Nonaqueous liquid electrolyte

Abstract

Disclosed is a nonaqueous and nonvolatile liquid type polymeric electrolyte comprising poly(siloxane-g-ethylene oxide). This electrolyte provides significant safety and stability. The present invention solves the problems of volatility, flammability and chemical reactivity of lithium ion type electrolytes. The disclosed electrolyte exhibits excellent stability, conductivity and low impedance characteristics. The electrolyte comprises a new class of structural siloxane polymers with one or more poly(ethylene oxide) side chains. The inorganic siloxanes comprising the main backbone of the copolymers are thermally very stable and resistant to decomposition by heat. Because the main chain of the disclosed class of electrolytes is an Si—O linkage, initiation of the combustion cycle is inhibited or prevented.

Description

FIELD OF THE INVENTION

[0003] The present invention relates to electrochemical storage devices containing a nonaqueous electrolyte with high ionic conductivity and nonvolatile characteristics. More particularly, the present invention relates to liquid type polymeric electrolytes that are superior in ionic conductivity, thermal stability and safety to most of those currently being used in lithium-ion cells today.

BACKGROUND OF THE INVENTION

[0004] The demand for lithium secondary batteries to meet high power and high-energy system applications has resulted in substantial research and development activities to improve their safety, as well as performance. As the world becomes increasingly dependent on portable electronic devices, and looks toward increased use of electrochemical storage devices for vehicles, power distribution load leveling and the like, it is increasingly important that the safety of such devices be paramount, especially as these devices are being used in such environments as airliners and space vehicles. The effort to date has included research in flame-retardants, solid polymer electrolytes and new electrolyte concepts with improved thermostability. Thus, the development of highly conductive electrolytes, free of any problems associated with volatile and combustible solvents, is of paramount importance. Electrolytes based on polymeric structures have basically better heat and chemical resistance than conventional organic carbonate-based electrolytes and can thus reduce many chemical side reactions occurring in lithium secondary batteries. Although, polymeric based electrolytes have many advantages over carbonate solvent based electrolytes, their application in lithium secondary batteries has been limited due to their low ionic conductivity, usually below 10−5 S/cm at room temperature.

[0005] To solve this problem, new electrolyte concepts are needed. The new electrolytes should be nonvolatile materials that have excellent electrochemical properties, such as high ionic conductivity of over 10−4 S/cm at room temperature and wide electrochemical stability windows of over 4.5 V (based on lithium metal).

[0006] Accordingly, the present inventors have developed a new type of ionically conductive electrolyte based on various polymeric structures, especially having a poly(siloxane-g-ethylene oxide) composition which overcomes the above mentioned problems of volatility, flammability and chemical reactivity inside of the lithium battery. The proposed liquid type poly(siloxane-g-ethylene oxide) materials also have an excellent electrochemical stability window and favorable room temperature ionic conductivity.

[0007] Carbonate solvents, such as ethylene carbonate and ethyl-methyl carbonate used for conventional lithium battery electrolytes can easily bum from low temperature sources of ignition and generate flame, carbon dioxide and H2O during thermal degradation. This is a critical problem in high capacity battery applications like lithium batteries for electric vehicles (EV) and satellites. Polymeric materials, however, usually have a somewhat different combustion mechanism than the carbonates. The initial stage of a fire occurs when a heat source decomposes the polymeric materials to flammable volatile products. Thus, for continuous burning to occur, (a) the application of heat must be sufficient to decompose the polymer, (b) the temperature must be sufficient to ignite the products of decomposition, and (c) the amount of heat transferred from the flame back to the polymer must be sufficient to maintain the cycle. In general, polymeric materials are more thermally stable than low molecular weight chemicals like the organic carbonates because they are not volatile and are vaporized at much higher temperatures.

[0008] The present inventors have carefully considered the combustion mechanisms of polymeric materials and concluded that to stop the propagation of the burning cycle one needed to develop new polymer materials that are thermally more stable and capable of dissolving the lithium salts to prepare electrolytes for electrochemical devices such as lithium batteries and/or capacitors. The present inventors have developed new structural siloxane polymers with one or more poly(ethylene oxide) side chains. Siloxanes are very thermally stable and are decomposed by heat with difficulty. Only a few flammable by-products are formed during the thermal decomposition of such polymers because their main chain is a Si—O linkage. Thus, its presence in the proposed polymers will delay the initiation of the combustion cycle.

[0009] Due to the merits of siloxane-poly(ethylene oxide) graft copolymers, substantial research has been done. See, for example, U.S. Pat. No. 5,112,512 to Nakamura and U.S. Pat. No. 6,124,062 to Horie et al. also describing siloxane-poly(ethylene oxide) graft copolymers (as a polymeric electrolyte material. The '512 patent discloses a crosslinked polymer electrolyte based on the graft copolymers, but its ionic conductivity is too low for room temperature applications. The '062 patent discloses direct use of siloxane-poly(ethylene oxide) grafted copolymers as a liquid for a lithium battery electrolyte with ionic conductivity of around 10−3 S/cm at ca. 25° C. (See General Formula I). The conductivity of the material disclosed in the '062 patent is disadvantageously low. In addition, the cost of such material is relatively high. The present inventors have discovered a much improved material with higher conductivity and lower cost. 1

[0010] wherein R is alkyl group.

[0011] The present inventors developed an improved liquid state siloxane polymer with one or more poly(ethylene oxide) side chains to ensure thermal stability and electrochemical properties. Poly(ethylene oxides) (PEO) in poly(siloxane-g-ethylene oxide) materials of this invention (see general formula II) are directly bonded to a Si atom. Poly(siloxane-g-ethylene oxide) materials of the present invention are easily synthesized through a simple dehydrocoupling reaction with simple metal carbonate based catalysts and the cost for synthesis of poly(siloxane-g-ethylene oxide) of this invention is much lower than the cost of synthesis of general formula (I) with a propylene spacer between siloxane and PEO. The present inventors also control the viscosity of the materials to get high ionic conductivities of around 10−3 S/cm at room temperature. 2

[0012] where R and R″ are alkyl groups and R′ is hydrogen or alkyl group.

[0013] As compared to the material disclosed in the '062 patent, ionic conductivity is improved by changing the chemical structure of siloxane, that is, directly grafting ethylene oxide onto Si atom without any alkyl carbon spacer between them. Changing the structure in this way increases hydrophilicity and solubility, leading to higher conductivity.

OBJECTIVES OF THE INVENTION

[0014] A primary objective of the present invention is to provide a safe liquid electrolyte for use in lithium ion type cells and allied devices such as super capacitors and hybrid devices. Specifically, a primary objective is to reduce or eliminate problems associated with volatility, flammability and chemical reactivity of liquid electrolytes.

[0015] A further objective of the invention is to provide a lithium-based secondary battery, capacitor or hybrid device with enhanced safety and excellent performance characteristics by use of the present polymeric electrolyte.

SUMMARY OF THE INVENTION

[0016] Accordingly, the present invention relates to lithium-based secondary batteries with a nonaqueous and nonvolatile polymeric electrolyte with high room temperature ionic conductivity with enhanced safety.

[0017] The invention also relates to nonaqueous and nonvolatile polymeric electrolytes processing controlled viscosity for the high-energy lithium secondary battery applications, especially for electric vehicles and satellite applications.

[0018] To fulfill the above objectives, the nonaqueous and nonvolatile polymeric electrolyte solutions in the present invention is prepared by using the compositions which comprise poly(siloxane-g-ethylene oxide) in a liquid state with proper viscosity and a dissolved lithium salt.

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] FIG. 1 is a is a trace of measured ionic conductivity vs. temperature for a cell made according to the present invention.

[0020] FIGS. 2 a and 2b are traces of cyclic voltammetry measurements to determine electrochemical stability of samples made according to the present invention.

[0021] FIG. 3 is a trace of measured ionic conductivity showing the effect of doping level, on the ionic conductivity of poly(siloxane-g-3 ethylene oxide) electrolyte at two different temperatures.

[0022] FIG. 4 is a trace of measured ionic conductivity of poly(siloxane-g-3 ethylene oxide) electrolyte with LiPF6 in place of LiTFSI at a doping level of 32:1.

[0023] FIG. 5 a is a data trace from accelerating rate calorimetry (ARC) tests of the electrolyte of the present invention.

[0024] FIG. 5 b is a comparative data trace from ARC tests of liquid electrolyte LiPF6 in a mixture of ethylene carbonate and ethyl methyl carbonate.

[0025] FIG. 6 is a graph of the results of comparative flame tests based on Underwriters Laboratories UL94 standard.

DETAILED DESCRIPTION OF THE INVENTION

[0026] The electrolyte solution of the present invention comprises siloxane polymers with one or more poly(ethylene oxide) as a side chain (see general formula II above). The inorganic siloxane main body ensures flame-retardancy and chemical stability, and poly(ethylene oxide) side chains give ionic conducting phases. A poly(ethylene oxide) group is directly grafted to silicon atoms in the siloxane polymer. The poly(siloxane-g-ethylene oxides) of the present invention are easily synthesized through simple dehydrogenation reactions to avoid problems that come from the use of metal catalysts such as platinum.

[0027] The poly(siloxane-g-ethylene oxide) easily dissolves lithium salt and has enough flexibility to transport lithium ions. Through the viscosity control of the poly(siloxane-g-ethylene oxide), the polymeric electrolyte solution provides excellent ionic conductivity of around 10−3 S/cm at room temperature.

[0028] The lithium salt to be used in the present invention is not particularly limited, as long as it serves as an electrolyte for a lithium secondary battery. Examples of specific lithium salts include, but are not limited to, LiClO4, LiBF4, LiAsF6, LiPF6, LiCF3SO3, Li(CF3SO2)2N, Li(CF3SO2)3C, LiN(SO2C2F5)2), lithium alkyl fluorophosphates, and mixtures thereof.

[0029] Further examples (without the intent to limit the scope of the invention) found to beneficial are lithium bis(chelato)borates having from five to seven membered rings as follows: 3

[0030] The oxygen versus Li ratio (doping level) is preferably 5:1 to 50: 1. If the doping level is greater than 50:1, the ionic conductivity of the resulting polymeric electrolyte is undesirably decreased because of the number of ions present in the solid polymer electrolyte. If the doping level is smaller than 5:1, the lithium salt is not sufficiently dissociated in the resulting polymeric electrolyte and the association of lithium ion reduces the ionic conductivity. Preferably, the average molecular weight of the poly(siloxane-g-ethylene oxide) should not exceed 20,000 g/mol. The dynamic viscosity of the poly(siloxane-g-ethylene oxide) is best in the range of 200 cPs, should preferably not exceed 1,000 cPs to 2,000 cPs, and should never exceed 10,000 cPs.

[0031] The present invention covers both polymeric electrolytes as well as the lithium secondary batteries that use them in the same way that the carbonate based electrolytes are applied in the state-of-the-art Li-ion batteries today. A lithium secondary battery with the polymeric electrolyte solution of this invention as a conducting medium can be fabricated by injecting the polymeric electrolyte solution into a spiral wound cell or prismatic type cell. It can be also coated onto the surface of electrodes and assembled with a porous separator to fabricate single or multi-stacked cells that are packaged with plastic pouches. Similarly, the electrolyte of the present invention may be used in ultra capacitors (also known as super capacitors) and hybrid devices incorporating aspects of batteries and capacitors.

[0032] In situ tests: Type 2032 button cells were assembled for the evaluation of cell performance with a MAG-10 anode, and LiNi0.8Co0.15Al0.05O2 as a cathode. Celgard® 2500 (microporous polypropylene membrane, available from CELGARD Inc.) was used as a separator. These cells contained MAG-10 graphite, with 8 wt % PVDF binder/poly(siloxane-g-3 ethylene oxide), doping level of 32:1 with LiTFSI, electrolyte/LiNi0.8Co0.15Al0.05O2, 8 wt % PVDF, 4 wt % SFG-6 graphite, and 4 wt % carbon black. The effective cell area was 1.6 cm2. Charge and discharge rate were C/10. There was no degradation peak caused by the metal oxide up to 4.1V and the specific charge capacity was over 140 mAh/g.

[0033] FIG. 1 shows the effect of temperature on the ionic conductivity of poly(siloxane-g-3 ethylene oxide) electrolyte (see general formula III). Poly(siloxane-g-3 ethylene oxide) and Li(CF3SO2)2N were mixed with a doping level of 32:1. The ionic conductivity of the polymeric electrolytes at temperatures ranging from 25 to 70° C. were measured from the AC impedance curves from type 2030 button cells assembled by injecting the polymeric electrolyte between two stainless steel discs with a glass filter (750 micron thick) to prevent short circuits. The measuring frequency range was from 1 MHz to 10 Hz. 4

[0034] Poly(siloxane-g-3 ethylene oxide) electrolyte shows an excellent ionic conductivity of 8.6×10−4 S/cm at 37° C.

[0035] FIGS. 2 a and 2b show the electrochemical stability of poly(siloxane-g-3 ethylene oxide) and poly(siloxane-g-7 ethylene oxide) (see general formula IV) electrolytes, respectively. Poly(siloxane-g-ethylene oxides) and Li(CF3SO2)2N were mixed with a doping level of 32:1. The electrochemical stability window of the polymer electrolytes were determined by cyclic voltammetry with type 2030 button cells assembled by sandwiching a glass filter containing the polymer electrolyte between a stainless steel disc as a working electrode and a lithium metal disc as a combined counter and reference electrode. These polymeric electrolytes were found to show excellent electrochemical stability windows over 0 to 4.5V(vs. Li) and only a minimal decomposition peak around 4.5V during the first anodic sweep. In the case of poly(siloxane-g-7 ethylene oxide), which is more stable, the stability window reaches ca. 5.5V. 5

[0036] FIG. 3 is a trace of measured ionic conductivity vs. doping level at two different temperatures (24° C. and 60° C.). These data show the effect of doping level, O vs. Li+, on the ionic conductivity of poly(siloxane-g-3 ethylene oxide) electrolyte (see general formula III). A doping level of 32:1 is an optimum formulation regardless temperature. In the case of doping level of 15:1, there is an improvement of ionic conductivity at 60° C. owing to the additional dissociation of lithium cluster formed at 24° C. A high concentration of lithium salt generally creates clusters at lower temperature, but can be dissociated a bit by increasing temperature.

[0037] FIG. 4 shows the ionic conductivity of poly(siloxane-g-3 ethylene oxide) electrolyte with LiPF6 in place of LiTFSI at a doping level of 32:1. Even though LiPF6 has smaller anion than LiTFSI, the ionic conductivity values are similar to that shown in FIG. 1. This is due to the highly flexible structure of poly(siloxane-g-3 ethylene oxide). The highly flexible structure of the siloxane electrolyte of this invention can overcome the lack of plasticizing effect by the anion part of lithium salt. Poly(siloxane-g-3 ethylene oxide) has the additional advantage of increasing the variety of usable lithium salts over that of General formula (I) (as disclosed in the '062 patent), siloxane with alkyl carbon spacer between Si and polyethylene oxide. This comes from the fact that the rotation barrier of the Si—O bond is less than 0.2 kcal, but that of Si—CH3 is 1.6 kcal (see, C. F. Rome, Hydrocarbon Asia, May/June (2001) 42-49).

[0038] FIG. 5(a) shows thermal stability of poly(siloxane-g-3 ethylene oxide) electrolyte at a doping level of 32:1 with LiPF6, using accelerating rate calorimetry (“ARC”). A heat-wait-search sequence was applied. Sample weight for the test was 500 mg. Each sample was introduced in a 2¼″×¼″ diameter stainless steel bomb for the ARC test.

[0039] ARC is more sensitive test method than differential scanning calorimetry (“DSC”). In a heat-wait-search sequence, ARC will search an exothermic reaction for 30 minutes at every 5° C. change from the starting temperature. In DSC, a 5 or 10° C./min heating rate is usually used and the sample quantity is only about 2 to 5 μL. In the case of some chemicals, the exothermic peak by DSC comes later than ARC due to its much faster scan rate than ARC.

[0040] Although solid LiPF6 itself decomposes to PF5 and LiF at about 250° C., as measured by the DSC method, (see, N. Katayama et al., J. Power Sources, 2001, in press at time of application) and PF5 reacts with solvents for further thermal decomposition, poly(siloxane-g-3 ethylene oxide) electrolyte has an exothermic peak above 300° C. This means that poly(siloxane-g-3 ethylene oxide) has excellent chemical stability even at an elevated temperature.

[0041] FIG. 5 b shows comparative data from an ARC test of a widely used liquid electrolyte, 1.2M LiPF6 in ethylene carbonate (EC):ethyl methyl carbonate (EMC) (3:7 weight ratio). This sample was tested in the same way as in FIG. 5a. Its exothermic peak is detected before 200° C. (approximately, 220° C. of onset temperature by DSC; see, N. Katayama et al., J. Power Sources, 2001, in press at time of application). It is thus found that the siloxane main backbone of poly(siloxane-g-ethylene oxide) significantly enhances the thermal stability of the electrolyte.

[0042] FIG. 6 is a graph of the results of a flame tests (propagation rate) based on Underwriters Laboratories UL94 standard. Flammability of poly(siloxane-g-3 ethylene oxide) electrolyte, doping level of 32:1 with LiPF6, was investigated using modified UL-94HB Horizontal Burning Test. Detail compositions of the test samples are listed in Table 1.

	TABLE 1
	Composition	Other
EC:DEC	1 M LiPF6 in EC:DEC (1:1 by wt)
EC:EMC	1.2 M LiPF6 in EC:EMC (3:7 by wt)
EC:PC:EMC	1 M LiPF6 in EC:PC:EMC (3:3:4 by wt)
4PEGDME	Poly(ethylene glycol) dimethyl ether +	4 ethylene oxide
	LiPF6	O/Li+ = 20:1
PMHS3C	Poly(siloxane-g-3 ethylene oxide) +	O/Li+ = 32:1
	LiPF6

[0043] UL intends this standard to serve as a preliminary indication of the acceptability of materials for use as part of electronic goods, lithium batteries, etc. with respect to flammability. The modified UL-94HB test uses a ¼″×5.5″ silanized glass wool wick specimen soaked with the electrolyte samples held at one end in a horizontal position with marks at 1.00″ and 4.94″ from the free end. The specimen contains 5 g of electrolyte. A flame is applied to the free end for 30 seconds or until the flame front reaches the 1″ mark. If combustion continues the duration is timed between the 1.00″ mark and the 4.94″ mark. If combustion stops before the 4.94″ mark, the time of combustion and the damaged length between the two marks are recorded. A set of five specimens is tested. If two specimens from the set of five fail to comply, then a second set of five are tested. All five of this second set must comply. Propagation rate of flame is given by the following equation:

Propagation Rate=Distance (cm)/Elapsed time (min)

[0044] Poly(siloxane-g-3 ethylene oxide) electrolyte shows outstanding flame resistance. Its propagation rate is significantly lower than conventional liquid electrolyte for lithium ion batteries and low molecular weight polyethylene oxide electrolyte. This is because the inorganic siloxane backbone naturally acts as a combustion inhibitor.

[0045] It should be apparent that the present invention solves the long-felt need to create safe, high energy electrochemical storage devices having liquid electrolytes. Such devices promise to have high energy rate capabilities as well as high energy density. Batteries containing the present electrolyte, especially large batteries such as those used in electric vehicles, would be inherently safer than those with more volatile, flammable and unstable electrolytes.

[0046] Having described the present invention, it should be apparent to the reader that many variations of the present invention are possible without departure from the scope of the present invention. The specific implementations disclosed above are by way of example and for the purposes of enabling persons skilled in the art to implement the invention only. Accordingly, the invention is not to be limited except by the appended claims and legal equivalents.

Claims

1. A nonaqueous liquid type polymeric electrolyte comprising poly(siloxane-g-ethylene oxide) represented by general formula

2. The nonaqueous liquid type polymeric electrolyte of claim 1, wherein the average molecular weight of the poly(siloxane-g-ethylene oxide) does not exceed 20,000 g/mol.

3. The nonaqueous liquid type polymeric electrolyte of claim 1, wherein the dynamic viscosity of the poly(siloxane-g-ethylene oxide) does not exceed 10,000 cPs.

4. The nonaqueous liquid type polymeric electrolyte of claim 1, wherein the dynamic viscosity of the poly(siloxane-g-ethylene oxide) does not exceed about 2,000 cPs.

5. The nonaqueous liquid type polymeric electrolyte of claim 1, wherein the dynamic viscosity of the poly(siloxane-g-ethylene oxide) does not exceed 200 cPs.

6. The nonaqueous liquid type polymeric electrolyte of claim 1, wherein the alkali metal salt is a lithium salt.

7. The nonaqueous liquid type polymeric electrolyte of claim 1, wherein said dissolved a alkali metal salt comprises at least one quaternary ammonium salt having an anion selected from the following group: ClO4−, BF4−, AsF6−, PF6−, CF3SO3−, (CF3SO2)2N−, (CF3SO2)3C−, N(SO2C2F5)2)−, PF3(C2F5)3−, PF3(CF3)3− and B(C2O4)2.

8. The nonaqueous liquid type polymeric electrolyte of claim 1, wherein the lithium salt comprises LiClO4, LiBF4, LiAsF6, LiPF6, LiCF3SO3, Li(CF3SO2)2N, Li(CF3SO2)3C, LiN(SO2C2F5)2, LiPF3(C2F5)3, LiPF3(CF3)3, LiB(C2O4)2 or mixtures thereof.

9. The nonaqueous liquid type polymeric electrolyte of claim 1, wherein the lithium salt comprises lithium bis(chelato)borates having five to seven rings.

10. The nonaqueous liquid type polymeric electrolyte of claim 1, wherein said electrolyte is non-volatile.

10. The nonaqueous liquid type polymeric electrolyte of claim 1, wherein the oxygen versus lithium ratio is 5:1 to 50:1.

12. The nonaqueous liquid type polymeric electrolyte of claim 1, further characterized by having an ionic conductivity of at least 6×10−4 S/cm at room temperature and at least 8.4×10−4 S/cm at 37° C.

13. The nonaqueous liquid type polymeric electrolyte of claim 1, further characterized by having a viscosity of not more than about 1,000 cPs.

14. An electrochemical device comprising the nonaqueous liquid type polymeric electrolyte of claim 1.

15. The electrochemical device of claim 14 wherein said dissolved a alkali metal salt comprises at least one quaternary ammonium salt having an anion selected from the following group: ClO4−, BF4−, AsF6−, PF6−, CF3SO3−, (CF3SO2)2N−, (CF3SO2)3C−, N(SO2C2F5)2)−, PF3(C2F5)3−, PF3(CF3)3− and B(C2O4)2−.

16. The electrochemical device of claim 14 wherein said dissolved a alkali metal salt comprises lithium bis(chelato)borates having five to seven membered rings.

17. The electrochemical device of claim 15 or 16 where said electrochemical device comprises a secondary battery.

18. The secondary battery of claim 17 further comprising a lithium metal oxide or lithium metal phosphate positive electrode, at least one porous separator, and at least one lithium-carbon, lithium-alloy, or lithium metal negative electrode.

19. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises at least one lithium salt.

20. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises LiCF3SO3.

21. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises Li(CF3SO2)2N.

22. The secondary batter of claim 17 wherein said dissolved alkali metal salt comprises Li(CF3SO2)C.

23. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises LiN(SO2C2F5).

24. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises LiPF6.

25. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises LiAsF6.

26. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises LiBF4.

27. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises LiClO4.

28. The electrochemical device of claim 14 wherein said dissolved alkali metal salt includes at least one electrolyte salt from the following group: LiClO4, LiBF4, LiAsF6, LiPF6, LiCF3SO3, Li(CF3SO2)2N, Li(CF3SO2)3C, LiN(SO2C2F5)2), LiPF3(C2F5)3, LiPF3(CF3)3, LiB(C2O4)2.

29. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises LiPF3(C2F5)3.

30. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises LiPF3(CF3)3.

31. The secondary battery of claim 17 wherein said dissolved alkali metal salt comprises LiB(C2O4)2.

32. The electrochemical device of claim 14 comprising at least one capacitor.

33. The capacitor of claim 32 wherein said dissolved a alkali metal salt comprises at least one quaternary ammonium salt having an anion selected from the following group: ClO4−, BF4−, AsF6−, PF6−, CF3SO3−, (CF3SO2)2N−, (CF3SO2)3C−, N(SO2C2F5)2)−, PF3(C2F5)3−, PF3(CF3)3− and B(C2O4)2.−.

34. A nonaqueous liquid type polymeric electrolyte having an ionic conductivity of at least 6×10−4 S/cm at 25° C.

35. A nonaqueous liquid type polymeric electrolyte having an ionic conductivity of at least 8.4×10−4 S/cm at 37° C.

36. The nonaqueous liquid type polymeric electrolyte of claim 34 further characterized by having ionic conductivity of at least 8.4×10−4 S/cm at 37° C.

37. A lithium secondary battery containing the nonaqueous liquid type polymeric electrolyte of claim 34.

38. A capacitor containing the nonaqucous liquid type polymeric electrolyte of claim 34.

39. A lithium secondary battery containing the nonaqueous liquid type polymeric electrolyte of claim 35.

40. A capacitor containing the nonaqueous liquid type polymeric electrolyte of claim 35.

41. The nonaqueous liquid type polymeric electrolyte of claim 34 wherein said electrolyte is nonvolatile.

42. The nonaqueous liquid type polymeric electrolyte of claim 35 wherein said electrolyte is nonvolatile.

43. The nonaqueous liquid type polymeric electrolyte of claim 34 wherein said electrolyte is electrochemically stable over 4.5 V.

44. The nonaqueous liquid type polymeric electrolyte of claim 35 wherein said electrolyte is electrochemically stable over 4.5 V.

45. The nonaqueous liquid type polymeric electrolyte of claim 36 wherein said electrolyte is nonvolatile.

46. The nonaqueous liquid type polymeric electrolyte of claim 36 wherein said electrolyte is electrochemically stable over 4.5 V.