Patent Grant
11262640
Nonlinear optical (NLO) materials may be employed for applications including optical switching and power limitation as well as image processing and manipulation. NLO behavior is the behavior of light in nonlinear materials where the dielectric polarization has a nonlinear response to the electric field of light applied, for example, when the electric field may be of an interatomic strength. In the field of nonlinear optical materials, a solid-state laser of a specific wavelength may be about 1064 nm (infrared), as compared to visible light which is from roughly 400 nm (blue) to 700 nm (red). The term ‘solid-state laser’ is used, since what is being used to lase is a Nd:YAG (neodymium-doped yttrium aluminum garnet—a solid material). When this laser light hits a NLO material, the resulting laser light is half the wavelength, i.e. 1064 nm goes in and 532 nm (green) comes out. With proper optics and a NLO crystal, a 532 nm laser may be fabricated by starting with a 1064 nm laser. This fabrication is termed second-harmonic generation (SHG)—1064 nm/2=532 nm. If another NLO crystal is disposed in front of the 532 nm light, that radiation would be halved, i.e. 532 nm/2=266 nm, or 1064 nm/4=266 nm. This is termed fourth harmonic generation (FHG). It is appreciated that the order of the harmonic generation is based on the original wavelength of 1064 nm.
Conventionally, there are commercially available materials for lasers that will go from 1064 mn to 532 nm and from 1064 nm to 266 nm. For the latter, materials such as β-BaB2O4 (β-BBO) and CsLiB6O10 (CLBO) are available and used in commercially available lasers. β-BBO and CLBO are the NLO crystals conventionally employed for 266 nm lasers. For example, a laser at 177.3 nm would be a sixth harmonic generation (SxHG), or 1064/6=177.3 nm. The solid-state laser that could work at 177.3 nm can be employed in photolithography and other advanced technologies. Conventionally, there has been one material that has been shown to lase at 177.3 nm-KBe2BO3F2 (KBBF). However, KBBF has both manufacturing and application challenges issues. For example, (1) To synthesize KBBF, BeO must be employed, and BeO is highly toxic and may have restrictions on experimentation and use; (2) Even though KBBF was discovered in the late 1990's, the largest crystal grown to date is 4 mm due to the layered structure of the material; and (3) KBBF was discovered overseas and exports of the material have been constrained or halted because of its technological applications. Previously, Sr2Be2B2O7 (SBBO) was designed and synthesized, [Be2B2O7]∞ double-layers are observed that do impart some stability, however, toxic BeO is still required in the synthesis and large single crystals have yet to be grown. In addition, β-BBO has a very high intrinsic birefringence that results in a large walk-off NLO effect that reduces the nonlinear optical properties of the material. CLBO is hygroscopic, i.e. the crystal must be kept rigorously dry or else the optical properties will deteriorate. Once a crystal of CLBO gets wet, it is no longer usable as a nonlinear optical material. If the CLBO crystal gets wet (humid air will do this) it is no longer usable as an NLO material.
Thus, an ongoing need exists for novel nonlinear optical materials and devices comprising same.
Aspects described herein comprise a combination of features and characteristics intended to address various shortcomings associated with certain prior devices, compositions, systems, and methods. The various features and characteristics described above, as well as others, will be readily apparent to those of ordinary skill in the art upon reading the following detailed description, and by referring to the accompanying drawings.
Disclosed herein is a device comprising a nonlinear optical (NLO) material according to the formula XLi2Al4B6O20F.
Also disclosed herein is a device comprising a nonlinear optical material (NLO) according to the formula KSrCO3F, wherein the NLO comprises at least one single crystal.
Also disclosed herein is a nonlinear optical material selected from the group consisting of KSrCO3F Rb3Ba3Li2Al4B6O20F and K3Sr3Li2Al4B6O20F.
The following discussion is directed to various exemplary aspects. However, one of ordinary skill in the art will understand that the examples disclosed herein have broad application, and that the discussion of any aspect is meant only to be exemplary of that aspect, and not intended to suggest that the scope of the disclosure, including the claims, is limited to that aspect.
The drawing figures are not necessarily to scale. Certain features and components herein may be shown exaggerated in scale or in somewhat schematic form and some details of conventional elements may not be shown in interest of clarity and conciseness.
In the following discussion and in the claims, the terms “including” and “comprising” are used in an open-ended fashion, and thus should be interpreted to mean “including, but not limited to . . . .”
A “laser damage threshold” is a term used herein to define a peak fluency of laser irradiation at which irreversible changes in a material's structure may occur. This laser damage threshold may be defined as the highest quantity of laser radiation that a material may absorb before there are changes to the material's optical properties. This may also be defined by the ISO standards 21254-1, 2, 3, and 4 definitions as the highest quantity of laser radiation incident upon the optical component for which the extrapolated probability of damage is zero where the quantity of laser radiation may be expressed as power density, linear power density or energy density.
“Anisotropy” is the term used to define properties/characteristics of material that may vary depending upon the direction in which the properties/characteristics are observed/measured.
“Birefringence,” which may be referred to as “double refraction,” is an optical material property where a light passing through a crystal is split into two unequal wavelengths, which then each pass through the crystal at different respective speeds. Birefringence is exhibited in optically anisotropic crystals.
“Non-centrosymmetric” is a term used to describe the symmetry (or lack thereof) of certain crystal structures. Non-centrosymmetric materials are materials where point groups lack an inversion center, in contrast to centrosymmetric structures and materials which comprise a unit cell (e.g., face-centered-cubic, “fcc”) that has a center of symmetry at, for example, (0,0,0). In this example, the inversion centers may be observed at atom sites such as the atom at (0, 0, ½), which would invert to the atom at (0, 0, −½), and the atom at (½, ½, 0) inverts to (−½, −½, 0). While an fcc structure comprises an inversion center at every atom, a structure may be characterized as centrosymmetric if it comprises at least one inversion center and may be characterized as non-centrosymmetric if it does not comprise any inversion centers.
“Band gap” is the characteristic of a material, such as an optical material, that is associated with the minimum energy needed to move an electron from a bound state (valence band) into a free state (conduction band). Varying energy band structures in semiconductors are associated with the electrical (including thermoelectric) properties exhibited by these semiconductors.
Disclosed herein are NLO materials and methods of making and using same. NLO materials are of intense interest owing to their ability to control and manipulate light for the generation of coherent radiation at a variety of difficult to access wavelengths. They have efficiently expanded the spectral ranges of solid state lasers from ultraviolet (UV) to infrared (IR). Accessing directly the deep-ultraviolet (DUV) region (150 nm-400 nm), however, is especially challenging, yet desirable for a number of advanced optical technologies, including photolithography for microelectronics and attosecond pulse generation for electron dynamic studies in matter.
In an aspect the NLOs of the present disclosure exhibit at least one of the following desirable characteristics: i) a noncentrosymmetric (NCS) crystal structure; ii) large SHG coefficient (dij>0.39 pm/V); iii) wide band gap (Eg>6.2 eV), i.e. an absorption edge <200 nm; iv) moderate birefringence at 1064 nm (dn˜0.05-0.09); v) chemical stability with a large laser damage threshold (LDT >5.0 gigawatts per cm2 or GW/cm2), and vi) easy growth of large—centimeter size—high quality single crystals.
In yet another aspect, NLOs of the present disclosure exhibit at least two, alternatively at least three or alternatively at least four of the following desirable characteristics: i) a noncentrosymmetric (NCS) crystal structure; ii) large SHG coefficient (dij>0.39 pm/V); iii) wide band gap (Eg>6.2 eV), i.e. an absorption edge <200 nm; iv) moderate birefringence at 1064 nm (dn˜0.05-0.09); v) chemical stability with a large laser damage threshold (LDT >5.0 GW/cm2), and vi) easy growth of large—centimeter size—high quality single crystals.
In some aspects, the NLO materials of the present disclosure are used in UV and/or DUV applications and exhibit the following characteristics: i) a noncentrosymmetric (NCS) crystal structure; ii) large SHG coefficient (dij>0.39 pm/V); iii) wide band gap (Eg>6.2 V), i.e. an absorption edge <200 nm; iv) moderate birefringence at 1064 nm (dn˜0.05-0.09); v) chemical stability with a large laser damage threshold (LDT >5.0 GW/cm2), and vi) easy growth of large—centimeter size—high quality single crystals.
In an aspect, the systems and methods disclosed herein produce NLO materials that have a small walk-off effect and are not hygroscopic. Herein the term “walk-off effect” refers to a material having too large a birefringence (Δn>0.11) resulting in a reduction in the intensity of the second-harmonic beam and the birefringence may be determined through refractive index measurements. An NLO material of the type disclosed herein may be characterized by a walk-off of from about 1 mrad to about 200 mrad, alternatively from about 10 mrad to about 65 mrad or alternatively from about 15 mrad to about 32 mrad. In an aspect, the NLO materials of the present disclosure comprise KSrCO3F, K3Sr3Li2Al4B6O20F or Rb3Ba3Li2Al4B6O20F, each of which are characterized by the presence of usable band gaps and birefringence.
In an aspect, the NLO materials of the present disclosure comprise KSrCO3F, K3Sr3Li2Al4B6O20F or Rb3Ba3Li2Al4B6O20F which display (i) moderate birefringence (i.e. ˜0.06) (ii) no walk-off issues (iii) are non-hygroscopic and (iv) form large, high quality single crystals. As will be understood by the ordinarily skilled artisans, large crystals are useful for technological NLO applications, and, as used herein, a “large” crystal is one that is commercially viable, in some aspects, a crystal suitable for use in the present disclosure has a minimum diameter of about 2 mm in at least two directions (e.g., the smallest dimension that is not a thickness is greater than 2 mm), alternative from about 2 mm to about 20 mm alternatively from about 3 mm to about 15 mm or alternatively from about 5 mm to about 10 mm.
In an aspect, the NLO materials of the present disclosure may form high quality crystals wherein the term “high quality” as used herein refers to a crystal that is optically clear and exhibits a full-width half-maximum (FWHM) of a Bragg reflection of <100″ (arc seconds). In an aspect, the NLO materials of the present disclosure form high quality single crystals with minimum diameters in the ranges disclosed herein.
In an aspect, a NLO of the present disclosure has the general formula XLi2Al4B6O20F wherein X comprises potassium (K) and strontium (Sr), alternatively X comprises K3Sr3. In an aspect, X comprises rubidium (Rb) and barium (Ba), alternatively, X comprises Rb3Ba3.
Disclosed herein are single crystals and methods of growing large (multi-mm) single crystals of KSrCO3F, a nonlinear optical material that can generate 266 nm radiation. As noted, crystals of KSrCO3F do not suffer from walk-off issues and are not hygroscopic. It is to be appreciated that as the generation of 266 nm radiation through second-harmonic generation occurs by using large single crystals, powders would not be desirable for this purpose.
In an aspect, an NLO of the present disclosure comprises a crystal of KSrCO3F. A crystal of KSrCO3F may be grown using any suitable methodology (e.g., top-seeded solution growth method) using KF—Li2CO3 as a flux with SrCO3 The components used to prepare the NLO were used in amounts that provided a ratio of 7:10:3—SrCO3:KF:Li2CO3 in the reaction mixture which was then heated to a temperature in the range of from about 600° C. to about 700° C. alternatively from about 615° C. to about 675° C. or alternatively from about 625° C. to about 650° C. at a heating rate of from about 25° C./hour to about 100° C./hour for a time period of from about 12 hours to about 48 hours or alternatively from about 18 hours to about 36 hours. In some aspects, NLO materials of the present disclosure may be present in amounts to provide ratios of SrCO3:KF:Li2CO3 of from about 1 to about 10: from about 5 to about 15: from about 1 to about 10 in the reaction mixture.
In an aspect, the NLO materials disclosed herein may be used as a material for converting the wavelength of laser light. In other aspects, the NLO materials disclosed herein may be components of a device such as a laser. It should, however, be noted that the use of the NLO materials of the present disclosure is by no means limited to wavelength converting devices and it can be applied to any devices that utilize the nonlinear optical effect. Other devices than wavelength converters with which the nonlinear optical material of the present invention can be used include optical bistable devices (e.g. optical memory devices, light pulse waveform control devices, photolimiters, differential amplifiers, phototransistors, A/D converters, optical logic devices, photomultivibrators and optical flip-flop circuits), optical modulators and phase conjugated optical devices.
The disclosure having been generally described, the following examples are given as particular aspects of the disclosure and to demonstrate the practice and advantages thereof. It is understood that the examples are given by way of illustration and are not intended to limit the specification of the claims to follow in any manner.
Fabrication and Characterization of LiAlBOF-Based NLO Materials
A plurality of single crystals of K3Sr3Li2Al4B6O20F was grown from a high temperature solution using the flux. The K3Sr3Li2Al4B6O20F crystal was grown by combining a mixture of SrCO3 (0.03 mol, 4.420 g), K2CO3 (0.01-0.03 mol, 1.38-4.1463 g), Li2CO3 (0.01-0.05 mol, 0.0738-3.69 g), LiF (0.01-0.05 mol, 0.259-1.295 g), H3BO3 (0.1-0.3 mol, 6.183-18.549 g) and Al2O3 (0.04 mol, 4.078 g). The mixture was melt at 850° C. and held at this temperature for 20 h to form a homogeneous melt. The melt quickly cooled down to 750-700° C., a platinum wire was promptly dipped into melt. The temperature was further decreased to 700-650° C. at a rate of 5° C./d, then the platinum wire was pulled out of the melt and allowed to cool to room temperature at a rate of 20° C./h. Colorless, transparent crystals were grow in in this manner. Thus, a Be-free deep-ultraviolet nonlinear optical material K3Sr3Li2Al4B6O20F has been successfully synthesized herein. K3Sr3Li2Al4B6O20F possess a short cut-off edge, ˜190 nm, and the SHG responses are 1.7×KH2PO4 and 0.3×β-BaB2O4 at 1064 and 532 nm incident radiation, respectively. The refractive indices measurement reveals a suitable birefringence of 0.0616 at 532 nm.
Reagents. SrCO3 and K2CO3 (Alfa Aesar, 99.0%), Li2CO3, LiF and H3BO3 (Alfa Aesar, 99.5%), and Al2O3 (Alfa Aesar, 99.99%) were used as starting materials.
Powder X-ray Diffraction (PXRD). The purity of the samples was confirmed by powder x-ray diffraction (PXRD). PXRD was performed on a PANalytical X'Pert PRO diffractometer equipped with a diffracted-beamed monochromatic set for Cu Kα (λ=1.54056 Å) radiation. The scanning step width was 0.02° and a fixed counting time is 1 s/step from 10° to 70° in 2θ.
Crystal Growth. The crystals of K3Sr3Li2Al4B6O20F were grown from a high temperature solution using the flux. The K3Sr3Li2Al4B6O20F crystal was grown by combining a mixture of SrCO3 (0.03 mol, 4.420 g), K2CO3 (0.015 mol, 2.073 g), Li2CO3 (0.025 mol, 1.845 g), LiF (0.02 mol, 0.518 g), H3BO3 (0.1 mol, 6.183 g) and Al2O3 (0.01 mol, 1.01 g). The mixture was melt at 850° C. and held at this temperature for 20 h to form a homogeneous solution. The solution quickly cooled down to 750° C., a platinum wire was promptly dipped into solution. The temperature was further decreased to 700° C. at a rate of 5° C./d, then the platinum wire was pulled out of the solution and allowed to cool to room temperature at a rate of 20° C./h. Colorless, transparent crystals that used for the seed crystal had crystallized on the platinum wire.
In another example, a plurality of large single crystals were grown by TSSG method by the Li2O—SrF2—B2O3 flux. The K3Sr3Li2Al4B6O20F crystal was grown by combining a mixture of SrCO3 (0.2 mol, 29.46 g), K2CO3 (0.075 mol, 10.37 g), Li2CO3 (0.125 mol, 9.24 g), LiF (0.1 mol, 2.59 g), H3BO3 (0.35 mol, 21.64 g) and Al2O3 (0.05 mol, 5.05 g). The mixture was melted at 850° C. and held at this temperature for 24 h to form a homogeneous solution. The solution was cooled down to 750° C. at a rate of 20° C./h. The Pt wire was dipped into the solution for 30 minutes to determine the saturation temperature. A saturation temperature of 720° C. was determined by introducing a K3Sr3Li2Al4B6O20F seed crystal to the solution and holding it for 48 h. During this time the seed crystal did not grow or dissolve, and no additional crystals were formed. A K3Sr3Li2Al4B6O20F seed crystal was introduced into the solution at 725° C. and held for 2 h that allowed the seed crystal surface to solution. The solution was cooled to the saturation temperature, 720° C., over 1 h. A large K3Sr3Li2Al4B6O20F crystal was gown by cooling the solution at a rate of 0.2° C./d to 716° C. and the seed crystal rotates at 10 rpm that controls by a Crystal growth Furnace Lifting Structure. The crystal was pulled out of solution and cooled at a rate of 10° C./h to room temperature. The total time for crystal growth was 27 d.
Single-crystal X-ray diffraction. A colorless block crystal (0.146×0.103×0.081 mm3) was selected for single-crystal diffraction analysis. Data were collected on a Bruker platform diffractometer equipped with a 4K CCD APEX II detector equipped with a diffracted-beamed graphite monochromatic set for Mo Kα radiation. For each sample, a hemisphere of data (3061 frames at 6 cm detector distance) was collected by a narrow-frame algorithm. The scan width was 0.30° in omega and the exposure time was 30 s per frame. The data including diffraction intensity, cell refinement and other related parameters were integrated using Bruker SAINT program. An empirical absorption correction was applied on the entire diffraction data. The crystal structure was solved by direct methods by the SHELXS-97 program and refined with the final least-squares program SHELXL. The PLATON program was used to check the structure, and no other higher symmetry was found. Relevant crystallographic data, selected bond distances and angles, atomic coordinates and equivalent isotropic displacement parameters for K3Sr3Li2Al4B6O20F are listed in Tables 1 and 2.
[a] R1 = Σ||Fo| − |Fc||/Σ|Fo| and wR2 = [Σw(Fo2 − Fc2)2/Σw Fo4]1/2 for Fo2 > 2σ(Fo2)
Table 2 shows the Atomic coordinates (×104) and equivalent isotropic displacement parameters (A2×103) for Li2K3Sr3Al4B6O20F as well as the bond valence sum (BVS) and the U(eq), which is defined as one third of the trace of the orthogonalized Uij tensor.
Thermal Analysis. Thermogravimetric analysis was performed on an EXSTAR TG/DTA 6300 instrument. Approximately 23 mg of K3Sr3Li2Al4B6O20F were placed in a platinum pan and heated at a rate of 10° C./min from room temperature to 1200° C. under flowing N2.
Powder SHG Measurement. Powder SHG measurements were performed on a modified Kurtz-NLO system using a pulsed Nd:YAG laser (Quantel Laser, Ultra 50) with a wavelength of 1064 and 532 nm. As the powder SHG response has been shown to strongly depend on particle size, the K3Sr3Li2Al4B6O20F sample was ground and sieved into distinct particle size ranges (<20, 20-45, 45-63, 63-75, 75-90, 90-125, 125-150 μm) to investigate its phase-matching behavior. Polycrystalline KH2PO4 (KDP) and β-BaB2O4 (β-BBO) were also sieved into similar particle sizes for SHG response comparison.
Optical Spectra Measurement.
Refractive Index Measurement. The refractive indices of K3Sr3Li2Al4B6O20F were determined using a Metricon Model 2010/M prism coupler (Metricon Co.) at five different wavelengths: 450.2, 532, 636.5, 829.3, and 1062.6 nm. A (001) wafer was polished by the Unipol-300 grinding/polishing machine (MTI Co.) for the measurement.
Table 3 shows the bond lengths [A] and angles [deg] for Li2K3Sr3Al4B6O20F.
Symmetry transformations used to generate equivalent atoms for Table 3: #1 −x+y,−x+1,z; #2 −y+1,x−y+1,z; #3 y−4/3,x+⅓,−z+4/3; #4 x,y−1,z; #5 y−⅓,x+⅓,−z+4/3; #6 x−y+⅔,−y+4/3,−z+4/3; #7 −x+y−1,−x,z; #8 −x−⅓,−x+y−⅔,−z+4/3; #9 x−y+1,−y+2,−z+1; #10 y,x+1,−z+1; #11 −x,−x+y,−z+1; #12 −y+1,x−y+2,z; #13 −x+y−1,−x+1,z; #14 −y,x−y+1,z; #15 x,y+1,z #16 x−1,y−1,z; #17 y−⅓,x+4/3,−z+4/3.
Three structural features are evident in K3Sr3Li2Al4B6O20F. First, the BO3 groups exhibit a coplanar configuration that favors a large (dij>0.39 pm/V) SHG response and moderate birefringence (e.g., dn=0.05-0.09). Second, the oxygen atoms on the BO3 groups are fully bonded, i.e. there are no dangling oxygen bonds, and, thus, a short absorption edge is observed. Third, the remaining Al—O and Li—F bonds connect the [LiAl2B3O6]∞ layer to create the double layers that generate stability and facilitate crystal growth. Before delving into the crystal growth and associated properties, a discussion on the powder SHG efficiency, thermal and moisture stabilities is desirable.
Addressing the layering tendency of NLO KBe2BO3F2 (KBBF) and Sr2Be2B2O7 (SBBO), large crystals of K3Sr3Li2Al4B6O20F were fabricated. The NLO active material exhibits an absorption edge of 190 nm, and is SHG active at 1064 nm and 532 nm. Large single crystals were grown using the top-seeded solution growth method. Optical measurements on these crystals revealed a moderate birefringence of 0.0574 at 1064 nm. Calculations indicate a Type I phase-matching wavelength behavior for fundamental (second-harmonic) radiation between 448-4970 nm (224-2485 nm) indicating that K3Sr3Li2Al4B6O20F is a viable material to generate 266 nm by FHG.
Rb3Ba3Li2Al4B6O20F crystals were grown by the top seed solution growth (TSSG) method according to certain aspects of the present disclosure. Some small Rb3Ba3Li2Al4B6O20F crystals with regular shape were picked from the crystals obtained by the above method and were used as seed crystals. And then a clear and homogeneous solution was prepared by using the same program as given above. A relatively large seed was attached to the platinum rod and was soaked in the solution. By observing the growth or dissolution of the seed, a saturation temperature of 712° C. was determined. Then a high quality Rb3Ba3Li2Al4B6O20F seed was dipped into the surface of the solution at 10° C. higher than the saturation temperature. This was followed by decreasing the temperature to the saturation point over 40 min. From this temperature, the solution was cooled at a rate of 0.25° C. per day. After the desired crystal size was obtained, the Rb3Ba3Li2Al4B6O20F crystal was pulled out of the solution and cooled to room temperature at a rate of 10° C./h.
A crystal of KSrCO3F was grown by the top-seeded solution growth method using KF—Li2CO3 as a flux. KF, SrCO3, and Li2CO3 with a molar ratio 10:7:3 were placed in an alumina crucible, heated to 630° C. at a heating rate of 100° C./h and held for 50 h in order to form a homogenous melt. Crystals of KSrCO3F were first grown by spontaneous crystallization, i.e. crystals formed on an alumina rod dipped into the melt. Seed crystals were selected from these spontaneously grown crystals. A crystallization temperature of 611° C. was determined by observing the growth or dissolution of the seed crystals when dipped into the melt. An oriented seed crystal was introduced into the melt at a rotation rate of 5 rpm at 2° C. higher than the crystallization temperature of 611° C. in order to reduce surface defects of the seed. The temperature was decreased to the crystallization temperature at a cooling rate of 0.5° C./min. From the crystallization temperature, the melt was cooled at a rate of 0.5° C. per day to 590° C. When the crystal growth process was done, i.e. by observing the gap between the growing crystal and the crucible wall (when the crystal edge is very close to the crucible wall the crystal growth is considered completed), the crystal was pulled from the melt and cooled (20° C./h) to room temperature. In the above manner, high quality and large single crystals of KSrCO3F can be grown for nonlinear optical applications.
Synthesis. Polycrystalline Rb3Ba3Li2Al4B6O20F was synthesized by conventional solid-state methods. Stoichiometric amount of Rb2CO3 (Alfa Aesar, 99%), BaCO3 (Alfa Aesar, 99.8%) and BaF2 (Alfa Aesar, 99%) Li2CO3 (Alfa Aesar, 99.0%), Al2O3 (Alfa Aesar, 99.997%), H3BO3 (Alfa Aesar, 99.8%) were ground thoroughly and pressed into pellet. The pellet was placed on a platinum plate and heated to 300° C. for 20 h to decompose carbonates and H3BO3, and then the temperature was raised to 630° C., held for 5 days, with several intermittent grindings. Laboratory powder x-ray diffraction indicated pure Rb3Ba3Li2Al4B6O20F was obtained,
Crystal Growth. The centimeter-size Rb3Ba3Li2Al4B6O20F crystal was grown by TSSG method with Li2O—BaF2—B2O3. The seed was obtained by recrystallize the Stoichiometric amount of Rb3Ba3Li2Al4B6O20F melts. Then a clear and homogeneous solution was prepared by using melt Rb3Ba3Li2Al4B6O20F and flux at molar ratio Rb3Ba3Li2Al4B6O20F:Li2O:BaF2:B2O3=1:4:3:5 at 750° C. for 10 h. A relatively large seed was attached to the platinum rod and was soaked in the solution. By observing the growth or dissolution of the seed, a saturation temperature of 712° C. was determined. Then a high quality Rb3Ba3Li2Al4B6O20F seed was dipped into the surface of the solution at 10° C. higher than the saturation temperature. This was followed by decreasing the temperature to the saturation point over 40 min. From this temperature, the solution was cooled at a rate of 0.25° C. per day. After the desired crystal size was obtained, the Rb3Ba3Li2Al4B6O20F crystal was pulled out of the solution and cooled to room temperature at a rate of 10° C./h.
Structural characterization: Single X-ray diffraction data with 3061 frames at 6 cm detector distance was collected on a Bruker SMART APEX2 diffractometer equipped with a 4K CCD area detector using graphite-monochromated Mo-Kα radiation (λ=0.71073 Å). Data were integrated using the Bruker SAINT program. Absorption corrections based on the multiscan technique were applied. The structure was solved by direct methods using SHELXS-97. All atoms were refined using full matrix least-squares techniques, final least-squares refinement is on Fo2 with data having Fo2≥2α (Fo2). The structure was checked with PLATON and no higher symmetry was found.
Infrared Spectroscopy. The Fourier transform infrared spectroscopy (FTIR) spectra in the 400-4000 cm−1 range were recorded on a Bruker Tensor 37 FTIR (see
Thermal analysis: The thermal property of Rb3Ba3Li2Al4B6O20F was measured on EXSTAR TG/DTA 6300 instrument under flowing nitrogen gas, heated from room temperature to 1100° C. at a rate of 10° C. min−1 in a platinum crucible (see
(Vacuum) UV-vis-NIR diffuse reflectance spectra: The UV-vis-NIR diffuse reflectance spectrum was measured at room temperature with a Cary 5000 UV-vis-NIR spectrophotometer in the 200-2500 nm wavelength range (see
SHG Measurement. Powder SHG were measured by using the Kurtz-Perry method with Q-switched Nd:YAG lasers at the wavelength of 1064 nm and 532 nm.[33] Polycrystalline samples of Rb3Ba3Li2Al4B6O20F and KH2PO4 (KDP) were ground and sieved into distinct particle size ranges (<20, 20-45, 45-63, 63-75, 75-90, 90-125, >125 μm). Sieved KDP powder was used as a reference. The intensity of the frequency-doubled output emitted from the sample was measured using a photomultiplier tube.
Refractive Index Measurements: A (100) wafer of Rb3Ba3Li2Al4B6O20F with size of 7×6×1 mm3 was polished using a Unipol-300 grinding/polishing machine (MTI Co.) for the refractive index measurements. The measurements were carried out using a Metricon Model 2010/M prism coupler (Metricon Co.) at 450.2, 532, 636.5, 829.3, and 1062.6 nm.
Laser Damage Threshold Measurement. The measurement was carried out on an Nd:YAG nanosecond laser (Model: Minilite II, Continuum Eletro-Optics, Inc.) at a wavelength of 1064 nm. The laser pulse duration was set at 6 ns, and the frequency was fixed at 15 Hz. The laser beam was focused with a convex lens, resulting in a beam diameter of 0.36 mm.
The structure of Rb3Ba3Li2Al4B6O20F is illustrated broken out into
The structure of Rb3Ba3Li2Al4B6O20F was determined by single X-ray diffraction and is illustrated in Table 6 below.
[a]R1 = Σ||Fo| − |Fc||/Σ|Fo| and wR2 = [Σw(Fo2 − Fc2)2/Σw Fo4]1/2 for Fo2 > 2σ(Fo2)
Table 7 lists atomic coordinates (×104) and equivalent isotropic displacement parameters (Å2×103) for Rb3Ba3Li2Al4B6O20F. Ueq is defined as one-third of the trace of the orthogonalized Uij tensor.
As shown in at least
Further, the refractive index of Rb3Ba3Li2Al4B6O20F is also measured by the prism coupling method. The measured no and ne at different wavelengths—450.2, 532, 636.5, 829.3, and 1062.6 nm are listed in Table 8.
Symmetry transformations used to generate equivalent atoms for Table 3: #1 −y+2,x−y+1,z #2 x−y+1,−y+2,−z #3 −x+1,−x+y,−z #4 −x+y,−x+1,z #5 y,x,−z, #6 x−y,−y+1,−z #7 x,y,−z+½ #8 −y+2,x−y+1,−z+½ #9 −x+y+1,−x+1,−z+½ #10 −x+y,−x+1,−z+½ #11 x,y−1,z #12 −y+1,x−y,z #13 −x+y+1,−x+1,z #14 −y+1,x−y+1,z #15 −x+y+1,−x+2,z #16 −x+y+1,−x+2,−z+½ #17 x,y+1,z.
Based on the measurement, the following Sellmeier equations for Rb3Ba3Li2Al4B6O20F, i.e. the refractive indices, no(λ) and ne(λ) as a function of wavelength λ were fitted by the least-squares method.
The experimental and calculated refractive indices are in agreement, as shown in
In addition, the laser damage threshold measurement at 1064 nm with 6 ns pulse width shows Rb3Ba3Li2Al4B6O20F has a damage threshold larger than 1 GW/cm2, which is comparable with commercialized NLO crystals.
In conclusion, based on crystal structural engineering design, a new deep-UV NLO material Rb3Ba3Li2Al4B6O20F has been successfully designed and synthesized. This compound retains the structural priority of KBBF and SBBO, but the structure features a 3D framework, which make Rb3Ba3Li2Al4B6O20F thoroughly resolve the layer habit and structural instability issues in KBBF and SBBO. Meanwhile, Rb3Ba3Li2Al4B6O20F exhibits excellent NLO properties, including relatively large SHG response, ˜1.5×KDP and 0.3×β-BBO at 532 nm and 266 nm, respectively, the short UV cut-off edge, and the suitable birefringence may be about at least 0.06. In addition, this compound melts congruently and high quality of single crystal with size of 12×8×7.6 mm3 was grown.
Table 9 illustrates wavelengths and refractive indexes for Rb3Ba3Li2Al4B6O20F fabricated according to certain aspects of the present disclosure.
The following enumerated aspects are provided as non-limiting examples
A first aspect which is a device comprising a nonlinear optical (NLO) material according to the formula XLi2Al4B6O20F.
A second aspect which is the device of the first aspect, wherein X comprises potassium (K) and strontium (Sr).
A third aspect which is the device of the first aspect, wherein X comprises K3Sr3.
A fourth aspect which is the device of the first aspect, wherein X comprises rubidium (Rb) and barium (Ba).
A fifth aspect which is the device of the first aspect, wherein X comprises Rb3Ba3.
A sixth aspect which is the device of any of the first through fifth aspects, wherein the NLO exhibits a walkoff of from about 1 mrad to about 200 mrad.
A seventh aspect which is the device of any of the first through sixth aspects, wherein the NLO forms single crystals with a minimum diameter of from about 2 mm to about 20 mm in at least two directions.
An eighth aspect which is the device of any of the first through seventh aspects, wherein the NLO exhibits a second harmonic generation coefficient of greater than 0.39 pm/V.
A ninth aspect which is the device of any of the first through eighth aspects, wherein the NLO exhibits a band gap of greater than 6.2 eV.
A tenth aspect which is the device of any of the first through ninth aspects, wherein the NLO exhibits an adsorption edge of less than 200 nm.
An eleventh aspect which is the device of any of the first through tenth aspects, wherein the NLO exhibits a laser damage threshold of greater than 5.0 GW/cm2.
A twelfth aspect which is the device of any of the first through eleventh aspects, wherein the NLO exhibits a birefringence at 1064 nm ranging from about 0.05 to about 0.09.
A thirteenth aspect which is a device comprising a nonlinear optical material (NLO) according to the formula KSrCO3F, wherein the NLO comprises at least one single crystal.
A fourteenth aspect which is the device of the thirteenth aspect, wherein the NLO exhibits a walkoff of from about 1 mrad to about 200 mrad.
A fifteenth aspect which is the device of any of the thirteenth through fourteenth aspects, wherein the NLO forms single crystals with a minimum diameter of from about 2 mm to about 20 mm in at least two directions.
A sixteenth aspect which is the device of any of the thirteenth through fifteenth aspects, wherein the NLO exhibits a second harmonic generation coefficient of greater than 0.39 pm/V.
A seventeenth aspect which is the device of any of the thirteenth through sixteenth aspects, wherein the NLO exhibits a band gap of greater than 6.2 eV.
An eighteenth aspect which is the device of any of the thirteenth through seventeenth aspects, wherein the NLO exhibits an adsorption edge of less than 200 nm.
A nineteenth aspect which is the device of any of the thirteenth through eighteenth aspects, wherein the NLO exhibits a laser damage threshold of greater than 5.0 GW/cm2.
A twentieth aspect which is the device of any of the thirteenth through nineteenth aspects, wherein the NLO exhibits a birefringence at 1064 nm ranging from about 0.05 to about 0.09.
A twenty-first aspect which is a nonlinear optical material selected from the group consisting of KSrCO3F Rb3Ba3Li2Al4B6O20F and K3Sr3Li2Al4B6O20F.
A twenty-second aspect which is a device comprising the nonlinear optical material of the twenty-first aspect.
Exemplary aspects are disclosed and variations, combinations, and/or modifications of the aspect(s) and/or features of the aspect(s) made by a person having ordinary skill in the art are within the scope of the disclosure. Alternative aspects that result from combining, integrating, and/or omitting features of the aspect(s) are also within the scope of the disclosure. Where numerical ranges or limitations are expressly stated, such express ranges or limitations should be understood to include iterative ranges or limitations of like magnitude falling within the expressly stated ranges or limitations (e.g., from about 1 to about 10 includes, 2, 3, 4, etc.; greater than 0.10 includes 0.11, 0.12, 0.13, etc.). For example, whenever a numerical range with a lower limit, Rl, and an upper limit, Ru, is disclosed, any number falling within the range is specifically disclosed. In particular, the following numbers within the range are specifically disclosed: R=Rl+k*(Ru−Rl), wherein k is a variable ranging from 1 percent to 100 percent with a 1 percent increment, i.e., k is 1 percent, 2 percent, 3 percent, 4 percent, 5 percent, . . . , 50 percent, 51 percent, 52 percent, . . . , 95 percent, 96 percent, 97 percent, 98 percent, 99 percent, or 100 percent. Moreover, any numerical range defined by two R numbers as defined in the above is also specifically disclosed. Use of broader terms such as “comprises,” “includes,” and “having” should be understood to provide support for narrower terms such as “consisting of,” “consisting essentially of,” and “comprised substantially of” Accordingly, the scope of protection is not limited by the description set out above but is defined by the claims that follow, that scope including all equivalents of the subject matter of the claims.
While exemplary aspects of the invention have been shown and described, modifications thereof can be made by one skilled in the art without departing from the scope or teachings herein. The aspects described herein are exemplary only and are not limiting. Many variations and modifications of the compositions, systems, apparatus, and processes described herein are possible and are within the scope of the invention that is claimed and thus defined below. Accordingly, the scope of protection is not limited to the aspects described herein, but is only limited by the claims that follow, the scope of which shall include all equivalents of the subject matter of the claims. Unless expressly stated otherwise, the steps in a method claim may be performed in any order and with any suitable combination of materials and processing conditions.
This application is a 35 U.S.C. § 371 national stage application of PCT/US2018/021802 filed Mar. 9, 2018, and entitled “Nonlinear Optical Material,” which claims benefit of U.S. provisional patent application Ser. No. 62/469,956 filed Mar. 10, 2017, and entitled “Nonlinear Optical Material,” each of which is hereby incorporated herein by reference in their entirety for all purposes.
This work is funded in part by the United States government, in particular by the National Science Foundation under DMR 1503573.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2018/021802 | 3/9/2018 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2018/165583 | 9/13/2018 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20020000541 | Sasaki et al. | Jan 2002 | A1 |
| Number | Date | Country |
|---|---|---|
| 103031605 | Apr 2013 | CN |
| 2007127356 | Nov 2007 | WO |
| Entry |
|---|
| Ye et al. English machine translation of CN 103031605 A (Year: 2013). |
| PCT/US2018/021802 International Search Report and Written Opinion dated May 8, 2018 (13 p.). |
| Kang, Lei et al., “Prospects for Fluoride Carbonate Nonlinear Optical Crystals in the UV and Deep-UV Regions,” The Journal of Physical Chemistry, vol. 117, Nov. 18, 2013, pp. 25684-25692 (9 p.). |
| Wu, Hongping et al., “Deep-Ultraviolet Nonlinear-Optical Material K3Sr3Li2AI4B6O20F: Addressing the Structural Instability Problem in KBe2BO3F2,” Inorganic Chemistry, vol. 56, No. 15, Jul. 25, 2017 (1 p.). |
| Number | Date | Country | |
|---|---|---|---|
| 20210200058 A1 | Jul 2021 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62469956 | Mar 2017 | US |