The following description relates to a nonaqueous electrolyte rechargeable battery and a method for manufacturing a positive electrode plate of a nonaqueous electrolyte rechargeable battery, and more particularly, a nonaqueous electrolyte rechargeable battery and a method for manufacturing a positive electrode plate of a nonaqueous electrolyte rechargeable battery that avoid high-rate deterioration.
A nonaqueous electrolyte rechargeable battery, such as a lithium-ion rechargeable battery, is light in weight and high in energy density, and thereby used as a preferred high-output power source that is installed in a vehicle. Such a nonaqueous electrolyte rechargeable battery includes a rolled electrode body in which an electricity storage element, formed by a stack of a positive electrode and a negative electrode insulated from each other by a separator or the like, is rolled into a columnar shape or an elliptical columnar shape in a battery case. Typically, the positive electrode and the negative electrode of the electrode body are designed such that a negative electrode mixture layer is wider than a positive electrode mixture layer. Thus, the negative electrode mixture layer opposes a positive electrode current collector, from which metal is exposed, with the separator located in between. Short circuiting will not occur under a normal situation because of the separator. However, when metal is deposited on the negative electrode or fine metal powder or the like enters the negative electrode, short circuiting may occur through the separator and generate heat.
In order to avoid such short circuiting, for example, Japanese Laid-Open Patent Publication No. 2017-157471 discloses the following invention. Specifically, a positive electrode includes a positive electrode current collector foil, an insulative protection layer including an insulative material, and a positive electrode mixture layer including a positive electrode active material. The positive electrode mixture layer and the insulative protection layer are formed on at least one surface of the positive electrode current collector foil of a positive electrode plate.
Such an insulative protection layer covers a metal plate forming the positive electrode current collector with an insulator so that occurrence of short circuiting in a negative electrode mixture layer through the separator is avoided effectively even when metal Li is deposited on the negative electrode mixture layer or when foreign matter such as fine metal powder enters the negative electrode mixture layer.
Further, Japanese Laid-Open Patent Publication No. 2017-157471 discloses a structure in which an overlapped portion of the insulative protection layer is covered with an overlapping portion of the positive electrode mixture layer. This avoids delamination of the insulative protection layer from the positive electrode current collector foil.
In a nonaqueous electrolyte rechargeable battery, an electrolyte moves when charging and discharging are performed at a high rate. In this case, if the insulative protection layer causes insufficient movement of the nonaqueous electrolyte within the battery cell, the concentration of the nonaqueous electrolyte becomes uneven. This may result in deterioration of the battery, or “high-rate deterioration”. However, such a problem is not recognized by the invention described in Japanese Laid-Open Patent Publication No. 2017-157471.
Further, although the invention described in Japanese Laid-Open Patent Publication No. 2017-157471 avoids delamination of the insulative protection layer from the positive electrode current collector foil at the portion where the insulative protection layer overlaps the positive electrode mixture layer, the invention does not disclose a structure that avoids delamination of the entire insulative protection layer.
This Summary is provided to introduce a selection of concepts in a simplified form that are further described below in the Detailed Description. This Summary is not intended to identify key features or essential features of the claimed subject matter, nor is it intended to be used as an aid in determining the scope of the claimed subject matter.
In one general aspect, a nonaqueous electrolyte rechargeable battery includes a positive electrode plate, a negative electrode plate, a separator insulating the positive electrode plate and the negative electrode plate, and a nonaqueous electrolyte. The positive electrode plate includes a positive electrode current collector, a positive electrode mixture layer arranged on a part of at least one surface of the positive electrode current collector and including positive electrode active material particles and a conductor, and an insulative protection layer arranged on another part of the at least one surface of the positive electrode current collector adjacent to the positive electrode mixture layer and including insulative particles and a binder. In the insulative protection layer, a value of (the insulative particles)/(the insulative particles+the binder) is between 75 wt % and 85 wt %, inclusive. A single-surface thickness TI of the insulative protection layer is between 3.01 μm and 151 μm, inclusive. A porosity PI of the insulative protection layer is between 42% and 55%, inclusive. A ratio of the single-surface thickness TI of the insulative protection layer to a single-surface thickness TP of the positive electrode mixture layer is between 0.12 and 0.80, inclusive. The ratio of the single-surface thickness TI of the insulative protection layer to the single-surface thickness TP of the positive electrode mixture layer may be between 0.12 and 0.60, inclusive. A density DP of the positive electrode mixture layer may be between 2.2 g/cm3 and 3.0 g/cm3, inclusive. A porosity PP of the positive electrode mixture layer may be between 30% and 50%, inclusive.
The conductor of the positive electrode mixture layer may be a conductive material having an aspect ratio of thirty or greater. The conductor may be formed by carbon nanotubes or carbon nanofibers.
The insulative protection layer may have a density DI of between 1.2 g/cm3 and 1.6 g/cm3, inclusive and a delamination strength of 10 N or greater.
The positive electrode mixture layer may overlap the insulative protection layer at a boundary portion where the positive electrode mixture layer is adjacent to the insulative protection layer.
The insulative particles may be formed from boehmite or alumina.
In another general aspect, in a method for manufacturing a positive electrode plate of a nonaqueous electrolyte rechargeable battery, the nonaqueous electrolyte rechargeable battery includes a positive electrode plate, a negative electrode plate, a separator insulating the positive electrode plate and the negative electrode plate, and a nonaqueous electrolyte. The positive electrode plate includes a positive electrode current collector, a positive electrode mixture layer arranged on a part of at least one surface of the positive electrode current collector and including positive electrode active material particles and a conductor, and an insulative protection layer arranged on another part of the at least one surface of the positive electrode current collector adjacent to the positive electrode mixture layer and including insulative particles and a binder. The method includes simultaneously applying an insulative protection paste including insulative particles, a binder, and a solvent, and a positive electrode mixture paste including positive electrode active material particles, a conductor, a binder, and a solvent on a surface of the positive electrode current collector to form the positive electrode mixture layer, the insulative protection layer arranged adjacent to the positive electrode mixture layer, and a boundary portion where the positive electrode mixture layer overlaps the insulative protection layer. The method further includes pressing the positive electrode mixture layer, and simultaneously pressing the insulative protection layer and the boundary portion.
At the boundary portion, the insulative protection layer may be formed on the positive electrode current collector, and the positive electrode mixture layer may be formed overlapping the insulative protection layer.
Further, the pressing the insulative protection layer and the boundary portion may be roller pressing and use a stepped roll that is stepped to have different radii in order to press the insulative protection layer and the boundary portion without pressing the positive electrode mixture layer.
The pressing the insulative protection layer and the boundary portion may include applying tension to the positive electrode current collector so that the insulative protection layer and the boundary portion are forced against the stepped roll.
Other features and aspects will be apparent from the following detailed description, the drawings, and the claims.
Throughout the drawings and the detailed description, the same reference numerals refer to the same elements. The drawings may not be to scale, and the relative size, proportions, and depiction of elements in the drawings may be exaggerated for clarity, illustration, and convenience.
This description provides a comprehensive understanding of the methods, apparatuses, and/or systems described. Modifications and equivalents of the methods, apparatuses, and/or systems described are apparent to one of ordinary skill in the art. Sequences of operations are exemplary, and may be changed as apparent to one of ordinary skill in the art, with the exception of operations necessarily occurring in a certain order. Descriptions of functions and constructions that are well known to one of ordinary skill in the art may be omitted.
Exemplary embodiments may have different forms, and are not limited to the examples described. However, the examples described are thorough and complete, and convey the full scope of the disclosure to one of ordinary skill in the art.
In this specification, “at least one of A and B” should be understood to mean “only A, only B, or both A and B.”
A nonaqueous electrolyte rechargeable battery and a method for manufacturing a positive electrode plate in accordance with the present disclosure will now be described with an embodiment of a lithium-ion rechargeable battery 1 and a method for manufacturing an electrode plate of the lithium-ion rechargeable battery 1 with reference to
However, in the lithium-ion rechargeable battery 1, an electrolyte moves when charging and discharging are performed at a high rate. As shown in
Porosity P (%)
Porosity P (%) is a scale indicating the volume of pores such as voids between particles. Porosity P (%) is generally proportional to a coefficient of water permeability. Thus, in the present embodiment, porosity P (%) is used as an index of the efficiency at which the electrolyte 13 flows through the positive electrode mixture layer 32 in a cell.
Further, porosity P (%) also serves an index of the distances between positive electrode active material particles 32b in the positive electrode mixture layer 32.
Porosity P (%) is measured by, for example, a liquid immersion method in which a porous sample is immersed in a liquid having a high wettability to saturate the pores with the liquid. Porosity P (%) may be measured using an optical method in which microscopic observation is conducted on a cross section of a sample to determine an area of the material and an area of the visible voids. Further, porosity P (%) may be measured by, for example, mercury porosimetry in which an amount of mercury, having a high surface tension, injected into fine pores of a sample is measured with respect to the externally applied pressure so as to obtain the distribution and volume of the pores.
Change in Porosity P (%) in Pressing Step
In the positive electrode mixture layer 32, when porosity P (%) is lowered in the pressing step, the distances between the positive electrode active material particles 32b in the positive electrode mixture layer 32 decrease so that the conductive path and the battery performance are improved.
However, in the invention described in the above patent publication, the insulative protection layer 34 is also compressed in the pressing step and thus the distances between insulative particles 34b in the insulative protection layer 34 decrease. This lowers porosity P (%) of the insulative protection layer 34. When porosity P (%) of the insulative protection layer 34 is lowered, the electrolyte 13 is exchanged with low efficiency in the positive electrode mixture layer 32. Accordingly, the concentration of the electrolyte 13 in the battery becomes uneven, particularly when charging and discharging of the battery is performed at a high rate. This increases the tendency of deterioration of the battery, or “high-rate deterioration” to occur.
Further, thickness TI of the insulative protection layer 34 is decreased as described above and the lower limit of porosity PI is set so that the nonaqueous electrolyte 13 moves easily under such a condition. However, even when the mechanical strength of the insulative protection layer 34 is increased to maintain the insulation property, the insulative protection layer 34 may be delaminated.
The present inventors have analyzed a structure that solves the above described problems together by changing conditions in various manners through a number of experiments.
Specific Conditions in Present Embodiment
The present inventors have found through experiments that the following numerical ranges are appropriate values to address the above problems.
(single-surface thickness TI of insulative protection layer 34)/(single-surface thickness TP of positive electrode mixture layer 32)
In the insulative protection layer 34 of the present embodiment, thickness TI of the insulative protection layer 34 at one side is set to 15 μm or less in order to avoid “high-rate degradation”. Further, the value of DI/DP is set to 0.12 to 0.80 so that the voids are ensured to allow the movement of the nonaqueous electrolyte 13. More preferably, the ratio of density DI of the insulative protection layer 34 to density DP of the positive electrode mixture layer 32 is set to 0.1 to 0.6.
Porosity PI of Insulative Protection Layer 34
Porosity PI is set to 55% or less so as to ensure the mechanical strength and, in turn, maintain the insulation property of the insulative protection layer 34.
Further, porosity PI is set to 42% or greater so as to allow the movement of the electrolyte and avoid “high-rate deterioration”.
Density DI of Insulative Protection Layer 34
When single-surface thickness TI of the insulative protection layer 34 is decreased, the insulative protection layer 34 becomes less resistant to foreign matter. Accordingly, density DI of the insulative protection layer 34 is set to 1.2 g/cm3 or greater.
Further, density DI of the insulative protection layer 34 is set to 1.6 g/cm3 or less so as to facilitate the movement of the electrolyte.
Single-Surface Thickness TI of Insulative Protection Layer 34
Single-surface thickness TI of the insulative protection layer 34 is set to 3.0 μm or greater so as to ensure the strength of the insulative protection layer 34 and, in turn, maintain the insulation property of the insulative protection layer 34
Composition of Insulative Protection Layer 34
In the composition of the insulative protection layer 34, the value of (insulative particles 34b)/(insulative particles 34b+binder 34c) on a weight basis is set to 85% or less so that the insulative protection layer 34 is less likely to delaminate from the positive electrode current collector 31. The sufficient amount of a binder 34c avoids delamination of the insulative protection layer 34 from the positive electrode current collector 31.
Further, the value of (insulative particles 34b)/(insulative particles 34b+binder 34c) is set to 75% or greater so as to maintain the insulation property. The insulative particles 34b obtaining a high hardness prevent entry of metallic foreign matter, thereby securing an adequate insulation property.
Delamination Strength
Even when the strength of the insulative protection layer 34 is improved by decreasing porosity PI and increasing density DI, if the insulative protection layer 34 is delaminated, the insulative protection layer 34 may act as foreign matter. Thus, it is further preferred that the delamination strength be 10 N or greater. The delamination strength is improved by, for example, selecting an appropriate binder 34c and setting the value of (insulative particles 34b)/(insulative particles 34b+binder 34c) to 85% or less.
Density DP of Positive Electrode Mixture Layer 32
Density DP (g/cm3) of the positive electrode mixture layer 32 is set to 2.2 g/cm3 or greater so that the density of the positive electrode active material particles 32b is increased and the battery performance is improved.
Further, density DP (g/cm3) of the positive electrode mixture layer 32 is set to 3.0 g/cm3 or less so that the electrolyte moves easily.
Porosity PP of Positive Electrode Mixture Layer 32
Porosity PP of the positive electrode mixture layer 32 is set to 50% or less so that the density of the positive electrode active material particles 32b is increased and the battery performance is improved.
Porosity PP of the positive electrode mixture layer 32 is set to 30% or greater so that the electrolyte moves easily.
Aspect Ratio
Preferably, the conductor 32c has an aspect ratio of thirty or greater so that porosity PP of the positive electrode mixture layer 32 is improved. The term “aspect ratio” refers to a ratio of the length to the diameter of a fiber. When the aspect ratio is thirty or greater, even a small mass of the conductor 32c can form an effective conductive network. Thus, the amount of the conductor 32c added to the positive electrode mixture layer 32 can be decreased, thereby increasing porosity PP. The conductor 32c having such characteristics may include, for example, carbon nanotubes (CNT) or carbon nanofibers (CNF).
Structure of Present Embodiment
Structure of Lithium-Ion Rechargeable Battery 1
As shown in
Electrode Body 12
In each positive electrode plate 3, the positive electrode mixture layer 32 is formed on the positive electrode current collector 31 that serves as a substrate. As shown in
In the present embodiment, the insulative protection layer 34 is arranged adjacent to the end of the positive electrode mixture layer 32 and opposes the negative electrode mixture layer 22. The insulative protection layer 34 is arranged to cover the exposed positive electrode current collector 31.
Stack Structure of Electrode Body 12
The negative electrode plate 2 includes the negative electrode mixture layer 22 on both surfaces of the negative electrode current collector 21, which serves as the negative electrode substrate. An end portion of the negative electrode current collector 21 located at one side of the electrode body 12 defines the negative electrode connection portion 23 where metal is exposed.
The positive electrode plate 3 includes the positive electrode mixture layer 32 on both surfaces of the positive electrode current collector 31, which serves as the positive electrode substrate. An end portion of the positive electrode current collector 31 located at the other side of the electrode body 12 defines the positive electrode connection portion 33 where the metal is exposed.
The negative electrode plate 2 and the positive electrode plate 3 are stacked with the separator 4 held in between. The stack is rolled in its longitudinal direction about the rolling axis to form the flat roll of the electrode body 12.
Further, in the present embodiment, the insulative protection layer 34 is arranged on the positive electrode current collector 31 adjacent to the end of the positive electrode mixture layer 32 that is located toward the positive electrode connection portion 33. If there was no insulative protection layer 34 as in the prior art, the positive electrode current collector 31 would be exposed between an end “a” of the positive electrode mixture layer 32 at the side of the positive electrode connection portion 33 and the edge of the positive electrode. In this case, the positive electrode current collector 31 opposes the negative electrode mixture layer 22 via the separator 4 between the end “a” and an end “b” of the negative electrode mixture layer 22 located at the side of the positive electrode. In such a state, fine metal powder may enter the above region. Further, dendrites of metal Li may grow in the negative electrode mixture layer 22. If such matter penetrates the separator 4, short-circuiting may occur between the negative electrode mixture layer 22 and the positive electrode current collector 31, and generate heat or cause self-discharge. Accordingly, in the present embodiment, the insulative protection layer 34 is arranged from the end “a” to an end “c” beyond the end “b”. Such an insulative protection layer 34 avoids occurrence of short circuiting.
Nonaqueous Electrolyte 13
As shown in
Components of Electrode Body 12
The components of the electrode body 12, namely, the negative electrode plate 2, the positive electrode plate 3, and the separator 4, will now be described.
In the present embodiment, “average diameter” means a median diameter (D50: 50% volume average particle diameter) that corresponds to 50% accumulation in a volume-based particle size distribution, unless specified otherwise. In the range where the average particle diameter is approximately 1 μm or greater, the average diameter can be obtained by a laser diffraction and light scattering method. In the range where the average particle diameter is approximately 1 μm or less, the average particle diameter can be obtained by a dynamic light scattering (DLS) method. The average particle diameter obtained by the DLS method may be measured in accordance with JISZ8828:2013.
Negative Electrode Plate 2
The negative electrode plate 2 has a structure in which the negative electrode mixture layer 22 is formed on both surfaces of the negative electrode current collector 21, which serves as the negative electrode substrate. The negative electrode current collector 21 is formed by a Cu foil in the embodiment. The negative electrode current collector 21 acts as the body and the base of the negative electrode mixture layer 22. Further, the negative electrode current collector 21 functions as a current collecting member that collects electricity from the negative electrode mixture layer 22. In the present embodiment, a negative electrode active material includes a material that is capable of storing and releasing lithium ions, namely, powders of a carbon material such as graphite or the like.
The negative electrode plate 2 is prepared by, for example, kneading the negative electrode active material, a solvent, and a binder, applying the kneaded negative electrode mixture paste to the negative electrode current collector 21, and then drying the paste.
Positive Electrode Plate 3
The positive electrode plate 3 includes the positive electrode current collector 31, the positive electrode mixture layer 32 applied to the positive electrode current collector 31, and the insulative protection layer 34.
Positive Electrode Current Collector 31
The positive electrode plate 3 has a structure in which the positive electrode mixture layer 32 is formed on both surfaces of the positive electrode current collector 31, which serves as the positive electrode substrate. The positive electrode current collector 31 is formed by an Al foil in the embodiment. The positive electrode current collector 31 acts as the body and the base and a frame of the positive electrode mixture layer 32. Further, the positive electrode current collector 31 functions as a current collecting member that collects electricity from the positive electrode mixture layer 32.
An Al foil is described above as an example of the positive electrode substrate that forms the positive electrode current collector 31. The positive electrode substrate is formed from, for example, a conductive material including a metal having satisfactory electric conduction. The conductive material may include, for example, a material including aluminum or an aluminum alloy. The structure of the positive electrode current collector 31 is not limited to the above description.
Positive Electrode Mixture Layer 32
Positive Electrode Mixture Paste 32a
The positive electrode mixture paste 32a is a paste obtained by adding a solvent 32e to the additives such as the conductor 32c, the binder 32d, the dispersant, and the like in addition to the positive electrode active material particles 32b. In the applying step (S3) illustrated in
Composition of Positive Electrode Active Material Particles 32b
The primary particles of the positive electrode active material particles 32b include a lithium transition metal oxide having a layered crystalline structure. The lithium transition metal oxide includes one or more predetermined transition metal elements in addition to Li. Preferably, the transition metal element included in the lithium transition metal oxide is at least one of Ni, Co, and Mn. A preferred example of the lithium transition metal oxide includes every one of Ni, Co, and Mn.
The positive electrode active material particles 32b may include one or more types of elements in addition to the transition metal element (i.e., at least one of Ni, Co, and Mn). The additional element may include any element in group 1 (alkali metal such as sodium), group 2 (alkaline earth metal such as magnesium or calcium), group 4 (transition metal such as titanium or zirconium), group 6 (transition metal such as chromium or tungsten), group 8 (transition metal such as iron), group 13 (metalloid element such as boron or metal such as aluminum), or group 17 (halogen such as fluorine) of the periodic table.
In a preferred embodiment, the positive electrode active material particles 32b may have a composition (average composition) represented by the following general expression (1).
Li1+xNiyCozMn(1-y-z)MAαMBβO2 (1)
In expression 1, the “x” may be a real number that satisfies 0≤x≤0.2. The “y” may be a real number that satisfies 0.1<y<0.6. The “z” may be a real number that satisfies 0.1<z<0.6. The “MA” is at least one type of metal element selected from W, Cr, and Mo. The “α” is a real number that satisfies 0<α≤0.01 (typically, 0.0005≤α≤0.01, for example, 0.001≤α≤0.01). The “MB” may be one or more types of elements selected from the group consisting of Zr, Mg, Ca, Na, Fe, Zn, Si, Sn, Al, B, and F. The “β” may be a real number that satisfies 0≤β≤0.01. The “β” may be substantially zero (that is, oxide including substantially no MB). To facilitate understanding, the chemical formula that expresses the lithium transition metal oxide having a layered structure indicates two as the composition ratio of O (oxygen). However, this numerical value should not be strictly interpreted, and some variations of the composition (typically included in range between 1.95 and 2.05, inclusive) are allowable.
Conductor 32c
The conductor 32c is a material that forms a conductive path in the positive electrode mixture layer 32. When an appropriate amount of the conductor is mixed into the positive electrode mixture layer 32, the conductivity of the positive electrode is increased. This enhances the charging/discharging efficiency and the output characteristics of the battery. The conductor 32c of the present embodiment may include, for example, a carbon material such as carbon nanotubes (CNT) or carbon nanofibers (CNF). Further, the conductor 32c of the present embodiment has the form of a string having the aspect ratio of thirty or greater.
Binder 32d
The binder 32d may include, for example, polyvinylidene fluoride (PVdF), polytetrafluoroethylene (PTFE), polyacrylic acid, polyacrylate, or the like.
Structure of Insulative Protection Layer 34
As shown in
Insulative Protection Paste 34a
The insulative protection paste 34a is a paste obtained by dispersing the insulative particles 34b in a liquid in which the solvent 34d is added to the binder 34c. Further, a dispersant is added to the insulative protection paste 34a so that the insulative particles 34b are uniformly dispersed in the paste.
The insulative protection layer 34 is formed by applying the insulative protection paste 34a to the positive electrode current collector 31 in the applying step (S3) illustrated in
Insulative Particles 34b
The insulative particles 34b are disposed between the negative electrode mixture layer 22 and the positive electrode current collector 31 to obtain electrical insulation thereof. The insulative particles 34b are, for example, a ceramic that is obtained by firing a metallic oxide or the like having a high insulation property and a hardness that prevents entry of foreign matter. Specifically, the insulative particles 34b include particles of boehmite, alumina, or the like. In the present embodiment, the insulative particles 34b include boehmite.
Boehmite
Boehmite is an aluminum hydroxide (γ-AlO(OH)) mineral and is a component of aluminum ore bauxite. Boehmite has a glassy to pearly luster, a Mohs hardness of 3 to 3.5, and a specific gravity of 3.00 to 3.07. Boehmite is high in insulation property, heat resistance, and hardness. Thus, boehmite may be industrially used as an inexpensive flame-retardant additive for fire-resistant polymers.
Boehmite is represented by a chemical composition of AlO(OH) or Al2O3*H2O, and is a chemically stable alumina monohydrate that is typically produced by performing a heating treatment or a hydrothermal treatment on alumina trihydrate in air. Boehmite has a high dehydration temperature of 450 to 530° C., and its shape can be controlled into various forms, such as plate-like, needle-like, and hexagonal plate-like, by adjusting the production conditions. Further, the aspect ratio and the particle diameter of boehmite can be controlled by adjusting the production conditions.
Although there are various types of conventional methods for producing boehmite, boehmite is typically produced through hydrothermal treatment of aluminum hydroxide, which is the raw material derived from bauxite. This production method includes a step of stirring and mixing slurry in which water is added to aluminum hydroxide and a reaction accelerator (metal compound). Further, the production method includes a hydrothermal treatment step by which the slurry is wet-cured while being heated in a water vapor atmosphere in a pressure vessel. Furthermore, in the production method, the reaction product undergoes steps of dehydration, water washing, filtration, and drying.
Particle Size of Insulative Particles 34b
When the average particle size (μm (D50)) of the insulative particles 34b is too large, the dispersibility becomes poor. If the average particle size is too small, aggregations form. In the present embodiment, the average particle size of the insulative particles 34b (μm (D50)) is particularly set to 1 to 3 μm to avoid aggregation.
Binder 34c
The binder 34c may include, for example, polyvinylidene fluoride (PVdF), polytetrafluoroethylene (PTFE), polyacrylic acid, polyacrylate, or the like.
Separator 4
The separator 4 may include a porous sheet formed from resin, such as polyethylene (PE), polypropylene (PP), or the like, so as to hold the nonaqueous electrolyte 13 between the positive electrode plate 3 and the negative electrode plate 2. Such a porous resin sheet may have a single-layer structure in which only one type of material is used. Alternatively, the porous resin sheet may have a multilayer structure in which various types of materials are combined.
Method for Manufacturing Positive Electrode Plate 3
Positive Electrode Mixture Paste Manufacturing Step (S1)
First, the positive electrode mixture paste 32a is manufactured. The details of this step are as described above.
Insulative Protection Paste Manufacturing Step (S2)
Further, the insulative protection paste 34a is manufactured. The details of this step are also as described above.
Applying Step (S3)
The applying step (S3) will now be described. The applying step (S3) is a step of simultaneously applying the positive electrode mixture paste 32a prepared in the positive electrode mixture paste manufacturing step (S1) and the insulative protection paste 34a prepared in the insulative protection paste manufacturing step (S2) to a predetermined position of the positive electrode current collector 31.
Structure of Coater 5
As shown in
The first nozzle 53 is a nozzle that extends from a lower part of the first die 52 to where the positive electrode mixture layer 32 of the positive electrode current collector 31 is formed on the stage 57. When the internal pressure of the first die 52 is increased by a pressurizing means (not shown), a predetermined amount of the positive electrode mixture paste 32a is discharged from the first nozzle 53 to where the positive electrode mixture layer 32 of the positive electrode current collector 31 is formed.
The second nozzle 55 is a nozzle that extends from a lower part of the second die 54 to where the insulative protection layer 34 of the positive electrode current collector 31 is formed on the stage 57. When the internal pressure of the second die 54 is increased by a pressurizing means (not shown), a predetermined amount of the insulative protection paste 34a is discharged from the second nozzle 55 to where the insulative protection layer 34 of the positive electrode current collector 31 is formed.
As shown in
Electrode Body 12 after Applying Step (S3)
As shown in
In the boundary portion B, air bubbles are likely to form at the boundary of the positive electrode mixture layer 32 and the insulative protection layer 34. It is desirable that the bubbles be removed because such bubbles may cause delamination.
Drying Step (S4)
As described above, the drying step (S3) is performed in a state in which the positive electrode mixture paste 32a and the insulative protection paste 34a are mixed in a mixed layer after the applying step (S4). In the drying step (S4), the solvent 32e of the positive electrode mixture layer 32 is volatilized so that the paste of the positive electrode mixture layer 32 becomes a solid that is not mixed with the insulative protection layer 34. Further, the solvent 34d of the insulative protection layer 34 is also volatilized so that the paste of the insulative protection layer 34 becomes a solid that is not mixed with the positive electrode mixture layer 32. The layers are stabilized in such state.
Positive Electrode Mixture Layer Pressing Step (S5)
The load of the press roll 71 is only applied to the insulative protection layer 34 included in the boundary portion B.
Boundary Portion and Insulative Protection Layer Pressing Step (S6)
Thus, when tension is applied to the positive electrode current collector 31 of the long positive electrode plate 3 with respect to the stepped roll 81, the tensioned positive electrode current collector 31 and the stepped roll 81 sandwich and press the boundary portion B of the positive electrode plate 3 and the insulative protection layer 34.
In the boundary portion and insulative protection layer pressing step (S6), tension is applied to the long positive electrode current collector 31, which is drawn from an accommodation reel (not shown), so that the positive electrode plate 3 is forced against the stepped roll 81. As in the positive electrode mixture layer pressing step (S6) shown in
In the boundary portion and insulative protection layer pressing step (S6), thickness TI (μm), porosity PI (%), and density DI (g/cm3) of the insulative protection layer 34 are adjustable by changing the pressing strength. Thickness TP (μm), porosity PP (%), and density DP (g/cm3) of the positive electrode mixture layer 32 are also adjustable by changing the pressing strength.
Cutting Step (S7)
When the thickness, porosity, and density are adjusted to desired values in the boundary portion and insulative protection layer pressing step (S6), the manufacture of the positive electrode mixture layer 32 and the insulative protection layer 34 is completed. Then, in a cutting step (S7), the positive electrode current collector 31 is cut to a length that corresponds to the electrode body 12. This completes the manufacture of the positive electrode plate 3.
Method for Manufacturing Vehicle Battery Pack
When the positive electrode plate 3 is obtained by the above manufacturing method of the positive electrode plate 3, the negative electrode plate 2 and the positive electrode plate 3 are stacked with the separator 4 held in between and rolled to form the electrode body 12. Subsequently, the positive electrode external terminal 14 and the negative electrode external terminal 15 are attached to the electrode body 12 via a lid of the battery case 11. Then, the electrode body 12 is accommodated in the battery case 11, and the lid is airtightly joined with the battery case 11 by laser welding or the like. After the battery case 11 accommodating the electrode body 12 is dried, the nonaqueous electrolyte 13 is injected into the battery case 11 and then the battery case 11 is sealed. Afterwards, the battery cell undergoes conditioning such as initial charging, open circuit voltage (OCV) testing, internal resistance testing, and aging. Multiple battery cells are stacked to form an assembled battery. Further, multiple assembled batteries are accommodated in a battery pack. A vehicle on-board lithium-ion rechargeable battery is completed when a controller and the like are mounted on the battery pack for monitoring and controlling charging, discharging, and the like of the battery pack.
Operation of Present Embodiment
Conditions of Lithium-Ion Rechargeable Battery 1 of Present Embodiment
The conditions of the lithium-ion rechargeable battery 1 in accordance with the present embodiment are now described as the “tolerable range”.
Thickness TI (μm) of the insulative protection layer 34 is 3 to 15 μm.
Porosity PI (%) of the insulative protection layer 34 is between 42% and 55%, inclusive.
In the composition of the insulative protection layer 34, the value of (insulative particles 34b)/(insulative particles 34b+binder 34c) on a weight basis is between 75 wt % and 85 wt %, inclusive. With respect to the binder 34c, the value of (binder 34c)/(insulative particles 34b+binder 34c) is between 15 wt % and 25 wt %, inclusive.
A ratio of single-surface thickness TI (μm) of insulative protection layer 34 to single-surface thickness TP (μm) of the positive electrode mixture layer 32 is between 0.12 and 0.80, inclusive.
The resistance increase rate (internal resistance DC-IR) is 1.15 or less.
Separation of the insulative protection layer 34 from the positive electrode current collector 31 is “absent”.
Short circuiting caused by foreign matter is “absent”.
In Example 1, thickness TI (μm) of the insulative protection layer 34 was 3 porosity PI (%) was 51%, the ratio of the insulative particles 34b was 85 wt %, the ratio of the binder 34c was 15 wt %, and the value of thickness TI/thickness TP was 0.15.
The evaluation results showed that the resistance increase rate was 1.15, which is in the tolerable range, separation of the insulative protection layer was “absent”, and short circuiting caused by foreign matter was “absent”.
In Example 2, thickness TI (μm) of the insulative protection layer 34 was 6 μm, porosity PI (%) was 55%, ratio of the insulative particles 34b was 85 wt %, the ratio of the binder 34c was 15 wt %, and the value of thickness TI/thickness TP was 0.2.
The evaluation results showed that the resistance increase rate was 1.10, which is in the tolerable range, separation of the insulative protection layer was “absent”, and short circuiting caused by foreign matter was “absent”.
In Example 3, thickness TI (μm) of the insulative protection layer 34 was 10 μm, porosity PI (%) was 46%, the ratio of the insulative particles 34b was 80 wt %, the ratio of the binder 34c was 20 wt %, and the value of thickness TI/thickness TP was 0.4.
The evaluation results showed that the resistance increase rate was 1.10, which is in the tolerable range, separation of the insulative protection layer was “absent”, and short circuiting caused by foreign matter was “absent”.
In Example 4, thickness TI (μm) of the insulative protection layer 34 was 15 porosity PI (%) was 49%, the ratio of the insulative particles 34b was 80 wt %, the ratio of the binder 34c was 20 wt %, and the value of thickness TI/thickness TP was 0.8.
The evaluation results showed that the resistance increase rate was 1.13, which is in the tolerable range, separation of the insulative protection layer was “absent”, and short circuiting caused by foreign matter was “absent”.
Comparative Example 1 is a comparative example that does not include the insulative protection layer 34.
The evaluation results showed that the resistance increase rate was 1.12, and short circuiting caused by foreign matter was “present”. That is, there was a problem of occurrence of short circuiting caused by foreign matter.
In Comparative Example 2, thickness TI (μm) of the insulative protection layer 34 was 2 μm, porosity PI (%) was 44%, the ratio of the insulative particles 34b was 80 wt %, the ratio of the binder 34c was 20 wt %, and the value of thickness TI/thickness TP was 0.12.
In this example, thickness TI (μm) of the insulative protection layer 34 was 2 μm, which is less than the tolerable value of 3.
The evaluation results showed that the resistance increase rate was 1.10, separation of the insulative protection layer was “absent”, and short circuiting caused by foreign matter was “present”. That is, there was a problem of occurrence of short circuiting caused by foreign matter.
In Comparative Example 3, thickness TI (μm) of the insulative protection layer 34 was 4 μm, porosity PI (%) was 63%, the ratio of the insulative particles 34b was 80 wt %, the ratio of the binder 34c was 20 wt %, and the value of thickness TI/thickness TP was 0.12.
In this example, porosity PI (%) was 63%, which is greater than the tolerable value of 55%.
The evaluation results showed that the resistance increase rate was 1.11, separation of the insulative protection layer was “absent”, and short circuiting caused by foreign matter was “present”. That is, there was a problem of occurrence of short circuiting caused by foreign matter.
In Comparative Example 4, thickness TI (μm) of the insulative protection layer 34 was 4 μm, porosity PI (%) was 52%, the ratio of the insulative particles 34b was 70 wt %, the ratio of the binder 34c was 30 wt %, and the value of thickness TI/thickness TP was 0.2.
In this example, the ratios of the insulative particles 34b and the binder 34c were 70 wt % and 30 wt %, respectively. The ratio of the insulative particles 34b is less than the tolerable value of 75 wt % or greater, and the ratio of the binder 34c is greater than the tolerable value of 25 wt % or less.
The evaluation results showed that the resistance increase rate was 1.13, separation of the insulative protection layer was “absent”, and short circuiting caused by foreign matter was “present”. That is, there was a problem of occurrence of short circuiting caused by foreign matter.
In Comparative Example 5, thickness TI (μm) of the insulative protection layer 34 was 25 μm, porosity PI (%) was 42%, the ratio of the insulative particles 34b was 80 wt %, the ratio of the binder 34c was 20 wt %, and the value of thickness TI/thickness TP was 0.9.
In this example, thickness TI (μm) of the insulative protection layer 34 was 25 μm, which is greater than the tolerable value of 15 μm. Further, the value of thickness TI/thickness TP was 0.9, which is greater than the tolerable value of 0.8.
The evaluation results showed that the resistance increase rate was 1.38, separation of the insulative protection layer was “absent”, and short circuiting caused by foreign matter was “absent”. That is, there was a problem in that the resistance increase rate was 1.38, which is greater than the tolerable value of 1.15.
In Comparative Example 6, thickness TI (μm) of the insulative protection layer 34 was 30 μm, porosity PI (%) was 35%, the ratio of the insulative particles 34b was 80 wt %, the ratio of the binder 34c was 20 wt %, and the value of thickness TI/thickness TP was 1.2.
In this example, thickness TI (μm) of the insulative protection layer 34 was 301 μm, which is greater than the tolerable value of 15 μm. Further, the value of thickness TI/thickness TP was 1.2, which is greater than the tolerable value of 0.8.
The evaluation results showed that the resistance increase rate was 1.52, separation of the insulative protection layer was “absent”, and short circuiting caused by foreign matter was “absent”. That is, there was a problem in that the resistance increase rate was 1.52, which is greater than the tolerable value of 1.15.
In Comparative Example 7, thickness TI (μm) of the insulative protection layer 34 was 15 μm, porosity PI (%) was 63%, the ratio of the insulative particles 34b was 85 wt %, the ratio of the binder 34c was 15 wt %, and the value of thickness TI/thickness TP was 0.6.
In this example, porosity PI (%) was 63%, which is greater than the tolerable value of 55%.
The evaluation results showed that the resistance increase rate was 1.12, separation of the insulative protection layer was “present”, and short circuiting caused by foreign matter was “present”. In other words, there were problems of separation of the insulative protection layer and occurrence of short circuiting caused by foreign material.
In Comparative Example 8, thickness TI (μm) of the insulative protection layer 34 was 15 μm, porosity PI (%) was 49%, the ratio of the insulative particles 34b was 90 wt %, the ratio of the binder 34c was 10 wt %, and the value of thickness TI/thickness TP was 0.6.
In this example, the ratios of the insulative particles 34b and the binder 34c were 90 wt % and 10 wt %, respectively. The ratio of the insulative particles 34b is greater than the tolerable value of 85 wt %, and the ratio of the binder 34c is less than the tolerable value of 15 wt %.
The evaluation results showed that the resistance increase rate was 1.12, separation of the insulative protection layer was “present”, and short circuiting caused by foreign matter was “absent”. In other words, there was a problem of separation of the insulative protection layer.
Experimental Examples Summary
Comparative Examples 1 to 4 and 7 indicated that the insulative protection layer 34 has an effect of avoiding short circuiting caused by foreign matter. In particular, it was found that such an insulative protection layer 34 has the conditions in which thickness TI (μm) is 3 μm or greater, porosity PI (%) is 55% or less, the ratio of the insulative particles 34b is 75 wt % or greater, and the ratio of the binder 34c is 25 wt % or less.
Based on Comparative Examples 5 and 6, it was found that the conditions for limiting the resistance increase rate to 1.15 times or less include that the ratio of thickness TI (μm) of the insulative protection layer 34 to thickness TP (μm) of the positive electrode mixture layer 32 is 0.8 or less.
Based on Comparative Examples 7 and 8, it was found that the conditions for avoiding separation of the insulative protection layer 34 include that porosity PI (%) of the insulative protection layer 34 is 55% or less, the ratio of the insulative particles 34b is 85 wt % or less, and the ratio of the binder 34c is 15 wt % or greater.
Advantages of Present Embodiment
Further, the value of (insulative particles 34b)/(insulative particles 34b+binder 34c) is set to 85 wt % or less. This avoids delamination of the insulative protection layer 34 from the positive electrode current collector 31 effectively.
Single-surface thickness TI of the insulative protection layer 34 is set to 15 μm or less. This facilitates the movement of the electrolyte.
The above embodiment is an example of the present disclosure, and can be modified and implemented as follows.
In the present embodiment, the positive electrode mixture layer 32 and the insulative protection layer 34 are formed on both surfaces of the positive electrode current collector 31 so that the present disclosure is implemented on both surfaces. However, the present disclosure may be implemented on the positive electrode current collector 31 on only one surface. Further, the positive electrode mixture layer 32 and the insulative protection layer 34 may be formed on only one surface of the positive electrode current collector 31, and the present disclosure may be implemented on that surface.
In the present embodiment, the lithium-ion rechargeable battery 1 is described as an example of a nonaqueous electrolyte rechargeable battery that is a plate-shaped battery cell to be mounted on a vehicle. However, the nonaqueous electrolyte rechargeable battery is not limited to such a structure and may be cylindrical and/or stationary. Further, the electrode body 12 is not limited to a flat roll type and may be a stack of rectangular plate-shaped electrodes. In addition, there is no limitation to the shape of the positive electrode external terminal 14 and the negative electrode external terminal 15.
The drawings are provided to illustrate the present embodiment, and depiction of elements may be exaggerated for clarity. Thus, the present disclosure is not limited to the drawings.
The flowchart shown in
The numerical values and ranges are merely examples, and can be optimized by one skilled in the art.
The composition, material characteristics, and the like of the positive electrode mixture paste 32a and the insulative protection paste 34a are examples of the present disclosure, and can be optimized by one skilled in the art.
The present embodiment is an embodiment of the present disclosure. It should be apparent to one skilled in the art that the present disclosure is not limited to the embodiment and can be implemented by adding, deleting, or changing the structure without departing from the scope of the claims.
Various changes in form and details may be made to the examples above without departing from the spirit and scope of the claims and their equivalents. The examples are for the sake of description only, and not for purposes of limitation. Descriptions of features in each example are to be considered as being applicable to similar features or aspects in other examples. Suitable results may be achieved if sequences are performed in a different order, and/or if components in a described system, architecture, device, or circuit are combined differently, and/or replaced or supplemented by other components or their equivalents. The scope of the disclosure is not defined by the detailed description, but by the claims and their equivalents. All variations within the scope of the claims and their equivalents are included in the disclosure.