Claims
- 1. A catalytic structure capable of reducing the concentration of undesirable gases in the exhaust gases of an internal combustion engine by chemically reducing oxides of nitrogen, said structure having high NO.sub.x reducing activity and comprising a thin, expanded metal foil structure having a plurality of strands defining openings therebetween said structure consisting essentially of a metallic reinforcing member and a metallic catalytic surface layer metallurgically bonded thereto, said layer comprising an NO.sub.x reducing catalyst comprising a mixture of nickel and copper, said metallic reinforcing member comprising:
- i. from about 50 to 85 weight percent of a first metal selected from the group consisting of nickel, mixtures of nickel and cobalt, mixtures of nickel and iron, and mixtures of nickel, iron and cobalt, said iron and cobalt individually not exceeding about 1 weight percent of said member and said nickel being present in said mixtures in an amount of at least about 48 weight percent of said member, and
- ii. from about 15 to about 50 weight percent of a second metal selected from the group consisting of chromium and mixtures of chromium and aluminum, said aluminum not exceeding about 10 weight percent of said member and said chromium being present in said mixtures in an amount of at least about 5 weight percent of said member.
- 2. The catalytic structure of claim 1 wherein said first metal is commercially pure nickel and is present in an amount of from 50 to 82 weight percent and said second metal is chromium and is present in an amount of from 18 to 50 weight percent of said metallic member.
- 3. The catalytic structure of claim 2 wherein said metallic reinforcing member consists essentially of about 80 weight percent commercially pure nickel and about 20 weight percent chromium.
- 4. The catalytic structure of claim 1 wherein said metallic reinforcing member is an expanded metal foil having a thickness less than about 0.010 inches.
- 5. The catalytic structure of claim 2 wherein said metallic reinforcing member is an expanded metal foil having a thickness less than about 0.010 inches.
- 6. The catalytic structure of claim 3 wherein said metallic reinforcing member is an expanded metal foil having a thickness less than about 0.010 inches.
- 7. The catalytic structure of claim 4 wherein said NO.sub.x catalyst consists essentially of a mixture of copper and nickel and constitutes about 0.5 to 50 weight percent of said structure.
- 8. The catalytic structure of claim 5 wherein said NO.sub.x catalyst consists essentially of 80 weight percent nickel and 20 weight percent copper.
- 9. The catalytic structure of claim 6 wherein said NO.sub.x catalyst consists essentially of 80 weight percent nickel and 20 weight percent copper.
- 10. The catalytic structure of claim 4 wherein said chromium is present throughout the catalytic structure as a gradient of chromium ranging from a maximum concentration in said reinforcing member to a minimum concentration up to about 15% by weight in said catalytic layer.
- 11. The catalytic structure of claim 5 wherein said chromium is present throughout the catalytic structure as a gradient of chromium ranging from a maximum concentration in said reinforcing member to a minimum concentration up to about 15% by weight in said catalytic layer.
- 12. The catalytic structure of claim 6 wherein said chromium is present throughout the catalytic structure as a gradient of chromium ranging from a maximum concentration in said reinforcing member to a minimum concentration up to about 15% by weight in said catalytic layer.
- 13. The catalytic structure of claim 1 prepared by
- a. forming an expanded metal foil having a plurality of strands defining openings therebetween,
- b. coating said expanded metal foil with chromium,
- c. heating said chromium coated foil in a non-oxidizing atmosphere to a temperature sufficient to cause said chromium to diffuse into said metal foil,
- d. coating said chromium coated foil with metallic NO.sub.x reducing catalyst, and
- e. heating the catalyst coated foil under non-oxidizing conditions at a temperature sufficient to cause said NO.sub.x reducing catalyst to metallurgically bond with said chromium coated foil.
- 14. The catalytic structure of claim 13 wherein said NO.sub.x reducing catalyst comprises a layer of nickel and a layer of copper.
- 15. The catalytic structure of claim 13 wherein said expanded metal foil consists essentially of commercially pure nickel.
- 16. The catalytic structure of claim 13 wherein said coating in steps (b) and (d) is accomplished by electroplating.
- 17. A catalytic structure capable of reducing the concentration of undesirable gases in the exhaust gases of an internal combustion engine by chemically reducing oxides of nitrogen, said structure having high NO.sub.x reducing activity and structural durability in the presence of said exhaust gases at temperatures up to 1900.degree. F, consisting essentially of an expanded metal reinforcing member having a plurality of strands defining openings therebetween which retains its strength and oxidation resistance at temperatures in excess of about 1100.degree. F. and up to about 1900.degree. F. and a metallic catalytic surface layer comprising an NO.sub.x reducing catalyst metallurgically bonded to said reinforcing member.
- 18. The structure of claim 17 wherein said expanded metal member is a foil having a thickness less than about .010 inches.
- 19. The structure of claim 18 wherein said NO.sub.x catalyst is selected from the group consisting of nickel, cobalt, iron, manganese, copper and mixtures thereof.
- 20. The structure of claim 19 wherein said NO.sub.x reducing catalyst is nickel.
- 21. The structure of claim 18 wherein said reinforcing member is chromium containing alloy and said chromium is present in said structure as a gradient of chromium ranging from a maximum concentration in said reinforcing member to a minimum concentration up to about 15% by weight in said catalytic layer.
- 22. The structure of claim 19 wherein said NO.sub.x reducing catalyst is copper.
- 23. The structure of claim 19 wherein said NO.sub.x reducing catalyst is an alloy of nickel and copper.
CROSS REFERENCE TO RELATED APPLICATIONS
This application is a continuation-in-part of U.S. patent applications Ser. No. 441,504 filed Feb. 11, 1974; Ser. No. 451,032 filed Mar. 22, 1974; Ser. No. 453,567 filed Mar. 22, 1974; Ser. No. 457,101 filed Apr. 1, 1974; Ser. No. 460,742 filed Apr. 15, 1974; Ser. No. 460,786 filed Apr. 15, 1974; Ser. No. 460,787 filed Apr. 15, 1974; Ser. No. 461,436 filed Apr. 15, 1974; Ser. No. 466,737 filed May 3, 1974, Ser. No. 466,965 filed May 6, 1974 and Ser. No. 467,106 filed May 6, 1974, which in turn are continuation-in-part applications of the therewith co-pending U.S. patent applications respectively Ser. No. 207,338, filed Dec. 13, 1971; Ser. No. 207,284, filed Dec. 13, 1971; Ser. No. 207,337, filed Dec. 13, 1971; Ser. No. 207,303, filed Dec. 13, 1971; Ser. No. 240,028, filed Mar. 31, 1972; Ser. No. 240,029, filed Mar. 31, 1972; Ser. No. 240,091, filed Mar. 31, 1972; Ser. No. 240,090, filed Mar. 31, 1972; Ser. No. 340,092, filed Mar. 31, 1972; Ser. No. 207,281, filed Dec. 13, 1971; Ser. No. 207,525, filed Dec. 13, 1971, all of which are now abandoned which in turn are continuation-in-part applications of the therewith copending application Ser. No. 149,331, filed June 2, 1971 (now abandoned).
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
3719739 |
Thompson |
Mar 1973 |
|
Non-Patent Literature Citations (2)
Entry |
Bernstein et al., "Application of Catalysts to Automotive NO.sub.x Emissions Control", AES, No. 710014, Jan. 1971. |
Chemical Abstracts, vol. 59, p. 1325g, 1963. |
Related Publications (20)
|
Number |
Date |
Country |
|
451032 |
Mar 1974 |
|
|
453567 |
Mar 1974 |
|
|
457101 |
Apr 1974 |
|
|
460742 |
Apr 1974 |
|
|
460786 |
Apr 1974 |
|
|
460787 |
Apr 1974 |
|
|
461436 |
Apr 1974 |
|
|
466737 |
May 1974 |
|
|
466965 |
May 1974 |
|
|
467106 |
May 1974 |
|
|
207284 |
Dec 1971 |
|
|
207337 |
Dec 1971 |
|
|
207303 |
Dec 1971 |
|
|
240028 |
Mar 1972 |
|
|
240029 |
Mar 1972 |
|
|
240091 |
Mar 1972 |
|
|
240090 |
Mar 1972 |
|
|
240092 |
Mar 1972 |
|
|
207281 |
Dec 1971 |
|
|
207525 |
Dec 1971 |
|
Continuation in Parts (3)
|
Number |
Date |
Country |
Parent |
441504 |
Feb 1974 |
|
Parent |
207338 |
Dec 1971 |
|
Parent |
149331 |
Jun 1971 |
|