrocarbon solvents until chloride ions disappear. Alternatively, magnesium dichloride is preactivated by methods known to one skilled in the art, and then treated with an excess of TiCl4 at a temperature of about 80 to 135° C. in the presence of the electron donor compounds. The treatment with TiCl4 can be repeated and the solid can be washed with a hydrocarbon solvent such as hexane to eliminate any non-reacted TiCl4.
In another example, the titanium compound, the magnesium chloride in an anhydrous state, the electron donor compounds can be milled together under conditions in which activation of the magnesium chloride occurs. The product can be treated with halogenated hydrocarbons such as 1,2-dichloroethane, chlorobenzene, dichloromethane, etc., for about 1 and 4 hours and at temperature of from 40° C. to the boiling point of the halogenated hydrocarbon. The product is then washed with inert hydrocarbon solvents such as hexane.
In another example, the solid catalyst component can be prepared by reacting a titanium compound of formula TiXx or Ti(OQ)gX4-g with a magnesium chloride deriving from an adduct of formula (MgCl2)pROH, in which p is a number between 0.1 and 6, for instance, between 2 to 3.5; and R is a C1-C18 hydrocarbyl. The adduct can be suitably prepared in spherical form by mixing alcohol and magnesium chloride in the presence of an inert hydrocarbon immiscible with the adduct, operating under stirring conditions at the melting temperature of the adduct (100-130° C.). The emulsion can then be quenched, causing the solidification of the adduct in form of spherical particles. Examples of spherical adducts prepared according to this procedure are described in U.S. Pat. Nos. 4,399,054 and 4,469,648, which are incorporated herein by reference in their entirety. The obtained adduct can be directly reacted with the titanium compound. Alternatively, the obtained adduct can be first subjected to thermally controlled dealcoholation (at 80-130° C.) to obtain an adduct in which the number of moles of alcohol is generally lower than 3, for instance, between 0.1 and 2.5. The reaction of the adduct with the titanium compound can be carried out by suspending the adduct (dealcoholated or not) in cold TiCl4 (generally at 0° C.), and heating the mixture to about 80-130° C. (the temperature can be kept at this range for about 0.5-2 hours). The treatment with TiCl4 can be carried out one or more times. The electron donor compounds can be added during the treatment with TiCl4, and can be added together in the same treatment with TiCl4 or separately in two or more treatments.
The preparations of the solid catalyst components in spherical forms are described, for example, in WO98/44001 and U.S. Patent Application Publication No. 2013/0197173, which are incorporated herein by reference in their entirety.
The solid Ziegler-Nata procatalyst composition can contain from about 0.5 to about 6.0 wt % titanium; from about 10 to about 25 wt % magnesium; from about 40 to about 70 wt % halogen; from about 1 to about 50 wt % internal electron donor compound; and optionally inert diluent from about 0 to about 15 wt %. For instance, the Ziegler-Nata procatalyst composition contains from about 2 to about 20 wt % of one or more of the internal electron donor compounds, or from about 5 to about 15 wt % of one or more of the internal electron donor compounds.
The amounts of the components used in preparing the solid Ziegler-Nata procatalyst composition may vary depending upon the method of preparation. For instance, from about 0.01 to about 5 moles of the total internal electron donor compounds and from about 0.01 to about 500 moles of the titanium compound are used per mole of the magnesium compound used to make the solid procatalyst composition. Typically, from about 0.05 to about 2 moles of the total internal electron donor compounds and from about 0.05 to about 300 moles of the titanium compound are used per mole of the magnesium compound used to make the solid procatalyst composition.
The Ziegler-Natta procatalyst composition may also include an inert support material. The support material may be an inert solid which does not adversely alter the catalytic performance of the transition metal compound. Exemplary inert support materials include metal oxides, such as alumina, and metalloid oxides, such as silica.
Cocatalyst
The non-phthalate catalyst system may further comprise an organometallic cocatalyst. The metal element in the organometallic cocatalyst is a Group 13 metal, for instance, aluminum. Suitable organoaluminum compounds include those having at least one aluminum-carbon bond in the molecule, such as alkylaluminum, alkylaluminum hydride, alkylaluminum halide, and alkylaluminum alkoxide containing from 1-10 or 1-6 carbon atoms in each alkyl or alkoxide group. Exemplary organoaluminum compounds are trialkyl aluminums, such as triethyl aluminum and tributyl aluminum; trialkenyl aluminums such as triisoprenyl aluminum; dialkyl aluminum alkoxides such as diethyl aluminum ethoxide and dibutyl aluminum butoxide; alkyl aluminum sesquialkoxides such as ethyl aluminum sesquiethoxide and butyl aluminum sesquibutoxide; dialkyl aluminum halides such as diethyl aluminum chloride, dibutyl aluminum chloride and diethyl aluminum bromide; alkyl aluminum sesquihalides such as ethyl aluminum sesquichloride, butyl aluminum sesquichloride, and ethyl aluminum sesquibromide; partially halogenated alkyl aluminums, e.g., alkyl aluminum dihalides such as ethyl aluminum dichloride, propyl aluminum dichloride, and butyl aluminum dibromide; dialkyl aluminum hydrides such as diethyl aluminum hydride and dibutyl aluminum hydride; other partially hydrogenated alkyl aluminum, e.g., alkyl aluminum dihyrides such as ethyl aluminum dihydride and propyl aluminum dihydride; and partially alkoxylated and halogenated alkyl aluminums, such as ethyl aluminum ethoxychloride, butyl aluminum butoxychloride, and ethyl aluminum ethoxybromide.
The organometallic cocatalyst used in the non-phthalate catalyst system is in an amount that the molar ratio of the metal in the organometallic cocatalyst to transition metal in the Ziegler-Natta procatalyst composition is from about 5 to about 1000, for instance, from about 10 to about 700, from about 25 to about 400, or from about 100 to about 300.
External Donor
The non-phthalate catalyst system also includes one or more non-silane external electron donor compounds. The external electron donor is a compound added independent of the Ziegler-Natta procatalyst formation, and contains at least one functional group that is capable of donating a pair of electrons to a metal atom. The external electron donor compound serves as one component of the non-phthalate Ziegler-Natta catalyst system for olefin polymerization, often contributing to the ability to obtain a polymer having a controllable molecular weight distribution and controllable crystallinity. In fact, when an external donor compound is absent, the isotactic index of the resulting polymer is not sufficiently high even if the internal donor is used. Also, for the non-phthalate catalyst system, the conventional alkoxysilane external donors often times do not have significant modifying effect on the performance of the non-phthalate catalyst system. The non-silane external donors below are chemically different from alkoxysilanes and provide improvements in the performance of the non-phthalate catalyst system.
The external donor compound is used in the non-phthalate catalyst system in an amount that the molar ratio of the total external donor compounds to the transition metal in the Ziegler-Natta procatalyst composition (e.g., titanium compound) ranges from about 0.5 to about 90, for instance, from about 1 to about 70, or from about 1 to about 30.
i) Triester Compound
The external electron donor can be a triester compound having a formula of
Each R is independently a C1-C10 hydrocarbyl group. For instance, each R is a C1 to C10 alkyl, such as methyl, ethyl, or isobutyl; optionally substituted with methyl, isobutyl, or 2-ethylhexyl. Each R′ is independently H or R. Each n is independently an integer from 1 to 4, for instance, from 1 to 2, or 1. The integer n′ ranges from 0 to 4, for instance, from 0 to 2 or 0. A typical triester compound is glyceryl triacetate
also referred to as triacetin), in which R is methyl, R′ is H, n is 1, and n′ is 0.
ii) Diester Compound
The external electron donor can be a diester compound having a formula of
X is CH2 or O. Each R is independently a C1-C10 hydrocarbyl group. For instance, each R is a C1 to C10 alkyl, such as methyl, ethyl, or isobutyl; optionally substituted with methyl, isobutyl, or 2-ethylhexyl. Each R′ is independently H or R. Each n is independently an integer from 1 to 4, for instance, from 1 to 2. Typical diester compounds include those having R as methyl, R′ as H, and n as 2. For instance, two typical diester compounds are 1,5-pentanediol diacetate (PDOA,
and diethyleneglycol diacetate (DEGA,
iii) Oxo-Substituted Diester Compound
The external electron donor can be an oxo-substituted triester compound having a formula of
Each R is independently a C1-C10 hydrocarbyl group. For instance, each R is a C1 to C10 alkyl, such as methyl, ethyl, or isobutyl; optionally substituted with methyl, isobutyl, or 2-ethylhexyl. Each R′ is independently H or R. Each n is independently an integer from 1 to 4, for instance, from 1 to 2. A typical oxo-substituted triester compound is diethyl-4-oxopimelate (DEOP,
in which each R is methyl, each R′ is H, and each n is 2.
A second aspect of the invention relates to a non-phthalate catalyst system for olefin polymerization. The non-phthalate catalyst system comprises (a) a solid Ziegler-Natta catalyst composition comprising a transition metal, a Group 2 metal, and one or more halogens; and one or more internal electron donor compounds; and (b) one or more external electron donor compounds.
The internal electron donor compound is i) a diester compound having a formula of
or ii) a cyclic diester compound having a formula of
In these formulas, each R5 is independently a C1 to C18 hydrocarbyl group which can optionally form one or more saturated or unsaturated mono- or poly-cyclic structures. Each R17 is independently H, halogen, or C1 to C18 hydrocarbyl group which can optionally form one or more saturated or unsaturated cyclic structures with the phenyl group it is attached to. Each R9 is independently H, halogen, or C1 to C18 hydrocarbyl group. Each R10 is independently C1 to C20 hydrocarbyl group. Each of R11 and R12 is independently R9 or —COOR10, provided that at least one of R11 and R12 is —COOR10. Each m′ is independently an integer from 0 to 5. The integer p ranges from 1 to 6. Each of R5, R9, and R17 can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group.
In certain embodiments, the internal donor is a diester compound having a formula of
The definition of m′, R5, and R17, and the exemplary embodiments for the m′, R5, and R17 groups are the same as those described for formula IIe in the first aspect of the invention.
A typical diester compound has a formula of:
The definition of m′, R16, and R17 and the exemplary embodiments for the m′, R16, and R17 groups are the same as those described for formula IIf in the first aspect of the invention. The exemplary 1,8-napthalene diester compounds are the same as those exemplary 1,8-napthalene diester compounds described for formula IIf in the first aspect of the invention.
Additional exemplary 1,8-napthalene diester compounds described for formula He in the first aspect of the invention also can be used in this aspect of the invention as the internal electron donor.
In certain embodiments, the internal donor is a cyclic diester compound having a formula of
The definitions of p, R9, R10, R11, and R12 and the exemplary embodiments for the p, R9, R10, R11, and R12 groups are the same as those described for formula III in the first aspect of the invention.
A typical cyclic diester compound has a formula of
The definitions of R9 and R10, and the exemplary embodiments for the R9 and R10 groups are the same as those described for formula IIIa and Mb in the first aspect of the invention. The exemplary cyclic diester compounds are the same as those exemplary cyclic diester compounds described for formulas IIIa and IIIb in the first aspect of the invention.
The non-phthalate catalyst system also includes one or more external electron donor compounds having a formula of
The external electron donor compound does not contain an alkoxysilane compound. In formula VIII, each R is independently a C1 to C10 hydrocarbyl group, and can contain one or more heteroatoms, selected from the group consisting of halogens, P, N, O, S, and Si, that replace one or more carbon atoms in the hydrocarbyl group. R′ is H or R. For instance, each R is a C1 to C10 alkyl, such as methyl, ethyl, propyl, butyl, or hexyl; C3-C8 cycloalkyl, such as C5-C6 cycloalkyl; or C3-C8 heterocycloalkyl, such as C5-C6 heterocycloalkyl containing one or more heteroatoms N, O, or S (e.g., piperidinyl); each of these groups can be optionally substituted with one or more C1 to C10 alkyl, such as methyl, ethyl, isobutyl, or 2-ethylhexyl. The integer n ranges from 1 to 10, for instance, from 1 to 8.
Exemplary external electron donor compounds for formula VIII include those containing R as methyl, ethyl, propyl, butyl, hexyl, or piperidinyl; optionally substituted with one or more C1-C6 alkyl; R′ as H; and n as 1 to 8. Typical external electron donor compounds for formula VIII are diethyl malonate, diethyl succinate, diethyl glutarate, diethyl adipate, diisopropyl adipate, dibutyl adipate, diisobutyl adipate, bis (2-ethylhexyl) adipate, diethyl pimelate, diethyl azelate, diethyl sebacate, and bis(2,2,6,6-tetramethyl-4-piperidyl) sebacate (e.g., Tinuvin® 770,
In this aspect of the invention, the transition metal compound and Group 2 metal compounds in the Ziegler-Natta procatalyst, and the preparation of solid Ziegler-Natta procatalyst composition are the same as those described in the first aspect of the invention. The organometallic cocatalyst in the non-phthalate catalyst system is the same as those described in the first aspect of the invention.
Process of Polymerization
Another aspect of the invention relates to a process for preparing a polyolefin. The process comprises polymerizing one or more olefins, in the presence of the non-phthalate catalyst system under reaction conditions known by one skilled in the art sufficient to form the polyolefin. The non-phthalate catalyst system may be any non-phthalate catalyst system described herein according to the embodiments in the first and second aspects of the invention.
The reaction conditions are temperature and pressure ranges within a polymerization reactor suitable for promoting polymerization and/or copolymerization between one or more olefins and the non-phthalate catalyst system to form the desired polymer. The polymerization process may be performed in any manner including gas phase, slurry, or a bulk polymerization process, with the polymerization occurring in one or more reactor(s).
The olefins may be linear or branched olefins having 2 to 20 carbon atoms, 2 to 16 carbon atoms, or 2 to 12 carbon atoms. Typically, the olefin used to prepare the polyolefin is an α-olefin. Exemplary linear or branched α-olefins includes, but are not limited to, ethylene, propylene, 1-butene, 2-butene, 1-pentene, 3-methyl-1-butene, 4-methyl-1-pentene, 3-methyl-1-pentene, 1-hexene, 3,5,5-trimethyl-1-hexene, 4,6-dimethyl-1-heptene, 1-octene, 1-decene, 1-undecene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene, and 1-eicocene. For instance, the olefin used to prepare a polyolefin is propylene. These olefins may contain one or more heteroatoms such as an oxygen, nitrogen, or silicon. The olefin may be used individually or in mixture, either the gaseous state or the liquid state.
The polymerization process may include a pre-activation step. Pre-activation includes contacting the Ziegler-Natta procatalyst composition with the cocatalyst and the external electron donor compound. The resulting preactivated catalyst stream is subsequently introduced into the polymerization reaction zone and contacted with the olefin monomer to be polymerized. Optionally, one or more of the external electron donor components may be added at this time. Pre-activation results in the combination of the procatalyst composition with the cocatalyst and the external electron donor compounds.
Alternatively, the polymerization process may include a pre-polymerization step. Pre-polymerization includes contacting a small amount of the olefin with the Ziegler-Natta procatalyst composition after the procatalyst composition has been contacted with the cocatalyst and the external donor compound. Then, the resulting preactivated catalyst stream is introduced into the polymerization reaction zone and contacted with the remainder of the olefin monomer to be polymerized. Optionally, one or more of the external electron donor components may be added at this time. Pre-polymerization results in the procatalyst composition being combined with the cocatalyst and the external electron donor compounds, with the combination being dispersed in a matrix of the polymer during polymerization, to facilitate the polymerization.
Typically, a catalyst is considered to be pre-polymerized when the amount of the polymer produced is from about 0.1 to about 1000 gram per gram of the solid catalyst system. The pre-polymerization step can be carried out at temperatures from about 0° C. to about 80° C., for instance, from 5° C. to 50° C., in liquid or gas phase. The pre-polymerization step can be performed in-line as a part of a continuous polymerization process or separately in a batch process.
Any kind of polymerization process suitable for preparing a polyolefin can be used with the non-phthalate catalyst system. The polymerization can be carried out, for example, in bulk phase using a liquid monomer (e.g., propylene) as a reaction medium, in slurry using an inert liquid (e.g., hydrocarbon) as a diluent, in solution using either monomers or inert hydrocarbons as solvent for the nascent polymer, or in gas phase, operating in one or more fluidized or mechanically agitated bed reactors.
The polymerization process can be a gas phase polymerization process, operating in one or more reactors. A suitable gas phase polymerization process includes the use of condensing mode as well as super condensing mode wherein gaseous components (including addition of inert low boiling compounds) are injected into the reactor in liquid form. When multiple reactors are employed, it is desirable that they operate in series, e.g., the effluent from the first reactor is charged to the second reactor, with an additional monomer (for homopolymerization) or different monomer (for copolymerization) added to continue the polymerization. Additional amount of the same or different non-phthalate catalyst system or catalyst components (e.g., the procatalyst composition, cocatalyst, or external donor compound) may be added.
As an example, the polymerization process includes preparing an ethylene-propylene copolymer by contacting propylene and ethylene with the non-phthalate catalyst system. For instance, the polymerization process can be conducted in two reactors in which two olefins, such as propylene and ethylene, are contacted to prepare a copolymer. Polypropylene is prepared in the first reactor by a bulk phase (e.g., solution) homopolymerization, and a copolymer of ethylene and propylene is prepared in the second reactor in the presence of the polypropylene from the first reactor by a gas phase copolymerization. Alternatively, the polymerization process can be conducted in one reactors but in two sequential steps, with a bulk phase homopolymerization of polypropylene in the first step, and a a gas phase copolymerization of ethylene and propylene in the presence of the polypropylene in the second step. This process is exemplified in Example 2. Regardless of the polymerization technique employed, it is understood that the procatalyst composition, the cocatalyst, and the external electron donor thereof may be contacted in the absence of other polymerization components, especially monomer, prior to addition to the reactor.
The temperature of the polymerization process can range from about 20 to about 130° C., from about 60 to about 100° C., or from about 70° C. to about 85° C. For instance, when the polymerization is carried out in gas phase, the temperature of the polymerization process can range from about 75 to about 85° C., for instance at about 80° C.; when the polymerization is carried out in bulk phase, the temperature of the polymerization process can range from about 70 to about 80° C., for instance at about 75° C. When the polymerization is carried out in gas phase, the operating pressure generally ranges from about 0.5 to about 10 MPa, from about 0.9 to about 5 MPa, or from about 4 to about 5 MPa. In the bulk polymerization, the operating pressure generally ranges from about 0.5 to about 6 MPa, from about 0.9 to about 4 MPa, or from about 3.5 to about 4 MPa.
The resulting polymer prepared according to the above process, using the non-phthalate catalyst system described in this invention, has an improved isotacticity. Moreover, the resulting polymer prepared according to the process of the invention has an improved hydrogen response characterized by melt flow rate. Surprisingly, the polymer prepared by the non-phthalate catalyst system described in this invention, with the non-silane external donors, can have improved hydrogen response and isotacticity at the same time. This is surprising behavior because, in a typical Ziegler-Natta catalyst system, the external donors that increase hydrogen response (i.e., characterized by MFR) typically decrease isotacticity (i.e., characterized by increased % XS).
In some embodiments, the non-phthalate catalyst system used contains the internal electron donor compound that is a diether compound having a formula of
and the external electron donor compound that is a triester compound having a formula of
or a diester compound having a formula of
The definitions of R3, R4, R15, R, R′, q, and n are the same as those described for formula Ib, V, and VI in the first aspect of the invention. The exemplary internal donor compounds and external donor compounds are the same as those exemplary compounds described for formulas Ib, V, and VI in the first aspect of the invention.
For instance, in a typical non-phthalate catalyst system, the internal electron donor compound is 9,9-bis(methoxymethyl)fluorene, and the external electron donor compound is triacetin, 1,5-pentanediol diacetate, diethyl-4-oxopimelate, or diethyleneglycol diacetate. For instance, one non-phthalate catalyst system uses 9,9-bis(methoxymethyl)fluorene as the internal electron donor compound and triacetin as the external electron donor compound; another non-phthalate catalyst system uses 9,9-bis(methoxymethyl)fluorene as the internal electron donor compound and diethyl-4-oxopimelate as the external electron donor compound. In these embodiments, the polymer prepared according to the process of the invention has an improved isotacticity. Moreover, the resulting polymer prepared according to the process of the invention has an improved hydrogen response characterized by melt flow rate. Surprisingly, the polymer prepared by the non-phthalate catalyst system described in this invention, with the non-silane external donors, can have improved hydrogen response and isotacticity at the same time. This is surprising behavior because, in a typical Ziegler-Nana catalyst system, the external donors that increase hydrogen response (i.e., characterized by MFR) mostly decrease isotacticity (i.e., characterized by increased % XS).
In some embodiments, the non-phthalate catalyst system used contains the internal electron donor compound that is a diester compound having a formula of
and one or more external electron donor compounds having a formula of
The definitions of R16, R17, R, R′, m′, and n are the same as those described for formula IIf and VIII in the first and second aspect of the invention. The exemplary internal donor compounds and external donor compounds are the same as those exemplary compounds described for formulas IIf and VIII in the first and second aspect of the invention.
For instance, in a typical non-phthalate catalyst system, the internal electron donor compound is 1,8-naphthyl dibenzoate, and the external electron donor compound is diethyl adipate, diethyl pimelate, diethyl sebacate, triacetin, Tinuvin 770® (bis(2,2,6,6-tetramethyl-4-piperidyl) sebacate), 1,5-pentanediol diacetate, diethyl-4-oxopimelate, or diethyleneglycol diacetate. For instance, one non-phthalate catalyst system uses 1,8-naphthyl dibenzoate as the internal electron donor compound and triacetin as the external electron donor compound; another non-phthalate catalyst system uses 1,8-naphthyl dibenzoate as the internal electron donor compound and diethyl-4-oxopimelate as the external electron donor compound. In these embodiments, the polymer prepared according to the process of the invention has an improved isotacticity. Moreover, the resulting polymer prepared according to the process of the invention has an improved hydrogen response characterized by melt flow rate. Surprisingly, the polymer prepared by the non-phthalate catalyst system described in this invention, with the non-silane external donors, can have improved hydrogen response and isotacticity at the same time. This is surprising behavior because, in a typical Ziegler-Natta catalyst system, the external donors that increase hydrogen response (i.e., characterized by MFR) mostly decrease isotacticity (i.e., characterized by increased % XS).
In some embodiments, the non-phthalate catalyst system used contains the internal electron donor compound that is a cyclic diester compound having a formula of
and one or more external electron donor compounds having a formula of
The definitions of R9, R10, R, R′, and n are the same as those described for formula IIIa, IIIb, and VIII in the first and second aspect of the invention. The exemplary internal donor compounds and external donor compounds are the same as those exemplary compounds described for formulas IIIa, IIIb, and VIII in the first and second aspect of the invention.
For instance, in a typical non-phthalate catalyst system, the internal electron donor compound is selected from the group consisting of diisobutyl cyclohexane-1,2-dicarboxylate, diethyl 3-methylcyclohexane-1,2-dicarboxylate, di-n-propyl 3-methylcyclohexane-1,2-dicarboxylate, diisopropyl 3-methylcyclohexane-1,2-dicarboxylate, di-n-butyl 3-methylcyclohexane-1,2-dicarboxylate, diisobutyl 3-methylcyclohexane-1,2-dicarboxylate, dihexyl 3-methylcyclohexane-1,2-dicarboxylate, diheptyl 3-methylcyclohexane-1,2-dicarboxylate, dioctyl 3-methylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3-methylcyclohexane-1,2-dicarboxylate, didecyl 3-methylcyclohexane-1,2-dicarboxylate, diethyl 4-methylcyclohexane-1,3-dicarboxylate, diisobutyl 4-methylcyclohexane-1,3-dicarboxylate, diethyl 4-methylcyclohexane-1,2-dicarboxylate, di-n-propyl 4-methylcyclohexane-1,2-dicarboxylate, diisopropyl 4-methylcyclohexane-1,2-dicarboxylate, di-n-butyl 4-methylcyclohexane-1,2-dicarboxylate, diisobutyl 4-methylcyclohexane-1,2-dicarboxylate, dihexyl 4-methylcyclohexane-1,2-dicarboxylate, diheptyl 4-methylcyclohexane-1,2-dicarboxylate, dioctyl 4-methylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 4-methylcyclohexane-1,2-dicarboxylate, didecyl 4-methylcyclohexane-1,2-dicarboxylate, diethyl 5-methylcyclohexane-1,3-dicarboxylate, diisobutyl 5-methylcyclohexane-1,3-dicarboxylate, diethyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, di-n-propyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, diisopropyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, di-n-butyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, diisobutyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, dihexyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, diheptyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, dioctyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, didecyl 3,4-dimethylcyclohexane-1,2-dicarboxylate, diethyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, di-n-propyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, diisopropyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, di-n-butyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, diisobutyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, dihexyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, diheptyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, dioctyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, didecyl 3,6-dimethylcyclohexane-1,2-dicarboxylate, diethyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, di-n-propyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, diisopropyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, di-n-butyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, diisobutyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, dihexyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, dioctyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, didecyl 3,6-diphenylcyclohexane-1,2-dicarboxylate, diethyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-n-propyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diisopropyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-n-butyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diisobutyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, dihexyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diheptyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, dioctyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, didecyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diethyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-n-propyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diisopropyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-n-butyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diisobutyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, dihexyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diheptyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, dioctyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, didecyl 3-methyl-6-ethylcyclohexane-1,2-dicarboxylate, diethyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, di-n-propyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, diisopropyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, di-n-butyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, diisobutyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, dihexyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, diheptyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, dioctyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, di-2-ethylhexyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, dodecyl 3-methyl-6-n-propylcyclohexane-1,2-dicarboxylate, diethyl 3-hexylcyclohexane-1,2-dicarboxylate, diisobutyl 3-hexylcyclohexane-1,2-dicarboxylate, diethyl 3,6-dihexylcyclohexane-1,2-dicarboxylate, and diisobutyl 3-hexyl-6-pentylcyclohexane-1,2-dicarboxylate; and the external electron donor compound is diethyl adipate, diethyl pimelate, diethyl sebacate, triacetin, 1,5-pentanediol diacetate, diethyl-4-oxopimelate, or diethyleneglycol diacetate. For instance, the non-phthalate catalyst system uses one of the above-listed compounds as the internal electron donor compound, and triacetin or diethyl-4-oxopimelate as the external electron donor compound. In these embodiments, the polymer prepared according to the process of the invention has an improved isotacticity. an improved hydrogen response characterized by melt flow rate, and in some cases an increased gas phase activity and/or broadened molecular weight distribution. Surprisingly, the polymer prepared by the non-phthalate catalyst system described in this invention, with the non-silane external donors, can have improved hydrogen response and isotacticity at the same time. This is surprising behavior because, in a typical Ziegler-Natta catalyst system, the external donors that increase hydrogen response (i.e., characterized by MFR) mostly decrease isotacticity (i.e., characterized by increased % XS).
Additional aspects, advantages and features of the invention are set forth in this specification, and in part will become apparent to those skilled in the art on examination of the following, or may be learned by practice of the invention. The inventions disclosed in this application are not limited to any particular set of or combination of aspects, advantages and features. It is contemplated that various combinations of the stated aspects, advantages and features make up the inventions disclosed in this application.
The following examples are for illustrative purposes only and are not intended to limit, in any way, the scope of the present invention.
Materials & Procedures
Table 1 lists the phthalate catalysts tested as reference systems (or comparative examples).
The alkoxysilanes used as reference systems in the comparative examples were C-donor (cyclohexylmethyl dimethoxysilane), D-donor (dicyclopentyl dimethoxysilane), P-donor (diisopropyl dimethoxysilane), and DIBS (diisobutyl dimethoxysilane).
Table 2 lists the non-phthalate procatalysts falling within the scope of this invention, listed below as Catalyst Example Nos. 1-5.
Structures of the non-silane aliphatic ester external donors, tested in combination with Catalyst Example Nos. 1-5, are shown below.
Polymerizations were carried out in either a 1- or 2-gallon autoclave reactor in bulk liquid propylene (2000 grams in 1 gallon, 3000 grams in 2 gallon). Polymerization temperature and the amount of hydrogen added varied. Prior to the polymerization, triethylaluminum (TEAL), external donor, and procatalysts (including the internal donors) were injected to the reactor sequentially at room temperature and low pressure (<5 psig). Propylene and hydrogen were then added, and the reactor temperature was increased to the desired set point.
Impact copolymers were made by sequential bulk homopolymerizationand gas phase copolymerization in a 2 gallon reactor. After the homopolymerization stage (at 75° C.), the reactor was depressured and purged with N2 for 15 minutes before feeding ethylene, propylene, and hydrogen gas into the reactor. The gases were fed continuously to the reactor and constant pressure was maintained using a back pressure regulator thus ensuring a constant gas ratio. The gas phase copolymerization conditions were: 80° C., 140 psi, and molar ratios of the components in the gas phase are: ethylene/(ethylene+propylene)=0.43; and H2/ethylene=0.067.
Molecular weight distribution of the polymers was measured by either GPC (Mw/Mn) or dynamic rheology (Polydispersity Index—PI). Polymer isotacticity was measured by xylene fractionation (% XS) or 500 MHz 13C NMR (Bruker). DSC thermal fractionation was carried out by heating a sample to 200° C. at 10° C./minute, equilibrating for two hours, and then lowering the temperature by 10° C. increments to 120° C. The sample was allowed to equilibrate for two hours at each successive temperature. At the end of this cycle, the sample was heated up to 200° C. at 10° C./minute, and the melting endotherm was measured.
Results and Discussion
The different phthalate and non-phthalate procatalyst systems listed in Table 1 and Table 2, respectively, were analyzed with conventional alkoxysilane external donors and analyzed in Table 3 and Table 4, respectively, below.
Unlike phthalate-based catalysts, most non-phthalate catalysts are not strongly influenced by the type of alkoxysilane external donor used. This is illustrated in Table 4 for several different non-phthalate systems. Note that the ranges of MFR and % XS are much narrower for the phthalate procatalysts in Table 3 than for the non-phthalate procatalysts in Table 4.
12-gallon reactor, 70° C., 3.5 g H2, ratio of donor/Ti compound = 10
22-gallon reactor, 75° C., 4.75 g H2, ratio of donor/Ti compound = 10
31-gallon reactor, 75° C., 0.6 g H2, ratio of donor/Ti compound = 10
41-gallon reactor, 75° C., 0.9 g H2, ratio of donor/Ti compound = 10
The effects of non-silane aliphatic diester external donors on different phthalate and non-phthalate procatalyst systems listed in Table 2 were analyzed. As shown in results below, each of these non-phthalate procatalysts had a particular deficiency that could not be influenced by alkoxysilanes, but were influenced by the new external donors.
Example No. 2 procatalyst is a non-phthalate catalyst containing 1,8-napthyl dibenzoate as an internal donor (see U.S. Pat. No. 8,003,558, which is incorporated herein by reference in its entirety). With typical alkoxysilane external donors (C, D, and P), Example No. 2 procatalyst had a significantly lower hydrogen response compared to a phthalate catalyst (Comparative Example 4) (see
A series of non-silane aliphatic diester molecules were tested as external donors to improve the hydrogen response of Example No. 2 procatalyst. The results are shown in
At least some of the activity appeared to be recovered at a lower ratio of donor/Ti compound. Therefore, lowering the ratio of donor/Ti compound may be desirable to provide an improved performance comparable to conventional alkoxysilane external donors. Lowering the ratio of donor/Ti compound may also result in lower donor residues in the final product as well as providing an economic advantage over conventional alkoxysilane external donors.
Example No. 5 is a non-phthalate procatalyst based on a cyclohexanedicarboxylate internal donor (see U.S. Pat. Nos. 7,649,062 and 7,888,438, which are incorporated herein by reference in their entirety). Table 6 shows that Example No. 5 procatalyst with conventional alkoxysilane external donor provided somewhat lower MFR and higher xylene solubles than Comparative Example 1 procatalyst (phthalate). However, using diethyladipate as the external donor increased both the hydrogen response and isotacticity of Example No. 5 procatalyst. The increase in isotacticity was enough to make this non-phthalate catalyst system comparable to Comparative Example 1 (a phthalate catalyst system).
Similar to Example No. 2 procatalyst and aliphatic diester external donors, the catalyst activity when using Example No. 5 procatalyst with an aliphatic diester external donor was somewhat decreased compared to the conventional alkoxysilane external donor at the same donor/Ti compound ratio.
Example No. 3 is a non-phthalate procatalyst based on a cyclohexanedicarboxylate internal donor which produces very broad MWD products (see U.S. Pat. No. 8,729,189, which is incorporated herein by reference in its entirety).
A comparison of polymerization with Example No. 3 procatalyst in combination with a conventional alkoxysilane external donor and in combination with the non-silane aliphatic diester external donors is shown in Tables 7.1 and 7.2. Although the catalyst activity was decreased, the hydrogen response was in some cases increased by the diester external donors compared to the conventional alkoxysilane external donor, isotacticity was improved and the MWD remained the same or was broadened.
It was previously observed that Example No. 3 procatalyst has relatively low gas phase activity in the production of impact copolymer compared to the phthalate catalyst of Comparative Example 1.
However, when the non-silane aliphatic ester compounds were used with Example No. 3 procatalyst, much more promising gas phase production was observed (
Example No. 1 is a commercial non-phthalate diether procatalyst (see U.S. Pat. No. 5,723,400, which is incorporated herein by reference in its entirety). Diether catalysts typically produce polypropylenes having lower crystallinity and stiffness than the phthalate catalysts, due to a narrower MWD and more regioirregular chain structure (Tables 8 and 10). Diether procatalysts also do not respond very differently to different alkoxysilane donors (see Tables 4 and 8).
Example No. 1 procatalyst was tested with alternative external donors to improve the attributes of the polymer product compared to the conventional alkoxysilane systems and to create products more similar to phthalate-based catalysts.
One particular advantage of the alternative external donors with Example No. 1 procatalyst is the increase in the isotacticity of polymers, while the polydispersity index (PI) appeared to be essentially unchanged (Table 9). Thus, these new donors can modify the polymer structure in a way that differs from conventional alkoxysilane donors.
The positive effect of the alternative donors on the hydrogen response of Example No. 1 procatalyst is illustrated in
The above results show that aliphatic di- and tri-ester donors appeared to improve both hydrogen response and isotacticity at the same time. This is a desirable and novel behavior compared to the conventional response of the Ziegler-Natta procatalysts to the external donors. Typically, external donors that increase MFR also decrease isotacticity (increase % XS).
Compared to conventional alkoxysilane external donors, a relatively lower activity is seen at the same donor/Ti compound with the diester external donors. However, at least some of the activity appeared to be recovered at a lower donor/Ti compound. Therefore, lowering the ratio of donor/Ti compound may be desirable to provide an improved performance comparable to conventional alkoxysilane external donors. Lowering the ratio of donor/Ti compound may also result in lower donor residues in the final product as well as providing an economic advantage over conventional alkoxysilane external donors.
The results of the new aliphatic ester external donors in combination with the non-phthalate procatalyst are surprising as the phthalate catalysts typically do not respond well to these non-silane aliphatic ester external donors. As shown in Table 10, when these non-silane aliphatic ester external donors in combination with the phthalate procatalyst, the catalyst activity was dramatically reduced and both the MFR and % XS were significantly increased.
Although preferred embodiments have been depicted and described in detail herein, it will be apparent to those skilled in the relevant art that various modifications, additions, substitutions, and the like can be made without departing from the spirit of the invention and these are therefore considered to be within the scope of the invention as defined in the claims which follow.
This application claims the benefit of priority to U.S. Provisional Patent Application Ser. No. 62/273,584, filed Dec. 31, 2015, and U.S. Provisional Patent Application Ser. No. 62/278,256, filed Jan. 13, 2016; which are hereby incorporated by reference in their entirety.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2016/069287 | 12/29/2016 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2017/117433 | 7/6/2017 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20050239636 | Gao et al. | Oct 2005 | A1 |
| 20070027275 | Chen et al. | Feb 2007 | A1 |
| 20070155616 | Wang et al. | Jul 2007 | A1 |
| 20110152481 | Chang | Jun 2011 | A1 |
| 20110207901 | Chang | Aug 2011 | A1 |
| 20140148565 | Denkwitz et al. | May 2014 | A1 |
| 20140275456 | Xu et al. | Sep 2014 | A1 |
| 20140378298 | Kipiani | Dec 2014 | A1 |
| 20160244538 | Liu | Aug 2016 | A1 |
| 20160289357 | Cai et al. | Oct 2016 | A1 |
| Number | Date | Country |
|---|---|---|
| 2947095 | Oct 2015 | CA |
| 2221320 | Aug 2010 | EP |
| 2373702 | Oct 2011 | EP |
| 2005030815 | Apr 2005 | WO |
| 2011160936 | Dec 2011 | WO |
| 2012007430 | Jan 2012 | WO |
| 2012052387 | Apr 2012 | WO |
| WO-2015077598 | May 2015 | WO |
| 2015197435 | Dec 2015 | WO |
| Entry |
|---|
| Office Action dated Jan. 24, 2020 in U.S. Appl. No. 16/067,350. |
| Number | Date | Country | |
|---|---|---|---|
| 20190010258 A1 | Jan 2019 | US |