Patent Application
20170268126
The present application relates to nonlinear optical crystal material, method for preparation thereof, and application thereof, belonging to the technical field of nonlinear optical crystal material.
Infrared nonlinear optical crystal materials have a promising future in the field of civil use, scientific research and military, such as molecular spectrum, non-invasive medical diagnostic test, environmental monitoring, deep space exploration, space telescope, infrared laser radar, laser communication, opto-electrionic countermeasure, and the like. At present, mid-/far-infrared laser with wavelength of 2˜20 μm is obtained based on the principles of nonlinear optics and infrared nonlinear optical frequency conversion technology. Commercial mid-/far-infrared nonlinear optical crystals mainly contain AgGaS2, AgGaSe2, ZnGeP2, and the like. These crystals have been widely used in production, live, scientific research and military equipment, while these crystals have respective shortcomings, such as low laser damage threshold, difficult growth of large crystal, and their comprehensive performance could not meet increasing application demands.
With development of technology and increasing demands, it is of great significance and urgent to develop more infrared nonlinear optical crystals with more outstanding comprehensive performance. Therefore, the development and growth of new infrared nonlinear optical crystals is not only a challenge for the synthesis and growth of crystal materials, hut has important strategic significance in development of civilian high-tech industry and strengthening of national defense capability.
According to an aspect of the present application, a nonlinear optical crystal material is disclosed. The nonlinear optical crystal material has an excellent infrared nonlinear optical performance, whose frequency-doubling intensity can reach 9.3 times of AgGaS2 (abbreviated as AGS) with the same particle size, and it meets type-I phase matching. And the laser damage threshold of the nonlinear optical crystal material can reach 7.5 times of AgGaS2 with the same particle size. The nonlinear optical crystal material has important application value in the frequency-converters which can be used for frequency doubling, sum frequency, difference frequency, optical parametric oscillation of laser in mid-/far-infrared waveband, and the like.
Said nonlinear optical crystal material, whose molecular formula is
Ga2Se3
wherein the crystal structure of said nonlinear optical crystal material belongs to trigonal system, space group R3 with the lattice parameters of a=b=3˜4.2 Å, c=9˜10 Å, α=β=90°, γ=120° and Z=1. The valences of gallium and selenium are +3 and −2, respectively. A gallium atom connects with four selenium atoms to form a GaSe4 tetrahedron, and GaSe4 tetrahedral share corners to form three-dimensional network structure.
As a preferred embodiment, in the lattice parameters, a=b=3.8˜3.9 Å, c=9.4˜9.5 Å.
As a more preferred embodiment, in the lattice parameters, a=b=3.86 Å, c=9.44 Å.
According to another aspect of the present application, a method for preparing said nonlinear optical crystal material is disclosed, wherein after homogeneously mixing raw materials containing gallium, boron and selenium with a fluxing agent, said nonlinear optical crystal material is obtained using high temperature solid state method under a vacuum condition.
As a preferred embodiment, in said raw materials, the molar ratio of element gallium, element boron and element selenium is Ga:B:Se=2:2:3.
As an embodiment, said high temperature solid state method is that the mixture of the raw materials and the fluxing agent is kept in the temperature range from 700° C. to 1000° C. for no less than 24 hours.
As a preferred embodiment, said high temperature solid state method is that the mixture of the raw materials and the fluxing agent is kept in the temperature range from 800° C. to 1000° C. for no less than 24 hours. As a more preferred embodiment, said high temperature solid phase method is that the mixture of the raw materials and the fluxing agent is kept in the temperature range from 850° C. to 950° C. for a time range from 1 day to 3 days.
As a preferred embodiment, said high temperature solid state method is that the mixture of the raw materials and the fluxing agent is kept in the temperature range from 500° C. to 700° C. for no less than 1 hour, and then kept in the temperature range from 800° C. to 950° C. for no less than 24 hours.
As a preferred embodiment, said raw materials contain gallium oxide, elementary substance of boron and elementary substance of selenium.
As a preferred embodiment, said fluxing agent is at least one selected from alkali metal halides, alkali earth metal halides. As a more preferred embodiment, said fluxing agent is at least one selected from NaCl, KCl, RbCl, CsCl, NaBr, KBr, RbBr, CsBr, NaI, KI, RbI, CsI, MgCl2, BaCl2, MgBr2, BaBr2, MgI2, BaI2. As a further preferred embodiment, said fluxing agent is KBr and/or KI.
A skilled person in this art can select the usage amount of said fluxing agent according to actual demand. As a preferred embodiment, the mass ratio of said fluxing agent to said raw material is that fluxing agent:said raw material=1˜10:1. As a more preferred embodiment, the mass ratio of said fluxing agent to said raw material is that fluxing agent:said raw material=2˜5:1. As a further preferred embodiment, the mass ratio of said fluxing agent to said raw material is that fluxing agent:said raw material=3˜5:1.
According to another aspect of the present application, an infrared detector is disclosed, which contains any said nonlinear optical crystal material and/or the nonlinear optical crystal material prepared by any said method.
According to another aspect of the present application, an infrared laser is disclosed, which contains any said nonlinear optical crystal material and/or the nonlinear optical crystal material prepared by any said method.
The advantages of the present application include but not limit to:
(1) The present application provides a new nonlinear optical crystal material with an excellent infrared nonlinear optical performance. Its frequency-doubling intensity can reach 9.3 times of AgGaS2, and it meets type-I phase matching; and its laser damage threshold can reach 7.5 times of AgGaS2.
(2) The present application provides a method for preparing the nonlinear optical crystal material using high temperature solid state method with the presence of a fluxing agent. Due to simple steps, high yields, high purity and high crystallinity of the crystal material product, the method is suitable for large scale industrial production.
(3) The nonlinear optical crystal material provided in the present application is a polar crystal with an outstanding infrared nonlinear optical performance, which is expected to have an important application value in the frequency-converters which can be used for frequency doubling, sum frequency, difference frequency, optical parametric oscillation of laser in mid and far infrared waveband, and the like.
The present application will be further described by combining with Examples. It should be understand that these Examples are only used to illustrate the present application and not to limit the scope of the present application.
A mixture was obtained by homogeneously mixing a fluxing agent with raw materials comprising of Ga2O3, elementary substance of boron and elementary substance of selenium with the molar ratio of Ga2O3:B:Se=1:2:3. After being grinded homogeneously, the mixture was put into a quartz reactor tube; and then the quartz reactor tube was sealed by oxyhydrogen flame after being vacuumized to 10−2 Pa. And then the quartz reactor tube was put into a high temperature furnace to be heated to solid melting temperature, and then kept at the solid melting temperature for some time. And then after the temperature was reduced to 300° C. at a cooling rate of no more than 5° C./hour, stop heating and naturally cool to room temperature. After being washed by distilled water to remove the fluxing agents and being dried, the powder samples of nonlinear optical crystal material were obtained.
The sample numbers, the components of raw materials, the component and amount of the fluxing agents, solid melting temperatures and holding time at solid melting temperature are shown in Table 1.
The components of raw materials and the mass ratio of fluxing agent to the raw material are same as Sample 1# at Example 1. The mixture of the raw material and the fluxing agent was grinded to be homogeneous and put into a quartz reactor tube; and then the quartz reactor tube was sealed by oxyhydrogen flame after being vacuumized to 10−2 Pa. And then the quartz reactor tube was put into a high temperature furnace to be heated to 650° C.; after being kept at 650° C. for 5 hours, the temperature was heated to 950° C. for 24 hours. And then after the temperature was reduced to 300° C. at a cooling rate of no more than 5° C./hour, stop heating and naturally cool to room temperature. After being washed by distilled water to remove the fluxing agent KI and being dried, the single crystal sample of nonlinear optical crystal material was obtained and denoted as Sample 4#.
The X-ray powder diffraction (XRD) patterns of Samples 1# to 4# were measured using Rigaku MiniFlex II X-ray Diffractometer with Cu target, Kα radiation source (λ=0.154184 nm). The results indicated that Samples 1# to 4# all were with high purity and high crystallinity. The typical one was the XRD pattern of Sample 4#, which was shown in
The single crystal X-ray diffraction analysis of Sample 4# was performed using Rigaku Mercury CCD X-ray Diffractometer with Mo target, Kα radiation source (λ=0.07107 nm), operated at 293K. The crystal structure was resolved by Shelxt197.
Crystallographic Data of Sample 4# was shown in Table 2. The structures of asymmetric unit and the unit cell were shown at
aR1 = ||Fo| − |Fc||/|Fo|
bwR2 = [w(Fo2 − Fc2)2]/[w(Fo2)2]1/2.
The second order nonlinear effects of Samples 1# to 4# were measured on Kurtz-Perry System. The UV-Vis-NIR diffuse reflectance spectra were measured on Perkin-Elmer Lambda 950 Ultraviolet—visible—near infrared spectrometer. The infrared transmission spectra of Samples 1# to 4# were measured on Bruker Vertex 70 infrared spectrometer.
The results indicated that Samples 1# to 4# had the similar optical properties.
The frequency-doubling intensities of Samples 1# to 4# all were over 9.3 times of AgGaS2 with the same particle size, ranging from 200 μm to 300 μm. The laser damage thresholds of Samples 1# to 4# all were over 7.5 times of commercial material AgGaS2 with the same particle size, ranging from 75 μm to 150 μm.
As typical sample, the laser-damaged threshold comparison of Sample 1# with AgGaS2 was shown in Table 3.
As a representative sample, the curve of frequency-doubling intensity as a function of particle size for Sample 1# was shown in
As a representative sample, the light transmittance property of Sample 1# were shown in
The foregoing is only several examples and preferred embodiments of the present application, and is not any kind of limit to the scope of the present application. However, it can be conceived that other variations and modifications can be made without departing from the scope covered by the claims of the present application, and all of these variations and modifications fall into the scope of protection of the present application.