Nonwoven webs with one or more surface treatments

Information

  • Patent Grant
  • 5834384
  • Patent Number
    5,834,384
  • Date Filed
    Tuesday, November 28, 1995
    29 years ago
  • Date Issued
    Tuesday, November 10, 1998
    26 years ago
Abstract
A nonwoven web having improved particulate barrier properties is provided. A surface treatment having a breakdown voltage no greater than 13 KV direct current is present on the nonwoven web. The particulate barrier properties are improved by subjecting said surface treatment treated nonwoven web to corona discharge.
Description

FIELD OF THE INVENTION
The present invention relates to fabrics useful for forming protective garments. More particularly, the present invention relates to nonwoven webs and surface coatings for such nonwoven webs.
BACKGROUND OF THE INVENTION
There are many types of limited use or disposable protective garments designed to provide barrier properties. Protective garments should be resistant to penetration by both liquids and/or particles. For a variety of reasons, it is undesirable for liquids and pathogens which may be carried by liquids to pass through the garment to contact persons working in an environment where pathogens are present.
Similarly, it is highly desirable to isolate persons from harmful substances which may be present in a work place or accident site. To increase the likelihood that the protective garment is correctly worn thereby reducing the chance of exposure, workers would benefit from wearing a protective garment that is relatively impervious to liquids and/or particles and durable but which is still comfortable so it does not reduce the worker's performance. After use, it is usually quite costly to decontaminate a protective garment that has been exposed to a harmful or hazardous substance. Thus, it is important that a protective garment be cost effective so as to be disposable.
One type of protective garment is disposable protective coveralls. Coveralls can be used to effectively isolate a wearer from a harmful environment in ways that open or cloak style protective garments such as drapes, gowns and the like are unable to do. Accordingly, coveralls have many applications where isolation of a wearer is desirable.
Disposable protective garments also include disposable surgical garments such as disposable surgical gowns and drapes. As is generally known, surgical gowns and drapes are designed to greatly reduce, if not prevent, the transmission through the surgical garment of liquids and biological contaminates which may become entrained therein. In surgical procedure environments, such liquid sources include the gown wearer's perspiration, patient liquids such as blood, saliva, perspiration and life support liquids such as plasma and saline.
Many surgical garments were originally made of cotton or linen and were sterilized prior to their use in the operating room. These surgical garments, however, permitted transmission therethrough or "strike-through" of many of the liquids encountered in surgical procedures. These surgical garments were undesirable, if not unsatisfactory, because such "strike through" established a direct path for transmission of bacteria and other contaminates to and from the wearer of the surgical garment. Furthermore, the garments were costly, and, of course, laundering and sterilization procedures were required before reuse.
Disposable surgical garments have largely replaced linen surgical gowns. Because many surgical procedures require generally a high degree of liquid repellency to prevent strike-through, disposable surgical garments for use under these conditions are, for the most part, made entirely from liquid repellent fabrics.
Therefore, generally speaking, it is desirable that disposable protective garments be made from fabrics that are relatively impervious to liquids and/or particulates. These barrier-type fabrics must also be suited for the manufacture of protective apparel at such low cost that make discarding the garments after only a single use economical.
Examples of disposable protective garments which are generally manufactured from nonwoven web laminates in order to assure that they are cost effectively disposable are coveralls, surgical gowns and surgical drapes sold by the Kimberly-Clark Corporation. Many of the disposable protective garments sold by Kimberly-Clark Corporation are manufactured from a three layer nonwoven web laminate. The two outer layers are formed from spunbonded polypropylene-based fibers and the inner layer is formed from meltblown polypropylene-based fibers. The outer layers of spunbonded fibers provide tough, durable and abrasion resistant surfaces. The inner layer is not only water repellent but acts as a breathable filter barrier allowing air and moisture vapor to pass through the bulk of the fabric while filtering out many harmful particles.
In some instances, the material forming protective garments may include a film layer or a film laminate. While forming protective garments from a film may improve particle barrier properties of the protective garment, such film or film-laminated materials may also inhibit or prevent the passage of air and moisture vapor therethrough. Generally, protective garments formed from materials which do not allow sufficient passage of air and moisture vapor therethrough become uncomfortable to wear correctly for extended periods of time.
Thus, while in some instances, film or film-laminated materials may provide improved particulate barrier properties as compared to nonwoven-laminated fabrics, nonwoven-laminated fabrics generally provide greater wearer comfort. Therefore, a need exists for inexpensive disposable protective garments, and, more particularly, inexpensive disposable protective garments formed from a nonwoven fabric which provide improved particulate barrier properties while also being breathable and thus comfortable to wear correctly for extended periods of time.
SUMMARY OF THE INVENTION
The present invention provides a nonwoven web having improved particulate barrier properties. In one embodiment, the nonwoven web may include at least one layer formed from fibers subjected to corona discharge. The fibers subjected to corona discharge may include a surface treatment having a breakdown voltage no greater than 13 thousand volts (KV) of direct current (DC) and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The nonwoven web may also include fibers formed from a blend of polypropylene and polybutylene. Desirably, the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend. Another surface treatment having a breakdown voltage greater than 13 KV DC may be present on the fibers subjected to corona discharge or on fibers not subjected to corona discharge or both.
In another embodiment, the nonwoven web may include at least one layer formed from spunbonded fibers and at least one layer formed from meltblown fibers. The fibers of at least one of the layers may be subjected to corona discharge and include a surface treatment having a breakdown voltage no greater than 13 KV DC, and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The nonwoven web may also include fibers formed from a blend of polypropylene and polybutylene. Desirably, the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend. Another surface treatment having a breakdown voltage greater than 13 KV DC may be present on the fibers subjected to corona discharge or on fibers not subjected to corona discharge or both.
In another embodiment, the nonwoven web may include at least two layers formed from spunbonded fibers and at least one layer formed from meltblown fibers. The layer formed from meltblown fibers is positioned between the two layers formed from spunbonded fibers. The fibers of at least one of the layers may be subjected to corona discharge and include a surface treatment having a breakdown voltage no greater than 13 KV DC, and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The nonwoven web may also include fibers formed from a blend of polypropylene and polybutylene. Desirably, the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend. Another surface treatment having a breakdown voltage greater than 13 KV DC may be present on the fibers subjected to corona discharge or on fibers not subjected to corona discharge or both.
In another embodiment, the nonwoven web may include at least two layers formed from spunbonded fibers and at least one layer formed from meltblown fibers wherein the layer formed from meltblown fibers is between the two layers formed from spunbonded fibers, and wherein the fibers forming at least one of the layers are subjected to corona discharge. At least one of the layers formed from spunbonded fibers may include a surface treatment having a breakdown voltage no greater than 13 KV DC, and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The layer formed from meltblown fibers includes a surface treatment having a breakdown voltage no greater than 13 KV DC, and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The meltblown layer may further be formed from fibers which are formed from a blend of polypropylene and polybutylene, and more particularly, the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend. Another surface treatment having a breakdown voltage greater than 13 KV DC may be present on the fibers subjected to corona discharge or on fibers not subjected to corona discharge or both.
In another embodiment, the nonwoven web includes at least two layers formed from spunbonded fibers and at least one layer formed from meltblown fibers wherein the layer formed from meltblown fibers is between the two layers formed from spunbonded fibers. The fibers forming at least one of the layers includes a surface treatment having a breakdown voltage no greater 13 KV DC, and wherein fibers forming another layer includes another surface treatment having a breakdown voltage greater than 13 KV DC. Each layer formed from fibers which includes a surface treatment is subjected to corona discharge. The spunbonded fibers of one of the layers may include a surface treatment having a breakdown voltage no greater than 13 KV DC, and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The spunbonded fibers of another layer may also include a surface treatment having a breakdown voltage greater than 13 KV DC. The layer formed from meltblown fibers may include a surface treatment having a breakdown voltage either no greater than 13 KV DC or greater than 13 KV DC or both.
DETAILED DESCRIPTION OF THE INVENTION
As used herein, the term "dielectric" means, according to McGraw-Hill Encyclopedia of Science & Technology, 7th Edition, Copyright 1992, a material, such as a polymer, which is an electrical insulator or which an electric field can be sustained with a minimum dissipation of power. A solid material is a dielectric if its valence band is full and is separated from the conduction band by at least 3 eV.
As used herein, the term "breakdown voltage" means that voltage at which electric failure occurs when a potential difference is applied to an electrically insulating material. The breakdown voltage reported for the various materials tested was determined by the ASTM test method for dielectric breakdown voltage (D 877-87).
As used herein, the term "electret" means a dielectric body possessing permanent or semipermanent electric poles of opposite sign.
As used herein, the term "surface treatment" means a material, for example a surfactant, which is present on the surface of another material, for example a shaped polymer such as a nonwoven. The surface treatment may be topically applied to the shaped polymer or may be added to a molten or semi-molten polymer. Methods of topical application include, for example, spraying, dipping or otherwise coating the shaped polymer with the surface treatment. Surface treatments which are added to a molten or semi-molten polymer may be referred to as "internal additives". Internal additives suitable for use in the present invention are generally non-toxic and have a low volatility. Desirably, these internal additives should be thermally stable at temperatures up to 300.degree. C., and sufficiently soluble in the molten or semi-molten polymer and should also sufficiently phase separate such that the additive migrates from the bulk of the shaped polymer towards a surface thereof as the shaped polymer cools.
As used herein, the terms "necking", "neck stretching" or "necked stretched" interchangeably refer to a method of elongating a fabric, generally in the machine direction, to reduce its width in a controlled manner to a desired amount. The controlled stretching may take place under cool, room temperature or greater temperatures and is limited to an increase in overall dimension in the direction being stretched up to the elongation required to break the fabric, which in many cases is about 1.2 to 1.4 times the original unstretched dimension. When relaxed, the web retracts toward its original dimensions. Such a process is disclosed, for example, in U.S. Pat. No. 4,443,513 to Meitner and Notheis and in U.S. Pat. Nos. 4,965,122, 5,226,992 and 5,336,545 to Morman which are all herein incorporated by reference.
As used herein the terms "neck softening" or "necked softened" mean neck stretching carried out without the addition of heat to the material as it is stretched, i.e., at ambient temperature. In neck stretching or softening, a fabric is referred to, for example, as being stretched by 20%.
As used herein, the term "nonwoven web" refers to a web that has a structure of individual fibers or filaments which are interlaid, but not in an identifiable repeating manner.
As used herein the term "spunbonded fibers" refers to fibers which are formed by extruding molten thermoplastic material as filaments from a plurality of fine, usually circular capillaries of a spinnerette with the diameter of the extruded filaments then being rapidly reduced as by, for example, in U.S. Pat. No. 4,340,563 to Appel et al., and U.S. Pat. No. 3,692,618 to Dorschner et al., U.S. Pat. No. 3,802,817 to Matsuki et al., U.S. Pat. Nos. 3,338,992 and 3,341,394 to Kinney, U.S. Pat. Nos. 3,502,763 and 3,909,009 to Levy, and U.S. Pat. No. 3,542,615 to Dobo et al which are all herein incorporated by reference. Spunbonded fibers are generally continuous and in some instances have an average diameter larger than 7 microns.
As used herein the term "meltblown fibers" means fibers formed by extruding a molten thermoplastic material through a plurality of fine, usually circular, die capillaries as molten threads or filaments into a high velocity, usually heated gas (e.g. air) stream which attenuates the filaments of molten thermoplastic material to reduce their diameter. Thereafter, the meltblown fibers are carried by the high velocity gas stream and are deposited on a collecting surface to form a web of randomly disbursed meltblown fibers. Meltblowing is described, for example, in U.S. Pat. No. 3,849,241 to Buntin, U.S. Pat. No. 4,307,143 to Meitner et al., and U.S. Pat. No. 4,707,398 to Wisneski et al which are all herein incorporated by reference. In some instances, meltblown fibers may generally have an average diameter smaller than 10 microns.
Polymers, and particularly polyolefins polymers, are well suited for the formation of fibers or filaments used in forming nonwoven webs which are useful in the practice of the present invention. Nonwoven webs can be made from a variety of processes including, but not limited to, air laying processes, wet laid processes, hydroentangling processes, spunbonding, meltblowing, staple fiber carding and bonding, and solution spinning.
The present invention provides a nonwoven web which may include at least one layer formed from fibers subjected to corona discharge. The nonwoven web may be formed from meltblown fibers or spunbonded fibers or both. The fibers subjected to corona discharge may include a surface treatment having a breakdown voltage no greater than 13 thousand volts or 13 kilovolts (KV) of direct current (DC) and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The nonwoven web may also include fibers formed from a blend of polypropylene and polybutylene. Desirably, the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend. Another surface treatment having a breakdown voltage greater than 13 KV DC may be present on the fibers subjected to corona discharge or on fibers not subjected to corona discharge or both.
In another embodiment, the nonwoven web may include at least one layer formed from spunbonded fibers and at least one layer formed from meltblown fibers. The fibers of at least one of the layers, and desirably the layer formed from meltblown fibers, may be subjected to corona discharge and include a surface treatment having a breakdown voltage no greater than 13 KV DC, and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The nonwoven web may also include fibers, and desirably the meltblown fibers, formed from a blend of polypropylene and polybutylene. Desirably, the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend. Another surface treatment having a breakdown voltage greater than 13 KV DC may be present on the fibers subjected to corona discharge or on fibers not subjected to corona discharge or both.
In another embodiment, the nonwoven web may include at least two layers formed from spunbonded fibers and at least one layer formed from meltblown fibers. The layer formed from meltblown fibers may be positioned between the two layers formed from spunbonded fibers. The fibers of at least one of the layers, and desirably the layer formed from meltblown fibers, may be subjected to corona discharge and include a surface treatment having a breakdown voltage no greater than 13 KV DC, and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The nonwoven web may also include fibers, and desirably meltblown fibers, formed from a blend of polypropylene and polybutylene. Desirably, the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend. Another surface treatment having a breakdown voltage greater than 13 KV DC may be present on the fibers subjected to corona discharge or on fibers not subjected to corona discharge or both.
In another embodiment, the nonwoven web may include at least two layers formed from spunbonded fibers and at least one layer formed from meltblown fibers wherein the layer formed from meltblown fibers may be positioned between the two layers formed from spunbonded fibers, and wherein the fibers forming at least one of the layers are subjected to corona discharge. At least one of the layers formed from spunbonded fibers may include a surface treatment having a breakdown voltage no greater than 13 KV DC, and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The layer formed from meltblown fibers includes a surface treatment having a breakdown voltage no greater than 13 KV DC, and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The meltblown layer may further be formed from fibers which are formed from a blend of polypropylene and polybutylene, and more particularly, the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend. Another surface treatment having a breakdown voltage greater than 13 KV DC may be present on the fibers subjected to corona discharge or on fibers not subjected to corona discharge or both.
In another embodiment, the nonwoven web includes at least two layers formed from spunbonded fibers and at least one layer formed from meltblown fibers wherein the layer formed from meltblown fibers may be positioned between the two layers formed from spunbonded fibers. The fibers forming at least one of the layers includes a surface treatment having a breakdown voltage no greater 13 KV DC, and wherein fibers forming another layer includes another surface treatment having a breakdown voltage greater than 13 KV DC. Each layer formed from fibers which includes a surface treatment is subjected to corona discharge. The spunbonded fibers of one of the layers may include a surface treatment having a breakdown voltage no greater than 13 KV DC, and desirably a breakdown voltage no greater than 8 KV DC and more desirably a breakdown voltage no greater than 5 KV DC and most desirably a breakdown voltage of between 1 KV DC and 5 KV DC. The spunbonded fibers of the other layer may include a surface treatment having a breakdown voltage greater than 13 KV DC. The layer formed from meltblown fibers may include a surface treatment having a breakdown voltage either no greater than 13 KV DC or greater than 13 KV DC or both.
As described in greater detail below, the entire thickness of the nonwoven web laminate may be subjected to corona discharge. Alternatively, individual nonwoven layers which, when combined, form the nonwoven web laminate may be separately subjected to corona discharge. When the entire thickness of the nonwoven web laminate is subjected to corona discharge, the fibers forming at least one of the nonwoven layers are desirably formed from a variety of dielectric polymers including, but not limited to, polyesters, polyolefins, nylon and copolymer of these materials. The fibers forming the other nonwoven layers may be formed from a variety of non-dielectric polymers, including, but not limited to, cellulose, glass, wool and protein polymers.
When one or more individual nonwoven layers are separately subjected to corona discharge, the fibers forming these nonwoven layers are desirably formed from the above described dielectric polymers. Those individual nonwoven layers which are not subjected to corona discharge may be formed from the above described non-dielectric polymers.
It has been found that nonwoven webs formed from thermoplastic based fibers and particularly polyolefin-based fibers are particularly well-suited for the above applications. Examples of such fibers include spunbonded fibers and meltblown fibers. Examples of such nonwoven webs formed from such fibers are the polypropylene nonwoven webs produced by the Assignee of record, Kimberly-Clark Corporation.
As previously described above, one embodiment of the present invention may include a nonwoven web laminate. For example, the nonwoven web laminate may include at least one layer formed from spunbonded fibers and another layer formed from meltblown fibers, such as a spunbonded/meltblown (S/M) nonwoven web laminate. In another embodiment, the nonwoven web laminate may include at least one layer formed from meltblown fibers which is positioned between two layers formed from spunbonded fibers, such as a spunbonded/meltblown/spunbonded (S/M/S) nonwoven web laminate. Examples of these nonwoven web laminates are disclosed in U.S. Pat. No. 4,041,203 to Brock et al., U.S. Pat. No. 5,169,706 to Collier, et al, and U.S. Pat. No. 4,374,888 to Bornslaeger which are all herein incorporated by reference. More particularly, the spunbonded fibers may be formed from polypropylene. Suitable polypropylenes for the spunbonded layers are commercially available as PD-9355 from the Exxon Chemical Company of Baytown, Tex.
More particularly, the meltblown fibers may be formed from polyolefin polymers, and more particularly a blend of polypropylene and polybutylene. Examples of such meltblown fibers are contained in U.S. Pat. Nos. 5,165,979 and 5,204,174 which are incorporated herein by reference. Still more particularly, the meltblown fibers may be formed from a blend of polypropylene and polybutylene wherein the polybutylene is present in the blend in a range from 0.5 to 20 weight percent of the blend. One such suitable polypropylene is designated 3746-G from the Exxon Chemical Co., Baytown, Tex. One such suitable polybutylene is available as DP-8911 from the Shell Chemical Company of Houston, Tex. The meltblown fibers may also contain a polypropylene modified according to U.S. Pat. No. 5,213,881 which is incorporated herein by reference.
The S/M/S nonwoven web laminate may be made by sequentially depositing onto a moving forming belt first a spunbonded fabric layer, then a meltblown fabric layer on top to the first spunbonded fabric and last another spunbonded fabric layer on top of the meltblown fabric layer and then bonding the laminate in a manner described below. Alternatively, the layers may be made individually, collected in rolls, and combined in a separate bonding step. Such S/M/S nonwoven web laminates usually have an average basis weight of from about 0.1 to 12 ounces per square yard (osy) (3 to 400 grams per square meter (gsm)), or more particularly from about 0.75 to about 5 osy (25 to 170 gsm) and still more particularly from about 0.75 to about 3 osy (25 to 100 gsm).
Methods of subjecting nonwoven webs to corona discharge, are well known by those skilled in the art. Briefly, corona discharge is achieved by the application of sufficient direct current (DC) voltage to an electric field initiating structure (EFIS) in the proximity of an electric field receiving structure (EFRS). The voltage should be sufficiently high such that ions are generated at the EFIS and flow from the EFIS to the EFRS. Both the EFIS and the EFRS are desirably formed from conductive materials. Suitable conductive materials include copper, tungsten, stainless steel and aluminum.
One particular technique of subjecting nonwoven webs to corona discharge is the technique disclosed in U.S. Pat. No. 5,401,446 which is assigned to the University of Tennessee, and is herein incorporated by reference. This technique involves subjecting the nonwoven web to a pair of electrical fields wherein the electrical fields have opposite polarities. Each electrical field forms a corona discharge.
In those instances where the nonwoven web is a nonwoven web laminate, the entire thickness of the nonwoven web laminate may be subjected to corona discharge. In other instances, one or more of the individual layers which form the nonwoven web laminate or the fibers forming such individual layers may be separately subjected to corona discharge and then combined with other layers in a juxtaposed relationship to form the nonwoven web laminate. In some instances, the electric charge on the surface of the nonwoven web laminate prior to corona discharge may be substantially the same as the electric charge on the surface of the corona discharge treated web. In other words, the surface of the nonwoven web laminate may not generally exhibit a higher electric charge after subjecting the web to corona discharge than the electric charge present on the surface of the web before subjecting it to corona discharge.
Nonwoven web laminates may be generally bonded in some manner as they are produced in order to give them sufficient structural integrity to withstand the rigors of further processing into a finished product. Bonding can be accomplished in a number of ways such as hydroentanglement, needling, ultrasonic bonding, adhesive bonding and thermal bonding.
Ultrasonic bonding is performed, for example, by passing the nonwoven web laminate between a sonic horn and anvil roll as illustrated in U.S. Pat. No. 4,374,888 to Bornslaeger.
Thermal bonding of a nonwoven web laminate may be accomplished by passing the same between the rolls of a calendering machine. At least one of the rollers of the calender is heated and at least one of the rollers, not necessarily the same one as the heated one, has a pattern which is imprinted upon the laminate as it passes between the rollers. As the fabric passes between the rollers it is subjected to pressure as well as heat. The combination of heat and pressure applied in a particular pattern results in the creation of fused bond areas in the nonwoven web laminate where the bonds thereon correspond to the pattern of bond points on the calender roll.
Various patterns for calender rolls have been developed. One example is the Hansen-Pennings pattern with between about 10 to 25% bond area with about 100 to 500 bonds/square inch as taught in U.S. Pat. No. 3,855,046 to Hansen and Pennings. Another common pattern is a diamond pattern with repeating and slightly offset diamonds.
The exact calender temperature and pressure for bonding the nonwoven web laminate depend on the thermoplastic(s) from which the nonwoven web is made. Generally for nonwoven web laminates formed from polyolefins, desirable temperatures are between 150.degree. and 350.degree. F. (66.degree. and 177.degree. C.) and the pressure is between 300 and 1000 pounds per linear inch. More particularly, for polypropylene, the desirable temperatures are between 270.degree. and 320.degree. F. (132.degree. and 160.degree. C.) and the pressure is between 400 and 800 pounds per linear inch.
In those instances where the nonwoven web is used in or around flammable materials and static discharge is a concern, the nonwoven web may be treated with any number of antistatic materials. In these instances, the antistatic material may be applied to the nonwoven by any number of techniques including, but not limited, to dipping the nonwoven into a solution containing the antistatic material or by spraying the nonwoven with a solution containing the antistatic material. In some instances the antistatic material may be applied to both the external surfaces of the nonwoven and/or the bulk of the nonwoven. In other instances, the antistatic material may be applied to portions of the nonwoven, such as a selected surface or surfaces thereof.
Of particular usefulness is the antistat or antistatic material known as ZELEC.RTM., an alcohol phosphate salt product of the Du Pont Corporation. The nonwoven web may be treated with the antistatic material either before or after subjecting the web to charging. Furthermore, some or all of the material layers may be treated with the antistatic material. In those instances where only some of the material layers are treated with antistatic material, the non-treated layer or layers may be subjected to charging prior to or after combining with the antistatic treated layer or layers.
Additionally, in those instances where the nonwoven web is used around alcohol, the nonwoven web may be treated with an alcohol repellent material. In these instances, the alcohol repellent material may be applied to the nonwoven by any number of techniques including, but not limited to, dipping or by spraying the nonwoven web with a solution containing the alcohol repellent material. In some instances the alcohol repellent material may be applied to both the external surfaces of the nonwoven and the bulk of the nonwoven. In other instances, the alcohol repellent material may be applied to portions of the nonwoven, such as a selected surface or surfaces thereof.
Of particular usefulness are the alcohol repellent materials formed from fluorinated urethane derivatives, an example of which includes FX-1801. FX-1801, formerly called L-10307, is available from the 3M Company of St. Paul, Minn. FX-1801 has a melting point of about 130.degree. to 138.degree. C. FX-1801 may be added to either the spunbonded and/or meltblown layer at an amount of about 0.1 to about 2.0 weight percent or more particularly between about 0.25 and 1.0 weight percent. FX-1801 may be topically applied or may be internally applied by adding the FX-1801 to the fiber forming polymer prior to fiber formation.
Generally, internal additives, such as the alcohol repellent additive FX-1801, suitable for use in the present invention should be non-toxic and have a low volatility. Additionally, the internal additive should be thermally stable at temperatures up to 300.degree. C., and sufficiently soluble in the molten or semi-molten fiber forming polymer. The internal additive should also sufficiently phase separate such that the additive migrates from the bulk of the polymer fiber towards the surface of the polymer fiber as the fiber cools without requiring the addition of heat. The layers of the fabric of the present invention may also contain fire retardants for increased resistance to fire, pigments to give each layer the same or distinct colors, and/or chemicals such as hindered amines to provide enhanced ultraviolet light resistance. Fire retardants and pigments for spunbonded and meltblown thermoplastic polymers are known in the art and may be internal additives. A pigment, if used, is generally present in an amount less than 5 weight percent of the layer.





EXAMPLES
To demonstrate the attributes of the present invention, several surface treatments were combined with nonwoven webs of various average basis weights and polymer blends as listed in TABLE I.
TABLE 1*__________________________________________________________________________SURFACETREATMENT AMOUNTINDUSTRIAL CHEMICAL APPLIED TO TYPE OFDESIGNATION DESCRIPTION SURFACE NONWOVEN WEB__________________________________________________________________________1. Y-12488 Polyalkyleneoxide Modified 4% and 1% 1.5 osy M Polydimethysiloxane Union Carbide Corporation2. HYPERMER Modified Polyester Surfactant 4% 1.5 osy M A409 98%; Xylene 2%; ICI America Inc.3. FC1802 C8 Fluorinated Alkyl Alkoxylate 86-89%; C8 Fluorinated Alkyl Sulfonamide 9-10%; C7 Fluorinated Alkyl 2.4% 1.5 osy M Alkocylate 2-4%; C7 Fluorinated Alkyl Sulfonamide 0.2-1%; 3M Corp.4. FX 1801 Fluorochemical Urethane 1%** 1.6 osy S/M/S Derivative - 100% - 3M Corp. (contained 0.03% ZELEC)5. TEGOPREN Polysiloxane Polyether 4% 1.5 osy M 5830 Copolymer - Goldschmidt Corp.6. TRITON Octlyphenoxypoylethoxy 2% 1.5 osy M X102 Ethanol having 12-13 Ethylene Oxide Groups - Rohm & Haas Co.7. ZELEC Alcohol Phosphate Salt; .03%*** 2.2 osy S/M/S Neutralized Mixed Alkyl KIMGUARD .RTM., & Phosphates - Du Pont 1.6 osy S/M/S8. FC808 Polymeric Fluoroalphatic Ester 2.95% 1.8 osy S/M/S 3M Corp. KLEENGUARD .RTM.9. MASIL Silicon Surfactant 2% 1.5 osy M SF19 PPG10. GEMTEX Dioctyl Sodium Sulfosuccinate .3% 1.5 osy M SM33 Based Anionic Finetex Corp.__________________________________________________________________________ S/M/S Spunbonded/Meltblown/Spunbonded Nonwoven Web Laminate S Spunbonded Nonwoven Web M Meltblown Nonwoven Web *All surface treatments applied topically except as noted. **Applied to molten polymer. Bloomed to surface of M. ***Applied topically to one S layer.
For samples 1-3, 5, 6, 9 and 10, the respective surface treatments were applied to a meltblown nonwoven web having an average basis weight of about 1.5 ounce per square yard (osy). These webs were made from Himont PF105 polypropylene.
For sample 4 and a portion of the nonwoven webs utilized in sample 7, the respective surface treatments were applied to a S/M/S laminate having an average basis weight of about 1.6 osy. These samples included a meltblown layer having an average basis weight of about 0.5 osy between two layers of spunbonded material, each spunbonded layer having an average basis weight of about 0.55 osy. The spunbonded layers were made from polypropylene copolymer designated PD-9355 by Exxon chemical Co. The meltblown layer was made from polypropylene designated 3746G from Exxon Chemical and polybutylene (10 weight percent) designated DP-8911 from Shell. The samples were necked softened by 8 percent at ambient temperature. The ZELEC surface treatment was present on one of the spunbonded surfaces in an amount of around 0.03% by weight of the spunbonded layer. Present in the meltblown layer of each of the above samples was FX 1801.
For the remaining portion of the nonwoven webs utilized in sample 7, the ZELEC surface treatment was applied to a S/M/S laminate having an average basis weight of about 2.2 osy. Both spunbonded layers had an average basis weight of around 0.85 osy and the meltblown layer had an average basis weight of around 0.5 osy. One of the spunbonded layers of this sample contained about 0.03% by weight of the spunbonded layer of ZELEC surface treatment.
For sample 8, the respective surface treatment was applied to a 1.8 osy S/M/S laminate. The spunbonded layers were formed from polypropylene resins--Exxon PD-3445 and Himont PF-301. White and dark blue pigments, Ampacet 41438 (Ampacet Inc., N.Y.) and SCC 4402 (Standrige Color Inc., GA.), respectively, were added to the polypropylene resins forming one of the spunbonded layers. The other spunbonded layer was formed from these polypropylene resins without pigments. The meltblown layer was formed from the polypropylene resin Himont PF-015 without pigments.
The meltblown layer had an average basis weight of about 0.45 osy and each spunbonded layer had an average basis weight of about 0.675 osy. The 2.95% FC808 solution was prepared by adding 0.5% hexanol, 2.95% FC808 and about 96.5% water. The FC808 solution was applied to one of the spunbonded layers. FC808 is an alcohol repellent surface treatment formed from a polymeric fluoroaliphatic ester (20%), water (80%) and traces of ethyl acetate (400 parts/million).
A portion of each of the surface treatment treated nonwoven webs described in TABLE 1, (samples 1-10) was removed and not subjected to corona discharge. The remainder of each of the surface treatment treated nonwoven web samples (1-10) was subjected to corona discharge. The corona discharge was produced by using a Model No. P/N 25A--120volt, 50/60 Hz reversible polarity power unit (Simco Corp., Hatfield, Pa.), which was connected to the EFIS, and a Model No. P16V 120V,.25A 50/60 Hz power unit (Simco Corp., Hatfield, Pa.) which was connected to the EFRS. The EFIS was a RC-3 Charge Master charge bar (Simco. Corp.) and the EFRS was a solid, three inch diameter, aluminum roller. The corona discharge environment was generally about 71.degree. F. and 53% relative humidity. As described in the above U.S. Pat. No. 5,401,446, two sets of EFIS/EFRS are used. The voltage applied to the first set of EFIS/EFRS was 15 KV DC/0.0 KV DC, respectively. The voltage applied to the second set of EFIS/EFRS was 25 KV DC/7.5 KV DC, respectively. The gap between the EFIS and the EFRS for each set was one inch.
The filtration efficiency for both corona treated and non-corona treated nonwoven web samples was analyzed. The particulate filtration test used to evaluate the particulate filtration properties of these nonwovens is generally known as the NaCl Filter Efficiency Test (hereinafter the "NaCl Test"). The NaCl Test was conducted on an automated filter tester, Certitest.TM. Model #8110, which is available from TSI Inc., St. Paul, Minn. The particulate filtration efficiency of the test fabric is reported as "% penetration". "% penetration" is calculated by the following formula--100.times.(downstream particles/upstream particles). The upstream particles represent the total quantity of approximately 0.1 .mu.m NaCl aerosol particles which are introduced into the tester. The downstream particles are those particles which have been introduced into the tester and which have passed through the bulk of the test fabric. Therefore, the "% penetration" value reported in TABLES I-V is a percentage of the total quantity of particles introduced into a controlled air flow within the tester which pass through the bulk of the test fabric. The size of the test fabric was 4.5" in diameter. The air flow may be constant or varied. At about 32 liters per minute of air flow, a pressure differential of between 4 and 5 mm Water Gage develops between the atmosphere on the upstream side of the test fabric as compared to the atmosphere on the down stream side of the test fabric. The filtration efficiency results for samples 1-6 and 8-10 are reported in TABLE 2. The filtration efficiency results for sample 7, the ZELEC surface treatment treated nonwovens webs, are not reported in TABLE 2.
TABLE 2______________________________________ FILTRATION EFFICIENCY % PENETRATION 0.1 .mu. NaClSURFACE NON-TREATMENT CORONA TREATED CORONA TREATED______________________________________1. Y 12488 (1%) 66.3 70.61. Y 12488 (4%) 54.3 55.22. A409 10.0 46.03. FC 1802 51.0 53.74. ZELEC + 1801 2.57 33.25. 5830 57.5 57.76. TRITON 102 1.30 51.38. FC808 62.4 63.09. SF19 45.5 80.910. GEMTEX SM33 6.30 71.2______________________________________
In view of TABLE 2, it was concluded that in those instances where there existed a substantial increase in filtration efficiency of the surface treatment treated nonwoven web between the non-corona treated and the corona treated, the corona treated nonwoven web had formed an electret.
Based upon the filtration efficiency results reported in TABLE 2, four liquid surface treatments were selected for breakdown voltage analysis. The filtration efficiency data for two of the liquid surface treatments, Y 12488 and TEGOPREN 5830, indicated generally an insubstantial difference in filtration efficiency between corona and non-corona treatment. The filtration efficiency data for the other two liquid surface treatments, TRITON 102 and SF19, indicated generally a substantial improvement in the filtration efficiency between corona and non-corona treatment.
The breakdown voltages for these liquid surface treatments are reported in TABLE 3. The breakdown voltage for each liquid surface treatment was determined by using a Hipot Tester, model no. Hipotronics 100, having a range of 0-25 KV DC and an accuracy of +/-2%. The electrodes were one inch diameter brass electrodes spaced 0.100 inches apart. The electrodes were submersed in a neat quantity of the respective liquid surface treatments. The voltage to the electrodes was increased from 0 KV DC at an approximate rate of 3 KV DC/second until breakdown occurred. The electrodes and the test vessel were thoroughly washed, rinsed with distilled water, and air dried before testing the next surface treatment.
TABLE 3______________________________________BREAKDOWN VOLTAGES*MATERIAL BREAKDOWN VOLTAGE (DC)______________________________________Y 12488 24 KVMASIL SF19 4.8 KVTEGOPREN 5830 15 KVTRITON X-102 1.8 KV______________________________________ *CURRENT AT BREAKDOWN VOLTAGE VARIED FROM 3.5 milliamps (MA) TO 4.9 MA.
For two of the liquid surface treatments, Y 12488 and TEGOPREN 5830, which indicated generally an insubstantial difference in filtration efficiency between corona and non-corona treatment, the breakdown voltages were 24 KV DC and 15 KV DC, respectively. For the two liquid surface treatments, TRITON 102 and SF19, which indicated generally a substantial improvement in the filtration efficiency between corona and non-corona treatment, the breakdown voltages were 1.8 KV DC and 4.8 KV DC, respectively.
While the invention has been described in detail with respect to specific embodiments thereof, it will be appreciated that those skilled in the art, upon attaining an understanding of the foregoing, may readily conceive of alterations to, variations of and equivalents to these embodiments. Accordingly, the scope of the present invention should be assessed as that of the appended claims and any equivalents thereto.
Claims
  • 1. A nonwoven electret comprising:
  • at least one layer of fibers, wherein the fibers have been subjected to corona discharge and include a surface treatment having a breakdown voltage no greater than 13 KV of direct current.
  • 2. The nonwoven electret of claim 1, wherein the fibers comprise a blend of polypropylene and polybutylene.
  • 3. The nonwoven electret of claim 1, wherein the breakdown voltage of the surface treatment is less than 8 KV of direct current.
  • 4. The nonwoven electret of claim 2, wherein the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend.
  • 5. A nonwoven electret comprising:
  • at least two layers of spunbonded fibers and at least one layer of meltblown fibers, wherein the layer of meltblown fibers is between the two layers of spunbonded fibers, wherein fibers of at least one layer have been subjected to corona discharge; and
  • wherein the fibers which have been subjected to corona discharge include a surface treatment having a breakdown voltage no greater than 13 KV of direct current.
  • 6. The nonwoven electret of claim 5, wherein the meltblown fibers comprise a blend of polypropylene and polybutylene.
  • 7. The nonwoven electret of claim 6 wherein the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend.
  • 8. The nonwoven electret of claim 5 wherein the average basis weight of the nonwoven web is about 1.8 ounces per square yard.
  • 9. The nonwoven electret of claim 5, wherein the meltblown fibers have been subjected to corona discharge.
  • 10. A nonwoven electret comprising:
  • at least two layers of spunbonded fibers and at least one layer of meltblown fibers, wherein the layer of meltblown fibers is between the two layers of spunbonded fibers, wherein the fibers forming at least one layer have been subjected to corona discharge; and
  • wherein at least one layer of spunbonded fibers includes a surface treatment having a breakdown voltage no greater than 13 KV of direct current and wherein the layer of meltblown fibers includes a surface treatment having a breakdown voltage no greater than 13 KV of direct current.
  • 11. The nonwoven electret of claim 10, wherein the meltblown fibers comprise a blend of polypropylene and polybutylene.
  • 12. The nonwoven electret of claim 11, wherein the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend.
  • 13. The nonwoven electret of claim 10, wherein the breakdown voltage of the surface treatment of the spunbonded fibers is less than 8 KV of direct current.
  • 14. The nonwoven electret of claim 10, where the breakdown voltage of the surface treatment of the meltblown fibers is less than 8 KV of direct current.
  • 15. The nonwoven electret of claim 10, wherein the meltblown fibers have been subjected to corona discharge.
  • 16. A nonwoven web comprising:
  • at least two layers of spunbonded fibers and at least one layer of meltblown fibers, wherein the layer of meltblown fibers is between the two layers of spunbonded fibers, wherein fibers of at least one layer include a surface treatment having a breakdown voltage no greater than 13 KV of direct current, and wherein fibers of at least one layer include a surface treatment having a breakdown voltage greater than 13 KV of direct current; and
  • wherein each layer of fibers having a surface treatment has been subjected to corona discharge.
  • 17. The nonwoven web of claim 16, wherein the spunbonded fibers of one of the layers include a surface treatment having a breakdown voltage no greater than 13 KV direct current, and wherein the spunbonded fibers of another layer include a surface treatment having a breakdown voltage greater than 13 KV direct current.
  • 18. The nonwoven web of claim 16, wherein the meltblown fibers include at least one of said surface treatments.
  • 19. A nonwoven web comprising:
  • at least one layer of fibers which has been subjected to corona discharge, wherein the fibers include a first surface treatment having a breakdown voltage no greater than 13 KV of direct current, and wherein the fibers include a second surface treatment having a breakdown voltage greater than 13 KV of direct current.
  • 20. The nonwoven web of claim 19, wherein the fibers comprise a blend of polypropylene and polybutylene.
  • 21. The nonwoven web of claim 20, wherein the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend.
  • 22. The nonwoven web of claim 19 wherein the breakdown voltage of the first surface treatment is less than 8 KV of direct current.
  • 23. The nonwoven web of claim 19, wherein the breakdown voltage of the second surface treatment is less than 8 KV of direct current.
  • 24. A nonwoven web comprising:
  • at least two layers of spunbonded fibers and at least one layer of meltblown fibers, wherein the layer of meltblown fibers is between the two layers of spunbonded fibers, at least one layer of fibers having been subjected to corona discharge, wherein at least one layer of fibers includes a first surface treatment having a breakdown voltage no greater than 13 KV of direct current, and wherein the at least one layer of fibers include a second surface treatment having a breakdown voltage greater than 13 KV of direct current.
  • 25. The nonwoven web of claim 24 wherein at least one of the fibers which include a surface treatment having a breakdown voltage no greater than 13KV has been subjected to corona discharge.
  • 26. The nonwoven web of claim 24 wherein the meltblown fibers comprise a blend of polypropylene and polybutylene.
  • 27. The nonwoven web of claim 26 wherein the polybutylene is present in the blend in a range from 0.5 to 20 percent weight of the blend.
  • 28. The nonwoven web of claim 24 wherein the breakdown voltage of the surface treatment of the spunbonded fibers is less than 8 KV of direct current.
US Referenced Citations (223)
Number Name Date Kind
RE30782 van Turnhout Oct 1981
RE31285 van Turnhout et al. Jun 1983
RE32171 van Turnhout Jun 1986
668791 Blake et al. Feb 1901
813063 Sutton et al. Feb 1906
859998 Wentworth Jul 1907
924032 Blake et al. Jun 1909
1222305 Kraus Apr 1917
1297159 Hedberg Mar 1919
1355477 Howell Oct 1920
2106865 Bantz et al. Feb 1938
2217444 Hill Oct 1940
2328577 Oglesby Sep 1943
2378067 Cook, Jr. Mar 1945
2398792 Johnson Apr 1946
2748018 Miller May 1956
2998051 Sittel Aug 1961
3012668 Fraas Dec 1961
3059772 Baron Oct 1962
3125547 Blatz Mar 1964
3281347 Winder Oct 1966
3323933 Barford et al. Jun 1967
3338992 Kinney Aug 1967
3341007 Mayer et al. Sep 1967
3341394 Kinney Sep 1967
3380584 Fulwyler Apr 1968
3402814 Morel et al. Sep 1968
3436797 Graf et al. Apr 1969
3502763 Hartman Mar 1970
3542615 Dobo et al. Nov 1970
3581886 Singewald et al. Jun 1971
3692606 Miller et al. Sep 1972
3692618 Dorschner et al. Sep 1972
3802817 Matsuki et al. Apr 1974
3821021 McMillan Jun 1974
3849241 Butin et al. Nov 1974
3855046 Hansen et al. Dec 1974
3859330 Proskow Jan 1975
3896802 Williams Jul 1975
3907604 Prentice Sep 1975
3909009 Cvetko et al. Sep 1975
3962386 Driscoll Jun 1976
3979529 Rebentisch et al. Sep 1976
3998916 van Turnhout Dec 1976
4011067 Carey, Jr. Mar 1977
4013816 Sabee et al. Mar 1977
4035164 Taylor Jul 1977
4041203 Brock et al. Aug 1977
4058724 McKinney et al. Nov 1977
4070218 Weber Jan 1978
4091140 Harrnon May 1978
4096289 Nischwitz et al. Jun 1978
4103062 Aberson et al. Jul 1978
4140607 Kreiseimeier et al. Feb 1979
4170304 Huke Oct 1979
4178157 van Turnhout et al. Dec 1979
4185972 Nitta et al. Jan 1980
4196245 Kitson et al. Apr 1980
4208366 Kinney Jun 1980
4209563 Sisson Jun 1980
4215682 Kubik et al. Aug 1980
4223677 Anderson Sep 1980
4273635 Beraud et al. Jun 1981
4298440 Hood Nov 1981
4305797 Knoll et al. Dec 1981
4307143 Meitner Dec 1981
4308223 Stern Dec 1981
4310478 Balslev et al. Jan 1982
4323374 Shinagawa et al. Apr 1982
4324198 Muz Apr 1982
4340563 Appel et al. Jul 1982
4342812 Selwood Aug 1982
4353799 Leonard Oct 1982
4357234 Inculet et al. Nov 1982
4363682 Thiebault Dec 1982
4363723 Knoll et al. Dec 1982
4373224 Bandai et al. Feb 1983
4374727 Takahashi et al. Feb 1983
4374888 Bornslaeger Feb 1983
4375718 Wadsworth et al. Mar 1983
4392876 Schmidt Jul 1983
4394235 Brandt et al. Jul 1983
4411795 Olson Oct 1983
4430277 Lin Feb 1984
4443513 Meitner et al. Apr 1984
4443515 Atlas Apr 1984
4451589 Morman et al. May 1984
4455195 Kinsley Jun 1984
4455237 Kinsley Jun 1984
4456648 Adamse et al. Jun 1984
4492633 Sandulyak et al. Jan 1985
4507539 Sando et al. Mar 1985
4513049 Yamasaki et al. Apr 1985
4514289 Inculet Apr 1985
4517143 Kisler May 1985
4534918 Forrest, Jr. Aug 1985
4547420 Krueger et al. Oct 1985
4551378 Carey, Jr. Nov 1985
4554207 Lee Nov 1985
4555811 Shimalla Dec 1985
4588537 Klaase et al. May 1986
4592815 Nakao Jun 1986
4594626 Frangesh Jun 1986
4618524 Groitzsch et al. Oct 1986
4622259 McAmish et al. Nov 1986
4623438 Felton et al. Nov 1986
4626263 Inoue et al. Dec 1986
4652282 Ohmori et al. Mar 1987
4652322 Lim Mar 1987
4657639 Mahadevan et al. Apr 1987
4657804 Mays et al. Apr 1987
4663220 Wisneski May 1987
4670913 Morell et al. Jun 1987
4671943 Wahlquist Jun 1987
4677017 DeAntonis et al. Jun 1987
4689241 Richart et al. Aug 1987
4699823 Kellenberger et al. Oct 1987
4705151 Eldridge Nov 1987
4707398 Boggs Nov 1987
4714647 Shipp, Jr. et al. Dec 1987
4720415 VanderWielen et al. Jan 1988
4729371 Krueger et al. Mar 1988
4738772 Giesfeldt Apr 1988
4739882 Parikh et al. Apr 1988
4749348 Klaase et al. Jun 1988
4761326 Barnes et al. Aug 1988
4789504 Ohmori et al. Dec 1988
4795668 Krueger et al. Jan 1989
4797201 Kuppers et al. Jan 1989
4797318 Brooker et al. Jan 1989
4818464 Lau Apr 1989
4826703 Kisler May 1989
4831664 Suda May 1989
4847914 Suda Jul 1989
4859266 Akasaki et al. Aug 1989
4863785 Berman et al. Sep 1989
4863983 Johnson et al. Sep 1989
4874399 Reed et al. Oct 1989
4874659 Ando et al. Oct 1989
4883052 Weiss et al. Nov 1989
4886527 Fottinger et al. Dec 1989
4894131 Jacobs et al. Jan 1990
4901370 Suda Feb 1990
4904174 Moosmayer et al. Feb 1990
4920168 Nohr et al. Apr 1990
4944854 Felton et al. Jul 1990
4948515 Okumura et al. Aug 1990
4948639 Brooker et al. Aug 1990
4960820 Hwo Oct 1990
4965122 Morman Oct 1990
4983677 Johnson et al. Jan 1991
5012094 Hamade Apr 1991
5021501 Ohmori et al. Jun 1991
5032419 Lamirand et al. Jul 1991
5035941 Blackburn Jul 1991
5051159 Togashi et al. Sep 1991
5055151 Duffy Oct 1991
5057710 Nishiura et al. Oct 1991
5062158 Oka et al. Nov 1991
5077468 Hamade Dec 1991
5090975 Requejo et al. Feb 1992
5110620 Tani et al. May 1992
5112048 Deeds May 1992
5112677 Tani et al. May 1992
5118942 Hamade Jun 1992
5135724 Dinter et al. Aug 1992
5138971 Nakajima et al. Aug 1992
5143767 Matsuura et al. Sep 1992
5149335 Killenberger et al. Sep 1992
5156902 Pieper et al. Oct 1992
5165979 Watkins et al. Nov 1992
5169706 Collier et al. Dec 1992
5173356 Eaton et al. Dec 1992
5178932 Perkins et al. Jan 1993
5183701 Jacobs et al. Feb 1993
5188885 Timmons et al. Feb 1993
5204174 Daponte et al. Apr 1993
5206061 Ando et al. Apr 1993
5213881 Timmons et al. May 1993
5213882 Sassa et al. May 1993
5226992 Morman Jul 1993
5230727 Pound et al. Jul 1993
5232770 Joseph Aug 1993
5238733 Joseph et al. Aug 1993
5244482 Hassenboehler, Jr. Sep 1993
5246637 Matsuura et al. Sep 1993
5247072 Ning et al. Sep 1993
5254297 Deeds Oct 1993
5256176 Matsuura et al. Oct 1993
5257982 Cohen et al. Nov 1993
5264276 McGregor et al. Nov 1993
5284703 Everhart et al. Feb 1994
5286326 Greve Feb 1994
5294482 Gessner Mar 1994
5306534 Bosses Apr 1994
5308674 Zafiroglu May 1994
5308691 Lim et al. May 1994
5336545 Morman Aug 1994
5350620 Sundet et al. Sep 1994
5389202 Everhart et al. Feb 1995
5397413 Trimble et al. Mar 1995
5401446 Tsai et al. Mar 1995
5407581 Onodera et al. Apr 1995
5409766 Yuasa et al. Apr 1995
5411576 Jones et al. May 1995
5436033 Mino et al. Jul 1995
5436066 Chen Jul 1995
5441550 Hassenboehler, Jr. Aug 1995
5443606 Hassenboehler, Jr. Aug 1995
5455108 Quincy et al. Oct 1995
5456972 Roth et al. Oct 1995
5464688 Timmons et al. Nov 1995
5468428 Hanschen et al. Nov 1995
5472481 Jones et al. Dec 1995
5482765 Bradley et al. Jan 1996
5486411 Hassenboehler, Jr. et al. Jan 1996
5491022 Smith Feb 1996
5493117 Tamaki et al. Feb 1996
5496507 Angadjivand et al. Mar 1996
5503745 Ogata et al. Apr 1996
5552012 Morris et al. Sep 1996
5620785 Watt et al. Apr 1997
5637165 Chen Jun 1997
Foreign Referenced Citations (40)
Number Date Country
1188452 Jun 1985 CAX
0 125 851 Nov 1984 EPX
0 156 160 Oct 1985 EPX
0 334 829 Sep 1989 EPX
0 337 662 Oct 1989 EPX
0 375 234 Jun 1990 EPX
0 391 725 Oct 1990 EPX
0 444 671 Sep 1991 EPX
0 462 574 Dec 1991 EPX
0 478 011 Apr 1992 EPX
0 497 072 Aug 1992 EPX
0 520 798 Dec 1992 EPX
0 550 029 Jul 1993 EPX
0 575 629 Dec 1993 EPX
0 576 738 Jan 1994 EPX
0 594 123 Apr 1994 EPX
0 754 796 Jan 1997 EPX
1 084 015 Sep 1957 DEX
44 47 152 Jul 1995 DEX
58-076118 Jul 1958 JPX
62-053719 Aug 1987 JPX
62-074423 Sep 1987 JPX
1-246413 Oct 1989 JPX
5-064713 Mar 1993 JPX
2 026 379 Feb 1980 GBX
2 242 142 Sep 1991 GBX
8103265 Nov 1981 WOX
9011784 Oct 1990 WOX
9108254 Jun 1991 WOX
9216681 Oct 1992 WOX
9306168 Apr 1993 WOX
9309156 May 1993 WOX
9400166 Jan 1994 WOX
9401068 Jan 1994 WOX
WO 9400166 Jan 1994 WOX
9505232 Feb 1995 WOX
9505501 Feb 1995 WOX
9522646 Aug 1995 WOX
9600093 Jan 1996 WOX
9704155 Feb 1997 WOX
Non-Patent Literature Citations (21)
Entry
U.S. application No. 08/198,298, Feb. 22, 1994, Improved Nonwoven Barrier And Method Of Making The Same.
U.S. application No. 08/266,293, Jul. 27, 1994, Improved Nonwoven Barrier And Method Of Making The Same.
U.S. application No. 08/351,966, Dec. 08, 1994, Method Of Forming A Particle Size Gradient In An Absorbent Article.
U.S. application No. 08/366,850, Dec. 30, 1994, Improved Nonwoven Laminate Barrier Material.
U.S. application No. 08/405,485, Mar. 16, 1995, Nonwoven Laminate Barrier Material.
U.S. application No. 08/450,043, May 25, 1995, Filter Matrix.
U.S. application No. 08/504,209, Jul. 19, 1994, Nonwoven Barrier And Method Of Making The Same.
U.S. application No. 08/690,587, Jul. 31, 1996, Improved Nonwoven Barrier.
J. van Turnhout: Topics in Applied Physics, vol. 33, Chapter 3 "Thermally Stimulated Discharge of Electrets", pp. 81-215 (1980).
J. van Turnhout: Thermally Stimulated Discharge of Polymer Electrets, Chapter 1, pp. 1-24 (1975).
G.M. Sessler: Electronic Properties of Polymers, Chapter 3 "Charge Storage", pp. 59-107.
"Bonding Process", IBM Technical Disclosure Bulletin, vol. 14, No. 12, May 1972.
USSN 08/242,948 filed May 16, 1994 entitled "Nonwoven Absorbent Polymeric Fabric Exhibition Improvement Fluid Management And Methods For Making The Same".
An Introduction to Electrostatic Separation, Technical Bulletin, Bulletin 8570, Carpco, Inc.
Electrostatic Separation of Mixed Granular Solids by Oliver C. Ralston, Elsevier Publishing Company, 1961, Chapter IV, "Applications of Electrostatic Separation", pp. 134-234.
Database WPI, Section Ch, Week 8930, Derwent Publications, Ltd., London, GB; Class A94,AN 89-217687 XP002005648 & JP,A,01 156 578 (Showa Denko), 20 Jun. 1989, See Abstract.
Database WPI, Section Ch, Week 8428, Derwent Publications Ltd., London, GB; Class A87, AN 84-173431, XP002008760, & JP,A,59 094 621 (Unitika KK), 31 May 1984, see abstract.
Patent Abstracts of Japan, vol. 10, No. 71 (C-334), 20 Mar. 1986 & JP,A,60 209220 (Kouken K.K.), 21 Oct. 1985, see abstract.
Patent Abstracts of Japan, vol. 6, No 191 (C-127), 30 Sep. 1982 & JP,A,57 105217 (Nitta K.K.), 30 Jun. 1982, see abstract & Chemical Abstracts, vol. 97, No. 26, 27 Dec. 1982, Columbus, Ohio, US; abstract No. 218901, "Fibrous Filtering Material", see abstract.
Patent Abstracts of Japan, vol. 11, No. 315 (C-451), 14 Oct. 1987 & JP,A,62 102809 (Mitsui Petrochem. Ind. Ltd.), 13 May 1987, see abstract & Database WPI, Section CH, Week 8725, Derwent Publications Ltd., London, GB; Class A12, AN 87-172842 & JP,A,62 102 809 (Mitsui Petrochem. Ind. Co. Ltd.), 13 May 1987, see abstract).
Journal of Electrostatics, vol. 21, 1988, Amsterdam NL, pp. 81-98, XP002012022, P. A. Smith & G. C. East: "Generation of Triboelectric Charge in Textile Fibre Mistures, and their use as Air Filters", see document.