NONAQUEOUS ELECTROLYTE SECONDARY BATTERY POROUS LAYER

Information

  • Patent Application
  • 20200335758
  • Publication Number
    20200335758
  • Date Filed
    April 15, 2020
    4 years ago
  • Date Published
    October 22, 2020
    4 years ago
Abstract
The present invention achieves a nonaqueous electrolyte secondary battery porous layer having further improved heat resistance. A nonaqueous electrolyte secondary battery porous layer in accordance with an aspect of the present invention has a shear strength per weight per unit area of not less than 140 N/[mm3/(g/m2)].
Description

This Nonprovisional application claims priority under 35 U.S.C. § 119 on Patent Application No. 2019-078117 filed in Japan on Apr. 16, 2019, the entire contents of which are hereby incorporated by reference.


TECHNICAL FIELD

The present invention relates to a porous layer for a nonaqueous electrolyte secondary battery (hereinafter referred to as a “nonaqueous electrolyte secondary battery porous layer”).


BACKGROUND ART

Nonaqueous electrolyte secondary batteries, particularly lithium ion secondary batteries, have a high energy density and are therefore in wide use as batteries for personal computers, mobile phones, portable information terminals, and the like. Such nonaqueous electrolyte secondary batteries have recently been developed as on-vehicle batteries.


As a member of such a nonaqueous electrolyte secondary battery, a separator having excellent heat resistance is under development. For example, in known art such as that of Patent Literature 1, there are laminated separators in which a porous layer containing a heat-resistant resin is formed on a base material.


CITATION LIST
Patent Literature

[Patent Literature 1]


Japanese Patent Application Publication Tokukai No. 2010-55942


SUMMARY OF INVENTION
Technical Problem

However, conventional technique such as that described above has room for further improvement in terms of heat resistance. An object of an aspect of the present invention is to achieve a nonaqueous electrolyte secondary battery porous layer having further improved heat resistance.


Solution to Problem

In order to attain the object, the inventor of the present invention conducted diligent research, and, as a result, found that heat resistance of a nonaqueous electrolyte secondary battery porous layer can be further improved by controlling a shear strength per weight per unit area of the nonaqueous electrolyte secondary battery porous layer to fall within a specific range. The present invention was thus completed. The present invention includes the following aspects.


<1> A nonaqueous electrolyte secondary battery porous layer, the nonaqueous electrolyte secondary battery porous layer having a shear strength per weight per unit area of not less than 140 N/[mm3/(g/m2)].


<2> The nonaqueous electrolyte secondary battery porous layer according to <1>, wherein the nonaqueous electrolyte secondary battery porous layer has a porosity of 20% by volume to 90% by volume.


<3> The nonaqueous electrolyte secondary battery porous layer according to <1> or <2>, wherein the nonaqueous electrolyte secondary battery porous layer contains at least one resin selected from a group consisting of a resin having a melting point or a glass transition temperature of not lower than 180° C., a polyamide-based resin, a polyimide-based resin, and a polyester-based resin.


<4> The nonaqueous electrolyte secondary battery porous layer according to <1> or <2>, wherein the nonaqueous electrolyte secondary battery porous layer contains a polyamide-based resin.


<5> A nonaqueous electrolyte secondary battery laminated separator including: a polyolefin porous film; and the nonaqueous electrolyte secondary battery porous layer according to any one of <1> to <4>, the nonaqueous electrolyte secondary battery porous layer being formed on at least one surface of the polyolefin porous film.


<6> A nonaqueous electrolyte secondary battery member including: a positive electrode; the nonaqueous electrolyte secondary battery porous layer according to any one of <1> to <4> or the nonaqueous electrolyte secondary battery laminated separator according to <5>; and a negative electrode, the positive electrode, the nonaqueous electrolyte secondary battery porous layer or the nonaqueous electrolyte secondary battery laminated separator, and the negative electrode being arranged in this order.


<7> A nonaqueous electrolyte secondary battery including: the nonaqueous electrolyte secondary battery porous layer according to any one of <1> to <4> or the nonaqueous electrolyte secondary battery laminated separator according to <5>.


Advantageous Effects of Invention

With an aspect of the present invention, it is possible to provide a nonaqueous electrolyte secondary battery porous layer having further improved heat resistance.





BRIEF DESCRIPTION OF DRAWINGS


FIG. 1 is a diagram schematically illustrating a test piece used in measurement of shear strength.



FIG. 2 is a diagram schematically illustrating an outline of a soldering iron test.





DESCRIPTION OF EMBODIMENTS

The following description will discuss embodiments of the present invention. Note, however, that the present invention is not limited to the embodiment. The present invention is not limited to arrangements described below, but may be altered in various ways by a skilled person within the scope of the claims. The present invention also encompasses, in its technical scope, any embodiment derived by combining technical means disclosed in differing embodiments.


Any numerical range expressed as “A to B” herein means “not less than A and not more than B” unless otherwise stated.


[1. Nonaqueous Electrolyte Secondary Battery Porous Layer]


A nonaqueous electrolyte secondary battery porous layer in accordance with an embodiment of the present invention has a shear strength per weight per unit area of not less than 140 N/[mm3/(g/m2)]. Hereinafter, a nonaqueous electrolyte secondary battery porous layer may also be referred to simply as a “porous layer”.


The shear strength of the porous layer reflects cohesive force of molecules contained in the porous layer. For example, in a case where branching in the structure of molecules is reduced, the molecules can be packed closely. This causes the porous layer to exhibit high cohesive force. That is, in general, higher cohesive force of a porous layer results in higher shear strength of the porous layer. With a porous layer having high shear strength and being therefore strong, even if, for example, the porous layer is damaged and then parts around the damage are exposed to high temperature due to an internal short circuit caused by the damage, it is still possible to reduce spreading of the damage caused by the heat. Specifically, a porous layer having a shear strength per weight per unit area of not less than 140 N/[mm3/(g/m2)] can reduce heat-caused spreading of damage, and therefore exhibits excellent heat resistance. The shear strength per weight per unit area of the porous layer is more preferably not less than 150 N/[mm3/(g/m2)], and still more preferably not less than 160 N/[mm3/(g/m2)].


Note that the shear strength of a porous layer is considered to be affected by a weight per unit area of the porous layer. Hence, according to an embodiment of the present invention, a shear strength, for which the effect of a weight per unit area is cancelled, is used as an index of heat resistance. The shear strength is therefore divided by the weight per unit area.



FIG. 1 is a diagram schematically illustrating a test piece used in measurement of shear strength. (b) of FIG. 1 illustrates the test piece as viewed from the Y-axis direction of (a) of FIG. 1. As illustrated in FIG. 1, the test piece 100 is constituted by a resin substrate 12a, double-sided tape 11a, a porous layer 1, double-sided tape 11b, and a resin substrate 12b, stacked in this order. In conformity with the test method of JIS K6850, the shear strength per weight per unit area is found as follows. The test piece used includes a porous layer measuring 10 mm (in the lengthwise direction of the test piece) by 30 mm (in the widthwise direction of the test piece). The test piece is pulled by up to 3 mm along the lengthwise direction at a pulling speed of 50 mm/s. The maximum value of the shear strength is then divided by the weight per unit area of the porous layer so as to obtain the shear strength per weight per unit area. The shear strength per weight per unit area is an average value obtained from three measurements. Further details about the measurement method are provided in the discussion of the Examples (described later).


The porous layer, as a member included in a nonaqueous electrolyte secondary battery, can be provided between (i) a polyolefin porous film and (ii) at least one of a positive electrode and a negative electrode. The porous layer can be provided on one surface of the polyolefin porous film or on both surfaces of the polyolefin porous film. Alternatively, the porous layer can be provided on an active material layer of at least one of the positive electrode and the negative electrode. Alternatively, the porous layer can be provided between (i) the polyolefin porous film and (ii) at least one of the positive electrode and the negative electrode, in a manner so as to be in contact with the polyolefin porous film and the at least one of the positive electrode and the negative electrode. The number of porous layer(s) provided between (i) the polyolefin porous film and (ii) at least one of the positive electrode and the negative electrode can be one, two, or more. The porous layer is preferably an insulating porous layer containing a resin.


In a case where the porous layer is formed on one surface of the polyolefin porous film, the porous layer is preferably formed on a surface of the polyolefin porous film which surface faces the positive electrode. The porous layer is more preferably formed on a surface which makes contact with the positive electrode.


It is preferable that the resin used in the porous layer be insoluble in the electrolyte of the nonaqueous electrolyte secondary battery and be electrochemically stable when the battery is in normal use.


Examples of resin(s) used in the porous layer encompass polyolefins; (meth)acrylate-based resins; fluorine-containing resins; polyamide-based resins; polyimide-based resins; polyester-based resins; rubbers; resins having a melting point or a glass transition temperature of not lower than 180° C.; water-soluble polymers; polycarbonate, polyacetal, and polyether ether ketone.


As the polyamide-based resins, aramid resins such as aromatic polyamides and wholly aromatic polyamides are preferable.


Specific examples of the aramid resins encompass poly(paraphenylene terephthalamide), poly(metaphenylene isophthalamide), poly(parabenzamide), poly(metabenzamide), poly(4,4′-benzanilide terephthalamide), poly(paraphenylene-4,4′-biphenylene dicarboxylic acid amide), poly(metaphenylene-4,4′-biphenylene dicarboxylic acid amide), poly(paraphenylene-2,6-naphthalene dicarboxylic acid amide), poly(metaphenylene-2,6-naphthalene dicarboxylic acid amide), poly(2-chloroparaphenylene terephthalamide), a paraphenylene terephthalamide/2,6-dichloroparaphenylene terephthalamide copolymer, and a metaphenylene terephthalamide/2,6-dichloroparaphenylene terephthalamide copolymer. Among these, poly(paraphenylene terephthalamide) is more preferable.


The polyester-based resins are preferably aromatic polyesters such as polyarylates, or liquid crystal polyesters.


Examples of the rubbers encompass a styrene-butadiene copolymer and a hydride thereof, a methacrylic acid ester copolymer, an acrylonitrile-acrylic acid ester copolymer, a styrene-acrylic acid ester copolymer, an ethylene propylene rubber, and polyvinyl acetate.


Examples of the fluorine-containing resins encompass polyvinylidene fluoride (PVDF), polytetrafluoroethylene, a vinylidene fluoride-hexafluoropropylene copolymer, a tetrafluoroethylene-hexafluoropropylene copolymer, a tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer, a vinylidene fluoride-tetrafluoroethylene copolymer, a vinylidene fluoride-trifluoroethylene copolymer, a vinylidene fluoride-trichloroethylene copolymer, a vinylidene fluoride-vinyl fluoride copolymer, a vinylidene fluoride-hexafluoropropylene-tetrafluoroethylene copolymer, and an ethylene-tetrafluoroethylene copolymer, and particularly fluorine-containing rubber having a glass transition temperature of not higher than 23° C.


Examples of the resins having a melting point or a glass transition temperature of not lower than 180° C. encompass polyphenylene ether, polysulfone, polyether sulfone, polyphenylene sulfide, polyetherimide, polyamide imide, polyether amide, and polyether ether ketone.


Examples of the water-soluble polymers encompass polyvinyl alcohol, polyethylene glycol, cellulose ether, sodium alginate, polyacrylic acid, polyacrylamide, and polymethacrylic acid.


Among these resins, the following resins are more preferable in terms of heat resistance: resins having a melting point or a glass transition temperature of not lower than 180° C.; polyamide-based resins; polyimide-based resins; and polyester-based resins.


The porous layer may contain only one of the above resins or two or more of the above resins in combination.


The porous layer may contain a filler. The filler may be an inorganic filler or an organic filler. An inorganic filler made of an inorganic oxide such as silica, calcium oxide, magnesium oxide, titanium oxide, alumina, mica, zeolite, aluminum hydroxide, or boehmite is more preferable.


The amount of filler contained in the porous layer, with respect to the total amount of the resin and the filler, can be not less than 10% by weight, and can be not less than 20% by weight. The amount of filler contained can be not more than 99% by weight, can be not more than 90% by weight, and not more than 75% by weight.


In particular, in a case where the resin used for the porous layer is an aramid resin, controlling the amount of filler contained so as to fall in the above-described range of 20% by weight to 75% by weight makes it possible to reduce an increase in the weight of the separator due to the filler, and also makes it possible to obtain a separator having favorable ion permeability.


In an embodiment of the present invention, sufficient heat resistance can be achieved even without particularly increasing the relative amount of the aramid resin. Therefore, the amount of filler contained with respect to the total amount of the resin and the filler can be not less than 50% by weight, not less than 55% by weight, and not less than 60% by weight.


The porous layer is preferably provided between the polyolefin porous film and a positive electrode active material layer of the positive electrode. The descriptions below of the physical properties of the porous layer describe at least the physical properties of a porous layer disposed between the polyolefin porous film and the positive electrode active material layer of the positive electrode in a nonaqueous electrolyte secondary battery.


The porous layer has a thickness (per one porous layer) of preferably 0.5 μm to 10 μm, and more preferably 1 μm to 5 μm, in order to secure (i) adhesiveness of the porous layer to an electrode and (ii) a high energy density. The porous layer having a thickness of not less than 0.5 μm (per one porous layer) makes it possible to sufficiently prevent an internal short circuit caused by e.g. damage to the nonaqueous electrolyte secondary battery, and also to retain a sufficient amount of the electrolyte in the porous layer. Setting the thickness of the porous layer to be not more than 10 μm (per one porous layer) decreases resistance to lithium ion permeation in the nonaqueous electrolyte secondary battery and therefore makes it possible to reduce a decrease in a rate characteristic and cycle characteristic. Setting the thickness of the porous layer to be less than 10 μm (per one porous layer) also reduces an increase in distance between the positive electrode and negative electrode, and therefore makes it possible to reduce a decrease in the internal volume efficiency of the nonaqueous electrolyte secondary battery.


The weight per unit area of the porous layer can be appropriately determined in view of the strength, film thickness, weight, and handleability of the porous layer. The weight per unit area of the porous layer is preferably 0.5 g/m2 to 20 g/m2, and more preferably 0.5 g/m2 to 10 g/m2, per one porous layer. A porous layer having a weight per unit area within the above numerical ranges allows a nonaqueous electrolyte secondary battery including the porous layer to have a higher weight energy density and a higher volume energy density. A porous layer whose weight per unit area exceeds the above ranges tends to cause a nonaqueous electrolyte secondary battery to be heavy.


The porous layer has a porosity of preferably 20% by volume to 90% by volume, and more preferably 30% by volume to 80% by volume, in order to achieve sufficient ion permeability. The pores in the porous layer have a diameter of preferably not more than 1.0 μm, and more preferably not more than 0.5 μm. In a case where the pores each have such a diameter, the porous layer can achieve sufficient ion permeability in a nonaqueous electrolyte secondary battery.


[2. Method of Producing Nonaqueous Electrolyte Secondary Battery Porous Layer]


The porous layer can be formed with use of a coating solution which is obtained by (i) dissolving or dispersing resin in a solvent and (ii) dispersing a filler in the solvent. The solvent can be described as both a solvent in which the resin is dissolved and a dispersion medium in which the resin or filler is dispersed. Examples of a method for forming the coating solution encompass a mechanical stirring method, an ultrasonic dispersion method, a high-pressure dispersion method, and a media dispersion method.


The porous layer can be formed by, for example, the following methods: (i) applying the coating solution directly to a surface of a base material and then removing the solvent, (ii) applying the coating solution to a suitable support, subsequently removing the solvent so as to form a porous layer, pressure-bonding the porous layer to the base material, and peeling the support off, (iii) applying the coating solution to a surface of a suitable support, pressure-bonding the base material to a coating surface, peeling the support off, and then removing the solvent, or (iv) carrying out dip coating by immersing the base material into the coating solution, and then removing the solvent.


The solvent preferably (i) does not have an adverse effect on the base material, (ii) allows the resin to be uniformly and stably dissolved in the solvent, and (iii) allows the filler to be uniformly and stably dispersed in the solvent. Examples of the solvent encompass N-methyl-2-pyrrolidone, N,N-dimethylacetamide, N,N-dimethylformamide, acetone, and water.


As necessary, the coating solution may contain, as a component(s) other than the resin and the filler, for example, a dispersing agent, a plasticizer, a surfactant, and/or a pH adjusting agent.


Examples of the base material other than the polyolefin porous film encompass a film other than the polyolefin porous film, a positive electrode, and a negative electrode.


The coating solution can be applied to the base material by a conventionally known method. Specific examples of such a method encompass a gravure coater method, a dip coater method, a bar coater method, and a die coater method.


In a case where the coating solution includes an aramid resin, the aramid resin can be deposited by applying moisture to the coating surface. The porous layer can be formed in this way. The specific method of applying moisture to the coating surface is applied is not particularly limited, but possible examples encompass (i) exposing the coating surface to a high humidity environment, (ii) spraying water, and (iii) blowing water vapor onto the surface with use of e.g. a nozzle.


Examples of a method of preparing the aramid resin encompass, but are not particularly limited to, condensation polymerization of para-oriented aromatic diamine and para-oriented aromatic dicarboxylic acid halide. In such a method, the aramid resin obtained is substantially composed of repeating units in which amide bonds occur at para or quasi-para positions of the aromatic ring. “Quasi-para positions” refers to positions at which bonds extend in opposing directions from each other, coaxially or in parallel, such as 4 and 4′ positions of biphenylene, 1 and 5 positions of naphthalene, and 2 and 6 positions of naphthalene.


A solution of poly(paraphenylene terephthalamide) can be prepared by, for example, a method including the following specific steps (I) through (IV).


(I) N-methyl-2-pyrrolidone is introduced into a dried flask. Then, calcium chloride which has been dried at 200° C. for 2 hours is added. Then, the flask is heated to 100° C. to completely dissolve the calcium chloride.


(II) The solution obtained in the step (I) is returned to room temperature, and then paraphenylenediamine is added and completely dissolved.


(III) While a temperature of the solution obtained in the step (II) is maintained at 20±2° C., terephthalic acid dichloride is added, the terephthalic acid dichloride being divided into 10 separate identical portions added at approximately 5-minute intervals.


(IV) While a temperature of the solution obtained in the step (III) is maintained at 20±2° C., the solution is matured for 1 hour, and is then stirred under reduced pressure for 30 minutes to eliminate air bubbles, so that the solution of the poly(paraphenylene terephthalamide) is obtained.


In an embodiment of the present invention, controlling particularly dissolved oxygen concentration during polymerization of the resin makes it possible to obtain a porous layer satisfying the above-described shear strength per weight per unit area. The dissolved oxygen concentration is preferably less than 10%, more preferably not more than 8%, and even more preferably not more than 5%. Setting the dissolved oxygen concentration to be less than 10% makes it possible to reduce or prevent oxidation polymerization of molecules that can become the starting point of a branched structure, and therefore makes it possible to sufficiently increase the cohesive force of molecules.


For example, in the method of preparing the poly(paraphenylene terephthalamide), in step (III) (in which terephthalic acid dichloride is added to a paraphenylenediamine solution) it is preferable to control the dissolved oxygen concentration in the solution. For example, it is possible to control the dissolved oxygen concentration by controlling the amount of nitrogen introduced during polymerization. In a case where the dissolved oxygen concentration is high, part of the paraphenylenediamine will undergo oxidation polymerization. This can result in branching of the structure of the poly(paraphenylene terephthalamide). This branching inhibits packing of the molecules, and consequently causes a decrease in cohesive force of the molecules. In a case where the dissolved oxygen concentration is low, a branched structure caused by the oxidation polymerization of the paraphenylenediamine is reduced. This allows a crystalline structure of the poly(paraphenylene terephthalamide) to easily develop, and consequently causes an increase in cohesive force of the molecules. As such, a porous layer produced under conditions where the dissolved oxygen concentration is low tends to have higher shear strength. Note that a decrease in cohesive force due to a branched structure occurs also in resins other than aramid resins. As such, in resins other than aramid resins as well, preventing the production of a branched structure makes it possible to increase cohesive force.


[3. Nonaqueous Electrolyte Secondary Battery Laminated Separator]


A laminated separator for a nonaqueous electrolyte secondary battery (herein also referred to as a “nonaqueous electrolyte secondary battery laminated separator”) in accordance with an embodiment of the present invention includes: a polyolefin porous film; and the above-described nonaqueous electrolyte secondary battery porous layer, the nonaqueous electrolyte secondary battery porous layer being formed on at least one surface of the polyolefin porous film. Hereinafter, a nonaqueous electrolyte secondary battery laminated separator may also be referred to simply as a “laminated separator”.


The laminated separator has an air permeability of preferably 30 s/100 mL to 1000 s/100 mL, and more preferably 50 s/100 mL to 800 s/100 mL, in terms of Gurley values. The laminated separator having an air permeability falling within the above range makes it possible for the laminated separator to achieve sufficient ion permeability in a nonaqueous electrolyte secondary battery.


<Polyolefin Porous Film>


Hereinafter, a polyolefin porous film may be referred to simply as a “porous film”. The porous film contains a polyolefin-based resin as a main component and has therein many pores connected to one another, so that gas and liquid can pass through the porous film from one surface to the other. A polyolefin porous film can serve as a base material for a laminated separator in which a porous layer (described later) is formed.


The porous film contains polyolefin at a proportion of not less than 50% by volume, preferably not less than 90% by volume, and more preferably not less than 95% by volume, relative to the entire porous film. The polyolefin more preferably contains a high molecular weight component having a weight-average molecular weight of 5×105 to 15×106. In particular, the polyolefin more preferably contains a high molecular weight component having a weight-average molecular weight of not less than 1,000,000 because such a high molecular weight component improves the strength of a resultant nonaqueous electrolyte secondary battery separator.


Examples of the polyolefin (thermoplastic resin) encompass a homopolymer or a copolymer each produced by polymerizing a monomer such as ethylene, propylene, 1-butene, 4-methyl-1-pentene, and 1-hexene. Examples of the homopolymer encompass polyethylene, polypropylene, and polybutene. Examples of the copolymer encompass an ethylene-propylene copolymer.


Among the above examples, polyethylene is more preferable as it is capable of preventing a flow of an excessively large electric current at a lower temperature. This preventing of an excessively large electric current is also referred to as shutdown. Examples of the polyethylene encompass low-density polyethylene, high-density polyethylene, linear polyethylene (ethylene-α-olefin copolymer), and ultra-high molecular weight polyethylene having a weight-average molecular weight of not less than 1,000,000. Among these examples, ultra-high molecular weight polyethylene having a weight-average molecular weight of not less than 1,000,000 is preferable.


The porous film has a thickness of preferably 4 μm to 40 μm, more preferably 5 μm to 30 μm, and even more preferably 6 μm to 15 μm.


A weight per unit area of the porous film can be set as appropriate in view of strength, thickness, weight, and handleability. Note, however, that the weight per unit area of the porous film is preferably 4 g/m2 to 20 g/m2, more preferably 4 g/m2 to 12 g/m2, and even more preferably 5 g/m2 to 10 g/m2, so as to allow the nonaqueous electrolyte secondary battery to have a higher weight energy density and a higher volume energy density.


The porous film has an air permeability of preferably 30 s/100 mL to 500 s/100 mL, and more preferably 50 s/100 mL to 300 s/100 mL, in terms of Gurley values. A porous film having the above air permeability can achieve sufficient ion permeability.


The porous film has a porosity of preferably 20% by volume to 80% by volume, and more preferably 30% by volume to 75% by volume, so as to (i) retain an electrolyte in a larger amount and (ii) obtain a function of reliably preventing a flow of an excessively large electric current at a lower temperature. Further, in order to achieve sufficient ion permeability and prevent particles from entering the positive electrode and/or the negative electrode, the porous film has pores each having a pore size of preferably not more than 0.3 μm, and more preferably not more than 0.14 μm.


[4. Method of Producing Nonaqueous Electrolyte Secondary Battery Laminated Separator]


A method of producing the nonaqueous electrolyte secondary battery laminated separator in accordance with an embodiment of the present invention can be, for example, a method in which, in the above-described method for producing the nonaqueous electrolyte secondary battery porous layer, the above-described polyolefin porous film is used as the base material which is coated with the coating solution. Note that, herein, a direction in which the porous film or laminated separator is transferred during production may also be referred to as a “machine direction” (MD), and a direction which is (i) parallel to the surface of the porous film or laminated separator and (ii) perpendicular to the MD may also be referred to as a “transverse direction” (TD).


A method of producing the porous film is not particularly limited. For example, the polyolefin porous film can be produced by a method as follows. First, polyolefin-based resin is kneaded together with a pore forming agent such as an inorganic bulking agent or a plasticizer, and optionally with another agent(s) such as an antioxidant. After kneading, the kneaded substances are extruded so as to produce a polyolefin resin composition in sheet form. The pore forming agent is then removed from the polyolefin resin composition in sheet form with use of a suitable solvent. After the pore forming agent is removed, the polyolefin resin composition is stretched so that a polyolefin porous film is obtained.


The inorganic bulking agent is not particularly limited. Examples of the inorganic bulking agent encompass inorganic fillers; one specific example is calcium carbonate. The plasticizing agent is exemplified by, but not particularly limited to, a low molecular weight hydrocarbon such as liquid paraffin.


Examples of methods for producing the porous film encompass a method including the following steps.


(A) Obtaining a polyolefin resin composition by kneading ultra-high molecular weight polyethylene, low molecular weight polyethylene having a weight-average molecular weight of not more than 10,000, a pore forming agent such as calcium carbonate or a plasticizer, and an antioxidant;


(B) Forming a sheet by (i) rolling the polyolefin resin composition with use of a pair of reduction rollers and (ii) cooling the polyolefin resin composition in stages while tensioning the polyolefin resin composition with use of a take-up roller whose velocity ratio differs from that of the reduction rollers;


(C) Removing the pore forming agent from the sheet with use of a suitable solvent; and


(D) Stretching the sheet, from which the pore forming agent has been removed, with use of a suitable stretch ratio.


[5. Nonaqueous Electrolyte Secondary Battery Member, Nonaqueous Electrolyte Secondary Battery]


A member for a nonaqueous electrolyte secondary battery (herein also referred to as a “nonaqueous electrolyte secondary battery member”) in accordance with an embodiment of the present invention includes: a positive electrode; the above-described nonaqueous electrolyte secondary battery porous layer or nonaqueous electrolyte secondary battery laminated separator; and a negative electrode, the positive electrode, the nonaqueous electrolyte secondary battery porous layer or nonaqueous electrolyte secondary battery laminated separator, and the negative electrode being arranged in this order. A nonaqueous electrolyte secondary battery in accordance with an embodiment of the present invention includes the above-described nonaqueous electrolyte secondary battery porous layer or nonaqueous electrolyte secondary battery laminated separator. The nonaqueous electrolyte secondary battery is not particularly limited in shape and can have any shape such as the shape of a thin plate (sheet), a disk, a cylinder, or a prism such as a cuboid.


The nonaqueous electrolyte secondary battery can be produced by a publicly known conventional method. As one example, first, a nonaqueous electrolyte secondary battery member is formed by providing a positive electrode, the polyolefin porous film, and a negative electrode in this order. The porous layer can be provided between the polyolefin porous film and at least one of the positive electrode and the negative electrode. Next, the nonaqueous electrolyte secondary battery member is inserted into a container which serves as a housing for the nonaqueous electrolyte secondary battery. The container is then filled with nonaqueous electrolyte, and then hermetically sealed while pressure is reduced in the container. In this way, the nonaqueous electrolyte secondary battery can be produced.


<Positive Electrode>


The positive electrode employed in an embodiment of the present invention is not limited to any particular one, provided that the positive electrode is one that is generally used as a positive electrode of a nonaqueous electrolyte secondary battery. Examples of the positive electrode encompass a positive electrode sheet having a structure in which an active material layer, containing a positive electrode active material and a binding agent, is formed on a positive electrode current collector. The active material layer may further contain an electrically conductive agent.


Examples of the positive electrode active material encompass materials each capable of being doped with and dedoped of metal ions such as lithium ions or sodium ions. Specific examples of the materials encompass lithium complex oxides each containing at least one transition metal such as V, Mn, Fe, Co, or Ni.


Examples of the electrically conductive agent encompass carbonaceous materials such as natural graphite, artificial graphite, cokes, carbon black, pyrolytic carbons, carbon fiber, and a fired product of an organic polymer compound. It is possible to use only one of the above electrically conductive agents, or two or more of the above electrically conductive agents in combination.


Examples of the binding agent encompass: fluorine-based resins such as polyvinylidene fluoride (PVDF); acrylic resin; and styrene butadiene rubber. Note that the binding agent serves also as a thickener.


Examples of positive electrode current collector encompass electric conductors such as Al, Ni, and stainless steel. Of these electric conductors, Al is more preferable because Al is easily processed into a thin film and is inexpensive.


Examples of a method for producing the positive electrode sheet encompass: a method in which the positive electrode active material, the electrically conductive agent, and the binding agent are pressure-molded on the positive electrode current collector; and a method in which (i) the positive electrode active material, the electrically conductive agent, and the binding agent are formed into a paste with use of an appropriate organic solvent, (ii) the positive electrode current collector is coated with the paste, and (iii) the paste is dried and then pressured so that the paste is firmly fixed to the positive electrode current collector.


<Negative Electrode>


The negative electrode employed in an embodiment of the present invention is not limited to any particular one, provided that the negative electrode is one that is generally used as a negative electrode of a nonaqueous electrolyte secondary battery. Examples of the negative electrode encompass a negative electrode sheet having a structure in which an active material layer, containing a negative electrode active material and a binding agent, is formed on a negative electrode current collector. The active material layer may further contain an electrically conductive agent.


Examples of the negative electrode active material encompass materials each capable of being doped with and dedoped of metal ions such as lithium ions or sodium ions. Examples of the materials encompass carbonaceous materials. Examples of the carbonaceous materials encompass natural graphite, artificial graphite, cokes, carbon black, and pyrolytic carbons.


Examples of the negative electrode current collector encompass Cu, Ni, and stainless steel. Of these materials, Cu is more preferable because Cu is not easily alloyed with lithium and is easily processed into a thin film.


Examples of a method for producing the negative electrode sheet encompass: a method in which the negative electrode active material is pressure-molded on the negative electrode current collector; and a method in which (i) the negative electrode active material is formed into a paste with use of an appropriate organic solvent, (ii) the negative electrode current collector is coated with the paste, and (iii) the paste is dried and then pressure is applied so that the paste is firmly fixed to the negative electrode current collector. The paste preferably contains an electrically conductive agent as described above and a binding agent as described above.


<Nonaqueous Electrolyte>


A nonaqueous electrolyte for an embodiment of the present invention is not limited to any particular one, provided that the nonaqueous electrolyte is one that is generally used for a nonaqueous electrolyte secondary battery. The nonaqueous electrolyte can be, for example, a nonaqueous electrolyte containing an organic solvent and a lithium salt dissolved therein. Examples of the lithium salt encompass LiClO4, LiPF6, LiAsF6, LiSbF6, LiBF4, LiCF3SO3, LiN(CF3SO2)2, LiC(CF3SO2)3, Li2B10Cl10, lower aliphatic carboxylic acid lithium salt, and LiAlCl4. It is possible to use only one of the above lithium salts or two or more of the above lithium salts in combination.


Examples of the organic solvent to be contained in the nonaqueous electrolyte encompass carbonates, ethers, esters, nitriles, amides, carbamates, sulfur-containing compounds, and fluorine-containing organic solvents each obtained by introducing a fluorine group into any of these organic solvents. It is possible to use only one of the above organic solvents or two or more of the above organic solvents in combination.


EXAMPLES

The present invention will be described below in more detail with reference to Examples and Comparative Examples. Note, however, that the present invention is not limited to such Examples.


[Measurement Methods]


The methods used for various measurements in the Examples and Comparative Example are as follows.


<Air Permeability of Laminated Separator>


The air permeability of the laminated separator was measured in conformance with JIS P8117.


<Thickness of Porous Layer>


The thickness of the laminated separator was measured with use of a high-precision digital measuring device manufactured by Mitutoyo Corporation. Thereafter, peel-off tape was affixed to a porous layer side of the laminated separator, and then the porous layer was peeled off from a polyethylene porous film of the laminated separator. The thickness of the polyethylene porous film from which the porous layer was peeled was then measured in the same manner as for the laminated separator. The thickness of the porous layer was calculated by subtracting (i) the thickness of the polyethylene porous film (from which the porous layer was peeled) from (ii) the thickness of the laminated separator.


<Weight Per Unit Area of Porous Layer>


A square sample measuring 8 cm×8 cm was cut out from the laminated separator, and the weight W1 [g] of the sample was measured. Then, peel-off tape was affixed to a porous layer side of the sample, and then the porous layer was peeled off from the polyethylene porous film. The weight W2 [g] of the polyethylene porous film after the peeling was measured. Then, the weight per unit area [g/m2] of the porous layer was calculated according to the following Formula (A).





Weight per unit area of porous layer=(W1−W2)/(0.08×0.08)  (A)


<Porosity of Porous Layer>


A 4 mm to 6 mm square piece of the porous layer was cut out from the laminated separator, and was vacuum-dried at 30° C. or lower for 17 hours. Then, a real density of the porous layer was measured by a helium gas displacement method with use of a dry-type automatic densimeter (AccuPye II 1340 manufactured by Micromeritics Instrument Corporation).


From the real density [g/m3], the thickness [μm], and the weight per unit area [g/m2], the porosity [% by volume] of the porous layer was calculated based on the following Formula (B).





(Porosity)=[1−(Weight per unit area of porous layer)/{(Thickness of porous layer)×10−6×(Real density of porous layer)}]×100  (B)


<Shear Strength Per Weight Per Unit Area of Porous Layer>


A glass epoxy resin substrate measuring 50 mm in length by 30 mm in width by 2 mm in thickness was used. A piece of double-sided tape (Nice Tack (trademark) NW-10, manufactured by Nichiban Co., Ltd.) measuring 10 mm in width was affixed to one lengthwise end of the resin substrate, with care being taken so as to avoid wrinkles in the tape. The double-sided tape was affixed such that the widthwise direction of the double-sided tape was parallel to the lengthwise direction of the resin substrate. A region of the resin substrate to which the double-sided tape was affixed measured 10 mm (in the lengthwise direction of the resin substrate) by 30 mm (in the widthwise direction of the resin substrate). Two resin substrates were prepared in the above manner for each Example and Comparative Example subject to measurement. Hereinafter, these two resin substrates may also be referred to respectively as a resin substrate (1) and a resin substrate (2).


Next, a peel-off film on the back side of the double-sided tape on the resin substrate (1) was removed to expose the adhesive surface of the tape. The porous-layer-side surface of a laminated separator (50 mm×50 mm) was affixed to the adhesive surface, with care being taken to avoid wrinkling or air bubbles. The laminated separator was affixed such that the MD of the laminated separator was parallel to the lengthwise direction of the resin substrate (1). After affixing the laminated separator, a 5 kg load was applied to the area of affixation for 30 minutes. Thereafter, while the resin substrate (1) was held down, the porous layer was separated from the base material of the laminated separator. In other words, the polyethylene porous film serving as the base material of the laminated separator was peeled off from the porous layer, in a manner so that the porous layer remained affixed to the resin substrate (1). After the peeling, it was confirmed that there were no cracks in surface of the porous layer and that the porous layer was intact. The size of the porous layer which had been thus separated was the same as the area of the resin substrate to which the double-sided tape was affixed, i.e., 10 mm (in the lengthwise direction of the resin substrate) by 30 mm (in the widthwise direction of the resin substrate).


Next, a peel-off film on the back side of the double-sided tape on the resin substrate (2) was removed to expose the adhesive surface. This adhesive surface was affixed to the surface of the porous layer affixed to the resin substrate (1). Thereafter, a 5 kg load was applied to the area of affixation for 30 minutes. Next, the load was removed, and the test piece was further allowed to stand for 24 hours in an environment at 23° C. The test piece produced in this manner was used in measurements. This test piece is illustrated in FIG. 1 as the test piece 100.


A tension test was carried out in accordance with the method in JIS K6850. A tension test device (Tensilon Universal Material Testing Instrument RTG-1310, manufactured by A&D Company, Limited) was used for the test. Test conditions were: temperature: 23° C.; and pulling speed: 50 mm/s. In the tension test, a maximum value of the shear strength when the test piece was pulled in the lengthwise direction by up to 3 mm was divided by the weight per unit area of the porous layer. The numerical value thus obtained was considered to be a shear strength per weight per unit area of the porous layer. Measurement was carried out 3 times for each Example and Comparative Example. An average value of the shear strengths per weight per unit area of the porous layer thus calculated was used as a shear strength per weight per unit area of the porous layer in each Example and Comparative Example.


<Heat Resistance Evaluation (Soldering Iron Test)>



FIG. 2 is a diagram schematically illustrating an outline of a soldering iron test. A laminated separator 2, which has been cut out to a size of 40 mm×60 mm, was placed so as to cover an opening of a 80 mm×80 mm metal sample base 20. The opening is positioned at a center of the metal sample base 20, and has dimensions of 20 mm in length by 20 mm in width by 4 mm in depth. The laminated separator was cut out to be 40 mm in the MD. The laminated separator was placed so that a surface on the porous layer side is facing upwards.


Next, with use of a polyimide adhesive tape manufactured by Nitto Denko Corporation, a short side of the laminated separator 2 was fixed to the metal sample base 20 such that no wrinkles are created. Then, the metal sample base 20, on which the laminated separator 2 is fixed, was placed on a precision jack 21. Then, a soldering iron 22 was placed above the precision jack 21 with use of a clamp. RX-80HRT-B manufactured by Taiyo Electric Ind. Co., Ltd. was used as a soldering bit of the soldering iron 22. After a temperature of the soldering bit was set to 450° C., the precision jack 21 was raised so that the soldering bit perforated the laminated separator 2 until the soldering bit came into contact with a bottom of the opening of the metal sample base 20. 5 seconds after the soldering bit came into contact with the bottom of the opening of the metal sample base 20, the precision jack 21 was lowered. This produced a laminated separator 2 having a through hole.


A photograph of the laminated separator having the through hole was taken. When the photograph was taken, the photograph included a 1-cm line which was drawn in the vicinity of the laminated separator so that the scale of the through hole can be recognized. Next, with use of image analysis software “Image J”, a line was drawn along the shape of the through hole, and an area of the through hole was calculated. The soldering iron test was conducted 3 times for each Example and Comparative Example. An average value of the areas of the through holes obtained was considered to be an opening area.


<Measurement of Dissolved Oxygen Concentration During Polymerization>


When measuring the dissolved oxygen concentration during preparation of the poly(paraphenylene terephthalamide) (described later), a rubber septum cap was fitted to the lid of the separable flask that was used. A reaction device was assembled such that nitrogen or a mixture of nitrogen and air was supplied from one direction, flowed through the separable flask, and flowed out toward another direction. The needle of a suction syringe connected to an oxygen concentration meter (Pack Keeper RO-103KS, manufactured by Iijima Denshi Kogyo) was stuck through the septum cap, and the concentration of gaseous oxygen was measured. Because the first measurement is insufficient to completely replace the gas in the oxygen concentration meter, a plurality of measurements were performed. A stable measured value obtained from a second or later measurement was used as the oxygen concentration. In a state of equilibrium, gaseous oxygen concentration is approximately equal to the dissolved oxygen concentration. As such, it is possible to use the oxygen concentration meter to determine the dissolved oxygen concentration in an indirect manner.


Example 1

Poly(paraphenylene terephthalamide) was produced with use of a 3-liter separable flask having a stirring blade, a thermometer, a nitrogen inflow tube, and a powder addition port. The separable flask was dried sufficiently, and then 2200 g of N-methyl-2-pyrrolidone (NMP) was introduced therein. Next, 151.07 g of calcium chloride powder which had been vacuum dried at 200° C. for 2 hours was added. Thereafter, the flask was heated to 100° C. to completely dissolve the calcium chloride powder. The flask was returned to room temperature, and then 68.23 g of paraphenylenediamine was added and completely dissolved. While a temperature of this solution was maintained at 20±2° C. and a dissolved oxygen concentration during polymerization was maintained at 0.5%, 124.97 g of terephthalic acid dichloride was added. Specifically, the terephthalic acid dichloride was divided into 10 separate identical portions which were added at approximately 5-minute intervals. The solution was then matured by stirring the solution for 1 hour while maintaining a temperature of 20±2° C. Thereafter, the solution was filtered through a 1500-mesh stainless steel gauze. The resulting solution had a poly(paraphenylene terephthalamide) concentration of 6 weight %.


Next, 100 g of this poly(paraphenylene terephthalamide) solution was weighed out into a flask. Thereafter, 300 g of NMP was added so as to obtain a solution in which the concentration of poly(paraphenylene terephthalamide) was 1.5 weight %. The solution (in which the concentration of poly(paraphenylene terephthalamide) was 1.5 weight %) was stirred for 60 minutes. Thereafter, 6 g of Alumina C (manufactured by Nippon Aerosil Co., Ltd.) and 6 g of AKP3000 (manufactured by Sumitomo Chemical Co., Ltd.) were) added to the solution, and stirring was performed for 240 minutes. A resultant solution was filtered through a 1000-mesh metal gauze. Thereafter, 0.73 g of calcium carbonate was added, followed by 240 minutes of stirring to achieve neutralization. A resultant solution was then defoamed under reduced pressure, so that a coating solution slurry was obtained.


The coating solution slurry was continuously coated onto a polyethylene porous film measuring 10.5 μm in thickness. A coating film thus formed was then brought into an atmosphere having a temperature 50° C. and a relative humidity of 70%, so that the poly(paraphenylene terephthalamide) was deposited. Next, the coating film from which the poly(paraphenylene terephthalamide) was deposited was rinsed with water, and then drying was performed. A laminated separator was thus obtained. The laminated separator obtained had an air permeability of 240.5 s/100 mL. The porous layer had a thickness of 2.1 μm, a weight per unit area of 1.8 g/m2, and a porosity of 64% by volume.


Example 2

A laminated separator was produced in a manner similar to Example 1, except that the dissolved oxygen concentration during polymerization was 3%. The laminated separator obtained had an air permeability of 252.9 s/100 mL. A porous layer had a thickness of 2.2 μm, a weight per unit area of 1.7 g/m2, and a porosity of 68% by volume.


Comparative Example 1

A laminated separator was produced in a manner similar to Example 1, except that the dissolved oxygen concentration during polymerization was 10%. The laminated separator obtained had an air permeability of 240.9 s/100 mL. A porous layer had a thickness of 2.8 μm, a weight per unit area of 1.8 g/m2, and a porosity of 73% by volume.


Comparative Example 2

A laminated separator was produced in a manner similar to Example 1, except that the dissolved oxygen concentration during polymerization was 21%. The laminated separator obtained had an air permeability of 245.1 s/100 mL. A porous layer had a thickness of 2.2 μm, a weight per unit area of 1.8 g/m2, and a porosity of 66% by volume.


[Results]


Measurement results are shown below. Note that the opening areas are each shown as a value relative to the value in Comparative Example 1 regarded as 100%.













TABLE 1






Example
Example
Comparative
Comparative



1
2
Example 1
Example 2



















Dissolved oxygen
0.5
3
10
21


concentration (%)






during






polymerization






Shear strength
179
162
121
117


per weight






per unit area






(N/[mm3/(g/m2)])






Relative value (%)
78
80
100
108


of opening area













By controlling the dissolved oxygen concentration during the polymerization, it was possible to control the shear strength per weight per unit area of the porous layer. In comparison with Comparative Examples 1 and 2 in which the shear strength per weight per unit area was less than 140 N/[mm3/(g/m2)], the opening area was reduced in Examples 1 and 2 in which the shear strength per weight per unit area was not less than 140 N/[mm3/(g/m2)]. This indicates that Examples 1 and 2, in which the shear strength per weight per unit area was not less than 140 N/[mm3/(g/m2)], show excellent heat resistance.


INDUSTRIAL APPLICABILITY

An aspect of the present invention can be used in production of a nonaqueous electrolyte secondary battery laminated separator having improved heat resistance.


REFERENCE SIGNS LIST






    • 1 Porous layer


    • 2 Laminated separator




Claims
  • 1. A nonaqueous electrolyte secondary battery porous layer, the nonaqueous electrolyte secondary battery porous layer having a shear strength per weight per unit area of not less than 140 N/[mm3/(g/m2)].
  • 2. The nonaqueous electrolyte secondary battery porous layer according to claim 1, wherein the nonaqueous electrolyte secondary battery porous layer has a porosity of 20% by volume to 90% by volume.
  • 3. The nonaqueous electrolyte secondary battery porous layer according to claim 1, wherein the nonaqueous electrolyte secondary battery porous layer contains at least one resin selected from a group consisting of a resin having a melting point or a glass transition temperature of not lower than 180° C., a polyamide-based resin, a polyimide-based resin, and a polyester-based resin.
  • 4. The nonaqueous electrolyte secondary battery porous layer according to claim 1, wherein the nonaqueous electrolyte secondary battery porous layer contains a polyamide-based resin.
  • 5. A nonaqueous electrolyte secondary battery laminated separator comprising: a polyolefin porous film; andthe nonaqueous electrolyte secondary battery porous layer according to claim 1,the nonaqueous electrolyte secondary battery porous layer being formed on at least one surface of the polyolefin porous film.
  • 6. A nonaqueous electrolyte secondary battery member comprising: a positive electrode;the nonaqueous electrolyte secondary battery porous layer according to claim 1; anda negative electrode,the positive electrode, the nonaqueous electrolyte secondary battery porous layer, and the negative electrode being arranged in this order.
  • 7. A nonaqueous electrolyte secondary battery comprising: the nonaqueous electrolyte secondary battery porous layer according to claim 1.
  • 8. A nonaqueous electrolyte secondary battery member comprising: a positive electrode;the nonaqueous electrolyte secondary battery laminated separator according to claim 5; anda negative electrode,the positive electrode, the nonaqueous electrolyte secondary battery laminated separator, and the negative electrode being arranged in this order.
  • 9. A nonaqueous electrolyte secondary battery comprising: the nonaqueous electrolyte secondary battery laminated separator according to claim 5.